A General Method for Generating Circular ... - ACS Publications

Subscriber access provided by UNIVERSITY OF THE SUNSHINE COAST

Article

A General Method for Generating Circular Gradients of Active Proteins on Nanofiber Scaffolds Sought for Wound Closure and Related Applications Tong Wu, Jiajia Xue, Haoxuan Li, Chunlei Zhu, Xiumei Mo, and Younan Xia ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.8b00129 • Publication Date (Web): 08 Feb 2018 Downloaded from http://pubs.acs.org on February 12, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Revised MS #am-2018-00129k

A General Method for Generating Circular Gradients of Active Proteins on Nanofiber Scaffolds Sought for Wound Closure and Related Applications

Tong Wu,†, ‡, ± Jiajia Xue,†, ± Haoxuan Li,† Chunlei Zhu,† Xiumei Mo,‡ Younan Xia†,ǁ,*

†

The Wallace H. Coulter Department of Biomedical Engineering, Georgia Institute of

Technology and Emory University, Atlanta, Georgia 30332, United States ‡

State Key Lab for Modification of Chemical Fibers and Polymer Materials, College of

Chemistry, Chemical Engineering and Biotechnology, Donghua University, Shanghai 201620, P. R. China ǁ

School of Chemistry and Biochemistry, School of Chemical and Biomolecular Engineering,

Georgia Institute of Technology, Atlanta, Georgia 30332, United States

*

Address correspondence to Y. X. ([email protected])

±

These two authors contributed equally to this work.

KEYWORDS: Radially aligned nanofibers, active protein gradient, cell migration, neurite extension, wound dressing

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT: Scaffolds functionalized with circular gradients of active proteins are attractive for tissue regeneration due to their enhanced capability to accelerate cell migration and/or promote neurite extension in a radial fashion. Here we report a general method for generating circular gradients of active proteins on scaffolds comprised of radially aligned nanofibers. In a typical process, the scaffold, with its central portion raised using a copper wire to take a cone shape, was placed in a container (upright or up-side-down), followed by dropwise addition of a bovine serum albumin (BSA) solution into the container. As such, a circular gradient of BSA was generated along each nanofiber. The bare regions uncovered by BSA were then filled with an active protein of interest. In demonstrating their potential applications, we used different model systems to examine the effects of two types of protein gradients. While the gradient of laminin and epidermal growth factor accelerated the migration of fibroblasts and keratinocytes, respectively, from the periphery towards the center of the scaffold, the gradient of nerve growth factor promoted the radial extension of neurites from the embryonic chick dorsal root ganglion. This method for generating circular gradients of active proteins can be readily extended to different types of scaffolds to suit wound closure and related applications that involve cell migration and/or neurite extension in a radial fashion.

2


Page 2 of 36

Page 3 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


1. INTRODUCTION In designing scaffolds for tissue regeneration, both topographical and biochemical cues should be incorporated to maximize the rates of cell migration and proliferation. In particular, the synergistic effect between topographical guidance and chemotaxing can contribute to the quick establishment of a microenvironment that simulates the structures and functions of the native extracellular matrix (ECM).1,2 To this end, electrospun nanofibers have been extensively explored as scaffolds for tissue regeneration owing to their capability to mimic the collagen nanofibers in ECM by offering topographic guidance.3-8 Electrospun nanofibers covered with linear gradients of active proteins have been demonstrated for promoting or regulating cell migration, proliferation, and differentiation.9-13 To this end, a variety of strategies have been developed for incorporating protein gradients into scaffolds based on electrospun nanofibers. Li et al. used an electrohydrodynamic jet printing technique to produce a linear gradient of protein droplets on electrospun fibers by adjusting the translation speed of the movable collector along the lateral directions.14 Similarly, a linear gradient of protein-encapsulated microparticles was generated across a substrate by spatially varying the deposition time during which the substrate was exposed to the electrosprayed microparticles.15 Another commonly used approach is based upon the strategy of varying the immersion time of a nanofiber scaffold in a solution along a particular direction. This approach has been successfully utilized to create linear gradients of proteins, mineral contents, and even cells on the scaffolds of electrospun nanofibers.11, 16-18 Despite the successful development of nanofiber scaffolds covered with linear gradients of active proteins, we still lack a general method for generating circular gradients of active 3



proteins. In a previous study, we demonstrated a facile method for fabricating radially aligned nanofibers using a collector consisting of a central point electrode and a peripheral ring electrode. It was shown that the dural fibroblasts cultured on the radially aligned nanofibers migrated towards the center of the scaffold at a higher speed than that on a counterpart consisting of random nanofibers.19 This class of scaffolds shows great potential as biomedical patches to accelerate the regeneration of dura mater. When integrated with circular gradients of active proteins, such scaffolds would be further empowered to accelerate cell migration from the periphery towards the center and thus speed up wound closure. For another application in the regeneration of optic nerve, this type of scaffold coated with a circular gradient of active protein would not only provide a topological structure to mimic the radial axon paths in the retina20 but also offer a biological cue to further enhance the guidance of neurite extension along the radial directions. However, to our knowledge, there is only one report by Li et al. for generating a circular gradient of collagen-binding domain (CBD)-fused proteins on radially aligned polycaprolactone (PCL)/collagen fibers. The CBD-fused proteins specifically bound to collagen, and the protein gradient was produced due to the gradual decrease in fiber density from the center to the periphery.10 Actually, the proteins were not deposited in a gradient along each individual nanofiber. In addition, it will not be easy to extend this method to nanofibers free of collagen and/or to proteins without CBD. As reported in a recent study, a linear gradient of active protein could be readily produced on a scaffold of uniaxially aligned nanofibers by back-filling the active protein onto the bare regions left behind by a graded mask of bovine serum albumin (BSA).21 Here we further demonstrate that the capability of this strategy can be extended to generate a circular gradient 4


Page 4 of 36

Page 5 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


of active protein along radially aligned nanofibers. Specifically, a scaffold of radially aligned nanofibers is placed in a container, with the center of the scaffold being raised or depressed using a copper wire. A graded mask of BSA along the radial alignment is then produced by introducing a BSA solution dropwise. Afterwards, an active protein is adsorbed onto the bare regions left behind by the BSA mask to generate a circular gradient of the active protein that runs countercurrent to BSA. As a major advantage, this simple and general method can be easily adapted for various types of active proteins and electrospun nanofibers. The use of BSA blocking also allows us to greatly reduce the usage of an expensive protein such as a growth factor in generating the desired gradient. As a proof-of-concept demonstration in terms of potential applications, we investigate the effects of a laminin gradient on fibroblasts migration and an epidermal growth factor (EGF) gradient on keratinocytes migration, respectively, from the periphery towards the center for the purpose of wound closure. Additionally, we examine the effect of a nerve growth factor (NGF) gradient increasing from the center to the periphery on neurite extension for potential use in the regeneration of retinal ganglion cell axons in the optic nerve.

2. EXPERIMENTAL METHODS 2.1 Fabrication and characterization of radially aligned PCL nanofibers. We fabricated the radially aligned nanofibers using an electrospinning setup similar to what was reported in our previous study.19 PCL (Mw ≈ 80,000 g/mol, Sigma-Aldrich, St. Louis, MO) was dissolved in 2,2,2-trifluoroethanol at a concentration of 10 wt.%. The PCL solution was pumped out at a rate of 1.0 mL/h through a blunt needle (22-gauge). A high voltage (DC) of 5



15 kV was applied between the needle and a grounded collector separated by 13 cm. A metallic ring with a sharp needle in the center was used as the collector to obtain radially aligned nanofibers. After 10 min, the electrospinning process was terminated. The sample was coated with Au/Pd using a Hummer 6 sputter (Anatech, Union City, CA) and then imaged using a Hitachi 8230 cold field emission scanning electron microscope (Tokyo, Japan). The average diameter of the nanofibers was measured using ImageJ software from 100 nanofibers in the scanning electron microscopy (SEM) images. 2.2 Generation and characterization of a circular gradient of active protein on radially aligned PCL nanofibers. A scaffold of radially aligned nanofibers was firstly treated with oxygen plasma for 2 min in a plasma cleaner (PlasmaEtch, Carson City, NV) and sterilized under UV for 1 h. The scaffold was placed in the well of a 24-well plate, with the center of the scaffold being raised by 4 mm using a copper wire. Then, 0.1% BSA solution was pumped into the well at a flow rate of 1.0 mL/h to create a graded mask of BSA. After the solution level had reached the top point, in about 35 min, the sample was removed from the BSA solution. The copper wire was dismissed, and the scaffold masked by a gradient of BSA was immediately rinsed three times with phosphate buffer solution (PBS). Afterwards, the scaffold was placed in the well of a 24-well plate and immersed in 100 µL of laminin solution (50 µg/mL) at 4 °C overnight, followed by rising three times with PBS. In this way, laminin was adsorbed onto the bare regions left behind by the BSA mask to generate a gradient increasing from the periphery to the center. The EGF gradient was generated using the same method as described above by immersing the BSA-masked scaffold in 100 µL of 10 µg/mL EGF solution at 4 °C overnight. To generate an opposite gradient of NGF (rather than 6


Page 6 of 36

Page 7 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


laminin or EGF) increasing from the center to the periphery, the same method of BSA blocking was used except that the center-raised scaffold was placed in the well up-side-down. Subsequently, the scaffold masked by a gradient of BSA was treated by immersing in 100 µL of 10 µg/mL NGF solution at 4 °C overnight, followed by rinsing with PBS. For comparison, a uniform coating of BSA was generated by immersing the nanofiber scaffold in the BSA solution and incubating for 35 min, followed by rinsing with PBS. The BSA-blocked scaffolds were then functionalized with laminin, EGF and NGF, respectively, using the method described above. The radially aligned nanofibers treated by immersing in PBS served as a control. We started with fluorescein isothiocyanate-labeled BSA (FITC-BSA) to characterize the resultant protein gradients after filling the uncovered regions left behind by BSA blocking. In this case, 100 µL of 0.1% FITC-BSA in PBS solution was pipetted onto the scaffolds masked by a graded or uniform layer of BSA. The samples were incubated in the dark for 2 h at room temperature. Subsequently, the nanofiber scaffolds were washed three times with 0.1% Tween 20 solution, rinsed three times with PBS, and observed under a Leica DMI 6000 B inverted microscope (Buffalo Grove, IL). On the circular nanofiber scaffold coated with graded or uniform FITC-BSA, we chose five different positions with the same incremental distance along the radial axis from the center to the periphery. At each position, a region with the same area was imaged under the fluorescence microscope. The average fluorescence intensity at each position was calculated from four samples using ImageJ software and plotted. 2.3 NIH-3T3 fibroblasts migration. We firstly assessed the cell viabilities of the 7



different types of nanofiber scaffolds. The Cell Counting Kit-8 (CCK-8; Sigma-Aldrich) assay was performed after seeding NIH-3T3 fibroblasts on the different scaffolds for 1, 3, 5, and 7 days. Cells cultured on tissue culture plates (TCP) and laminin-coated TCP served as the control groups. At each time point, the cells were washed with PBS and then the fresh culture medium with 10% CCK-8 reagent was added into each well. After 4 h, the well plate was shaken for 15 min, and the absorbance of the supernatant at 450 nm was measured using a microplate reader. We then investigated the combined effect of nanofiber alignment and laminin gradient on the migration of NIH-3T3 fibroblasts. The nanofiber scaffolds coated with a graded and uniform layer of laminin, as well as scaffolds made of bare nanofibers, were separately transferred into the wells of a 24-well plate after lifting off the scaffolds from the edge of the metal rings. The cells cultured on laminin-coated TCP served as control. In each well, a polydimethylsiloxane (PDMS) cylinder of 6 mm in diameter was placed in the center. The NIH-3T3 fibroblasts were dissociated in Dulbecco's modified eagle medium (DMEM) supplemented with 10% fetal bovine serum (FBS) and 1% antibiotic-antimycotic (ABAM), and then seeded at a concentration of 1 × 105 cells/mL onto the surrounding areas left by the PDMS cylinders. After cell adhesion for 4 h, the cylinders were removed to allow the cells to migrate inward. After incubation for 3 days, the NIH-3T3 fibroblasts on different samples were stained with Alexa Fluor 555 phalloidin and 4′,6-diamidino-2-phenylindole (DAPI). Briefly, the cells were fixed in 3% glutaraldehyde solution at room temperature for 10 min and permeabilized with 0.1% Triton X-100 for 5 min. Staining solution of Alexa Fluor 555 phalloidin was 8


Page 8 of 36

Page 9 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


prepared by diluting 5 µL methanolic stock solution in 200 µL of PBS for each sample. Then, 1% BSA was added into the staining solution to reduce nonspecific background staining. The samples were incubated in the staining solution for 20 min at room temperature. Afterwards, the nuclei of the cells were stained with DAPI for 5 min. Between each procedure, the samples were washed three times with PBS. After staining, the samples were imaged using the Leica DMI 6000 B inverted microscope. Micrographs were taken at low magnification to analyze the distribution and migration of cells on different samples. High-magnification micrographs were also acquired to examine the morphology and alignment of the cells. The migration zone on each sample was divided into three regions with the same incremental distance along the radial axis from the center to the periphery. The number of cells in each migration region was measured from the fluorescence micrographs of DAPI staining using ImageJ software. The migration index (MI) of each sample was calculated to evaluate the migration ability of the cells. The ratio of the sum of the numbers of practically migrated cells multiplied by migrated distances to the theoretical value, termed as MI, was calculated using the following equation: MI =

N1 × L1 + N2 × L2 + N3 × L3 (N1 + N2+N3 ) × L1

where N1, N2, and N3 are the numbers of migrated cells in three consecutive regions, respectively. L1, L2, and L3 are the correspondingly migrated distances from the originally seeded site to different migration regions. 2.4 Keratinocytes migration. To investigate the combined effect of nanofiber alignment and EGF gradient on the migration of keratinocytes, we separately transferred the nanofiber

9



scaffolds coated with a graded and uniform layer of EGF, masked by a gradient of BSA, and made of bare nanofibers, into the wells of a 24-well plate. We then followed the same method as described in Section 2.3 to investigate keratinocytes migration on the different scaffolds, except that the keratinocytes were dissociated and cultured in medium 154 supplemented with 1% human keratinocyte growth supplement (HKGS) and 1% ABAM. After incubation for 3 days, the keratinocytes were stained with Alexa Fluor 555 phalloidin and DAPI. The number of cells in each migration region was measured, and the migration index of cells on each type of scaffold was calculated. 2.5 DRG neurites extension. We further investigated the combined effect of nanofiber alignment and NGF gradient on the extension of neurites from the embryonic chick dorsal root ganglion (DRG). All DRG cells were isolated from the thoracic region of the spinal column in embryonic chick via sterile microdissection.22 Embryonic day 8 (E8, stage HH35−36) chicks were removed from the white leghorn egg and decapitated. DRG cells were dissected from the thoracic region and collected in Hanks' balanced salt solution (HBSS). Then, the DRG cells were seeded onto the samples (1 DRG per sample) and cultured in a modified neurobasal medium supplemented with 10% FBS, 1% N-2 supplement, 1% ABAM, and 50 ng/mL NGF. After incubation for 6 days, the samples were fixed in 3% glutaraldehyde for 10 min, permeabilized with 0.1% Triton X-100 for 5 min, and blocked with 3% BSA/PBS solution for 1 h. Then, the samples were incubated with Tuj1 primary antibody at 4 °C overnight, followed by staining using Alexa Fluor 488 secondary antibody for 1 h. Between steps, the samples were rinsed three times with PBS solution. Fluorescence micrographs were captured using the Leica DMI 6000 B inverted microscope. The average 10


Page 10 of 36

Page 11 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


lengths of the extended neurites on either side of the DRG bodies were measured from the fluorescence micrographs using ImageJ software. Six DRG cells on each type of sample were used to calculate the neurite length. 2.6 Statistical analysis. Comparison between groups was performed using one-way ANOVA, followed by Student’s t-tests for all pairwise comparisons. All the values were averaged at least in triplicate and presented in the form of mean ± standard deviation.

3. RESULTS AND DISCUSSION 3.1 Generation of a circular gradient of active protein on radially aligned PCL nanofibers. We firstly fabricated radially aligned PCL nanofibers by electrospinning, with the use of a collector comprised of a metallic ring (the ring electrode) and a metallic needle (the point electrode).19 Figure 1A shows a schematic of the setup. The electrospun nanofibers were deposited across the gap between the needle and the ring in a radial alignment (Figure 1B). Figure 1C shows a photograph of the as-obtained nanofiber scaffold while Figure 1D presents an optical micrograph captured from the central portion of the scaffold. As confirmed by the SEM images in Figure S1, the deposited nanofibers were radially aligned from the center towards the periphery of the scaffold, with an average fiber diameter of 428 ± 34 nm. We then generated a circular gradient of active protein on the radially aligned nanofibers. As illustrated in Figure 2, the nanofiber scaffold was placed in the well of a 24-well plate after the central portion had been raised with a copper wire. We then added a BSA solution dropwise into the well at a fixed injection rate to create a gradient of BSA. Afterwards, the 11



copper wire was removed and the regions on the nanofibers unblocked by BSA were filled with an active protein to generate a gradient of the protein that ran countercurrent to BSA. In this way, we obtained a circular gradient of active protein, whose coverage density increased from the periphery to the center. Similarly, a circular gradient of active protein that increased from the center to the periphery was also created using the same strategy except that the center-raised scaffold was placed in the well up-side-down. For comparison, a uniform coating of BSA was generated by immersing the nanofiber scaffold in the BSA solution, followed by rinsing with PBS. The BSA-masked scaffold was then functionalized with the active protein. A scaffold of bare nanofibers was also treated by directly immersing in PBS and used as a control. Figure S2 shows a schematic of the scaffold coated with a graded or uniform layer of BSA and the corresponding scaffold with a graded or uniform coating of the active protein. To visualize the gradients, we used FITC-BSA as a model protein and performed the above procedures to obtain nanofiber scaffolds covered with a graded or uniform coating of FITC-BSA. Figure 3 shows the relative fluorescence intensities at different locations on the nanofiber scaffolds, as marked in the illustration, and the corresponding fluorescence images are shown in Figure S3. Along the radial direction, a continuous change in fluorescence intensity was clearly observed for the nanofiber scaffold coated with FITC-BSA in a gradient, while no obvious change was found for the nanofiber scaffold uniformly coated with FITC-BSA. For the scaffold with a gradient of FITC-BSA that increased from the center to the periphery, the fluorescence intensity at the periphery was nearly four times stronger than that at the center. Similarly, the fluorescence intensity of the nanofiber scaffold with an 12


Page 12 of 36

Page 13 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


opposite gradient of FITC-BSA showed a three-fold decrease from the center to the periphery. These results confirmed that a circular gradient of active protein was successfully generated along the radially aligned nanofibers. We further evaluated the stability of the as-obtained gradient of FITC-BSA on the nanofiber scaffold. No obvious change to the gradient of fluorescence intensity was observed even after the scaffold had been immersed in PBS for one week. It is well documented that proteins tend to spread across a surface during adsorption and are only irreversibly bound as a monolayer.23,24 The proteins reversibly bound to the surface were washed away when the nanofiber scaffold was rinsed with buffer solution at each step. Taken together, it can be concluded that the resulting gradient was comprised of irreversibly bound proteins and that is why the gradient showed good stability. 3.2 Migration of NIH-3T3 fibroblasts and keratinocytes. Scaffolds made of radially aligned nanofibers could promote wound closure by inducing cell migration along the radial direction.19 Here we demonstrate that the contact guidance for cell migration can be further enhanced by combining a biological cue with the topographic cue presented by the nanofibers. Laminin is a major component of the basal lamina, and is known to play critical roles in cell migration, proliferation, and differentiation.25 To study the combined effect of radial alignment and laminin gradient on the migration and proliferation of NIH-3T3 fibroblasts, we fabricated and compared nanofiber scaffolds coated with graded laminin increasing from the periphery to the center, covered with a uniform coating of laminin, and made of bare nanofibers. We firstly investigated cell viabilities on the three different types of scaffolds, with TCP and laminin-coated TCP served as two control groups. As shown in Figure 4A, cell proliferation on scaffolds covered with a graded or uniform coating of laminin was better 13



relative to the scaffold comprised of bare nanofibers, regardless of the culturing time. The cell viability on the scaffolds coated with graded laminin was significantly greater (at P < 0.05 level) than that on TCP when the cells proliferated to 5 and 7 days (Figure 4B). These findings indicate that coating nanofiber scaffolds with laminin could indeed improve both the proliferation and viability of cells, mainly due to the bioactivity of laminin and the improved surface wettability.26 The migration of NIH-3T3 fibroblasts on the different types of nanofiber scaffolds was investigated using a specific cell culture system (Figure S4), with laminin-coated TCP serving as a control. Briefly, a PDMS cylinder was placed in the center of the nanofiber scaffold as a physical block to generate a migration region with a diameter of 6 mm. Cells were seeded around the periphery of the PDMS cylinder. The cylinder was removed at 4 h post seeding to allow the cells to migrate inward. After 3 days, we stained the cells with DAPI and Alexa Fluor 555 phalloidin to reveal the positions of the cells on the various substrates. In general, the actin cytoskeleton stained by Alexa Fluor 555 phalloidin should be organized in the same direction as cell movement.27 Figure 5 shows the fluorescence micrographs of the cells on different types of nanofiber scaffolds and laminin-coated TCP. On the scaffolds coated with graded laminin, the cells almost covered the entire area of the migration zone, and a large number of cells were observed in the center. The contact guidance provided by the underneath nanofibers and the circular gradient of laminin synergistically promoted cell migration towards the increased content of laminin along the radial alignment. By contrast, fewer cells were found in the migration zones of scaffolds covered with a uniform coating of laminin, scaffolds comprised of bare nanofibers, and 14


Page 14 of 36

Page 15 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


laminin-coated TCP. In particular, very few cells appeared in the central areas of scaffolds made of bare nanofibers and laminin-coated TCP. The cells tended to migrate along the radially aligned nanofibers while the cells took a random track on TCP. It has been reported that the cytoskeleton, comprised of actin microfilaments, microtubules, and intermediate filaments, plays a critical role in cell migration.28 As shown in Figure 6A-C, the cytoskeleton took an elongated morphology and large extension on the radially aligned nanofibers. By contrast, the cells took a random arrangement and less extension when cultured on laminin-coated TCP (Figure 6D). Recent studies have demonstrated that cell migration relies strongly on the ECM, and the regulation of cell motility depends on the dimensionality of features, as well as physical and biochemical environments.29 Cells can sense the guide taxis provided by the radial alignment of nanofibers and the circular gradient of laminin, taking an elongated orientation and migrating towards the central region with the highest laminin content. From the fluorescence micrographs of DAPI nuclear staining (Figure S5), we separately measured the average cell number in three consecutive regions in the migration zone along the direction of radial alignment, as illustrated in Figure S6. Figure 7A shows the average number of cells in each region of the migration zone on different types of nanofiber scaffolds and laminin-coated TCP. The number of cells migrated to the central area (region 1) of the scaffold coated with a circular gradient of laminin was increased by 1.24-, 1.99-, and 6.24-fold, respectively, relative to those on the scaffolds covered with a uniform coating of laminin or comprised of bare nanofibers, and laminin-coated TCP. We further calculated the migration index in relation to the ability of cell migration on the different types of substrates. 15



Figure S6 illustrates the method used for calculating the migration index. The migration index is defined as the ratio of the sum of the numbers of practically migrated cells multiplied by migrated distances to the theoretical value. From the calculation formula, cells possess greater migration ability when their migration indices approach unity. Figure 7B shows the migration indices for cells cultured on different types of nanofiber scaffolds and laminin-coated TCP. For the cells cultured on the nanofiber scaffolds covered with a gradient of laminin, they possessed the greatest migration index of 0.594 ± 0.004. This value was significantly different (at P < 0.01 level) when compared with those of cells cultured on scaffolds covered with a uniform coating of laminin (0.559 ± 0.005), scaffolds consisted of bare nanofibers (0.531 ± 0.014), and laminin-coated TCP (0.471 ± 0.002). We also demonstrated that the graded coating of BSA on the nanofiber scaffolds had no impact on cell migration when compared with that on the scaffolds made of bare nanofiber. The number of cells migrated to the central area and the migration index of cells on the scaffolds coated with graded laminin were significantly larger (at P < 0.01 level) than those cultured on scaffolds masked by graded BSA, as shown in Figure S7. These results confirm that the cells possess the greatest migration ability when cultured on the scaffolds comprised of radially aligned nanofibers and coated with a circular gradient of laminin. Compared with the random pattern and slow migration on TCP substrates, the contact guidance provided by the radially aligned nanofibers induced elongation, orientation, and quick migration of cells along the radial alignment. Furthermore, the laminin coating on the nanofiber scaffolds enhanced cells viability and proliferation, promoting additional cell migration compared with scaffolds consisted of bare nanofibers. Cells tended to migrate faster on the scaffolds coated with 16


Page 16 of 36

Page 17 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


graded laminin than those with a uniform coating of laminin, mainly because of the guide taxis provided by the protein gradient, which could promote cells to migrate towards higher protein content. The results indicate that the circular gradient of laminin along with the radial nanofiber alignment has a synergetic effect in promoting cell migration away from the cell source and towards the region with the greatest laminin content. To evaluate the potential of protein gradient in wound closure, we also examine the effect of a circular gradient of EGF on the migration of keratinocytes (Figure 8). We found that the number of keratinocytes migrated to the central area (region 1) on the scaffolds coated with graded EGF was increased by 1.50-, 3.52-, and 3.42-fold, respectively, relative to those on the scaffolds covered by a uniform coating of EGF, masked by graded BSA, and comprised of bare nanofibers. The number of cells migrated to the middle area (region 2) on the scaffolds coated with graded EGF was increased by 1.65-, 3.84-, and 3.59-fold, respectively, relative to those on the scaffolds covered with a uniform coating of EGF, masked by graded BSA, and comprised of bare nanofibers. For the keratinocytes cultured on the scaffolds covered with a gradient of EGF, they possessed the greatest migration index of 0.626 ± 0.008. This value was significantly higher than those obtaining by culturing the cells on the scaffolds covered with a uniform coating of EGF (0.598 ± 0.014) at P < 0.05 level, masked by graded BSA (0.509 ± 0.020) and consisted of bare nanofibers (0.512 ± 0.006) at P < 0.01 level, respectively. These results indicate that a circular gradient of EGF on radially aligned nanofibers can promote keratinocytes migration from the periphery to the center. Taken together, this class of scaffolds coated with a gradient of active protein shows great promise for wound closure. 17



3.3 DRG neurites extension. Scaffolds consisting of radially aligned nanofibers provide a potential alternative to direct the growth of retinal ganglion cell axons radially, in an effort to mimic the radial axon paths in the retina.20 The neurotrophic effect, when combined with the contact guidance of aligned nanofibers, could be used to maximize neurite extension.30 Herein, we fabricated radially aligned nanofiber scaffolds coated with an increasing NGF gradient from the center to the periphery to investigate neurite extension from DRG. The scaffolds covered with a uniform coating of NGF and scaffolds consisted of bare nanofibers served as controls. Figure 9A-C shows fluorescence micrographs of the typical neurite fields extending from DRG seeded on the different types of nanofiber scaffolds. Due to the contact guidance provided by the underneath nanofibers in all cases, the neurites extruding from DRG bodies followed the radial alignment of nanofibers, as indicated by white arrows. By contrast, the neurites on TCP extended with a random and isotropic pattern around the DRG body.30 The average neurite lengths outgrowing from the DRG bodies towards the center or the periphery are displayed in Figure 9D. Due to the guidance provided by the increasing NGF gradient from the center to the periphery, the average neurite length towards the periphery was significantly enhanced to 1.34 ± 0.19 mm by additional 44% as compared with 0.93 ± 0.23 mm towards the center on the scaffolds coated with a circular gradient of NGF. When NGF was uniformly coated on the scaffolds, the average neurite length towards the center and the periphery was 0.79 ± 0.18 mm and 0.73 ± 0.18 mm, respectively. No significant difference was found between either side of the DRG cell mass. In the presence of NGF, the DRG neurites extended longer on the nanofiber scaffolds covered with a graded and uniform 18


Page 18 of 36

Page 19 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


coating of NGF than those on bare nanofibers (0.27 ± 0.06 mm towards the center and 0.24 ± 0.04 mm towards the periphery, respectively), regardless of the extending directions. It has been reported that the growth cones of DRG neurites could recognize the growth factor, expand their membranes, and then stretch for the next bound factor when DRG cells were cultured on nanofibers coated with NGF.31 The NGF enhanced the attachment of growth cones on nanofibers and provided an anchor to further expand the growth cones for neurite extension.21 By increasing the NGF content along the radially aligned nanofibers, the growth cones of neurites could sense more growth factors within their reach and further expand their membranes along the direction of NGF gradient.21,32 As a result, the neurites extending towards the increased content in NGF were significantly longer by 1.44-fold than neurites extending against the gradient on the radially aligned nanofibers.

4. CONCLUSION In summary, we have demonstrated a simple and general strategy for generating circular gradients of active proteins on radially aligned nanofibers by firstly creating a graded mask of BSA. By constantly increasing the volume of BSA solution introduced into a container with a center-raised nanofiber scaffold placed in the upright or up-side-down configuration, a gradient of BSA can be generated along the radially aligned nanofibers. Then, the bare regions left behind by the BSA are filled with an active protein of interest to generate a circular gradient of the active protein that runs countercurrent to BSA. This class of scaffolds is able to present both a topographic cue in radial alignment and a biochemical cue in protein gradient towards the center or the periphery, which can be readily adapted for various types 19



of active proteins and polymer scaffolds. As a demonstration for the potential applications in tissue engineering, a circular gradient of laminin, EGF, or NGF was generated on radially aligned PCL nanofibers along the nanofiber orientation. We showed that the migration of fibroblasts or keratinocytes towards the center of the nanofiber scaffold could be accelerated with the presence of a laminin or EGF gradient along the radial alignment. For the radially aligned nanofibers coated with a gradient of NGF, DRG neurites extended along the radial alignment of nanofibers, and the neurites extending towards the increase in NGF content were significantly longer by 1.44-fold than those extending in the opposite direction. Taken together, these studies provide valuable information for designing biochemically graded scaffolds integrated with a radially aligned topographical cue for potential use in wound closure and related applications requiring cell migration and/or neurite extension in a radial pattern.

ASSOCIATED CONTENT Supporting Information    The Supporting Information is available free of charge on the ACS Publications website at DOI: xxx. SEM images of the radially aligned nanofibers; schematic illustration of the gradients of active proteins after BSA blocking; fluorescence images showing a gradient or uniform coating of FITC-BSA; schematic illustration of the cell culture system; representative DAPI immunofluorescence micrographs used for measuring cell numbers in the migration zones; schematic showing how to calculate migration index based on the fluorescence micrographs 20


Page 20 of 36

Page 21 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


of cell migration; immunofluorescence micrographs showing fibroblast migration on the scaffolds masked with a gradient of BSA (PDF) AUTHOR INFORMATION Corresponding Authors *E-mail: [email protected]. ORCID Tong Wu: 0000-0001-8822-1868 Jiajia Xue: 0000-0002-7209-7935 Chunlei Zhu: 0000-0003-2477-306X Xiumei Mo: 0000-0001-9238-6171 Younan Xia: 0000-0003-2431-7048 Author Contributions ±

T.W. and J.X. contributed equally to this work.

Notes The authors declare no competing financial interest. ACKNOWLEDGMENTS This work was supported in part by a grant from the NIH (R01 EB020050) and startup funds from the Georgia Institute of Technology. As a jointly supervised PhD candidate from Donghua University, T.W. was also partially supported by a fellowship from the China Scholarship Council.

REFERENCES 21



(1) Braghirolli, D. I.; Steffens, D.; Pranke, P. Electrospinning for Regenerative Medicine: A Review of the Main Topics. Drug Discov. Today 2014, 19, 743-753. (2) Kim, S. E.; Harker, E. C.; De Leon, A. C.; Advincula, R. C.; Pokorski, J. K. Coextruded, Aligned, and Gradient-Modified Poly(ε-caprolactone) Fibers as Platforms for Neural Growth. Biomacromolecules 2015, 16, 860-867. (3) Liu, W.; Thomopoulos, S.; Xia, Y. Electrospun Nanofibers for Regenerative Medicine. Adv. Healthcare Mater. 2012, 1, 10-25. (4) He, J.; Zhou, Y.; Wu, Y.; Liu, R. Nanofiber Coated Hybrid Yarn Fabricated by Novel Electrospinning-Airflow Twisting Method. Surf. Coat. Technol. 2014, 258, 398-404. (5) Joseph, J.; Nair, S. V.; Menon, D. Integrating Substrateless Electrospinning with Textile Technology for Creating Biodegradable Three-Dimensional Structures. Nano Lett. 2015, 15, 5420-5426. (6) Li, H.; Xu, Y.; Xu, H.; Chang, J. Electrospun Membranes Control of the Structure and Structure Related Applications in Tissue Regeneration and Drug Delivery. J. Mater. Chem. B 2014, 2, 5492-5510. (7) Lu, P.; Xia, Y. Maneuvering the Internal Porosity and Surface Morphology of Electrospun Polystyrene Yarns by Controlling the Solvent and Relative Humidity. Langmuir 2013, 29, 7070-7078. (8) Liu, W.; Lipner, J.; Moran, C. H.; Feng, L.; Li, X.; Thomopoulos, S.; Xia, Y. Generation of Electrospun Nanofibers with Controllable Degrees of Crimping Through a Simple, Plasticizer-Based Treatment. Adv. Mater. 2015, 27, 2583-2588. (9) Dinis, T. M.; Elia, R.; Vidal, G.; Auffret, A.; Kaplan, D. L.; Egles, C. Method to Form a 22


Page 22 of 36

Page 23 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Fiber/Growth Factor Dual-Gradient Along Electrospun Silk for Nerve Regeneration. ACS Appl. Mater. Interfaces 2014, 6, 16817-16826. (10) Li, X.; Li, M.; Sun, J.; Zhuang, Y.; Shi, J.; Guan, D.; Chen, Y.; Dai, J. Radially Aligned Electrospun Fibers with Continuous Gradient of SDF1α for the Guidance of Neural Stem Cells. Small 2016, 12, 5009-5018. (11) Liu, W.; Lipner, J.; Xie, J.; Manning, C. N.; Thomopoulos, S.; Xia, Y. Nanofiber Scaffolds with Gradients in Mineral Content for Spatial Control of Osteogenesis. ACS Appl. Mater. Interfaces 2014, 6, 2842-2849. (12) Benetti, E. M.; Gunnewiek, M. K.; van Blitterswijk, C. A.; Julius Vancso, G.; Moroni, L. Mimicking Natural Cell Environments: Design, Fabrication and Application of Bio-Chemical Gradients on Polymeric Biomaterial Substrates. J. Mater. Chem. B 2016, 4, 4244-4257. (13) Zou, B.; Liu, Y.; Luo, X.; Chen, F.; Guo, X.; Li, X. Electrospun Fibrous Scaffolds with Continuous Gradations in Mineral Contents and Biological Cues for Manipulating Cellular Behaviors. Acta Biomater. 2012, 8, 1576-1585. (14) Li, X.; Liang, H.; Sun, J.; Zhuang, Y.; Xu, B.; Dai, J. Electrospun Collagen Fibers with Spatial Patterning of SDF1α for the Guidance of Neural Stem Cells. Adv. Healthcare Mater. 2015, 4, 1869-1876. (15) Li, X.; Macewan, M. R.; Xie, J. D.; Siewe, D.; Yuan, X.; Xia, Y. Fabrication of Density Gradients of Biodegradable Polymer Microparticles and Their Use in Guiding Neurite Outgrowth. Adv. Funct. Mater. 2010, 20, 1632-1637. (16) Shi, J.; Wang, L.; Zhang, F.; Li, H.; Lei, L.; Liu, L.; Chen, Y. Incorporating Protein Gradient into Electrospun Nanofibers as Scaffolds for Tissue Engineering. ACS Appl. Mater. 23



Interfaces 2010, 2, 1025-1030. (17) Li, X.; Xie, J.; Lipner, J.; Yuan, X.; Thomopoulos, S.; Xia, Y. Nanofiber Scaffolds with Gradations in Mineral Content for Mimicking the Tendon-to-Bone Insertion Site. Nano Lett. 2009, 9, 2763-2768. (18) Liu, W.; Zhang, Y.; Thomopoulos, S.; Xia, Y. Generation of Controllable Gradients in Cell Density. Angew. Chem. Int. Ed. 2013, 52, 429-432. (19) Xie, J.; MacEwan, M. R.; Ray, W. Z.; Liu, W.; Siewe, D. Y.; Xia, Y. Radially Aligned, Electrospun Nanofibers as Dural Substitutes for Wound Closure and Tissue Regeneration Applications. ACS Nano 2010, 4, 5027-5036. (20) Kador, K. E.; Montero, R. B.; Venugopalan, P.; Hertz, J.; Zindell, A. N.; Valenzuela, D. A.; Uddin, M. S.; Lavik, E. B.; Muller, K. J.; Andreopoulos, F. M.; Goldberg, J. L. Tissue Engineering the Retinal Ganglion Cell Nerve Fiber Layer. Biomaterials 2013, 34, 4242-4250. (21) Tanes, M. L.; Xue, J.; Xia, Y. A General Strategy for Generating Gradients of Bioactive Proteins on Electrospun Nanofiber Mats by Masking with Bovine Serum Albumin. J. Mater. Chem. B 2017, 5, 5580-5587. (22) Powell, S.; Vinod, A.; Lemons, M. L. Isolation and Culture of Dissociated Sensory Neurons from Chick Embryos. J. Visualized Exp. 2014, 91, No. e51991. (23) Kim, J.; Somorjai, G. A. Molecular Packing of Lysozyme, Fibrinogen, and Bovine Serum Albumin on Hydrophilic and Hydrophobic Surfaces Studied by Infrared-Visible Sum Frequency Generation and Fluorescence Microscopy. J. Am. Chem. Soc. 2003, 125, 3150-3158. (24) Latour, R. A. Biomaterials: Protein-Surface Interactions. Encycl. Biomater. Biomed. Eng. 24


Page 24 of 36

Page 25 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


2005, 1, 270-278. (25) Lee, D. Y.; Lee, J. H.; Ahn, H. J.; Oh, S. H.; Kim, T. H.; Kim, H. B.; Park, S. W.; Kwon, S. K. Synergistic Effect of Laminin and Mesenchymal Stem Cells on Tracheal Mucosal Regeneration. Biomaterials 2015, 44, 134-142. (26) Koh, H. S.; Yong, T.; Chan, C. K.; Ramakrishna, S. Enhancement of Neurite Outgrowth Using Nano-Structured Scaffolds Coupled with Laminin. Biomaterials 2008, 29, 3574-3582. (27) Friedl, P.; Wolf, K.; Lammerding, J. Nuclear Mechanics During Cell Migration. Curr. Opin. Cell Biol. 2011, 23, 55-64. (28) Etienne-Manneville, S. Microtubules in Cell Migration. Annu. Rev. Cell Dev. Biol. 2013, 29, 471-499. (29) Doyle, A. D.; Petrie, R. J.; Kutys, M. L.; Yamada, K. M. Dimensions in Cell Migration. Curr. Opin. Cell Biol. 2013, 25, 642-649. (30) Xue, J.; Yang, J.; O'Connor, D. M.; Zhu, C.; Huo, D.; Boulis, N. M.; Xia, Y. Differentiation of Bone Marrow Stem Cells into Schwann Cells for the Promotion of Neurite Outgrowth on Electrospun Fibers. ACS Appl. Mater. Interfaces 2017, 9, 12299-12310. (31) Kapur, T. A.; Shoichet, M. S. Immobilized Concentration Gradients of Nerve Growth Factor Guide Neurite Outgrowth. J. Biomed. Mater. Res. A 2004, 68, 235-243. (32) Cao, X.; Shoichet, M. Defining the Concentration Gradient of Nerve Growth Factor for Guided Neurite Outgrowth. Neuroscience 2001, 103, 831-840.

25



Figure 1. (A) Schematic of the electrospinning setup used for generating a scaffold consisted of radially aligned PCL nanofibers. (B) Schematic showing the nanofibers aligned across the point and ring electrodes. (C) Photograph showing a typical sample of radially aligned PCL nanofibers. (D) Optical micrograph captured from the central portion of the scaffold.

26


Page 26 of 36

Page 27 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 2. Schematic for generating a circular gradient of active protein along radially aligned nanofibers. A plasma-treated nanofiber scaffold, whose center is raised by 4 mm with a copper wire, is placed in the well of a 24-well plate. A gradient of BSA is then created by pumping 0.1% BSA solution into the well at a rate of 1 mL/h. The bare regions left by BSA are then filled with an active protein to generate a gradient that runs countercurrent to the BSA gradient. In this way, a radial gradient increasing from the periphery to the center is generated. Similarly, an opposite gradient increasing from the center towards the periphery can be produced using the same approach except that the center-raised scaffold is placed in the well up-side-down.

27



Figure 3. Relative fluorescence intensity showing a graded or uniform coating of FITC-BSA along the radially aligned nanofibers generated through BSA blocking. The inset shows a schematic of the corresponding positions along the radial direction.

28


Page 28 of 36

Page 29 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 4. (A) The proliferation of NIH-3T3 fibroblasts on the different types of nanofiber scaffolds tested by CCK-8 assay. *P < 0.05 relative to the other groups at the same culture time; #P < 0.05 relative to the scaffolds coated with graded and uniform laminin, and bare nanofibers; +P < 0.05 as compared with that on bare nanofibers. (B) The viabilities of cells cultured on the scaffolds covered with a gradient of laminin and on TCP at different incubation times. *P < 0.05 as compared with that on scaffolds coated with graded laminin at 1 day; #P < 0.05 as compared with that on TCP at 1 day; +P < 0.05 as compared with that on scaffolds coated with graded laminin at the same time point.

29



Figure 5. Fluorescence micrographs showing the migration of NIH-3T3 fibroblasts on radially aligned nanofibers covered with (A) a graded and (B) uniform coating of laminin, respectively, (C) bare radially aligned nanofibers, and (D) laminin-coated TCP after culture for 3 days. The cells nuclei were stained with DAPI (blue) and the actin cytoskeleton was stained with Alexa Fluor 555 phalloidin (red). The dashed lines indicate the border of cell seeding.

30


Page 30 of 36

Page 31 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 6. Fluorescence micrographs showing the morphology and alignment of NIH-3T3 fibroblasts cultured on radially aligned nanofibers covered with (A) a graded and (B) uniform coating of laminin, respectively, (C) bare radially aligned nanofibers, and (D) laminin-coated TCP. The images were captured from the migration zones. The cells nuclei were stained with DAPI (blue) and the actin cytoskeleton was stained with Alexa Fluor 555 phalloidin (red). The arrows indicate the direction of nanofiber alignment.

31



Figure 7. (A) The number of cells in different regions of the migration zone on radially aligned nanofibers covered with a graded or uniform coating of laminin, bare nanofibers, and laminin-coated TCP after 3 days of culture. *P < 0.05 as compared with that on scaffolds covered with a uniform coating of laminin; ##P < 0.01 relative to the scaffolds made of bare nanofibers and laminin-coated TCP; **P < 0.01 relative to the scaffolds covered with a uniform coating of laminin, scaffolds made of bare nanofibers, and laminin-coated TCP. (B) Migration index calculated from the numbers of migrated cells in different regions. **P < 0.01 when compared with those of cells cultured on scaffolds covered with a uniform coating of laminin, scaffolds made of bare nanofibers, and laminin-coated TCP.

32


Page 32 of 36

Page 33 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 8. Fluorescence micrographs showing the migration of keratinocytes on radially aligned nanofibers covered with (A) a graded and (B) uniform coating of EGF, respectively, (C) radially aligned nanofibers masked by a gradient of BSA, and (D) bare radially aligned nanofibers after culture for 3 days. The cells nuclei were stained with DAPI (blue) and the actin cytoskeleton was stained with Alexa Fluor 555 phalloidin (red). The dashed lines indicate the border of cell seeding. (E) The number of cells in different regions of the 33



migration zone on different scaffolds after 3 days of culture. (F) Migration index calculated from the numbers of migrated cells in different regions. *P < 0.05 and **P < 0.01 when compared with that of cells cultured on scaffolds coated with graded EGF.

34


Page 34 of 36

Page 35 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 9. Fluorescence micrographs of the typical neurite fields extending from DRG bodies when cultured on radially aligned nanofibers coated with (A) a graded and (B) uniform layer of NGF, respectively, and (C) bare radially aligned nanofibers for 6 days. The neurites were stained with Tuj1 marker (green). The arrows indicate the direction of nanofiber alignment. (D) Analyses of the average lengths of the neurites outgrowing from the chick DRG bodies cultured on different nanofiber scaffolds. ***P < 0.001 as compared with that extending from DRG bodies towards the center. No significant difference was found between either side of the DRG bodies on scaffolds covered with a uniform coating of NGF and made of bare nanofibers.

35



Table of Contents

36


Page 36 of 36