Aqueous Aggregation Behavior of Engineered Superparamagnetic

Nov 4, 2016 - (3) As described by our lab and others, a highly effective oleic acid bilayer stabilizing strategy was incorporated to facilitate the tr...
0 downloads 10 Views 2MB Size
Subscriber access provided by University of Otago Library

Article

Aqueous Aggregation Behavior of Engineered Superparamagnetic Iron Oxide Nanoparticles: Effects of Oxidative Surface Aging Wenlu Li, Seung Soo Lee, Anjuliee M. Mittelman, Di Liu, Jiewei Wu, Carl H Hinton, Linda M. Abriola, Kurt D Pennell, and John D. Fortner Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.6b04130 • Publication Date (Web): 04 Nov 2016 Downloaded from http://pubs.acs.org on November 7, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 34

Environmental Science & Technology

1

Aqueous Aggregation Behavior of Engineered

2

Superparamagnetic Iron Oxide Nanoparticles:

3

Effects of Oxidative Surface Aging

4

Wenlu Li, † Seung Soo Lee, † Anjuliee M. Mittelman, §Di Liu, † Jiewei Wu, † Carl H. Hinton, †

5

Linda M. Abriola, § Kurt D. Pennell, §and John D. Fortner*, †

6 7 8 9



Department of Energy, Environmental and Chemical Engineering, Washington University in St. Louis, St. Louis, MO 63130, USA §

Department of Civil and Environmental Engineering, Tufts University, Medford, MA 02155, USA

10 11

Submitted to

12

Environmental Science and Technology

13

2016

14 15

*To whom correspondence should be addressed:

16

John D. Fortner: Tel: +1-314-935-9293; Fax: +1-314-935-5464; Email: [email protected]

ACS Paragon Plus Environment

1

Environmental Science & Technology

Page 2 of 34

17

ABSTRACT

18

For successful aqueous-based applications, it is necessary to fundamentally understand and

19

control nanoparticle dispersivity and stability over a range of dynamic conditions, including

20

variable ionic strengths/types, redox chemistries, and surface ligand reactivity/degradation states

21

(i.e. surface aging). Here, we quantitatively describe the behavior of artificially aged, oleic acid

22

(OA) bilayer coated iron oxide nanoparticles (IONPs) under different scenarios. Hydrogen

23

peroxide (H2O2), used here as a model oxidant under both dark and light ultra-violet (UVA)

24

conditions, was employed to ‘age’ materials, to varying degrees, without increasing ionic

25

strength. Short-term stability experiments indicate that OA-IONPs, while stable in the dark, are

26

effectively de-stabilized when exposed to UVA/H2O2/OH based oxidation processes. Compared

27

to bicarbonate, phosphate (1.0 mM) has a net stabilizing effect on OA-IONPs under oxidative

28

conditions, which can be attributed to (surface-based) functional adsorption. Corresponding

29

aggregation kinetics in the presence of monovalent (Na+) and divalent cations (Ca2+) show that

30

attachment efficiencies (α) are strongly dependent on the cation concentrations/types and degree

31

of surface aging. Taken together, our findings directly highlight the need to understand the

32

critical role of particle surface transformation(s), via oxidative aging, among other routes, with

33

regard to the ultimate stability and environmental fate of surface functionalized engineered

34

nanoparticles.

ACS Paragon Plus Environment

2

Page 3 of 34

Environmental Science & Technology

35

KEYWORDS

36

Engineered

37

aggregation, nanoparticle stability, nanoparticle aging, surface oxidation

nanomaterials,

superparamagnetic

iron

oxide

nanoparticles,

nanoparticle

ACS Paragon Plus Environment

3

Environmental Science & Technology

38

Page 4 of 34

INTRODUCTION

39

The development and production of engineered iron oxide nanoparticles (IONPs) are

40

motivated by their broad material applications in biomedical research, high-capacity data

41

storage, advanced drug delivery, magnetic resonance imaging (MRI), magnetic separations,

42

environmental sensing, and remediation technologies, among others.1-11 For engineered

43

nanomaterials with large surface-to-volume ratio and high surface energies in water, surface

44

modification is required to avoid (or reduce) aggregation, (surface) attachment, and

45

sedimentation phenomena.1,

46

including ligand addition and/or ligand exchange (e.g., stabilizing agents coated onto

47

nanoparticle surfaces), which can alter wettability, surface charge, and hydrophobicity, thus

48

enhancing the monomeric stability of nanoparticles.3, 5, 15-17 For example, Tombácz et al. found

49

that, at a moderate surface coverage (1-2 mmol/g), carboxylated (e.g., citric acid, gallic acid, and

50

poly(acrylic acid)) magnetite nanoparticles have a critical coagulation concentration (CCC) of

51

approximately 500 mM NaCl compared to the CCC of 1 mM NaCl for bare magnetite.18 Our

52

previous work demonstrated that engineered oleic acid bilayer coated iron oxide nanoparticles

53

(OA-IONPs) have relatively high CCC values of 710 mM NaCl and 10.2 mM CaCl 2 at neutral

54

pH.3 For these types of particles, ligands are strongly adsorbed onto particle surfaces through

55

either physisorption or chemisorption, whereby the adsorption process is irreversible and/or the

56

desorption process is minor under relevant conditions.19 However, desorption or degradation of

57

attached ligands may occur in the environment under more reactive or extreme conditions.6, 20

5, 6, 12-14

This can be accomplished via a number of methods,

58

Upon inadvertent release to and/or intended applications within environmental systems, such

59

nanoparticles may be exposed to reductive or oxidative surface reactions, including photo-

60

catalyzed reactions.4,

20-24

Surface reactions leading to particle destabilization in water,

ACS Paragon Plus Environment

4

Page 5 of 34

Environmental Science & Technology

61

specifically particle-particle aggregation and surface deposition processes, will likely play a

62

critical role in the material’s behavior over time and, in the case of technical applications, will

63

also affect performance regimes.16,

64

surface aging processes of nanomaterials is key to predicting the ultimate material fate and

65

transport behavior, and thus the environmental volume/endpoints affected.4,

66

Typically, for charge stabilized particles, elevated ionic strengths can compress the (particle

67

surface) electrical double layer, thus lowering the energy barrier required for aggregation and/or

68

surface deposition. Noting that the critical coagulation concentration (CCC) of our

69

aforementioned OA-IONPs is much higher than the concentration of common cations found in

70

typical surface waters, it may be expected that these (and other similar) nanoparticles can remain

71

stable for extended periods of time.3 In such scenarios, particle surface reactions, including

72

oxidation processes and potential sunlight irradiation (photo-enhanced chemistries), are likely to

73

affect ultimate particle stabilities. Sun et al. observed that the stability of TiO2 nanoparticles

74

decreased more than 27-fold, as measured by aggregation rates, following 50 h of UV irradiation,

75

which was attributed to the changes in surface hydroxyl groups.25 Conversely, when nC60

76

nanoparticles were subjected to extensive UVA irradiation (up to 7 days), their stability (in the

77

presence of NaCl) increased significantly due to an effective increase in surface charge.30 A

78

recent study by Li et al. demonstrated that surfactant coated (PVP and citrate) Ag NPs show

79

enhanced colloidal stability compared to bare Ag NPs under natural solar irradiation and UV

80

irradiation, highlighting the importance of surface passivation with regard to stability,

81

dissolution, and photo-transformation.31

20, 24-27

In the case of inadvertent release, understanding

6, 20, 26, 28, 29

82

The objective of this study is to elucidate the effect of (UVA) light irradiation and chemical

83

oxidation on the stability of OA-IONPs under varied water chemistries. Short-term stabilities of

ACS Paragon Plus Environment

5

Environmental Science & Technology

Page 6 of 34

84

these nanoparticles was quantitatively investigated in the presence of two ubiquitous aqueous

85

buffers, bicarbonate and phosphate, as a function of irradiation time, cation type, and ionic

86

strength using time-resolved dynamic light scattering (TR-DLS). The organic aging products

87

were further probed via gas chromatography–mass spectrometry (GC-MS) and Fourier transform

88

infrared spectroscopy (FTIR) analyses. Lastly, we explore and propose a simplified aging

89

mechanism/pathway through (artificially) synthesizing and evaluating a model product (mixed

90

bilayer coatings) for comparison. To our knowledge, this is the first study to describe the short-

91

term stability and aggregation behaviors of engineered OA-IONPs upon exposure to

92

environmentally relevant oxidative aging conditions. Findings highlight the importance of

93

recognizing and understanding particle surface aging as it relates to the environmental fate and

94

transport of engineered nanoparticles.

95

MATERIALS AND METHODS

96

Materials: Iron(III) oxide (hydrated, catalyst grade), 1-octadecene (technical grade, 90%),

97

oleic acid (technical grade, 90%), sodium chloride (ACS reagent, ≥99.0%), calcium chloride

98

dihydrate (ACS reagent, ≥99%), sodium hydroxide (ACS reagent, ≥97.0%), sodium bicarbonate

99

(ACS reagent, 99.7-100.3%), sodium phosphate dibasic (ACS reagent, ≥99%), sodium phosphate

100

monobasic (ReagentPlus, ≥99.0%), hydrogen peroxide solution (TraceSELECT, ≥30%) and

101

nitric acid (trace metal grade) were purchased from Sigma-Aldrich. Reagent grade ethanol,

102

acetone and hexane were used as received without further purification.

103

Preparation and Characterization of OA-IONPs: Monodisperse IONPs were first

104

synthesized by high temperature pyrolysis of iron carboxylate salts in the presence of organic

105

solvent.2 To prepare 8 nm IONPs, 2 mmol FeO(OH) fine powder, 2 mmol oleic acid, and 5 g 1-

106

octadecene (1-ODE) were mixed intensively in a three-necks flask under ultra pure argon. The

ACS Paragon Plus Environment

6

Page 7 of 34

Environmental Science & Technology

107

mixture was then heated gradually (5-10 °C/min) to 240 °C to dissolve the FeO(OH) and further

108

heated to 320 °C to decompose the iron carboxylate salts formed in the previous procedure. The

109

reaction was maintained at 320 °C for 1-3 h before removing the heating mantle. After cooling

110

down to room temperature, the black colloid was purified with a standard hexane/acetone

111

procedure five times.2 Purified IONPs were transferred and stored in hexane. In order to disperse

112

the synthesized IONPs into water, an oleic acid bilayer (surface) structure was employed, as

113

described previously.3, 32 Approximately 20 µL of pure oleic acid was added to 1 mL of IONPs

114

in hexane and the mixture was sonicated for 1 min using a bath sonicator (Branson 2510,

115

Danbury, CT), followed by the addition of 10 mL of ultrapure water (Millipore, 18.2 MΩcm). A

116

probe sonicator (Qsonica, Q-700, Taperd microtip, 2 mm) was then utilized for extensive mixing

117

of the hexane and water phases at 50% amplitude for 5-10 min. Through a fast centrifugation

118

(6,000 g) step, the sonicated emulsion was separated into two phases with nanoparticles in the

119

bottom water phase. The aqueous phase was then collected and the nanoparticles were purified

120

via centrifugation, redispersion, and filtration through a syringe filer (polyethersulfone, pore size

121

of 0.2 µm, Millipore).

122

Nanoparticle Characterization: The size and morphology of IONPs and OA-IONPs were

123

characterized by transmission electron microscopy (TEM, FEI Tecnai G2 Spirit) operated at 120

124

kV. A small drop (10-20 µL) of suspension was placed on a carbon-coated copper grid (300

125

mesh, Electron Microscopy Sciences) and dried under N2 flow. In order to calculate the size

126

distribution of IONPs, randomly chosen nanoparticles (> 2,000) from several different TEM

127

micrographs were selected and analyzed using ImageJ software (National Institutes of Health).

128

To determine the iron concentration in samples, the IONPs were digested using concentrated

129

nitric acid and analyzed by inductively coupled plasma mass spectrometry (ICP-MS, Agilent

ACS Paragon Plus Environment

7

Environmental Science & Technology

Page 8 of 34

130

7500ce). The concentration of the water stable OA-IONPs stock suspension was measured and

131

set to 100 mg/L as Fe. The hydrodynamic diameter and zeta potential of OA-IONPs were

132

measured by dynamic light scattering (DLS) with a He-Ne laser operated at the wavelength of

133

633 nm (Zetasizer, Malvern Nano ZS, Malvern, UK). All size and zeta potential measurements

134

were conducted in triplicate at room temperature (22 °C).

135

UV Initiated Reactions: UVA light was used to mimic the actual sunlight exposure in real

136

environmental systems. A custom build UV-reactor equipped with two UV lamps (351 nm, BHK

137

Inc. CA) was used to achieve a total irradiation intensity of 2000 ± 50 mW/cm2 in the middle of

138

the reactor, as measured by a radiometer (UVP, Inc. CA). Ambient air was circulated through the

139

photo-reactor to maintain the temperature at 22 °C. For each experiment, 50 mL of 8nm OA-

140

IONPs solution was added to a 100 mL quartz vial (Technical Glass Products, OH). The final

141

concentration of OA-IONPs was 50 mg/L as Fe. Varied amounts of H2O2 were then added to

142

initiate oxidative aging reactions. H2O2 was used as a model oxidant as it does not increase the

143

ionic strength of the system and thus eliminates potential aggregation of nanoparticles by the

144

oxidant (which also acts as an ion) itself. Bicarbonate and phosphate buffers were used to adjust

145

the initial pH to 7.5 and the reactions were allowed to run continuously for 7 days. Samples were

146

collected periodically and evaluated for size, zeta potential, and particle stability. Control

147

experiments were conducted by wrapping samples with aluminum foil to avoid exposure to light

148

irradiation. UV-Vis spectra (200-800 nm) of the samples containing H2O2 were analyzed by

149

using a Varian Cary Bio50 UV-Visible spectrometer. The concentration of H2O2 was determined

150

by TiSO4 spectrophotometry at low concentrations following methods described previously.33, 34

151

Solvated products were analyzed using attenuated total reflection Fourier transform infrared

152

spectroscopy (Nexus 470 FTIR, Thermo Nicolet, NC) with a ZnSe trough. Liquid samples in the

ACS Paragon Plus Environment

8

Page 9 of 34

Environmental Science & Technology

153

trough were dried under vacuum at room temperature for one day. The transmittance spectra

154

were recorded from 800-3600 cm-1 with spectral resolution of 1 cm-1. Aging products were

155

extracted and analyzed by GC-MS (Hewlett Packard model 7890A, Agilent Technologies)

156

equipped with a DB5-MS column (J&W Scientific) and a mass spectrometer (5975C, Agilent

157

Technologies). The GC program was as follows, the column was equilibrated at 80 °C for 1 min,

158

then ramped to 280 °C at 30 °C/min, and was held at constant temperature for 3 min. The mass

159

spectra of the products were analyzed using Enhanced Data Analysis software (Agilent

160

Technologies).

161

Aggregation Kinetics: DLS measurements were carried out using a Nano ZS Zetasizer

162

(Malvern Instruments, UK) equipped with a photodetector at a fixed scattering angle of 173°.

163

The OA-IONPs stock solution was diluted to 1 mg/L for the DLS experiments and pH was

164

adjusted to 7.5. For each measurement, a predetermined volume of diluted nanoparticle

165

suspension was added into a polystyrene vial. After that, a certain amount of electrolyte stock

166

solution was injected into the vial to a total sample volume of 1 mL. After vortexing (1.5 s),

167

samples were immediately transferred to the DLS chamber and measured. Size measurements

168

were collected every 15 s and recorded continuously from 20 to 60 min, depending on the

169

aggregation rate of each sample.

170

The attachment efficiency (α) of the OA-IONP aggregates in the presence of various

171

electrolyte concentrations was calculated by the following equation35-37 where k is the initial

172

aggregation rate constant at any salt concentration, kfast is the aggregation rate constant under

173

diffusion-limited (fast) aggregation conditions, N0 is the initial particle concentration and Dh(t) is

174

the intensity-weighted hydrodynamic diameter of nanoparticles at time t.

ACS Paragon Plus Environment

9

Environmental Science & Technology

175

Page 10 of 34

(1)

176

Fast aggregation rate constants in diffusion-limited regimes can be calculated under relatively

177

high ionic strengths (above the CCC point). In reaction-limited regimes (i.e., below the CCC), an

178

increase in electrolyte concentration will further compress the electric double layer, thus

179

decreasing the electrostatic repulsion forces between nanoparticles and promoting particle

180

aggregation. The CCC refers to the point at which the energy barrier to aggregation is effectively

181

screened. Above the CCC, the addition of electrolyte will fully destabilize the nanoparticles and

182

the aggregation becomes solely dependent on the number of particle collisions: this is referred to

183

as the diffusion-limited regime. At points above the CCC, the aggregation rate becomes

184

independent of salt concentration and the attachment efficiency is equal to 1. Nanoparticles with

185

a lower CCC are more prone to aggregation and thus exhibit a low degree of stability compared

186

to nanoparticles with a high CCC in the same electrolyte solutions. CCC values are often used to

187

directly compare and predict the stability of nanoparticles in real or simulated environmental

188

scenarios.4

189

Phosphate Sorption: OA-IONPs (50 ppm as Fe) were analyzed for phosphate sorption at

190

phosphate concentrations ranging from 0 to 1200 mg/L as PO43-. The solution pH was adjusted

191

with HNO3 and/or NaOH to pH 7.5. After 48 h of equilibrium, OA-IONPs were separated using

192

ultracentrifugation at 60,000 g for 2 h and the remaining concentrations of phosphate in the

193

supernatant solution were analyzed by an inductively coupled plasma optical emission

194

spectroscopy (ICP-OES, Perkin Elmer Optima 7300DV). All measurements were conducted in

195

triplicate. The measured phosphate sorption capacity as a function of equilibrium concentration

196

of phosphate (mg/L) was fit using the Langmuir isotherm equation:

ACS Paragon Plus Environment

10

Page 11 of 34

Environmental Science & Technology

197

(2)

198

where qe is the amount of adsorbed phosphate at equilibrium concentration (mg/g), k is the

199

sorption constant, qmax is the maximum sorption density (mg/g, mass of the sorbed phosphate per

200

mass of Fe), and Ce is the equilibrium concentration of phosphate.

201

RESULTS AND DISCUSSION

202

Characterization of IONPs

203

Highly monodispersed, spherical IONPs were synthesized by thermal decomposition of iron

204

precursor (iron carboxylate) in an organic solvent at 320 °C, as reported previously.2, 8 TEM

205

micrographs of 8 nm (8.1 ± 0.6 nm) IONPs are shown in Figure 1a. These engineered

206

nanoparticles are highly reproducible while remaining single domain, single crystalline, and

207

highly monodispersed with a very narrow size distribution (Figure 1b).3 As described by our lab

208

and others, a highly effective oleic acid bilayer stabilizing strategy was incorporated to facilitate

209

the transfer of IONPs from the organic phase (hexane) into water.3, 14, 32 Corresponding TEM

210

micrographs (Figure 1c) show aqueous transferred IONPs remain monodisperse with no core

211

size and shape change.32 The number-weighted hydrodynamic diameter of the OA-IONPs was

212

measured to be 16.2 ± 1.8 nm for the 8 nm IONPs cores dispersed in hexane, which is similar to

213

the value we have reported before for these materials (15.6 ± 1.3 nm).3 OA-IONPs aqueous

214

suspensions are colloidally stable for over 6 months with negligible change in hydrodynamic

215

diameter.14

216

Short-term Colloidal Stability of OA-IONPs

217

The average hydrodynamic diameter of OA-IONPs as a function of time (7 days) in the

218

presence of bicarbonate or phosphate and H2O2 is shown in Figure 2. Bicarbonate and phosphate

219

are two common anions in both surface and ground waters, albeit at different concentrations (10-

ACS Paragon Plus Environment

11

Environmental Science & Technology

Page 12 of 34

220

3

to 10 mN for HCO3- and < 10-5 mN for HPO42-).38 Their concentrations can be found up to 1.5

221

mM in wastewater.39 H2O2, a naturally occurring oxidant,40 was used as a model oxidant to avoid

222

introducing additional ionic strength into the system (upon redox reactions). For (dark) control

223

experiments (Figure 2a), OA-IONPs remain highly stable with negligible size change over the

224

entire 7 days except in the presence of 10 mM phosphate, whereby the hydrodynamic diameter

225

slightly increased to ca. 30 nm due to the reduced energy barrier to aggregation at elevated ionic

226

strength, consistent with classic Derjaguin–Landau–Verwey–Overbeek (DLVO) theory.22

227

Colloidal stability of parallel OA-IONPs solution under UVA irradiation is shown in Figure 1b.

228

In the presence of bicarbonate, OA-IONPs are quasi-stable under direct UVA irradiation for up

229

to 4 days in the absence of H2O2, with the hydrodynamic diameter increasing from ca. 20 nm to

230

ca. 50 nm at the end of 7 days. Corresponding TEM micrographs of the aged nanoparticles (7

231

day UVA exposure) also show the formation of small clusters (SI Figure S1b). The addition of

232

H2O2 was found to promote the destabilization of the nanoparticles. With 0.03 wt. % of H2O2,

233

OA-IONPs are severely destabilized, forming larger flocs, and settle out from the solution after 5

234

days (reaching an average size of > 500 nm). The addition of a higher concentration of H2O2

235

(0.12 wt. %) accelerates the destabilization process, with nanoparticles completely settling out

236

from solution upon ca. 4 days of UVA irradiation. After 7 days of UVA irradiation, the OA-

237

IONPs were no longer monodispersed and formed aggregate flocs visible to the naked eye under

238

both conditions, as depicted in SI Figure S1. The shape and size of OA-IONPs were evaluated

239

before and after aging via TEM micrographs; results indicate the existence of large OA-IONPS

240

aggregates, while primary nanoparticle shape and size does not change. This observation was

241

further confirmed by the ICP-OES results, as no substantial dissolved (released) iron was

ACS Paragon Plus Environment

12

Page 13 of 34

Environmental Science & Technology

242

observed for any of the aging scenarios under neutral pH conditions (SI Figure S2), indicating

243

minimal (particle core) dissolution during surface aging processes.21

244

The colloidal stability of OA-IONPs under UVA irradiation was investigated in the presence

245

phosphate concentrations of 0.1 mM, 1.0 mM, and 10 mM. Results indicate that 1.0 mM

246

phosphate effectively stabilizes OA-IONPs upon 7 days of UVA irradiation without the addition

247

of H2O2, while the hydrodynamic diameter of OA-IONPs only moderately increases in the

248

presence of 0.1 mM and 10 mM phosphate under the same conditions (Figure 2b). Similar to

249

observations from parallel bicarbonate experiments, the addition of H2O2 also promotes the

250

destabilization of OA-IONPs under UVA irradiation, but to a relatively lesser extent. The

251

effective rate of particle size increase (or rate of destabilization) is slower in the presence of

252

phosphate buffer when compared to bicarbonate buffered systems. The presence of phosphate

253

ions inhibits the decomposition of H2O2 and thus enhancing the stabilizing effect (SI Figure

254

S3).33 Additionally, in the presence of 10 mM tert-butanol (t-BuOH), a highly efficient hydroxyl

255

radical scavenger,29, 41, 42 the size of OA-IONPs modestly increased from ca. 20 nm to ca. 30 nm

256

under UVA irradiation for 7 days. This final particle hydrodynamic diameter after 7 days was

257

relatively small compared to that observed in the absence of t-BuOH, indicating hydroxyl

258

radicals generated from UVA (photo)oxidation may be involved in the NPs destabilization

259

process(es). It is expected that other oxygen reactive species (e.g., peroxides, superoxide, and

260

singlet oxygen) may also possibly contribute to this process as well; however, the exact

261

combination of oxidation/degradation mechanisms remain unclear and will be further

262

investigated in future reports. Taken together, results show that a phosphate buffer concentration

263

of 1.0 mM (higher than typical surface water background concentrations) provided the greatest

ACS Paragon Plus Environment

13

Environmental Science & Technology

Page 14 of 34

264

stabilizing effect for OA-IONPs during UVA/H2O2 irradiation when compared to bicarbonate

265

and t-BuOH under neutral pH condition.

266

Aggregation Kinetics of Pristine and Aged OA-IONPs

267

Aggregation kinetics of OA-IONPs before and after aging were evaluated as a function of

268

ionic strength and composition using TR-DLS. The hydrodynamic diameter increase (through

269

aggregation processes) of pristine OA-IONPs over time in the presence of varied NaCl and

270

CaCl2 concentrations is shown in the SI Figure S4. We observe aggregation rates increase from

271

0.89 nm/min to 12.69 nm/min when NaCl concentration was correspondingly increased from 100

272

mM to 700 mM. However, at higher NaCl concentrations (1000 and 1400 mM), the increase in

273

electrolyte concentration did not affect the aggregation rate, as the energy barrier was effectively

274

eliminated, indicating a maximum aggregation rate has been reached. Similar behavior was

275

observed in the presence of CaCl2 (SI Figure S4b), albeit at lower concentrations (1-50 mM).

276

Calculated attachment efficiencies (α) of OA-IONPs, before and after aging, in the presence of

277

NaCl and CaCl2 are presented in Figure 3. For these systems, aggregation kinetics can be

278

classically divided into two regimes: reaction-limited (where α is less than 1) and diffusion-

279

limited aggregation (where α is equal to 1). By extrapolating the reaction limited and diffusion

280

limited regimes, the critical coagulation concentration (CCC) can be derived. For these systems,

281

distinct reaction-limited and diffusion-limited regime observations indicate that particle

282

aggregation before and after aging follows classical DLVO theory. In each of the experiments,

283

the CCC decreases as UVA irradiation time was increased. CCC values of OA-IONPs were 763

284

mM, 507 mM, 381 mM, and 174 mM NaCl for samples irradiated for 0h (pristine OA-IONPs),

285

10 h, 1 d, and 3d, respectively. Similar trends were observed with CaCl2; however, due to charge

286

neutralization and surface complexation effects, divalent cations, such as Ca2+, are more effective

ACS Paragon Plus Environment

14

Page 15 of 34

Environmental Science & Technology

287

in reducing the surface charge, resulting in lower CCC values compared to monovalent cations

288

(Na+).35, 43 CCC values of OA-IONPs in CaCl2 were 10.4 mM, 9.3 mM, 8.2 mM, and 5.8 mM for

289

samples irradiated for 0 h, 10 h, 1 d, and 3 d, respectively. Decreasing CCC values indicate

290

destabilization effects from extended periods of UVA irradiation: calculated CCC ratios for Ca2+

291

to Na+ are 2-6.2 for pristine OA-IONPs and 2-5.8, 2-5.5, and 2-4.9 for samples irradiated for 10 h, 1 d,

292

and 3d, respectively. These power terms generally follow the theoretical Schulze-Hardy rule,

293

where the ratio of CCC values is proportional to z-6 to z-2 depending on the zeta potential value

294

of the material (z is the valence of counterion).44

295

Attachment efficiencies (α) of OA-IONPs as a function of electrolyte type upon 3 day (UVA)

296

aging in the presence of phosphate and carbonate buffers are shown in Figure 4. In the presence

297

of monovalent electrolyte (NaCl), OA-IONPs aged in bicarbonate buffer solution have a

298

relatively low CCC value of 174 mM compared to the CCC value (249 mM) of OA-IONPs aged

299

in phosphate buffer (under parallel conditions). However, in the presence of a divalent

300

electrolyte (CaCl2), OA-IONPs aged in bicarbonate buffer have a relatively higher CCC value

301

(5.8 mM) compared to OA-IONPs aged in phosphate buffer (3.0 mM). At neutral pH,

302

bicarbonate and phosphate ions exist as HCO3- and H2PO4-, respectively. While the adsorption of

303

bicarbonate anions onto the OA-IONPs was not anticipated, phosphate anions demonstrate

304

favorable sorption onto the surface of OA-IONPs (SI Figure S5).45 The adsorption of phosphate

305

onto OA-IONPs likely alters surface charge/access, leading to relatively higher CCC values

306

(more stable).46 Ren et al. has reported the enhanced stabilization of graphene oxide (GO) in the

307

presence of strongly adsorbing phosphate anion (H2PO4-) due to increased electrostatic repulsion

308

and charge screening of monovalent cation (Na+).46 In the case of calcium, we hypothesize that

309

the additional phosphate sorbed onto OA-IONPs forms inner sphere complexes with calcium

ACS Paragon Plus Environment

15

Environmental Science & Technology

Page 16 of 34

310

cations, further promoting particle-particle aggregation, as described by others.47, 48 The CCC

311

ratio of Ca2+ to Na+ is 2-6.4 for OA-IONPs aged in phosphate buffer for 3 days. The power term is

312

larger than that for pristine OA-IONPs (6.2) and the sample aged in bicarbonate buffer (4.9).

313

This discrepancy in aggregation behavior for OA-IONPs aged in phosphate buffer can be

314

attributed to the interactions between Ca2+ and the nanoparticle surface, presumably with either

315

carboxyl or phosphate groups, as discussed above.27, 30

316

Zeta potentials of pristine and aged OA-IONPs (3 days UVA irradiation) are plotted as a

317

function of NaCl and CaCl2 in Figure 5. As the electrolyte concentration is increased, the zeta

318

potential of all three samples becomes less negative, due to charge screening effects. Comparison

319

of the zeta potentials for pristine and aged OA-IONPs shows that pristine OA-IONPs exhibits

320

higher absolute zeta potential values in the presence of NaCl or CaCl2, which is consistent with

321

higher CCC values. The reduction of apparent zeta potential for aged particles suggests a surface

322

potential change during aging processes. Further, zeta potential values indicate that the divalent

323

calcium cation is more effective at neutralizing surface charge, which is in agreement with

324

results from prior aggregation kinetic studies.49

325

Proposed Aging Mechanisms/Pathway

326

Alterations in the surface coating chemistry of OA-IONPs before and after aging were further

327

analyzed using ATR-FTIR spectroscopy. The spectra of pure oleic acid, IONPs in hexane,

328

pristine OA-IONPs, aged OA-IONPs in bicarbonate, and aged OA-IONPS in phosphate are

329

presented in Figure 6. Pure oleic acid exhibited strong symmetric and asymmetric –CH2 stretch

330

bands at 2923 and 2854 cm-1 (Figure 6a).50-52 The intense peak shown at 1710 cm-1 is derived

331

from the asymmetric –C=O stretch and the band at 1285 cm-1 is attributed to C–O stretch.50, 51, 53

332

The O–H in plane and out-of-plane bands appear at 1460 and 935 cm-1, respectively.50, 51 For

ACS Paragon Plus Environment

16

Page 17 of 34

Environmental Science & Technology

333

IONPs dispersed in hexane, similar symmetric and asymmetric –CH2 stretch bands at 2923 and

334

2854 cm-1 are observed, respectively.50 The characteristic band at 1710 cm-1 for oleic acid is

335

almost absent in the spectrum for IONPs dispersed in hexane, possibly from trace residue of free

336

oleic acid in the hexane.50 Compared with pure oleic acid, two new bands at 1590 and 1545 cm-1

337

in the spectrum of IONPs in hexane were characteristics of the asymmetric –COO- and the

338

symmetric –COO- stretches, respectively. The presence of these bands indicates the

339

complexation between the carboxylate group from oleic acid and the iron oxide surface.51, 52 This

340

confirms the attachment of first oleic acid layer on the surface of IONPs, as reported by others.50

341

As the peak of –C=O at 1710 cm-1 is a characteristic peak of free oleic acid, the resulting sharp

342

peak of –C=O for OA-IONPs was attributed to the free oleic acid from the outer (second) layer

343

of OA-IONPs.52, 53 The intensity of this peak, however, decreased when the OA-IONPs were

344

subjected to different aging conditions as seen in Figure 6d and 6e, indicating transformation of

345

the outer oleic acid layer during aging process. No new peaks were observed after the samples

346

were aged, and the only discernible functional group in the FTIR spectra was attributed to

347

carboxylate moiety. Taken together, FTIR results support an aging mechanism whereby the inner

348

coating layer was still fully/partially attached to the IONPs surface while the outer layer

349

underwent transformations during (photo)chemical oxidation processes.

350

During (photo)oxidation processes, oleic acid bilayer surface coatings on IONPs are likely

351

susceptible to transformation/degradation.54 Reactive oxygen species (ROS), such as hydroxyl

352

radicals, generated from UVA light and H2O2, can attack electron-rich double bonds (oxidative

353

cleavage of C=C double bond),12,

354

nonanal, 9-oxononanoic acid, nonanoic acid and azelaic acid.55,

355

process, molecular (organic) aging products were analyzed by GC-MS using Enhanced Data

55-58

resulting in a potential suite of products that include 59-65

To explore this aging

ACS Paragon Plus Environment

17

Environmental Science & Technology

Page 18 of 34

356

Analysis software (Agilent Technologies). As shown in Figure 7, nonanal was detected as a

357

major product with other identified fragments, such as heptanal, decane, octanal, 1-octanol, and

358

octanoic acid, confirming the degradation of oleic acid coatings during the oxidative aging

359

process.59, 62, 63, 66 No degradation products (from the surface coatings) were observed in the dark

360

control experiments.

361

As GC-MS and ATR-FTIR analyses along with previous TEM and ICP results indicate that

362

the aging process took place on the surface of the nanoparticles, a simplified reaction pathway

363

was proposed to mimic and evaluate, thus confirm, the aging process and resulting

364

materials/surfaces. For this, one of the major (identified) aging products from oleic acid,

365

nonanoic acid, was successfully used (in place of oleic acid) for the phase transfer of IONPs

366

from hexane into water. Thus, instead of an oleic acid bilayer structure, a layer of nonanoic acid

367

was added to the original layer of oleic acid on the nanoparticle surface, forming a mixed bilayer

368

structure, which is depicted in Figure 8). Aggregation kinetics studies were performed for these

369

model materials with CCC values observed at 47.4 mM for NaCl and 3.3 mM for CaCl2 (SI

370

Figure S6), which are considerably lower when compared CCC values of aged OA-IONPs in

371

bicarbonate (174 mM of NaCl and 5.8 mM of CaCl2) and phosphate (249 mM of NaCl and 3.0

372

mM of CaCl2) buffer, supporting the proposed aging mechanism. In this simplified model, we

373

only take into account the situation where the second layer first undergoes oxidative

374

transformation and converts to an ideal layer of nonanoic acid. However, we certainly recognize

375

that actual aging processes and resulting surface complexes will likely be more complicated, as

376

surface reactions could happen to both outer and inner layer(s), with remaining coating layers

377

existing as mixtures of different short-chain molecules with varying functional groups. It should

ACS Paragon Plus Environment

18

Page 19 of 34

Environmental Science & Technology

378

be expected that such alterations of surface coating structure/chemistry will likely subsequently

379

affect particle stabilities.

380

Environmental Implications

381

This study demonstrates that (organic) surfactant-coated IONPs can undergo dynamic surface

382

(photo)chemical oxidative transformations upon simple UVA irradiation and/or with ubiquitous

383

oxidants. Upon chemical aging, surface-functionalized nanoparticles exhibit considerably

384

different environmental behavior(s) compared to parent materials. OA-IONP stability is highest

385

in the presence of phosphate buffer, due to strong adsorption behavior of phosphate anions. The

386

degradation/transformations of surface coating(s) result in significant destabilization of

387

engineered particles, highlighting the sensitivity of nanoparticle behavior/transport to surface

388

coating type and stability (reactivity). These results also suggest that intentional exposure to

389

specific chemical conditions (e.g., oxidation) may be useful for controlled (mitigated) migration

390

of nanoparticles after their application lifespan is fulfilled. Further, natural organic matter

391

(NOM), which is ever-present in natural aquatic environments, will also likely alter surface

392

reaction/aggregation behavior of these and similar engineered nanoparticles, leading to varied

393

stability and environmental fate of these materials. Evaluating the (photo)oxidation process of

394

surfactant-coated engineered nanoparticles with real world waters, including NOM, is ongoing.

ACS Paragon Plus Environment

19

Environmental Science & Technology

Page 20 of 34

395 396

Figure 1. (a) TEM micrograph of the as-prepared 8 nm IONPs in hexane, scale bar is 50 nm, (b)

397

Histograms of as-prepared 8 nm IONPs in hexane, (c) TEM micrograph of the as-prepared 8 nm

398

OA-IONPs in water, and (d) number mean average size distribution of OA-IONPs in water as

399

measured by DLS.

ACS Paragon Plus Environment

20

Page 21 of 34

Environmental Science & Technology

400 401

Figure 2. Hydrodynamic diameters of OA-IONPs as a function of time: (a) control in the dark,

402

(b) under UVA irradiation. 50 ppm OA-IONP were present in 1.0 mM NaHCO3, 1.0 mM

403

NaHCO3 with 0.03 wt. % H2O2, 1.0 mM NaHCO3 with 0.12 wt. % H2O2, 0.1 mM phosphate, 1.0

404

mM phosphate, 10 mM phosphate, 1.0 mM phosphate with 0.03 wt. % H2O2, 1.0 mM phosphate

405

with 0.12 wt. % H2O2, and 10 mM t-BuOH, respectively.

ACS Paragon Plus Environment

21

Environmental Science & Technology

Page 22 of 34

406 407

Figure 3. Attachment efficiencies of pristine and aged OA-IONPs in bicarbonate buffer as

408

functions of (a) NaCl and (b) CaCl2 concentration. The critical coagulation concentration (CCC)

409

for pristine OA-IONPs, and OA-IONPs under UVA irradiation for 10h, 1 day, and 3 days were

410

763 mM, 507 mM, 381 mM, 174 mM for NaCl, and 10.4 mM, 9.3 mM, 8.2 mM, 5.8 mM for

411

CaCl2, respectively. CCC values are derived from the intersection between lines extrapolated

412

from the reaction-limited and diffusion-limited regimes.

ACS Paragon Plus Environment

22

Page 23 of 34

Environmental Science & Technology

413 414

Figure 4. Attachment efficiencies of pristine and aged OA-IONPs as functions of (a) NaCl and

415

(b) CaCl2 concentration. The critical coagulation concentration (CCC) for pristine OA-IONPs,

416

and OA-IONPs aged in bicarbonate and phosphate buffer were 763 mM, 174 mM, and 249 mM

417

for NaCl, and 10.4 mM, 5,8 mM, and 3.0 mM for CaCl2, respectively. CCC values are derived

418

from the intersection betweens lines extrapolated from the reaction-limited and diffusion-limited

419

regimes.

ACS Paragon Plus Environment

23

Environmental Science & Technology

Page 24 of 34

420 421

Figure 5. Zeta potentials of pristine and aged OA-IONPs as a function of (a) NaCl and (b) CaCl2

422

concentrations. Each data point was the average of 30 measurements from triplicate samples and

423

the error bars represent standard deviations.

ACS Paragon Plus Environment

24

Page 25 of 34

Environmental Science & Technology

424 425

Figure 6. FTIR spectra of (a) pure oleic acid; (b) IONPs in hexane; (c) pristine OA-IONPs; (d)

426

aged OA-IONPs in 1.0 mM bicarbonate buffer; and (e) aged OA-IONPs in 1.0 mM phosphate

427

buffer.

ACS Paragon Plus Environment

25

Environmental Science & Technology

Page 26 of 34

428 429

Figure 7. GC-MS analysis of organic aging products: (a) dark control in bicarbonate buffer, (b)

430

aged sample in 1.0 mM NaHCO3, (c) aged sample in 1.0 mM NaHCO3 with 0.03 wt. % H2O2,

431

(d) aged sample in 1.0 mM NaHCO3 with 0.12 wt. % H2O2, (e) dark control in phosphate buffer,

432

(f) aged sample in 1.0 mM phosphate, (g) aged sample in 1.0 mM phosphate with 0.03 wt. %

433

H2O2, and (h) aged sample in 1.0 mM phosphate with 0.12 wt. % H2O2.

ACS Paragon Plus Environment

26

Page 27 of 34

Environmental Science & Technology

434 435

Figure 8. Proposed (photo)oxidation-induced aging mechanism of OA-IONPs under UVA/H2O2

436

oxidation process. Oleic acid is oxidized by ROS and yield aldehyde and carboxylic acid

437

formations. In a simplified model, the oleic acid bilayer coated IONPs were transformed to

438

nonanoic acid-oleic acid mixed bilayer coated IONPs during this process.

ACS Paragon Plus Environment

27

Environmental Science & Technology

439

Page 28 of 34

ASSOCIATED CONTENT

440

Supporting Information. TEM micrographs and digital images of pristine and aged OA-

441

IONPs, soluble Fe concentration, H2O2 degradation process, aggregation profiles of OA-IONPs,

442

phosphate sorption onto OA-IONPs, and CCC values of nonanoic acid coated IONPs. These 6

443

figures are available free of charge via the Internet at http://pubs.acs.org.

444

AUTHOR INFORMATION

445

Corresponding Author

446

*To whom correspondence should be addressed:

447

John D. Fortner: Tel: +1-314-935-9293; Fax: +1-314-935-5464; Email: [email protected]

448

Funding Sources

449

The authors would like to thank the American Chemical Society’s Petroleum Research Fund

450

(#52640-DNI10) and the National Science Foundation (CBET, #1236653) for supporting this

451

work.

452

ACKNOWLEDGMENT

453

This work was supported by American Chemical Society’s Petroleum Research Fund (#52640-

454

DNI10) and the National Science Foundation (CBET, #1236653). TEM, DLS facilities were

455

provided by the Nano Research Facility (NRF) at Washington University in St. Louis, a member

456

of the National Nanotechnology Infrastructure Network (NNIN), which is supported by the

457

National Science Foundation under Grant No. ECS-0335765.

ACS Paragon Plus Environment

28

Page 29 of 34

Environmental Science & Technology

458

REFERENCES

459 460 461 462 463 464 465 466 467 468 469 470 471 472 473 474 475 476 477 478 479 480 481 482 483 484 485 486 487 488 489 490 491 492 493 494 495 496 497 498 499 500 501

1. Laurent, S.; Forge, D.; Port, M.; Roch, A.; Robic, C.; Vander Elst, L.; Muller, R. N., Magnetic Iron Oxide Nanoparticles: Synthesis, Stabilization, Vectorization, Physicochemical Characterizations, and Biological Applications. Chemical Reviews 2008, 108, (6), 2064-2110. 2. Yu, W. W.; Falkner, J. C.; Yavuz, C. T.; Colvin, V. L., Synthesis of monodisperse iron oxide nanocrystals by thermal decomposition of iron carboxylate salts. Chemical Communications 2004, (20), 2306-2307. 3. Li, W.; Liu, D.; Wu, J.; Kim, C.; Fortner, J. D., Aqueous Aggregation and Surface Deposition Processes of Engineered Superparamagnetic Iron Oxide Nanoparticles for Environmental Applications. Environmental Science & Technology 2014, 48, (20), 11892-11900. 4. Dwivedi, A. D.; Dubey, S. P.; Sillanpää, M.; Kwon, Y.-N.; Lee, C.; Varma, R. S., Fate of engineered nanoparticles: Implications in the environment. Coordination Chemistry Reviews 2015, 287, (0), 64-78. 5. Zhou, L.; Yuan, J.; Wei, Y., Core-shell structural iron oxide hybrid nanoparticles: from controlled synthesis to biomedical applications. Journal of Materials Chemistry 2011, 21, (9), 2823-2840. 6. Tang, S. C. N.; Lo, I. M. C., Magnetic nanoparticles: Essential factors for sustainable environmental applications. Water Research 2013, 47, (8), 2613-2632. 7. Xu, P.; Zeng, G. M.; Huang, D. L.; Feng, C. L.; Hu, S.; Zhao, M. H.; Lai, C.; Wei, Z.; Huang, C.; Xie, G. X.; Liu, Z. F., Use of iron oxide nanomaterials in wastewater treatment: A review. Science of The Total Environment 2012, 424, (0), 1-10. 8. Wenlu, L.; Seung Soo, L.; Jiewei, W.; Carl, H. H.; John, D. F., Shape and size controlled synthesis of uniform iron oxide nanocrystals through new non-hydrolytic routes. Nanotechnology 2016, 27, (32), 324002. 9. Li, W.; Mayo, J. T.; Benoit, D. N.; Troyer, L. D.; Lewicka, Z. A.; Lafferty, B. J.; Catalano, J. G.; Lee, S. S.; Colvin, V. L.; Fortner, J. D., Engineered superparamagnetic iron oxide nanoparticles for ultra-enhanced uranium separation and sensing. Journal of Materials Chemistry A 2016, 4, (39), 15022-15029. 10. Yavuz, C. T.; Prakash, A.; Mayo, J. T.; Colvin, V. L., Magnetic separations: From steel plants to biotechnology. Chemical Engineering Science 2009, 64, (10), 2510-2521. 11. Yavuz, C. T.; Mayo, J. T.; Yu, W. W.; Prakash, A.; Falkner, J. C.; Yean, S.; Cong, L. L.; Shipley, H. J.; Kan, A.; Tomson, M.; Natelson, D.; Colvin, V. L., Low-field magnetic separation of monodisperse Fe3O4 nanocrystals. Science 2006, 314, (5801), 964-967. 12. Ge, S.; Agbakpe, M.; Wu, Z.; Kuang, L.; Zhang, W.; Wang, X., Influences of Surface Coating, UV Irradiation and Magnetic Field on the Algae Removal Using Magnetite Nanoparticles. Environmental Science & Technology 2015, 49, (2), 1190-1196. 13. Gambinossi, F.; Mylon, S. E.; Ferri, J. K., Aggregation kinetics and colloidal stability of functionalized nanoparticles. Advances in Colloid and Interface Science 2015, 222, 332-349. 14. Li, W.; Hinton, C. H.; Lee, S. S.; Wu, J.; Fortner, J. D., Surface engineering superparamagnetic nanoparticles for aqueous applications: design and characterization of tailored organic bilayers. Environmental Science: Nano 2016, 3, (1), 85-93. 15. Saleh, N.; Kim, H.-J.; Phenrat, T.; Matyjaszewski, K.; Tilton, R. D.; Lowry, G. V., Ionic Strength and Composition Affect the Mobility of Surface-Modified Fe0 Nanoparticles in WaterSaturated Sand Columns. Environmental Science & Technology 2008, 42, (9), 3349-3355.

ACS Paragon Plus Environment

29

Environmental Science & Technology

502 503 504 505 506 507 508 509 510 511 512 513 514 515 516 517 518 519 520 521 522 523 524 525 526 527 528 529 530 531 532 533 534 535 536 537 538 539 540 541 542 543 544 545 546 547

Page 30 of 34

16. Saleh, N.; Sirk, K.; Liu, Y. Q.; Phenrat, T.; Dufour, B.; Matyjaszewski, K.; Tilton, R. D.; Lowry, G. V., Surface modifications enhance nanoiron transport and NAPL targeting in saturated porous media. Environ. Eng. Sci. 2007, 24, (1), 45-57. 17. Lattuada, M.; Hatton, T. A., Functionalization of Monodisperse Magnetic Nanoparticles. Langmuir 2007, 23, (4), 2158-2168. 18. Tombácz, E.; Tóth, I. Y.; Nesztor, D.; Illés, E.; Hajdú, A.; Szekeres, M.; L.Vékás, Adsorption of organic acids on magnetite nanoparticles, pH-dependent colloidal stability and salt tolerance. Colloids and Surfaces A: Physicochemical and Engineering Aspects 2013, 435, (0), 91-96. 19. Kim, H.-J.; Phenrat, T.; Tilton, R. D.; Lowry, G. V., Fe0 Nanoparticles Remain Mobile in Porous Media after Aging Due to Slow Desorption of Polymeric Surface Modifiers. Environmental Science & Technology 2009, 43, (10), 3824-3830. 20. Hotze, E. M.; Phenrat, T.; Lowry, G. V., Nanoparticle Aggregation: Challenges to Understanding Transport and Reactivity in the Environment. J. Environ. Qual. 2010, 39, (6), 1909-1924. 21. Lin, D. H.; Tian, X. L.; Wu, F. C.; Xing, B. S., Fate and Transport of Engineered Nanomaterials in the Environment. J. Environ. Qual. 2010, 39, (6), 1896-1908. 22. Petosa, A. R.; Jaisi, D. P.; Quevedo, I. R.; Elimelech, M.; Tufenkji, N., Aggregation and Deposition of Engineered Nanomaterials in Aquatic Environments: Role of Physicochemical Interactions. Environmental Science & Technology 2010, 44, (17), 6532-6549. 23. Chowdhury, I.; Hou, W.-C.; Goodwin, D.; Henderson, M.; Zepp, R. G.; Bouchard, D., Sunlight affects aggregation and deposition of graphene oxide in the aquatic environment. Water Research 2015, 78, (0), 37-46. 24. Cheng, Y.; Yin, L.; Lin, S.; Wiesner, M.; Bernhardt, E.; Liu, J., Toxicity Reduction of Polymer-Stabilized Silver Nanoparticles by Sunlight. The Journal of Physical Chemistry C 2011, 115, (11), 4425-4432. 25. Sun, J.; Guo, L.-H.; Zhang, H.; Zhao, L., UV Irradiation Induced Transformation of TiO2 Nanoparticles in Water: Aggregation and Photoreactivity. Environmental Science & Technology 2014, 48, (20), 11962-11968. 26. Lowry, G. V.; Gregory, K. B.; Apte, S. C.; Lead, J. R., Transformations of Nanomaterials in the Environment. Environmental Science & Technology 2012, 46, (13), 6893-6899. 27. Hua, Z.; Zhang, J.; Bai, X.; Ye, Z.; Tang, Z.; Liang, L.; Liu, Y., Aggregation of TiO2– graphene nanocomposites in aqueous environment: Influence of environmental factors and UV irradiation. Science of The Total Environment 2016, 539, 196-205. 28. Mittelman, A. M.; Fortner, J. D.; Pennell, K. D., Effects of ultraviolet light on silver nanoparticle mobility and dissolution. Environmental Science: Nano 2015, 2, (6), 683-691. 29. Wu, J.; Goodwin, D. G.; Peter, K.; Benoit, D.; Li, W.; Fairbrother, D. H.; Fortner, J. D., Photo-Oxidation of Hydrogenated Fullerene (Fullerane) in Water. Environmental Science & Technology Letters 2014, 1, (12), 490-494. 30. Qu, X.; Hwang, Y. S.; Alvarez, P. J. J.; Bouchard, D.; Li, Q., UV Irradiation and Humic Acid Mediate Aggregation of Aqueous Fullerene (nC60) Nanoparticles. Environmental Science & Technology 2010, 44, (20), 7821-7826. 31. Li, Y.; Zhang, W.; Niu, J.; Chen, Y., Surface-Coating-Dependent Dissolution, Aggregation, and Reactive Oxygen Species (ROS) Generation of Silver Nanoparticles under Different Irradiation Conditions. Environmental Science & Technology 2013, 47, (18), 1029310301.

ACS Paragon Plus Environment

30

Page 31 of 34

548 549 550 551 552 553 554 555 556 557 558 559 560 561 562 563 564 565 566 567 568 569 570 571 572 573 574 575 576 577 578 579 580 581 582 583 584 585 586 587 588 589 590 591 592 593

Environmental Science & Technology

32. Prakash, A.; Zhu, H.; Jones, C. J.; Benoit, D. N.; Ellsworth, A. Z.; Bryant, E. L.; Colvin, V. L., Bilayers as Phase Transfer Agents for Nanocrystals Prepared in Nonpolar Solvents. ACS Nano 2009, 3, (8), 2139-2146. 33. Watts, R. J.; Foget, M. K.; Kong, S.-H.; Teel, A. L., Hydrogen peroxide decomposition in model subsurface systems. Journal of Hazardous Materials 1999, 69, (2), 229-243. 34. Kong, S.-H.; Watts, R. J.; Choi, J.-H., Treatment of petroleum-contaminated soils using iron mineral catalyzed hydrogen peroxide. Chemosphere 1998, 37, (8), 1473-1482. 35. Huynh, K. A.; Chen, K. L., Aggregation Kinetics of Citrate and Polyvinylpyrrolidone Coated Silver Nanoparticles in Monovalent and Divalent Electrolyte Solutions. Environmental Science & Technology 2011, 45, (13), 5564-5571. 36. Chen, K. L.; Elimelech, M., Aggregation and Deposition Kinetics of Fullerene (C60) Nanoparticles. Langmuir 2006, 22, (26), 10994-11001. 37. Huangfu, X.; Jiang, J.; Ma, J.; Liu, Y.; Yang, J., Aggregation Kinetics of Manganese Dioxide Colloids in Aqueous Solution: Influence of Humic Substances and Biomacromolecules. Environmental Science & Technology 2013, 47, (18), 10285-10292. 38. Reinsch, B. C.; Forsberg, B.; Penn, R. L.; Kim, C. S.; Lowry, G. V., Chemical Transformations during Aging of Zerovalent Iron Nanoparticles in the Presence of Common Groundwater Dissolved Constituents. Environmental Science & Technology 2010, 44, (9), 34553461. 39. Zhu, X.; Nanny, M. A.; Butler, E. C., Effect of inorganic anions on the titanium dioxidebased photocatalytic oxidation of aqueous ammonia and nitrite. Journal of Photochemistry and Photobiology A: Chemistry 2007, 185, (2–3), 289-294. 40. Zepp, R. G.; Faust, B. C.; Hoigne, J., Hydroxyl radical formation in aqueous reactions (pH 3-8) of iron(II) with hydrogen peroxide: the photo-Fenton reaction. Environmental Science & Technology 1992, 26, (2), 313-319. 41. Fortner, J. D.; Kim, D.-I.; Boyd, A. M.; Falkner, J. C.; Moran, S.; Colvin, V. L.; Hughes, J. B.; Kim, J.-H., Reaction of Water-Stable C60 Aggregates with Ozone. Environmental Science & Technology 2007, 41, (21), 7497-7502. 42. Ma, J.; Graham, N. J. D., Degradation of atrazine by manganese-catalysed ozonation: Influence of humic substances. Water Research 1999, 33, (3), 785-793. 43. Chen, K. L.; Mylon, S. E.; Elimelech, M., Aggregation Kinetics of Alginate-Coated Hematite Nanoparticles in Monovalent and Divalent Electrolytes. Environmental Science & Technology 2006, 40, (5), 1516-1523. 44. Gregory, J., Particles in Water: Properties and Processes. 2006. 45. Daou, T. J.; Begin-Colin, S.; Grenèche, J. M.; Thomas, F.; Derory, A.; Bernhardt, P.; Legaré, P.; Pourroy, G., Phosphate Adsorption Properties of Magnetite-Based Nanoparticles. Chemistry of Materials 2007, 19, (18), 4494-4505. 46. Ren, X.; Li, J.; Tan, X.; Shi, W.; Chen, C.; Shao, D.; Wen, T.; Wang, L.; Zhao, G.; Sheng, G.; Wang, X., Impact of Al2O3 on the Aggregation and Deposition of Graphene Oxide. Environmental Science & Technology 2014, 48, (10), 5493-5500. 47. Nguyen, T. H.; Chen, K. L., Role of Divalent Cations in Plasmid DNA Adsorption to Natural Organic Matter-Coated Silica Surface. Environmental Science & Technology 2007, 41, (15), 5370-5375. 48. Zhang, X.; Yang, S., Nonspecific Adsorption of Charged Quantum Dots on Supported Zwitterionic Lipid Bilayers: Real-Time Monitoring by Quartz Crystal Microbalance with Dissipation. Langmuir 2011, 27, (6), 2528-2535.

ACS Paragon Plus Environment

31

Environmental Science & Technology

594 595 596 597 598 599 600 601 602 603 604 605 606 607 608 609 610 611 612 613 614 615 616 617 618 619 620 621 622 623 624 625 626 627 628 629 630 631 632 633 634 635 636 637 638 639

Page 32 of 34

49. Chowdhury, I.; Duch, M. C.; Mansukhani, N. D.; Hersam, M. C.; Bouchard, D., Colloidal Properties and Stability of Graphene Oxide Nanomaterials in the Aquatic Environment. Environmental Science & Technology 2013, 47, (12), 6288-6296. 50. Jaime, I.; Julio, M.; Mario, A.; María, G. B.; Pablo, T.; Josué, J.; Miguel, A. V., Synthesis and characterization of magnetite/PLGA/chitosan nanoparticles. Materials Research Express 2015, 2, (9), 095010. 51. Zhang, L.; He, R.; Gu, H.-C., Oleic acid coating on the monodisperse magnetite nanoparticles. Applied Surface Science 2006, 253, (5), 2611-2617. 52. Yang, K.; Peng, H.; Wen, Y.; Li, N., Re-examination of characteristic FTIR spectrum of secondary layer in bilayer oleic acid-coated Fe3O4 nanoparticles. Applied Surface Science 2010, 256, (10), 3093-3097. 53. Lee, S.-Y.; Harris, M. T., Surface modification of magnetic nanoparticles capped by oleic acids: Characterization and colloidal stability in polar solvents. Journal of Colloid and Interface Science 2006, 293, (2), 401-408. 54. Li, Y.; Niu, J.; Shang, E.; Crittenden, J., Photochemical Transformation and Photoinduced Toxicity Reduction of Silver Nanoparticles in the Presence of Perfluorocarboxylic Acids under UV Irradiation. Environmental Science & Technology 2014, 48, (9), 4946-4953. 55. Tedetti, M.; Kawamura, K.; Narukawa, M.; Joux, F.; Charrière, B.; Sempéré, R., Hydroxyl radical-induced photochemical formation of dicarboxylic acids from unsaturated fatty acid (oleic acid) in aqueous solution. Journal of Photochemistry and Photobiology A: Chemistry 2007, 188, (1), 135-139. 56. Haji, S.; Benstaali, B.; Al-Bastaki, N., Degradation of methyl orange by UV/H2O2 advanced oxidation process. Chemical Engineering Journal 2011, 168, (1), 134-139. 57. Choe, E.; Min, D. B., Chemistry and Reactions of Reactive Oxygen Species in Foods. Journal of Food Science 2005, 70, (9), R142-R159. 58. Liao, C.-H.; Gurol, M. D., Chemical Oxidation by Photolytic Decomposition of Hydrogen Peroxide. Environmental Science & Technology 1995, 29, (12), 3007-3014. 59. Stephanou, E. G.; Stratigakis, N., Oxocarboxylic and .alpha.,.omega.-dicarboxylic acids: photooxidation products of biogenic unsaturated fatty acids present in urban aerosols. Environmental Science & Technology 1993, 27, (7), 1403-1407. 60. Hearn, J. D.; Smith, G. D., Kinetics and Product Studies for Ozonolysis Reactions of Organic Particles Using Aerosol CIMS†. The Journal of Physical Chemistry A 2004, 108, (45), 10019-10029. 61. Grimm, R. L.; Hodyss, R.; Beauchamp, J. L., Probing Interfacial Chemistry of Single Droplets with Field-Induced Droplet Ionization Mass Spectrometry:  Physical Adsorption of Polycyclic Aromatic Hydrocarbons and Ozonolysis of Oleic Acid and Related Compounds. Analytical Chemistry 2006, 78, (11), 3800-3806. 62. Kieber, R. J.; Hydro, L. H.; Seaton, P. J., Photooxidation of triglycerides and fatty acids in seawater: Implication toward the formation of marine humic substances. Limnol. Oceanogr. 1997, 42, (6), 1454-1462. 63. Hung, H.-M.; Ariya, P., Oxidation of Oleic Acid and Oleic Acid/Sodium Chloride(aq) Mixture Droplets with Ozone:  Changes of Hygroscopicity and Role of Secondary Reactions. The Journal of Physical Chemistry A 2007, 111, (4), 620-632. 64. Kawamura, K.; Gagosian, R. B., Implications of [omega]-oxocarboxylic acids in the remote marine atmosphere for photo-oxidation of unsaturated fatty acids. Nature 1987, 325, (6102), 330-332.

ACS Paragon Plus Environment

32

Page 33 of 34

640 641 642 643 644 645

Environmental Science & Technology

65. Rathouský, J.; Kalousek, V.; Kolář, M.; Jirkovský, J.; Barták, P., A study into the selfcleaning surface properties—The photocatalytic decomposition of oleic acid. Catalysis Today 2011, 161, (1), 202-208. 66. Hung, H.-M.; Katrib, Y.; Martin, S. T., Products and Mechanisms of the Reaction of Oleic Acid with Ozone and Nitrate Radical. The Journal of Physical Chemistry A 2005, 109, (20), 4517-4530.

646 647

ACS Paragon Plus Environment

33

Environmental Science & Technology

648

Page 34 of 34

TOC

649

ACS Paragon Plus Environment

34