Chemically-Active, Porous 3D-Printed ... - ACS Publications

National Security Directorate,. ‡. Energy and Environment Directorate, and. §. Physical ... complex internal structural features accessed via a sta...
5 downloads 0 Views 5MB Size
Research Article www.acsami.org

Cite This: ACS Appl. Mater. Interfaces 2018, 10, 15112−15121

Chemically Active, Porous 3D-Printed Thermoplastic Composites Kent A. Evans,† Zachary C. Kennedy,† Bruce W. Arey,‡ Josef F. Christ,† Herbert T. Schaef,§ Satish K. Nune,*,‡ and Rebecca L. Erikson*,† †

National Security Directorate, ‡Energy and Environment Directorate, and §Physical and Computational Sciences Directorate, Pacific Northwest National Laboratory, Richland, Washington 99352, United States S Supporting Information *

ABSTRACT: Metal−organic frameworks (MOFs) exhibit exceptional properties and are widely investigated because of their structural and functional versatility relevant to catalysis, separations, and sensing applications. However, their commercial or large-scale application is often limited by their powder forms which make integration into devices challenging. Here, we report the production of MOF−thermoplastic polymer composites in well-defined and customizable forms and with complex internal structural features accessed via a standard three-dimensional (3D) printer. MOFs (zeolitic imidazolate framework; ZIF-8) were incorporated homogeneously into both poly(lactic acid) (PLA) and thermoplastic polyurethane (TPU) matrices at high loadings (up to 50% by mass), extruded into filaments, and utilized for on-demand access to 3D structures by fused deposition modeling. Printed, rigid PLA/MOF composites display a large surface area (SAavg = 531 m2 g−1) and hierarchical pore features, whereas flexible TPU/MOF composites achieve a high surface area (SAavg = 706 m2 g−1) by employing a simple method developed to expose obstructed micropores postprinting. Critically, embedded particles in the plastic matrices retain their ability to participate in chemical interactions characteristic of the parent framework. The fabrication strategies were extended to other MOFs and illustrate the potential of 3D printing to create unique porous and high surface area chemically active structures. KEYWORDS: 3D printing, metal−organic framework, fused deposition modeling, polymer composite, flexible, porous, extrusion



INTRODUCTION A multitude of metal−organic frameworks (MOFs) have been developed and used broadly throughout the fields of chemistry, materials science, and engineering. The ability to fine-tune the crystalline structure of a MOF through judicious selection of both the organic linker moieties and metal ion centers allows the modulation of catalytic activities, pore sizes for molecular storage and separations, and luminescent properties for sensing applications.1−3 One outstanding hurdle to the commercial and industrial applications of MOFs is their powder form as pure crystalline materials.4,5 For incorporation into devices, ideally MOF crystallites could be integrated into a composite platform to improve the mechanical properties but still retain their desired chemical reactivity characteristics by the preservation of their crystallinity, porosity, and surface area (SA). To this end, MOFs have been incorporated into polymers and cast into films or formed into “mixed-matrix membranes” (MMMs), grown in situ on the surface of other materials, deposited onto surfaces using a layer-by-layer strategy, electrospun into mats, or inkjet-printed onto surfaces.6−10 In some cases, the growth of a MOF layer directly on a preformed substrate may be adequate. However, issues related to the chemical compatibility of the underlying structure and the MOF synthetic procedure and the potential for poor adhesion of the MOF to the prefabricated structure motivate the development of novel © 2018 American Chemical Society

methods to disperse pregrown MOFs entirely throughout a composite structure. Three-dimensional (3D) printing is a disruptive technology poised to fundamentally augment small-scale manufacturing capabilities in numerous industries spanning from automotive and aerospace, healthcare, to nuclear energy.11−14 Currently, a major limitation across 3D printing technologies is the versatility of feedstock materials.15 For example, typical 3D printing thermoplastics, used primarily for their mechanical and structural properties, have little intrinsic functionality to act as sensors, conduct electricity, or perform catalytic functions, which significantly limits their application. As such, there is an impetus behind the development of printable feedstocks with intrinsic chemical and physical functionalities in addition to mechanical stability. Although a number of fillers and additives have been explored to address many of the functional shortcomings of 3D printing materials,16−18 surprisingly little has been done to apply the functionalities intrinsic to MOFs (catalytic sites, defined pore structures for chemical separation and storage, etc.) in this space. The ability to fine-tune the properties of MOFs through their structures makes them ideal Received: November 19, 2017 Accepted: January 31, 2018 Published: January 31, 2018 15112

DOI: 10.1021/acsami.7b17565 ACS Appl. Mater. Interfaces 2018, 10, 15112−15121

Research Article

ACS Applied Materials & Interfaces

and then selectively removed. The use of sacrificial polymeric additives to induce porosity is a relatively unexplored area, generally in 3D printing. The reported printed composites remain open to gaseous (CO2) and liquid guests (solvents). The fabrication strategies were also extended successfully to another class of MOF (UiO-66) to illustrate the potential generality of this method. The approach we developed offers an access to a new class of 3D printing materials that retain the valuable framework and functional characteristics while also imparting new structural properties from the polymeric foundation.

candidates as additives for developing multifunctional 3D printing feedstocks. Although a number of MOF composites have been proposed, there have been few efforts to design printable MOF-infused materials.19−24 Specifically, protocols to coat the surface of previously 3D-printed objects with MOFs for dye removal have been introduced.25,26 In addition, another account reports the fabrication of MOF composites using acrylonitrile−butadiene−styrene (ABS) as the base polymer with MOF loadings up to 10 wt %, although framework degradation and composite inhomogeneity were observed.27 In addition, 3D-printed monolithic contactors containing MOF74(Ni) and UTSA-16(Co) MOFs were recently fabricated by the extrusion of a paste precursor in a pressurized syringe.28 3D printing techniques have also been used to print reactors and disposable pressure vessels for the synthesis of MOFs.29,30 In this work, we aimed to apply straightforward and generalizable approaches to achieve thermoplastic−MOF composites, utilize the resulting composites as feedstocks for fused deposition modeling (FDM) printing, and maintain a valuable MOF structure and chemical activity in the printed objects. Poly(lactic acid) (PLA) was selected as an initial matrix polymer for our investigations for printing MOF composites. The thermoplastic properties of PLA are well-understood;31 both experts and nonspecialists find it simple to print PLA with a standard benchtop FDM printer, as well as cost-effective, making a 3D-printed PLA/MOF composite poised for widespread adoption in numerous applications. In addition, we targeted the production of thermoplastic polyurethane (TPU)/MOF composites. TPU-based 3D printing, although less established than PLA or ABS matrices for FDM, offers a significant advantage of high flexibility that if conferred to a MOF composite could be useful in device fabrication. Semiflex, a particular TPU that demonstrates substantial flexibility by sustaining up to 600% elongation while simultaneously retaining the structural stability with a shore hardness of 98A, was used in these studies. ZIF-8 was selected as the model MOF component because of its proven effectiveness in catalysis, chemical separations and sensing, high stability (thermal and chemical),32 and for its commercial availability in large quantities.33−35 ZIF-8 possesses tetrahedrally coordinated zinc atoms bridged by imidazolate linkers and is readily synthesized by a variety of methods (e.g., solvothermally, hydrothermally, or simply at room temperature in an aqueous or organic solution) in a range of crystallite sizes (down to the nanoscale).36,37 Herein, we demonstrate the production of MOF composites with a large SA, in customizable dimensions, as a result of high MOF particle loadings in both rigid PLA and flexible Semiflex polymer matrices using a benchtop 3D printer. Composite preparation by solution blending and subsequent casting into films prior to extrusion into printing feedstocks was critical to achieve a homogeneous and well-adhered MOF dispersion even at loadings as high as 50% by mass. Our formulation method yields composites with mechanical properties suitable for 3D printing freestanding materials with complex structures. In the rigid PLA matrix, a hierarchical porosity resulting from a combination of preserved MOF crystallinity, micropores, mesopores, and giant voids in the composites was observed at 40% MOF loadings. With more elastic Semiflex, large voids are absent and micropores are blocked at similarly high MOF filler ratios. Access to MOF micropores in Semiflex composites was instead achieved by a procedure where a sacrificial fluoropolymer was doped in, maintained throughout printing,



EXPERIMENTAL SECTION

Materials and General Methods. ZIF-8 powder (Basolite Z1200) and poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP, pellets, PN 427187, melt index = 4−10 g/10 min @ 230 °C) were purchased from Sigma-Aldrich (St. Louis, MO, USA). Natural PLA pellets were obtained from Push Plastic (Springdale, AR, USA) and Semiflex (as a 1.75 mm diameter filament), a TPU polyester elastomer with a shore hardness of 98A, from NinjaTek (Manheim, PA, USA). Zirconium 1,4-dicarboxybenzene MOF (UiO-66) powder was purchased from Strem Chemicals (Newburyport, MA, USA). The solvents used in these studies were of reagent grade at a minimum and were obtained by commercial suppliers (typically Sigma-Aldrich or Fisher Scientific (USA)). All materials were used as received. Branson 2510 was used for bath sonication, and Hielscher UP50H operating at 60% power was used for ultrasonic horn processing. Preparation of PLA/ZIF-8 Composites. A PLA stock solution (0.05 g mL−1) was prepared by dissolving PLA pellets (7.5 g) in trichloromethane (CHCl3) (150 mL) while stirring at room temperature. A typical composite with a total mass of 2 g and a ZIF-8 loading of 40% by mass was achieved first by dispersing ZIF-8 (800 mg) in ethyl acetate (10 mL) by bath sonication for 15 min. The PLA stock solution (24 mL) was then added to the MOF solution, briefly stirred (∼1 min), and the mixture was sonicated by an ultrasonic horn for 20 min. The resulting mixture was cast onto a Teflon dish, most of the solvents were removed by placing the dish on a hot plate at 75 °C, and then the composite was fully dried at 75 °C for ≥16 h in a vacuum oven under low vacuum to obtain a thick film. Preparation of Semiflex/ZIF-8 Composites. A Semiflex stock solution (0.1 g mL−1) was prepared by dissolving a Semiflex filament (5.0 g) in dimethylformamide (DMF) (50 mL) while stirring at 55 °C. Upon complete dissolution, the stock solution was stored at room temperature. A typical composite with a total mass of 2 g and ZIF-8 loading of 40% by mass was achieved first by dispersing ZIF-8 (800 mg) in acetone (15 mL) by bath sonication for 15 min. The Semiflex stock solution (12 mL) was then added to the MOF solution and blended, and acetone was removed by rotary evaporation, cast, and then dried similar to the PLA composite. For a composite with composition (50:40:10)-Semiflex/ZIF-8/PVDF-HFP and a total mass of 2 g, ZIF-8 (800 mg) was first dispersed in acetone (15 mL) by bath sonication for 10 min. A PVDF-HFP stock solution (0.1 g mL−1 in DMF, 2 mL) was added to the MOF solution and blended by bath sonication for 10 min. Last, a Semiflex solution (0.1 g mL−1 in DMF, 10 mL) was added to the ZIF-8/PVDF-HFP mixture, stirred by gently shaking the mixture (∼1 min), and then blended by an ultrasonic horn for 10 min. The composite was cast and dried as above. Filament Extrusion and 3D Printing. The composite films were cut into discrete sections and loaded into the heating barrel of a custom extruder (Figure 3b). The material was allowed approximately 2 min to reach the targeted barrel temperature of 185 °C. The material was then pressed through a 1.56 mm die to form the feedstock filaments. Using this simple extrusion method, the filament diameter for a (60:40)-PLA/ZIF-8 feedstock was 1.67 ± 0.05 mm (n = 21 measurements, along a ∼1 m section) and the filament diameter for a (40:40:20)-Semiflex/ZIF-8/PVDF-HFP was 1.64 ± 0.05 mm (n = 21, along a ∼0.8 m section of filament). For all subsequent experiments reported, the feedstock was then printed through a 400 μm diameter 15113

DOI: 10.1021/acsami.7b17565 ACS Appl. Mater. Interfaces 2018, 10, 15112−15121

Research Article

ACS Applied Materials & Interfaces

Figure 1. (a) PXRD data for (60:40)-PLA/ZIF-8 as an extruded 1750 μm (diameter) filament (top) and the simulated ZIF-8 PXRD pattern (bottom) generated from single-crystal data. (b) TGA data recorded in air of PLA; (60:40)-PLA/ZIF-8 as a 400 μm printed strand before and after activation by CH3OH treatment and evacuation. (c) N2 adsorption isotherms recorded at −196 °C on 400 μm strands (as printed) and after activation with corresponding desorption isotherms denoted with open markers. brass nozzle (E3D, Oxfordshire, UK) mounted onto a MakerBot Replicator 2X printer preheated to 200 °C with a bed temperature of 60 °C. The filament feedstock could also be printed through hardened steel nozzles (E3D) (Figure S1) using the same printing conditions. Solvent Exchange for MOF Activation and Postprocessing Treatments of Ternary Semiflex/ZIF-8/PVDF-HFP Composites. The extruded or printed samples were submerged in a solution of methyl alcohol (CH3OH) (min. 48 h). The solution was then removed, and the sample was “activated” by drying in a low vacuum oven at 75 °C (min. 3 h) prior to further analysis. The postprinting treatment of Semiflex/ZIF-8/PVDF-HFP composites was performed by submerging the material in boiling acetone for 10 min, removing from the acetone solution, washing the material with deionized water (3×), and drying the sample in a low vacuum oven similar to the activation procedure. Characterization Procedures. Nitrogen physisorption isotherms were measured on QUADRASORB SI (Quantachrome Instruments). Prior to measurement, the samples were degassed under vacuum at 105 °C for ≥18 h. The measurements were performed at −196 °C with 3 min pressure equilibration times. The SA values were determined using the Brunauer−Emmett−Teller (BET) method. Appropriate pressure points (min. 7 points) used to calculate the BET SA were selected by satisfying the criteria originally outlined by Rouquerol and discussed in detail in relation to MOF−polymer composites previously studied.38 The water vapor adsorption isotherms were obtained using a water vapor adsorption analyzer (VTI-SA+, TA Instruments). Typically, a sample was regenerated at 105 °C with a dry N2 flow for 12 h before the measurements. The relative humidity was achieved by controlling the ratio of the flow rates of the moisture stream out from the humidity generator using N2 as the carrier gas. Pure CO2 isotherms were collected at 25 °C and up to 1 bar using a Quantachrome Autosorb iQ2 gas adsorption instrument. Thermogravimetric analyses (TGAs) were run on Netzsch TG 209 F3 in Al2O3 pans. The samples were initially held at 40 °C for 20 min and then heated to 800 °C at a ramp rate of 5 °C min−1 in an air atmosphere. The powder X-ray diffraction (PXRD) patterns were characterized on a D8 Discover XRD unit equipped with a rotating Cu

anode (1.54 Å), Göbel Mirror, 0.5 mm collimator, and 0.5 mm pin hole. A GADDS area detector system positioned at 28.0° 2θ with a measured distance from the sample of 15 cm was used to capture diffraction images. The collection of individual XRD tracings required 200 s with power settings of 45 kV and 200 mA. Initially, the images were processed with Bruker-AXS GADDS software before importing into JADE XRD software to obtain peak positions (° 2θ) and intensities. Helium ion microscopy (HeIM) was performed using Zeiss Helium Ion ORION PLUS. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) data were acquired on FEI Helios 660 DualBeam and EDAX TEAM EDS software with an Apollo detector. Secondary electron (SE) and backscatter electron (BSE) images along with elemental maps were obtained in the plane view and on the cross sections of printed samples. The samples for cross-sectional analysis were prepared by standard metallographic specimen preparation techniques where the printed materials were placed vertically into mounts, sandwiched between two glass slides, and then polished with a diamond abrasive. An elemental analysis of the bulk F content in the printed samples was performed by the ionselective electrode method at Robertson Microlit Laboratories (Ledgewood, NJ, USA).



RESULTS AND DISCUSSION 3D Printing of Rigid PLA/MOF Composites. Solution casting was the first step in the preparation of all MOF composite filaments in this study, a technique previously proven effective for the generation of MMM with highparticulate loadings.39 PLA/ZIF-8 composites were obtained by suspending commercial ZIF-8 (Basolite Z1200) in ethyl acetate (EtOAc) by sonication, followed by the addition of a dilute PLA solution (0.05 g mL−1 in CHCl3) to the MOF suspension. After additional sonication, the mixtures were cast and dried. The resulting thick films were cut, fed into the heated (185 °C) barrel of a custom-built extruder, and pressed through a die to yield filament composites with a diameter of ca. 1750 μm. 15114

DOI: 10.1021/acsami.7b17565 ACS Appl. Mater. Interfaces 2018, 10, 15112−15121

Research Article

ACS Applied Materials & Interfaces

Figure 2. HeIM images of a 400 μm printed (60:40)-PLA/ZIF-8 strand at a low magnification (left), an intermediate magnification (center), and high magnifications (right, right inset) where the embedded ZIF particles are more clearly observed protruding out of the polymer matrix. Left inset: photograph of a freestanding sorbent waffle architecture printed using a (60:40)-PLA/ZIF-8 filament.

intervals (maximum 3−5 min at 185 °C during extrusion and ∼30 s to a few minutes up to 200 °C), the decomposition of PLA is not expected to occur to an appreciable extent when printing. Importantly, the thermogravimetric behavior of the composite suggests that the MOF pores remain accessible to the guest molecules as validated by their ability to undergo solvent exchange. The SAs of extruded and printed ZIF-8/PLA composites, an important metric to further assess the gas accessibility to the MOFs and their presentation within the composites, were determined using the BET method from nitrogen adsorption experiments at −196 °C. The extruded filament (d = 1750 μm) with a 40% ZIF-8 loading and no other postprocessing yielded a very low BET SA (