Multimodal GRAS ZnO/nano-Copper composite: A novel antimicrobial material for the management of citrus phytopathogens Mikaeel Imran Young, Ali Ozcan, Monty E. Myers, Evan G. Johnson, James H. Graham, and Swadeshmukul Santra J. Agric. Food Chem., Just Accepted Manuscript • DOI: 10.1021/acs.jafc.7b02526 • Publication Date (Web): 23 Aug 2017 Downloaded from http://pubs.acs.org on August 23, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of Agricultural and Food Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

Journal of Agricultural and Food Chemistry

Multimodal GRAS ZnO/nano-Copper composite: A novel antimicrobial material for the management of citrus phytopathogens Mikaeel Young1, 2, Ali Ozcan1, 3, Monty E. Myers5, Evan G. Johnson6 James H. Graham6, * and Swadeshmukul Santra1, 2, 3, 4,*

1

NanoScience Technology Center, 2Burnett School of Biomedical Sciences, 3Department of Chemistry and 4Department of Materials Science and Engineering

University of Central Florida, 12424 Research Parkway, Suite 400, Orlando, FL 32826, USA E-mail: [email protected] (Santra) 5

Indian River Research and Education Center, University of Florida, 2199 South Rock Road, Fort Pierce, Florida 34945, USA 6

Citrus Research and Education Center, University of Florida, 700 Experiment Road, Lake Alfred, FL 33850, USA. E-mail: [email protected] (Graham)

1 ACS Paragon Plus Environment


1

Abstract

2

Copper (Cu) bactericides/fungicides are used extensively for crop protection in agriculture.

3

Concerns for Cu accumulation in soil, Cu leaching into the surrounding ecosystem and

4

development of Cu resistance in phytopathogenic bacteria are evident. While there is no suitable

5

alternative to Cu available to date for agricultural uses, it is possible to reduce Cu per application

6

by supplementing with Zn and improving Cu bioavailability using nanotechnology. We have

7

prepared a non-phytotoxic composite material consisting of GRAS (Generally Recognized As

8

Safe) ZnO 800 particles and nano-Copper loaded silica gel (ZnO-nCuSi). The morphology of the

9

ZnO-nCuSi material was characterized using SEM, showing ZnO particles dispersed in the silica

10

gel matrix. The ZnO-nCuSi demonstrated strong in-vitro antimicrobial properties against several

11

model plant bacterial species. Two consecutive year field efficacy results showed that agri-grade

12

ZnO-nCuSi was effective in controlling citrus canker disease at less than half the metallic rate of

13

the commercial cuprous oxide/zinc oxide pesticide.

14

Keywords: copper, silica gel, zinc oxide, nanotechnology, antimicrobial, citrus canker

15


Page 2 of 22

Page 3 of 22

16


Introduction

17

The citrus industry maintains a strong agricultural presence in the United States despite

18

setbacks from a variety of diseases including citrus canker and Huanglongbing (HLB, also known

19

as citrus greening). The United States produced more than 4.8 million tons of fresh oranges,

20

600,000 tons of grapefruit and 800,000 tons of tangerine/mandarin in 2016-2017

21

(http://www.fas.usda.gov/ psdonline/circulars/citrus.pdf). Even though new challenges are rising,

22

technological improvements to protect against infection are at a slower pace. Copper (Cu) based

23

pesticides continue to be the most commonly used formulation for crop protection. Cu exhibits

24

antimicrobial properties only at higher concentration (>50 µM) 1, and it is an essential

25

micronutrient for many organisms including plants and animals 2. Copper bactericides/fungicides

26

are the most frequently used metal-based crop protectants for managing bacterial and fungal

27

diseases of a wide variety of crops including citrus, vegetables, stone fruit, legumes, cereals, pome

28

fruit and berries

29

plague citrus industries worldwide. Application rates and frequency interval of foliar spray vary

30

per crop as well as climate conditions. In Florida citrus groves, citrus crops receive approximately

31

5-15 applications per season, starting from March through October 6-7. Long-term usage of Cu has

32

created numerous limitations: (i) soil Cu accumulation over time that reduces uptake of other

33

essential elements such as Zn, (ii) development of Cu resistance to target microbial species 8-9 and

34

(iii) higher risk of Cu toxicity to the target crop and non-target soil microbiome.

2-4

. Citrus canker, caused by Xanthomonas citri subsp. citri (Xcc)5 continues to

35

Most marketable Cu products such as Cu oxides, Cu hydroxides, Cu oxychlorides have limited

36

solubility in water and therefore form a water-stable film after foliar application. Low solubility

37

greatly minimizes the risk of phytotoxicity but also diminishes Cu bioavailability. In contrast,

38

soluble forms of Cu such as Cu chelates, Cu salts have higher bioavailability but may cause severe 3 ACS Paragon Plus Environment


39

phytotoxicity if applied at the rate of film-forming Cu. To address these limitations of Cu

40

phytotoxicity and bioavailability, we have developed a composite of GRAS (Generally

41

Recognized as Safe) Zinc oxide-nano-Copper silica gel (ZnO-nCuSi) following a modified version

42

of our previously published copper silica gel

43

materials including TiO2, silica particles, graphene oxide and carbon nanoparticles demonstrate

44

the strong potential for nanomaterials in agriculture for crop protection and pathogen detection 11-

45

12

46

protection. However, recent innovations are promoting the development of ZnO as an

47

antimicrobial due to its ability to release antimicrobial Zn ions 11, 13. ZnO nanoparticles are being

48

investigated for the potential role it may play in agriculture to improve crop nutrient and production

49

14-15

50

possess antimicrobial properties. The copper silica gel coating will additionally serve as a reservoir

51

for both soluble and insoluble Cu compounds.

10

. In the last decade, a series of next generation

. ZnO has traditionally been used as a fertilizer but not labeled as bactericides/fungicides for crop

. The ZnO-nCuSi is therefore a multi-modal antimicrobial system as both copper and zinc

52

We hypothesize that the ZnO-nCuSi will display different modes of action due to the presence

53

of both Cu and Zn. As a result, it is possible to reduce the amount of Cu per application without

54

compromising overall efficacy. Less Cu per application will reduce Cu loading into the

55

environment.

56 57

Materials and Methods

58

Materials

59

All chemicals were reagent grade and used without any further purification. Copper sulfate

60

pentahydrate was purchased from CQ Concepts (Ringwood, IL), resazurin sodium salt from Sigma 4 ACS Paragon Plus Environment

Page 4 of 22

Page 5 of 22


61

(St. Louis, MO, USA). Sodium hydroxide, sodium silicate and phosphate-buffered saline (PBS)

62

were obtained from Fisher Scientific (Pittsburgh, PA). Zinc oxide (ZnO) 800 was received as a

63

sample from Zinc oxide LLC (Dickson, TN). De-ionized (DI) water was obtained from Nanopure

64

water purifier (Barnstead, model # D11911). Nutrient broth (NB) broth and nutrient agar (NA)

65

were purchased from Fluka (St. Louis, MO, USA) while Brain Heart Infusion (BHI) broth and

66

agar were purchased from B-D Chemical Co., Inc. (Greenwood Village, CO). Xanthomonas

67

alfalfae subsp. citrumelonis (ATCC 49120), Pseudomonas syringae pv. syringae (ATCC 19310)

68

and Clavibacter michiganensis subsp. michiganensis (ATCC 10202) was acquired from ATCC

69

(U.S. Department of Agriculture permits P526P-12-04060 and P526P-15-01601).

70 71

ZnO-nCuSi synthesis

72

The ZnO-nCuSi was synthesized based on our previous core-shell research with

73

modifications 16. Material synthesis was carried out at room temperature under an overhead stirrer

74

(Arrow 6000, Arrow Engineering) to make large volumes for field trials. Briefly, 1.14 kg of copper

75

sulfate pentahydrate was first dissolved in 5.0 L of deionized water to create a solution in a 5 gallon

76

bucket. After 20 minutes of stirring at 600 rpm, the pH of the solution was raised to ~7 using 1M

77

sodium hydroxide. This solution was allowed to stir for an additional 20 minutes before adding

78

100 mL of 37% sodium silicate. Separately, 285 g of ZnO 800 was dispersed into 5L of deionized

79

and stirred at 600 rpm with an overhead stirrer. The first bucket containing the copper silica

80

solution was allowed to stir for at least 4 hr before the dispersed ZnO solution was completely

81

added to it. The combined solution was raised to a volume of 11.3 L with deionized water and left

82

to stir overnight. The ZnO-nCuSi composite was created with a ratio of metallic Cu:Zn of 1:0.8.

83

ZnO-nCuSi was compared against commercial cuprous oxide/ zinc oxide which contains a metallic 5 ACS Paragon Plus Environment


84

Cu:Zn of 1:1. The approximate metallic Cu concentration is estimated at 25,675 µg/mL along with

85

a metallic Zn concentration of 20,177 µg/mL. The ZnO-nCuSi was used as synthesized (no

86

purification steps were involved to mimic an industrially-viable process for bulk scale production).

87 88

ZnO-nCuSi characterization

89

The viscosity of ZnO-CuSi was determined using a Fungilab Lead One viscometer with a

90

L1 spindle, while the pH and specific gravity were determined with a Mettler Toledo pH meter

91

and balance respectively. Characterization of ZnO-nCuSi was carried out using Field Emission

92

Scanning Electron Microscopy (SEM; Zeiss Ultra-55 FEG) and High Resolution Transmission

93

Electron Microscopy (HR-TEM; FEI Tecnai F30 TEM) techniques. SEM samples were drop cast

94

onto mica wafers while TEM samples were drop cast onto ultra-thin carbon coated gold TEM

95

grids. Structure and morphology of ZnO-nCuSi materials was studied using SEM and HRTEM

96

imaging techniques. SEM and HRTEM studies were conducted at the Advanced Materials and

97

Processing Analysis Center - Materials Characterization Facility (AMPAC-MCF) at the University

98

of Central Florida.

99 100

ZnO-nCuSi antimicrobial studies

101

The antimicrobial properties of the ZnO-nCuSi were evaluated by determining the

102

Minimum Inhibitory Concentration (MIC). Samples were tested against Gram-negative

103

Xanthomonas alfalfae subsp. citrumelonis strain F1 (ATCC 49120, a citrus canker surrogate),

104

Gram-negative Pseudomonas syringae pv. syringae (ATCC 19310, causative agent of bacterial

105

speck in lilac, almond, apricots, peaches and wild beans among others) and Gram-positive

106

Clavibacter michiganensis subsp. michiganensis (ATCC 10202, causative agent of bacterial wilt 6 ACS Paragon Plus Environment

Page 6 of 22

Page 7 of 22


107

and canker in tomato). X. alfalfae and P. syringae were maintained on NA and NB while C.

108

michiganensis was grown with BHI medium. All bacteria were grown at 26 ºC. ZnO-nCuSi was

109

compared to copper silica gel, ZnO 800, cuprous oxide/zinc oxide, copper hydroxide (commercial

110

industry standard) and copper sulfate (commercial industry standard).

111 112 113

Minimum Inhibitory Concentration (MIC)

114

The MIC values of ZnO-nCuSi along with controls including copper silica gel, ZnO 800,

115

Copper sulfate and copper hydroxide. MIC was carried out using broth microdilution in

116

accordance with the guidelines of the Clinical and Laboratory Standards Institute (CLSI) 17. The

117

accuracy of the MIC determination was improved by adding 10 μL of resazurin dye (0.0125 %

118

w/v) per 100 μL well volume and observing color changes (blue to pink for live organisms). The

119

suitability of this assay was validated for ZnO-nCuSi containing opaque solutions.

120 121

Phytotoxicity Studies

122

Plant tissue safety as evaluated in a Panasonic Environmental Test Chamber (Model MLR-

123

352H) which allowed for controlled day/night cycling temperatures, light intensity and humidity

124

to simulate summer weather conditions (temperature > 80 °F, humidity 60−80%, biocide

125

application season). Studies conducted on tomato the model fruit plant and Vinca sp. an ornamental

126

plant. Treatments were applied early in the morning and results were assessed after 72 hr as

127

previously published 18.



Page 8 of 22

128 129

‘Ruby’ grapefruit citrus canker trial

130

In 2015 and 2016, a field trial was conducted with 8 and 9-year-old non-bearing ‘Ruby’

131

grapefruit trees in Ft. Pierce, St. Lucie County, FL. The ZnO-nCuSi was applied at a foliar spray

132

of 0.22 Kg/ha metallic Cu and compared with commercial controls cuprous oxide (1.12 Kg/ha Cu)

133

and cuprous oxide/zinc oxide (0.5 and 1.01 Kg/ha Cu). It was found previously by the authors and

134

others that a rate of 0.5-1.0 Kg/ha Cu is sufficient to achieve strong disease suppression as higher

135

rates such as >2.0 Kg/ha did not significantly reduce canker infection further

136

spacing was 3.65 m x 7.62 m (360 trees per ha). The experimental design was a randomized

137

complete block design with multiple treatments replicated 5 times in blocks of five contiguous

138

trees. The untreated check (UTC) trees received a water-only spray treatment at each foliar spray

139

time. Materials were mixed with water and applied as foliar sprays at 3.0 L per tree with a handgun

140

sprayer at 1380 kPa of air pressure. During the 2015 trial, treatments were initiated after the spring

141

flush and were sprayed at roughly 21 day intervals on 4/14, 5/5, 5/26, 6/16, 7/7, 7/28, 8/18, 9/8,

142

9/28 and 10/6. Disease evaluation was on 11/02/15. During the 2016 trial, the same methodology

143

for treatment was applied with treatments sprayed on 4/19, 5/10, 5/31, 6/20, 7/11, 8/1, 8/22, 9/12,

144

10/10 and 10/24. Disease evaluation was on Nov 14. Disease incidence: the incidence of fruit with

145

canker lesions was assessed for 100 fruit per treatment from the middle 3 trees in each plot. Lesions

146

were classified as “old” if they were larger than 0.6 mm in diameter, coalescing with surrounding

147

lesions, black in color, exuding gum or had a prominent yellow halo; and “young” if lesions were

148

smaller than 0.6 cm in diameter, brown in color, and were not coalescing with surrounding lesions.

149

Disease severity was rated for each fruit based on the estimated number of old or young lesions:

150

1= 0 lesions, 2= 1-5 lesions, 3= 6-20 lesions, 4= 21 or more lesions. Monthly rainfall in 2014 was 8 ACS Paragon Plus Environment

13, 19-21

. The tree

Page 9 of 22


151

recorded at University of Florida/ IFAS, Indian River Research and Education Center, Ft. Pierce,

152

FL

153

(http://fawn.ifas.ufl.edu/). The monthly rainfall was compared to the average for the last 10 years.

site,

and

obtained

from

the

Florida

Automated

Weather

Network

website

154 155

Results and Discussion

156

Determination of basic formulation characteristics such as pH, specific gravity and

157

viscosity along with the active ingredient characterization is important for developing a

158

commercially viable product. The pH of ZnO-nCuSi formulation was 9.85, which is comparable

159

to Cu hydroxide based industry standards. The specific gravity and viscosity were determined to

160

be 1.14 and ~18.8 mPa/s, respectively (Table 1). The size, morphology and state of dispersion of

161

ZnO-nCuSi were observed through electron microscopy. The ZnO core material was irregular,

162

mostly rod-like (600-1100 nm) in size and fairly dispersed (Figure 1, Panel A). In contrast, the

163

ZnO-nCuSi composite appeared irregular in shape. Particle size was in the multi-micron range.

164

Dispersibility of the composite was somewhat compromised due to neutralization of surface

165

charge at pH 7.0 (Figure 1, Panel B). HRTEM images (Figure 1, Panel C and D) further

166

supported the ZnO-nCuSi morphology as seen under SEM. The ZnO particles appeared in the

167

darker contrast relative to the silica gel matrix. As shown in Figure 1, Panel D, Cu crystallites

168

measuring 3-6 nm were seen embedded in the silica gel. Average lattice spacing between crystal

169 170

planes was calculated. Values were determined as ∼2.32,∼1.87, ∼2.47, and ∼3.02 Å to reveal Cu

171

The in-vitro antimicrobial efficacy of the ZnO-nCuSi was evaluated by determining the

172

MIC against multiple model phytopathogens. Efficacy of ZnO-nCuSi was significantly higher

173

compared to ZnO 800, cuprous oxide/zinc oxide, copper silica gel, copper hydroxide and copper

crystallites of cupric oxide and cuprous oxide 22.



Page 10 of 22

174

sulfate (MIC results are shown in Table 2). The superior antimicrobial activity of ZnO-nCuSi over

175

cuprous oxide/zinc oxide demonstrates that the metals in ZnO-nCuSi are more bioavailable than

176

in the other formulations.

177

Phytotoxicity testing was conducted for ZnO-nCuSi compared to copper hydroxide,

178

cuprous oxide/ zinc oxide, copper sulfate and copper silica gel. Copper sulfate exhibited severe

179

toxicity while the other tested compounds showed no phytotoxicity except cuprous oxide/zinc

180

oxide at 1000 µg/mL Cu (Table 3).

181

In the 2015 and 2016 citrus canker trials (conducted in Fort Pierce, FL on ‘Ruby’

182

grapefruit), ZnO-nCuSi was more efficacious for control of canker incidence on fruit than cuprous

183

oxide, copper sulfate and cuprous oxide/zinc oxide. The average rainfall was higher in 2016 than

184

in 2015, which can explain the increase in disease incidence in the untreated control (UTC)

185

between the trials (Table 4). Both years exhibited higher rainfall over the ten year average. During

186

2015, ZnO-nCuSi reduced incidence of fruit infection to 25% from 60% in the untreated control

187

and compared to cuprous oxide (29%), copper sulfate (25%) and cuprous oxide/ zinc oxide (21-

188

23 %). ZnO-nCuSi was more effective at a significantly lower metallic Cu rate than the other

189

treatments containing Cu (Table 5). During the 2016 trial, ZnO-nCuSi reduced canker incidence

190

from 93% to 58% compared to cuprous oxide (56%) and cuprous oxide/zinc oxide (56%) while

191

being applied at a significantly lower metallic Cu rate (Table 5). During the 2015 and 2016 trials,

192

ZnO-nCuSi activity against fungal diseases, citrus scab and melanose was also assessed. The

193

results indicate that ZnO-nCuSi control was comparable to commercial Cu controls at lower

194

metallic rates (Table 6).

195 196

The improved protective ability of ZnO-nCuSi points to the parallel antimicrobial modes of action exhibited by zinc and copper. Zinc oxide induces oxidative stress 10 ACS Paragon Plus Environment

23

while cupric and

Page 11 of 22


197

cuprous oxide have been shown to cause protein inactivation

198

membrane integrity through potential disruption 26. Our results confirm the hypothesis that multi-

199

modal approach is effective in maintaining efficacy against canker infection at lower Cu

200

application rate. The present ZnO-nCuSi composite formulation contains 25,450 µg/mL metallic

201

Cu along with 20,000 µg/mL metallic Zn and the process is scalable.

24

, DNA damage25 and loss of

202

ZnO-nCuSi has the potential to become a competing technology due to its several attractive

203

attributes: GRAS, low-cost, commercially-viable synthesis process, EPA acceptable actives and

204

inerts, reduced Cu exposure in the environment and most importantly strong field efficacy. Future

205

studies will be conducted to ascertain the exact mechanistic effect exerted by the multi-modal

206

ZnO-nCuSi upon plant pathogens to elucidate its bactericidal activity.

207 208

Acknowledgment

209

We acknowledge the Materials Characterization Facility (MCF) at the UCF Advanced

210

Materials and Processing Analysis Center (AMPAC) where SEM and TEM analysis were

211

conducted. We acknowledge financial support from the Florida Department of Citrus (Grant 186)

212

and the Citrus Research and Development Foundation, Inc. (Grants 328 and 544).

213 214

References

215 216 217 218 219 220

1. Outten, F. W.; Huffman, D. L.; Hale, J. A.; O'Halloran, T. V., The independent cue and cusSystems confer copper tolerance during aerobic and anaerobic growth inEscherichia coli. J. Biol. Chem. 2001, 276 (33), 30670-30677. 2. Borkow, G.; Gabbay, J., Copper as a Biocidal Tool. Curr. Med. Chem. 2005, 12 (18), 2163-2175. 3. Kiely, T.; Donaldson, D.; Grube, A. Pesticide industry sales and usage: 2000 and 2001 market estimates; U.S EPA: Washington, DC, 2004.



221 222 223 224 225 226 227 228 229 230 231 232 233 234 235 236 237 238 239 240 241 242 243 244 245 246 247 248 249 250 251 252 253 254 255 256 257 258 259 260 261 262 263 264 265 266 267

4. Pavlovic, M., A review of Agribusiness copper Use effects on environment. Bulg J Agric Sci 2011, 17 (4), 491-500. 5. Schaad, N. W.; Postnikova, E.; Lacy, G.; Sechler, A.; Agarkova, I.; Stromberg, P. E.; Stromberg, V. K.; Vidaver, A. K., Emended classification of xanthomonad pathogens on citrus. Syst. Appl. Microbiol. 2006, 29 (8), 690-695. 6. Behlau, F.; Belasque Jr, J.; Bergamin Filho, A.; Graham, J. H.; Leite Jr, R. P.; Gottwald, T. R., Copper sprays and windbreaks for control of citrus canker on young orange trees in southern Brazil. Crop Prot. 2008, 27 (3–5), 807-813. 7. Behlau, F.; Belasque Jr, J.; Graham, J. H.; Leite Jr, R. P., Effect of frequency of copper applications on control of citrus canker and the yield of young bearing sweet orange trees. Crop Prot. 2010, 29 (3), 300-305. 8. Behlau, F.; Canteros, B. I.; Minsavage, G. V.; Jones, J. B.; Graham, J. H., Molecular characterization of copper resistance genes from Xanthomonas citri subsp. citri and Xanthomonas alfalfae subsp. citrumelonis. Appl. Environ. Microbiol. 2011, 77 (12), 4089-4096. 9. Behlau, F.; Hong, J. C.; Jones, J. B.; Graham, J. H., Evidence for acquisition of copper resistance genes from different sources in citrus-associated xanthomonads. Phytopathology 2013, 103 (5), 409418. 10. Young, M.; Santra, S., Copper (Cu)–Silica nanocomposite containing valence-engineered Cu: a new strategy for improving the antimicrobial efficacy of Cu biocides. J. Agric. Food. Chem. 2014, 62 (26), 6043-6052. 11. Khot, L. R.; Sankaran, S.; Maja, J. M.; Ehsani, R.; Schuster, E. W., Applications of nanomaterials in agricultural production and crop protection: a review. Crop Prot. 2012, 35, 64-70. 12. Chen, J.; Peng, H.; Wang, X.; Shao, F.; Yuan, Z.; Han, H., Graphene oxide exhibits broad-spectrum antimicrobial activity against bacterial phytopathogens and fungal conidia by intertwining and membrane perturbation. Nanoscale 2014, 6 (3), 1879-1889. 13. Graham, J.; Johnson, E.; Myers, M.; Young, M.; Rajasekaran, P.; Das, S.; Santra, S., Potential of Nano-Formulated Zinc Oxide for Control of Citrus Canker on Grapefruit Trees. Plant Dis. 2016, 100 (12), 2442-2447. 14. Anderson, A. J.; McLean, J. E.; Jacobson, A. R.; Britt, D. W., CuO and ZnO Nanoparticles Modify Interkingdom Cell Signaling Processes Relevant to Crop Production. J. Agric. Food. Chem. 2017. 15. Zhao, L.; Peralta-Videa, J. R.; Rico, C. M.; Hernandez-Viezcas, J. A.; Sun, Y.; Niu, G.; Servin, A.; Nunez, J. E.; Duarte-Gardea, M.; Gardea-Torresdey, J. L., CeO2 and ZnO Nanoparticles Change the Nutritional Qualities of Cucumber (Cucumis sativus). J. Agric. Food. Chem. 2014, 62 (13), 2752-2759. 16. Maniprasad, P.; Santra, S., Novel copper (Cu) loaded core–shell silica nanoparticles with improved Cu bioavailability: Synthesis, characterization and study of antibacterial properties. J. Biomed. Nanotechnol. 2012, 8 (4), 558-566. 17. CLSI, Methods for Dilution Antimicrobial Susceptibility Tests for Bacteria That Grow Aerobically;Approved Standard-Ninth Edition. In CLSI Document M07-A9, Clinical and Laboratory Standards Institute: Wayne, PA, 2012. 18. Rajasekaran, P.; Kannan, H.; Das, S.; Young, M.; Santra, S., Comparative analysis of copper and zinc based agrichemical biocide products: materials characteristics, phytotoxicity and in vitro antimicrobial efficacy. AIMS Environ. Sci. 2016, 3 (3), 439-455. 19. Behlau, F.; Scandelai, L. H. M.; da Silva Junior, G. J.; Lanza, F. E., Soluble and insoluble copper formulations and metallic copper rate for control of citrus canker on sweet orange trees. Crop Prot. 2017, 94, 185-191. 20. Graham, J.; Dewdney, M.; Myers, M. In Streptomycin and copper formulations for control of citrus canker on grapefruit, Proc. Fla. State Hortic. Soc, 2010; pp 92-99.


Page 12 of 22

Page 13 of 22

268 269 270 271 272 273 274 275 276 277 278


21. Graham, J.; Dewdney, M.; Yonce, H. In Comparison of copper formulations for control of citrus canker on ‘Hamlin’orange, Proc. Fla. State Hortic. Soc, 2011; pp 79-84. 22. Data, I. c. f. D., Powder Diffraction File Search Manual. In Inorganic, JCPDS: PA.USA, 1984. 23. Xie, Y.; He, Y.; Irwin, P. L.; Jin, T.; Shi, X., Antibacterial activity and mechanism of action of zinc oxide nanoparticles against Campylobacter jejuni. Appl. Environ. Microbiol. 2011, 77 (7), 2325-2331. 24. Macomber, L.; Imlay, J. A., The iron-sulfur clusters of dehydratases are primary intracellular targets of copper toxicity. Proc. Natl. Acad. Sci. U. S. A. 2009, 106 (20), 8344-8349. 25. Aruoma, O. I.; Halliwell, B.; Gajewski, E.; Dizdaroglu, M., Copper-ion-dependent damage to the bases in DNA in the presence of hydrogen peroxide. Biochem. J 1991, 273 (3), 601-604. 26. Santo, C. E.; Quaranta, D.; Grass, G., Antimicrobial metallic copper surfaces kill Staphylococcus haemolyticus via membrane damage. Microbiologyopen 2012, 1 (1), 46-52.

279



Figure Captions Figure 1: (A) SEM image of ZnO 800 core material used in the synthesis of ZnO-nCuSi material, displaying irregular was generally rod-like sub-micron shape and size. (B) SEM image of The ZnO-nCuSi after the ZnO 800 has been coated with a copper silica shell. HRTEM images in the low magnification (C) and (D) high magnification of the ZnO-nCuSi. The more electron dense ZnO are seen in the darker contrast to the silica gel in (C). Cu crystallites seen in (D) measured between 3-6 nm.


Page 14 of 22

Page 15 of 22


Tables pH

9.85

Specific gravity

1.14

Viscosity (mPa/s)

18.78 ± 0.84

Table 1: Properties of ZnO-nCuSi MIC ( µg/mL metallic Cu or Zn) Xanthomonas

Pseudomonas

Clavibacter

alfalfae subsp.

syringae pv.

michiganensis subsp.

citrumelonis

syringae

michiganensis

(ATCC 49120)

(ATCC 19310)

(ATCC 10202)

16-31 (Cu),

31-62 (Cu),

31-62 (Cu),

13-26 (Zn)

26-52 (Zn)

26-52 (Zn)

ZnO 800

125

125

62-125

Copper silica gel

125-250

125-250

125-250

Cuprous oxide/

62-125 (Cu),

125-250 (Cu),

125 (Cu),

zinc oxide

62-125 (Zn)

125-250 (Zn)

125 (Zn)

Copper hydroxide

250-500

250

125-250

Copper sulfate

125-250

250

125-250

Material

ZnO-nCuSi

Table 2: MIC of ZnO-nCuSi demonstrates stronger in-vitro bactericidal activity compared with either ZnO 800 compound or copper silica gel alone, indicating at least an additive effect.



Page 16 of 22

Material Tested

Vinca sp

Tomato sp

Untreated Control (H2O)

-

-

Copper sulfate at 1000 µg/mL

+++

+++

Copper hydroxide at 1000 µg/mL

-

-

Cuprous oxide/ zinc oxide at 500 µg/mL

-

-

Cuprous oxide/ zinc oxide at 1000 µg/mL

+

+

ZnO 800 at 500 µg/mL

-

-

ZnO 800 at 1000 µg/mL

-

-

Copper silica gel at 500 µg/mL

-

-

Copper silica gel at 1000 µg/mL

-

-

ZnO-nCuSi at 500 µg/mL

-

-

ZnO-nCuSi at 1000 µg/mL

-

-

(+++), (++), (+) – Severe, Moderate or low toxicity. (-) – Zero toxicity Table 3: Phytotoxicity analysis demonstrates both ZnO-nCuSi and its components are not toxic to plant tissue compared to soluble and insoluble copper compounds.


Page 17 of 22


Monthly rainfall (mm)

March

April

May

June

July

Aug.

Sept.

Oct

2015

41

124

19

239

193

152

254

51

2016

89

66

231

119

109

236

145

102

Ft. Piercez average

64

58

84

168

173

165

150

97

Trial Year

z

Average monthly rainfall from 2000-2010 obtained from FAWN at IRREC

Table 4: Rainfall at Indian River FAWN station, 2016



Page 18 of 22

Metallic

Incidence

Incidence

Total incidence

Cu (kg/ha)

old lesions (%)

young lesions (%)

(%)

Treatment

2015 Untreated check (UTC)

-

23 a

37 a

60 a

Cuprous oxide

1.12

10 cde z

20 b z

29 c z

Copper sulfate

0.16

16 bc

8.8 c

25 cd

0.5

8.2 cde

13 bc

21 defg

1.01

9.0 cde

14 bc

23 def

0.22

11 cde

14 bc

25 cd

Untreated check (UTC)

-

50 a

43 a

93 a

Cuprous oxide

1.12

28 ef z

28 cdef z

56 def z

0.5

30 def

27 def

56 def

1.01

30 def

27 def

56 def

0.22

29 def

30 bcde

58 de

Cuprous oxide/Zinc oxide Cuprous oxide/Zinc oxide

ZnO-nCuSi 2016


ZnO-nCuSi z

Treatments followed by unlike letters are significantly different at P ≤ 0.05 according to StudentNewman-Keuls multiple range test


Page 19 of 22


Table 5: Effect of ZnO-nCuSi on incidence of citrus canker-infected fruit with old lesions, young lesions and total incidence of lesions on 8 and 9 year-old ‘Ray Ruby’ grapefruit trees, Ft. Pierce, FL, USA.

Metallic Treatment

Melanose

Burn

Incidence (%)

Incidence (%)

Scab incidence (%) Cu (kg/ha)

2015 Untreated check (UTC)

-

25.4 a

12.2 a

0.0

Cuprous oxide

1.12

2.4 d z

1.0 b z

0.0

Copper sulfate

0.16

3.4 bcd

4.6 b

0.0

0.5

2.2 d

1.0 b

0.0

1.01

2.4 d

1.6 b

0.0

0.22

5.4 b

4.0 b

0.0

Untreated check (UTC)

-

17.92 a

22.08 a

0.0

Cuprous oxide

1.12

5.56 fg

6.04 fgh

0.0

0.5

6 efg

5.08 h

0.0

1.01

5.4 fg

5.2 gh

0.0

0.22

7.84 cdef

7.64 def

0.0


ZnO-nCuSi 2016


ZnO-nCuSi



z

Page 20 of 22

Treatments followed by unlike letters are significantly different at P ≤ 0.05 according to StudentNewman-Keuls multiple range test

Table 6: Effect of ZnO-nCuSi on incidence of scab and melanose on fruit of 8 and 9 yr-old ‘Ray Ruby’ grapefruit trees, Ft. Pierce, USA, October 2016 Figure Graphics Figure 1


Page 21 of 22


TOC Graphic

For Table of Contents Only



244x116mm (96 x 96 DPI)

ACS Paragon Plus Environment

Page 22 of 22