A Full-Visible-Spectrum Invisibility Cloak for Mesoscopic Metal Wires

high-speed defroster for automotive windshields. Keywords: ..... broadband invisibility over the full visible spectrum, blue- (λ = 450 nm), green- (Î...
0 downloads 3 Views 2MB Size
Subscriber access provided by Kaohsiung Medical University

Communication

A Full-Visible-Spectrum Invisibility Cloak for Mesoscopic Metal Wires Sang-Woo Kim, Byeong Wan An, Eunjin Cho, Byung Gwan Hyun, Yoon-Jong Moon, Sun-Kyung Kim, and Jang-Ung Park Nano Lett., Just Accepted Manuscript • DOI: 10.1021/acs.nanolett.8b01157 • Publication Date (Web): 16 May 2018 Downloaded from http://pubs.acs.org on May 16, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

A Full-Visible-Spectrum Invisibility Cloak for Mesoscopic Metal Wires Sang-Woo Kim1†, Byeong Wan An2†, Eunjin Cho2, Byung Gwan Hyun2, Yoon-Jong Moon1, Sun-Kyung Kim1*, and Jang-Ung Park2* 1

Department of Applied Physics, Kyung Hee University, Gyeonggi-do 17104, Republic of

Korea, 2School of Materials Science and Engineering, Ulsan National Institute of Science and Technology (UNIST), Ulsan Metropolitan City 44919, Republic of Korea

*

email: J.-U.P ([email protected]) and S.K.K. ([email protected])



These authors contributed equally to this work.

Abstract: Structured metals can sustain a very large scattering cross-section that is induced by localized surface plasmons, which often has an adverse effect on their use as transparent electrodes in displays, touch screens, and smart windows due to an issue of low clarity. Here, we report a broadband optical cloaking strategy for the network of mesoscopic metal wires with submicrometer to micrometer diameters, which is exploited for manufacturing and application of high-clarity metal-wires-based transparent electrodes. We prepare electrospun Ag wires with 300 – 1800 nm in diameter and perform a facile surface oxidation process to form Ag/Ag2O core/shell heterogeneous structures. The absorptive Ag2O shell, together with the coating of a dielectric cover, leads to the cancellation of electric multipole moments in Ag 1

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 21

wires, thereby drastically suppressing plasmon-mediated scattering over the full visible spectrum and rendering Ag wires to be invisible. Simultaneously with the effect of invisibility, the transmittance of Ag/Ag2O wires is significantly improved compared to bare Ag wires, despite the formation of an absorptive Ag2O shell. As an application example, we demonstrate that these invisible Ag wires serve as a high-clarity, high-transmittance, and high-speed defroster for automotive windshields. Keywords: invisibility cloak / scattering suppression / multipole cancelation / Ag fibers / transparent electrodes

The negative permittivity (ε) of metals at optical frequencies enables them to function as a broadband high-reflectivity mirror.1 More interestingly, structuring metals at the nanometer to micrometer scale can induce localized surface plasmon resonances at specific wavelengths, which convert the energy of free propagating radiation into the energy of subwavelengthvolume electromagnetic modes, and vice versa; both phenomena are referred to as plasmonic scattering.2 The concept of plasmonic scattering has been utilized to improve the performance of a diverse range of photonic devices including optical sensors, lithography systems, solar cells, and light-emitting diodes.3–6 However, plasmon-mediated scattering often causes an unwanted situation, particularly for imaging applications such as displays, touch screens, and smart windows that use metal wires as a transparent electrode; metal wires can be vividly observed by the naked eye, thereby lowering the clarity of visibility,7 as illustrated in Figure 1a. The electric-field profiles show that a bare metal wire significantly disturbs the phase of an incoming plane wave, whereas a cloaked metal wire marginally interacts with an incoming plane wave. Such degraded clarity has impeded the extensive use of metal wires that are 2

ACS Paragon Plus Environment

Page 3 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

made of periodic grids, nanowires (NWs),8–13 nanofibers (NFs),14,15 or nanotroughs (NTs)16–19 of metals as transparent electrodes, despite a high figure of merit (i.e., a ratio of transmittance to sheet resistance). Therefore, there is a need for the development of an economically viable strategy for concealing such two-dimensional metal networks over the full visible spectrum while simultaneously retaining their high transmittance and low sheet resistance. To date, optical cloaks prepared from rationally designed metamaterials and metasurfaces have attracted significant attention for various industrial and military purposes.20–29 For example, the Zhang group demonstrated a metasurface film using phase delaying Au nanobars that cover up the information on the curvature of an arbitrarily shaped surface.20 The Kocabas group demonstrated a graphene-based tunable absorber operating at microwave frequencies to avoid radar detection.21 The Brongersma group demonstrated a 50nm-diameter Si-NW-based photodetector featuring reduced scattering by coating a thin (< 20 nm) conformal Au shell.22 These demonstrations are based on the manipulation of the propagation wave vector, absorption, or scattering of incoming light. Although the optical cloaks that have been developed thus far have successfully opened up a new paradigm of nanomaterial-enabled photonics, they have limitations such as operation at a limited range of wavelengths and specific polarization. A few studies on broadband optical cloaks based on the principle of transformation optics have been reported;23–26 however, for the implementation of transformation optics, a macroscopic and sophisticated optical design is required, which would not be appropriate for practical devices. Furthermore, for implementation in optoelectronic devices, there is a lingering issue of whether cloaking structures can preserve device performance; the aforementioned invisible Si-NW photodetector would sacrifice the absorption efficiency owing to the presence of a thin Au shell as a cloaking structure.22 In this study, we report a facile cloaking strategy that conceals 3

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

mesoscopic (i.e., subwavelength to wavelength scale) metal wires over the full visible spectrum for two orthogonal polarizations. It was believed that such giant metal structures cannot be readily cloaked because of their large electric multipole moments.28,29 Metal wires on the invisibility cloak serve as an ultrahigh figure-of-merit transparent electrode, simultaneously maintaining the level of clarity as good as a pristine glass substrate. Furthermore, we highlight that the invisibility cloak studied herein is generalized for a wide range of sizes (a few hundred nanometers to a few micrometers) and different shapes (solid NFs and hollow NTs) in metal wires. As an application example, we demonstrate a highclarity, transparent, and ultrafast defroster for automotive windshields by using the network of invisible metal wires. To prepare the mesoscopic metal wires used for our invisibility cloak experiments, continuous networks of ultralong Ag NFs were directly electrospun on a glass substrate by using a suspension of Ag nanoparticles as an ink (Figure 1b). A subsequent thermal annealing process at 150 °C for 30 mins in air coalesced the Ag nanoparticles, thereby transforming them into electrically conductive Ag NFs. These electrospun Ag NFs were adequate for these experiments because they were uniformly dispersed on a substrate without bunching or stacking. In addition, the diameter of the Ag NFs was readily tunable by adjusting the flow rate of the Ag nanoparticle ink. We successfully obtained Ag NFs with diameters (D) ranging between 300 and 1800 nm (Supporting Information Figure S1). This direct electrospinning method allows relatively rapid production of large-area (potentially larger than 1 m2) metalwire based transparent electrodes. Fabricated ultralong Ag NFs minimize the number of interconnections between NFs, leading to a decrease of the sheet resistance despite small Ag area fractions; this geometrical factor also promises high transmittance. Although Ag NFs serve as a high figure-of-merit transparent electrode, which outperforms conductive oxide 4

ACS Paragon Plus Environment

Page 4 of 21

Page 5 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

films, conducting polymers, graphene, metal grids, and even random networks of Ag NWs,14 the large amount of scattering induced by individual NFs degrades the clarity of visibility through a substrate, as shown in the left images of Figure 1c. To enhance the clarity of randomly networked Ag NFs through a glass substrate, we propose Ag/oxide core/shell NFs that were covered with an optically thick (~7 µm) indexmatching layer (IML) composed of SiO2 and binding polymers, as shown in Figure 1b. The surface of the Ag core was gently oxidized under an ultraviolet-ozone (UVO) illumination to generate a Ag2O shell, as evident from the scanning electron microscopy (SEM) images in Figure 1b and X-ray photoelectron spectroscopy (XPS) spectra in Supporting Information Figures S2a and S2b. It is well known that a Ag2O material has a large extinction coefficient (k) over the full visible spectrum, as previously reported in ref. 30 (Supporting Information Figure S2c). In general, a dielectric shell coating on metal or semiconductor nanostructures can be leveraged to amplify their optical antenna effect (i.e., scattering cross section).31 Alternatively, metal/dielectric (or dielectric/metal) core/shell nanostructures can sustain reduced scattering cross section owing to their ε’s with opposite signs (ε < 0 for metal and ε > 0 for dielectric).22,28,29 Particularly for mesoscopic objects beyond the quasistatic approximation, which is indeed our case, the design rules established by previous theoretical studies indicate that a low-ε dielectric shell and a high-ε background medium are desirable to eliminate high-order scattering coefficients.28, 29 These conditions are met well with the use of a highly absorptive Ag2O shell and a dielectric (n = 1.5) IML. The surfaces of as-grown Ag NFs and the following AgO2 shell are fairly rough; therefore, an IML can additionally reduce rough surface scattering. The thickness (t) of a Ag2O shell can be precisely controlled by the duration of the UVO illumination, and the formation of a Ag2O shell reduces the diameter of the Ag core at the 5

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

same time (Supporting Information Figure S3). Notably, a thin void layer is observed after the oxidation, separating the core (Ag) and shell (Ag2O) (Figure 1b) because the diffusion velocity of the oxygen atoms from the shell is relatively slower than that of the Ag atoms from the core, which is known as the Kirkendall effect.32 Randomly networked Ag/Ag2O NFs with (D, t) = (300, 150) nm, covered with an IML, displayed dramatically enhanced clarity through a glass substrate in typical room light and even focused high-intensity light with 251 mW/cm2 (right images in Figure 1c, Supporting Information Figure S4, and Supporting Information Movie S1). The level of clarity progressively improved with each fabrication step, indicating that both the oxidation and coating processes were important for rendering the Ag NFs to be near invisible to the naked eye. Remarkably, a thin void layer in the oxidized Ag NFs only had a marginal effect on the level of clarity through a glass substrate, which was supported by electromagnetic simulations, as shown in Supporting Information Figure S5. To probe whether the cloaked Ag/Ag2O NFs preserved their pristine performance as a transparent electrode, we obtained the transmittance (T), sheet resistance (Rs), and haze for three types of samples (bare Ag NFs, Ag/Ag2O NFs, and Ag/Ag2O NFs/IML) for a wide range (300 – 1800 nm) of initial Ag NF diameters (D), as shown in Figures 1d and Supporting Information Figure S6. For all of the samples, the area fractions of the Ag NFs were initially the same at each Ag NF diameter. The oxidized samples had a 150-nm-thick Ag2O shell. The results showed that the bare Ag NFs exhibited a high figure of merit over the entire range of Ag NF diameters, characterized by T > 92% and Rs < 8.6 Ω/sq. More importantly, the cloaked samples (i.e., Ag/Ag2O NFs/IML) had greater transmittance and lower haze than the bare Ag NFs, despite the addition of an absorptive Ag2O shell. The improved transmittance was partly attributed to the shrinkage of the Ag core. However, the 6

ACS Paragon Plus Environment

Page 6 of 21

Page 7 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

comparison of the transmittance data from the Ag/Ag2O NFs before and after the IML indicated that the improvement in transmittance was mostly owing to the invisibility phenomenon by which the optical loss within the Ag2O shell was fully compensated. Although the Ag2O shell slightly increased Rs owing to its relatively low carrier density, the cloaked samples still had a high figure of merit as a transparent electrode; T = 99 % and Rs = 4.8 ± 1.1 Ω/sq were recorded at a Ag NF diameter of 750 nm. The same trend was observed for randomly networked Ag/Ag2O NTs covered with an IML, as shown in Supporting Information Figures S7 and S8, which had higher clarity and improved transmittance compared to bare NTs. These results suggested that the cloaking effect could conceal any forms of mesoscopic metallic wires by introducing an absorptive conformal shell and a dielectric cover. To delineate the principle of the observed invisibility, we obtained optical images of the three types of samples by dark-field microscopy with a 100× magnification lens (Figure 2a); the diameters of the Ag NFs were 750 (left group) and 1800 nm (right group). For the oxidized samples, the thickness of the AgO2 shell was 150 nm. Based on the microscopy images, both the sub-micrometer- and micrometer-scale Ag NFs gradually dimmed as each fabrication step (i.e., oxidation and coating) proceeded, consistent with the camera images in Figure 1c and Supporting Information Figure S4. At the final step, the Ag-based NFs were near invisible in the dark-field microscopy images, which was indicative of suppressed backward scattering. The level of backward scattering was accurately evaluated by scattering distribution measurements, for which a photodetector was programmed to move along the polar (ө) and azimuthal (ϕ) directions, as shown in Figure 2b.33 For the examination of the broadband invisibility over the full visible spectrum, blue- (λ = 450 nm), green- (λ = 532 nm), red-emitting (λ = 660 nm) lasers were individually used as an incoming light source. The 7

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

polarization of the incoming light on such random network configuration is irrelevant. The measured backward scattering distributions revealed two key features related to the invisibility (Figures 2c–2e and Supporting Information Figure S9). First, for a fixed Ag NF diameter and light wavelength, the scattering distribution becomes significantly localized after each fabrication step; the final cloaked samples behaved as a specular surface that was characterized by a point-like scattering distribution. Second, such broadband invisibility was observed for all the considered diameters (300, 750, and 1800 nm), although the level of scattering was slightly augmented with increasing Ag NF diameter. The scattering cross section of a metal wire tends to increase with increasing its diameter because a larger metal wire excites more numbers of electric multipoles. Therefore, the level of scattering suppression is slightly reduced for relatively large Ag NFs (e.g., D = 750 and 1800 nm). Taken together, our cloaking strategy, which concealed mesoscopic metallic wires via the suppression of scattering, was reliable for a broad range of wire diameters and light wavelengths. As discussed in Figure 1b, the formation of an Ag2O shell was accompanied by the reduction of the diameter of the Ag core. To rationalize that the invisibility observed herein occurs marginally by the reduced Ag core and dominantly by the presence of the thin Ag2O shell, we prepared a series of micrometer-scale (D = 1800 nm) Ag NFs samples with a gradual variation of the Ag2O shell thicknesses (t = 0 – 150 nm), as shown in Supporting Information Figure S10. Such giant Ag NFs can be relatively free from the argument related to the shrinkage of a Ag core. The results showed that the scattering distributions became significantly localized after oxidation for 5 min only for the Ag/Ag2O NFs/IML samples, as shown in Supporting Information Figure S11. The transmission electron microscopy (TEM) images (Supporting Information Figure S10a) revealed that a very thin (approximately 20 8

ACS Paragon Plus Environment

Page 8 of 21

Page 9 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

nm) Ag2O shell abruptly formed after an oxidation time of 5 min. This observation confirmed that the presence of a Ag2O shell dominated the invisibility, in conjunction with the IML coating. Furthermore, the cloaked Ag NF samples dramatically suppressed the forward scattering as much as the backward scattering, as shown in Supporting Information Figure S12, which suggests their generic use for both external and internal illuminations. To support the experimental findings discussed thus far, we conducted numerical scattering analyses using finite-difference time-domain (FDTD) simulations. In the simulation model, a single hemispherical Ag NF with a conformal Ag2O shell was placed on a glass substrate, embedded within a background medium of air (n = 1.0) or a dielectric layer (n = 1.5), as shown in Figure 3a. To clearly verify the effect of the Ag2O shell, the diameter of the Ag core was not changed by the introduction of an Ag2O shell. Typical snapshots of the electric-field intensity for a Ag NF, a Ag/AgO2 NF, and a Ag/AgO2 NF/IML show that the scattering was significantly suppressed by both oxidation and coating steps, as shown in Figure 3b. For a more quantitative investigation, we obtained the scattering cross sections of the three structures with a variation of the Ag NF diameters (D = 260 – 1800 nm), for a normally incident broadband (λ = 400 – 700 nm) plane wave with transverse-electric (TE) or transverse-magnetic (TM) polarization (Figure 3c for TE data and Supporting Information Figure S13a for TM data). These surface plots represent a size-independent scattering suppression that was preserved over the full visible spectrum for both TE and TM polarizations, which was consistent with the measured scattering distributions shown in Figures 2c – 2e and Supporting Information Figure S9. Bare Ag NFs sustained discrete highamplitude bands that were identified as localized surface plasmon resonances; however, the Ag/Ag2O NF, covered with a dielectric layer, significantly mitigated the plasmon-mediated scattering. 9

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 21

In addition to the studies of cloaked Ag NFs with a wide range of sizes, we investigated the effect of the Ag2O shell thickness. Figure 3d and Supporting Information Figure S13b show the electric-field intensity snapshots of the 800-nm-diameter Ag NFs with different Ag2O shell thicknesses (0, 20, and 100 nm) for TE and TM polarizations, respectively. The simulated profiles indicated that the scattering was drastically suppressed by the addition of an ultrathin Ag2O (20 nm) shell; a thicker Ag2O shell slightly boosted the suppression of scattering. A surface plot of the scattering efficiencies with the variation of the Ag2O shell thicknesses and wavelengths revealed a cut-off Ag2O shell thickness (approximately 20 nm in this simulation) at which the scattering behavior was dramatically altered (Figure 3e for TE data and Supporting Information Figure S13c for TM data). This simulated result accounted for the measured scattering distributions with a fine increment in the Ag2O shell thickness shown in Supporting Information Figure S11. As a final analysis, we obtained the scattering efficiencies of the Ag NFs with a strongly absorptive (k = 0.5), weakly absorptive (k = 0.1), or transparent (k = 0) dielectric shell to verify the effectiveness of an absorptive Ag2O shell, as shown in Figure S14. A comparison of these surface plots indicated that the plasmonic scattering induced by a Ag NF vanished only when the dielectric shell was absorptive. Interestingly, the cloaked Ag NFs with an absorptive Ag2O shell samples have a significantly higher transmittance than their counterpart bare Ag NFs samples (Figure 1c). In general, scattering and absorption processes are strongly correlated and thus, a cloaked structure can reduce an absorption cross section as much as a scattering one.31 While the diameter of Ag NFs increases, the level of scattering suppression becomes reduced, as shown in Figures 2c– 2e, because larger Ag NFs are capable of sustaining more numbers of high-order electric multipoles. This accounts for the more improved transmittance for relatively small Ag NFs (e.g., D = 300 nm), as shown in Figure 1d. 10

ACS Paragon Plus Environment

Page 11 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

As an application example, we developed a defroster (namely, a heater) using random networks of cloaked Ag NFs, functioning as a transparent electrode for Joule heating. For a thermal test, a sample of cloaked Ag NFs (D = 750 nm) characterized by Rs of 4.8 ± 1.1 Ω/sq and T of 99% was prepared. Both ends of this sample were connected to a voltage supplier by using a silver epoxy paste (Figures 4a, 4b, and Supporting Information Figure S15). The fabricated sample exhibited a uniform temperature distribution at a constant DC bias, as evident from an infrared (IR) image shown in Figure 4c. Figure 4d shows the change of temperature with increasing DC bias; the input DC bias was elevated to 6 V with a step increase of 1 V every 30 sec, which finally yielded an average temperature of 248.2 ± 0.8 °C. A heating cycle test was conducted by repeatedly applying a DC bias (6 V) to the same sample, as shown in Supporting Information Figure S16; no significant degradation in thermal performance was observed throughout this test. To highlight the effectiveness of the Ag NFs developed in this study as transparent electrodes, we prepared two samples containing Ag NWs (Rs = 15 Ω/sq) or an ITO film (Rs = 60 Ω/sq), and conducted a thermal test for all these samples at a DC bias of 2V, as shown in Figure 4e. For comparison, the transmittance of these three samples was adjusted to the same value (94% in this experiment). To obtain this identical T value, random networks of Ag/Ag2O NFs (average diameter: 1139 nm) with Rs of 1.9 ± 0.5 Ω/sq and T of 94% at 550 nm were used. A dramatic increase in the thermal equilibrium temperature was observed for the Ag NFs, in contrast to that of the Ag NWs and ITO film, which stemmed from their different Rs’s. Figure 4f and Supporting Information Figure S17 represent the heating and cooling rates of these three samples for which different DC biases (2V for the cloaked Ag NFs, 5.5 V for the Ag NWs, and 11 V for the ITO film) were applied to reach the same thermal equilibrium 11

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 21

temperature of 120 °C. The cloaked Ag NFs sample had faster heating and cooling rates than the other samples, as shown in Figure 4f, because the Ag NFs had greater thermal conductivity that results from their higher electrical conductivity by the Wiedemann-Franz law. In addition, we conducted a heat spreading test for the same samples; one end of these samples was connected to a hot plate with a constant temperature of 140 °C, while the opposite end was placed on a cooling pad with a constant temperature of 23 °C, as schematically shown in Supporting Information Figure S18a. The Ag NFs sample featured relatively fast heat spreading, as shown in Supporting Information Figures S18b and S18c. These great thermal and optical capabilities of cloaked Ag NFs can be appropriately harnessed for the manufacturing of a defroster that requires high clarity, high transmittance, and high defogging speed. A defroster fabricated from cloaked Ag NFs (Rs = 4.8 ± 1.1 Ω/sq and T = 99%) exhibited a linear relation between defogging time and an applied DC bias, as shown in Figure 4g; defogging time was less than 1 sec at a DC bias of 6 V. Such rapid defogging is desirable for automotive windshields that require a clear view while driving. To do this, we fabricated a windshield using the cloaked Ag NFs for an automobile model and conducted a defogging test, as shown in Figure 4h. Intentionally formed frost covering the entire surface of the windshield was completely evaporated within 1 sec at a DC bias of 6 V (Supporting Information Movie S2). The broadband invisibility cloak discussed herein is not limited to Ag wires but can be generalized to mesoscopic particles and flakes of any metal, including Cu as a cost-effective electrode material. The effect of the scattering suppression can be further enhanced by tailored design of the shell and cover layer (e.g., appropriately designed double shells combined with a high-refractive-index cover layer). These experimental and theoretical 12

ACS Paragon Plus Environment

Page 13 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

results will be utilized for the development of various imaging applications that require a high-clarity view and use metal structures. ASSOCIATED CONTENT Supporting Information Detailed description of experimental and numerical methods and additional figures. This material is available free of charge via the Internet at http://pubs.acs.org. AUTHOR INFORMATION Corresponding Authors *E-mail: [email protected] (J.-U.P); [email protected] (S.-K.K.) Notes The authors declare no competing financial interests. ACKNOWLEDGMENTS J.-U.P. was supported by the Ministry of Science & ICT and the Ministry of Trade, Industry and

Energy

(MOTIE)

of

Korea

through

the

National

(2016R1A2B3013592 and 2016R1A5A1009926),

the

Nano

Research

Foundation

Material

Technology

Development Program (2015M3A7B4050308 and 2016M3A7B4910635), the Convergence Technology Development Program for Bionic Arm (NRF-2017M3C1B2085316), the Industrial Technology Innovation Program (10080577), and the Pioneer Research Center Program (NRF-2014M3C1A3001208). S.-K.K. was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF-2017R1A2B4005480) funded by the Ministry of Science, ICT, and Future Planning.

13

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 21

REFERENCES (1) Johnson, P. B. & Christy, R.-W. Phys. Rev. B 1972, 6, 4370 – 4379. (2) Novotny, L.; Van Hulst, N. Nat. Photon. 2011, 5, 83–90. (3) Atwater, H. A.; Polman, A. Nat, Mater, 2010, 9, 205–213. (4) Kim, N. Y.; Hong, S. H.; Kang, J. W.; Myoung, N.; Yim, S. Y.; Jung, S.; Lee, K.; Tu, C. W.; Park, S. J. RSC Adv. 2015, 5, 19624–19629. (5) Park, K. D.; Jiang, T.; Clark, G.; Xu, X. D.; Raschke, M. B. Nat. Nanotechnol. 2017, 13, 59–64. (6) Pan, L.; Park, Y.; Xiong, Y.; Ulin-Avila, E.; Wang, Y.; Zeng, L.; Xiong, S. M.; Rho, J.; Sun, C.; Bogy, D. B.; Zhang, X. Sci. Rep. 2011, 1. (7) Fang, Y. S.; Wu, Z. C.; Li, J.; Jiang, F. Y.; Zhang, K.; Zhang, Y. L.; Zhou, Y. H.; Zhou, J.; Hu, B. Adv. Funct. Mater. 2018, 28, 1705409. (8) Lee, M. S.; Lee, K.; Kim, S. Y.; Lee, H.; Park, J.; Choi, K. H.; Kim, H. K.; Kim, D. G.; Lee, D. Y.; Nam, S.; Park, J. U. Nano Lett. 2013, 13, 2814–2821. (9) Kim, J.; Kim, M.; Lee, M. S.; Kim, K.; Ji, S.; Kim, Y. T.; Park, J.; Na, K.; Bae, K. H.; Kim, H. K.; Bien, F.; Lee, C. Y.; Park, J. U. Nat. Commun. 2017, 8. (10) Kim, J.; Lee, M. S.; Jeon, S.; Kim, M.; Kim, S.; Kim, K.; Bien, F.; Hong, S. Y.; Park, J. U. Adv. Mater. 2015, 27, 3292–3297. (11) Yu, G. H.; Cao, A. Y.; Lieber, C. M. Nat. Nanotechnol. 2007, 2, 372–377. (12) Wu, Y.; Xiang, J.; Yang, C.; Lu, W.; Lieber, C. M. Nature 2004, 430, 61–65. (13) Park, J.; Kim, J.; Kim, S. Y.; Cheong, W. H.; Jang, J.; Park, Y. G.; Na, K.; Kim, Y. T.; Heo, J. H.; Lee, C. Y.; Lee, J. H.; Bien, F.; Park, J. U. Sci. Adv. 2018, 4, eaap9841. (14) Jang, J.; Hyun, B. G.; Ji, S.; Cho, E.; An, B. W.; Cheong, W. H.; Park, J. U. NPG Asia Mater. 2017, 9, e432. 14

ACS Paragon Plus Environment

Page 15 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

(15) Wu, H.; Hu, L. B.; Rowell, M. W.; Kong, D. S.; Cha, J. J.; McDonough, J. R.; Zhu, J.; Yang, Y. A.; McGehee, M. D.; Cui, Y. Nano Lett. 2010, 10, 4242–4248. (16) An, B. W.; Gwak, E. J.; Kim, K.; Kim, Y. C.; Jang, J.; Kim, J. Y.; Park, J. U. Nano Lett. 2015, 16 , 471–478. (17) An, B. W.; Hyun, B. G.; Kim, S. Y.; Kim, M.; Lee, M. S.; Lee, K.; Koo, J. B.; Chu, H. Y.; Bae, B. S.; Park, J. U. Nano Lett. 2014, 14, 6322–6328. (18) Im, H. G.; An, B. W.; Jin, J.; Jang, J.; Park, Y. G.; Park, J. U.; Bae, B. S. Nanoscale 2016, 8, 3916–3922. (19) Wu, H.; Kong, D. S.; Ruan, Z. C.; Hsu, P. C.; Wang, S.; Yu, Z. F.; Carney, T. J.; Hu, L. B.; Fan, S. H.; Cui, Y. Nat. Nanotechnol. 2013, 8, 421–425. (20) Ni, X. J.; Wong, Z. J.; Mrejen, M.; Wang, Y.; Zhang, X. Science 2015, 349, 1310–1314. (21) Balci, O.; Polat, E. O.; Kakenov, N.; Kocabas, C. Nat. Commun. 2015, 6, 6628. (22) Fan, P. Y.; Chettiar, U. K.; Cao, L. Y.; Afshinmanesh, F.; Engheta, N.; Brongersma, M. L. Nat. Photon. 2012, 6, 380–385. (23) Chen, X. Z.; Luo, Y.; Zhang, J. J.; Jiang, K.; Pendry, J. B.; Zhang, S. A. Nat. Commun. 2011, 2, 176. (24) Gabrielli, L. H.; Cardenas, J.; Poitras, C. B.; Lipson, M. Nat. Photon. 2009, 3, 461–463. (25) Valentine, J.; Li, J. S.; Zentgraf, T.; Bartal, G.; Zhang, X. Nat. Mater. 2009, 8, 568–571. (26) Liu, R.; Ji, C.; Mock, J. J.; Chin, J. Y.; Cui, T. J.; Smith, D. R. Science 2009, 323, 366– 369. (27) Kim, K. H.; No, Y. S.; Chang, S.; Choi, J. H.; Park, H. G. Sci. Rep. 2015, 5, 16027. (28) Alu, A.; Engheta, N. Phys. Rev. E 2005, 72, 016623. (29) Alu, A.; Engheta, N. Phys. Rev. Lett. 2008, 100, 113901.

15

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 21

(30) Gao, X. Y.; Wang, S. Y.; Li, J.; Zheng, Y. X.; Zhang, R. J.; Zhou, P.; Yang, Y. M.; Chen, L. Y. Thin Solid Films 2004, 455, 438–442. (31) Kim, S. K.; Zhang, X.; Hill, D. J.; Song, K. D.; Park, J. S.; Park, H. G.; Cahoon, J. F. Nano Lett. 2015, 15, 753–758. (32) Yu, L.; Yan, Z. Y.; Cai, Z. H.; Zhang, D. T.; Han, P.; Cheng, X. M.; Sun, Y. G. Nano Lett. 2016, 16, 6555–6559. (33) Moon, Y.-J.; Na, J.-Y.; Park, Y. H.; Kim, S. B.; Lee, S. W.; Kim, S.-K. ACS Photon. 2018, DOI: 10.1021/acsphotonics.7b01364.

16

ACS Paragon Plus Environment

Page 17 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Figure 1. Fabrication and optoelectronic characterization of Ag-NFs-based electrodes. (a) Schematics of the network of metal wires with low (left) or high (right) clarity. Typical profiles of the electric field of a bare Ag NF (left) and a cloaked Ag/Ag2O NF (right) are shown together. (b) Schematic illustration of the formation of Ag2O shells by exposure to UVO and the coating of an IML layer. SEM cross-sectional images of these samples. Scale bars, 500 nm. (c) Photographs of samples with random networks of bare Ag NFs, Ag/Ag2O NFs, and Ag/Ag2O NFs/IML on a glass substrate in typical room light (upper images) and focused high-intensity light with 251 mW/cm2 (lower images). The structural parameters of (D, t) are (300, 150) nm. Scale bars, 2 cm. (d) Measured transmittance (λ = 550 nm) and sheet resistance of bare Ag NFs, Ag/Ag2O NFs, and Ag/Ag2O NFs/IML electrodes as a function of D. The oxidized samples have the same t value of 150 nm. 17

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 21

Figure 2. Wavelength-resolved scattering distribution of cloaked Ag NFs. (a) Dark-field microscopic images of bare Ag NFs, Ag/Ag2O NFs, and Ag/Ag2O NFs/IML with D’s of 1800 (left groups) and 750 nm (right groups). Scale bars, 10 µm. (b) Schematic of the measurement setup for the backward scattering distribution. (c–e) Measured backward scattering distributions of bare Ag NFs, Ag/Ag2O NFs, and Ag/Ag2O NFs/IML with D = 300 (c), 750 (d), 1800 nm (e), acquired at λ = 450, 532, and 660 nm. The incident angle was set to 60º to the specimen. The two white dashed lines indicate the angular boundaries of ±40º. The oxidized samples have the same t value of 150 nm.

18

ACS Paragon Plus Environment

Page 19 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Figure 3. Electromagnetic analysis of the optical cloaking effects. (a) Schematic of a Ag/Ag2O NF on a glass substrate for simulation. The orthogonal polarizations of TE and TM were defined as shown in the schematic. (b) Profiles of the electric-field intensity of a bare Ag NF, a Ag/Ag2O NF, and a Ag/Ag2O NF/IML, acquired at λ = 530 nm for TE polarized light. The structural parameters of (D, t) are (800, 160) nm. (c) Surface plots presenting the wavelength-dependent scattering efficiencies of a bare Ag NF, a Ag/Ag2O NF, and a Ag/Ag2O NF/IML with the variation of the D’s for TE polarized light. (d) Profiles of the electric-field intensity of the structures with a Ag/Ag2O NF/IML (D = 800 nm) with a different t of 0, 20, or 100 nm, acquired at λ = 530 nm for TE polarized light. (e) Surface plots presenting the wavelength-dependent scattering efficiencies of Ag/Ag2O NFs/IML (D = 800 nm) with a variation of the t’s for TE polarized light.

19

ACS Paragon Plus Environment

Nano Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 21

Figure 4. Thermal characteristics of cloaked Ag NFs and demonstration of a defroster for automobile windshields. (a) Schematic illustration of a thermal test experiment using Ag NFs. (b) Photograph of the fabricated Ag/Ag2O NFs/IML heater. Scale bar, 2 cm. (c) The temperature distribution of the fabricated Ag/Ag2O NFs/IML heater at a DC bias of 6 V obtained with an IR camera. Scale bar, 2 cm. (d) Measured temporal change of the average temperatures of the fabricated Ag/Ag2O NFs/IML heater with increasing DC bias. The DC bias was elevated to 6 V with a step increase of 1 V every 30 sec. (e) Measured temporal change of the average temperatures of the heaters containing Ag/Ag2O NFs/IML (Rs = 1.9 Ω/sq), Ag NWs (Rs = 15 Ω/sq), ITO film (Rs = 60 Ω/sq), at a DC bias of 2 V. All the heaters exhibited the same transmittance of 94% at λ = 550 nm. (f) Comparison of the heating and cooling rates of the same heaters as shown in (e), with different applied DC biases (2 V for the Ag/Ag2O NFs/IML, 5.5 V for the Ag NWs, and 11 V for the ITO film), to obtain the same thermal equilibrium temperature of 120 ℃. (g) Measured defogging time of the Ag/Ag2O NFs/IML heater with variation of the DC biases. (h) Photographs of the Ag/Ag2O-NF/IML heater integrated automobile windshield at turn-off (left) and turn-on (right) modes. The applied DC bias was 6 V. Scale bars, 5 cm. The insets show a driver’s view through the windshield (lower) and an image captured with an IR camera displaying the temperature distribution of the windshield (upper).

20

ACS Paragon Plus Environment

Page 21 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60