Bioinspired Bifunctional Membrane for Efficient ... - ACS Publications

Dec 8, 2015 - In this study, we explored a new approach that uses solar light for both water ... Synthetic Graphene Oxide Leaf for Solar Desalination ...
1 downloads 0 Views 7MB Size
Research Article www.acsami.org

Bioinspired Bifunctional Membrane for Efficient Clean Water Generation Yang Liu,†,∥ Jinwei Lou,†,∥ Mengtian Ni,† Chengyi Song,† Jianbo Wu,† Neil P. Dasgupta,‡ Peng Tao,*,† Wen Shang,*,† and Tao Deng† †

State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai, 200240, P. R. China ‡ Department of Mechanical Engineering, University of Michigan, Ann Arbor, Michigan 48109, United States S Supporting Information *

ABSTRACT: Solving the problems of water pollution and water shortage is an urgent need for the sustainable development of modern society. Different approaches, including distillation, filtration, and photocatalytic degradation, have been developed for the purification of contaminated water and the generation of clean water. In this study, we explored a new approach that uses solar light for both water purification and clean water generation. A bifunctional membrane consisting of a top layer of TiO2 nanoparticles (NPs), a middle layer of Au NPs, and a bottom layer of anodized aluminum oxide (AAO) was designed and fabricated through multiple filtration processes. Such a design enables both TiO2 NP-based photocatalytic function and Au NP-based solar-driven plasmonic evaporation. With the integration of these two functions into a single membrane, both the purification of contaminated water through photocatalytic degradation and the generation of clean water through evaporation were demonstrated using simulated solar illumination. Such a demonstration should also help open up a new strategy for maximizing solar energy conversion and utilization. KEYWORDS: membrane, bifunctional, photocatalytic, evaporation, water purification



INTRODUCTION With the accelerated development of modern society and rapid population growth, the consumption of energy increases significantly every year, which in turn leads to severe environmental pollution problems, especially air and water pollution. Overdischarging of contaminants into natural water resources leads to the shortage of clean water globally.1,2 It is predicted that by the year 2025, nearly two-thirds of the world’s population will live in water-stressed countries.3 One way to battle water shortage is to reuse contaminated water through various decontamination processes, such as purification or distillation. Due to the cleanness and sustainability of solar energy, using solar energy for clean water regeneration has attracted significant attention, and tremendous progress has been reported recently.4−7 One promising and widely studied route to use solar energy for the purification of water is decontamination through photocatalytic processes. In the photocatalytic decontamination process, a photoactive material absorbs sunlight and creates highly active species, such as H2O2, OH•, O2•−, and O3, which can react with contaminants to produce small nontoxic molecules.7 Most of the catalysts studied, however, can only be activated by specific ranges of photon wavelengths, while the other wavelengths of the solar spectrum are not efficiently used. For example, titanium dioxide (TiO2), which has received the most attention among all the photocatalytic materials studied in © XXXX American Chemical Society

the removal of highly toxic and nonbiodegradable pollutants in water,8,9 has a narrow light absorption band in the near-UV region. This narrow absorption band contributes to the low photocatalytic efficiency of TiO2.10 There have been many studies on the modification of structure and morphology,11,12 surface chemistry,13−15 and composition16−18 of TiO2 in order to enhance its photocatalytic efficiency. In addition to increasing the range of the absorption through materials engineering of catalysts, expanding the usage of photons in the range outside of the catalytic absorption band will also lead to an increased efficiency of solar energy utilization. Even within the absorption band, some of the absorbed photons are converted into heat,8 and approaches that take advantage of such heat can also help improve the overall efficiency in solar energy usage. Another promising route for the use of solar energy for water purification is the solar-driven water evaporation process. In photocatalytic reactions, solar energy is converted into chemical energy and induces the degradation of contaminates, while in solar-driven water evaporation processes the solar energy is converted into thermal energy, which in turn drives efficient water evaporation.19−21 Solar-driven water evaporation has Received: October 20, 2015 Accepted: December 8, 2015

A

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces

Figure 1. Bifunctional TiO2−Au-AAO membrane has three layers: a top TiO2 NP layer, a middle Au NP layer, and a bottom AAO layer. This design integrates both photocatalytic degradation and solar vapor generation functions into a single system for the purification of contaminated water.

attracted increased attention lately.22,23 In particular, plasmonic photothermal conversion was demonstrated to be a highly efficient approach for solar-driven water evaporation.24,25 We recently developed a plasmonic interfacial evaporation system that was inspired by the localized heating effects of biological systems.26−28 In this bioinspired interfacial evaporation system, a gold nanoparticle (Au NP) film fabricated through either selfassembly or filtration floats at the air−water interface. Under the solar irradiation, the plasmonic Au NP film is heated, and generates a localized “hot-zone” at the air−water interface. This confined heating effect can maximize the energy efficiency of the water evaporation because it avoids the unnecessary heating of the bulk liquid. In this work, we intend to combine solar-driven evaporation with photocatalytic reactions to expand the usage of solar energy that is not used by the photocatalysts. Specifically, we would like to demonstrate a bifunctional membrane system, with the intention of maximizing the usage of solar energy and further increasing the efficiency of water purification. Nature already provides examples of bifuncational systems that utilize solar energy for both catalytic reaction and water evaporation. The most typical examples include plant leaves. Plant leaves absorb and convert solar energy into chemical energy through photosynthesis process. Besides the function of photosynthesis, plant leaves also have the function of transpiration, in which the leaves use solar energy to drive surface water evaporation and therefore facilitate the transportation of nutrients from the plant root to other parts of the plant. This evaporation process also helps cool the plant. Inspired by the multifunctionality of plant leaves for solar energy utilization, we designed and fabricated a bifunctional membrane system that combines both the solar-driven catalytic degradation of water contaminants and solar-driven water evaporation for the purification of water. The membrane (TiO2−Au-AAO membrane) is composed of a photocatalyst layer of TiO2 NPs, a plasmonic photon-to-heat converting layer of Au NPs, and a supporting anodized aluminum oxide (AAO) layer (Figure 1). Upon simulated solar light irradiation, the photocatalytic function of the membrane degrades the contaminants in the water for the generation of purified water; the evaporation function of the membrane

through localized heating can generate clean water vapor and therefore purified water after condensation. Through these two simultaneous processes, water with different degrees of purities could be produced at the same time and used for different applications. This bioinspired bifunctional membrane offers an alternative approach in solar-driven clean water generation and will help improve the efficiency in solar energy usage.



EXPERIMENTAL SECTION

Materials. Chloroauric acid (HAuCl4, 49−50% Au basis), trisodium citrate dihydrate, hydroxylamine hydrochloride, and Rhodamine B (RhB) were obtained from Aladdin (Shanghai, China). All the materials were analytical grade and used without further purification. Titanium dioxide (TiO2, anatase, ∼25 nm in diameter) was also purchased from Aladdin. Anodic Aluminum Oxide (AAO) membranes were purchased from Lessonnano Technology Co. Ltd. (Guangzhou, China) with a pore size of ∼20 nm. Deionized water was produced by the Millipore Water Purification System (NANO pure, Billerica, MA, U.S.A., 18.2 MΩ). Fabrication of Bifunctional Membrane. Au NPs were synthesized using the citrate reduction method.29,30 First, a 50 mL aqueous solution of 1 mM HAuCl4 was injected into a 100 mL roundbottom flask attached with a condenser and brought to boil under vigorous stirring. Next, a 5 mL solution of 38.8 mM sodium citrate was added into the flask, and the color of the solution immediately changed from pale yellow to reddish-purple. After boiling for 10 min, the solution was cooled down and stirring was continued for an additional 15 min. The as-synthesized colloidal Au NPs were further grown into larger particles through the addition of 1.25 mL of 0.2 M hydroxylamine hydrochloride and 1.5 mL of 1% HAuCl4 at room temperature to the flask. After 35 min of reaction, Au NPs with a diameter of ∼50 nm were obtained, and the particle solution was stored for later use. To construct the bifunctional TiO2−Au-AAO membrane, first ∼25 mL of as-synthesized 50 nm Au NPs solution was filtered through an AAO membrane and dried in air. Next, a 0.5 mL solution of 25 nm TiO2 NPs (1.0 mg/mL, dispersed in DI water through sonication) was filtered through the Au NP-coated AAO membrane to form a photoactive layer on the top. This composite membrane was dried and stored for the subsequent testing of properties. Two types of control samples that contain either a Au NP-only film or a TiO2 NP-only film on top of the AAO membrane were also prepared using the same filtration method with same amount of corresponding NP solutions. B

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces

Figure 2. Fabrication of bifunctional membrane. (a) Cross-sectional SEM image of 2-layer structured Au NP/AAO membrane; (b) Cross-sectional SEM image of three-layer structured TiO2 NP/Au NP/AAO membrane; (c) Preparation schematic of bifunctional membrane. Characterizations. The morphology and size of the synthesized Au NPs were observed with a transmission electron microscopy (TEM, Tecnai G2 Spirit Biotwin, FEI). The bifunctional TiO2−AuAAO membrane samples were examined by a field-emission scanning electron microscopy (SEM, FEI Sirion 200, 5 kV). The optical absorption spectra of the samples in the range of 200−800 nm were obtained by an UV−Vis-NIR spectrometer (PerkinElmer, Lambda 750S). The optical absorbance measurement for RhB solution was performed using an Ocean Optics spectrometer (HR2000+CG, Ocean Optics, U.S.A.) attached with two optical fibers (QR400−7-Vis-NIR fiber, Ocean Optics, U.S.A.). A 6W tungsten-halogen light source (HL2000, Ocean Optics, U.S.A.) was also used for the measurement. Photocatalytic Activity Test. To evaluate the photocatalytic property of the fabricated bifunctional membrane, an organic dye RhB was used as the model material, and its photodegradation processes by both the bifunctional membrane and the control membrane samples were studied. For a typical test, an aqueous RhB solution (20 mg/L) was prepared and 10 mL of the solution was injected into a 15 mL quartz beaker. The membrane sample was inserted and floated on top of the RhB solution. Before exposure to simulated solar light, the mixtures were kept in the dark at room temperature for 12 h to reach adsorption−desorption equilibrium. A 300 W Xe lamp (Shanghai Bilon Instrument Co., Ltd.) equipped with a Fresnel lens (Shenzhen Salens Technology Co., Ltd.) was used as the light source. After preconditioning, the quartz beaker with RhB solution and membrane sample was placed at the focal position of the Xe lamp and irradiated by the Xe light from the top. The illumination power was maintained at ∼2.1 W during the irradiation, and the absorbance spectra of the sample solution were recorded every 30 min using the Ocean Optics spectrometer. The concentration of RhB was determined by the absorbance at 553 nm. The following equation was used to calculate the degradation degree (De) of RhB:

addition, an infrared (IR) camera (FLIR T620, FLIR Systems, Inc., U.S.A.) was used to monitor the surface temperature of the samples during the experimental process. Before measurement, the temperature of the IR camera was calibrated using a calibrated thermocouple (Model K−H-GGF; Beijing Qiaomu Automation Technology Company, China), and the temperature uncertainty of the IR camera is ∼1.0 °C.



RESULTS AND DISCUSSION The Au NPs synthesized were visualized by TEM. The size of the particles was estimated to be ∼50 nm based on a statistical calculation.30 After filtering through the AAO membrane, the Au NPs (0.5 mg) formed a uniform and dense packed layer on top of the AAO with layer thickness of ∼1 μm (Figure 2a). As a directly contacting layer on the porous AAO substrate (with a pore size of 20 nm), the particle size of Au NPs was chose to be ∼50 nm, which is large enough to avoid blocking the pores in AAO substrate during the filtration process, and also small enough to minimize the loss of TiO2 NPs during the filtration process to deposit the TiO2 NP layer. Compared with other assembly processes for NPs, such as evaporation-assisted assembly,31,32 interfacial assembly,30,33 and spin-coating,34−36 filtration is a fast and simple approach for the generation of uniform NP films.37,38 Such a process is especially useful for the fabrication of thick NP films over a relatively large area. Another important advantage of using a filtration process in the assembly of NPs is the flexibilityboth the composition and the thickness of the NP films can be easily tuned through the control of NP solutions. This flexibility also provides the possibility of tuning the microstructure and functionality of the NP films generated. In this study, to fabricate membranes with both TiO2 NPs for the photocatalytic degradation function and Au NPs for the function of plasmonic enabled solar-driven evaporation, a layer of 25 nm TiO2 NP film with discrete islands (Figure 2b) was formed on top of the Au NP film layer through the second filtration process after the first filtration step for the formation of Au NP film. The distinct three-layered structure can be clearly seen with a cross-sectional SEM image under a high magnification and also EDS mapping in Figure S1 (Supporting Information). The morphology of the separated micron-sized islands of TiO2 NPs helps the penetration of solar light into the underlying Au NP film. Such three-layered membrane design provides the desired bifunctionalityphoto-

De = (C0 − C)/C0 × 100% where C0 is the initial concentration of RhB and C is the concentration at the irradiation time of t. Due to the evaporation of water during the photocatalytic testing, the concentration of the RhB was calibrated according to the weight loss of the solution. After finishing each test, the membrane samples were rinsed with DI water thoroughly and dried for the next measurement. The above procedure was repeated at least 3 times for each sample. Evaporation Performance Measurement. To test the performance of solar-driven water evaporation using the bifunctional membrane, the weight loss of the sample solution was measured every 30 min by an electronic balance with four-decimal precision (FR124CN, Ohaus Instrument, Shanghai, China). The weight loss of the sample solution was plotted as the function of irradiation time. In C

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces

Figure 3. Schematic setup for photocatalytic degradation and evaporation test of the bifunctional membrane under solar illumination.

Figure 4. Optical absorption and photodegradation performance of different samples: (a) Absorption spectra; (b) Photocatalytic degradation of RhB; (c) Repeated photocatalytic degradation of RhB for continuous 8 cycles.

catalysis for pollution degradation and photothermal conversion for solar-driven water evaporation, both of which contribute to the purification of the contaminated water. Figure 3 shows the experimental setup for the performance evaluation of the bifunctional membrane. The sample was inserted and floated on the upper part of the solution with the

top surface immersed under the air−water interface. The placement of the membrane at the top portion of the solution helps localize the solar-thermal heat close to the air−water interface and thus enables efficient solar-driven evaporation process without losing heat to the bulk of the liquid underneath the membrane. The immersion of the membrane below the D

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces

Figure 5. Water vapor generation by different samples. (a) Evaporation of different samples under the simulated solar light. (b−e) Surface temperature study of different samples during the testing. (b) TiO2−Au-AAO sample before light illumination; (c) TiO2−Au-AAO sample after 2 h of light illumination; (d) Au-AAO sample after 2 h of light illumination; (e) TiO2-AAO sample after 2 h of light illumination.

the membrane with 0.5 mg of TiO2 has demonstrated stable photocatalytic degradation performance after repeating the degradation test for 8 cycles continuously. The improvement in the photocatalytic property of the TiO2−Au-AAO membrane should be attributed to the following three effects. First, the Au NP film under the TiO2 film helps enhance the light absorption of the TiO2 NPs through the plasmonic enhancement effect.40−42 Such enhancement leads to the improvement in the efficiency of photoreaction of the nearby TiO2 NPs. Second, the Au NP film should also facilitate electron−hole charge transfer and separation through the formation of Schottky junctions between the Au NPs and TiO2 NPs, which results in the increased photocatalytic activity.43 Third, the thermal effect caused by plasmonic photothermal conversion of the Au NP film should also play a role in the improvement of photocatalytic activity of the three-layer composite membrane.44 Solar-driven evaporation is an environmentally friendly and cost-efficient approach that has recently attracted increased attention.22−25 As demonstrated in our recent studies, efficient evaporation can be achieved by taking advantage of localized heating effect of self-assembled plasmonic Au NP thin film freefloating or floating on a support at the air−water interface.26−28 Due to the confinement of the solar absorption at the top portion of the bulk liquid, the thermal energy converted from the absorbed solar light could be mostly used for the evaporation process at the evaporative surface. In this study, the localized heating effect of the Au NP film within the TiO2− Au-AAO membrane was also employed for the efficient water vapor generation. Purified water was generated after the condensation of the evaporated water. As shown in Figure 5b−e, the surface temperature of the TiO 2 −Au-AAO membrane was ∼34 °C before Xe light illumination. After 60 min of light radiation, the surface temperature reached ∼58 °C. The Au-AAO sample showed a slightly higher surface temperature of 62 °C than that of the TiO2−Au-AAO sample while the TiO2-AAO sample showed relatively low surface temperature of 48 °C after same duration of irradiation, which is attributed to the absence of the Au NP layer. The temperature rise for the TiO2-AAO samples is due to the absorption of infrared light from the Xe-lamp and also the optical-thermal conversion from the photons even within the

air−water interface facilitates the solution exchange for photodegradation. During the measurement, the sample beaker was placed on a balance so the weight loss could be recorded in situ. The IR camera was used to measure the surface temperature of the samples. The light absorbance spectra for different samples are shown in Figure 4a. The sample of AAO covered with only TiO2 NPs showed good light absorbance in the wavelength range below 400 nm. Both the Au-AAO sample and the TiO2−Au-AAO sample showed broadband light absorbance. This increased light absorbance should be attributed to the Au NP film underneath the TiO2 NP layer. The Au NPs have surface plasmonic absorption. When the NPs form the continuous film, the plasmonic absorption delocalizes and such delocalization results in the broadening of the light absorption for the samples that contain Au NP layers.39 The photocatalytic property of different membrane samples was evaluated through a liquid-phase photodegradation study of the model contaminant compound, RhB dye. As displayed in Figure 4b, under Xe light exposure with a light intensity of ∼6.7 sun, the aqueous solution containing only RhB showed a very small degree of degradation. After 2 h of irradiation, only ∼8% of RhB was degraded. This small degree of degradation could be due to the self-degradation of RhB without any catalysts. On the other hand, the Au-AAO, TiO2-AAO, TiO2−Au-AAO membrane samples all showed increased photocatalytic performance. The TiO2−Au-AAO membrane floating at the air−water interface showed the highest photocatalytic activity with ∼60% of RhB degraded after 2 h of light irradiation. Without the middle Au NP layer between the TiO2 NP layer and AAO layer, the photocatalytic activity decreased, and ∼48% RhB was degraded after 2 h for TiO2-AAO membrane sample. Under the same condition, the sample containing only Au NP layer on AAO showed an even lower activity in the degradation of RhB, with ∼35% RhB was degraded after the same duration of light illumination. We also studied the impact of the amount of TiO2 NP on photocatalytic degradation performance. As shown in Figure S2, with 2.5-fold reduction of TiO2 NP amount, there are much less and smaller islands of TiO2, which reduced the total surface area of the TiO2 layer. Such reduced surface area actually led to the small decrease in the degradation performance (Figure S3a). The bifunctional membrane design also showed a relatively good reusability. Figure 4c shows that E

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces

Figure 6. Water purification by bifunctional membrane: (a) absorption before and after purification for 2 h; (b) optical images of the water in cuvettes before and after purification for 2 h.

TiO2 absorption band. For the Au-AAO and TiO2−Au-AAO samples, the plasmonic photothermal effect from Au NPs converts solar energy into thermal energy. Such conversion results in a higher interfacial temperature and also enables the higher rates of evaporation than the samples without Au NPs. As indicated in Figure 5a, without the Au NP layer, the evaporation rate for the TiO2-AAO sample is 0.24 g/cm2/h. The Au-AAO sample and TiO2−Au-AAO sample, on the other hand, showed a much higher evaporation capability, with evaporation rates of 0.51 g/cm2/h and 0.44 g/cm2/h, respectively. The Au-AAO sample has a slightly higher rate of evaporation than that of TiO2−Au-AAO sample. The light absorption and scattering from the TiO2 NP islands on top of the Au NP layer decreased the amount of the photons that reached the surface of the Au NPs, and resulted in the decreased evaporation performance for TiO2−Au-AAO sample. In the three-layered bifunctional membrane that was fabricated in this study, each layer has its desired role. The top TiO2 NP layer works as the photocatalytic layer for the degradation of contaminates in water. The middle Au NP layer works as the plasmonic photothermal converter for the water vapor generation and also helps enhance the photocatalytic activity through plasmonic effects.40−42 As long as the size of the Au NP is larger than the pore size of AAO membrane, the photothermal-enabled evaporation performances are close to each other for films with Au NPs of different sizes (Figure S4) due to the broad band absorption of the films.26−28 The bottom AAO membrane serves the following three functions: at the fabrication step it works as the filter for the fabrication of bifunctional membrane; later during the water purification step, it serves as the supporting layer to ensure both the mechanical robustness of the composite membrane and the capillary flow of the water through the numerous pores on the membrane. Additionally, the low thermal conductivity of the AAO membrane also makes it a good thermal insulation layer to minimize the heat loss to the lower part of the solution through thermal conduction. With the three-layer design, this composite membrane works as a bifunctional membrane for different degrees of water purification. After light illumination, the liquid remaining in the

beaker is the partially purified water that was cleaned through the photocatalytic reaction by TiO2. The evaporative function of the membrane, on the other hand, generates purified water vapor and thus purified liquid water after the condensation process. Indeed, the absorbance study showed that the liquid collected from the water vapor contains no RhB, while the solution left in the beaker after 2 h of Xe light illumination contains partial purified water with ∼40% of RhB remaining in the solution (Figure 6). Increasing the irradiation time would further purify the water left in the beaker to the degree that is needed for different applications.



CONCLUSION In summary, a three-layer bifunctional composite membrane with photocatalytic function and photothermal driven evaporation function was designed and fabricated for efficient water purification using solar light. Previously, the loss of energy efficiency in the photocatalytic water purification has been the result of two processes: (1) the absorption process with relative narrow absorption band of photocatalysts; and (2) the photothermal conversion with the absorbed photons. The integration of the photothermal driven evaporation function with the photocatalytic function helps expand the range of useful solar light for the clean water generation and also takes advantage of the heat generated by the catalysts for further efficiency enhancement. Such multilayered membrane enables the generation of both pure and partial purified water in a single step. Pure water was generated through the photothermal evaporation process and subsequent condensation, and partially purified water was the result of the photocatalytic degradation process. Compared to the membrane with only a single functionality, the bifunctional design provides a new approach for water purification, and the novel method also opens up an alternative strategy to maximize solar energy conversion and utilization. This reported membrane design could be further improved, for example, by replacing the Au NPs with other low cost photothermal converters, such as carbon NPs, and by utilizing flexible porous substrates instead of the rigid ceramic AAO substrate, to explore practical applications for pure water generation in large scale in the future. F

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces



(10) Chen, X.; Mao, S. S. Titanium Dioxide Nanomaterials: Synthesis, Properties, Modifications, and Applications. Chem. Rev. 2007, 107, 2891−2959. (11) Chandrasekharan, N.; Kamat, P. V. Improving the Photoelectrochemical Performance of Nanostructured TiO2 Films by Adsorption of Gold Nanoparticles. J. Phys. Chem. B 2000, 104, 10851−10857. (12) Li, H.; Bian, Z.; Zhu, J.; Huo, Y.; Li, H.; Lu, Y. Mesoporous Au/ TiO2 Nanocomposites with Enhanced Photocatalytic Activity. J. Am. Chem. Soc. 2007, 129, 4538−4539. (13) Yan, W.; Mahurin, S. M.; Pan, Z.; Overbury, S. H.; Dai, S. Ultrastable Au Nanocatalyst Supported on Surface-Modified TiO2 Nanocrystals. J. Am. Chem. Soc. 2005, 127, 10480−10481. (14) Arabatzis, I. M.; Stergiopoulos, T.; Andreeva, D.; Kitova, S.; Neophytides, S. G.; Falaras, P. Characterization and Photocatalytic Activity of Au/TiO2 Thin Films for Azo-Dye Degradation. J. Catal. 2003, 220, 127−135. (15) Fujishima, A.; Zhang, X.; Tryk, D. A. TiO2 Photocatalysis and Related Surface Phenomena. Surf. Sci. Rep. 2008, 63, 515−582. (16) Bian, Z.; Tachikawa, T.; Zhang, P.; Fujitsuka, M.; Majima, T. Au/TiO2 Superstructure-based Plasmonic Photocatalysts Exhibiting Efficient Charge Separation and Unprecedented Activity. J. Am. Chem. Soc. 2013, 136, 458−465. (17) Li, X. Z.; Li, F. B. Study of Au/Au3+-TiO2 Photocatalysts toward Visible Photooxidation for Water and Wastewater Treatment. Environ. Sci. Technol. 2001, 35, 2381−2387. (18) Sonawane, R. S.; Dongare, M. K. Sol−Gel Synthesis of Au/TiO2 Thin Films for Photocatalytic Degradation of Phenol in Sunlight. J. Mol. Catal. A: Chem. 2006, 243, 68−76. (19) Ghasemi, H.; Ni, G.; Marconnet, A. M.; Loomis, J.; Yerci, S.; Miljkovic, N.; Chen, G. (2014). Solar Steam Generation by Heat Localization. Nat. Commun. 2014, 5, 4449. (20) Zhang, L.; Tang, B.; Wu, J.; Li, R.; Wang, P. Hydrophobic Lightto-Heat Conversion Membranes with Self-Healing Ability for Interfacial Solar Heating. Adv. Mater. 2015, 27, 4889−4894. (21) Ito, Y.; Tanabe, Y.; Han, J.; Fujita, T.; Tanigaki, K.; Chen, M. Multifunctional Porous Graphene for High-Efficiency Steam Generation by Heat Localization. Adv. Mater. 2015, 27, 4302−4307. (22) Neumann, O.; Urban, A. S.; Day, J.; Lal, S.; Nordlander, P.; Halas, N. J. Solar Vapor Generation Enabled by Nanoparticles. ACS Nano 2012, 7, 42−49. (23) Hogan, N. J.; Urban, A. S.; Ayala-Orozco, C.; Pimpinelli, A.; Nordlander, P.; Halas, N. J. Nanoparticles Heat through Light Localization. Nano Lett. 2014, 14, 4640−4645. (24) Yen, Y. T.; Chen, C. W.; Fang, M.; Chen, Y. Z.; Lai, C. C.; Hsu, C. H.; Wang, Y. C.; Lin, H.; Shen, C. H.; Shieh, J. M.; Ho, J. C.; Chueh, Y. L. Thermoplasmonics-Assisted Nanoheterostructured AuDecorated CuInS2 Nanoparticles: Matching Solar Spectrum Absorption and its Application on Selective Distillation of Non-Polar Solvent Systems by Thermal Solar Energy. Nano Energy 2015, 15, 470−478. (25) Neumann, O.; Feronti, C.; Neumann, A. D.; Dong, A.; Schell, K.; Lu, B.; Kim, E.; Quinn, M.; Thompson, S.; Grady, N.; Nordlander, P.; Oden, M.; Halas, N. J. Compact Solar Autoclave Based on Steam Generation Using Broadband Light-Harvesting Nanoparticles. Proc. Natl. Acad. Sci. U. S. A. 2013, 110, 11677−11681. (26) Liu, Y.; Yu, S.; Feng, R.; Bernard, A.; Liu, Y.; Zhang, Y.; Duan, H.; Shang, W.; Tao, P.; Song, C.; Deng, T. A Bioinspired, Reusable, Paper-Based System for High-Performance Large-Scale Evaporation. Adv. Mater. 2015, 27, 2768−2774. (27) Wang, Z.; Liu, Y.; Tao, P.; Shen, Q.; Yi, N.; Zhang, F.; Liu, Q.; Song, C.; Zhang, D.; Shang, W.; Deng, T. Evaporation: Bio-Inspired Evaporation Through Plasmonic Film of Nanoparticles at the Air− Water Interface. Small 2014, 10, 3234−3239. (28) Yu, S.; Zhang, Y.; Duan, H.; Liu, Y.; Quan, X.; Tao, P.; Shang, W.; Wu, J.; Song, C.; Deng, T. The Impact of Surface Chemistry on the Performance of Localized Solar-Driven Evaporation System. Sci. Rep. 2015, 5, 13600.

ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsami.5b09996. Energy-dispersive spectroscopy (EDS) mapping of the TiO2−Au-AAO membrane; SEMs and performance of membranes with TiO2 NP layer of different thicknesses; evaporation rate of membranes with Au NP (50 and 100 nm in diameter) layer of different thicknesses (PDF)



AUTHOR INFORMATION

Corresponding Authors

*E-mail: [email protected]. *E-mail: [email protected]. Author Contributions ∥

Y.L. and J.L. contributed to this work equally.

Notes

The authors declare no competing financial interest.



ACKNOWLEDGMENTS This work was supported by National Natural Science Foundation of China (Grant No: 91333115, 51420105009, 51521004, 51403127 and 21401129), Natural Science Foundation of Shanghai (Grant No: 13ZR1421500, 14ZR1423300), and the Zhi-Yuan Endowed fund from Shanghai Jiao Tong University. The authors thank Professor Peng Zhang, Mr. Shipu Li, Mr. Shengtao Yu, Mr. Yao Zhang, Mr. Zhongyong Wang for the help with this project. We also thank the Instrumental Analysis Center of Shanghai Jiao Tong University for the access to SEM and TEM.



REFERENCES

(1) Malato, S.; Fernández-Ibáñ ez, P.; Maldonado, M. I.; Blanco, J.; Gernjak, W. Decontamination and Disinfection of Water by Solar Photocatalysis: Recent Overview and Trends. Catal. Today 2009, 147, 1−59. (2) Shannon, M. A.; Bohn, P. W.; Elimelech, M.; Georgiadis, J. G.; Marinas, B. J.; Mayes, A. M. Science and Technology for Water Purification in the Coming Decades. Nature 2008, 452, 301−310. (3) Elimelech, M.; Phillip, W. A. The Future of Seawater Desalination: Energy, Technology, and the Environment. Science 2011, 333, 712−717. (4) Mills, A.; Davies, R. H.; Worsley, D. Water Purification by Semiconductor Photocatalysis. Chem. Soc. Rev. 1993, 22, 417−425. (5) Dong, S.; Feng, J.; Fan, M.; Pi, Y.; Hu, L.; Han, X.; Liu, M.; Sun, J.; Sun, J. Recent Developments in Heterogeneous Photocatalytic Water Treatment Using Visible Light-Responsive Photocatalysts: a Review. RSC Adv. 2015, 5, 14610−14630. (6) Fan, Y.; Ma, W.; Han, D.; Gan, S.; Dong, X.; Niu, L. Convenient Recycling of 3D AgX/Graphene Aerogels (X = Br, Cl) for Efficient Photocatalytic Degradation of Water Pollutants. Adv. Mater. 2015, 27, 3767−3773. (7) Sugita, T.; Mori, M.; Mase, A.; Noguchi, S. N.; Tokutome, T.; Fujii, K.; Hara, C.; Katayama, K.; Iwamoto, S.; Itabashi, H. Evaluation of the Water-treatment Ability of Silica-doped Titanium Dioxidecoated Glass Plates Using a Cationic Coupling Reagent Based on a Flow Analytical System. Anal. Sci. 2015, 31, 15−21. (8) Gaya, U. I.; Abdullah, A. H. Heterogeneous Photocatalytic Degradation of Organic Contaminants over Titanium Dioxide: a Review of Fundamentals, Progress and Problems. J. Photochem. Photobiol., C 2008, 9, 1−12. (9) Linsebigler, A. L.; Lu, G.; Yates, J. T. Photocatalysis on TiO2 Surfaces: Principles, Mechanisms, and Selected Results. Chem. Rev. 1995, 95, 735−758. G

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX

Research Article

ACS Applied Materials & Interfaces (29) Brown, K. R.; Walter, D. G.; Natan, M. J. Seeding of Colloidal Au Nanoparticle Solutions. 2. Improved Control of Particle Size and Shape. Chem. Mater. 2000, 12, 306−313. (30) Liu, Y.; Liu, Y.; Tao, P.; Shang, W.; Song, C.; Deng, T. Vertical Segregation in the Self-Assembly of Nanoparticles at the Liquid/Air Interface. Nanoscale 2014, 6, 14662−14666. (31) Bigioni, Y. P.; Lin, X. M.; Nguyen, T. T.; Corwin, E. I.; Witten, T. A.; Jaeger, H. M. Kinetically Driven Self-Assembly of Highly Ordered Nanoparticle Monolayers. Nat. Mater. 2006, 5, 265−270. (32) Rabani, E.; Reichman, D. R.; Geissler, P. L.; Brus, L. E. DryingMediated Self-Assembly of Nanoparticles. Nature 2003, 426, 271−274. (33) Duan, H.; Wang, D.; Sobal, N. S.; Giersig, M.; Kurth, D. G.; Mohwald, H. Magnetic Colloidosomes Derived from Nanoparticle Interfacial Self-Assembly. Nano Lett. 2005, 5, 949−952. (34) Xia, D.; Brueck, S. R. J. A Facile Approach to Directed Assembly of Patterns of Nanoparticles Using Interference Lithography and Spin Coating. Nano Lett. 2004, 4, 1295−1299. (35) Xia, D.; Biswas, A.; Li, D.; Brueck, S. R. J. Directed SelfAssembly of Silica Nanoparticles into Nanometer-Scale Patterned Surfaces Using Spin-Coating. Adv. Mater. 2004, 16, 1427−1432. (36) Lin, Y.; Boker, A.; He, J.; Sill, K.; Xiang, H.; Abetz, C.; Li, X.; Wang, J.; Emrick, T.; Long, S.; Wang, Q.; Balazs, A.; Russell, T. P. SelfDirected Self-Assembly of Nanoparticle/Copolymer mixtures. Nature 2005, 434, 55−59. (37) Kong, B.; Geng, J.; Jung, H. Layer-by-Layer Assembly of Graphene and Gold Nanoparticles by Vacuum Filtration and Spontaneous Reduction of Gold Ions. Chem. Commun. 2009, 16, 2174−2176. (38) Zhu, C.; Guo, S.; Zhai, Y.; Dong, S. Layer-by-Layer SelfAssembly for Constructing a Graphene/Platinum Nanoparticle ThreeDimensional Hybrid Nanostructure Using Ionic Liquid as a Linker. Langmuir 2010, 26, 7614−7618. (39) Taylor, R. W.; Esteban, R.; Mahajan, S.; Coulston, R.; Scherman, O. A.; Aizpurua, J.; Baumberg, J. J. Simple Composite Dipole Model for the Optical Modes of Strongly-Coupled Plasmonic Nanoparticle Aggregates. J. Phys. Chem. C 2012, 116, 25044−25051. (40) Linic, S.; Christopher, P.; Ingram, D. B. Plasmonic-Metal Nanostructures for Efficient Conversion of Solar to Chemical Energy. Nat. Mater. 2011, 10, 911−921. (41) Wang, P.; Huang, B.; Dai, Y.; Whangbo, M. H. Plasmonic Photocatalysts: Harvesting Visible Light with Noble Metal Nanoparticles. Phys. Chem. Chem. Phys. 2012, 14, 9813−9825. (42) Hou, W.; Cronin, S. B. A Review of Surface Plasmon Resonance-Enhanced Photocatalysis. Adv. Funct. Mater. 2013, 23, 1612−1619. (43) Qu, Y.; Duan, X. Progress, Challenge and Perspective of Heterogeneous Photocatalysts. Chem. Soc. Rev. 2013, 42, 2568−2580. (44) Clavero, C. Plasmon-induced Hot-Electron Generation at Nanoparticle/Metal-oxide Interfaces for Photovoltaic and Photocatalytic Devices. Nat. Photonics 2014, 8, 95−103.

H

DOI: 10.1021/acsami.5b09996 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX