Band Tailing and Deep Defect States in CH3NH3Pb(I1−xBrx)3 Perovskites As Revealed by Sub-Bandgap Photocurrent Carolin M. Sutter-Fella,†,‡,∥,⊥ D. Westley Miller,#,⊥ Quynh P. Ngo,†,‡ Ellis T. Roe,# Francesca M. Toma,∥ Ian D. Sharp,∥ Mark C. Lonergan,*,§ and Ali Javey*,†,‡ †

Electrical Engineering and Computer Sciences, University of California, Berkeley, California 94720, United States Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720, United States ∥ Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720, United States # Department of Physics, University of Oregon, Eugene, Oregon 97403, United States § Department of Chemistry and Biochemistry, University of Oregon, Eugene, Oregon 97403, United States ‡

S Supporting Information *

ABSTRACT: Organometal halide perovskite semiconductors have emerged as promising candidates for optoelectronic applications because of the outstanding charge carrier transport properties, achieved with low-temperature synthesis. Here, we present highly sensitive sub-bandgap external quantum efficiency (EQE) measurements of Au/spiro-OMeTAD/CH3NH3Pb(I1−xBrx)3/TiO2/FTO/glass photovoltaic devices. The room-temperature spectra show exponential band tails with a sharp onset characterized by low Urbach energies (Eu) over the full halide composition space. The Urbach energies are 15−23 meV, lower than those for most semiconductors with similar bandgaps (especially with Eg > 1.9 eV). Intentional aging of CH3NH3Pb(I1−xBrx)3 for up to 2300 h, reveals no change in Eu, despite the appearance of the PbI2 phase due to decomposition, and confirms a high degree of crystal ordering. Moreover, sub-bandgap EQE measurements reveal an extended band of sub-bandgap electronic states that can be fit with one or two point defects for pure CH3NH3PbI3 or mixed CH3NH3Pb(I1−xBrx)3 compositions, respectively. The study provides experimental evidence of defect states close to the midgap that could impact photocarrier recombination and energy conversion efficiency in higher bandgap CH3NH3Pb(I1−xBrx)3 alloys. nonradiative recombination and modify the band alignment.7 Second, there is a growing consensus that current−voltage hysteresis and photocurrent transients in organometal perovskite solar cells are due to defect states and related mobile ionic species.7,8 Third, alloying might be expected to increase disorder in a crystal as the variety of possible defect states is increased. Importantly, the optical band edge, characterized by the Urbach energy (Eu),9 can be broadened by disorder in the crystal lattice (or by impurities). Low Urbach energies are highly desirable for any semiconductor used in optoelectronic devices. Finally, the evolution of defect states and structural disorder upon aging could play a role in cell degradation.

O

rganometal halide perovskites, with the general formula ABX3, have generated enormous interest over the last 7 years as their solar cell power conversion efficiencies have increased from 3.8% in 20091 to the current world record of 22.1%.2 Much of this progress has been realized by composition engineering at the A site with cations3 including CH(NH2)2+, CH3NH3+, and Cs+, at the B site with Pb2+ and Sn2+ cations,4 and at the X site with I−, Br−, and Cl− anions.5,6 These changes have allowed researchers to increase photovoltaic power conversion efficiencies and chemical stabilities, as well as engineer the bandgap (Eg) for use in high-efficiency tandem photovoltaic devices. Despite the intense interest in composition engineering, the effects of alloying on structural disorder and the densities of states (DOS), particularly within the bandgap, are not well documented. Their characterization is of central importance to identifying factors that contribute to efficiency loss and instability for a number of reasons. First, defects cause © 2017 American Chemical Society

Received: December 23, 2016 Accepted: February 15, 2017 Published: February 15, 2017 709

DOI: 10.1021/acsenergylett.6b00727 ACS Energy Lett. 2017, 2, 709−715

Letter

http://pubs.acs.org/journal/aelccp

Letter

ACS Energy Letters

CH3NH3Pb(I1−xBrx)3 films on FTO/TiO2 substrates were synthesized by a two-step, low-pressure, vapor-assisted, solution process (LP-VASP)15,16 that yields high material uniformity and quality, with previously reported solar cell power conversion efficiencies of up to 19%.17 In brief, the process starts with spin-coating and drying of the PbI2/PbBr2 precursor on the substrate in a N2 atmosphere for 15 min at 110 °C and is followed by annealing in CH3NH3I and CH3NH3Br vapor for 2 h at 120 °C (schematic inset of Figure 1a; details on device

Probing the role of defects and disorder on optoelectronic properties requires sensitive spectroscopic probes. Defect transitions typically have much longer absorption lengths than interband transitions, therefore requiring analysis of optical absorption over several orders of magnitude below that at Eg. To this end, photothermal deflection spectroscopy (PDS)10,11 and Fourier transform photocurrent spectroscopy (FTPS)10 have been performed on isolated thin films, and subbandgap external quantum efficiency (EQE), transient photocapacitance, and transient photocurrent measurements have been applied to full photovoltaic devices.12,13 For CH3NH3PbI3 films, previous PDS and FTPS measurements have shown purely exponential absorptance behavior with steep slopes that correspond to low values of Eu (∼15 meV) and without the signatures of deep states within the bandgap for up to 4 orders of magnitude of response below Eg.10 Similarly low values of Eu have been observed for CH3NH3PbBr3 films by PDS (∼25 meV)11 and devices by photocurrent spectroscopy (∼14 meV).14 Values on mixed bromide/iodide alloys CH3NH3Pb(I1−xBrx)3 have been more varied. Sadhanala et al. observed higher values of Eu at intermediate x with a peak of 90 meV for x = 0.8.11 In contrast, Hoke et al. observed low values of Eu = 12−17 meV over nearly the full range of x, with an outlier at x = 0.5.14 Although the methods described above have been successful at characterizing Eu in CH3NH3Pb(I1−xBrx) materials and solar cells, the signatures of electronically active defect states residing deep in the gap are rarely observed. In this regard, highly sensitive sub-bandgap EQE is a particularly powerful approach because it is capable of probing ultralow photocurrents due to sub-bandgap absorption that can be several orders of magnitude weaker than absorption at Eg. High sensitivity is enabled by using a high-throughput monochromator, a low-noise-current preamplifier, and careful filtering of above-bandgap stray light, allowing investigation of the sub-bandgap DOS (see the Supporting Information for experimental details). Indeed, this method has recently been applied to CH3NH3PbI3 solar cells to reveal a defect band at 1.34 eV with varying density that was linked to photovoltaic characteristics.12 Here, we present sub-bandgap EQE measurements of Au/ spiro-OMeTAD/CH3NH3Pb(I1−xBrx)3/TiO2/FTO/glass photovoltaic devices at room temperature and extending over the full halide composition space (0 ≤ x ≤ 1). In addition, we assess the impact of long-term aging of devices under atmospheric conditions, as monitored via formation of PbI2, on photoluminescence quantum yields (PLQYs) and Urbach energies. Samples were aged for up to 2300 h in a typical laboratory environment with a temperature of 22 ± 1 °C and a relative humidity of 50 ± 7%. For all compositions, we found Urbach energies in the range of 15−23 meV that remain approximately constant throughout the experiment. Moreover, we found direct evidence of sub-bandgap electronic states within the perovskite light absorbers. For pure CH3NH3PbI3, a single, relatively shallow state was observed. With increasing Br content, this state moves closer to the midgap while another shallow defect is revealed. If the densities of defect states near midgap cannot be controlled, then they will likely enhance Shockley−Read−Hall recombination in higher bandgap perovskites and potentially limit device performance. Our results provide important insight into the defect characteristics of the explored perovskite compositions, with implications for understanding disorder- and defect-induced performance limits.

Figure 1. (a) Change in the lattice parameter, as evaluated by the (110) XRD peak angle, plotted versus the halide composition, x, determined by EDX measurements. The methylammonium lead halide (CH3NH3Pb(I1−xBrx)3) perovskite films were prepared by the vapor-assisted solution process (schematic inset). The upper xaxis provides the bandgap corresponding to composition, calculated according to ref 15. (b) False colored cross-sectional scanning electron microscopy image of a typical planar Au/spiroOMeTAD/CH3NH3Pb(I1−xBrx)3/TiO2/FTO photovoltaic device fabricated for this study.

processing can be found in the Supporting Information and ref 17). This process allows access to the full halide composition space and results in the expected decrease of the lattice parameter with increasing Br content, as evaluated by the (110) X-ray diffraction (XRD) peak angle. In Figure 1a, the (110) peak angle is plotted versus the halide composition of the film, as measured by energy-dispersive X-ray spectroscopy (10 kV, FEI Quanta FEG 250), and is approximately linear over this small range of angles. The halide composition, x, in CH3NH3Pb(I1−xBrx)3 was related to the optical bandgap as described by the empirical equation Eg(x) = 1.598 + 0.36x + 0.34x2 and is displayed as the upper x-axis in Figure 1a.15 As mentioned above, sub-bandgap EQE measurements were 710

DOI: 10.1021/acsenergylett.6b00727 ACS Energy Lett. 2017, 2, 709−715

Letter

ACS Energy Letters

Figure 2. (a) Sub-bandgap EQE spectra for x = 0, 0.4, and 1 reveal the presence of electronically active defects. Fits to the data are shown as solid gray lines, with the underlying Gaussian defect distributions shown as solid blue and magenta lines. (b) Internal PLQY extracted at 1 sun illumination for different CH3NH3Pb(I1−xBrx)3 compositions. The shaded area illustrates nonradiative recombination losses. (c) Summary of Urbach energies extracted from EQE and PL measurements plotted against the bandgap. The investigated CH3NH3Pb(I1−xBrx)3 films show consistently low Urbach energies (Eu) between 15 and 23 meV over the full bandgap range of 1.6 ≤ Eg ≤ 2.3 eV.

plotted as solid blue and magenta lines (more sub-bandgap EQE spectra are illustrated in Figure S1 as well as full EQE spectra on a linear scale in Figure S2, Supporting Information). They reveal photocurrent due to optical transitions in the bandgap that likely involve point defects within the perovskite thin films. Sub-bandgap defect-related transitions in the EQE spectra (EQEd) were fit using a function of the form

performed on photovoltaic devices. We fabricated the full stack of Au/spiro-OMeTAD/CH3NH3Pb(I1−xBrx)3/TiO2/FTO/ glass with a planar device architecture, as illustrated in the cross-sectional scanning electron microscopy image in Figure 1b. The sub-bandgap EQE was measured using long-pass filters to limit above-bandgap stray light from a scanning monochromator to 1 part in 107 throughout most of the spectral range (more experimental details can be found in the Supporting Information and in ref 12). Given that lightinduced halide segregation has been reported to create I- and Br-rich domains,14,18 it is important to note that the monochromatic light intensity used during EQE measurements was 1.9 eV. This is remarkable given the polycrystalline nature of the hybrid organic−inorganic perovskite thin films and the nature of the synthesis process, which does not exceed 120 °C and is performed on nonlattice matched substrates. Furthermore, the available literature data for Urbach energies in CH3NH3Pb(I1−xBrx)3 yielded significantly higher Urbach energy values than those reported here for some of the mixed I/Br compositions (compare blue triangles in Figure 3).11,14 Possibly, the synthesis method could play a role in defining disorder, particularly in compositionally complex mixed halide perovskites. While it is well established that methylammonium lead halide perovskites decompose upon exposure to ambient air,37 less is known about how this process impacts defects and disorder in the material. As mentioned earlier, the unencapsulated devices

than any defect response observed from perovskite-containing photovoltaic devices. No sub-bandgap response was observed from TiO2. While the TiO2 photoconductor would be expected to show a band-edge optical response in the ultraviolet, the light source provided insufficient intensity in this spectral range and did not produce any measurable photocurrent. On the basis of these reference measurements, it is concluded that the sub-bandgap response detected from full photovoltaic device stacks is generated within the CH3NH3Pb(I1−xBrx)3 absorber layers. While the sub-bandgap EQE response corresponds to transitions from bound to free electronic states that generate a photocurrent, it does not indicate whether the observed transitions are associated with trapped holes that are excited to the valence band or trapped electrons that are excited to the conduction band. Therefore, further research will be required to identify the specific nature of these defects, as well as their energetic positions on an absolute scale relative to each band edge, as a function of composition. Regardless of the exact defect positions, the observed sub-bandgap responses suggest that the higher bandgap alloys tend to form defects closer to the midgap. For example, the 1.36 eV defect observed in the x = 0 sample corresponds to a state that is 220 meV from a band edge and 570 meV away from the midgap position. In stark contrast, the 1.42 eV transition seen in the x = 1 sample is positioned 880 meV away from a band edge and only 270 meV from the middle of the bandgap. Defects closer to the midgap are much more efficient recombination centers, even for the same defect density. In contrast to our finding, some previous density functional theory (DFT) studies have found that deep defects should have prohibitively high formation energies in organolead iodide perovskites.21,22 However, others predict a high density of deep traps under I-rich synthesis conditions due to the formation of I-on-Pb antisite (IPb) defects with a formation energy < 0.2 eV.23 The 1.36, 1.43, and 1.42 eV transitions observed in the x = 0, 0.4, and 1 cells, respectively, are within one standard deviation of each other and are a reasonably close match for the VPb (−1/−2) transition energy predicted as the dominant defect for x = 0.21 Furthermore, this matches a previously observed defect in x = 0 perovskites grown by another technique and whose density was correlated with steady-state performance losses and large J−V hysteresis.12 Our findings are most consistent with the VPb appearing at near the same energy relative to the conduction band across the samples studied. The 1.89 eV transition observed in the x = 1 cell is a close match for the VPb (0/−1) transition, which is predicted to be obscured by the valence band in CH3NH3PbI3.21 Previous studies have indicated that alloying CH3NH3PbI3 with Br mostly shifts the energetic position of the valence band,24,25 suggesting that such defect states would become optoelectronically active as the bandgap opens. Note that the jump in the data appearing near 1.55 eV (Figure 2a) is an artifact of the measurement due to the addition of a long-pass filter at that energy eliminating the contribution of above-bandgap stray light. The impact of stray light on our EQE spectra is discussed in great detail in the Supporting Information. Both time-resolved photoluminescence (PL)26 and PLQY15 measurements corroborate the sub-bandgap EQE detection of deep defects by showing that trap-assisted recombination is the limiting mechanism at low illumination intensities, which are of relevance to the current work. In particular, the former study explained the monoexponential decay observed at low laser fluence by monomolecular (trap-assisted) recombination, and 712

DOI: 10.1021/acsenergylett.6b00727 ACS Energy Lett. 2017, 2, 709−715

Letter

ACS Energy Letters

show approximately constant Urbach energies, in the range of 15−23 meV, for over 2300 h of degradation. This result indicates that aging and decomposition do not significantly increase disorder and band tail states within the material. Examination of the EQE response further below the bandgap reveals that aging does not increase concentrations of energetically deeper defect states, as shown in Figure 4c. For the case of CH3NH3PbI3-based devices, the defect-related response appears to be unaffected by aging for up to 791 h, whereas for CH3NH3Pb(I0.1Br0.9)3-based devices the density of defect states seems to decrease after 706 and 2316 h of aging, during which time this mixed halide sample partially decomposes, as indicated by the formation of PbI2. This finding is consistent with an observed increase in internal PLQY after several weeks of aging, which implies lower defectmediated recombination rates at low illumination intensities (Supporting Information Figure S4). This increase of PL efficiency with aging time can be explained by passivation of interface states by formation of PbI2.38,39 After longer degradation times, it must be considered that the actual active absorptive volume within the device is reduced due to consumption of the perovskite phase and formation of PbI2, which leads to lower overall light absorption and, thus, lower photocurrent response. It is also important to note that PbI2 precipitation was highly nonuniform over the sample (compare the photograph in Figure S5b, Supporting Information) and XRD patterns represent an average over regions much larger than the device area probed by EQE (i.e., XRD samples regions with and without the Au contact layers, whereas EQE measurements only sample the device active area under the Au contacts). In summary, we have presented sub-bandgap EQE measurements on Au/spiro-OMeTAD/CH3NH3Pb(I1−xBrx)3/TiO2/ FTO/glass photovoltaic devices. All CH3NH3Pb(I1−xBrx)3 compositions, with corresponding bandgaps of 1.6 ≤ Eg ≤ 2.3 eV, exhibit low Urbach energies in the range of 15−23 meV. These Urbach energies are significantly lower than those of most conventional inorganic semiconductors with similar bandgaps, especially for Eg > 1.9 eV, and are not affected by long-term aging of perovskite-based photovoltaic devices (as indicated by the co-presence of PbI2). Moreover, this study

Figure 3. Urbach energies versus bandgap with the range accessible by CH3NH3Pb(I1−xBrx)3 perovskites highlighted in the shaded region. Urbach energies from CH3NH3Pb(I1−xBrx)3 perovskites in this study are shown as red squares, and those from literature data are shown as blue triangles.11,14 Also shown are a range of technologically important semiconductors (black dots): CZTSSe (Se-rich Cu2ZnSn(S,Se)4),20 Si,10 CIGS (Cu(In,Ga)Se2),19 InP,29 GaAs,30 CdTe,31 CZTS (S-rich Cu2ZnSnS4),20 CGS (CuGaSe2),32 a-Si,33 a-SiC:H,34 Al0.05In0.95N,35 and InxGa1−xN (In-rich, graded In profile).36

in this study were aged in the dark under laboratory conditions for up to 2300 h. Reaction with atmospheric species leaves PbI2 as a primary solid-state product. Therefore, XRD can be used to probe changes of the film in fully assembled devices, with the evolution of the (001) PbI2/(110) perovskite (PbBr2/perovskite for x = 1) XRD integrated peak area ratio providing a useful metric for tracking decomposition as a function of time after synthesis. As shown in Figure 4a (and Figure S5a, Supporting Information), XRD reveals a general trend of increasing PbI2 with time for mixed I/Br compositions, while the pure I- and Br-perovskites exhibit very little decomposition during the investigated time interval. In parallel, we recorded the sub-bandgap EQE data on the aged samples and extracted the Urbach energies. Figure 4b displays the evolution of the Urbach energies over time for different CH3NH3Pb(I1−xBrx)3 devices. The data points are connected for better visibility and

Figure 4. (a) Repeated XRD measurements showing the integrated XRD peak ratio of the (001) PbI2/(110) perovskite (PbBr2/perovskite for x = 1) phase as a function of time for different CH3NH3Pb(I1−xBrx)3 compositions. (b) Time evolution of Urbach energies under aging, as extracted from sub-bandgap EQE measurements. (Data points in (a) and (b) are connected as a guide for the eye.) (c) Sub-bandgap EQE spectra taken on the same photovoltaic devices as-received (0 h) and after extended aging under laboratory conditions. 713

DOI: 10.1021/acsenergylett.6b00727 ACS Energy Lett. 2017, 2, 709−715

Letter

ACS Energy Letters

Science, Office of Basic Energy Sciences, of the U.S. Department of Energy under Contract No. DE-AC0205CH11231. The sub-bandgap EQE measurements and analyses presented were funded by the Office of Basic Energy Sciences of the U.S. Department of Energy through DESC0012363. This work utilized equipment in the SuNRISE Photovoltaic Laboratory supported by Oregon BEST. C.M.S.-F. acknowledges financial support from the Swiss National Science Foundation (P2EZP2_155586).

reveals the presence of sub-bandgap defect states for all compositions. These states can be fit with one or two point defects for pure CH3NH3PbI3 or mixed CH3NH3Pb(I1−xBrx)3 compositions, respectively. With increasing Br content, the second state emerges, and the observed defect responses indicate that the higher bandgap alloys are characterized by deep level defects with states close to the midgap. The combination of sub-bandgap EQE, which can directly detect midgap states, and PL-based studies, which can identify recombination pathways and probabilities, provides a future path toward assessing the roles of synthesis and processing on efficiency-limiting recombination centers in the material.





(1) Kojima, A.; Teshima, K.; Shirai, Y.; Miyasaka, T. Organometal Halide Perovskites as Visible-Light Sensitizers for Photovoltaic Cells. J. Am. Chem. Soc. 2009, 131, 6050−6051. (2) Zhang, W.; Eperon, G. E.; Snaith, H. J. Metal Halide Perovskites for Energy Applications. Nat. Energy 2016, 1, 16048. (3) Saliba, M.; Matsui, T.; Seo, J.-Y.; Domanski, K.; Correa-Baena, J.P.; Nazeeruddin, M. K.; Zakeeruddin, S. M.; Tress, W.; Abate, A.; Hagfeldt, A.; Grätzel, M. Cesium-Containing Triple Cation Perovskite Solar Cells: Improved Stability, Reproducibility and High Efficiency. Energy Environ. Sci. 2016, 9, 1989−1997. (4) Eperon, G. E.; Leijtens, T.; Bush, K. A.; Green, T.; Wang, J. T.W.; McMeekin, D. P.; Volonakis, G.; Milot, R. L.; Slotcavage, D. J.; Belisle, R.; et al. Perovskite-Perovskite Tandem Photovoltaics with Ideal Bandgaps. Science 2016, 354, 861. (5) Noh, J. H.; Im, S. H.; Heo, J. H.; Mandal, T. N.; Seok, S. I. Chemical Management for Colorful, Efficient, and Stable Inorganic− Organic Hybrid Nanostructured Solar Cells. Nano Lett. 2013, 13, 1764−1769. (6) Sadhanala, A.; Ahmad, S.; Zhao, B.; Giesbrecht, N.; Pearce, P. M.; Deschler, F.; Hoye, R. L. Z.; Gödel, K. C.; Bein, T.; Docampo, P.; et al. Blue-Green Color Tunable Solution Processable Organolead Chloride−Bromide Mixed Halide Perovskites for Optoelectronic Applications. Nano Lett. 2015, 15, 6095−6101. (7) Ball, J. M.; Petrozza, A. Defects in Perovskite-Halides and Their Effects in Solar Cells. Nat. Energy 2016, 1, 16149. (8) Unger, E. L.; Hoke, E. T.; Bailie, C. D.; Nguyen, W. H.; Bowring, A. R.; Heumüller, T.; Christoforo, M. G.; McGehee, M. D. Hysteresis and Transient Behavior in Current−voltage Measurements of HybridPerovskite Absorber Solar Cells. Energy Environ. Sci. 2014, 7, 3690− 3698. (9) Urbach, F. The Long-Wavelength Edge of Photographic Sensitivity and of the Electronic Absorption of Solids. Phys. Rev. 1953, 92, 1324−1324. (10) De Wolf, S.; Holovsky, J.; Moon, S.-J.; Löper, P.; Niesen, B.; Ledinsky, M.; Haug, F.-J.; Yum, J.-H.; Ballif, C. Organometallic Halide Perovskites: Sharp Optical Absorption Edge and Its Relation to Photovoltaic Performance. J. Phys. Chem. Lett. 2014, 5, 1035−1039. (11) Sadhanala, A.; Deschler, F.; Thomas, T. H.; Dutton, S. E.; Goedel, K. C.; Hanusch, F. C.; Lai, M. L.; Steiner, U.; Bein, T.; Docampo, P.; et al. Preparation of Single-Phase Films of CH3NH3Pb(I1−xBrx)3 with Sharp Optical Band Edges. J. Phys. Chem. Lett. 2014, 5, 2501−2505. (12) Miller, D. W.; Eperon, G. E.; Roe, E. T.; Warren, C. W.; Snaith, H. J.; Lonergan, M. C. Defect States in Perovskite Solar Cells Associated with Hysteresis and Performance. Appl. Phys. Lett. 2016, 109, 153902. (13) Wang, H.-P.; Sutter-Fella, C. M.; Lobaccaro, P.; Hettick, M.; Zheng, M.; Lien, D.-H.; Miller, D. W.; Warren, C. W.; Roe, E. T.; Lonergan, M. C.; et al. Increased Optoelectronic Quality and Uniformity of Hydrogenated P-InP Thin Films. Chem. Mater. 2016, 28, 4602−4607. (14) Hoke, E. T.; Slotcavage, D. J.; Dohner, E. R.; Bowring, A. R.; Karunadasa, H. I.; McGehee, M. D. Reversible Photo-Induced Trap Formation in Mixed-Halide Hybrid Perovskites for Photovoltaics. Chem. Sci. 2015, 6, 613−617. (15) Sutter-Fella, C. M.; Li, Y.; Amani, M.; Ager, J. W.; Toma, F. M.; Yablonovitch, E.; Sharp, I. D.; Javey, A. High Photoluminescence

ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsenergylett.6b00727. Experimental section describing film formation, device processing, sensitive sub-bandgap EQE, including fitting of the spectra, and PLQY measurements; sub-bandgap EQE measurements on glass/FTO/spiro-OMeTAD/Au and glass/FTO/TiO2/Ti photoconductors; full EQE spectra on a linear scale; photoluminescence quantum yield measurements on a CH3NH3Pb(I0.9Br0.1)3 film under pump-power-dependent illumination as-synthesized and remeasured after aging; and XRD measurements over time and a photograph of the aged sample (PDF)



REFERENCES

AUTHOR INFORMATION

Corresponding Authors

*E-mail: [email protected] (M.C.L.). *E-mail: [email protected] (A.J.). ORCID

Carolin M. Sutter-Fella: 0000-0002-7769-0869 Ian D. Sharp: 0000-0001-5238-7487 Author Contributions ⊥

The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. C.M.S.-F. and D.W.M. contributed equally. Notes

The authors declare no competing financial interest.



ACKNOWLEDGMENTS Perovskite synthesis, characterization, and device fabrication were performed with support by the Solar Photochemistry Program of the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, Division of Chemical, Geological and Biosciences under Contract No. DE-AC0205CH11231 (I.D.S.) and by the Laboratory Directed Research and Development Program of Lawrence Berkeley National Laboratory under U.S. Department of Energy Contract Number DE-AC02-05CH11231 (F.M.T). The optical characterization and quantum yield measurements were supported by the Electronic Materials program, funded by the Director, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231. Some electrical performance measurements were performed at the Molecular Foundry, which is supported by the Office of 714

DOI: 10.1021/acsenergylett.6b00727 ACS Energy Lett. 2017, 2, 709−715

Letter

ACS Energy Letters

nance Plasma-Enhanced Chemical-Vapor Deposition. J. Appl. Phys. 1999, 85, 3327−3338. (35) Jiang, L. F.; Shen, W. Z.; Guo, Q. X. Temperature Dependence of the Optical Properties of AlInN. J. Appl. Phys. 2009, 106, 013515. (36) Valdueza-Felip, S.; Bellet-Amalric, E.; Núñez-Cascajero, A.; Wang, Y.; Chauvat, M.-P.; Ruterana, P.; Pouget, S.; Lorenz, K.; Alves, E.; Monroy, E. High In-Content InGaN Layers Synthesized by Plasma-Assisted Molecular-Beam Epitaxy: Growth Conditions, Strain Relaxation, and In Incorporation Kinetics. J. Appl. Phys. 2014, 116, 233504. (37) Tiep, N. H.; Ku, Z.; Fan, H. J. Recent Advances in Improving the Stability of Perovskite Solar Cells. Adv. Energy Mater. 2016, 6, 1501420. (38) Chen, Q.; Zhou, H.; Song, T.-B.; Luo, S.; Hong, Z.; Duan, H.-S.; Dou, L.; Liu, Y.; Yang, Y. Controllable Self-Induced Passivation of Hybrid Lead Iodide Perovskites toward High Performance Solar Cells. Nano Lett. 2014, 14, 4158−4163. (39) Jiang, F.; Rong, Y.; Liu, H.; Liu, T.; Mao, L.; Meng, W.; Qin, F.; Jiang, Y.; Luo, B.; Xiong, S.; et al. Synergistic Effect of PbI2 Passivation and Chlorine Inclusion Yielding High Open-Circuit Voltage Exceeding 1.15 V in Both Mesoscopic and Inverted Planar CH3NH3PbI3(Cl)Based Perovskite Solar Cells. Adv. Funct. Mater. 2016, 26, 8119−8127.

Quantum Yield in Band Gap Tunable Bromide Containing Mixed Halide Perovskites. Nano Lett. 2016, 16, 800−806. (16) Li, Y.; Cooper, J. K.; Buonsanti, R.; Giannini, C.; Liu, Y.; Toma, F. M.; Sharp, I. D. Fabrication of Planar Heterojunction Perovskite Solar Cells by Controlled Low-Pressure Vapor Annealing. J. Phys. Chem. Lett. 2015, 6, 493−499. (17) Li, Y.; Cooper, J. K.; Liu, W.; Sutter-Fella, C. M.; Amani, M.; Beeman, J. W.; Javey, A.; Ager, J. W.; Liu, Y.; Toma, F. M.; et al. Defective TiO2 with High Photoconductive Gain for Efficient and Stable Planar Heterojunction Perovskite Solar Cells. Nat. Commun. 2016, 7, 12446. (18) Bischak, C. G.; Hetherington, C. L.; Wu, H.; Aloni, S.; Ogletree, D. F.; Limmer, D. T.; Ginsberg, N. S. Origin of Reversible PhotoInduced Phase Separation in Hybrid Perovskites. ArXiv160607366 Cond-Mat Physics 2016. (19) Heath, J. T.; Cohen, J. D.; Shafarman, W. N.; Liao, D. X.; Rockett, A. A. Effect of Ga Content on Defect States in CuIn1−xGaxSe2 Photovoltaic Devices. Appl. Phys. Lett. 2002, 80, 4540−4542. (20) Miller, D. W.; Warren, C. W.; Gunawan, O.; Gokmen, T.; Mitzi, D. B.; Cohen, J. D. Electronically Active Defects in the Cu2ZnSn(Se,S)4 Alloys as Revealed by Transient Photocapacitance Spectroscopy. Appl. Phys. Lett. 2012, 101, 142106. (21) Yin, W.-J.; Shi, T.; Yan, Y. Unusual Defect Physics in CH3NH3PbI3 Perovskite Solar Cell Absorber. Appl. Phys. Lett. 2014, 104, 063903. (22) Yin, W.-J.; Shi, T.; Yan, Y. Unique Properties of Halide Perovskites as Possible Origins of the Superior Solar Cell Performance. Adv. Mater. 2014, 26, 4653−4658. (23) Buin, A.; Pietsch, P.; Xu, J.; Voznyy, O.; Ip, A. H.; Comin, R.; Sargent, E. H. Materials Processing Routes to Trap-Free Halide Perovskites. Nano Lett. 2014, 14, 6281−6286. (24) Schulz, P.; Edri, E.; Kirmayer, S.; Hodes, G.; Cahen, D.; Kahn, A. Interface Energetics in Organo-Metal Halide Perovskite-Based Photovoltaic Cells. Energy Environ. Sci. 2014, 7, 1377−1381. (25) Butler, K. T.; Frost, J. M.; Walsh, A. Band Alignment of the Hybrid Halide Perovskites CH3NH3PbCl3, CH3NH3PbBr3 and CH3NH3PbI3. Mater. Horiz. 2015, 2, 228−231. (26) Stranks, S. D.; Burlakov, V. M.; Leijtens, T.; Ball, J. M.; Goriely, A.; Snaith, H. J. Recombination Kinetics in Organic-Inorganic Perovskites: Excitons, Free Charge, and Subgap States. Phys. Rev. Appl. 2014, 2, 34007. (27) Tauc, J.; Grigorovici, R.; Vancu, A. Optical Properties and Electronic Structure of Amorphous Germanium. Phys. Status Solidi B 1966, 15, 627−637. (28) van Roosbroeck, W.; Shockley, W. Photon-Radiative Recombination of Electrons and Holes in Germanium. Phys. Rev. 1954, 94, 1558−1560. (29) Chen, K.; Kapadia, R.; Harker, A.; Desai, S.; Seuk Kang, J.; Chuang, S.; Tosun, M.; Sutter-Fella, C. M.; Tsang, M.; Zeng, Y.; et al. Direct Growth of Single-Crystalline III-V Semiconductors on Amorphous Substrates. Nat. Commun. 2016, 7, 10502. (30) Johnson, S. R.; Tiedje, T. Temperature Dependence of the Urbach Edge in GaAs. J. Appl. Phys. 1995, 78, 5609−5613. (31) Warren, C. W.; Li, J.; Wolden, C. A.; Meysing, D. M.; Barnes, T. M.; Miller, D. W.; Heath, J. T.; Lonergan, M. C. The Effect of Copper on the Sub-Bandgap Density of States of CdTe Solar Cells. Appl. Phys. Lett. 2015, 106, 203903. (32) Cohen, J. D. Identifying the Electronic Properties Relevant to Improving the Performance of High Band-Gap Copper Based I−III−VI2 Chalcopyrite Thin Film Photovoltaic Devices; Subcontract Report NREL/SR-520-43909; 2008. (33) van Veen, M. K.; Schropp, R. E. I. Beneficial Effect of a Low Deposition Temperature of Hot-Wire Deposited Intrinsic Amorphous Silicon for Solar Cells. J. Appl. Phys. 2003, 93, 121−125. (34) Conde, J. P.; Chu, V.; da Silva, M. F.; Kling, A.; Dai, Z.; Soares, J. C.; Arekat, S.; Fedorov, A.; Berberan-Santos, M. N.; Giorgis, F.; Pirri, C. F. Optoelectronic and Structural Properties of Amorphous Silicon− Carbon Alloys Deposited by Low-Power Electron-Cyclotron Reso715

DOI: 10.1021/acsenergylett.6b00727 ACS Energy Lett. 2017, 2, 709−715