CeO2 Catalyst with Optimized CeO2 Support ... - ACS Publications

Apr 16, 2019 - Ru/CeO2 Catalyst with Optimized CeO2 Support Morphology and Surface Facet for Propane Combustion. Zheng Wang , Zhenpeng Huang ...
0 downloads 0 Views 922KB Size
Subscriber access provided by UNIV OF LOUISIANA

Remediation and Control Technologies

Ru/CeO2 Catalyst with Optimized CeO2 Support Morphology and Surface Facet for Propane Combustion Zheng Wang, Zhenpeng Huang, John Brosnahan, Sen Zhang, Yanglong Guo, Yun Guo, Li Wang, Yunsong Wang, and Wangcheng Zhan Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.9b01929 • Publication Date (Web): 16 Apr 2019 Downloaded from http://pubs.acs.org on April 21, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 23

Environmental Science & Technology

1

Ru/CeO2 Catalyst with Optimized CeO2 Support Morphology and

2

Surface Facet for Propane Combustion

3

Zheng Wang,† Zhenpeng Huang,† John T. Brosnahan,‡ Sen Zhang,‡ Yanglong Guo,† Yun Guo,† Li

4

Wang,† Yunsong Wang,† Wangcheng Zhan*,†

5



6

Chemistry and Molecular Engineering, East China University of Science and Technology,

7

Shanghai 200237, P. R. China

8



9

* Corresponding Author: Fax: +86-21-64252923, E-mail: [email protected] (W.C. Zhan)

Key Laboratory for Advanced Materials, Research Institute of Industrial Catalysis, School of

Department of Chemistry, University of Virginia, Charlottesville, Virginia 22904, United States

10 11

Abstract: Tailoring the interfaces between active metal centers and supporting materials is an

12

efficient strategy to obtain a superior catalyst for a certain reaction. Herein, an active interface

13

between Ru and CeO2 was identified and constructed by adjusting the morphology of CeO2 support,

14

such as rods (R), cubes (C) and octahedra (O), to optimize both the activity and stability of Ru/CeO2

15

catalyst for propane combustion. We found that the morphology of CeO2 support does not

16

significantly affect the chemical states of Ru species, but controls the interaction between the Ru

17

and CeO2, leading to the tuning of oxygen vacancy in the CeO2 surface around the Ru-CeO2

18

interface. The Ru/CeO2 catalyst possesses more oxygen vacancy when CeO2-R with predominantly

19

exposed CeO2{110} surface facet is used, providing a higher ability to adsorb and activate oxygen

20

and propane. As a result, the Ru/CeO2-R catalyst exhibits higher catalytic activity and stability for

21

propane combustion compared to the Ru/CeO2-C and Ru/CeO2-O catalysts. This work highlights a

22

new strategy for the design of efficient metal/CeO2 catalysts by engineering morphology and

23

associated surface facet of CeO2 support for the elimination of light alkane pollutants and other

24

volatile organic compounds.

25

Keywords: Volatile organic compounds; CeO2 morphology; Surface facet, Oxygen vacancy;

26

Propane oxidation

ACS Paragon Plus Environment

Environmental Science & Technology

Page 2 of 23

27 28

1. Introduction

29

Emissions of volatile organic compounds (VOCs) have caused serious harm to the ecological

30

environment and human health in recent years, due to their toxicity and involvement in the formation

31

of photochemical smog. The elimination of VOC pollutants from the atmosphere therefore becomes

32

imperative to protect environmental sustainability and human health1-2. Among various treatment

33

methods, catalytic oxidation is considered as a promising technology to control the emission of

34

VOCs, because of its high adaptability to exhaust gas concentration, no secondary pollution and

35

moderate operation temperature3-5. Various kinds of catalysts including noble metal-based

36

materials6-15, nonnoble metal oxides16-22 and zeolites23-24 have been synthesized and applied for

37

VOC removal, greatly boosting development of the catalytic oxidation technique. Currently, a

38

challenging issue in this area is the design of a robust catalyst for the total oxidation of light alkanes

39

(the largest fraction of hydrocarbons in automobile exhaust of gas-powered vehicles) at a low

40

temperature, because short carbon chain molecules are thermodynamically and chemically stable,

41

and subsequently are difficult to be converted1,2,5. For example, propane, a primary short-chain

42

pollutant from liquefied petroleum gas, requires intermediate/high reaction temperatures to be

43

activated. With the increasing demand for propane as a fuel in transport vehicles, a high-

44

performance catalyst which can totally oxidize propane at moderate operation temperature is

45

essential to controlling VOC emissions.

46

For propane combustion, supported Pt or Pd catalysts25-30 have always been the focus of research

47

among various kinds of catalysts. Recent studies have demonstrated that Ru-based catalysts31-36 can

48

also deliver appealing catalytic activities for the total oxidation of propane. As a cheaper noble metal,

49

Ru is regarded as a promising alternative to Pt and Pd with potential to reduce cost in industrial

50

applications1,2. For example, the Ru/γ-Al2O3 catalyst exhibited a high activity for total oxidation of

51

propane, and TOF of 0.0035 s-1 can be achieved at 175 °C for the Cl-free Ru/γ-Al2O3 catalyst (4.6

52

wt.% Ru)35. Meanwhile, it was reported that the most active sites in the propane oxidation reaction

53

consist of a few layers of surface oxide on the large Ru particles and small RuxOy clusters34-35. ACS Paragon Plus Environment

Page 3 of 23

Environmental Science & Technology

54

Although previous studies have investigated the preparation method, catalyst pretreatment, and the

55

addition of another component into Ru in correlation to Ru-based catalyst performance36, it is still

56

unknown how supporting materials can influence the activity of Ru-based catalysts for propane

57

oxidation and how to optimize it.

58

Essentially, the nature of the support is a critical factor to determine the catalytic activity of

59

supported metal catalysts. The support can either modify or determine the electronic state of active

60

metal through the interaction between active metal and the support37-38, or take part in the reaction

61

to enable more favorable kinetic pathways39-41. On the other hand, with the rapid development of

62

synthetic methodology for nanomaterials, various metal and metal oxide nanocrystals with well-

63

defined morphologies and structures have been successfully synthesized, making it possible to

64

precisely modulate the interface between metal and metal oxide support at the atom level.42-52 For

65

example, Li et al.51 studied CO adsorption and oxidation on Au/TiO2 catalysts with different TiO2

66

morphologies predominantly exposing {001}, {100}, or {101} facets, and found TiO2 morphology-

67

dependent dual-perimeter-sites catalysis by Au/TiO2 catalysts in CO oxidation. Hu et al.52

68

demonstrated that ceria with different morphologies can affect the structure and chemical states of

69

Pd species. The ceria {111} facets on Pd/CeO2-O (octahedrons) favors the existence of PdO, which

70

are beneficial for propane activation and the total oxidation of propane. We envision that the Ru-

71

support interaction also plays an essential role in propane oxidation, and may be optimized by

72

carefully engineering support morphology and surface facet.

73

In the present work, we report a superior catalyst for propane oxidation utilizing CeO2 nanorods

74

(CeO2-R) with CeO2 {110} surface facets as a support for composite Ru nanocrystals. In order to

75

understand and systematically evaluate the CeO2 support effect, CeO2 with different morphology,

76

such as CeO2 nanocubes (CeO2-C) and nano-octahedra (CeO2-O), as well as CeO2-R, were

77

synthesized and used to support Ru in the same condition. Their structures and catalytic activities

78

for propane combustion were studied in detail, and then the mechanism of influence of CeO2 support

79

morphology on the catalytic performances of Ru/CeO2 catalysts for propane combustion was refined.

ACS Paragon Plus Environment

Environmental Science & Technology

Page 4 of 23

80

The interaction between the Ru species and CeO2, dependent on CeO2 support morphology-

81

associated surface facet, can optimize oxygen vacancy on the CeO2 surface around the Ru-CeO2

82

interface, providing a higher ability to adsorb and activate oxygen and propane, which leads to

83

excellent catalytic activity and stability for propane combustion. This work exemplifies a promising

84

strategy for developing robust supported catalysts for the efficient removal of short-chain

85

hydrocarbon VOCs.

86

2. Materials and Methods

87

2.1. Catalyst preparation

88

CeO2-R, CeO2-C and CeO2-O were synthesized by hydrolysis of Ce(NO3)3 in an alkaline medium,

89

followed by a hydrothermal treatment42,52. To obtain CeO2-R and CeO2-C, 4 mmol of

90

Ce(NO3)3·6H2O and 480 mmol of NaOH were dissolved in 10 and 70 mL of deionized water

91

seperately, and then these two solutions were slowly mixed and kept stirring for 30 min.

92

Subsequently, the mixed solution was transferred into a Teflon-lined stainless steel autoclave and

93

heated at 100 and 180 °C for 24 h to get CeO2-R and CeO2-C, respectively. After the hydrothermal

94

treatment, the precipitates were washed with distilled water and ethanol several times until pH=7,

95

then dried at 120 °C overnight and calcined in air at 400 °C for 4 h. For CeO2-O, 2 mmol of

96

Ce(NO3)3·6H2O and 0.02 mmol of Na3PO4 12H2O were dissolved in 80 mL of distilled water. After

97

being stirred at room temperature for 30 min, the solution was transferred into a Teflon-lined

98

stainless steel autoclave and heated at 170 °C for 10 h. After being cooled to room temperature, the

99

precipitates were washed with distilled water and ethanol, then dried at 120 °C overnight and

100

calcined in air at 400 °C for 4 h.

101

The Ru/CeO2-R catalyst with the Ru loading of 2 wt% was prepared by the deposition-

102

precipitation (DP) method. Firstly, 1.0 g of CeO2-R was suspended in 50 mL of water, followed by

103

adding desired amount of RuCl3 solution. The suspension pH was adjusted to 8.0 with NaOH

104

aqueous solution (0.01 M), and the resulting suspension was aged at 25 °C for 3 h with stirring. The

105

precipitate obtained was separated by centrifugation, washed thoroughly with distilled water, and

ACS Paragon Plus Environment

Page 5 of 23

Environmental Science & Technology

106

dried at 60 °C overnight, followed by calcination in 10% H2/Ar mixed gas at 400 °C for 90 min.

107

The Ru/CeO2-C and Ru/CeO2-O catalysts are prepared using the same procedure.

108

2.2. Catalytic activity testing

109

The catalytic performance of the catalysts prepared for C3H8 combustion was tested in a fixed

110

bed quartz reactor. 100 mg of catalyst was used in the test. The feed gas consisted of 0.2 vol.%

111

C3H8, 2 vol.% O2 and Ar balance with a flow rate of 50 mL/min. The temperature of reaction bed

112

was ramped up to 300 °C at a heating rate of 2°C/min. The conversion of C3H8 was measured after

113

the catalytic reaction by an online gas chromatograph (GC-2060) that was equipped with an FID.

114

The C3H8 conversion (XC3H8) was calculated by X

115

[C3H8]in and [C3H8]out are the C3H8 concentration in the inlet and outlet gas, respectively.

C3H8

=

[C3H8]in - [ C3H8]out × 100 %, where [C3H8]in

116

The stability of the Ru/CeO2 catalyst for propane combustion was conducted at 200 °C. 100 mg

117

of the catalyst was used. The feed gas consisted of 0.2 vol.% C3H8, 2 vol.% O2, 3 vol.% H2O (when

118

used) balanced by Ar with a flow rate of 50 mL/min. An online gas chromatograph (GC-2060) was

119

applied to measure C3H8 concentration in the inlet and outlet gas.

120

2.3. Reaction Kinetics Measurement

121

The kinetic parameters for C3H8 oxidation were measured at 155 °C in a fixed-bed reactor with

122

C3H8 conversion below 15%. The catalytic reaction data were obtained after 30 min of stable

123

reaction. The effects of the internal/external diffusion has been eliminated by changing the catalyst

124

particle size and feed gas velocity, and also be excluded by making a Weisz-Prater analysis for

125

Internal Diffusion and a Mears analysis for External Diffusion52-53. Turnover frequency (TOF) (s−1)

126

was calculated with TOF=XC8H8∙VC3H8∙NA/N, where XC3H8 is the conversion of C3H8, VC3H8 is the

127

gas flow rate (mol/s) of C3H8, NA is the Avogadro constant and N is the number of catalytically

128

active sites (N=Ntotal ∙ DRu). The Ru dispersion (DRu) was measured by CO chemical adsorption at

129

25 °C (CO/Ru=1/1) on a micromeritics AutoChem II 2920 chemical adsorption instrument. Ntotal is

130

total atom numbers of Ru, which can be calculated with Ntotal = (mRu/MRu) × NA, where mRu is the

131

mass of Ru and MRu is relative atomic mass of Ru.

ACS Paragon Plus Environment

Environmental Science & Technology

132

Page 6 of 23

2.4. Catalyst Characterization

133

Powder X-ray diffraction (XRD) patterns were collected on a Bruker D8 Focus diffractometer

134

with Cu Kα radiation (λ=1.54056 Å) operated at 40 kV and 40 mA. The specific surface areas of

135

the samples were measured on a Micromeritics ASAP 2400 instrument at 77K and calculated by the

136

Brunauer-Emmett-Teller (BET) method. Transmission electron microscopy (TEM) images of

137

samples were recorded on a JEOL Model 2100F electron microscope operated at 200 kV.

138

Ruthenium content was determined by X-ray fluorescence (XRF) using a Shimadzu (XRF-1800)

139

wavelength dispersive X-ray fluorescence spectrometer. The Raman spectra were obtained on a

140

Renishaw in Viat + Reflex spectrometer equipped with a CCD detector at ambient temperature and

141

moisture-free conditions. The emission line at 514.5 nm from an Ar+ ion laser (Spectra Physics) was

142

focused, analyzing spot about 1 mm, on the sample under the microscope. The power of the incident

143

beam on the sample was 3 mW. Time of acquisition was varied according to the intensity of the

144

Raman scattering. The wave numbers obtained from spectra were accurate to within 2 cm−1. X-ray

145

photoelectron spectroscopy (XPS) spectra were obtained at 25 °C on a PHI-Quantera spectrometer

146

under ambient conditions, and the 514 nm line of a Spectra Physics Ar+ laser was used for excitat

147

SXM spectrometer with Al Kα (1486.6 eV) radiation as the excitation source under ultra-high

148

vacuum (6.7×10−8 Pa). All binding energies (BE) were determined with respect to the C1s line

149

(284.8 eV) originating from adventitious carbon.

150

The temperature-programmed desorption of O2 (O2-TPD) was conducted using a Micromeritics

151

AutoChem II 2920 equipment associated with a computer-interfaced quadruple mass spectrometer

152

(Hiden HPR 20). 50 mg of catalyst was pre-treated with 3 vol.% O2/He (40 mL/min) at 400 °C for

153

30 min, then cooled to room temperature and being purged with He for 1 h, the sample was heated

154

from 30 to 700 °C at a rate of 10 °C/min in a flow of He (40 mL/min). The signal of O2 desorbed

155

from the samples was measured by the quadruple mass spectrometer.

156

For measurement of the temperature programmed surface reaction with C3H8 (C3H8-TPSR), 50

157

mg of the sample was pretreated with 3% vol. O2/He (40 mL/min) at 400 °C for 30 min, and then

ACS Paragon Plus Environment

Page 7 of 23

Environmental Science & Technology

158

cooled to 30 °C. After being swept with 5% vol. C3H8/Ar for 1h, the sample was heated from 30 to

159

600 °C at a rate of 10 °C/min in 5 vol.% C3H8/Ar flow (40 mL/min). A mass spectrometer (HPR20

160

QIC) was used to monitor the effluent gas and the MS signals of both C3H8 (m/z = 43) and CO2

161

(m/z =44) were recorded.

162

Diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) data were recorded on a

163

Nicolet Nexus 670 FTIR spectrometer with 64 scans at an effective resolution of 4 cm−1. Prior to

164

the measurements, the sample was heated at 250 °C in Ar for 1 h and then cooled to 200 °C. After

165

the background spectrum was recorded at 200 °C, Ar was replaced by the mixed gas (30 mL/min)

166

of 0.5 vol.% C3H8 - 99.5 vol.% Ar and in situ DRIFTS spectra of the samples were taken at a certain

167

time. At the C3H8 + O2 reaction stage, the gas of 0.5 vol.% C3H8/Ar was changed to 0.5 vol.% C3H8

168

- 5 vol.% O2 - 94.5 vol.% Ar (30 mL/min) and the DRIFTS spectra of the samples were collected at

169

a specific time.

170

3. Results and Discussion

171

3.1. Catalytic activity of the catalysts

172

The catalytic activities of CeO2 and Ru/CeO2 samples were evaluated for C3H8 combustion, and

173

are shown in Figure 1A. All pure CeO2 supports show a negligible catalytic activity for C3H8

174

combustion under the experimental conditions. After Ru loading on the CeO2 supports, C3H8

175

conversion improved drastically. The following oxidation performance, in terms of total-conversion

176

temperature, was observed: Ru/CeO2-R (198 °C) > Ru/CeO2-C (226 °C) > Ru/CeO2-O (255 °C). In

177

order to further compare the catalytic activity of three catalysts, C3H8 conversion rates were

178

calculated by normalizing over Ru weight (Figure 1B and Table S1). At a reaction temperature of

179

155 °C, Ru/CeO2-R displays a rate of 21.26106 molecules C3H8 gRu−1 s−1, while Ru/CeO2-C and

180

Ru/CeO2-O present the lower values of 7.30106 and 1.25106 molecules C3H8 gRu−1 s−1,

181

respectively. The apparent activation energy (Ea) for Ru/CeO2-R, Ru/CeO2-C, and Ru/CeO2-O is

182

28.6, 58.5, and 74.9 kJ/mol, respectively.

183

To highlight the superior catalytic performance of the Ru/CeO2 catalysts in propane combustion,

184

Table S2 compares catalytic activity of the Ru/CeO2 catalysts with different morphology to that of ACS Paragon Plus Environment

Environmental Science & Technology

Page 8 of 23

185

catalysts reported in references. Excitingly, the reaction rate and TOF of the Ru/CeO2-R are much

186

higher than those of other supported Ru catalysts and even the well-known noble metal-based

187

catalysts (e.g., Ru/CeO232, Ru/TiO233, Pt/ZSM-527 and Pd/Al2O328). Meanwhile, to evaluate the

188

durability of Ru/CeO2 for propane combustion, C3H8 conversion over three catalysts are detected at

189

200 °C within 60 h. The results show that the C3H8 conversion over the Ru/CeO2-C catalyst

190

dramatically decreases with the extension of the reaction time, while C3H8 conversion over other

191

two catalysts is retained well, indicating that the Ru/CeO2-R and Ru/CeO2-O catalysts have high

192

stability for propane combustion.

193 194

Figure 1. Catalytic activity (A), ln r as a function of 1/T (B) and the stability at 200 °C (C) of the

195

Ru/CeO2 catalysts for propane combustion. (The feed gas is consisted of 0.2 vol.% C3H8 + 2

196

vol.% O2 + 3 vol.% H2O (when used) balanced by Ar, and GHSV was 30000 mL·h-1·gcat-1 for A

197

and C, and 120000 mL·h-1·gcat-1 for B).

198

3.2. Catalyst structures and chemical states of Ru species

199

Figures 2A, D and H show the typical transmission electron microscopy (TEM) images of three

200

CeO2 supports above mentioned, confirming the formation of CeO2 nanorods, nanocubes and nano-

201

octahedra, respectively. High-resolution TEM (HRTEM) analysis indicates that CeO2-R

202

predominantly exposes well-defined {110} facets, while CeO2-C and CeO2-O have {100} and {111}

203

surface facets, respectively54-55 (Figure S1B, D and F). TEM images in Figures 2B, E and I show

204

the typical morphologies of Ru/CeO2 samples and corresponding Ru particle size distributions. The

205

morphology of the CeO2 supports can be well preserved after Ru loading. Ru nanocrystals are

206

uniformly distributed on the CeO2 support with an average size of 2.8, 1.2 and 1.7 nm for the

207

Ru/CeO2-R, Ru/CeO2-C and Ru/CeO2-O catalysts, respectively (Table S3). On the other hand, as is

208

well known, thin RuOx layers can be easily formed when Ru metal is exposed to air at room ACS Paragon Plus Environment

Page 9 of 23

Environmental Science & Technology

209

temperature, leading to the formation of Ru@RuOx species56-57, which would be confirmed by the

210

following X-ray photoelectron spectroscopy (XPS) results. However, only the interplanar spacing

211

of 0.21 nm assigned to the Ru {101} plane is observed in the FFT patterns, and the thin oxide layer

212

was absent in the HRTEM images of the Ru nanocrystals over Ru/CeO2 catalysts (Figures 2C, F

213

and J). This may be attributed to the amorphous phase of RuOx58-60.

214 215

Figure 2. TEM images of CeO2 (A, D and H) and Ru/CeO2 (B, E and I) and high-resolution TEM

216

images of Ru/CeO2 (C, F and J): rod (A, B and C); cube (D, E and F); octahedra (H, I and J).

217 218

The XRD patterns of the CeO2 and Ru/CeO2 catalysts are shown in Figure 3A. All CeO2 supports

219

display a cubic fluorite-type CeO2 phase (JCPDS 34-0394). Their grain sizes as calculated by the

220

Scherrer equation were 9.1, 30.2 and 39.8 nm for CeO2-R, CeO2-C and CeO2-O, respectively (Table

221

S3). After Ru loading, XRD patterns of the Ru/CeO2 catalysts are almost the same as those of the

222

corresponding CeO2 supports. There is no diffraction peak of Ru species (metallic Ru at 44º, RuOx

223

at 35º and 54º) for the Ru/CeO2 catalysts, due to the small particle size of Ru species as shown in

224

TEM results58-60.

ACS Paragon Plus Environment

Environmental Science & Technology

Page 10 of 23

225

The chemical states of Ru and their concentrations on the surface of the catalysts were detected

226

by X-ray photoelectron spectroscopy (XPS). Figure 3B shows the Ru 3p XPS spectra of the

227

Ru/CeO2 catalysts. The peaks at about 461.5 and 463.0 eV could be assigned to Ru0 and Run+ (0
Ru/CeO2-C (0.13) > Ru/CeO2-O (0.07). The

267

relative concentration of oxygen vacancy was further confirmed by calculating with the nature of

268

the major peak at 459 cm-1 based on the spatial correlation model53,73. The relative values are

269

4.721021 cm−3 (Ru/CeO2-R), 4.081021 cm−3 (Ru/CeO2-C) and 3.771021 cm−3 (Ru/CeO2-O)

270

respectively, which is consistent with the order of the ID/IF2g ratio. These results reveal that different

271

CeO2 surface facets can affect the interaction between the Ru species and CeO2, leading to different

272

amounts of oxygen vacancy on the CeO2 surface around the Ru-CeO2 interface.

ACS Paragon Plus Environment

Environmental Science & Technology

Page 12 of 23

273

Figure 4B shows the Ce 3d XPS spectra. It consists of two series of spin-orbit lines u and v. Ce

274

3d3/2 spin-obit components which correspond to u lines include three characteristic peaks labeled as

275

u (901.1 eV), u" (907.1 eV) and u‴ (917.1 eV). Ce 3d5/2 spin-orbit components which correspond to

276

v lines include three peaks labeled as v (882.4 eV), v" (888.7 eV) and v‴ (898.5 eV). These three

277

pairs of peaks are attributed to the characteristic peaks of Ce4+. Moreover, the residual four spectral

278

lines labeled as u0 (899.2 eV), v0 (880.5 eV), u' (903.7 eV) and v' (885.3 eV) belong to the Ce3+

279

species. The Ce3+ concentration that correlates with the amount of oxygen vacancy on CeO2 surfaces,

280

can be estimated by calculating the ratio of the area of Ce3+ peak to the area of all peaks54, 58-59. As

281

show in Table S4, the Ru/CeO2-R catalyst has the highest atomic ratio of Ce3+/Ce (30.9%), followed

282

by the Ru/CeO2-C (27.9%) and Ru/CeO2-O (26.3%) catalysts. Since the Ce3+ concentration on CeO2

283

surface correlates with the amount of oxygen vacancies on CeO2 surfaces54, 58-59, it can be concluded

284

that the Ru/CeO2-R catalyst has more oxygen vacancies on the catalyst surface consistent with the

285

Raman results.

286 287

Figure 4. Raman spectra (A), Ce 3d (B) and O1s (C) XPS of the Ru/CeO2 catalysts

288 289

The O 1s XPS spectra of the Ru/CeO2 catalysts are shown in Figure 4C. All the catalysts display

290

one strong peak (OL) at 529.5 eV and a wide shoulder peak (OS) at 531.5 eV, which can be mainly

291

attributed to the lattice oxygen and surface-adsorbed oxygen belonging to carbonate (CO32−),

292

hydroxyl (OH-) species and/or the contributions from O of RuOx, respectively74-80. Since the content

293

of Ru in the Ru/CeO2 catalysts was very low, the ratio between the area of OS and OL (OS/OL) for

294

the Ru/CeO2 catalysts is analogous to the amount ratio between surface-adsorbed oxygen belonging

295

to defect oxides and the lattice oxygen. As shown in Table S4, the OS/OL ratio decreases in the order

ACS Paragon Plus Environment

Page 13 of 23

Environmental Science & Technology

296

of Ru/CeO2-R (43.2%) > Ru/CeO2-C (33.8%) > Ru/CeO2-O (31.9%), indicating that the Ru/CeO2-

297

R catalyst possesses the highest amount of surface-adsorbed oxygen due to more oxygen vacancy

298

on the surface of the Ru/CeO2-R catalyst. The Ru/CeO2-C catalyst comes second, and the Ru/CeO2-

299

O catalyst is the least. These results is consistent with those of Raman and the Ce 3d XPS spectra.

300

3.4. Amount of active oxygen

301

Since an oxygen vacancy is a good site for oxygen adsorption and activation during oxidation

302

reactions54,60,76, the presence of oxygen vacancies on the surfaces of the Ru/CeO2 catalysts is

303

beneficial for improving their catalytic activity in the total oxidation of propane. To further

304

determine the amount of active oxygen species on the surface of the Ru/CeO2 catalysts, the

305

temperature-programmed desorption of O2 (O2-TPD) and the temperature programmed surface

306

reaction with C3H8 (C3H8-TPSR) were conducted, and the results are summarized in Figure 5. In

307

the O2-TPD spectra of the Ru/CeO2 catalysts (Figure 5A), there is a broad overlapping desorption

308

peak for all catalysts, assigned to the chemisorbed oxygen and lattice oxygen of CeO270, 81. The

309

Ru/CeO2-R catalyst exhibits a desorption peak in the temperature range of 100-500oC, while the

310

Ru/CeO2-C and Ru/CeO2-O in 250-500 oC. The integrated areas of desorption peaks are 1.41×10-7,

311

8.25×10-8, 5.56×10-8 for the Ru/CeO2-R, Ru/CeO2-C and Ru/CeO2-O, respectively. On the basis of

312

the temperature and area of desorption peaks, it can be concluded that the Ru/CeO2-R has the highest

313

ability to adsorb oxygen among all catalysts, while the Ru/CeO2-C catalyst is middle and the

314

Ru/CeO2-O catalyst is least. As indicated by Raman and XPS, the morphology of CeO2 support can

315

affect the amount of oxygen vacancy on the CeO2 surface around the Ru-CeO2 interface, leading to

316

a different ability to adsorb oxygen for the Ru/CeO2 catalyst.

317

Figure S3 and 5B shows the C3H8-TPSR results over CeO2 support and the Ru/CeO2 catalysts.

318

The mass spectrometry (MS) signals of both C3H8 (m/z = 43) and CO2 (m/z =44) were recorded.

319

For CeO2 supports, almost no reaction product can be obtained in the temperature range 100-400 °C

320

(Figure S3), indicating that all CeO2 supports are poorly active for propane combustion at < 400 °C.

321

After Ru was introduced on CeO2, a strong peak (m/z = 44) and a negative peak (m/z = 43) appeared

322

at about 200 °C, indicating that total oxidation of propane occurred (Figure 5B). Although the curve ACS Paragon Plus Environment

Environmental Science & Technology

Page 14 of 23

323

is similar for the different Ru/CeO2 catalysts, the area of CO2 desorption peak (m/z = 44) is 4.54,

324

2.18 and 1.70 for the Ru/CeO2-R, Ru/CeO2-C and Ru/CeO2-O catalyst, respectively. This result

325

further confirms that the amount of active oxygen on the catalysts’ surfaces is in the order of

326

Ru/CeO2-R > Ru/CeO2-C > Ru/CeO2-O, in agreement with the results of O 1s XPS spectra.

327 328

Figure 5. O2-TPD (A) and C3H8-TPSR (B) of the Ru/CeO2 catalysts

329 330

3.5. C3H8 adsorption and activation

331

Figure 6 shows the DRIFT spectra of C3H8 adsorption and reaction on CeO2 and Ru/CeO2

332

catalysts at 200 °C. When the chamber was purged with feed gas consisting of 0.5 vol % C3H8-99.5

333

vol % Ar at 200 °C for 30 min, absorption bands are detected at 2800-3000 cm−1 for the CeO2-R

334

support, assigned to the absorption of gaseous propane (the details are listed in Table S5). In addition,

335

several absorption bands assigned to the carboxylate and carbonate species are present at 1200-1700

336

cm-1 (listed in Table S5), indicating that propane reacted with the oxygen of the CeO2-R support to

337

a certain degree. When the feed gas was replaced with 0.5 vol % C3H8-5 vol % O2-94.5 vol % Ar,

338

the intensity of the corresponding absorption bands at 1200-1700 cm-1 on the CeO2-R support

339

increases after exposure for 30 min at 200 °C, due to the enhancement of oxidation reaction.

340

However, the DRIFT spectra of C3H8 adsorption and reaction on CeO2-C and CeO2-O supports are

341

much different from that on CeO2-R support. The intensities of all absorption bands on CeO2-C and

342

CeO2-O supports are very weak, and the absorption bands at 1200-1700 cm-1 almost even

343

disappeared on CeO2-O support, after they were exposed to feed gas with and without O2 at 200 °C

344

for 30 min, indicating the low ability of CeO2-C and CeO2-O supports to adsorb and activate C3H8.

ACS Paragon Plus Environment

Page 15 of 23

Environmental Science & Technology

345

After Ru was introduced on CeO2, the ability to absorb and activate C3H8 is significantly

346

improved for CeO2-R and CeO2-C supports (a different scale of values on the vertical axis), and

347

intermediate species have changed to some extent. However, the relative order of the ability to

348

absorb and activate C3H8 has not changed, i.e. Ru/CeO2-R >> Ru/CeO2-C > Ru/CeO2-O. An

349

absorption band at 1850 cm-1 appears on the Ru/CeO2-C catalyst, and the Ru/CeO2-O catalyst only

350

has trace amounts of carboxylate species in its DRIFTS spectra. In contrast, the strong absorption

351

bands at 1200-1900 cm-1 (the details are listed in Table S5) are present on the Ru/CeO2-R catalyst,

352

and O2 in the feed gas can also affect the intermediate species. Compared to the feed gas without

353

O2, the absorption bands at 1430 and 1544 cm-1 related to the carboxylate species became more

354

intense on the Ru/CeO2-R catalyst after exposed to feed gas containing O2 due to the enhancement

355

of oxidation degree.

356 357 358 359 360 361

Figure 6. DRIFT spectra of C3H8 adsorption (0.5 vol % C3H8-99.5 vol % Ar, black line) and C3H8 + O2 reaction (0.5 vol % C3H8-5 vol % O2-94.5 vol % Ar, red line) on the CeO2 and Ru/CeO2 catalysts at 200 °C. The feed gas was 30 mL/min. All spectra were obtained after the catalysts were exposed in the feed gas for 30 min.

362

To conclude, CeO2 supports with different morphologies (nanorods, nanotubes, and nano-

363

octahedra, exposing {110}, {100} and {111} surface facets, respectively) were prepared, and the

364

effect of CeO2 morphology on the catalytic performances of Ru/CeO2 catalysts for propane

365

oxidation were investigated. It is revealed that the morphology of CeO2 support mainly influences ACS Paragon Plus Environment

Environmental Science & Technology

Page 16 of 23

366

the amount of oxygen vacancy in the CeO2 surface around the Ru-CeO2 interface due to the

367

difference in the interaction between the Ru species and CeO2 with different surfaces. The Ru/CeO2-

368

R catalyst possesses more oxygen vacancies in the CeO2 surface, leading to a high ability to adsorb

369

and activate oxygen and propane. As a result, the Ru/CeO2-R catalyst exhibits the higher catalytic

370

activity and reaction stability for propane combustion compared to the Ru/CeO2-C and Ru/CeO2-O

371

catalysts. In contrary, among three Ru/CeO2 catalysts, the Ru/CeO2-O catalyst possesses the least

372

oxygen vacancies in the CeO2 surface, leading to a lowest ability to adsorb and activate oxygen and

373

propane, as well as the lowest catalytic activity for propane combustion. In order to confirm

374

influence mechanism of surface oxygen vacancies, the difference in vacancy concentration, the

375

amount of surface-adsorbed oxygen, and the TOF on three catalysts has been evaluated. As shown

376

in Figure 7, the TOF at 155 ºC is correlated well with vacancy concentration (ID/IF2g), the amount

377

of surface-adsorbed oxygen (peak area in O2-TPD and Os/OL). This work can open up a facile and

378

reliable strategy for the design and construction of efficient metal/CeO2 catalysts by engineering the

379

surface facets of CeO2 support for the elimination of VOC pollutants. 45

0.3

15

12

0.2

15

9

40

36

OS/OL XPS

30

O2-TPD area

ID/IF2g Raman

TOF S-1 102 at 155 C

44

0.1 6

32

0

380 381

Ru/CeO2-R

Ru/CeO2-C

Ru/CeO2-O

Figure 7. Correlation between TOF (at 155 ºC) and oxygen vacancy concentration of catalysts.

382 383 384

ASSOCIATED CONTENT

385

Supporting information ACS Paragon Plus Environment

Page 17 of 23

Environmental Science & Technology

386

The reaction kinetics measurements are provided, together with catalytic activity, lnA as a function

387

of Ea and TEM images. The supporting information is available free of charge on the ACS

388

Publications website.

389 390

AUTHOR INFORMATION

391

Corresponding authors

392

*Email: Wangcheng Zhan ([email protected])

393

ORCID

394

Wangcheng Zhan: 0000-0002-0712-4917

395

Sen Zhang: 0000-0002-1716-3741

396

Yun Guo: 0000-0003-4778-6007

397

Yanglong Guo: 0000-0003-0021-9128

398

Notes

399

The authors declare no competing financial interest.

400 401

ACKNOWLEDGEMENTS

402

Z.W. and Z.H. appreciate the financial support from the National Key Research and Development

403

Program of China (2016YFC0204300), the National Natural Science Foundation of China

404

(21577034) and the Fundamental Research Funds for the Central Universities (222201717003).

405

Y.G. thanks the National Natural Science Foundation of China (21571061).

406 407

References

ACS Paragon Plus Environment

Environmental Science & Technology

408 409 410 411 412 413 414 415 416 417 418 419 420 421 422 423 424 425 426 427 428 429 430 431 432 433 434 435 436 437 438 439 440 441 442 443 444 445 446 447 448 449 450

Page 18 of 23

(1) Atkinson, R.; Arey, J. Atmospheric Degradation of Volatile Organic Compounds. Chem. Rev. 2003, 103, 4605-4638. (2) Lewis, A. C.; Carslaw, N.; Marriott, P. J.; Kinghorn, R. M.; Morrison, P.; Lee, A. L.; Bartle, K. D.; Pilling, M. J. A larger pool of ozone-forming carbon compounds in urban atmospheres. Nature 2000, 405, 778–781. (3) Domeño, C.; Rodríguez-Lafuente, Á.; Martos, J.; Bilbao, R.; Nerín, C. VOC Removal and Deodorization of Effluent Gases from an Industrial Plant by Photo-Oxidation, Chemical Oxidation, and Ozonization. Environ. Sci. Technol. 2010, 44, 2585-2591. (4) Gänzler, A. M.; Casapu, M.; Vernoux, P.; Loridant, S.; Cadete Santos Aires, F. J.; Epicier, T.; Betz, B.; Hoyer, R.; Grunwaldt, J.-D. Tuning the Structure of Platinum Particles on Ceria In Situ for Enhancing the Catalytic Performance of Exhaust Gas Catalysts. Angew. Chem. Int. Ed. 2017, 56, 13078−13082. (5) Cargnello, M.; Jaén, J. J. D.; Garrido, J. C. H.; Bakhmutsky, K.; Montini, T.; Gámez, J. J. C.; Gorte, R. J.; Fornasiero, P. Exceptional activity for methane combustion over modular Pd@CeO2 subunits on functionalized Al2O3. Science 2012, 337, 713−717. (6) Willis, J. J.; Goodman, E. D.; Wu, L.; Riscoe, A. R.; Martins, P.; Tassone, C. J.; Cargnello, M. Systematic Identification of Promoters for Methane Oxidation Catalysts Using Size-and Composition-Controlled Pd-Based Bimetallic Nanocrystals. J. Am. Chem. Soc. 2017, 139, 11989−11997. (7) Wang, H.; Dong, J.; Allard, L. F.; Lee, S.; Oh, S.; Wang, J.; Li, W.; Shen, M.; Yang, M. Singlesite Pt/La-Al2O3 stabilized by barium as an active and stable catalyst in purifying CO and C3H6 emissions. Appl. Catal. B: Environ. 2019, 244, 327–339. (8) Deng, J.; He, S.; Xie, S.; Yang, H.; Liu, Y.; Guo, G.; Dai, H. Ultralow Loading of Silver Nanoparticles on Mn2O3 Nanowires Derived with Molten Salts: A High-Efficiency Catalyst for the Oxidative Removal of Toluene. Environ. Sci. Technol. 2015, 49, 11089–11095. (9) Zhan, W.; Wang, J.; Wang, H.; Zhang, J.; Liu, X.; Zhang, P.; Chi, M.; Guo, Y.; Guo, Y.; Lu, G.; Sun, S.; Dai, S.; Zhu, H. Crystal Structural Effect of AuCu Alloy Nanoparticles on Catalytic CO Oxidation. J. Am. Chem. Soc. 2017, 139, 8846-8854. (10) Arandiyan, H.; Dai, H.; Ji, K.; Sun, H.; Li, J. Pt Nanoparticles Embedded in Colloidal Crystal Template Derived 3D Ordered Macroporous Ce0.6Zr0.3Y0.1O2: Highly Efficient Catalysts for Methane Combustion. ACS Catal. 2015, 5, 1781–1793. (11) Jiang, Y.; Deng, J.; Xie, S.; Yang, H.; Dai, H. Au/MnOx/3DOM La0.6Sr0.4MnO3: Highly Active Nanocatalysts for the Complete Oxidation of Toluene. Ind. Eng. Chem. Res. 2015, 54, 900–910. (12) Xie, S.; Liu, Y.; Deng, J.; Zang, S.; Zhang, Z.; Arandiyan, H.; Dai, H. Efficient Removal of Methane over Cobalt-Monoxide-Doped AuPd Nanocatalysts. Environ. Sci. Technol. 2017, 51, 2271–2279. (13) Zhan, W.; Shu, Y.; Sheng, Y.; Zhu, H.; Guo, Y.; Wang, L.; Guo, Y.; Zhang, J.; Lu, G.; Dai, S. Surfactant-Assisted Stabilization of Au Colloids on Solids for Heterogeneous Catalysis. Angew. Chem. Int. Ed. 2017, 56, 4494-4498. (14) Yang, X.; Gao, Q.; Zhao, Z.; Guo, Y.; Guo, Y.; Wang, L.; Wang, Y.; Zhan, W. Surface tuning of noble metal doped perovskite oxide by synergistic effect of thermal treatment and acid etching: A new path to high-performance catalysts for methane combustion. Appl. Catal. B. 2018, 239, 373– 382.

ACS Paragon Plus Environment

Page 19 of 23

451 452 453 454 455 456 457 458 459 460 461 462 463 464 465 466 467 468 469 470 471 472 473 474 475 476 477 478 479 480 481 482 483 484 485 486 487 488 489 490 491 492 493 494

Environmental Science & Technology

(15) Zhan, W.; He, Q.; Liu, X.; Guo, Y.; Wang, Y.; Wang, L.; Guo, Y.; Borisevich, A. Y.; Zhang, J.; Lu, G.; Dai, S. A Sacrificial Coating Strategy Toward Enhancement of Metal−Support Interaction for Ultrastable Au Nanocatalysts. J. Am. Chem. Soc. 2016, 138, 16130−16139. (16) Wang, Y.; Aghamohammadi, S.; Li, D.; Li, K.; Farrauto, R. Structure dependence of Nb2O5-X supported manganese oxide for catalytic oxidation of propane: Enhanced oxidation activity for MnOx on a low surface area Nb2O5-X. Appl. Catal. B. 2019, 244, 438–447. (17) Solsona, B.; García, T.; Sanchis, R.; Soriano, M. D.; Moreno, M.; Rodríguez-Castellón, E.; Agouram, S.; Dejoz, A.; López Nieto, J. M. Total oxidation of VOCs on mesoporous iron oxide catalysts: soft chemistry route versus hard template method, Chem. Eng. J. 2016, 290, 273–281. (18) Hu, Z.; Qiu, S.; You, Y.; Guo, Y.; Guo, Y.; Wang, L.; Zhan, W.; Lu, G. Hydrothermal synthesis of NiCeOx nanosheets and its application to the total oxidation of propane, Appl. Catal. B. 2018, 225, 110–120. (19) Zhan, W.; Yang, S.; Zhang, P.; Guo, Y.; Lu, G.; Chisholm, M. F.; Dai, S. Incorporating Rich Mesoporosity into a Ceria-Based Catalyst via Mechanochemistry. Chem. Mater. 2017, 29, 7323−7329. (20) Xie, S.; Liu, Y.; Deng, J.; Yang, J.; Zhao, X.; Han, Z.; Zhang, K.; Dai, H. Insights into the active sites of ordered mesoporous cobalt oxide catalysts for the total oxidation of oxylene, J. Catal. 2017, 352, 282–292. (21) Deng, J.; Dai, H.; Jiang, H.; Zhang, L.; Wang, G.; He, H.; Au, C. T., Hydrothermal Fabrication and Catalytic Properties of La1-xSrxM1-yFeyO3 (M = Mn, Co) That Are Highly Active for the Removal of Toluene. Environ. Sci. Technol. 2010, 44, 2618–2623. (22) Si, W.; Wang, Y.; Zhao, S.; Hu, F.; Li, J. A facile method for in situ preparation of the MnO2/LaMnO3 catalyst for the removal of toluene, Environ. Sci. Technol. 2016, 50, 4572–4578. (23) Zhu, Z.; Lu, G.; Zhang, Z.; Guo, Y.; Guo, Y.; Wang, Y. Highly Active and Stable Co3O4/ZSM5 Catalyst for Propane Oxidation: Effect of the Preparation Method. ACS Catal. 2013, 3, 1154−1164. (24) Yi, N.; Cao, Y.; Su, Y.; Dai, W.-L.; He, H.-Y.; Fan, K.-N. Nanocrystalline LaCoO3 perovskite particles confined in SBA-15 silica as a new efficient catalyst for hydrocarbon oxidation. J. Catal. 2005, 230, 249–253. (25) Kovalyov, E. V.; Sadovskaya, E. M.; Bal'zhinimaev, B. S. Kinetic features of the deep oxidation of propane over a Pt/fiberglass catalyst. Chem. Eng. J. 2018, 349, 547–553. (26) Luo, Y.; Zuo, J.; Feng, X.; Qian, Q.; Zheng, Y.; Lin, D.; Huang, B.; Chen, Q. Good interaction between well dispersed Pt and LaCoO3 nanorods achieved rapid Co3+/Co2+ redox cycle for total propane oxidation. Chem. Eng. J. 2019, 357, 395–403. (27) Zhu, Z.; Lu, G.; Guo, Y.; Guo, Y.; Zhang, Z.; Wang, Y.; Gong, X.-Q. High Performance and Stability of the Pt-W/ZSM-5 Catalyst for the Total Oxidation of Propane: The Role of Tungsten. Chemcatchem. 2013, 5, 2495-2503. (28) Yazawa, Y.; Yoshida, H.; Takagi, N.; Komai, S.-i.; Satsuma, A.; Hattori, T. Acid strength of support materials as a factor controlling oxidation state of palladium catalyst for propane combustion. J. Catal. 1999, 187, 15-23. (29) Xiong, H.; Wiebenga, M. H.; Carrillo, C.; Gaudet, J. R.; Pham, H. N.; Kunwar, D.; Oh, S. H.; Qi, G.; Kim, C. H.; Datye, A. K. Design considerations for low-temperature hydrocarbon oxidation reactions on Pd based catalysts. Appl. Catal. B. 2018, 236, 436–444. (30) Rao, C.; Peng, C.; Peng, H.; Zhang, L.; Liu, W.; Wang, X.; Zhang, N.; Wu, P. In Situ Embedded Pseudo Pd−Sn Solid Solution in Micropores Silica with Remarkable Catalytic Performance for CO ACS Paragon Plus Environment

Environmental Science & Technology

495 496 497 498 499 500 501 502 503 504 505 506 507 508 509 510 511 512 513 514 515 516 517 518 519 520 521 522 523 524 525 526 527 528 529 530 531 532 533 534 535 536 537 538

Page 20 of 23

and Propane Oxidation. ACS Appl. Mater. Interfaces 2018, 10, 9220−9224. (31) Okal, J.; Zawadzki, M.; Krajczyk, L. Light alkane oxidation over Ru supported on ZnAl2O4, CeO2 and Al2O3. Catal. Today 2011, 176, 173– 176. (32) Hu, Z.; Wang, Z.; Guo, Y.; Wang, L.; Guo, Y.; Zhang, J.; Zhan, W. Total Oxidation of Propane over a Ru/CeO2 Catalyst at Low Temperature. Environ. Sci. Technol. 2018, 52, 16, 9531-9541. (33) Debecker, D. P.; Farin, B.; Gaigneaux, E. M.; Sanchez, C.; Sassoye, C. Total oxidation of propane with a nano-RuO2/TiO2 catalyst. Appl. Catal. A: Gen. 2014, 481, 11–18. (34) Okal, J.; Zawadzki, M. Influence of Catalyst Pretreatments on Propane Oxidation Over Ru/ɣAl2O3. Catal Lett. 2009, 132, 225–234. (35) Okal, J.; Zawadzki, M. Catalytic combustion of butane on Ru/γ-Al2O3 catalysts, Appl. Catal. B. 2009, 89, 22-32. (36) Okal, J.; Zawadzki, M.; Tylus, W. Microstructure characterization and propane oxidation over supported Ru nanoparticles synthesized by the microwave-polyol method, Appl. Catal. B: Environ. 2011, 101, 548-559. (37) Tang, H.; Wei, J.; Liu, F.; Qiao, B.; Pan, X.; Li, L.; Liu, J.; Wang, J.; Zhang, T. Strong Metal– Support Interactions between Gold Nanoparticles and Nonoxides, J. Am. Chem. Soc. 2016, 138, 5659. (38) Ma, C. Y.; Mu, Z.; Li, J. J.; Jin, Y. G.; Cheng, J.; Lu, G. Q.; Hao, Z. P.; Qiao, S. Z. Mesoporous Co3O4 and Au/Co3O4 Catalysts for Low-Temperature Oxidation of Trace Ethylene, J. Am. Chem. Soc. 2010, 132, 2608-2613. (39) Ma, C.; Wang, D.; Xue, W.; Dou, B.; Wang, H.; Hao, Z. Investigation of Formaldehyde Oxidation over Co3O4−CeO2 and Au/Co3O4−CeO2 Catalysts at Room Temperature: Effective Removal and Determination of Reaction Mechanism, Environ. Sci. Technol. 2011, 45, 3628-3634. (40) Wu, H.; Wang, L.; Shen, Z.; Zhao, J. Catalytic oxidation of toluene and p-xylene using gold supported on Co3O4 catalyst prepared by colloidal precipitation method, J. Mol. Catal. A: Chem. 2011, 351, 188-195. (41) Wang, B.; Wu, X.; Ran, R.; Si, Z.; Weng, D. IR characterization of propane oxidation on Pt/CeO2-ZrO2: The reaction mechanism and the role of Pt, J. Mol. Catal. A: Chem. 2012, 356, 100105. (42) Carltonbird, M.; Eaimsumang, S.; Pongstabodee, S.; Boonyuen, S.; Smith, S. M. Effect of the exposed ceria morphology on the catalytic activity of gold/ceria catalysts for the preferential oxidation of carbon monoxide. Chem. Eng. J. 2018, 344, 545–555. (43) Cheng, Q.; Tian, Y.; Lyu, S.; Zhao, N.; Ma, K.; Ding, T.; Jiang, Z.; Wang, L.; Zhang, J.; Zheng, L.; Gao, F.; Dong, L.; Tsubaki, N.; Li, X., Confined small-sized cobalt catalysts stimulate carbonchain growth reversely by modifying ASF law of Fischer–Tropsch synthesis. Nat. Commun. 2018, 9, 3250. (44) Zou, W.; Deng, B.; Hu, X.; Zhou, Y.; Pu, Y.; Yu, S.; Ma, K.; Sun, J.; Wan, H.; Dong, L., Crystal-plane-dependent metal oxide-support interaction in CeO2/g-C3N4 for photocatalytic hydrogen evolution. Appl. Catal. B: Environ. 2018, 238, 111-118. (45) Wu, C. H.; Liu, C.; Su, D.; Xin, H. L.; Fang, H. T.; Eren, B.; Zhang, S.; Murray, C. B.; Salmeron, M. B. Bimetallic synergy in cobalt–palladium nanocatalysts for CO oxidation. Nat. Catal. 2019. doi.org/10.1038/s41929-018-0190-6. (46) Zou, W.; Shao, Y.; Pu, Y.; Luo, Y.; Sun, J.; Ma, K.; Tang, C.; Gao, F.; Dong, L., Enhanced visible light photocatalytic hydrogen evolution via cubic CeO2 hybridized g-C3N4 composite. Appl. ACS Paragon Plus Environment

Page 21 of 23

539 540 541 542 543 544 545 546 547 548 549 550 551 552 553 554 555 556 557 558 559 560 561 562 563 564 565 566 567 568 569 570 571 572 573 574 575 576 577 578 579 580 581 582 583 584

Environmental Science & Technology

Catal. B: Environ. 2017, 218, 51-59. (47) Lee, J.; Zhang, S.; Sun, S. High-Temperature Solution-Phase Syntheses of Metal-Oxide Nanocrystals. Chem. Mater. 2013, 25, 1293-1304. (48) Cao, Y.; Zhao, L.; Gutmann, T.; Xu, Y.; Dong, L.; Buntkowsky, G.; Gao, F., Getting Insights into the Influence of Crystal Plane Effect of Shaped Ceria on Its Catalytic Performances. J. Phys. Chem. C. 2018, 122, 20402-20409. (49) Meng, A.; Zhang, L.; Cheng, B.; Yu, J., TiO2–MnOx–Pt Hybrid Multiheterojunction Film Photocatalyst with Enhanced Photocatalytic CO2-Reduction Activity. ACS Appl. Mater. Interfaces 2019, 11, 5581-5589. (50) Guo, S.; Zhang, S.; Sun, S. Tuning nanoparticle catalysis for the oxygen reduction reaction. Angew. Chem. Int. Ed. 2013, 52, 8526-44. (51) Li, D.; Chen, S.; You, R.; Liu, Y.; Yang, M.; Cao, T.; Qian, K.; Zhang, Z.; Tian, J.; Huang, W. Titania-morphology-dependent dual-perimeter-sites catalysis by Au/TiO2 catalysts in lowtemperature CO oxidation. J. Catal. 2018, 368, 163–171. (52) Hu, Z.; Liu, X.; Meng, D.; Guo, Y.; Guo, Y.; Lu, G. Effect of Ceria Crystal Plane on the Physicochemical and Catalytic Properties of Pd/Ceria for CO and Propane Oxidation. ACS Catal. 2016, 6, 2265−2279. (53) Lu, J.; Wang, J.; Zou, Q.; He, D.; Zhang, L.; Xu, Z.; He, S.; Luo, Y. Unravelling the Nature of the Active Species as well as the Doping Effect over Cu/Ce-Based Catalyst for Carbon Monoxide Preferential Oxidation. ACS Catal. 2019. 10.1021/acscatal.8b04035. (54) Lei, Y.; Li, W.; Liu, Q.; Lin, Q.; Zheng, X.; Huang, Q.; Guan, S.; Wang, X.; Wang, C.; Li, F. Typical crystal face effects of different morphology ceria on the activity of Pd/CeO2 catalysts for lean methane combustion. Fuel 2018, 233, 10–20. (55) Li, C.; Sun, Y.; Djerdj, I.; Voepel, P.; Sack, C. C.; Weller, T.; Ellinghaus, R.; Sann, J.; Guo, Y.; Smarsly, B. M.; Over, H., Shape-Controlled CeO2 Nanoparticles: Stability and Activity in the Catalyzed HCl Oxidation Reaction. ACS Catal. 2017, 7, 6453-6463. (56) Over, H. Surface Chemistry of Ruthenium Dioxide in Heterogeneous Catalysis and Electrocatalysis: From Fundamental to Applied Research. Chem. Rev. 2012, 112, 3356−3426. (57) Herd, B.; Goritzka, J. C.; Over, H. Room Temperature Oxidation of Ruthenium. J. Phys. Chem. C. 2013, 117, 15148−15154. (58) Lin, B.; Liu, Y.; Heng, L.; Wang, X.; Ni, J.; Lin, J.; Jiang, L. Morphology Effect of Ceria on the Catalytic Performances of Ru/CeO2 Catalysts for Ammonia Synthesis. Ind. Eng. Chem. Res. 2018, 57, 9127−9135. (59) Sakpal, T.; Lefferts, L. Structure-dependent activity of CeO2 supported Ru catalysts for CO2 methanation. J. Catal. 2018, 367, 171–180. (60) Wang, F.; Li, C.; Zhang, X.; Wei, M.; Evans, D. G.; Duan, X. Catalytic behavior of supported Ru nanoparticles on the {100}, {110}, and {111} facet of CeO2. J. Catal. 2015, 329, 177–186. (61) Liang, G.; Zhou, Y.; Zhao, J.; Khodakov, A. Y.; Ordomsky, V. V. Structure-Sensitive and Insensitive Reactions in Alcohol Amination over Nonsupported Ru Nanoparticles. ACS Catal. 2018, 8, 11226−11234. (62) Xianfeng, M.; Rui, L.; Christopher, B.; James, E. J.; Sherine, O. O.; Robert, Y. O. Effects of surface activation on the structural and catalytic properties of ruthenium nanoparticles supported on mesoporous silica. Nanotechnology 2014, 25, 045701. (63) Wang, J.; Wei, Z.; Mao, S.; Li, H.; Wang, Y. Highly uniform Ru nanoparticles over N-doped carbon: pH and temperature-universal hydrogen release from water reduction. Energy Environ. Sci. 2018, 11, 800. ACS Paragon Plus Environment

Environmental Science & Technology

585 586 587 588 589 590 591 592 593 594 595 596 597 598 599 600 601 602 603 604 605 606 607 608 609 610 611 612 613 614 615 616 617 618 619 620 621 622 623 624 625 626 627 628

Page 22 of 23

(64) Okal, J.; Zawadzki, M.; Kraszkiewicz, P.; Adamska, K. Ru/CeO2 catalysts for combustion of mixture of light hydrocarbons: Effect of preparation method and metal salt precursors. Appl. Catal. A: Gen. 2018, 549, 161–169. (65) Ledwa, K. A.; Pawlyta, M.; Kępiński, L. RuxCe1-xO2-y nanoparticles deposited on functionalized γ-Al2O3 as a thermally stable oxidation catalyst. Appl. Catal. B: Environ. 2018, 230, 135–144. (66) Aitbekova, A.; Wu, L.; Wrasman, C. J.; Boubnov, A.; Hoffman, A. S.; Goodman, E. D.; Bare, S. R.; Cargnello, M. Low-Temperature Restructuring of CeO2‑Supported Ru Nanoparticles Determines Selectivity in CO2 Catalytic Reduction. J. Am. Chem. Soc. 2018, 140, 13736-13745. (67) Wang, R.; Wang, Y.; Ren, M.; Sun, G.; Gao, D.; Chin Chong, Y. R.; Li, X.; Chen, G. Effect of ceria morphology on the catalytic activity of Ru/ceria for the dehydrogenation of ammonia borane. Int. J. Hydrogen Energy, 2017, 42, 6757-6764. (68) Trovarelli, A. Catalytic properties of ceria and CeO2-containing materials, Catal. Rev. Sci. Eng. 1996, 38, 439–520. (69) Liu, X.; Zhou, K.; Wang, L.; Wang, B.; Li, Y. Oxygen Vacancy Clusters Promoting Reducibility and Activity of Ceria Nanorods. J. Am. Chem. Soc. 2009, 131, 3140–3141. (70) Wu, Z.; Li, M.; Howe, J.; Meyer, H. M.; Overbury, S. H. Probing Defect Sites on CeO2 Nanocrystals with Well-Defined Surface Planes by Raman Spectroscopy and O2 Adsorption. Langmuir 2010, 26, 16595–16606. (71) Campbell, C. T.; Peden, C. H. F. Oxygen Vacancies and Catalysis on Ceria Surfaces. Science 2005, 309, 713-714. (72) Wang, F.; He, S.; Chen, H.; Wang, B.; Zheng, L.; Wei, M.; Evans, D. G.; Duan, X. Active Site Dependent Reaction Mechanism over Ru/CeO2 Catalyst toward CO2 Methanation. J. Am. Chem. Soc. 2016, 138, 6298−6305. (73) Kosacki, I.; Suzuki, T.; Anderson, H. U.; Colomban, P., Raman scattering and lattice defects in nanocrystalline CeO2 thin films. Solid State Ion. 2002, 149, 99-105. (74) Dai, Q.; Zhang, Z.; Yan, J.; Wu, J.; Johnson, G.; Sun, W.; Wang, X.; Zhang, S.; Zhan, W. Phosphate-Functionalized CeO2 Nanosheets for Efficient Catalytic Oxidation of Dichloromethane. Environ. Sci. Technol. 2018, 52, 13430−13437. (75) Meng, D.; Zhan, W.; Guo, Y.; Guo, Y.; Wang, L.; Lu, G. A Highly Effective Catalyst of SmMnOx for the NH3‑SCR of NOx at Low Temperature: Promotional Role of Sm and Its Catalytic Performance. ACS Catal. 2015, 5, 5973−5983. (76) Chang, S.; Li, M.; Hua, Q.; Zhang, L.; Ma, Y.; Ye, B.; Huang, W. Shape-dependent interplay between oxygen vacancies and Ag–CeO2 interaction in Ag/CeO2 catalysts and their influence on the catalytic activity. J. Catal. 2012, 293, 195–204. (77) Zhan, W.; Guo, Y.; Gong, X.; Guo, Y.; Wang, Y.; Lu, G. Current status and perspectives of rare earth catalytic materials and Catalysis. Chin. J. Catal. 2014, 35, 1238–1250. (78) Meng, D.; Xu, Q.; Jiao, Y.; Guo, Y.; Guo, Y.; Wang, L.; Lu, G.; Zhan, W., Spinel structured CoaMnbOx mixed oxide catalyst for the selective catalytic reduction of NOx with NH3. Appl. Catal. B: Environ. 2018, 221, 652-663. (79) Wu, M.; Zhan, W.; Guo, Y.; Guo, Y.; Wang, Y.; Wang, L.; Lu, G., An effective Mn-Co mixed oxide catalyst for the solvent-free selective oxidation of cyclohexane with molecular oxygen. Appl. Catal. A: Gen. 2016, 523, 97-106. (80) Zhan, W.; Guo, Y.; Wang, Y.; Guo, Y.; Lu, G., Synthesis of lathanum or La-B doped KIT-6 ACS Paragon Plus Environment

Page 23 of 23

629 630 631 632 633 634 635 636 637 638 639

Environmental Science & Technology

mesoporous materials and their application in the catalytic oxidation of styrene. J. Rare Earths 2010, 28, 369-375. (81) Jiang, D.; Wang, W.; Zhang, L.; Zheng, Y.; Wang, Z. Insights into the Surface-Defect Dependence of Photoreactivity over CeO2 Nanocrystals with Well-Defined Crystal Facets. ACS Catal. 2015, 5, 4851−4858.

Insert Table of Contents artwork here

640

ACS Paragon Plus Environment