ATRP of MMA Catalyzed by FeIIBr2 in the Presence of Triflate Anions

Macromolecules , 2011, 44 (6), pp 1226–1228. DOI: 10.1021/ma1029357. Publication Date (Web): February 1, 2011. Copyright © 2011 American Chemical ...
0 downloads 0 Views 869KB Size
COMMUNICATION TO THE EDITOR pubs.acs.org/Macromolecules

ATRP of MMA Catalyzed by FeIIBr2 in the Presence of Triflate Anions Yu Wang and Krzysztof Matyjaszewski* Center for Macromolecular Engineering, Department of Chemistry, Carnegie Mellon University, 4400 Fifth Avenue, Pittsburgh, Pennsylvania 15213, United States

bS Supporting Information tom transfer radical polymerization (ATRP)1-6 was extensively studied during the past decade. Many transition metals, such as Cu, Ru, Fe, Ni, and Os, were successfully employed as ATRP catalysts.7,8 Fe-based ATRP is a very attractive system because iron has the lowest toxicity and lowest price. The first Fe-based ATRPs, conducted in the presence of phosphines, amine, or pyridine containing ligands, were reported in 1997.9,10 Later, various Fe-based complexes containing half-metallocene,11 cyclic amines,12 diimines,13 substituted phosphines,14 carbenes,15 carboxylic acids,16,17 or halide ligands forming anionic Fe species18,19 or ionic liquids20 were successfully reported to conduct ATRP. Recently, we reported FeIIBr2-catalyzed ATRP of methyl methacrylate (MMA) in polar solvents without any additional ligand.21 However, we were unable to conduct the polymerization in nonpolar solvents because FeIIBr2 could not be dissolved. Herein, we present FeIIBr2-catalyzed ATRP of MMA in a nonpolar solvent, anisole, in the presence of tetra(n-butyl)ammonium triflate (TBAOTf). TBAOTf helps to dissolve FeIIBr2 in the monomer/solvent mixture but does not coordinate strongly to Fe center. This catalytic system leads to robust control over ATRP of MMA. Triflate anions are considered as either noncoordinating22 or weakly coordinating,23 since their coordination is weak and reversible. Weakly coordinating or noncoordinating anions are those which do not form permanent coordinative bond with the metal and which are weak Lewis bases. Generally, their negative charge is delocalized. The coordination sites occupied by weakly coordinating anions could be considered as “vacant” because they would easily vacate this coordination site in the presence of other ligands. The polymerization of MMA did not occur in anisole, even after 8 h at 60 °C, in the absence of TBAOTf because FeIIBr2 was not soluble. The triflate anions facilitated FeIIBr2 dissolution and led to a well-controlled polymerization. FeIIBr2/TBAOTf-catalyzed ATRP of MMA was successfully carried out in 33.3% (v/v) anisole at 60 °C with the molar ratio [MMA]:[EBrPA]:[FeIIBr2] = 400:1:1 (EBrPA: ethyl 2-bromo-2-phenylacetate) in the presence of various ratios [TBAOTf]/[FeIIBr2] (Figure 1). With 0.5 equiv of TBAOTf, the solution was still heterogeneous. As a result, the activity was lower than with 1 equiv of TBAOTf. Conversion of 44% was achieved after 4 h with 0.5 equiv of TBAOTf, while the conversion 57% was reached with 1 equiv of TBAOTf. However, once FeIIBr2 was completely dissolved, the activity did not change with a further increase of [TBAOTf] added. The conversion reached 56%, 57%, and 55% in 4 h with 0.75, 1, and 2 equiv of TBAOTf, respectively. Independently of the excess TBAOTf added, the polymerizations were well

A

r 2011 American Chemical Society

controlled, yielding polymers with Mw/Mn values around 1.15 throughout the polymerizations, and resulted in PMMA with molecular weights agreeing with theoretical values. Similar polymerization rates with 0.75, 1, or 2 equiv TBAOTf suggest the reversible weak coordination of triflate anions. Solvent, monomer, and triflate anions likely occupy the “vacant” coordination sites of iron centers, increasing solubility, while they do not significantly influence the catalytic properties and allow the alkyl halides to be activated by the atom transfer process. These observations were very different from those with tetra(n-butyl)ammonium bromide (TBABr). In the presence of 1 equiv of TBABr, the activity was higher (73% conversion in 4 h) than with 1 equiv of TBAOTf, although Mw/Mn values were also higher (1.28 vs 1.17). However, when 2 equiv of TBABr was added, the activity dropped (29% conversion in 4 h) while Mw/ Mn values decreased from 1.29 to 1.15. In the presence of 5 equiv of TBABr, the activity was even lower (22% conversion in 4 h) and the Mw/Mn values increased to 1.42-1.59. In all cases, the molecular weights of obtained PMMA agreed with theoretical values. These experiments indicate that triflate anions interact with iron centers weakly and do not significantly affect their catalytic properties but nevertheless facilitate dissolution of FeIIBr2 in less polar media. FeIIBr2/TBAOTf-catalyzed ATRP of MMA with different targeted degrees of polymerization (DP) was evaluated in 33.3% (v/v) anisole at 60 °C, using the molar ratio [MMA]:[EBrPA]:[FeIIBr2]: [TBAOTf] = (100, 200, or 400):1:1:1 (Table 1). The polymerizations were well controlled, providing PMMA with Mw/Mn = 1.14-1.24, and the molecular weights in good agreement with the theoretical values. The conversion reached 63%, 56%, and 42% after 2 h polymerization for targeted DP = 100, 200, and 400, respectively. Higher conversion could be achieved at longer times. For example, 98% conversion was reached after 16 h with targeted DP = 200. The molecular weight of obtained PMMA was Mn = 17 900 with Mw/Mn = 1.20. The polymerization of MMA was also well controlled in bulk and toluene, indicating that anisole was not a specific solvent for FeIIBr2/TBAOTf controlled ATRP of MMA. The rates of polymerization in NMP with or without TBAOTf were both slower (36% and 44% conversion in 2 h, respectively) than that in anisole with TBAOTf (63% conversion in 2 h). The Mw/Mn values in NMP with or without TBAOTf were 1.28-1.29, which were higher than that in anisole (1.19). The influence of NMP solvent was more significant than that of TBAOTf, which further illustrated the weakly coordinating nature of anions. Received: August 17, 2010 Revised: January 23, 2011 Published: February 01, 2011 1226

dx.doi.org/10.1021/ma1029357 | Macromolecules 2011, 44, 1226–1228

Macromolecules

COMMUNICATION TO THE EDITOR

Figure 1. (a) Kinetic plots of ln([M]0/[M]) vs time and (b) plot of number-average molecular weights Mn and Mw/Mn values vs conversion for FeIIBr2/TBAOTf- and FeIIBr2/TBABr-catalyzed ATRP of MMA with different ratio between FeIIBr2 and TBAOTf or TBABr. [MMA]:[EBrPA]:[FeIIBr2]: = 400:1:1 at 60 °C in 33.3% (v/v) anisole.

Table 1. FeIIBr2/TBAOTf ATRP of MMA with Different Targeted Degree of Polymerization and in Different Solventsa solvent

molar ratiob

time (h)

conv (%)

Mn,GPC

Mn,th

Mw/Mn

anisole

100:1:1:1

2

63

6600

6500

1.19

anisole

200:1:1:1

2

56

12400

11400

anisole

200:1:1:1

4

67

15500

anisole

200:1:1:1

16

98

anisole anisole

400:1:1:1 400:1:1:1

2 8

none

100:1:1:1

toluene

Table 2. ATRP of MMA with Different Ratios of Bromide Anions to FeII Speciesa entry

FeII salt

salt (ratio)

Br/FeII conv (%) Mn,GPC Mn,th Mw/Mn

1 FeII(OTf)2

0

0

1.22

2 FeII(OTf)2 TBABr (1) 3 FeII(OTf)2 TBABr (2)

1 2

43 32

14900 17400 11600 13000

1.14 1.14

13700

1.24

4 FeII(OTf)2 TBABr (3)

3

23

11100

9500

1.14

17900

19900

1.20

5 FeII(OTf)2 TBABr (4)

4

17

6300

7100

1.28

42 71

17600 26400

16900 28600

1.14 1.14

6 FeIIBr2

TBAOTf (2)

2

55

21800 22300

1.13

7 FeIIBr2

TBABr (1)

3

73

27700 29400

1.28

2

67

8500

6900

1.19

8 FeIIBr2

TBABr (2)

4

29

13200 12100

100:1:1:1

2

65

7900

6700

1.22

9 FeIIBr2

TBABF4 (3)

2

7

3600

3000

1.24

NMP

100:1:1:1

2

36

4400

3800

1.29

NMP

100:1:1:0

2

44

5000

4600

1.28

10 FeIIBr2 11 FeIIBr2

TBAPF6 (3) TBAClO4 (3)

2 2

9 1

3700 1200

3800 600

1.23 1.27

1.15

Monomer/solvent = 2/1 (v/v) or in bulk, at 60 °C. b [MMA]0: [EBrPA]0:[FeIIBr2]0:[TBAOTf ]0.

a [MMA]:[EBrPA]:[FeII] = 400:1:1; in 33.3% anisole (v/v), at 60 °C, for 4 h polymerization.

The catalytic activity of FeII(OTf)2 was also studied. FeII(OTf)2 is soluble in anisole but has very low activity in ATRP without any additional halide ligand (Table 2). When 1 equiv TBABr was added, a well-controlled polymerization was attained, and 43% conversion was reached in 4 h. However, a further increase in the ratio of TBABr decreased the catalytic activity. The control of polymerization was still acceptable even when 3 equiv of TBABr was added, but it decreased with 4 equiv of TBABr. The highest activity was found when the ratio between bromide anions and iron centers was 1:1. Compared to the experiments starting with FeIIBr2 and various ratios of TBABr, the results were slightly different, even when the ratio between bromide anions and iron centers was the same (cf. entry 3 and 6;

entry 4 and 7; entry 5 and 8 in Table 2). Probably, the association/exchange process between iron centers and bromide anions could not reach equilibrium, and consequently the activity of the complexes in ATRP was different or some iron species were hydrolyzed.18,19 The effect of adding other weakly coordinating anions was also investigated. In the presence of tetra(n-butyl)ammonium perchlorate, TBAClO4, the system was heterogeneous even with the ratio of TBAClO4 to FeIIBr2 3:1. The polymerization was very slow with low initiation efficiency. Tetra(n-butyl)ammonium with BF4 anion and PF6 anion behaved in a similar way. The activity was much lower with TBABF4 (7% conversion in 4 h) or TBAPF6 (9% conversion in 4 h) than with TBAOTf (55% conversion in 4 h). While the polymerizations were controlled,

a

1227

dx.doi.org/10.1021/ma1029357 |Macromolecules 2011, 44, 1226–1228

Macromolecules

COMMUNICATION TO THE EDITOR

’ AUTHOR INFORMATION Corresponding Author

*E-mail: [email protected].

’ ACKNOWLEDGMENT The authors thank the National Science Foundation (CHE10-26060), WCU (World Class University) program through the Korea Science and Engineering Foundation funded by the Ministry of Education, Science and Technology (R33-10035-0), and the members of the CRP Consortium at Carnegie Mellon University for their financial support. Figure 2. Chain extension of FeIIBr2/TBAOTf-catalyzed ATRP of MMA.

these experiments suggest the activity of the iron halide complexes vary for different weakly (or non-) coordinating anions. FeIIBr2 in the presence of TBAOTf appears to be the best catalytic system of those tested in this study. The role of halide and other noncoordinative anions in Fe-based ATRP is still under investigation. Polymerization of MMA with FeIICl2/TBAOTf was not as well controlled, plausibly due to slower deactivation, as Mw/Mn values were much larger (cf. Supporting Information). Also, ATRP of styrene with (FeIICl2 or FeIIBr2)/TBAOTf was not successful, yielding oligomers, most likely formed via cationic oligomerization catalyzed by strong Lewis (FeX3) or Bronstad acid (traces of triflic acid; cf. Supporting Information). The chain extension experiment showed the well-preserved chain-end functionality (Figure 2). First, PMMA macroinitiator was synthesized using molar ratio of reagents [MMA]:[EBrPA]: [FeIIBr2]:[FeIIIBr3]:[TBAOTf] = 100:1:0.8:0.2:1, in 33.3% (v/v) anisole at 60 °C. The reaction was stopped after 1 h at 41% conversion, yielding PMMA with Mn = 4800 and Mw/Mn = 1.16. The macroinitiator, precipitated in petroleum ether and dried under vacuum, was filtered through an alumina column to remove the catalyst. PMMA was obtained as a white powder with slightly higher molecular weight (Mn = 5000 and Mw/Mn = 1.13). The chain extension experiment was performed using the following molar ratio of reagents: [MMA]:[PMMA-Br]:[FeIIBr2]:[FeIIIBr3]: [TBAOTf] = 1000:1:0.8:0.2:1, in 33.3% (v/v) anisole at 60 °C. PMMA with Mn = 25 200 and Mw/Mn = 1.26 was obtained after 2 h polymerization at 20% conversion. A very small amount of dead chains (