Band Alignment Boosts Charge-Carrier Collection in Sn-Based

5 days ago - The diverse elemental compositions endow metal halide perovskites with tailorable electronic structures and broad optoelectronic applicat...
0 downloads 0 Views 494KB Size
Subscriber access provided by BOSTON UNIV

Energy Conversion and Storage; Plasmonics and Optoelectronics

Band Alignment Boosts Charge-Carrier Collection in Sn-Based Perovskite over Pb Counterparts Binghan Li, Ruiying Long, Qishun Yao, Zihao Zhu, and Qixi Mi J. Phys. Chem. Lett., Just Accepted Manuscript • DOI: 10.1021/acs.jpclett.9b01405 • Publication Date (Web): 27 May 2019 Downloaded from http://pubs.acs.org on May 28, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 16 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Band Alignment Boosts Charge-Carrier Collection in Sn-Based Perovskite over Pb Counterparts Binghan Li,a,b,c,‡ Ruiying Long,a,b,c,‡ Qishun Yao,a Zihao Zhu ,a and Qixi Mi,a,* a

School of Physical Science and Technology, ShanghaiTech University, Shanghai 201210,

China b

Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China

c

University of Chinese Academy of Sciences, Beijing 100049, China

AUTHOR INFORMATION Corresponding Author * [email protected]

1 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 16

ABSTRACT. The diverse elemental compositions endow metal halide perovskites with tailorable electronic structures and broad optoelectronic applications. For Sn-based perovskites, their bandedge positions, which govern interfacial charge-carrier transport, are less well studied than their Pb counterparts. In this work, the valence band maximum (VBM) of CsSnBr3 was experimentally and theoretically determined to be −5.2 eV, to which Au forms a good contact. The conduction band minimum (CBM) of CsSnBr3 at −3.4 eV is matched by 1,3,5-tris(4phenylquinolin-2-yl)benzene (TQB), an organic electron transport material and a ligand to Sn(II). Thanks to proper band alignment, the device structure Al/TQB/CsSnBr3/Au constitutes a photodetector responsive to the entire visible spectrum without a bias voltage, and outperforms Pb-based devices under similar conditions. Our results highlight the advantage of combined experimental and theoretical tools in understanding intrinsic material properties and guiding device fabrication.

TOC GRAPHICS

2 ACS Paragon Plus Environment

Page 3 of 16 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Metal halide perovskites are noted for exceptional optoelectronic properties1,2 and rich applications in high-performance solar cells,3 photodetectors,4 and luminescent devices.5 In particular, lead halide perovskites feature a unique electronic band structure where the valence band maximum (VBM) consists of the Pb2+ s and halide p orbitals, and the conduction band minimum (CBM) mainly involves the empty Pb2+ p orbital. As a result, the bandgap energy of lead halide perovskites can be tuned by using various combinations of halides, and also by replacing the toxic Pb2+ with its lighter congener Sn2+. The univalent A-site cation, typically methylammonium (MA+) or Cs+, also indirectly affects the VBM and CBM of the perovskite by adjusting its crystal structure. The structural flexibility in metal halide perovskites results in diverse material compositions and properties. In addition to the well-studied MAPbI3 benchmark, all-inorganic perovskites such as CsPbBr3 show distinct advantages in terms of long-term device stability,6,7 as well as applications in X-ray detection8 and light-emitting quantum dots.9 Another all-inorganic perovskite CsSnBr3 has lately been studied10 to reveal excellent semiconducting properties and thermal stability that are comparable or superior to those of MAPbI3. The bandgap energy, which can be directly measured, determines the spectral range of light absorption and emission of the perovskite material, and hence its application areas. By contrast, the bandedge positions are less evident properties that underlie charge-carrier collection and injection in optoelectronic devices. Inappropriate band alignment could explain why solar cells made of bromide perovskites (e.g., MAPbBr3, CsPbBr3, and CsSnBr3) usually suffer from large losses in open-circuit voltages.11 In this study, we aimed at finding out whether optimized contact materials, based on accurate VBM and CBM values, can help Sn-based perovskite devices to achieve the performance levels of their Pb counterparts. Crystal photodetectors were chosen as

3 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

devices for proof of concept, because the device structure and interfaces can be well controlled for all Sn- and Pb-based perovskites.

E vs. vacuum (eV)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 16

a

b

c

−4.2 −3.4 −3.4

−4.2 −3.4

−5.2 −5.2 Al TQB

Au

CsSnBr3

−3.3 −5.6

Al TQB

−4.2 −3.4 −3.6 −5.2

−5.2 −5.9

Au

CsPbBr3

Al TQB

Au

MAPbBr3

Figure 1. Band alignment diagrams for several device structures consisting of (a) CsSnBr3, (b) CsPbBr3, or (c) MAPbBr3 as the active layer and 1,3,5-tris(4-phenylquinolin-2-yl)benzene (TQB) as the electron transport layer, showing absolute energy levels with an uncertainty of ~0.1 eV.

Fig. 1 illustrates the interfacial energetics in three device structures studied herein. The absolute energy of valence band maximum (EVBM vac ) of CsSnBr3 was experimentally found to be −5.2 eV and corroborated by theoretical calculations. It was then straightforward to employ Au to form an ohmic contact and a semitransparent top layer for incident light. Based on a bandgap energy Eg = 1.8 eV for CsSnBr3,2 its absolute energy of conduction band minimum (ECBM vac ) was derived to be VBM −3.4 eV, relatively high for perovskite semiconductors. The Evac and ECBM vac values of CsPbBr3

have been reported to be −5.6 and −3.3 eV,7,12-14 respectively. After a survey of literature in polymer solar cells and light emitting diodes, we identified 1,3,5-tris(4-phenylquinolin-2yl)benzene (TQB)15 as a suitable electron transport material for both CsSnBr3 and CsPbBr3. For VBM 16-19 Au and TQB would make contacts with MAPbBr3 with Evac = −5.9 eV and ECBM vac = −3.6 eV,

a barrier.

4 ACS Paragon Plus Environment

Page 5 of 16

DOS (eV-1)

10

5

0

E vs. EF (eV) -10 -5

-15

5 0 VBM Evac

Intensity

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Ecutoff

-5.2 eV

x100 0

-5

-10 -15 -20 E vs. vacuum (eV)

-25

Figure 2. The valence-band electronic structure of CsSnBr3, calculated as the distribution of density of states (DOS, top panel), or measured by ultraviolet photoemission spectroscopy (UPS) relative to the vacuum level (bottom panel). Inset: The experimental spectrum near the valence band maximum (VBM) is magnified by 100 times for clarity.

We determined EVBM vac of CsSnBr3 by both experimental and computational methods. In Fig. 2, ultraviolet photoelectron spectroscopy (UPS) reveals the electronic structure of the valence band of CsSnBr3. The deepest energy level that can be excited by UPS is the negative of He I photon energy (21.22 eV), appearing in the spectrum as a cutoff energy for photoelectrons with low kinetic energy. The UPS signals in the high-energy end are less clear cut, because the VBM of CsSnBr3 consists of a single energy-dispersed band,20 unlike metals with a high density of states (DOS) near the Fermi level (EF). To pinpoint the VBM, we compared the UPS data with the calculated distribution of DOS of CsSnBr3 in Fig. 2. The excellent agreement between the experimental and theoretical results helped us determine EVBM vac = −5.2 eV.

5 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

b

E (eV)

5 Evac slab

0

Eavg slab

-5

0

E vs. vacuum (eV)

a

-10

Eavg slab

-5

E vs. vacuum (eV)

Evac slab

0

-10

-2

EVBM vac

PBE = -4.9 ± 0.1 eV

-4 -6 -8 0

5

E (eV)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 16

-2 -4 -6 -8

0

10 20 30 40 z along [001] (Å)

50

HSE06 EVBM = -5.2 ± 0.1 eV vac

MA

MA SOC

CLA

CLA SOC

Figure 3. (a) Slab models of SnBr2- (top) and CsBr- (bottom) terminated CsSnBr3 (100) surfaces, vac their electrostatic potential curves starting from the vacuum level (Eslab ), and the macroscopic avg

average inside the slab (Eslab ). (b) Calculated absolute energy of valence band maximum (EVBM vac ) of CsSnBr3, using the PBE (top) and HSE06 (bottom) functionals. Dash lines indicate average EVBM vac between SnBr2 (yellow) and CsBr (blue) terminations. MA: macroscopic averaging; CLA: core-level alignment; SOC: spin-orbit coupling.

We also carried out ab initio computational study for EVBM vac of CsSnBr3 by building slab models having SnBr2 or CsBr termination exposed to a vacuum layer. (Fig. 3a) Density functional theory VBM (DFT) calculations generated the VBM energy Ebulk of bulk CsSnBr3, as well as vacuum energy

Evac slab from the slab models. These two energies must be subtracted by their respective references, VBM : before deriving Evac VBM ref vac ref EVBM vac = (Ebulk − Ebulk ) − (Eslab − Eslab ) .

(1)

6 ACS Paragon Plus Environment

Page 7 of 16 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

ref We worked out the energy references Eref bulk and Eslab using two methods. In the macroscopic

averaging21 (MA) method described in Fig. 3a, the three-dimensional electrostatic potential field is first averaged within the xy plane to yield a potential curve along the z direction.22 The avg

macroscopic average Eslab of the electrostatic potentials inside the slab is taken as the energy ref . Similar macroscopic averaging of electrostatic potentials in bulk CsSnBr3 led to reference Eslab ref ref ref Ebulk = 0 by convention. In the core-level alignment23,24 (CLA) method, Ebulk and Eslab are

represented by the Sn 1s core levels in the bulk and inside the slab, respectively. For the two slab VBM models, the more electronegative SnBr2 termination consistently produced more negative Evac

than the CsBr termination, and the mean value of the two terminations was adopted as EVBM vac for bulk CsSnBr3. Fig. 3b and Table S1 summarize the calculated absolute potentials. The CLA method gave VBM Evac values 0.1–0.2 eV more negative than the MA method.21 Whether or not to include spin–

orbit coupling (SOC) had little effect ( 100 cm−1).

Fig. 5 plots the internal quantum efficiencies (IQE) of photodetectors made of CsSnBr3 and MAPbBr3 crystals, as a result of dividing the external quantum efficiencies (EQE) by the transmittance (20–50%) of the top Au electrode. In the absence of a bias voltage, the Al/TQB/CsSnBr3/Au device is responsive to the entire visible spectrum, coincident with the absorption spectrum of the black CsSnBr3 crystal. The IQE curve reaches its peak value of 7% at λ = 700 nm, and follows the steep drop of the absorption edge of CsSnBr3 at longer λ, because of ineffective light absorption. For above-bandgap photons, CsSnBr3 and CsPbBr3 possess absorption coefficients as high as 104–105 cm−1 and thus low (≤1 μm) penetration depths. Therefore, the response of the Al/TQB/CsSnBr3/Au device to excitation at λ < 660 nm is the overall effect of four individual steps: 1) photogeneration of free charge carriers; 2) efficient collection of hole at the

9 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 16

CsSnBr3/Au interface; 3) diffusion of electrons across the 1-mm-thick crystal plate; and 4) efficient collection of electrons arriving at the TQB/CsSnBr3 interface. In addition to our previous discussion on interfacial collection of electrons and holes (Steps 2 and 4), the facile generation (Step 1) and diffusion (Step 3) of charge carriers in CsSnBr3 are also noteworthy. Halide perovskites are excitonic materials and a binding energy (Eb) is required to separate the photoinitiated exciton into free charge carriers. We have recently found10 Eb = 20 meV for CsSnBr3, lower than the thermal energy at room temperature (kBTrt = 26 meV), which means that charge separation of excitons in CsSnBr3 is spontaneous. For Sn-based perovskites, it is a general concern32,33 that p-type defects in the form of Sn4+ or Sn vacancies create trap states that induce charge-carrier recombination. From our observation of electron diffusion across 1-mm thickness of CsSnBr3 as minority carriers, it can be inferred that trap states in the CsSnBr3 crystal plate have been substantially diminished and that higher IQE values can be achieved by thinner plates or films of CsSnBr3. By contrast, the absorption spectrum of CsPbBr3 features a prominent exciton peak, reflecting a relatively high exciton binding energy Eb. This value may be comparable to Eb = 60 meV for MAPbBr3,34 which is much greater than that of CsSnBr3 and can favor charge-carrier recombination. The spectral response of the Al/TQB/CsPbBr3/Au photodetector is weaker and narrower than its CsSnBr3 counterpart, and shows a divergence between the two regimes of abovebandgap and near-bandedge excitation, suggesting less efficient charge-carrier diffusion in bulk CsPbBr3 than in CsSnBr3. For the Al/TQB/MAPbBr3/Au device, no photocurrent could be detected in the entire visible range, which indicates hindered electron collection at the TQB/MAPbBr3 interface. This result is consistent with the band alignment diagram in Fig. 1c showing an uphill CBM offset from MAPbBr3 to TQB.

10 ACS Paragon Plus Environment

Page 11 of 16 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

In conclusion, we performed experiments and computations on CsSnBr3 and located its VBM and CBM at −5.2 eV and −3.4 eV vs. vacuum, respectively. We further fabricated CsSnBr3 crystal plates into photodetectors of the device structure Al/TQB/CsSnBr3/Au with aligned band positions. Without an external bias, the CsSnBr3-based photodetector is responsive to the entire visible spectral range and exhibits a maximum IQE of 7% at 700 nm, significantly enhanced from photodetectors made of CsPbBr3 or MAPbBr3 in terms of both efficiency and spectral range. These findings suggest that the VBM of Sn-based perovskites generally lie higher than their Pb counterparts, and that the polypyridyl compound TQB is suitable for transporting high-lying electrons in CsSnBr3 and CsPbBr3 by energy-level matching and coordinating interactions. Lastly, the functional CsSnBr3 photodetector underscores the importance of interfacial engineering and clarifies undue concerns about bulk defects in this material. Further improvements in Sn-based perovskite photodetector and solar cells can be achieved by using a proper hole transport material and reducing the active layer thickness.

ASSOCIATED CONTENT Supporting Information. Details for preparation and characterization of materials and devices, and for theoretical calculations, Tables S1 & S2 (PDF) Crystallographic information file for TQB (CIF) AUTHOR INFORMATION Corresponding Author

11 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 16

[email protected] Author Contributions ‡These authors contributed equally. Notes The authors declare no competing financial interest. ACKNOWLEDGMENT This work is financially supported by a State Key Research Project (No. 2016YFA0204000) from the Ministry of Science and Technology of China and a Shell–CAS Frontier Sciences Program (No. PT78963), and technically supported by the Analytical Instrumentation Center and the High-Performance Computing (HPC) Platform of ShanghaiTech University. The authors thank Dr. Peihong Cheng, Dr. Na Yu, Mr. Zhifang Shi, and Ms. Qi Wei for assistance with experiments and calculations.

REFERENCES (1) Lin, Q.; Armin, A.; Nagiri, R. C. R.; Burn, P. L., Meredith, P., Electro-optics of Perovskite Solar Cells. Nat. Photonics 2015, 9, 106-112. (2) Manser, J. S.; Christians, J. A., Kamat, P. V., Intriguing Optoelectronic Properties of Metal Halide Perovskites. Chem. Rev. 2016, 116, 12956-13008. (3) Wu, Y.; Xie, F.; Chen, H.; Yang, X.; Su, H.; Cai, M.; Zhou, Z.; Noda, T., Han, L., Thermally Stable MAPbI3 Perovskite Solar Cells with Efficiency of 19.19% and area over 1 cm2 achieved by Additive Engineering. Adv. Mater. 2017, 29, 1701073.

12 ACS Paragon Plus Environment

Page 13 of 16 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(4) Saidaminov, M. I.; Haque, M. A.; Savoie, M.; Abdelhady, A. L.; Cho, N.; Dursun, I.; Buttner, U.; Alarousu, E.; Wu, T., Bakr, O. M., Perovskite Photodetectors Operating in Both Narrowband and Broadband Regimes. Adv. Mater. 2016, 28, 8144-8149. (5) Stranks, S. D., Snaith, H. J., Metal-halide Perovskites for Photovoltaic and Light-emitting Devices. Nat. Nanotech. 2015, 10, 391-402. (6) Kulbak, M.; Gupta, S.; Kedem, N.; Levine, I.; Bendikov, T.; Hodes, G., Cahen, D., Cesium Enhances Long-Term Stability of Lead Bromide Perovskite-Based Solar Cells. J. Phys. Chem. Lett. 2016, 7, 167-172. (7) Liang, J.; Wang, C.; Wang, Y.; Xu, Z.; Lu, Z.; Ma, Y.; Zhu, H.; Hu, Y.; Xiao, C.; Yi, X., et al., All-Inorganic Perovskite Solar Cells. J. Am. Chem. Soc. 2016, 138, 15829-15832. (8) Stoumpos, C. C.; Malliakas, C. D.; Peters, J. A.; Liu, Z.; Sebastian, M.; Im, J.; Chasapis, T. C.; Wibowo, A. C.; Chung, D. Y.; Freeman, A. J., et al., Crystal Growth of the Perovskite Semiconductor CsPbBr3: A New Material for High-Energy Radiation Detection. Cryst. Growth Des. 2013, 13, 2722-2727. (9) Song, J.; Li, J.; Li, X.; Xu, L.; Dong, Y., Zeng, H., Quantum Dot Light-Emitting Diodes Based on Inorganic Perovskite Cesium Lead Halides (CsPbX3). Adv. Mater. 2015, 27, 71627167. (10) Li, B.; Long, R.; Xia, Y., Mi, Q. X., All-Inorganic Perovskite CsSnBr3 as a Thermally Stable, Free-Carrier Semiconductor. Angew. Chem. Int. Ed. 2018, 57, 13154-13158. (11) Correa-Baena, J.-P.; Saliba, M.; Buonassisi, T.; Grätzel, M.; Abate, A.; Tress, W., Hagfeldt, A., Promises and Challenges of Perovskite Solar Cells. Science 2017, 358, 739-744. (12) Endres, J.; Kulbak, M.; Zhao, L.; Rand, B. P.; Cahen, D.; Hodes, G., Kahn, A., Electronic Structure of the CsPbBr3/polytriarylamine (PTAA) System. J. Appl. Phys. 2017, 121, 035304.

13 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 16

(13) He, Y.; Matei, L.; Jung, H. J.; McCall, K. M.; Chen, M.; Stoumpos, C. C.; Liu, Z.; Peters, J. A.; Chung, D. Y.; Wessels, B. W., et al., High Spectral Resolution of Gamma-rays at Room Temperature by Perovskite CsPbBr3 Single Crystals. Nat. Commun. 2018, 9, 1609. (14) Dong, Y.; Gu, Y.; Zou, Y.; Song, J.; Xu, L.; Li, J.; Xue, J.; Li, X., Zeng, H., Improving AllInorganic Perovskite Photodetectors by Preferred Orientation and Plasmonic Effect. Small 2016, 12, 5622-5632. (15) Earmme, T.; Ahmed, E., Jenekhe, S. A., Solution-Processed Highly Efficient Blue Phosphorescent Polymer Light-Emitting Diodes Enabled by a New Electron Transport Material. Adv. Mater. 2010, 22, 4744-4748. (16) Schulz, P.; Edri, E.; Kirmayer, S.; Hodes, G.; Cahen, D., Kahn, A., Interface Energetics in Organo-metal Halide Perovskite-based Photovoltaic Cells. Energy Environ. Sci. 2014, 7, 13771381. (17) Carli, S.; Baena, J. P. C.; Marianetti, G.; Marchetti, N.; Lessi, M.; Abate, A.; Caramori, S.; Grätzel, M.; Bellina, F.; Bignozzi, C. A., et al., A New 1,3,4-Oxadiazole-Based Hole-Transport Material for Efficient CH3NH3PbBr3 Perovskite Solar Cells. ChemSusChem 2016, 9, 657-661. (18) Li, Z.; Boix, P. P.; Xing, G.; Fu, K.; Kulkarni, S. A.; Batabyal, S. K.; Xu, W.; Cao, A.; Sum, T. C.; Mathews, N., et al., Carbon Nanotubes as an Efficient Hole Collector for High Voltage Methylammonium Lead Bromide Perovskite Solar Cells. Nanoscale 2016, 8, 6352-6360. (19) Longo, G.; Wong, A.; Sessolo, M., Bolink, H. J., Effect of the Precursor's Stoichiometry on the Optoelectronic Properties of Methylammonium Lead Bromide Perovskites. J. Lumin. 2017, 189, 120-125. (20) http://aflow.org/material.php?id=Br3Cs1Sn1_ICSD_4071 (accessed 7th Mar. 2019).

14 ACS Paragon Plus Environment

Page 15 of 16 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(21) Mrovec, M.; Albina, J. M.; Meyer, B., Elsässer, C., Schottky Barriers at Transitionmetal/SrTiO3(001) Interfaces. Phys. Rev. B 2009, 79, 245121. (22) Wang, V., Xu, N. VASPKIT: A Pre- and Post-Processing Program for the VASP Code. http://vaspkit.sourceforge.net (accessed 9th Apr. 2019). (23) Jung, Y.-K.; Lee, J.-H.; Walsh, A., Soon, A., Influence of Rb/Cs Cation-Exchange on Inorganic Sn Halide Perovskites: From Chemical Structure to Physical Properties. Chem. Mater. 2017, 29, 3181-3188. (24) Jong, U.-G.; Yu, C.-J.; Kye, Y.-H.; Choe, Y.-G.; Hao, W., Li, S., First-Principles Study on Structural, Electronic, and Optical Properties of Inorganic Ge-Based Halide Perovskites. Inorg. Chem. 2019, 58, 4134-4140. (25) Fabini, D. H.; Laurita, G.; Bechtel, J. S.; Stoumpos, C. C.; Evans, H. A.; Kontos, A. G.; Raptis, Y. S.; Falaras, P.; Van der Ven, A.; Kanatzidis, M. G., et al., Dynamic Stereochemical Activity of the Sn2+ Lone Pair in Perovskite CsSnBr3. J. Am. Chem. Soc. 2016, 138, 1182011832. (26) Huang, L., Lambrecht, W. R. L., Electronic Band Structure, Phonons, and Exciton Binding Energies of Halide Perovskites CsSnCl3 ,CsSnBr3 ,and CsSnI3. Phys. Rev. B 2013, 88, 49774984. (27) Perdew, J. P.; Burke, K., Ernzerhof, M., Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 1996, 77, 3865-3868. (28) Krukau, A. V.; Vydrov, O. A.; Izmaylov, A. F., Scuseria, G. E., Influence of the Exchange Screening Parameter on the Performance of Screened Hybrid Functionals. J. Chem. Phys. 2006, 125, 224106.

15 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 16

(29) Archer, S. J.; Koch, K. R., Schmidt, S., Nitrogen Donor Chelates of Bivalent Tin Chloride. Part II. The crystal Structures of SnCl2·(2,2′-bipyridyl) and SnCl2·(1,10-phenanthroline). Inorg. Chim. Acta 1987, 126, 209-218. (30) Jurca, T.; Hiscock, L. K.; Korobkov, I.; Rowley, C. N., Richeson, D. S., The Tipping Point of the Inert Pair Effect: Experimental and Computational Comparison of In(i) and Sn(ii) Bis(imino)pyridine Complexes. Dalton Trans. 2014, 43, 690-697. (31) Gao, W.; Zielinski, K.; Drury, B. N.; Carl, A. D., Grimm, R. L., Elucidation of Chemical Species and Reactivity at Methylammonium Lead Iodide and Cesium Tin Bromide Perovskite Surfaces via Orthogonal Reaction Chemistry. J. Phys. Chem. C 2018, 122, 17882-17894. (32) Song, T. B.; Yokoyama, T.; Stoumpos, C. C.; Logsdon, J.; Cao, D. H.; Wasielewski, M. R.; Aramaki, S., Kanatzidis, M. G., Importance of Reducing Vapor Atmosphere in the Fabrication of Tin-Based Perovskite Solar Cells. J. Am. Chem. Soc. 2017, 139, 836-842. (33) Gupta, S.; Cahen, D., Hodes, G., How SnF2 Impacts the Material Properties of Lead-Free Tin Perovskites. J. Phys. Chem. C 2018, 122, 13926-13936. (34) Sestu, N.; Cadelano, M.; Sarritzu, V.; Chen, F.; Marongiu, D.; Piras, R.; Mainas, M.; Quochi, F.; Saba, M.; Mura, A., et al., Absorption F-Sum Rule for the Exciton Binding Energy in Methylammonium Lead Halide Perovskites. J. Phys. Chem. Lett. 2015, 6, 4566-4572.

16 ACS Paragon Plus Environment