Cellulose Anionic Hydrogels Based on Cellulose ... - ACS Publications

Subscriber access provided by HACETTEPE UNIVERSITESI KUTUPHANESI

Article

Cellulose anionic hydrogels based on cellulose nanofibers as natural stimulants for seed germination and seedling growth Hao Zhang, Minmin Yang, Qian Luan, Hu Tang, Fenghong Huang, Xia Xiang, Chen Yang, and Yuping Bao J. Agric. Food Chem., Just Accepted Manuscript • Publication Date (Web): 24 Apr 2017 Downloaded from http://pubs.acs.org on April 25, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of Agricultural and Food Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 26

Journal of Agricultural and Food Chemistry

1 2 3

Cellulose anionic hydrogels based on cellulose nanofibers as natural stimulants for seed germination and seedling growth

4 5

Hao Zhang#, †, Minmin Yang#, ‡, Qian Luan†, Hu Tang*, †, Fenghong Huang*, †, Xia

6

Xiang†, Chen Yang†, Yuping Bao†

7 8

†

9

Chemistry and Nutrition, Ministry of Agriculture Key Laboratory of Oil Crops

10

Oil Crops Research Institute, Chinese Academy of Agricultural Sciences, Wuhan

11

430062, China

Department of Product Processing and Nutriology, Hubei Key Laboratory of Lipid

‡

12

Key Laboratory of Biology and Genetic Improvement of Oil Crops, Ministry

13

of Agriculture, Sesame Genetic Improvement Laboratory,Oil Crops Research Institute,

14

Chinese Academy of Agricultural Sciences, Wuhan 430062, China

15 16 17 18 19 20

*

Corresponding author: E-mail:[email protected] (Dr. Hu Tang); Tel: +86 027 86711615; Fax: +86 027

86815916

ACS Paragon Plus Environment


21 22

Page 2 of 26

Abstract Cellulose

anionic

hydrogels

were

successfully

prepared

by

dissolving

23

TEMPO-oxidized cellulose nanofibers in NaOH/urea aqueous solution and

24

crosslinked with epichlorohydrin. The hydrogels exhibited microporous structure and

25

high hydrophilicity, which contribute to the excellent water absorption property. The

26

growth indexes including the germination rate, root length, shoot length, fresh weight,

27

and dry weight of the seedlings were investigated. The results showed that cellulose

28

anionic hydrogels with suitable carboxylate contents as plant growth regulators could

29

be beneficial for seed germination and growth. Moreover, they presented preferable

30

antibacterial activity during the breeding and growth of the sesame seed breeding.

31

Thus the cellulose anionic hydrogels with suitable carboxylate contents could be

32

applied as soilless culture mediums for plant growth. This research provided a simple

33

and effective method for the fabrication of cellulose anionic hydrogel and evaluated

34

its application in agriculture.

35 36

Keywords: Cellulose nanofiber; cellulose anionic hydrogel; soilless culture; plant

37

growth regulator; antibacterial

38 39 40 41 42


Page 3 of 26


43

Introduction

44

Most of the crops are aerobic organisms depending upon a steady supply of oxygen

45

from environment, especially the ancient oil crop sesame which widely planted in

46

many countries, and it meets a high-end requirement for high quality oil with the

47

abundant and component balanced content of linoleic and oleic acid.1-3 However,

48

sesame is very sensitive to waterlogging. Waterlogging is the first stress factor which

49

seriously affecting the organs built of sesame at early blooming, thereby affecting the

50

sesame growth and the productivity.4-7 Waterlogging will inhibit the oxygen supply to

51

the roots thus limiting root respiration, leading to a serious decline in energy status of

52

root cells endangering important metabolic processes of sesame. Thence, one way of

53

solving the problem involves the application of a superabsorbent, which could absorb

54

and retain large number of water while providing an environment for seed

55

germination and growth.8

56

Hydrogels, attractive functional materials with excellent hydrophilic, biodegradable

57

and biocompatible properties, have been extensively researched in food, agriculture,

58

industry, biomedical field.9-12 Recently, several researches have pointed out that

59

hydrogels could act as seed growing mediums and preserve water and nutrients for

60

seed growth.13, 14 The hydrogels can reduce the stress of waterlogging periods for

61

plant seed by improving the reserved water availability, and more than 95 % of stored

62

water store in hydrogels could gradually release to the root system. Thus, hydrogels

63

could be applied as medium for the germination of plant seed instead of soil or

64

agar.15-17



65

Cellulose is the most abundant organic resource in nature which has potential to be

66

an attractive alternative for many materials due to it is nontoxic, biodegradable,

67

chemically stable and highly hydrophilic.18-23 Hydrogels based on cellulose nanofibers

68

could be fabricated from chemical modification of cellulose, cellulose-polymer

69

compositing and cellulose derivatives. Chemical modifications of cellulose could be

70

exclusively modified on the hydroxyl groups through oxidation, esterification and

71

etherification reactions.24-26 In present work, we attempted to design an attractive

72

ultra-hydrophilic cellulose plant hydrogel based on cellulose nanofibers and applied

73

for sesame seed germination and growth. Cellulose is a safe, biodegradable, and

74

hydrophilic natural polymer, and the prepared hydrogels with suitable carboxylate

75

groups applied as plant growth regulators could facilitate seed germination and

76

growth, and might be a promising candidate for soilless culture in agricultural

77

application. 22, 27-29

78 79

Materials and methods

80

Materials. Commercial never-dried softwood sulphite pulp was provided by

81

Nordic Paper. The pulp contained ca. 86% cellulose (degree of polymerization, 1200),

82

13.8% hemicellulose, and traces of residual lignin (0.7%). 2,2,6,6,-tetramethyl-1-

83

piperidinyloxy radical (TEMPO), hydrochloric acid, sodium hydroxide, sodium

84

bromide (NaBr), sodium hypochlorite (NaClO) were purchased from Sigma-Aldrich

85

and used without further purification.

86

Preparation of cellulose nanofibers. Cellulose nanofibers (CNF) were prepared


Page 4 of 26

Page 5 of 26


87

through a TEMPO-mediated oxidation reaction as previously reported by Isogai. et

88

al.30 As presented in Scheme 1a, wood pulp fibers were suspended at a concentration

89

of 1 wt% in water with the addition of TEMPO (16 mg/g cellulose) and NaBr (100

90

mg/g cellulose). NaClO (7.5 mmol/g cellulose) was added dropwise to the suspension

91

with vigorous stirring. The pH of the suspension was maintained at a constant value

92

of 10 with the addition of 0.1 M NaOH solution until all NaClO was consumed. The

93

resulting fibers were then thoroughly washed by using deionized water through

94

filtration until the filtrate solution was neutral, and the CNF was obtained. The

95

carboxylate contents of CNF were measured by using a conductometric titration

96

method and calculated as 1.5 mmol/g.31 By changing the added amount of NaClO (3.5,

97

5.0, 6.5 and 7.5 mmol/g cellulose), CNF with various carboxylate contents of 0.7, 1.0,

98

1.3 and 1.5 mmol/g were obtained. The CNF were never dried and kept in water

99

suspension with a solid content of 1.0 wt%.31

100

Preparation of cellulose anionic hydrogels. Preparation of cellulose anionic

101

hydrogels is presented in Scheme 1b, a mixture of NaOH/urea/water (7:12:81 by

102

weight) was pre-cooled to -12.5 oC. 6 g CNF with different carboxylate contents was

103

immediately added into the NaOH/urea mixtures and stirred vigorously for 5 min to

104

obtain a 6% cellulose solution.23 Then cross-linker epichlorohydrin (ECH) was added

105

(5 mL/100 g cellulose solution), stirred at room temperature for 20 min, and

106

centrifuged at 3000 rpm for 5 min. The resulting mixtures were heated at 60 oC for 30

107

min to transform into hydrogels. Finally, the hydrogels were washed with distilled

108

water until the residual NaOH, urea and extra ECH were removed. The hydrogels



Page 6 of 26

109

coded as CH, CH07 and CH15, according to the carboxylate contents of 0, 0.7 and 1.5

110

mmol/g.

111

Characterization. The carboxylate contents of CNF were determined by

112

conductometric titration.31 The morphology of the CNF samples were examined by

113

transmission electron microscopy (TEM). A drop of the dilute water dispersion of

114

CNF was deposited on a carbon-coated grid and treated with 1% uranyl acetate

115

negative stain. The specimens were observed using the Hitachi Model HT7700

116

transmission electron microscope operated in high-resolution mode at 100 kV.

117

Fourier transform infrared spectroscopy (FTIR) was conducted on a Perkin-Elmer

118

Spectrum 2000 FTIR. The test specimens were prepared by the KBr-disk method.

119

Thermal gravimetric analysis (TGA) was carried out by using a thermogravimetric

120

analyzer (Perkin-Elmer Co., USA) at a heating rate of 15 oC min-1 from 30 to 800 oC

121

under nitrogen atmospheres. The dried samples were cut into powders and dried in

122

vacuum oven at 60 °C for 24 h before FTIR and TGA measurements.

123

The micro porous structure of the hydrogels was observed by using a scanning

124

electron microscope (SEM, Hitachi, S-570, Japan). The swollen samples were frozen

125

directly in liquid nitrogen, freeze-dried under vacuum, and sputtered with gold prior

126

to the SEM observation.

127

The gravimetric method was employed to measure the swelling ratios of the

128

hydrogels in distilled water at 37 oC. The equilibrium swelling ratio (ESR) was

129

calculated as:

130

ESR = Ws/Wd


(1)

Page 7 of 26


131

where Ws is the weight of the swollen hydrogel after reaching swelling equilibrium,

132

and Wd is the weight of the dried hydrogel.

133

Seed germination. The seed materials used in this study were black sesame

134

cultivar (zhongzhi NO.9, 2n=26) from the National Oil Crops Medium-term

135

Genebank of China (Wuhan, China). Germination experiments were performed in

136

green house (65 % relative humidity) and incubated 27 ± 2 oC for 16h light culture

137

and 8h dark culture and random designed with 3 replications and 9 seeds for each

138

replicate. Seeds grown in the summer (from June to September in 2015) were

139

collected, dried and stored in desiccant preserved. A seed was considered germinated

140

when the tip of the radicle (1-2 mm) had grown out of the seed.32 Germination

141

percentage was recorded daily for 7 days, then the seedlings were harvested, and root

142

length, shoot length, fresh weight and dry weight were evaluated.33 Soil, CH, CH07,

143

CH15, agar hydrogels with agar concentration of 0.3 wt% (AG03) and 0.6 wt%

144

(AG06) were used as culture mediums. The black sesame cultivar was sowed on the

145

surface of the culture mediums.

146

Fungal growth experiments. Pathogen was obtained from the National Oil Crops

147

Medium-term Genebank of China (Wuhan, China), and identified as Colletotrichum

148

gloeosporioides (C109) and Fusarium solani (83). The pathogen was cultured under

149

dark condition in Potato Saccharose Agar (PSA) medium for two days at 30 oC. Then

150

punched at the edge of colony and transferred to fresh PSA medium and cultured in

151

the same condition for another two days, and repeated 3 times. Subsequent transferred

152

the activated C109 and 83 into petri dishes with sterile AG03, AG06, Soil and CH07,



153

cultured for 3 days at 30 oC and measured the colony diameters.

154

Statistics of swelling ratios of the hydrogels, seed germination and colony

155

diameters were analyzed using SAS system V8.0 by performing repeated measure

156

analysis of variance (ANOVA). Statistical significance was determined by Duncan’s

157

new multiple range test (P < 0.05), and values not sharing a common superscript (a, b,

158

c, d and e) differ significantly.

159 160

Results and discussion

161

Figure 1 displayed the photographs of a suspension of Cellulose fibers (CF) (0.1%)

162

and dispersions of CNF (0.1%) of different carboxylate contents treated with an

163

ultrasonic homogenizer. It was clearly observed that the CF precipitated to the bottom

164

of the bottle. However, CNF with various carboxylate contents ranging from 0.7 to 1.5

165

mmol/g was homogeneously dispersed, and the transparency of the dispersions was

166

improved with increasing carboxylate contents of CNF.

167

The dispersions of CNF with lower carboxylate contents displayed a low

168

transparency were owing to the reason that these CNFs will form lateral aggregates in

169

water, as shown in Figure 2a and b in TEM images of CNF07 and CNF15. CNF07

170

formed lateral aggregates, whereas CNF15 was mostly transformed to uniform

171

cellulose nanofibers, and it was the small width that contributes to the transparency of

172

the dispersion.34

173

Figure S1 (Supporting Information) shows the FTIR of CF, CNF07 and CNF15. In

174

comparison with CF, an absorption band at 1731 cm-1 appeared in the spectra curve of


Page 8 of 26

Page 9 of 26


175

CNF07 and CNF15, and this was owing to the C=O stretching of the protonated

176

carboxyl groups.35, 36 And it was obviously exhibited that the intensity of CNF15 is

177

stronger than CNF07 due to the increased contents of carboxyl groups. These results

178

confirmed the successful preparation of CNF with various carboxylate contents.37

179

Figure S2a and b showed the TG and DTG curves of CF, CNF07 and CNF15. It was

180

shown that CF began to degrade at about 300 °C under N2 atmosphere, however,

181

degradation started at about 200 °C for CNF07 and CNF15. The thermal degradation

182

of CNF07 and CNF15 included two independent pyrolysis processes, owing to the

183

thermal degradation of TEMPO-oxidized cellulose on the surface and pristine

184

cellulose in the core of CNFs, respectively.24, 38 The results indicated that CNF07 and

185

CNF15 possessed decreased thermal stability because of the formation of carboxylate

186

groups on cellulose nanofiber surfaces during the TEMPO-mediated oxidation

187

process.39

188

The porous structure of hydrogels is presented in Figure 3, where SEM images of

189

CH, CH07 and CH15 are shown. It was clearly observed that the hydrogels exhibited

190

homogeneous porous structure, and this could be beneficial for soilless culture, for the

191

reason that a lot of water molecules could be easily diffused and stored in the porous

192

hydrogels, resulting in higher swelling behavior.40 The average pore diameters of

193

hydrogels were found to increase from 40 to 60 µm from CH to CH15, owing to the

194

increasing carboxylate contents in hydrogels which would contribute to the formation

195

of pores, and it was obvious that the pore walls folded with higher carboxylate

196

contents in hydrogels because of high hydrophilicity of the carboxyl group would



197

absorb large number of water and enlarge the pore sizes.

198

Figure 4a shows the FTIR spectra of CH, CH07 and CH15, the absorption band at

199

3440 cm-1 detected was ascribing to the stretching vibration of hydroxyl groups on the

200

cellulose backbone.41 In comparison to CH and CH07, the –OH stretching vibration

201

bands of CH15 were shifted to a lower wavenumber, indicating that a stronger

202

hydrogen bond occurred when carboxylate content increased. Moreover, the peak at

203

1649 cm-1 for CH is attributed to water molecule, however, it shifted to 1634 cm-1 for

204

CH07 and 1620 cm-1 for CH15 are assigned to the antisymmetric COO- stretching

205

vibration of the salified carboxyl group.35, 37

206

The swelling behavior was studied to evaluate the water absorption property of the

207

hydrogels, and the equilibrium swelling ratios (ESR) of CH, CH07 and CH15 in

208

distilled water at 37 oC were exhibited in Figure 4b. It was shown that ESR of CH,

209

CH07 and CH15 were 80 ± 8 %, 174 ± 2 % and 309 ± 6 %, respectively, which

210

displayed an increase of ESR with the increase of the carboxyl groups in hydrogels.

211

The results indicated that the hydrophilicity of carboxyl group would be favorable for

212

water absorption of hydrogels and it would be helpful for the application of these

213

hydrogels in plant growth.13

214

The starting temperature of the thermal degradation of CH was almost the same as

215

CF, whereas the initiate temperature of thermal degradation of CH07 and CH15

216

shifted toward higher temperatures (~220 oC), which was ~20 oC higher than CNF07

217

and CNF15 as shown in Figure 4c. And the DTG curve of CH15 consist of one peak

218

near 320 oC, for CNF15, it consists of two peaks. These results indicated that only one


Page 10 of 26

Page 11 of 26


219

kind of homogeneous substance existed in CH15 due to the crosslinking process.42

220

To investigate whether the synthesized hydrogels can affect germination and

221

development of seedlings, sesame seeds were sowed on the surface of CH07 and

222

photographed on 1, 3, 4 and 5 days, respectively. As shown in Figure 5a-d, the sesame

223

seeds spread uniformly on the surface of CH07, the seed germinated within 3 days,

224

and followed the appearance of plumules in 4 days, and complete emergence of all

225

seedlings occurred after 5 days.

226

Most seeds need sufficient water to be moistened but not to be soaked, therefore,

227

suitable water is of great importance for germination and seedling growth.43 As shown

228

in Figure 6a, cellulose anionic hydrogel with suitable carboxylate groups could be an

229

appropriate candidate for soilless culture because of the proper absorption of water

230

through the presence of carboxyl groups could stimulates germination and seedling

231

growth. We investigated the seeds germination on various culture mediums, as shown

232

in Figure 6b, the germination percentage in soil, CH, CH07, CH15, AG03 and AG06

233

with time increasing was recorded.44 The germination rate of CH07 was the highest of

234

all on the first day, and it increased to 100% within four days. However, the seeds in

235

CH haven’t germinated completely until the sixth day, and seeds in CH15 germinated

236

from 42% to 75% with no further increase. Seeds in CH07 germinated earlier by

237

comparison to the others. The highly effective germination of CH07 resulting from

238

the homogeneous macro-porous structure of the CH and the proper carboxylate

239

contents, which retaining large amount of water.

240

We further studied the influence of various culture mediums on seedlings growth



241

and development.45 The root length, shoot length, fresh weight and dry weight of the

242

seedlings were shown in Figure 6c and d. Seedling germinated and grown on CH07

243

displayed longer root and heavier fresh weight compared with those on CH, CH15,

244

AG03 and AG06, but presented similar lengths of root and fresh weight compared

245

with soil seedlings. These results indicate that cellulose hydrogel with suitable

246

carboxylate contents could be beneficial for seed germination and growth.

247

Figure 7 shows a typical antimicrobial test result of AG03, AG06, Soil and CH07

248

against Colletotrichum gloeosporioides (C109) and Fusarium solani (83) as

249

determined by evaluating fugal growth through the measurement of colony

250

diameter.46 It was clearly displayed in Figure 7a and b that the fugal growth was

251

closely affected by the culture medium. Experimental data were obtained by

252

calculating the average of colony diameter on the surface of eight different plates, as

253

shown in Figure 7c, the colony diameter of CH07 against either C109 or 83 was

254

almost the same as on the surface of Soil. The cellulose anionic hydrogel presented

255

preferable antibacterial activity during the breeding and growth of the sesame seed

256

breeding.

257

In summary, we have prepared CNF with various carboxylate contents through a

258

TEMPO-mediated oxidation reaction. Then a simple and effective method for the

259

fabrication of cellulose anionic hydrogels from CNF dissolved in NaOH/urea aqueous

260

solution was reported for the first time. The prepared cellulose anionic hydrogels

261

exhibited an increasing water absorption property with the increase of carboxylate

262

contents of CNF. The seed germination experiments confirmed that the cellulose


Page 12 of 26

Page 13 of 26


263

anionic hydrogels with suitable carboxylate contents could act as a plant growth

264

regulator and promote the germination and growth of seed. Fungal growth

265

experiments indicated that the cellulose anionic hydrogels exhibited antimicrobial

266

activity as well as soil. These results proved that cellulose anionic hydrogels with

267

suitable carboxylate contents can be an attractive seed germination material for

268

agricultural application.

269 270 271 272

Supporting information FTIR spectra of CF, CNF07 and CNF15 (Figure S1), TG and DTG curves of CF, CNF07 and CNF15 (Figure S2).

273 274 275

Acknowledgments

276

This work was supported by the Agricultural Science and Technology Innovation

277

Project of Chinese Academy of Agricultural Sciences (CAAS-ASTIP-2013-OCRI)

278

and the Director Fund of Oil Crops Research Institute (1610172016006).

279 280 281 282 283 284



285

References

286 287 288 289 290 291 292 293 294 295 296 297 298 299 300 301 302 303 304 305 306 307 308 309 310 311 312 313 314 315 316 317 318 319 320 321 322 323 324 325 326 327

1.

Yin, D.; Chen, S.; Chen, F.; Guan, Z.; Fang, W., Morphological and physiological responses of

two chrysanthemum cultivars differing in their tolerance to waterlogging. Environmental & Experimental Botany 2009, 67, (1), 87-93. 2.

Sairam, R. K.; Dharmar, K.; Chinnusamy, V.; Meena, R. C., Waterlogging-induced increase in

sugar mobilization, fermentation, and related gene expression in the roots of mung bean ( Vigna radiata ). Journal of Plant Physiology 2009, 166, (6), 602-616. 3.

Kumutha, D.; Sairam, R. K.; Ezhilmathi, K.; Chinnusamy, V.; Meena, R. C., Effect of

waterlogging on carbohydrate metabolism in pigeon pea ( Cajanus cajan L.): Upregulation of sucrose synthase and alcohol dehydrogenase. Plant Science 2008, 175, (5), 706-716. 4.

Aggarwal, P. K.; Kalra, N.; Chander, S.; Pathak, H., InfoCrop: A dynamic simulation model for

the assessment of crop yields, losses due to pests, and environmental impact of agro-ecosystems in tropical environments. I. Model description. Agricultural Systems 2006, 7, (1), 1-25. 5.

Vartapetian, B. B.; Jackson, M. B., Plant adaptations to anaerobic stress. Annals of Botany 1997,

79, (suppl 1), 3-20. 6.

Grassini, P.; Indaco, G. V.; Pereira, M. L.; Hall, A. J.; Trápani, N., Responses to short-term

waterlogging during grain filling in sunflower. Field Crops Research 2007, 101, (3), 352-363. 7.

Fukao, T.; Bailey-Serres, J., Plant responses to hypoxia – is survival a balancing act? Trends in

Plant Science 2004, 9, (9), 449-456. 8.

Xie, L.; Liu, M.; Ni, B.; Wang, Y., Utilization of Wheat Straw for the Preparation of Coated

Controlled-Release Fertilizer with the Function of Water Retention. Journal of Agricultural & Food Chemistry 2012, 60, (28), 6921-6928. 9.

Zhou, X.; Li, C.; Shao, Y.; Chen, C.; Yang, Z.; Liu, D., Reversibly tuning the mechanical

properties of a DNA hydrogel by a DNA nanomotor. Chemical Communications 2016, 52, (70), 10668-10671. 10. Barros, S. C., Thermal–mechanical behaviour of chitosan–cellulose derivative thermoreversible hydrogel films. Cellulose 2015, 22, (3), 1-19. 11. Mohammed, N.; Grishkewich, N.; Berry, R. M.; Tam, K. C., Cellulose nanocrystal–alginate hydrogel beads as novel adsorbents for organic dyes in aqueous solutions. Cellulose 2015, 22, (6), 1-14. 12. Cheng, J.; Park, M.; Hyun, J., Thermoresponsive hybrid hydrogel of oxidized nanocellulose using a polypeptide crosslinker. Cellulose 2014, 21, (3), 1699-1708. 13. Montesano, F. F.; Parente, A.; Santamaria, P.; Sannino, A.; Serio, F., Biodegradable Superabsorbent Hydrogel IncreasesWater Retention Properties of Growing Media and Plant Growth ☆. Agriculture & Agricultural Science Procedia 2015, 4, 451-458. 14. Chan, B.; Sufen, Z.; Lei, H.; Haiyan, W.; Wei, W.; Qingfu, Y., Starch-based hydrogel loading with carbendazim for controlled-release and water absorption. Carbohydrate Polymers 2015, 125, 376-383. 15. Ciolacu, D.; Rudaz, C.; Vasilescu, M.; Budtova, T., Physically and chemically cross-linked cellulose cryogels: Structure, properties and application for controlled release. Carbohydrate Polymers 2016, 151, 392-400. 16. Isobe, N.; Nishiyama, Y.; Kimura, S.; Wada, M.; Kuga, S., Origin of hydrophilicity of cellulose hydrogel from aqueous LiOH/urea solvent coagulated with alkyl alcohols. Cellulose 2014, 21, (2), 1043-1050.


Page 14 of 26

Page 15 of 26


328 329 330 331 332 333 334 335 336 337 338 339 340 341 342 343 344 345 346 347 348 349 350 351 352 353 354 355 356 357 358 359 360 361 362 363 364 365 366 367 368 369 370 371

17. Seki, Y., Carboxymethylcellulose (CMC)–hydroxyethylcellulose (HEC) based hydrogels: synthesis and characterization. Cellulose 2014, 21, (3), 1689-1698. 18. Luo, X.; Hao, Z.; Cao, Z.; Ning, C.; Xue, Y.; Yu, F., A simple route to develop transparent doxorubicin-loaded nanodiamonds/cellulose nanocomposite membranes as potential wound dressings. Carbohydrate Polymers 2016, 143, 231-238. 19. Chang, C.; Chen, S.; Zhang, L., Novel hydrogels prepared via direct dissolution of chitin at low temperature: structure and biocompatibility. Journal of Materials Chemistry 2011, 21, (11), 3865-3871. 20. Li, W.; Luo, X.; Song, R.; Zhu, Y.; Li, B.; Liu, S., Porous cellulose microgel particle: A fascinating host for the encapsulation, protection and delivery of Lactobacillus plantarum. Journal of Agricultural & Food Chemistry 2016, 64, 3430-3436. 21. Chang, C.; Han, K.; Zhang, L., Structure and properties of cellulose/poly(N-isopropylacrylamide) hydrogels prepared by IPN strategy. Polymers for Advanced Technologies 2011, 22, (9), 1329-1334. 22. Luo, X.; Lei, X.; Xie, X.; Bo, Y.; Ning, C.; Yu, F., Adsorptive removal of Lead from water by the effective and reusable magnetic cellulose nanocomposite beads entrapping activated bentonite. Carbohydrate Polymers 2016, 151, 640-648. 23. Wang, S.; Lu, A.; Zhang, L., Recent Advances in Regenerated Cellulose Materials. Progress in Polymer Science 2015, 53, 169-206. 24. Hu, T.; Núria, B.; Qi, Z., A Transparent, Hazy, and Strong Macroscopic Ribbon of Oriented Cellulose Nanofibrils Bearing Poly(ethylene glycol). Advanced Materials 2015, 27, (12), 2070-2076. 25. Chang, C.; He, M.; Zhou, J.; Zhang, L., Swelling Behaviors of pH- and Salt-Responsive Cellulose-Based Hydrogels. Macromolecules 2011, 44, (6), 1642-1648. 26. Isogai, T.; Saito, T.; Isogai, A., TEMPO electromediated oxidation of some polysaccharides including regenerated cellulose fiber. Biomacromolecules 2010, 11, (6), 1593-1599. 27. Chang, C.; Zhang, L., Cellulose-based hydrogels: Present status and application prospects. Carbohydrate Polymers 2011, 84, (1), 40-53. 28. Wu, Y.; Luo, X.; Li, W.; Song, R.; Li, J.; Li, Y.; Li, B.; Liu, S., Green and biodegradable composite films with novel antimicrobial performance based on cellulose. Food Chemistry 2016, 197, (Pt A), 250-256. 29. Luo, X.; Lei, X.; Cai, N.; Xie, X.; Xue, Y.; Yu, F., Removal of Heavy Metal Ions from Water by Magnetic Cellulose-Based Beads with Embedded Chemically Modified Magnetite Nanoparticles and Activated Carbon. Acs Sustainable Chemistry & Engineering 2016, 4, (7), 3960-3969 30. Hiraoki, R.; Ono, Y.; Saito, T.; Isogai, A., Molecular mass and molecular-mass distribution of TEMPO-oxidized celluloses and TEMPO-oxidized cellulose nanofibrils. Biomacromolecules 2015, 16, (2), 675-681. 31. Ye, C.; Malak, S. T.; Hu, K.; Wu, W.; Tsukruk, V. V., Cellulose Nanocrystal Microcapsules as Tunable Cages for Nano- and Microparticles. Acs Nano 2015, 9, (11), 10887-10895. 32. Sotomayor, D. A.; Lortie, C. J.; Lamarque, L. J., Nurse-plant effects on the seed biology and germination of desert annuals. Austral Ecology 2014, 39, (7), 786–794. 33. Das, S. N.; Dutta, S.; Kondreddy, A.; Chilukoti, N.; Pullabhotla, S. V. S. R. N.; Vadlamudi, S.; Podile, A. R., Plant Growth-Promoting Chitinolytic Paenibacillus elgii Responds Positively to Tobacco Root Exudates. Journal of Plant Growth Regulation 2010, 29, (4), 409-418. 34. Tsuguyuki Saito; Satoshi Kimura; Yoshiharu Nishiyama, A.; Akira Isogai, Cellulose Nanofibers Prepared by TEMPO-Mediated Oxidation of Native Cellulose. Biomacromolecules 2007, 8, (8), 2485-2491.



372 373 374 375 376 377 378 379 380 381 382 383 384 385 386 387 388 389 390 391 392 393 394 395 396 397 398 399 400

35. Fujisawa, S.; Okita, Y.; Fukuzumi, H., Preparation and characterization of TEMPO-oxidized cellulose nanofibril films with free carboxyl groups. Carbohydrate Polymers 2011, 84, (1), 579–583. 36. Liu, D.; Bian, Q.; Li, Y.; Wang, Y.; Xiang, A.; Tian, H., Effect of oxidation degrees of graphene oxide on the structure and properties of poly (vinyl alcohol) composite films. Composites Science and Technology 2016, 129, 146-152. 37. Yang, Q.; Saito, T.; Berglund, L. A.; Isogai, A., Cellulose nanofibrils improve the properties of all-cellulose composites by the nano-reinforcement mechanism and nanofibril-induced crystallization. Nanoscale 2015, 7, (42), 17957-17963. 38. Fukuzumi, H.; Saito, T.; Okita, Y.; Isogai, A., Thermal stabilization of TEMPO-oxidized cellulose. Polymer Degradation & Stability 2010, 95, (9), 1502-1508. 39. Fukuzumi, H.; Saito, T.; Iwata, T., Transparent and High Gas Barrier Films of Cellulose Nanofibers Prepared by TEMPO-Mediated Oxidation. Biomacromolecules 2009, 10, (1), 162-165. 40. Chang, C.; Duan, B.; Cai, J.; Zhang, L., Superabsorbent hydrogels based on cellulose for smart swelling and controllable delivery. European Polymer Journal 2010, 46, (1), 92-100. 41. Karabulut, E.; Pettersson, T.; Ankerfors, M.; Wågberg, L., Adhesive Layer-by-Layer Films of Carboxymethylated Cellulose Nanofibril–Dopamine Covalent Bioconjugates Inspired by Marine Mussel Threads. Acs Nano 2012, 6, (6), 4731-4739. 42. Tang, H.; Chen, H.; Duan, B.; Lu, A.; Zhang, L., Swelling behaviors of superabsorbent chitin/carboxymethylcellulose hydrogels. Journal of Materials Science 2014, 49, (5), 2235-2242. 43. Contributors, W., Germination. Wikipedia, The Free Encyclopedia 2016. 44. Khodakovskaya, M.; Dervishi, E.; Mahmood, M.; Xu, Y.; Li, Z.; Watanabe, F.; Biris, A. S., Carbon Nanotubes Are Able To Penetrate Plant Seed Coat and Dramatically Affect Seed Germination and Plant Growth. ACS Nano 2009, 3, (10), 3221-3227. 45. Lahiani, M. H.; Dervishi, E.; Chen, J.; Nima, Z.; Gaume, A.; Biris, A. S.; Khodakovskaya, M. V., Impact of Carbon Nanotube Exposure to Seeds of Valuable Crops. ACS Applied Materials & Interfaces 2013, 5, (16), 7965-7973. 46. Tremarin, A.; Longhi, D. A.; Aragão, G. M. F., Modeling the growth of Byssochlamys fulva and Neosartorya fischeri on solidified apple juice by measuring colony diameter and ergosterol content. International Journal of Food Microbiology 2015, 193, 23-28.

401 402 403 404 405 406 407 408


Page 16 of 26

Page 17 of 26


409

Scheme caption

410

Scheme 1. Schematic illustration for the preparation of cellulose nanofibers (a) and

411

cellulose anionic hydrogels (b).

412 413

Figure captions

414

Figure 1. Photographs of dispersion states of CF and CNF with different carboxylate

415

contents.

416

Figure 2.TEM images of dispersions of CNF07 (a) and CNF15 (b).

417

Figure 3. SEM images of CH (a), CH07 (b) and CH15 (c).

418

Figure 4. FTIR spectra (a), Equilibrium swelling ratios (b), TG (c) and DTG (d)

419

curves of CH, CH07 and CH15.

420

Figure 5. Photographs of sesame seeds sowed on the surface of CH07 after 1 (a), 3

421

(b), 4 (c) and 5 (d) days.

422

Figure 6. The mechanism of seed germination and seedling growth (a), the

423

germination percentage of sesame seeds (b), comparison of the length of roots and

424

shoots (c) and comparison of the weight of seeding at fresh and dry states (d) in soil,

425

CH, CH07, CH15, AG3 and AG6.

426

Figure 7. Colony appearance of C109 (a) and 83 (b), and colony diameter (c) grown

427

on AG03, AG06, Soil and CH07 after 3 days of incubation.

428 429 430



431 432

Scheme 1.

433 434 435 436 437 438 439 440


Page 18 of 26

Page 19 of 26


441 442

Figure 1.

443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 458



459 460

Figure 2.

461 462 463 464 465 466 467 468 469 470 471 472


Page 20 of 26

Page 21 of 26


473 474

Figure 3.

475 476 477 478 479 480 481 482 483 484



485 486

Figure 4.

487 488 489 490 491


Page 22 of 26

Page 23 of 26


492 493

Figure 5.

494 495 496 497 498



499 500

Figure 6.

501 502


Page 24 of 26

Page 25 of 26


503 504

Figure 7.

505 506 507 508 509 510 511 512



513

Table of content

514 515

Cellulose anionic hydrogels were successfully prepared from dissolving

516

Tempo-oxidized cellulose nanofibers in NaOH/urea aqueous solution and then

517

crosslinked with epichlorohydrin. The prepared cellulose anionic hydrogels exhibited

518

an increasing water absorption property with the increase of carboxylate contents of

519

CNF. The seed germination experiments confirmed that the cellulose anionic

520

hydrogels with suitable carboxylate contents could act as a plant growth regulator and

521

promote the germination and growth of seed. Fungal growth experiments indicated

522

that the cellulose anionic hydrogels exhibited antimicrobial activity as well as soil.

523

These results proved that cellulose anionic hydrogels with suitable carboxylate

524

contents can be an attractive seed germination material for agricultural application.

525


Page 26 of 26