Carbon Nanotube-Supported Cu3P as High-Efficiency and Low-Cost

Subscriber access provided by RUTGERS UNIVERSITY

Article

Carbon Nanotube-supported Cu3P as high-efficiency and low-cost cocatalysts for exceptional semiconductor-free photocatalytic H2 Evolution Rongchen Shen, Jun Xie, Yingna Ding, Shu-yuan Liu, Andrzej Adamski, Xiaobo Chen, and Xin Li ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.8b05185 • Publication Date (Web): 26 Dec 2018 Downloaded from http://pubs.acs.org on January 1, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Carbon Nanotube-supported Cu3P as high-efficiency and low-cost cocatalysts for exceptional semiconductor-free photocatalytic H2 Evolution Rongchen Shen,a,b Jun Xie,a,b Yingna Ding,b Shu-yuan Liu,c Andrzej Adamski,d Xiaobo Chen,e* Xin Lia,b* a

College of Forestry and Landscape Architecture, Key Laboratory of Energy Plants

Resource and Utilization, Ministry of Agriculture, South China Agricultural University, Guangzhou 510642, PR China b

College of Materials and Energy, South China Agricultural University, Guangzhou

510642, PR China c

Department of pharmacology, Shenyang Medical College, Shenyang, 110034, PR

China. d

Jagiellonian University, Faculty of Chemistry, Ingardena 3, PL 30-060 Cracow,

Poland. e

Department of Chemistry, University of Missouri – Kansas City, Kansas City, MO, 64110, USA.

*Corresponding

author at: College of Forestry and Landscape Architecture, South China Agricultural University, Guangzhou 510642, P. R. China. Tel.: +86 20 85282633; fax: +86 20 85285596. E-mail address: [email protected] (X. Li), [email protected] (X. Chen).

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT Developing an inexpensive and high-efficiency hydrogen-production cocatalyst to replace the noble metal Pt remains a big challenge in the fields of sustainable photocatalytic hydrogen evolution. Herein, we report the exploration of a high-efficient binary noble metal free Cu3P-CNT H2-evolution cocatalyst by direct high-temperature phosphatizing of Cu(OH)2-CNT. Impressively, combining the advantages of noble metal free Cu3P and carbon nanotube (CNT), the binary Cu3P-CNT cocatalysts show high-efficient photocatalytic H2 evolution in Eosin Y(EY)-contained semiconductor-free photocatalytic systems. The maximum visible-light H2-generation rate for promising EY-Cu3P-CNT systems was 17.22 mmolg-1h-1. The highest apparent quantum efficiency (AQE) could reach 10.23% at 500 nm. More importantly, we found that the separation of photogenerated electrons and holes in the Eosin Y, the efficiency of electron transfer from EY to the active edge sites of Cu3P, and the electrocatalytic H2-evolution activity of Cu3P, could be simultaneously boosted via readily adding the conductive CNT, thus achieving the significantly improved photocatalytic H2 evolution. This work provides a simple and facile strategy to design highly efficient semiconductor-free photocatalytic proton-reduction systems using high-activity transition metal phosphides (TMPs) and inexpensive carbon nanomaterials. KEYWORDS: Photocatalytic Hydrogen Evolution, noble metal-free Cu3P Cocatalysts, Solar Fuel, Carbon nanotube (CNT), Dye sensitization.

Introduction Hydrogen, as an ideal replacement for fossil fuels, has long been recognized as one of the most promising, renewable and environmental fuels.1,2 The photocatalytic water splitting for hydrogen production, as a cost-effective and environmentally hydrogen-production way, has gained international interest in recent years.3,4 Previous work had fully confirmed that noble metal Pt could serve as an efficient cocatalyst for photocatalytic HER. However, its application was limited by its expensive price and scare abundance. Thus, it is of great urgency to


Page 2 of 22

Page 3 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


exploit high-performance and earth-abundant cocatalysts toward HER.5-7 To date, many no-noble metal cocatalyst such as NiSx8-11 MoS212-18, Ni3C19,20, Ni(OH)x21-24 and WS225 had been studied. Particularly, transition metal phosphides (TMPs) have received lots of attention due to their merits of reversible binding and favorable dissociation of H2. Various earth-abundant TMPs, including NiPx26-29, CoPx30-32, CoNiPx33 and FeP34,35, have been shown to be the potential and appealing cocatalysts for photocatalytic HER applications.36 However, finding the really efficient and active TMPs-based photocatalytic hydrogen-production systems remains a great challenge. Noteworthily, integrating various nanostructured semiconducting photocatalysts (i.e, CdS,5,37-40 ZnxCd1-xS,41,42 g-C3N47,26-30,34, TiO231 and their composites43) and TMP cocatalysts (i.e., NiPx, CoPx, FePx and CoNiPx) have been extensively considered a promising and effective strategy toward improving the photocatalytic HER.44 For instance, in our previous work, we found that g-C3N4 could achieve a significant improvement in the photocatalytic activity by loading Co2P or Ni12P5 as a cocatalyst.27,36 Furthermore, Co2P and single Co1-P4 site have been found to act as a cocatalyst to boost the photocatalytic performance of g-C3N4.30 Cu3P as an effective electrocatalyst has been widely employed in electrocatalytic hydrogen evolution.45-47 In principle, Cu3P has been extensively employed as an efficient cocatalyst to modify semiconductor photocatalysts for photocatalytic HER.6,48,49 However, to the best of our knowledge, there has been no report on TMPs as the cocatalysts to construct the novel semiconductor-free hybrid systems for highly efficient photocatalytic H2 evolution. Compared with semiconductor-containing photocatalysts, semiconductor-free photocatalytic systems using the dye as light harvester could exhibit many disadvantages, such as easy fabrication, low cost, avoided light shading effects, large number of charge-transfer channels and interfaces, and the perfect focus on the design and optimization of active cocatalyst sites. As well known, the rapid shift of photogenerated charge is an important factor for efficient photocatalytic HER.50 Typically, in our previous work, the metallic nanocarbon materials with the excellent conductivity could serve as a conductive



Page 4 of 22

additives to effectively improve photocatalytic hydrogen-generation performance for the earth-abundant cocatalysts over the semiconductor photocatalysts.51 In general, the metallic carbon nanomaterials could accelerate the transfer of photogenerated electrons, thus resulting in an enhancement of the photocatalytic hydrogen-production

activity

and

stability

over

the

earth-abundant

cocatalysts.22,50,52-54 Inspired by these works, we aimed to improve the photocatalytic H2-evolution activity of TMP cocatalysts by loading a conductive CNT. In this way, CNT could induce the transfer of photogenerated charges from the excited dye to the surface of TMP due to its excellent conductivity. Thus result in an enhancement of the photocatalytic H2 evolution. Herein, strongly inspired by these meaningful works, we report for the first time on rationally integrating the noble metal-free Cu3P-CNT cocatalyst and Eosin Y dye in one semiconductor-free system for high-efficient photocatalytic H2 generation. The high-efficient binary noble metal free Cu3P-CNT H2-evolution cocatalyst was synthesized by high-temperature phosphatizing of Cu(OH)2-CNT. The Cu3P-CNT sensitized by Eosin Y (EY) displayed an excellent photocatalytic hydrogen-production performance. The optimal H2-generation rate of the photocatalysts in a 15% triethanolamine (TEOA) aqueous solution could reach 17.22 mmol g-1h-1. A high AQE of 10.23% over EY-Cu3P-CNT was achieved at 500 nm illumination. Experimental section Synthesis of Cu3P-CNT Cu3P were prepared by our previous work, first copper nitrate and NaOH were mixed by magnetic stirring for 0.5 h to obtain the Cu(OH)2. The Cu3P was synthesized by heating Cu(OH)2 and NaH2PO2 at 300 ℃ (3 ℃ min-1) for 1h. The Cu3P-CNT was prepared by adding the CNT into the copper nitrate solution and sonicating for 2 h. Then add the NaOH in to the previous slurry to obtain Cu(OH)2CNT. The Cu3P-CNT was synthesized by heating Cu(OH)2-CNT and NaH2PO2 at 300 ℃for 1h. The mass ratio of Cu(OH)2 to CNT was denoted as Cu3P-X%CNT. Characterizations


Page 5 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


XRD (Cu Kα, MSAL-XD2 diffractometer), TEM and HRTEM (JEM-2100HR 200 kV, Japan), photoluminescence (PL) spectra (LS 50B Perkin Elmer) were done according to our previous methods. 6,32 Photocatalytic and electrocatalytic reaction procedures The photocatalytic H2 production experiments were carried out in a 100 ml three-neck Pyrex flask. 0.05 g of Cu3P-CNT binary composites and 18 mg EY were sonicated in 80 ml 15 vol% TEOA aqueous solution. Before illuminating with a 350 W Xe lamp (PLS-SXE300, Beijing Perfect Light Technology Co., Ltd), the reactant solution was bubbled with N2 for 30 min. The produced hydrogen was determined using a GC-9500 chromatograph. The following equation 1 was used to calculate the AQE. < 𝝉 >=

𝒕𝒉𝒆 𝒏𝒖𝒎𝒃𝒆𝒓 𝒐𝒇 𝒉𝒚𝒅𝒓𝒐𝒈𝒆𝒏 𝒎𝒐𝒍𝒆𝒄𝒖𝒍𝒆 𝒕𝒉𝒆 𝒏𝒖𝒎𝒃𝒆𝒓 𝒐𝒇 𝒊𝒏𝒄𝒊𝒅𝒆𝒏𝒕 𝒑𝒉𝒐𝒕𝒐𝒔

∗ 𝟏𝟎𝟎%

(1)

The electrocatalytic H2 production reactions were also same as our previous work.5,6,32,52 Results and discussion The structures and compositions of photocatalysts Figure 1 displays the XRD patterns of prepared samples. None difference could be found between pure Cu3P and Cu3P-3%CNT. Three primary peaks at 35.4°, 44.1° and 45.6° are attributed to the (102), (103) and (110) plane diffraction for hexagonal Cu3P (PDF#25-0302). Furthermore, the intense peak at around 24° was attributed to amorphous carbon22. Obviously, three main diffraction peaks do not show a significant change, which indicates the crystal structure of hexagonal Cu3P still remains untouched after loading CNT.



Figure 1. The XRD patterns of CNT, Cu3P and Cu3P-CNT The structure and morphology of the as prepared Cu3P-CNT were further investigated by TEM and HRTEM. As displayed in Figure 2A and B, CNT is comprised of nanotubes with diameters range from 30 to 50 nm. For the HRTEM images (Figure 2C and D), the hexagonal Cu3P exhibits an interlayer distance of 0.204 nm and 0.252 nm, corresponding to the (110) and (102) plane of hexagonal Cu3P. Notably, there is not lattice fringe corresponding to CNT could be found in the HRTEM images due to the amorphous structures of CNT.53 The TEM and HRTEM results clearly show that CNT were deposited on the surface of the Cu3P. Additionally, elemental maps (Figure 3A-D) displayed a uniform spatial distribution of C, Cu and P species. The profiles revealed the coexistence of Cu3P and CNT.


Page 6 of 22

Page 7 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 2. (A) and (B) TEM images of Cu3P-3%CNT sample; (C) and (D) HRTEM of Cu3P-3%CNT sample.

Figure 3. (A) FESME and (B-D) the corresponding elemental mapping of C, Cu and P elements Cu3P-3%CNT sample.



Figure 4. (A)XPS survey spectra, (B)-(D) high-resolution of XPS spectra of C 1s, Cu 2p and P 2p region for Cu3P-3%CNT composites.

Figure 5. high-resolution of XPS spectra of (A) Cu 2p and (B) P 2p region for Cu3P and Cu3P-3%CNT composites.

To future understand the chemical bonds of the Cu3P-CNT, X-ray photoelectron spectra (XPS) of Cu3P-CNT were analyzed. As shown in Figure 4A. The binary Cu3PCNT mainly consisted of P, C, O and Cu, which consists with the elemental mapping results. Notably, as observed in Figure 4B, one peak of the C=C bonds at around 284.4 eV, which was often used to represent the standard reference carbon. Furthermore, for


Page 8 of 22

Page 9 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


high resolution Cu 2p spectra (Figure 4C), two peaks of Cu 2p3/2 and Cu 2p1/2 at around 932.6 eV as well as 952.8 eV, which are attributed to Cu3P. The peaks at 935.1 eV (Cu 2p3/2), 940.9 eV and 943.1 eV (Cu1+ satellite) as well as 954.8 eV (Cu2+ 2p1/2) are corresponding to oxidized copper Cu(II) due to the surface oxidation

probably.47,55

Additionally, as showed in Figure 4D, the characteristic peaks at 129.2 eV, 130.1 eV and 133.4 eV can be supposed to the phosphide species (P 2p3/2 and P2p1/2) and oxidized species (P2O5 or PO43-), respectively. Furthermore, in Cu3P, the Cu 2p3/2 (932.6 eV)

is

positively shifted from that of metallic Cu(932.3 eV), while the P 2p3/2 (129.2 eV) has a lower binding energy than red P (130.0 eV), indicating that the Cu possess positive charge but the P possess negative charge.45 As showed in Figure 5A, compared to the Cu 2p3/2 binding energy in the pure Cu3P, the binding energy of Cu 2p3/2 in the Cu3P3%CNT was positive to 932.6 eV. Furthermore, the binding energy of P 2p3/2 and P2p1/2 in Cu3P-3%CNT also showed a positive shift compared to the P 2p3/2 and P2p1/2 in Cu3P (Figure 5B). These results suggest that there is a strong interaction between Cu3P and CNT, which was from the co-electron cloud formed between Cu3P and CNT.56 The XRD, TEM, HRTEM, EDS mapping and XPS results suggest that the CNT were successfully loaded on the surface of Cu3P and CNT have little effect on the crystal structure of the Cu3P. The activities and stabilities of photocatalysts The HER occurs on the surface of catalysts via the Volmer reaction.57 C + e- + H2O→C-Hads + OH-

(2)

followed by an electrochemical desorption via the Heyrovsky reaction58 H2O + e- + C-Hads→C+ OH + H2

(3)

Where C is the cocatalyst and Hads is H-adsorbed state. The as-prepared Cu3PCNT binary cocatalysts were carried out for hydrogen evolution in 15% TEOA and EY solution under visible light. The results showed that CNT play an important role in enhancing the photocatalytic hydrogen evolution activity. Figure 6A shows the comparison of the photocatalytic hydrogen generation performance over Cu3PCNT and pure Cu3P. The corresponding average H2-evolution rates were calculated



Page 10 of 22

and shown in Figure 6B. It could be found that an appropriate amount of CNT could significantly improve the photocatalytic hydrogen generation over the Cu3P cocatalyst. For Cu3P cocatalyst alone, a hydrogen evolution rate of 7.44 mmolh1g-1

can be achieved. When loading an appropriate amount of CNT as the additives,

Cu3P-3%CNT shows a hydrogen-generation rate of 17.22 mmolh-1g-1, which was 2.5-folder enhanced compared to the pure Cu3P. Notably, the binary Cu3P-CNT cocatalyst displayed an increase of photocatalytic performance when the loading contents of CNT are increased from 0.5 to 3 wt%, giving an average hydrogen evolution rate of 8.99 to 17.22 mmolh-1g-1. On the contrary, an obvious decrease of photocatalytic hydrogen-evolution performance was observed when the content of CNT is higher 3%. This result could be explained by follows: excessive amount of CNT may lead to decrease the surface-active sites of the Cu3P.22,50,54,59 More importantly,

compared

with

previously-reported

system,

although

the

photocatalytic performance over this EY-Cu3P-CNT is lower than that of THPP/Pt system (19.5mmolh-1g-1)60, its performance is better than the previously reported photocatalytic system for TPPH/RGO/Pt system (11.2 mmolh-1g-1)61, ZnTCPPMoS2/TiO2 system (0.102 mmolh-1g-1)62 and [ZnTMPyP]4+−MoS2/RGO system (2.56 mmolh-1g-1)63. These results suggested that the Cu3P-CNT could be served as a potential cocatalysts for HER. The stability of the photocatalyst was an important criterion. The stability of the EY-Cu3P-CNT photocatalyst was measured by repeating experiments were shown in Figure 7. The stability performance of Cu3P-3%CNT was tested over four cycles. In first cycle, the amount of hydrogen evolution was 34.7 mmol. After renewing the TEOA and EY, the hydrogen production performance was measured in the next cycle. The H2-evolution performance has fallen by about 20 percent after four cycle. This phenomenon is caused by the separation of the Cu3P from CNT during the photocatalytic process. Additionally, the AQE of EY-Cu3P-CNT system have also measured under 500nm. The highest AQE could reach as high as 10.23%.


Page 11 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 6. (A) Time profiles of photocatalytic hydrogen generation and (B) the average hydrogen-generation rate of (a) Cu3P (b) Cu3P-0.5%CNT, (c) Cu3P1%CNT, (d) Cu3P-3%CNT, (e) Cu3P-5%CNT and (f) Cu3P-10%CNT.

Figure 7. Repeated cycles of hydrogen production with Cu3P-3%CNT The mechanism investigation



Figure 8. (A) Steady state PL spectra and (B) impedance spectroscopy for different composites. Here, the loading of CNT could improve the migration and transfer of the photogenerated electron from EY to Cu3P cocatalyst. To confirm this, the photoluminescence (PL) spectra had been measured. It can be found that CNT loading could improve photocarrier separation compared to the pure Cu3P. From Figure 8A, the EY solution showed a typical emission peak at around 540 nm. With the incorporation of CNT into the Cu3P, the fluorescence emission of Cu3P was decreased obviously. It has been further confirmed that CNT could effectively improve the photogenerated-electron transfer in Cu3P-CNT binary photocatalyst. The role of CNT in the separation of hole-electron pairs could be further confirmed by using electrochemical impedance spectroscopy (EIS). As showed in Figure 8B, the diameter of the EIS spectrum for Cu3P-3%CNT was smaller than that of other samples. This result suggests that the lower electron-transfer resistance and recombination rate of charges in Cu3P-CNT-EY due to the introduction of CNT51. This EIS result is consistent with the result of the PL emission spectroscopy.


Page 12 of 22

Page 13 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 9. Polarization curves of different composites. The HER polarization curve is fit for analyzing the underlying photocatalytic H2-evolution mechanism. As displayed in Figure 9, the HER polarization curves of Cu3P, CNT and CNT-Cu3P composite photocatalysts. The cathodic current ranging from −0.4 to −0.8V vs RHE is dominantly attributed to the electrocatalytic H2 evolution. Obviously, electrocatalytic hydrogen-production overpotentials of the CNT-Cu3P sample exhibits much lower than Cu3P and CNT. A much lower overpotential at same condition for Cu3P-CNT suggests that CNT with high electrical conductivity and poor electrocatalytic HER performances could effectively separate the photogenerated holes and electrons as well as improve the hydrogen-generation kinetics during photocatalytic reaction. Therefore, Cu3PCNT exhibit a higher photocatalytic hydrogen-production activity in photocatalytic HER.



Scheme 1. The possible photocatalytic H2 production mechanism. Based on compression with previous work, as showed in Figure 9A, the work function of singlet state energy of excited EY (-2.97 eV vs. AVS.)64 is higher than the CB of Cu3P (-3.8 eV vs. AVS)48. As Cu3P contact with EY, electrons move from excited EY to Cu3P is thermodynamically favorable. More important, The CB of Cu3P is higher than the energy level for hydrogen production from water. (-4.50 eV vs. AVS).65 Thus, the reaction process of photocatalytic hydrogen generation in ternary EY-Cu3P-CNT systems could be described in Scheme 1. During the light absorption, EY were excited at a state of 1*EY form. Then the 1*EY transform to triplet excited states 3*EY quickly by an intercrossing transition. Next, the 3*EY were reduced to EY•− by TEOA66. EY was combined with the CNT with the noncovalent π−π interactions. The electrons were input from the EY•− to the CNT.56,67 Lastly, electrons were transferred to the surface of


Page 14 of 22

Page 15 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Cu3P. Interestingly, the loading of CNT on the surface of Cu3P could trap more electrons from photoexcited EY. Based on previous report, p atoms on the one hand can trap the protons, and on the other hand provide high performance for the separation of hydrogen.68 Wang and his coworkers indicated that P atoms on the P terminated surface of (001)-MoP could combine hydrogen at low coverage whilst desorbed hydrogen at high coverage.69 Based on the above conclusions, we forecast the hydrogen-evolution active sites of Cu3P catalyst is P atoms on the P terminated. Furthermore, the boosted electron transform from the surface of the CNT to the surface of the Cu3P could drive the more efficient photocatalytic hydrogen generation. These results demonstrate that dye-sensitization of Cu3P-CNT cocatalyst provides a new idea to construct nanocarbonbased photocatalysts for photocatalytic HER. Conclusions In this work, the Cu3P-CNT cocatalyst had been successful fabricated by a one-step phosphatizing Cu(OH)2-CNT composite. The as-prepared cocatalyst shows a excellent photocatalytic hydrogen evolution activity in a EY sensitized photocatalytic system. The maximum hydrogen-generation rate of the photocatalysts could reach 17.22 mmol g-1h-1 under visible light. The highest apparent quantum efficiency (AQE) could reach 10.23% at 500 nm. The CNT could act as an admirable electron acceptor and transporter for enhancing the charge separation, thus resulting in a great improvement in photocatalytic HER performance. we believed that the dye-sensitization low-cost cocatalyst and nanocarbon materials strategy will provide a fresh idea to construct a superefficient non nobol metal cocatalyst for photocatalytic water splitting HER. Acknowledgements X. Li would like to thank National Natural Science Foundation of China (51672089), Special funding on Applied Science and technology in Guangdong (2017B020238005) and the State Key Laboratory of Advanced Technology for Material Synthesis and Processing (Wuhan University of Technology) (2015-KF7) for their support. X. Chen appreciates the financial support from the U.S.



National Science Foundation (DMR-1609061), the College of Arts and Sciences, University of Missouri-Kansan City and University of Missouri Research Board. References: (1) Cao, S.; Yu, J. Carbon-based H2-production photocatalytic materials. J. Photoch. Photobio. C 2016, 27, 72-99. DOI: 10.1016/j.jphotochemrev.2016.04.002. (2) Low, J.; Yu, J.; Jaroniec, M.; Wageh, S.; Al-Ghamdi, A. A. Heterojunction Photocatalysts. Adv. Mater. 2017, 29, 1601694. DOI: 10.1002/adma.201601694. (3) Li, X.; Shen, R.; Ma, S.; Chen, X.; Xie, J. Graphene-based heterojunction photocatalysts. Appl. Surf. Sci. 2018, 430, 53-107. DOI: 10.1016/j.apsusc.2017.08.194. (4) Christoforidis, K. C.; Fornasiero, P. Photocatalytic Hydrogen Production: A Rift into the Future Energy Supply. Chemcatchem 2017, 9, 1523-1544. DOI: 10.1002/cctc.201601659. (5) Yuan, J.; Wen, J.; Zhong, Y.; Li, X.; Fang, Y.; Zhang, S.; Liu, W. Enhanced photocatalytic H2 evolution over noble-metal-free NiS cocatalyst modified CdS nanorods/g-C3N4 heterojunctions. J. Mater. Chem. A 2015, 3, 18244-18255. DOI: 10.1039/c5ta04573h. (6) Shen, R.; Xie, J.; Lu, X.; Chen, X.; Li, X. Bifunctional Cu3P Decorated g-C3N4 Nanosheets as a Highly Active and Robust Visible-Light Photocatalyst for H2 Production. Acs Sustain. Chem. Eng. 2018, 6, 4026-4036. DOI: 10.1021/acssuschemeng.7b04403. (7) Wen, J.; Xie, J.; Chen, X.; Li, X. A review on g-C3N4-based photocatalysts. Appl. Surf. Sci. 2017, 391, 72-123. DOI: 10.1016/j.apsusc.2016.07.030. (8) Zhang, J.; Qi, L.; Ran, J.; Yu, J.; Qiao, S. Z. Ternary NiS/ZnxCd1-xS/Reduced Graphene Oxide Nanocomposites for Enhanced Solar Photocatalytic H2-Production Activity. Adv. Energy Mater. 2014, 4, 1301925. DOI: 10.1002/aenm.201301925. (9) He, K.; Xie, J.; Li, M.; Li, X. In situ one-pot fabrication of g-C3N4 nanosheets/NiS cocatalyst heterojunction with intimate interfaces for efficient visible light photocatalytic H2 generation. Appl. Surf. Sci. 2018, 430, 208-217. DOI: 10.1016/j.apsusc.2017.08.191. (10)Jiang, D.; Zhu, L.; Irfan, R. M.; Zhang, L.; Du, P. Integrating noble-metal-free NiS cocatalyst with a semiconductor heterojunction composite for efficient photocatalytic H2 production in water under visible light. Chinese. J. Catal. 2017, 38, 2102-2109. DOI: 10.1016/s1872-2067(17)62956-5. (11)Chen, F.; Yang, H.; Wang, X. F.; Yu, H. G. Facile synthesis and enhanced photocatalytic H2-evolution performance of NiS2-modified g-C3N4 photocatalysts. Chinese. J. Catal. 2017, 38, 296-304. DOI: 10.1016/s1872-2067(16)62554-8. (12)Kumar, D. P.; Song, M. I.; Hong, S.; Kim, E. H.; Gopannagari, M.; Reddy, D. A.; Kim, T. K. Optimization of Active Sites of MoS2 Nanosheets Using Nonmetal Doping and Exfoliation into Few Layers on CdS Nanorods for Enhanced Photocatalytic Hydrogen Production. Acs Sustain. Chem. Eng. 2017, 5, 7651-7658. DOI: 10.1021/acssuschemeng.7b00978. (13)Lu, D.; Wang, H.; Zhao, X.; Kondamareddy, K. K.; Ding, J.; Li, C.; Fang, P.


Page 16 of 22

Page 17 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Highly Efficient Visible-Light-Induced Photoactivity of Z-Scheme g-C3N4/Ag/MoS2 Ternary Photocatalysts for Organic Pollutant Degradation and Production of Hydrogen. Acs Sustain. Chem. Eng. 2017, 5, 1436-1445. DOI: 10.1021/acssuschemeng.6b02010. (14)Wang, M.; Ju, P.; Li, J.; Zhao, Y.; Han, X.; Hao, Z. Facile Synthesis of MoS2/g-C3N4/GO Ternary Heterojunction with Enhanced Photocatalytic Activity for Water Splitting. Acs Sustain. Chem. Eng. 2017, 5, 7878-7886. DOI: 10.1021/acssuschemeng.7b01386. (15)Chava, R. K.; Do, J. Y.; Kang, M. Smart Hybridization of Au Coupled CdS Nanorods with Few Layered MoS2 Nanosheets for High Performance Photocatalytic Hydrogen Evolution Reaction. Acs Sustain. Chem. Eng. 2018, 6, 6445-6457. DOI: 10.1021/acssuschemeng.8b00249. (16)Gogoi, G.; Keene, S.; Patra, A. S.; Sahu, T. K.; Ardo, S.; Qureshi, M. Hybrid of g-C3N4 and MoS2 Integrated onto Cd0.5Zn0.5S: Rational Design with Efficient Charge Transfer for Enhanced Photocatalytic Activity. Acs Sustain. Chem. Eng. 2018, 6, 67186729. DOI: 10.1021/acssuschemeng.8b00512. (17)Huang, T.; Luo, Y. T.; Chen, W.; Yao, J. C.; Liu, X. H. Self-assembled MoS2GO Framework as an Efficient Cocatalyst of CuInZnS for Visible-Light Driven Hydrogen Evolution. Acs Sustain. Chem. Eng. 2018, 6, 4671-4679. DOI: 10.1021/acssuschemeng.7b03693. (18)Chai, B.; Liu, C.; Wang, C.; Yan, J.; Ren, Z. Photocatalytic hydrogen evolution activity over MoS2/ZnIn2S4 microspheres. Chinese. J. Catal. 2017, 38, 2067-2075. DOI: 10.1016/s1872-2067(17)62981-4. (19)He, K.; Xie, J.; Liu, Z.-Q.; Li, N.; Chen, X.; Hu, J.; Li, X. Multi-functional Ni3C cocatalyst/g-C3N4 nanoheterojunctions for robust photocatalytic H2 evolution under visible light. J. Mater. Chem. A 2018, 6, 13110-13122. DOI: 10.1039/c8ta03048k. (20)Ma, S.; Deng, Y.; Xie, J.; He, K.; Liu, W.; Chen, X.; Li, X. Noble-metal-free Ni3C cocatalysts decorated CdS nanosheets for high efficiency visible-light-driven photocatalytic H2 evolution. Appl. Catal. B-Environ. 2018, 227, 218-228. DOI: 10.1016/j.apcatb.2018.01.031. (21)Fu, J.; Zhu, B.; Jiang, C.; Cheng, B.; You, W.; Yu, J. Hierarchical Porous ODoped g-C3N4 with Enhanced Photocatalytic CO2 Reduction Activity. Small 2017, 13, 1603938. DOI: 10.1002/smll.201603938. (22)Bi, G.; Wen, J.; Li, X.; Liu, W.; Xie, J.; Fang, Y.; Zhang, W. Efficient visiblelight photocatalytic H2 evolution over metal-free g-C3N4 co-modified with robust acetylene black and Ni(OH)2 as dual co-catalysts. Rsc. Adv. 2016, 6, 31497-31506. DOI: 10.1039/c6ra03118h. (23)Yu, J.; Wang, S.; Cheng, B.; Lin, Z.; Huang, F. Noble metal-free Ni(OH)2-gC3N4 composite photocatalyst with enhanced visible-light photocatalytic H2-production activity. Catal. Sci. Technol. 2013, 3, 1782-1789. DOI: 10.1039/c3cy20878h. (24)He, K. L.; Xie, J.; Luo, X. Y.; Wen, J. Q.; Ma, S.; Li, X.; Fang, Y. P.; Zhang, X. C. Enhanced visible light photocatalytic H2 production over Z-scheme g-C3N4 nansheets/WO3 nanorods nanocomposites loaded with Ni(OH)x cocatalysts. Chinese. J. Catal. 2017, 38, 240-252. DOI: 10.1016/s1872-2067(17)62759-1. (25)Akple, M. S.; Low, J.; Wageh, S.; Al-Ghamdi, A. A.; Yu, J.; Zhang, J.



Enhanced visible light photocatalytic H2-production of g-C3N4/WS2 composite heterostructures. Appl. Surf. Sci. 2015, 358, 196-203. DOI: 10.1016/j.apsusc.2015.08.250. (26)Dong, Y.; Kong, L.; Jiang, P.; Wang, G.; Zhao, N.; Zhang, H.; Tang, B. A General Strategy To Fabricate NixP as Highly Efficient Cocatalyst via Photoreduction Deposition for Hydrogen Evolution. Acs Sustain. Chem. Eng. 2017, 5, 6845-6853. DOI: 10.1021/acssuschemeng.7b01079. (27)Sun, Z.; Zhu, M.; Fujitsuka, M.; Wang, A.; Shi, C.; Majima, T. Phase Effect of NixPy Hybridized with g-C3N4 for Photocatalytic Hydrogen Generation. Acs Appl. Mater. Inter. 2017, 9, 30583-30590. DOI: 10.1021/acsami.7b06386. (28)Zhao, H.; Sun, S.; Jiang, P.; Xu, Z. J. Graphitic C3N4 modified by Ni2P cocatalyst: An efficient, robust and low cost photocatalyst for visible-light-riven H2 evolution from water. Chem. Eng. J. 2017, 315, 296-303. DOI: 10.1016/j.cej.2017.01.034. (29)Wen, J.; Xie, J.; Shen, R.; Li, X.; Luo, X.; Zhang, H.; Zhang, A.; Bi, G. Markedly enhanced visible-light photocatalytic H2 generation over g-C3N4 nanosheets decorated by robust nickel phosphide (Ni12P5) cocatalysts. Dalton Trans. 2017, 46, 1794-1802. DOI: 10.1039/c6dt04575h. (30)Wu, F.; Li, X.; Liu, W.; Zhang, S. Highly enhanced photocatalytic degradation of methylene blue over the indirect all-solid-state Z-scheme g-C3N4 -RGO-TiO2 nanoheterojunctions. Appl. Surf. Sci. 2017, 405, 60-70. DOI: 10.1016/j.apsusc.2017.01.285. (31)Yue, X.; Yi, S.; Wang, R.; Zhang, Z.; Qiu, S. Cobalt Phosphide Modified Titanium Oxide Nanophotocatalysts with Significantly Enhanced Photocatalytic Hydrogen Evolution from Water Splitting. Small 2017, 13, 1603301. DOI: 10.1002/smll.201603301. (32)Shen, R.; Xie, J.; Zhang, H.; Zhang, A.; Chen, X.; Li, X. Enhanced Solar Fuel H2 Generation over g-C3N4 Nanosheet Photocatalysts by the Synergetic Effect of Noble Metal-Free Co2P Cocatalyst and the Environmental Phosphorylation Strategy. Acs Sustain. Chem. Eng. 2018, 6, 816-826. DOI: 10.1021/acssuschemeng.7b03169. (33)Bi, L.; Gao, X.; Zhang, L.; Wang, D.; Zou, X.; Xie, T. Enhanced Photocatalytic Hydrogen Evolution of NiCoP/g-C3N4 with Improved Separation Efficiency and Charge Transfer Efficiency. Chemsuschem 2018, 11, 276-284. DOI: 10.1002/cssc.201701574. (34)Zhao, H.; Wang, J.; Dong, Y.; Jiang, P. Noble-Metal-Free Iron Phosphide Cocatalyst Loaded Graphitic Carbon Nitride as an Efficient and Robust Photocatalyst for Hydrogen Evolution under Visible Light Irradiation. Acs Sustain. Chem. Eng. 2017, 5, 8053-8060. DOI: 10.1021/acssuschemeng.7b01665. (35)Sun, Z.; Chen, H.; Huang, Q.; Du, P. Enhanced photocatalytic hydrogen production in water under visible light using noble metal-free ferrous phosphide as an active cocatalyst. Catal. Sci. Technol. 2015, 5, 4964-4967. DOI: 10.1039/C5CY01293G. (36)Shi, Y.; Zhang, B. Recent advances in transition metal phosphide nanomaterials: synthesis and applications in hydrogen evolution reaction. Chem. Soc.


Page 18 of 22

Page 19 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Rev. 2016, 45, 1529-1541. DOI: 10.1039/c5cs00434a. (37)Sun, Z.; Zheng, H.; Li, J.; Du, P. Extraordinarily efficient photocatalytic hydrogen evolution in water using semiconductor nanorods integrated with crystalline Ni2P cocatalysts. Energy Environ. Sci. 2015, 8, 2668-2676. DOI: 10.1039/C5EE01310K. (38)Sun, Z.; Lv, B.; Li, J.; Xiao, M.; Wang, X.; Du, P. Core-shell amorphous cobalt phosphide/cadmium sulfide semiconductor nanorods for exceptional photocatalytic hydrogen production under visible light. J. Mater. Chem. A 2016, 4, 1598-1602. DOI: 10.1039/C5TA07561K. (39)Cao, S.; Chen, Y.; Wang, C.-J.; Lv, X.-J.; Fu, W.-F. Spectacular photocatalytic hydrogen evolution using metal-phosphide/CdS hybrid catalysts under sunlight irradiation. Chem. Commun. 2015, 51, 8708-8711. DOI: 10.1039/c5cc01799h. (40)Cao, S.; Chen, Y.; Hou, C.-C.; Lv, X.-J.; Fu, W.-F. Cobalt phosphide as a highly active non-precious metal cocatalyst for photocatalytic hydrogen production under visible light irradiation. J. Mater. Chem. A 2015, 3, 6096-6101. DOI: 10.1039/c4ta07149b. (41)Dai, D.; Wang, L.; Xiao, N.; Li, S.; Xu, H.; Liu, S.; Xu, B.; Lv, D.; Gao, Y.; Song, W.; Ge, L.; Liu, J. In-situ synthesis of Ni2P co-catalyst decorated Zn0.5Cd0.5S nanorods for high-quantum-yield photocatalytic hydrogen production under visible light irradiation. Appl. Catal. B-Environ. 2018, 233, 194-201. DOI: https://doi.org/10.1016/j.apcatb.2018.04.013. (42)Dai, D.; Xu, H.; Ge, L.; Han, C.; Gao, Y.; Li, S.; Lu, Y. In-situ synthesis of CoP co-catalyst decorated Zn0.5Cd0.5S photocatalysts with enhanced photocatalytic hydrogen production activity under visible light irradiation. Appl. Catal. B-Environ. 2017, 217, 429-436. DOI: https://doi.org/10.1016/j.apcatb.2017.06.014. (43)Wu, M.; Zhang, J.; Liu, C. X.; Gong, Y. S.; Wang, R.; He, B. B.; Wang, H. W. Rational Design and Fabrication of Noble-metal-free NixP Cocatalyst Embedded 3D N-TiO2/g-C3N4 Heterojunctions with Enhanced Photocatalytic Hydrogen Evolution. Chemcatchem 2018, 10, 3069-3077. DOI: 10.1002/cctc.201800197. (44)Cao, S.; Wang, C.-J.; Fu, W.-F.; Chen, Y. Metal Phosphides as Co-Catalysts for Photocatalytic and Photoelectrocatalytic Water Splitting. Chemsuschem 2017, 10, 4306-4323. DOI: 10.1002/cssc.201701450. (45)Tian, J.; Liu, Q.; Cheng, N.; Asiri, A. M.; Sun, X. Self-Supported Cu3P Nanowire Arrays as an Integrated High-Performance Three-Dimensional Cathode for Generating Hydrogen from Water. Angew. Chem. Int. Edit. 2014, 53, 9577-9581. DOI: 10.1002/anie.201403842. (46)Ma, L.; Shen, X.; Zhou, H.; Zhu, J.; Xi, C.; Ji, Z.; Kong, L. Synthesis of Cu3P nanocubes and their excellent electrocatalytic efficiency for the hydrogen evolution reaction in acidic solution. Rsc. Adv. 2016, 6, 9672-9677. DOI: 10.1039/c5ra24427g. (47)Hou, C.-C.; Chen, Q.-Q.; Wang, C.-J.; Liang, F.; Lin, Z.; Fu, W.-F.; Chen, Y. Self-Supported Cedarlike Semimetallic Cu3P Nanoarrays as a 3D High-Performance Janus Electrode for Both Oxygen and Hydrogen Evolution under Basic Conditions. Acs Appl. Mater. Inter. 2016, 8, 23037-23048. DOI: 10.1021/acsami.6b06251. (48)Sun, Z.; Yue, Q.; Li, J.; Xu, J.; Zheng, H.; Du, P. Copper phosphide modified



cadmium sulfide nanorods as a novel p-n heterojunction for highly efficient visiblelight-driven hydrogen production in water. J. Mater. Chem. A 2015, 3, 10243-10247. DOI: 10.1039/c5ta02105g. (49)Yue, X.; Yi, S.; Wang, R.; Zhang, Z.; Qiu, S. A novel and highly efficient earth-abundant Cu3P with TiO2 "P-N" heterojunction nanophotocatalyst for hydrogen evolution from water. Nanoscale 2016, 8, 17516-17523. DOI: 10.1039/c6nr06620h. (50)Ma, S.; Xu, X.; Xie, J.; Li, X. Improved visible-light photocatalytic H2 generation over CdS nanosheets decorated by NiS2 and metallic carbon black as dual earth-abundant cocatalysts. Chinese. J. Catal. 2017, 38, 1970-1980. DOI: 10.1016/s1872-2067(17)62965-6. (51)Ma, S.; Xie, J.; Wen, J.; He, K.; Li, X.; Liu, W.; Zhang, X. Constructing 2D layered hybrid CdS nanosheets/MoS2 heterojunctions for enhanced visible-light photocatalytic H2 generation. Appl. Surf. Sci. 2017, 391, 580-591. DOI: 10.1016/j.apsusc.2016.07.067. (52)Shen, R.; Xie, J.; Guo, P.; Chen, L.; Chen, X.; Li, X. Bridging the g-C3N4 nanosheets and robust CuS cocatalysts by metallic acetylene black interface mediators for active and durable photocatalytic H2 production. ACS Applied Energy Materials 2018, 1, 2232-2241. DOI: 10.1021/acsaem.8b00311. (53)Wen, J.; Xie, J.; Yang, Z.; Shen, R.; Li, H.; Luo, X.; Chen, X.; Li, X. Fabricating the Robust g-C3N4 Nanosheets/Carbons/NiS Multiple Heterojunctions for Enhanced Photocatalytic H2 Generation: An Insight into the Trifunctional Roles of Nanocarbons. Acs Sustain. Chem. Eng. 2017, 5, 2224-2236. DOI: 10.1021/acssuschemeng.6b02490. (54)Wen, J.; Li, X.; Li, H.; Ma, S.; He, K.; Xu, Y.; Fang, Y.; Liu, W.; Gao, Q. Enhanced visible-light H2 evolution of g-C3N4 photocatalysts via the synergetic effect of amorphous NiS and cheap metal-free carbon black nanoparticles as co-catalysts. Appl. Surf. Sci. 2015, 358, 204-212. DOI: 10.1016/j.apsusc.2015.08.244. (55)Wang, R.; Dong, X.-Y.; Du, J.; Zhao, J.-Y.; Zang, S.-Q. MOF-Derived Bifunctional Cu3P Nanoparticles Coated by a N,P-Codoped Carbon Shell for Hydrogen Evolution and Oxygen Reduction. Adv. Mater. 2018, 30, 1703711. DOI: 10.1002/adma.201703711. (56)Kong, C.; Min, S.; Lu, G. Dye-sensitized NiSx catalyst decorated on graphene for highly efficient reduction of water to hydrogen under visible light irradiation. Acs Catal. 2014, 4, 2763-2769. (57)Burchardt, T. Hydrogen evolution on NiP x alloys: the influence of sorbed hydrogen. Int. J. Hydrogen. Energ. 2001, 26, 1193-1198. (58)Zhen, W.; Gao, H.; Tian, B.; Ma, J.; Lu, G. Fabrication of Low Adsorption Energy Ni-Mo Cluster Cocatalyst in Metal-Organic Frameworks for Visible Photocatalytic Hydrogen Evolution. Acs Appl. Mater. Inter. 2016, 8, 10808-10819. DOI: 10.1021/acsami.5b12524. (59)Wang, X.; Li, T.; Yu, R.; Yu, H.; Yu, J. Highly efficient TiO2 single-crystal photocatalyst with spatially separated Ag and F-bi-cocatalysts: orientation transfer of photogenerated charges and their rapid interfacial reaction. J. Mater. Chem. A 2016, 4, 8682-8689. DOI: 10.1039/c6ta02039a.


Page 20 of 22

Page 21 of 22 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(60)Zhang, N.; Wang, L.; Wang, H.; Cao, R.; Wang, J.; Bai, F.; Fan, H. SelfAssembled One-Dimensional Porphyrin Nanostructures with Enhanced Photocatalytic Hydrogen Generation. Nano Lett. 2018, 18, 560-566. DOI: 10.1021/acs.nanolett.7b04701. (61)Zhu, M.; Li, Z.; Xiao, B.; Lu, Y.; Du, Y.; Yang, P.; Wang, X. Surfactant Assistance in Improvement of Photocatalytic Hydrogen Production with the Porphyrin Noncovalently Functionalized Graphene Nanocomposite. Acs Appl. Mater. Inter. 2013, 5, 1732-1740. DOI: 10.1021/am302912v. (62)Yuan, Y.; Lu, H.; Ji, Z.; Zhong, J.; Ding, M.; Chen, D.; Li, Y.; Tu, W.; Cao, D.; Yu, Z.; Zou, Z. Enhanced visible-light-induced hydrogen evolution from water in a noble-metal-free system catalyzed by ZnTCPP-MoS2/TiO2 assembly. Chem. Eng. J. 2015, 275, 8-16. DOI: 10.1016/j.cej.2015.04.015. (63)Yuan, Y.-J.; Chen, D.; Zhong, J.; Yang, L.-X.; Wang, J.-J.; Yu, Z.-T.; Zou, Z.G. Construction of a Noble-Metal-Free Photocatalytic H2 Evolution System Using MoS2/Reduced Graphene Oxide Catalyst and Zinc Porphyrin Photosensitizer. J. Phys. Chem. C 2017, 121, 24452-24462. DOI: 10.1021/acs.jpcc.7b08290. (64)Mou, Z.; Dong, Y.; Li, S.; Du, Y.; Wang, X.; Yang, P.; Wang, S. Eosin Y functionalized graphene for photocatalytic hydrogen production from water. Int. J. Hydrogen. Energ. 2011, 36, 8885-8893. DOI: 10.1016/j.ijhydene.2011.05.003. (65)Yeh, T.-F.; Syu, J.-M.; Cheng, C.; Chang, T.-H.; Teng, H. Graphite Oxide as a Photocatalyst for Hydrogen Production from Water. Adv. Funct. Mater. 2010, 20, 2255-2262. DOI: 10.1002/adfm.201000274. (66)Min, S.; Lu, G. Enhanced Electron Transfer from the Excited Eosin Y to mpgC3N4 for Highly Efficient Hydrogen Evolution under 550 nm Irradiation. J. Phys. Chem. C 2012, 116, 19644-19652. DOI: 10.1021/jp304022f. (67)Kong, C.; Min, S.; Lu, G. Dye-sensitized cobalt catalysts for high efficient visible light hydrogen evolution. Int. J. Hydrogen. Energ. 2014, 39, 4836-4844. DOI: 10.1016/j.ijhydene.2014.01.089. (68)Liu, P.; Rodriguez, J. A. Catalysts for hydrogen evolution from the NiFe hydrogenase to the Ni2P(001) surface: The importance of ensemble effect. J. Am. Chem. Soc. 2005, 127, 14871-14878. DOI: 10.1021/ja0540019. (69)Li, Q.; Meng, H.; Yu, J.; Xiao, W.; Zheng, Y.; Wang, J. Enhanced Photocatalytic Hydrogen-Production Performance of Graphene–ZnxCd1−xS Composites by Using an Organic S Source. Chemistry – A European Journal 2014, 20, 1176-1185. DOI: doi:10.1002/chem.201303446. For Table of Contents Use Only



The Carbon Nanotube-supported Cu3P as high-efficiency and low-cost cocatalysts could significantly boost the photocatalytic H2 evolution in Eosin Y(EY)-contained semiconductor-free systems.


Page 22 of 22

Carbon Nanotube-Supported Cu3P as High-Efficiency and Low-Cost