A Bell-Shaped Mn11Gd2 Single-Molecule Magnet - American

Jul 11, 2007 - CNRS, Centre de Recherche Paul PascalsUPR8641, 115 aVenue du Dr. ... at the shoulder of the bell, and the remaining six MnIII centers...
0 downloads 0 Views 135KB Size
Published on Web 07/11/2007

A Bell-Shaped Mn11Gd2 Single-Molecule Magnet Valeriu M. Mereacre,† Ayuk M. Ako,† Rodolphe Cle´ rac,‡ Wolfgang Wernsdorfer,§ George Filoti,# Juan Bartolome´ ,# Christopher E. Anson,† and Annie K. Powell*,† Institut fu¨r Anorganische Chemie der UniVersita¨t Karlsruhe, D-76128 Karlsruhe, Germany, UniVersite´ Bordeaux 1, CNRS, Centre de Recherche Paul PascalsUPR8641, 115 aVenue du Dr. Albert Schweitzer, 33600 Pessac, France, Institut Ne´ elsCNRS, 38042 Grenoble Cedex 9, France, and Instituto de Ciencia de Materiales de Aragon, Ciuda UniVersitaria, 50009-Zaragoza, Spain Received February 14, 2007; E-mail: [email protected]

The synthesis of transition-metal clusters with unusual magnetic properties has become an area of intense research activity since the discovery of single-molecule magnets (SMMs).1 The quest for new SMMs displaying high blocking temperatures has focused mainly on the use of paramagnetic 3d metal ions.2-5 SMM behavior results from the favorable arrangement of metal ions with single ion anisotropy in a high-ground-spin state molecule, and some recent synthetic efforts have turned attention to combining 3d and 4f ions in complexes to enhance both spin and anisotropy. Recent success in synthesizing mixed transition metal and lanthanide SMMs presenting various core topologies includes Cu2Tb26 and Mn6Dy67, which have been described as SMMs on the observation of frequency-dependent out-of-phase ac signals, and Mn11Dy48, Mn2Dy29, Fe2Dy210, and Fe2Ho210, which additionally show hysteresis loops in the magnetization. Recently we reported on triangular dysprosium compounds showing SMM behavior of thermally excited spin states11 which has attracted us to exploring mixed d/f compounds as a means of enhancing anisotropy and/or spin state. Herein we report an efficient procedure toward the isolation of high-nuclearity heterometallic complexes using a preformed hexanuclear Mn complex, [MnIII2MnII4O2(piv)10(4-Me-py)2.5(pivH)1.5]12 (1) (pivH ) tBuCO2H), as a source of MnII/III ions. Reaction of 1 with Gd(NO3)3‚6H2O in the presence of 2-furan-carboxylic acid (fcaH) in CH3CN results in the formation of the high-nuclearity complex [MnIII9MnII2Gd2(O)8(OH)2(piv)10.6(fca)6.4(NO3)2(H2O)]‚13CH3CN‚H2O (2‚13MeCN‚ H2O).13 The Mn11Gd2 aggregate 2 crystallizes14 in the triclinic space group P1h, and its molecular structure is shown in Figure 1. The oxidation states of the Mn centers were determined by bond-valence sum (BVS) calculations,15 with Mn(1)-Mn(9) assigned as MnIII and Mn(10) and Mn(11) as MnII. The assignments of O(10) as (µ3-O)2- and of O(2) and O(3) as (µ3-OH)- were also confirmed by BVS calculations; the H-atoms on O(2) and O(3) could be located and refined. The core of the complex 2 can be described as bell-shaped. The MnIII and MnII centers form the shell of the bell, with Mn(9) at the apex, Mn(5), Mn(8), Mn(10), and Mn(11) at the shoulder of the bell, and the remaining six MnIII centers forming the rim of the bell. The two Gd centers can be thought of as forming the bell’s clapper, and since the Gd‚‚‚Gd vector is inclined with respect to the axis of the bell, this gives the impression that the bell is ringing. Gd(1) is ten-coordinate and is connected to each of the eleven Mn atoms through the six (µ4-O), one (µ3-O), and two (µ3-OH) bridges. Its coordination polyhedron may be best described as a bicapped square antiprism. The second Gd is nine† ‡ § #

Universita¨t Karlsruhe. Universite´ Bordeaux 1; CNRS, Centre de Recherche Paul Pascal. Institut Ne´el - CNRS. Instituto de Ciencia de Materiales de Aragon.

9248

9

J. AM. CHEM. SOC. 2007, 129, 9248-9249

Figure 1. Molecular structure of 2 (above) and its core (below). Disorder and organic H-atoms omitted for clarity: Gd, green; MnIII, purple; MnII, pink; O, red; N, blue; C, gray.

coordinate and hangs below the rim of the bell. It is connected to the other Gd and four of the MnIII atoms through one (µ4-O) and the two (µ3-OH) bridges, and two oxygen atoms from two (µ3carboxylate) bridges. Its coordination sphere is completed by two chelating nitrate ions. The Mn centers all have octahedral coordination geometries except for Mn(6), which is square-pyramidal, with the MnIII all showing the expected Jahn-Teller distortions. Of the 17 carboxylate ligands (ten pivalate, six furoate, and one that is a disordered superposition), the unusual (µ4,η2,η2) bridging mode is seen for one furoate and one pivalate ligand. In addition to these µ4-bridging carboxylates, four of the furoates adopt a (µ3, η2, η1) triply bridging mode, while the sixth furoate and all the remaining pivalates form simple bridges between two metal centers. In other words, five of the six furoates bridge between three or four metal centers, whereas all but one of the pivalates adopt a simple µ2bridging mode. The MnIII Jahn-Teller axes have an irregular 10.1021/ja071073m CCC: $37.00 © 2007 American Chemical Society

COMMUNICATIONS

Figure 2. Plots of the out-of-phase (χ′′) ac susceptibility signals versus temperature for complex 2 with an applied 3 Oe ac field in zero dc field.

the temperature lowered to a chosen value, the field switched off, and the decay monitored with time. The data were scaled in a single master curve to construct the Arrhenius plot, and the fit of the thermally activated region above ∼0.5 K gave τ0 ) 2 × 10-12 s and an effective barrier ∆eff ) 18.4 K, which is the highest value reported so far for 3d-4f SMMs.8,9 Given the lack of obvious intermolecular interactions, the relatively low value of τ0 compared with other 3d-4f SMMs might be the result of the presence of a higher spin state. Below ∼0.16 K, the relaxation time becomes essentially temperature-independent, consistent with the purely quantum regime where QTM is only via the lowest energy (ms levels. Probably the Jahn-Teller distortions of the MnIII centers make the major contribution to the anisotropy with the MnII and GdIII centers contributing to the spin. In conclusion, this tridecanuclear manganese-lanthanide complex has an unusual topology and SMM properties. The synthetic method allows for the assembly of related materials. Acknowledgment. We thank MAGMANet (NMP3-CT-2005515767), Bordeaux 1 University, the CNRS, the Region Aquitaine, and the Alexander von Humboldt Foundation (V.M.). Supporting Information Available: Crystallographic details in CIF format, experimental details, and magnetic data. This material is available free of charge via the Internet at http://pubs.acs.org.

Figure 3. Magnetization (M) versus applied dc field (µoH) for 2.

arrangement within the aggregate core (Figure S1). In addition to the bell-shaped core topology, 2 is the first mixed-valence MnII,IIILnIII d/f complex and only the second synthesized Mn-Ln cluster with as many as eleven Mn centers.8 The dc magnetic susceptibility of 2 measured at 1000 Oe in the 1.8-300 K temperature range, reveals a room temperature χT value per complex of 46.9 cm3 K/mol. On lowering the temperature, χT first continuously decreases reaching 35.2 cm3 K/mol at 37 K and then increases to a maximum value at 1.81 K of 74.5 cm3 K/mol. The fact that the χT product starts to saturate at 1.81 K suggests that below this temperature a well-defined high-spin ground state is almost exclusively thermally populated (Figure S2). The fit of the experimental data to a Curie Weiss law above 30 K (Figure S3) leads to a Curie constant of 50.8 cm3 K/mol and a Weiss constant of -28.1 K indicating dominant antiferromagnetic interactions between spin carriers. The Curie constant is close to the expected value for nine MnIII (S ) 2), two MnII (S ) 5/2) and two GdIII (S ) 7/2) noninteracting ions (51.5 cm3 K/mol). The ac susceptibility measurements taken over the frequency range 1-1500 Hz and at temperatures of 1.8-3 K display frequency-dependent out-of-phase signals (Figure 2) suggesting that the complex exhibits slow relaxation of its magnetization and potential SMM behavior. To investigate this further, single-crystal magnetization measurements were performed using an array of micro-SQUIDs at temperatures down to 40 mK.16 Hysteresis loops collected for complex 2 at varying temperatures and sweep rates (Figure 3) show a superparamagnet-like increasing coercivity with decreasing temperature confirming 2 to be a SMM. No steps due to quantum tunneling of magnetization (QTM) were observed, probably as a result of ligand and lattice solvent disorder, as there are no obvious pathways for intermolecular interactions. The dc magnetization decay data were collected in the 0.04-1.0 K range: at each temperature, the magnetization was saturated with a dc field,

References (1) (a) Sessoli, R.; Tsai, H.-L.; Schake, A. R.; Wang, S.; Vincent, J. B.; Folting, K.; Gatteschi, D.; Christou, G.; Hendrickson, D. N. J. Am. Chem. Soc. 1993, 115, 1804. (b) Sessoli, R.; Gatteschi, D.; Caneschi, A.; Novak, M. A. Nature 1993, 365, 141. (2) (a) Price, J. P.; Batten, S. R.; Moubaraki, B.; Murray, K. S. Chem. Commun. 2002, 762. (b) Sanudo, E. C.; Wernsdorfer, W.; Abboud, K. A.; Christou, G. Inorg. Chem. 2004, 43, 4137. (c) Coronado, E.; FormentAliaga, A.; Gaita-Arino, A.; Gimenez-Saiz, C.; Romero, F. M.; Wernsdorfer, W. Angew. Chem., Int. Ed. 2004, 45, 6152. (d) Maheswaran, S.; Chastanet, G.; Teat, S. J.; Mallah, T.; Sessoli, R.; Wernsdorfer. W.; Winpenny, R. E. P. Angew. Chem. 2005, 117, 5172. (3) Delfs, C.; Gatteschi, D.; Pardi, L.; Sessoli, R.; Wieghardt, K.; Hanke, D. Inorg. Chem. 1993, 32, 3099. (4) Cadiou, C.; Murrie, M.; Paulsen, C.; Villar, V.; Wernsdorfer, W.; Winpenny, R. E. P. Chem. Commun. 2001, 2666. (5) (a) Yang, E.-C.; Hendrickson, D. N.; Wernsdorfer, W.; Nakano, M.; Zakharov, L. N.; Sommer, R. D.; Rheingold, A. L.; Ledezma-Gairaud, M.; Christou, G. J. Appl. Phys. 2002, 91, 7382. (b) Murrie, M.; Teat, S. J.; Stoeckli-Evans, H.; Gudel, H. U. Angew. Chem. 2003, 115, 4801; Angew. Chem., Int. Ed. 2003, 42, 4653. (6) Osa, S.; Kido, T.; Matsumoto, N.; Re, N.; Pochaba, A.; Mrozinski, J. J. Am. Chem. Soc. 2004, 126, 420. (7) Zaleski, C.; Depperman, E.; Kampf, J.; Kirk, M.; Pecoraro, V. Angew. Chem., Int. Ed. 2004, 43, 3912. (8) Mishra, A.; Wernsdorfer, W.; Abboud, K.; Christou, G. J. Am. Chem. Soc. 2004, 126, 15648. (9) Mishra, A.; Wernsdorfer, W.; Parson, S.; Christou, G.; Brechin, E. Chem. Commun. 2005, 2086. (10) Murugesu, M.; Mishra, A.; Wernsdorfer, W.; Abboud, K.; Christou, G. Polyhedron 2006, 26, 613. (11) Tang, J.; Hewitt, I.; Madhu, N. T.; Chastanet, G.; Wernsdorfer, W.; Anson, C. E.; Benelli, C.; Sessoli, R.; Powell, A. K. Angew. Chem. 2006, 118, 1761. (12) See Supporting Information. (13) Anal. Found (calcd for 2‚CH3CN‚H2O): C, 34.39 (34.12); H, 4.21 (4.00); N, 1.19 (1.37). (14) Crystal data for 2‚13CH3CN‚H2O: C111H157.6Gd2 Mn11N2O58.4, 3555.36 g mol-1, triclinic, P1h, a ) 15.8893(10) Å, b ) 17.5285(11) Å, c ) 27.2474(17) Å, R ) 86.985(1), β ) 78.083(1), γ ) 72.737(1)°, Z ) 2, V ) 7090.5(8) Å3, T ) 100 K, Fcalcd ) 1.665 g cm-3, F(000) ) 3598, µ(Mo KR) ) 1.957 mm-1; 2θmax ) 52.7°, 33399 data, 28136 unique (Rint ) 0.0246), 1408 parameters, final wR2 ) 0.0907, S ) 0.992 (all data), R1 (18636 data with I > 2σ(I)) ) 0.0409. See Supporting Information for refinement details; CCDC 637050. (15) Liu, W.; Thorp, H. H. Inorg. Chem., 1993, 32, 4102. Calculated values: Mn(1)-Mn(9) 2.82-2.94, Mn(10) 2.01, Mn(11) 1.91; O(1) and O(4)O(10) 1.85-1.96, O(2) 1.18, O(3) 1.28. (16) Wernsdorfer, W. AdV. Chem. Phys. 2001, 118, 99.

JA071073M

J. AM. CHEM. SOC.

9

VOL. 129, NO. 30, 2007 9249