Atomically Dispersed Co and Cu on N-Doped Carbon for Reactions

Mar 22, 2018 - Atomically dispersed Co(II) cations coordinated to nitrogen in a carbon matrix (Co-N-C) catalyze oxidative dehydrogenation of benzyl al...
0 downloads 4 Views 3MB Size
Subscriber access provided by Kaohsiung Medical University

Atomically-Dispersed Co and Cu on N-doped Carbon for Reactions involving C-H Activation Jiahan Xie, James D. Kammert, Nicholas Kaylor, Jonathan Zheng, Eunjin Choi, Hien N. Pham, Xiahan Sang, Eli Stavitski, Klaus Attenkofer, Raymond R. Unocic, Abhaya K. Datye, and Robert J Davis ACS Catal., Just Accepted Manuscript • DOI: 10.1021/acscatal.8b00141 • Publication Date (Web): 22 Mar 2018 Downloaded from http://pubs.acs.org on March 22, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

1

Atomically-Dispersed Co and Cu on N-doped Carbon for

2

Reactions Involving C-H Activation

3 4

Jiahan Xie,a James Kammert,a Nicholas Kaylor,a Jonathan Zheng,a Eunjin Choi,a,b

5

Hien N. Pham,c Xiahan Sang,d Eli Stavitski,e

6

Klaus Attenkofer,e Raymond R. Unocic,d Abhaya K. Datye,c Robert J. Davis a,*

7 8

a: Department of Chemical Engineering, University of Virginia, 102 Engineers’ Way, PO Box

9

400741, Charlottesville, VA 22904-4741, United States

10

b: Department of Emerging Materials Science, Daegu Gyeongbuk Institute of Science

11

&Technology, Daegu, 42988, Republic of Korea

12

c: Department of Chemical and Biological Engineering and Center for Micro-Engineered

13

Materials, University of New Mexico, Albuquerque, NM 87131, United States

14

d: Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, TN

15

37831, United States

16

e: National Synchrotron Light Source II, Brookhaven National Laboratory, Upton, NY, 11976,

17

United States

18 19

*Author to whom correspondence is addressed

20

Phone: 1 - 434 - 924 - 6284

21

Email: [email protected]

22 23 24 25 1 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

26

Page 2 of 41

Abstract:

27

Atomically-dispersed Co(II) cations coordinated to nitrogen in a carbon matrix (Co-N-C)

28

catalyze oxidative dehydrogenation of benzyl alcohol in water, with a specific activity

29

approaching that of supported Pt nanoparticles. Whereas Cu(II) cations in N-doped carbon

30

also catalyze the reaction, they are about an order of magnitude less active compared to Co(II)

31

cations. Results from X-ray absorption spectroscopy suggest that oxygen is also bound to

32

N-coordinated Co(II) sites, but that it can be partially removed by H2 treatments at 523 – 750

33

K. The N-coordinated Co(II) sites remained cationic in H2 up to 750 K and these stable sites

34

were demonstrated to be active for propane dehydrogenation. In-situ characterization of Cu(II)

35

in N-doped carbon revealed that reduction of the metal in H2 started at about 473 K,

36

indicating a much lower thermal stability of Cu(II) in H2 relative to Co(II). The demonstrated

37

high catalytic activity and thermal stability of Co-N-C in reducing environments suggests this

38

material may have broad utility in a variety of catalytic transformations.

39 40

Key words:

41

Heterogeneous catalyst; C-H activation; Alcohol oxidation; Propane dehydrogenation;

42

Non-precious metal; N-doped carbon; in-situ XAS; Coordination environment.

43

2 / 40

ACS Paragon Plus Environment

Page 3 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

44

Introduction

45

The catalytic transformation of carbon feedstocks to liquid fuels and useful chemicals

46

usually involves the activation of C-H bonds, whether the feedstock source is petroleum,

47

natural gas or biomass.1–3 Precious-metal catalysts have been recognized for many years as

48

possessing the features needed to activate C-H bonds.4,5 However, high costs limit their

49

application in large-scale and distributed systems.6 Therefore, a strong motivation exists to

50

discover or engineer earth-abundant elements in chemical environments that catalyze desired

51

chemical transformations similar to those typical of precious metals. Recently, non-precious

52

metals confined in a nitrogen-containing carbon matrix (M-N-C) were developed for the

53

electro-catalytic oxygen reduction (ORR) and the water splitting reaction, in which

54

comparable activity and stability to the well-known Pt catalysts were observed.7–12

55

Considering its demonstrated redox activity, M-N-C catalysts were further applied in organic

56

reactions involving oxidative C-H activation at mild temperature (usually lower than 400 K),

57

such as dehydrogenation, coupling, esterification and nitrification.13–24

58

The M-N-C catalysts are commonly prepared by a high-temperature pyrolysis method,

59

which usually produces a variety of metal species simultaneously, such as exposed or

60

encapsulated metal nanoparticles along with the atomically-dispersed metals in a variety of

61

coordination environments. The co-existence of these different species complicates

62

investigations into the nature of the catalytically-active sites. Catalysts predominantly

63

containing atomically-dispersed Fe and Co, which also exhibited catalytic activity in ORR or

64

C-H activation, were utilized to study the coordination environment and chemical state

65

around the metal.17,19,22,25–44 Atomic dispersion of the metals on these catalysts has been

66

verified by aberration-corrected scanning transmission electron microscopy (AC-STEM) and

67

X-ray absorption spectroscopy (XAS). The chemical state and coordination environment

68

were also probed by XAS, along with X-ray photoelectron spectroscopy (XPS), Mössbauer 3 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 41

69

spectroscopy, electron energy loss spectroscopy (EELS) and density-functional theory

70

(DFT).17,19,30–32,34,38,39,41,43,45 Although the existence of nitrogen-coordinated metal sites (MNx)

71

has been well documented, the coordination number of N atoms to the active metal center is

72

still unresolved.19,23,40,41,43 Additionally, in-situ XAS and XPS have been used to study

73

Fe-based catalysts for ORR,32,34,37,39 but in-situ characterization of materials for chemical

74

catalysis is lacking.

75

In a recently-published work,21 atomically-dispersed Co and Cu in N-containing carbon

76

exhibited the highest activity for catalytic alcohol oxidation among a series of M-N-C

77

catalysts. In the current work, Co and Cu catalysts were comprehensively characterized and

78

correlated with reaction rates to identify and quantify the active sites. In-situ XAS was

79

performed to investigate the evolution of Co and Cu sites under oxidizing and reducing

80

conditions at different temperatures (up to 750 K). In addition to oxidative dehydrogenation

81

of benzyl alcohol at mild temperature (353 K), the dehydrogenation of propane to propene

82

was demonstrated over Co-N-C.

83 84

Experimental Methods

85

Preparation of catalysts

86

Black Pearls 2000 from Cabot Corporation and Davisil 636 silica from Sigma-Aldrich

87

were used as the carbon and silica supports in this study. The aqueous ammonia was

88

purchased from Fisher Scientific. All other chemicals were purchased from Sigma-Aldrich

89

Corporation or Alfa Aesar and gases were from Praxair Inc. distributed by GTS-Welco. The

90

M-N-C catalysts were prepared by a modified pyrolysis method.13,21 First, an ethanol solution

91

of 1,10-phenanthroline was mixed with an aqueous solution of Co(NO3)26H2O or

92

Cu(NO3)23H2O with a 1:2 molar ratio of metal to 1,10-phenanthroline. The mixture was

93

stirred for 20 min at 353 K and added dropwise to slurry of carbon black in a 0.1 M NaOH 4 / 40

ACS Paragon Plus Environment

Page 5 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

94

aqueous solution under vigorous stirring at 353 K. After 2 h, the slurry was cooled, filtered,

95

washed thoroughly with distilled, deionized water (DI water) and dried overnight at 343 K.

96

The filtered medium was colorless, indicating the efficient adsorption of metal complex onto

97

the carbon support. The prepared materials were subsequently impregnated with an acetone

98

solution of dicyandiamide and dried at 343 K overnight. The amount of impregnated

99

dicyandiamide relative to carbon support was 40 wt% for samples with 1 wt% metal loading

100

or 80 wt% for catalysts with a 3 or 5 wt% metal loading. The obtained solid was pyrolyzed at

101

873, 973 or 1073 K for 2 h with a ramping rate of 10 K min-1 under ultra-high-purity N2 flow

102

(100 cm3 min-1). To investigate the influence of ammonia treatment,10,44 Co and Cu catalysts

103

pyrolyzed at 973 K with 1 wt% nominal metal loading were treated at 1223 K in NH3 with a

104

ramping rate of 10 K min-1 for 2 h under NH3 flow (100 cm3 min-1). To remove the

105

nanoparticles that were observed on the optimized Co-N-C, the catalyst was treated in 1 M

106

HCl solution overnight at room temperature, filtered, washed thoroughly and dried at 393 K.

107

The acid-treated catalyst was denoted as Co-N-C-HCl. To prepare a metal-free

108

nitrogen-doped carbon (N-C), an acetone solution of dicyandiamide (0.4 g) was impregnated

109

into carbon black (0.5 g) followed by a pyrolysis step at 973 K for 2 h under a dinitrogen

110

flow of 100 cm3 min-1. As references, supported Co (5 wt%) and Cu (1.5 wt%) nanoparticles

111

were prepared by incipient wetness impregnation using an aqueous solution of

112

Co(NO3)26H2O or Cu(NO3)23H2O as the metal precursor and silica, carbon black or N-C as

113

the support. After impregnation, the Co precursors on carbon or N-doped carbon were

114

decomposed by thermal treatment in N2 flow (100 cm3 min-1) at 973 K. The C or

115

N-C-supported Cu nanoparticles were prepared by reducing the impregnated Cu(NO3)2 under

116

H2 flow at 623 K. The nanoparticles on Co/SiO2 were prepared by reducing the impregnated

117

support under H2 flow at 923 K. Nitrogen-doped carbon layers were subsequently added to

118

carbon-supported Co and Cu nanoparticle by a modified pyrolysis methods using 5 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 41

119

4-aminoantipyrine as the N-C precursor.46,47 Additionally, a well-dispersed 2.5 nominal wt%

120

Co/SiO2 catalyst was synthesized by an ion exchange method described elsewhere (denoted

121

as CoOx-SiO2).48,49 Briefly, 4.875 g of acid-washed silica was dispersed in 98 cm3 of DI water

122

under vigorous stirring and then heating to 373 K. A solution containing 0.573 g Co(NH3)6Cl3,

123

2.765 cm3 aqueous ammonia, and 104 cm3 DI water was added dropwise over 10 min to the

124

SiO2 slurry, followed by stirring at 373 K for 1 h. Afterwards, the mixture was cooled to room

125

temperature, washed in DI water, dried, and calcined in 100 cm3 min-1 air at 573 K for 2 h

126

after heating with a 1 K min-1 ramp rate. As references, the commercial carbon-supported 3

127

wt% Pt nanoparticles (Pt/C) (from Sigma-Aldrich) with a surface Pt fraction of 0.5950 were

128

evaluated in alcohol oxidation reaction. Silica-supported Pt nanoparticles (Pt/SiO2) were

129

prepared by incipient wetness impregnation (details described elsewhere51) with a surface Pt

130

fraction of 0.40 and evaluated in the propane dehydrogenation reaction

131 132

Characterization of catalysts

133

The X-ray diffraction (XRD) patterns were recorded using a PANalytical X'Pert Pro

134

MPD (Multi-Purpose Diffractometer) instrument with Cu Kα radiation (45 kV, 40 mA) and

135

scanning of 2θ from 10° to 70° with a step size of 0.0025° at a rate of 0.5° min−1.

136

The scanning transmission electron microscopy (STEM) was performed on an FEI Titan

137

80-300 operating at 300 kV or a JEOL 2010 F instrument operating at 200 kV. High angle

138

annular dark filed (HAADF) STEM images were acquired using a Nion UltraSTEM 100

139

operated at 60 kV and equipped with a probe aberration corrector, to achieve a spatial

140

resolution of 1.1 Å. A convergence angle of 31 mrad was used, with HAADF detector inner

141

and outer collection angles of 86 mrad and 200 mrad, respectively. The electron energy loss

142

spectroscopy (EELS) was collected with a dispersion of 0.5 eV using Gatan Enfina

143

spectrometer. 6 / 40

ACS Paragon Plus Environment

Page 7 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

144

The metal loading on Cu-N-C and Co-N-C-HCl was determined by inductively coupled

145

plasma atomic emission spectroscopy (ICP-AES, performed by Galbraith Laboratories (2323

146

Sycamore Drive, Knoxville, TN 37921).

147

The XPS was performed on a Thermo Scientific ESCALAB 250 spectrometer equipped

148

with a focused monochromatic Al Kα X-ray radiation source (1486.6 eV) and a

149

hemispherical analyzer with a 6-element multichannel detector. The incident X-ray beam was

150

45° off normal to the sample while the X-ray photoelectron detector was normal to the

151

sample. A large area magnetic lens with a 500 µm spot size in constant analyzer energy mode

152

was utilized with a pass energy of 20 eV for region scans. Charge compensation was

153

employed during data collection with an internal electron flood gun (2 eV) and a low energy

154

external Ar ion flood gun. The binding energy of the C 1s peak assigned at 284.5 eV, which is

155

attributed to the support, was used to reference the peak positions.52

156

X-ray absorption spectroscopy (XAS) at the Co K and Cu K edges was collected at

157

beamline 8-ID at the National Synchrotron Light Source II, Brookhaven National Laboratory,

158

operating at a ring energy of 3.0 GeV and beam current 325 mA. The Cu and Co metal foils

159

(Goodfellow Corporation) were used as references at the Cu (8979 eV) and Co (7709 eV) K

160

edges,

161

(NH3)6CoCl3, Co(II) phthalocyanine, CuO, Cu(NO3)23H2O, and Cu(II) phthalocyanine

162

powders were crushed and pelletized with boron nitride to provide an absorption edge jump

163

of near unity. Spectra were collected by suspending the pellets in the beam path inside a

164

temperature controlled transmission chamber with Kapton windows. A gas mixture of 5% H2

165

in N2 or 10% O2 in N2 was flowed through the transmission chamber at 100 cm3 min-1 to

166

provide the reducing and oxidizing conditions, respectively. The XAS data were processed

167

using the Demeter software package created by Bruce Ravel.53 The Co-N, Co-O Cu-N/O and

168

Cu-Cu amplitude reduction factors were obtained from fitting to Co phthalocyanine, Co3O4,

respectively.

Chemical standards including CoO,

Co(NO3)26H2O, Co3O4,

7 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

169

Page 8 of 41

Cu phthalocyanine and Cu foil standards.

170 171

Oxidative dehydrogenation of benzyl alcohol

172

The high-pressure, semi-batch alcohol oxidation reactions were performed in a

173

50 cm3 Parr Instrument Company 4592 batch reactor with a 30 cm3 glass liner. An aqueous

174

benzyl alcohol solution (10 cm3) and catalyst were added to the glass liner. The glass liner

175

was inserted into the reactor, sealed, purged with Ar, heated to 353 K and initiated by

176

pressurizing the reactor with O2. The conversion of alcohol during the initial heating stage

177

was negligible. Liquid samples were periodically taken, and the catalyst was removed using a

178

0.2 µm PTFE filter before product analysis with a Waters e2695 high performance liquid

179

chromatograph (HPLC) equipped with refractive index detector. Product separation in the

180

HPLC was accomplished on an Aminex HPX-87H column (Bio-Rad) operating at 318 K

181

with an aqueous 5 mM H2SO4 solution as the mobile phase flowing at 5 cm3 min−1. The

182

retention times and calibration curves were determined by injecting known concentrations of

183

standards. The carbon balance was greater than 90 % unless otherwise stated.

184

The amount of catalyst added to the reactor was chosen so that the alcohol oxidation rate

185

would not be limited by O2 mass transfer from the gas to the liquid.50 Selectivity to a specific

186

product is defined as moles of that product formed divided by moles of all products produced.

187

The initial reaction rates were calculated from the initial conversions of the alcohol (573 K), the Co(II) cations remained atomically-dispersed and

430

coordinated to nitrogen in the carbon at up to 750 K. The stable Co(II) cations in N-doped

431

carbon catalyze the dehydrogenation of propane to propene at 773 K. Cu (II) cations confined

432

in nitrogen-doped carbon also catalyze aerobic alcohol oxidation at 353 K but the turnover

433

frequency of the highly active CuNx sites is an order of magnitude lower than that associated

434

with CoNx. Although Cu(II) cations remained in the N-doped carbon matrix at 373 K under

435

reducing conditions, partial reduction of the Cu was observed above 473 K. These findings

436

provide new insights into the structural and chemical properties that may allow Co-N-C and

437

Cu-N-C catalysts to become desirable replacements for a variety of precious metal catalysts.

438 439

Associated Content

440

Supporting Information

441

The Supporting Information is available free of charge on the ACS Publications websites at

442

DOI: (TO BE ADDED AFTER ACCEPTANCE)

443

Additional analytical and characterization data including optimization of Co and Cu catalysts, 18 / 40

ACS Paragon Plus Environment

Page 19 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

444

alcohol oxidation rates over different material, X-ray photoelectron spectra, X-ray absorption

445

spectra, XRD patterns, STEM images and EELS mapping.

446 447

Acknowledgements

448

This work is supported by the US NSF under grant numbers EEC-0813570 (Center for

449

Biorenewable Chemicals, CBiRC) and CBET-1157829. A portion of the microscopy research

450

was conducted at the Center for Nanophase Materials Sciences in Oak Ridge National Lab,

451

which is a DOE Office of Science User Facility. This research used resources of the National

452

Synchrotron Light Source II, a U.S. Department of Energy (DOE) Office of Science User

453

Facility operated for the DOE Office of Science by Brookhaven National Laboratory under

454

Contract No. DE-SC0012704. Helpful discussion with Zhongwen Luo, Prof. T. Brent Gunnoe

455

and Prof. Matthew Neurock are acknowledged.

456 457

References:

458

(1)

The Path to Refining in the Future. Catal. Today 2005, 101, 3–7.

459 460

(2)

(3)

(4)

467

Santoro, S.; Kozhushkov, S. I.; Ackermann, L.; Vaccaro, L. Heterogeneous Catalytic Approaches in C–H Activation Reactions. Green Chem. 2016, 18, 3471–3493.

465 466

Corma, A.; Iborra, S.; Velty, A. Chemical Routes for the Transformation of Biomass into Chemicals. Chem. Rev. 2007, 107, 2411–2502.

463 464

Matar, S.; Hatch, L. F. Chemistry of Petrochemical Processes; Second Edi.; Gulf Publishing Company: Houston, Texas, 2000.

461 462

Sousa-Aguiar, E. F.; Appel, L. G.; Mota, C. Natural Gas Chemical Transformations:

(5)

Santen, R. A. V.; Neurock, M.; Shetty, S. G. Reactivity Theory of Transition-Metal Surfaces: A Brønsted-Evans-Polanyi Linear Activation Energy-Free-Energy Analysis. 19 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chem. Rev. 2010, 110, 2005–2048.

468 469

(6)

(7)

Zou, X.; Zhang, Y. Noble Metal-Free Hydrogen Evolution Catalysts for Water Splitting. Chem. Soc. Rev 2015, 44, 5148–5180.

472 473

Vesborg, P. C. K.; Jaramillo, T. F. Addressing the Terawatt Challenge: Scalability in the Supply of Chemical Elements for Renewable Energy. RSC Adv. 2012, 2, 7933–7947.

470 471

Page 20 of 41

(8)

Zhu, Y. P.; Guo, C.; Zheng, Y.; Qiao, S.-Z. Surface and Interface Engineering of

474

Noble-Metal-Free Electrocatalysts for Efficient Energy Conversion Processes. Acc.

475

Chem. Res. 2017, 50, 915–923.

476

(9)

for Oxygen Reduction Reaction. Chem. Rev. 2016, 116, 3594–365.

477 478

Shao, M.; Chang, Q.; Dodelet, J.-P.; Chenitz, R. Recent Advances in Electrocatalysts

(10)

Jaouen, F.; Lefèvre, M.; Dodelet, J. P.; Cai, M. Heat-Treated Fe/N/C Catalysts for O2

479

Electroreduction: Are Active Sites Hosted in Micropores? J. Phys. Chem. B 2006, 110,

480

5553–5558.

481

(11)

Huang, D.; Luo, Y.; Li, S.; Zhang, B.; Shen, Y.; Wang, M. Active Catalysts Based on

482

Cobalt oxide@cobalt/N-C Nanocomposites for Oxygen Reduction Reaction in

483

Alkaline Solutions. Nano Res. 2014, 7, 1054–1064.

484

(12)

Yang, F.; Abadia, M.; Chen, C.; Wang, W.; Li, L.; Zhang, L.; Rogero, C.; Chuvilin, A.;

485

Knez, M. Design of Active and Stable Oxygen Reduction Reaction Catalysts by

486

Embedding CoxOy Nanoparticles into Nitrogen-Doped Carbon. Nano Res. 2017, 10,

487

97–107.

488 489

(13)

Jagadeesh, R. V; Junge, H.; Pohl, M.; Radnik, J.; Brückner, A.; Beller, M. Selective Oxidation of Alcohols to Esters Using Heterogeneous Co3O4–N@C Catalysts under 20 / 40

ACS Paragon Plus Environment

Page 21 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

Mild Conditions. J. Am. Chem. Soc. 2013, 135, 10776–10782.

490 491

(14)

Cui, X.; Li, Y.; Bachmann, S.; Scalone, M.; Surkus, A. E.; Junge, K.; Topf, C.; Beller,

492

M. Synthesis and Characterization of Iron-Nitrogen-Doped Graphene/Core-Shell

493

Catalysts: Efficient Oxidative Dehydrogenation of N-Heterocycles. J. Am. Chem. Soc.

494

2015, 137, 10652–10658.

495

(15)

Jagadeesh, R. V; Stemmler, T.; Surkus, A. E.; Bauer, M.; Pohl, M. M.; Radnik, J.;

496

Junge, K.; Junge, H.; Bruckner, A.; Beller, M. Cobalt-Based Nanocatalysts for Green

497

Oxidation and Hydrogenation Processes. Nat. Protoc. 2015, 10, 916–926.

498

(16)

Metal Oxides-Based Nanocatalysts. Nat. Commun. 2014, 5, 4123.

499 500

Jagadeesh, R. V; Junge, H.; Beller, M. Green Synthesis of Nitriles Using Non-Noble

(17)

Zhang, L.; Wang, A.; Wang, W.; Huang, Y.; Liu, X.; Miao, S.; Liu, J.; Zhang, T.

501

Co-N-C Catalyst for C-C Coupling Reactions: On the Catalytic Performance and

502

Active Sites. ACS Catal. 2015, 5, 6563–6572.

503

(18)

Slot, T. K.; Eisenberg, D.; van Noordenne, D.; Jungbacker, P.; Rothenberg, G.

504

Cooperative Catalysis for Selective Alcohol Oxidation with Molecular Oxygen. Chem.

505

- A Eur. J. 2016, 22, 12307–12311.

506

(19)

Liu, W.; Zhang, L.; Liu, X. X.; Liu, X. X.; Yang, X.; Miao, S.; Wang, W.; Wang, A.;

507

Zhang, T. Discriminating Catalytically Active FeNx Species of Atomically Dispersed

508

Fe-N-C Catalyst for Selective Oxidation of the C-H Bond. J. Am. Chem. Soc. 2017,

509

139, 10790–10798.

510 511

(20)

Li, M.; Wu, S.; Yang, X.; Hu, J.; Peng, L.; Bai, L.; Huo, Q.; Guan, J. Highly Efficient Single Atom Cobalt Catalyst for Selective Oxidation of Alcohols. Appl. Catal. A Gen. 21 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

2017, 543, 61–66.

512 513

Page 22 of 41

(21)

Xie, J.; Yin, K.; Serov, A.; Artyushkova, K.; Pham, H. N.; Sang, X.; Unocic, R. R.;

514

Atanassov, P.; Datye, A. K.; Davis, R. J. Selective Aerobic Oxidation of Alcohols over

515

Atomically-Dispersed Non-Precious Metal Catalysts. ChemSusChem 10, 359–362.

516

(22)

Nakatsuka, K.; Yoshii, T.; Kuwahara, Y.; Mori, K.; Yamashita, H. Controlled Synthesis

517

of

518

Characterization of the Structural Transformation and Investigation of Their Oxidation

519

Catalysis. Phys. Chem. Chem. Phys. 2017, 19, 4967–4974.

520

(23)

Carbon-Supported

Co

Catalysts

from

Single-Sites

to

Nanoparticles:

Cheng, T.; Yu, H.; Peng, F.; Wang, H.; Zhang, B.; Su, D. Identifying Active Sites of

521

CoNC/CNT from Pyrolysis of Molecularly Defined Complexes for Oxidative

522

Esterification and Hydrogenation Reactions. Catal. Sci. Technol. 2016, 6, 1007–1015.

523

(24)

Huang, F.; Liu, H.; Su, D. Graphitized Nanocarbon-Supported Metal Catalysts:

524

Synthesis, Properties, and Applications in Heterogeneous Catalysis. Sci. China Mater.

525

2017, 60, 1149–1167.

526

(25)

Kattel, S.; Atanassov, P.; Kiefer, B. Stability, Electronic and Magnetic Properties of

527

in-Plane Defects in Graphene: A First-Principles Study. J. Phys. Chem. C 2012, 116,

528

8161–8166.

529

(26)

Kattel, S.; Atanassov, P.; Kiefer, B. Catalytic Activity of Co-N(x)/C Electrocatalysts for

530

Oxygen Reduction Reaction: A Density Functional Theory Study. Phys. Chem. Chem.

531

Phys. 2013, 15, 148–153.

532 533

(27)

Kamiya, K.; Koshikawa, H.; Kiuchi, H.; Harada, Y.; Oshima, M.; Hashimoto, K.; Nakanishi, S. Iron-Nitrogen Coordination in Modified Graphene Catalyzes a 22 / 40

ACS Paragon Plus Environment

Page 23 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

534

Four-Electron-Transfer Oxygen Reduction Reaction. ChemElectroChem 2014, 1, 877–

535

884.

536

(28)

Liang, W.; Chen, J.; Liu, Y.; Chen, S. Density-Functional-Theory Calculation Analysis

537

of Active Sites for Four-Electron Reduction of O2 on Fe/N-Doped Graphene. ACS

538

Catal. 2014, 4, 4170–4177.

539

(29)

Serov, A.; Artyushkova, K.; Atanassov, P. Fe-N-C Oxygen Reduction Fuel Cell

540

Catalyst Derived from Carbendazim: Synthesis, Structure, and Reactivity. Adv. Energy

541

Mater. 2014, 4, 1–7.

542

(30)

Zhou, J.; Duchesne, P. N.; Hu, Y.; Wang, J.; Zhang, P.; Li, Y.; Regier, T.; Dai, H. Fe-N

543

Bonding in a Carbon Nanotube-Graphene Complex for Oxygen Reduction: An XAS

544

Study. Phys. Chem. Chem. Phys. 2014, 16, 15787–15791.

545

(31)

Artyushkova, K.; Serov, A.; Rojas-Carbonell, S.; Atanassov, P. Chemistry of

546

Multitudinous Active Sites for Oxygen Reduction Reaction in Transition

547

Metal-Nitrogen-Carbon Electrocatalysts. J. Phys. Chem. C 2015, 119, 25917–25928.

548

(32)

Jia, Q.; Ramaswamy, N.; Hafiz, H.; Tylus, U.; Strickland, K.; Wu, G.; Barbiellini, B.;

549

Bansil, A.; Holby, E. F.; Zelenay, P.; Mukerjee, S. Experimental Observation of

550

Redox-Induced Fe-N Switching Behavior as a Determinant Role for Oxygen

551

Reduction Activity. ACS Nano 2015, 9, 12496–12505.

552

(33)

Kabir, S.; Artyushkova, K.; Kiefer, B.; Atanassov, P. Computational and Experimental

553

Evidence for a New TM–N3/C Moiety Family in Non-PGM Electrocatalysts. Phys.

554

Chem. Chem. Phys. 2015, 17, 17785–17789.

555

(34)

Serov, A.; Artyushkova, K.; Niangar, E.; Wang, C.; Dale, N.; Jaouen, F.; Sougrati, 23 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 41

556

M.-T.; Jia, Q.; Mukerjee, S.; Atanassov, P. Nano-Structured Non-Platinum Catalysts

557

for Automotive Fuel Cell Application. Nano Energy 2015, 16, 293–300.

558

(35)

Cui, X.; Ren, P.; Deng, D.; Deng, J.; Bao, X. Single Layer Graphene Encapsulating

559

Non-Precious Metals as High-Performance Electrocatalysts for Water Oxidation.

560

Energy Environ. Sci. 2016, 9, 123–129.

561

(36)

Cui, X.; Xiao, J.; Wu, Y.; Du, P.; Si, R.; Yang, H.; Tian, H.; Li, J.; Zhang, W. H.; Deng,

562

D.; Bao, X. A Graphene Composite Material with Single Cobalt Active Sites: A Highly

563

Efficient Counter Electrode for Dye-Sensitized Solar Cells. Angew. Chemie - Int. Ed.

564

2016, 100190, 6708–6712.

565

(37)

Jia, Q.; Ramaswamy, N.; Tylus, U.; Strickland, K.; Li, J.; Serov, A.; Artyushkova, K.;

566

Atanassov, P.; Anibal, J.; Gumeci, C.; Barton, S. C.; Sougrati, M. T.; Jaouen, F.; Halevi,

567

B.; Mukerjee, S. Spectroscopic Insights into the Nature of Active Sites in Iron–

568

nitrogen–carbon Electrocatalysts for Oxygen Reduction in Acid. Nano Energy 2016,

569

29, 65–82.

570

(38)

Liu, W.; Zhang, L.; Yan, W.; Liu, X.; Yang, X.; Miao, S.; Wang, W.; Wang, A.; Zhang,

571

T. Single-Atom Dispersed Co–N–C Catalyst: Structure Identification and Performance

572

for Hydrogenative Coupling of Nitroarenes. Chem. Sci. 2016, 7, 5758–5764.

573

(39)

Artyushkova, K.; Matanovic, I.; Halevi, B.; Atanassov, P. Oxygen Binding to Active

574

Sites of Fe-N-C ORR Electrocatalysts Observed by Ambient-Pressure XPS. J. Phys.

575

Chem. C 2017, 121, 2836–2843.

576 577

(40)

Chen, X.; Yu, L.; Wang, S.; Deng, D.; Bao, X. Highly Active and Stable Single Iron Site Confined in Graphene Nanosheets for Oxygen Reduction Reaction. Nano Energy 24 / 40

ACS Paragon Plus Environment

Page 25 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

2017, 32, 353–358.

578 579

(41)

Chung, H. T.; Cullen, D. A.; Higgins, D.; Sneed, B. T.; Holby, E. F.; More, K. L.;

580

Zelenay, P. Direct Atomic-Level Insight into the Active Sites of a High-Performance

581

PGM-Free ORR Catalyst. Science. 2017, 357, 479–484.

582

(42)

Guo, S.; Yuan, P.; Zhang, J.; Jin, P.; Sun, H.; Lei, K.; Pang, X.; Xu, Q.; Cheng, F.

583

Atomic-Scaled Cobalt Encapsulated in P,N-Doped Carbon Sheaths over Carbon

584

Nanotubes for Enhanced Oxygen Reduction Electrocatalysis under Acidic and

585

Alkaline Media. Chem. Commun. 2017, 53, 9862–9865.

586

(43) Shen, H.; Gracia-Espino, E.; Ma, J.; Tang, H.; Mamat, X.; Wagberg, T.; Hu, G.; Guo, S.

587

Atomically FeN2 Moieties Dispersed on Mesoporous Carbon: A New Atomic Catalyst

588

for Efficient Oxygen Reduction Catalysis. Nano Energy 2017, 35, 9–16.

589

(44)

Fei, H.; Dong, J.; Feng, Y.; Allen, C. S.; Wan, C.; Volosskiy, B.; Li, M.; Zhao, Z.;

590

Wang, Y.; Sun, H.; An, P.; Chen, W.; Guo, Z.; Lee, C.; Chem, D.; Shakir, I.; Liu, M.;

591

Hu, T.; Li, Y.; Kirkland, A. I.; Duan, X.; Huang, Y. General Synthesis and Definitive

592

Structural

593

Electrocatalytic Activities. Nat. Catal. 2018, 1, 63–72.

594

(45)

Identification

of

MN4C4

Single-Atom

Catalysts

with

Tunable

Artyushkova, K.; Kiefer, B.; Halevi, B.; Knop-Gericke, A.; Schlogl, R.; Atanassov, P.

595

Density Functional Theory Calculations of XPS Binding Energy Shift for

596

Nitrogen-Containing Graphene-like Structures. Chem. Commun. 2013, 49, 2539.

597

(46)

Pham, H. N.; Anderson, A. E.; Johnson, R. L.; Schwartz, T. J.; O’Neill, B. J.; Duan, P.;

598

Schmidt-Rohr, K.; Dumesic, J. A.; Datye, A. K. Carbon Overcoating of Supported

599

Metal Catalysts for Improved Hydrothermal Stability. ACS Catal. 2015, 5, 4546–4555. 25 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

600

(47)

Page 26 of 41

Pham, H. N.; Anderson, A. E.; Johnson, R. L.; Schmidt-Rohr, K.; Datye, A. K.

601

Improved Hydrothermal Stability of Mesoporous Oxides for Reactions in the Aqueous

602

Phase. Angew. Chemie Int. Ed. 2012, 51, 13163–13167.

603

(48)

Kaylor, N.; Xie, J.; Kim, Y.-S.; Pham, H. N.; Datye, A. K.; Lee, Y.-K.; Davis, R. J.

604

Vapor Phase Deoxygenation of Heptanoic Acid over Silica-Supported Palladium and

605

Palladium-Tin Catalysts. J. Catal. 2016, 344, 202–212.

606

(49) Lam, Y. M.; Boudart, M. Preparation of Small Au-Pd Particles on Silica. J. Catal. 1977, 50, 530–540.

607 608

(50)

Xie, J.; Huang, B.; Yin, K.; Pham, H. N.; Unocic, R. R.; Datye, A. K.; Davis, R. J.

609

Influence of Dioxygen on the Promotional Effect of Bi during Pt-Catalyzed Oxidation

610

of 1,6-Hexanediol. ACS Catal. 2016, 6, 4206–4217.

611

(51)

Xie, J.; Duan, P.; Kaylor, N.; Yin, K.; Huang, B.; Schmidt-Rohr, K.; Davis, R. J.

612

Deactivation of Supported Pt Catalysts during Alcohol Oxidation Elucidated by

613

Spectroscopic and Kinetic Analyses. ACS Catal. 2017, 7.

614

(52)

Xie, J.; Falcone, D. D.; Davis, R. J. Restructuring of Supported PtSn Bimetallic

615

Catalysts during Aqueous Phase Oxidation of 1,6-Hexanediol. J. Catal. 2015, 332, 38–

616

50.

617

(53)

Ravel, B., Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: Data Analysis for

618

X-Ray Absorption Spectroscopy Using IFEFFIT. J. Synchrotron Radiat. 2005, 12,

619

537–541.

620 621

(54)

Biesinger, M. C.; Payne, B. P.; Grosvenor, A. P.; Lau, L. W. M.; Gerson, A. R.; Smart, R. S. C. Resolving Surface Chemical States in XPS Analysis of First Row Transition 26 / 40

ACS Paragon Plus Environment

Page 27 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

622

Metals, Oxides and Hydroxides: Cr, Mn, Fe, Co and Ni. Appl. Surf. Sci. 2011, 257,

623

2717–2730.

624

(55)

Yokoyama, T. Metastable Photoinduced Phase of Cu (II) Ethylenediamine Complexes

625

Studied by X-Ray-Absorption Fine-Structure Spectroscopy. Phys. Rev. B 2003, 67, 1–

626

4.

627

(56)

Control Catalytic Reactions. ACS Catal. 2012, 2, 270–279.

628 629

Lyaskovskyy, V.; de Bruin, B. Redox Non-Innocent Ligands: Versatile New Tools to

(57)

Wang, Y.; DuBois, J. L.; Hedman, B.; Hodgson, K. O.; Stack, T. D. Catalytic Galactose

630

Oxidase Models: Biomimetic Cu(II)-Phenoxyl-Radical Reactivity. Science 1998, 279,

631

537–540.

632

(58)

Mamtani, K.; Jain, D.; Zemlyanov, D.; Celik, G.; Luthman, J.; Renkes, G.; Co, A. C.;

633

Ozkan, U. S. Probing the Oxygen Reduction Reaction Active Sites over

634

Nitrogen-Doped Carbon Nanostructures (CNx) in Acidic Media Using Phosphate

635

Anion. ACS Catal. 2016, 6, 7249–7259.

636

(59)

Sattler, J. J. H. B.; Ruiz-Martinez, J.; Santillan-Jimenez, E.; Weckhuysen, B. M.

637

Catalytic Dehydrogenation of Light Alkanes on Metals and Metal Oxides. Chemical

638

Reviews, 2014, 114, 10613–10653.

639

(60)

Li, W.; Yu, S. Y.; Meitzner, G. D.; Iglesia, E. Structure and Properties of

640

Cobalt-Exchanged H-ZSM5 Catalysts for Dehydrogenation and Dehydrocyclization of

641

Alkanes. J. Phys. Chem. B 2001, 105, 1176–1184.

642 643

(61)

Yu, S. Y.; Yu, G. J.; Li, W.; Iglesia, E. Kinetics and Reaction Pathways for Propane Dehydrogenation and Aromatization on Co/H-ZSM5 and H-ZSM5. J. Phys. Chem. B 27 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

2002, 106, 4714–4720.

644 645

Page 28 of 41

(62)

Hu, B.; Bean Getsoian, A.; Schweitzer, N. M.; Das, U.; Kim, H.; Niklas, J.; Poluektov,

646

O.; Curtiss, L. A.; Stair, P. C.; Miller, J. T.; Hock, A. S. Selective Propane

647

Dehydrogenation with Single-Site CoII on SiO2 by a Non-Redox Mechanism. J. Catal.

648

2015, 322, 24–37.

649

28 / 40

ACS Paragon Plus Environment

Page 29 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

650

Tables and Figures

651

Table 1. Kinetic isotope effect for benzyl alcohol oxidationa Catalyst

Co-N-C

Cu-N-C

Reaction

RateD -6

-1

RateH/ -1

(10 mol s gcat )

RateD

C6H5CD2OH+H2O

2.3

2.9

C6H5CD2OH+H2O+0.1 M NaOH

10

1.6

C6H5CD2OH+H2O

0.57

2.8

C6H5CD2OH+H2O+0.1 M NaOH

3.9

1.8

652

a. Reaction conditions: 10 cm3 0.05 M benzyl alcohol aqueous solution, 10 mg catalyst, 1

653

MPa O2, 353 K. Conversion was less than 20% when calculating the rate.

654

29 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 41

655

Table 2. Weight loadings of metal sites associated with atomically-dispersed Co and Cu

656

catalysts Overall metal loading (wt%) Catalyst

ICP-AESa

XPSb

Co-N-C-HCl

1.5

1.3±0.2

Cu-N-C

1.2

0.5±0.1

657

a. The relative standard deviation of ICP-AES measurement is less than 10% (provided by

658

Galbraith Laboratories).

659

b. The metal loadings are derived from the quantitative XPS analysis shown in Table S3.

660

30 / 40

ACS Paragon Plus Environment

Page 31 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

661

ACS Catalysis

Table 3. Rates of benzyl alcohol oxidation over reference materialsa Entry

Metal loadingb

Catalyst

Rate (10-6 mol s-1 gcat-1)

(wt%) 1

CoPhen/C

1

0.013

2

CuPhen/C

1

0.010

3

N-C



0.041

4

Cu/C

1.5

0.035

5

Cu/N-C

1

0.022

6

N-C-Cu/C

1.5

0.024

7

Co/C

5

0.040

8

Co/N-C

5

0.085

9

N-C-Co/C

5

0.062

10

Co/SiO2

5

0.0026

11

CoOx-SiO2

2.5

0.0025

12

Pt/C

3

30

3

662

a. Reaction conditions: 10 cm 0.05 M benzyl alcohol aqueous solution, 1 MPa O2, 353 K,

663

rates were calculated based on the alcohol conversion after 15 min of reaction.

664

b. The nominal metal loadings are calculated based on the amounts of precursors for catalyst

665

preparation.

666

31 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 32 of 41

667

Table 4. Results from the analyses of Co EXAFS from Co-N-C-HCl catalyst before and after

668

H2 treatmenta Conditions As-prepared After H2 treatmentb

Shell Coordination number

r (Å)

∆σ2 (Å2)

∆E0 (eV)

Co-N

2.4±0.9

1.91±0.03

0.005±0.003

-0.3±0.6

Co-O

2.1±0.9

2.09±0.03

0.005±0.005

-0.3±0.6

Co-N

2.4±0.9

1.89±0.03 0.0041±0.003 -0.3±0.6

Co-O

1.2±0.9

2.06±0.05 0.0037±0.005 -0.3±0.6

669

a: Fitting parameters: Fourier transform range, ∆k, 2-14 Å-1; fitting range ∆R, 1-2.2 Å;

670

k2-weighting, S02(Co-N/O) = 0.775 (Calibrated from Co phthalocyanine). The fitted Fourier

671

transforms are present in Figure 6.

672

b: Co-N-C-HCl catalyst was treated in H2 from room temperature to 750 K and then cooled to

673

313 K.

674

32 / 40

ACS Paragon Plus Environment

Page 33 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

675 676

Figure 1. Influence of adsorbed acids on metal sites on the reaction rate of benzyl alcohol

677

oxidation over a) Co-N-C and b) Cu-N-C catalysts. Reaction conditions: 10 cm3 0.1 M benzyl

678

alcohol aqueous solution, 10 mg catalyst, 353 K, 1 MPa O2, the reaction rates were calculated

679

from the conversion after 15 min of reaction. The results from linear fit of first four points

680

(dashed lines) are presented in Table S6.

33 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 34 of 41

681 682

Figure 2. a) Normalized XANES at the Co K-edge and b) the k2-weighted Fourier transform

683

(not corrected for phase shift) of Co EXAFS associated with Co-N-C-HCl at room

684

temperature, at 373 K under 10% O2 and at 373 K under 5% H2; and c) normalized XANES

685

at the Cu K-edge and d) the k2-weighted Fourier transform (not corrected for phase shift) of

686

Cu EXAFS associated with Cu-N-C at room temperature, at 373 K under 10% O2 and at 373

687

K under 5% H2.

34 / 40

ACS Paragon Plus Environment

Page 35 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

688 689

ACS Catalysis

Figure 3. AC-STEM images of a) Co-N-C-HCl and b) Cu-N-C.

35 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 36 of 41

690 691

Figure 4. a) Co 2p3/2 X-ray photoelectron spectrum of Co-N-C-HCl; b) Cu 2p3/2 X-ray

692

photoelectron spectrum of Cu-N-C and N 1s X-ray photoelectron spectra of c) Co-N-C-HCl

693

and d) Cu-N-C.

36 / 40

ACS Paragon Plus Environment

Page 37 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

694 695

Figure 5. a) Normalized XANES at the Co K-edge and b) the k2-weighted Fourier transform

696

(not corrected for phase shift) of Co EXAFS associated with Co-N-C-HCl under 5% H2 flow

697

from 373 to 750 K; c) normalized XANES at the Cu K-edge and d) the k2-weighted Fourier

698

transform (not corrected for phase shift) of the Cu EXAFS associated with Cu-N-C under 5%

699

H2 flow from 373 to 573 K.

37 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 38 of 41

700 701

Figure 6. a) The k2-weighted experimental and fitted Fourier transforms of Co EXAFS

702

associated with Co-N-C-HCl as-prepared and after H2 treatment at 750 K followed by

703

cooling in H2 to 313 K and b) the contributions of different paths including Co–N and Co–O

704

in k-space for the Co-N-C-HCl, as-prepared and after H2 treatment at 750 K followed by

705

cooling in H2 to 313 K. The fitting parameters are presented in Table 4.

38 / 40

ACS Paragon Plus Environment

Page 39 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

706 707

Figure 7: a) Conversion of propane and b) nominal TOF during propane dehydrogenation

708

over 0.05 g Co-N-C-HCl and 0.1 g CoOx-SiO2. TOF was based on total Co loading in the

709

sample. Reaction conditions: 773 K, 0.1 MPa, N2:propane = 3:1.

710

39 / 40

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

711

Page 40 of 41

Table of Contents Graphic:

712

713

40 / 40

ACS Paragon Plus Environment

Page 41 of 41 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

84x47mm (149 x 149 DPI)

ACS Paragon Plus Environment