Chemically Engineered Substrates for Patternable Growth of Two

Oct 17, 2016 - Since the discovery of graphene, the realm of two-dimensional (2D) chalcogenide crystals hosting rich electronic or optoelectronic prop...
3 downloads 11 Views 6MB Size
Chemically Engineered Substrates for Patternable Growth of Two-Dimensional Chalcogenide Crystals Mingzhan Wang, Jinxiong Wu, Li Lin, Yujing Liu, Bing Deng, Yunfan Guo, Yuanwei Lin, Tian Xie, Wenhui Dang, Yubing Zhou, and Hailin Peng* Center for Nanochemistry, Beijing Science and Engineering Center for Nanocarbons, Beijing National Laboratory for Molecular Sciences, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, P.R. China S Supporting Information *

ABSTRACT: The key challenge of direct integration of two-dimensional (2D) chalcogenide crystals into functional modules is precise control of the nucleation sites of the building blocks. Herein, we exploit the chemical activities and surface engineering of the substrates to manipulate the nucleation energy barrier of 2D crystals and thereby realize the patternable growth of 2D crystals. The selective-region chemical modifications of the substrates are achieved via microcontact printing combined with the elegant self-assembly of octadecyltrichlorosilane molecules on the substrates. The patternable growth method is versatile and can be used as a general strategy for growing a broad class of high-quality 2D chalcogenide crystals with tailorable configurations on a variety of chemically engineered substrates. Moreover, we demonstrate flexible transparent electrodes based on largescale patterned nanogrids of topological insulator Bi2Se3, which possess tailored trade-off between electric conductivity and optical transmittance across the visible to near-infrared regime. We hope this method may open an avenue to the efficient integration and batch production of 2D chalcogenide crystals and could inspire ongoing efforts of the fabrication of van der Waals heterostructures. KEYWORDS: patternable growth, 2D crystals, chemical activity, substrate

S

the nanoscale building blocks, the key point is the precise control over nucleation sites and the concomitant layout of patterned crystals, including the size, geometry, and orientation, etc. In terms of the controlled growth of various 2D crystals, van der Waals epitaxy was proven to be a versatile technique on substrates such as mica and SiO2/Si, which are tolerant of considerable lattice mismatch.12−18 The thickness and nucleation density can be well-controlled by tuning the growth parameters such as the deposition temperature, pressure, and growth duration. However, the tuning of these parameters still falls short of precisely controlling the nucleation sites therewith usually random locations of the resultant 2D crystals, let alone the patternable growth. From the perspective of the crystal nucleation and growth mechanism, the rationale dominating the patternable growth of the building block is to induce a dramatic energy difference of the nucleation barrier. Therefore,

ince the discovery of graphene, the realm of twodimensional (2D) chalcogenide crystals hosting rich electronic or optoelectronic properties has been intensely explored.1−3 To achieve the full potential of 2D chalcogenide crystals, it is of technological significance to integrate the 2D nanostructures into sophisticated functional electronic or optoelectronic modules with patterned architectures, for example, the integrated circuits (IC). Actually, this bottom-up paradigm is persistently pursued since the inception of nanoscience and nanotechnology (e.g., oriented carbon nanotubes,4,5 semiconductor nanowires arrays,6,7 inorganic nanocrystal arrays,8 and organic semiconductor arrays).9,10 To this end, two approaches are usually employed. One approach is the postgrowth manipulation of the random nanoscale building blocks,7,11 and the other one is the direct configuration of the nanoscale building blocks into predesigned pattern during growth,9,10 viz. the patternable growth of the nanoscale building blocks. The latter approach is generally believed to be superior for its simple procedure, and more importantly, it avoids potential damages or contaminations of the vulnerable nanoscale materials. With regard to the patternable growth of © 2016 American Chemical Society

Received: September 6, 2016 Accepted: October 17, 2016 Published: October 17, 2016 10317

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323

Article

www.acsnano.org

Article

ACS Nano

Figure 1. Patternable growth of 2D-layered crystals. (a) Schematic illustration of the procedure of patterning 2D crystal arrays by chemically engineering the substrates. (b) Layered crystal structure of Bi2Se3, Bi2Te3, and In2Se3 composed of quintuple layers. (c) Typical optical microscope (OM) image of large-area patterned topological insulator Bi2Se3 2D nanoplate arrays on mica. Inset: Zoomed-in OM image of (c); scale bar is 20 μm. (d) AFM image of two adjacent patterned 2D Bi2Se3 nanoplates on mica. (e) Typical Raman spectrum of the patterned 2D Bi2Se3 nanoplates. (f) Raman mapping (Eg2 mode) of two adjacent patterned 2D Bi2Se3 nanoplates on mica.

scanning electron microscopy (SEM) (Figure S2e), and atomic force microscopy (AFM) (Figure S2f) indicate that mica was readily modified by OTS-SAMs and the pattern transfer proceeded with excellent fidelity. Bi2Se3, Bi2Te3, and In2Se3 are studied in this work as the model systems to verify the efficacy of this methodology for the patternable growth of 2D crystals because of their potential in electronics or optoelectronics. In detail, Bi2Se3 and Bi2Te3 are members of the family identified to be topological insulators (TIs), a quantum phase matter combining trivial gaped bulk states with nontrivial surface/edge states.24,25 This exotic electronic signature renders TIs as promising building block candidates for next-generation low-power consumption electronics. In2Se3, a traditional phase change material, has recently been proven to be highly efficient in photocurrent conversion.13,22,26 As depicted in Figure 1b, the layered chalcogenides of Bi2Se3, Bi2Te3, and In2Se3 have similar crystal structures, composed of planar quintuple layer (QL) units. Atoms within each QL unit (height ca. 1 nm) are strongly bonded by covalence, while adjacent QLs are weakly connected by van der Waals interactions. The as-modified mica substrates together with the Bi2Se3 crystal powders were loaded into the apparatus similar to previous works (Figure S3).13,14,17,18,22,27 Strikingly, preferential crystallization of Bi2Se3 nanoplate arrays takes place on the modified regions of the substrate unambiguously. Figure 1c demonstrates a typical optical microscope (OM) image of a large-area patterned Bi2Se3 nanoplate arrays. The arrays correspond to 10 μm square domains and 5 μm intervals, corresponding to the density of nanoplate arrays as high as 2.8 × 106 per square inch. The uniform color contrast is indicative of the uniform thickness of the nanoplate arrays. Such uniformity was further confirmed by AFM and micro-Raman spectroscopy. The thickness of the nanoplates can be wellcontrolled down to 4 nm (4 QLs) with excellent flatness (Figure 1d). Raman spectrum exhibits three sharp peaks, characteristic of Bi2Se3 (Figure 1e).14,28 Raman mapping also

the current methodology is concentrated on the selectiveregion engineering of the substrates. Nevertheless, the finite methods reported for the patternable growth of 2D crystals thus far are either short of scalability and freedoms of pattern design or plagued by substrates. For instance, the mask-assisted plasma etching performs physical surgeries of the substrate and suffers from scalability.13,17,18 The seeded growth method heavily relies on costly and ponderous microfabrication technologies.19−21 Moreover, the patterned architectures show poor crystallinity and limited freedoms of pattern design. The microintaglio printing method demonstrates incredibly flexible freedoms of pattern design and distinct scalability.22 However, the microintaglio printing method is plagued by substrates due to its patternbable growth process. Clearly, versatile and scalable patternable growth methods for high-quality 2D crystals are highly desired. Herein, we exploit the chemical activities of the substrates to achieve large-area patternable growth of 2D chalcogenide crystals. Our method not only shows flexible freedoms of pattern design and excellent scalability but also remarkablyremoves the limitations imposed by substrates due to its growth mechanism, which has not been reported for the patternable growth of 2D crystals.

RESULTS AND DISCUSSION The key of this strategy relies on the manipulation of the nucleation energy barrier by selective-region chemical modification of the substrates. As schematically illustrated in Figure 1a, we take advantage of the microcontact printing technique combined with the molecular self-assembly of octadecyltrichlorosilane (OTS) molecules on muscovite mica (KAl2(Si3Al)O10(OH)2), which is ultrahydrophilic (Figure S2a) and atomically flat (Figure S2d).23 As elastomeric polydimethylsiloxane (PDMS) stamp conformally contacted the mica substrate, OTS molecules were printed onto the substrate. Thereby, OTS self-assembled monolayers (OTSSAMs) form on the surface via chemical bonds, perfectly reproducing the artificially tailorable relief structures of the stamp (Figure S1). Contact angle examinations (Figure S2b), 10318

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323

Article

ACS Nano

Figure 2. Structural analyses of the patterned Bi2Se3 nanoplate arrays. (a) XRD pattern of Bi2Se3 nanoplate arrays on mica (red line), freshly cleaved muscovite mica (blue line), and reference diffractogram of rhombohedral Bi2Se3 (black line, PDF#33-0214). Note that the intensity is in logarithmic scale to manifest the signals of Bi2Se3. (b) Low-magnification bright-field TEM image of Bi2Se3 nanoplate arrays. (c) Highresolution TEM image of Bi2Se3 nanoplate edge. (d−j) SAED patterns corresponding to sites 1−7 in (b); scale bar is 5 nm−1. (k) Histogram of the SAED angle of 20 different sites.

characterizations (Figure 2b and Figure S7a). The EDX analysis confirms the atomic ratio of Bi and Se to be approximately 2:3 (Figure S7b,c). As shown in the high-resolution TEM image, the Bi2Se3 crystals are of high quality with a clear lattice spacing of ∼0.21 nm, consistent with the lattice plane of (11−20) in rhombohedral Bi2Se3 (Figure 2c). Interestingly, as shown in Figure 2d−j, the SAED patterns of adjacent nanoplates show almost identical lattice direction (deviation smaller than ±1°, Figure 2k), reminiscent of the single-crystalline nature of aspatterned Bi2Se3 crystal arrays as well as the substrate-induced orientation alignment on unmodified mica.13,17 The singlecrystalline nature can be further confirmed by the perfect hexagonal diffraction pattern and same orientation of the thick Bi2Se3 nanoplate arrays (Figure S9c). In brief, the systematic structural characterizations indicate the high quality of aspatterned Bi2Se3 nanoplate arrays obtained via our method. For better manipulation of the patternable growth, it is of prime significance to investigate the underlying mechanism. Consequently, we conducted control experiments as follows: chemically modified substrates were annealed under conditions similar to that of general growth, whereas no source powders were loaded. The pristine OTS-SAMs are densely compact and uniform in height, as evident in the AFM image (Figure 3a and Figure S8a,d). In contrast, OTS-SAMs turn into loose and discrete particles with the same height in the modified domain after being annealed at 490 °C (Figure 3b and Figure S8b,e). This phenomenon becomes more self-evident when the annealing temperature is increased to 750 °C (Figure 3c and Figure S8c,f). Thus, we postulate that these particles serve as the nucleation sites, in good consistency with the crystal growth theory dictating that heterogeneous nucleations need dramat-

reveals the ultrahigh homogeneity of nanoplate arrays as well as the inappreciable crosstalk between the crystals (Figure 1f). To check the versatility of this methodology, we change the source crystals, stamp relief structures, as well as the target substrates. Figure S4e presents the optical images of as-grown In2Se3 nanoplate arrays using a PDMS stamp identical to that of Bi2Se3 nanoplate arrays. By utilizing the PDMS stamp with reverse relief structures (Figure S1d), large-area Bi 2Se 3 nanogrids were achieved (Figure 4b and Figure S4b−d). Furthermore, other configurations, including different domain sizes (Figure S5) and elaborate geometries of the patterned crystal, were achieved (Figure S6). These observations further corroborate that the configurations of the patterned nanostructures are purely contingent on the relief structure of the PDMS stamp or the manipulation of the PDMS stamp, justifying the highly flexible freedoms of pattern design. Subsequently, to evaluate the quality of the patterned 2D crystal arrays, we carried out systematic structural characterizations, including the X-ray diffraction (XRD), transmission electron microscopy (TEM), selective area electron diffraction (SAED), and energy-dispersive spectroscopy (EDX). XRD measurements of the as-synthesized thick Bi2Se3 nanoplate arrays were directly performed on mica without transfer. The as-achieved Bi2Se3 crystal arrays crystallize into the phase-pure rhombohedral structure, as revealed by the XRD patterns (Figure 2a). Meanwhile, the peaks are well-indexed into the (0001) family planes of a Bi2Se3 rhombohedral crystal, indicating that the c-axis of as-grown crystal is perpendicular to the mica plane. Moreover, the patterned Bi2Se3 2D crystal arrays were faithfully transferred onto the holey carbon film with the aid of poly(methyl methacrylate) (PMMA) for TEM 10319

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323

Article

ACS Nano

Figure 3. Patternable growth mechanism. (a) AFM image of the pristine OTS-SAMs on mica; scale bar is 5 μm. (b,c) AFM image of the OTSSAMs on mica after being annealed at 490 and 750 °C, respectively; scale bar is 5 μm. (d−f) OM images showing the morphology evolution of Bi2Se3 nanoplate arrays during the patternable growth with mild rate of carrier gas (typically 500 sccm). Insets are OM images of nuclei on mica corresponding to respective domain size. (i) SEM images of patterned Bi2Se3 nanoplate arrays with a domain size of ∼2 μm; scale bar is 5 μm.

aligned in our method, as clearly demonstrated in Figure 3g. The trick is presumably due to the growth mechanism, in which the coalesced uniform nuclei (∼2 QLs) may serve as the buffer layer and therefore removes the limitations imposed by substrates. The hypothesis is supported by the well-developed buffer-layer methodology, which has been verified to be powerful for both traditional epitaxy and van der Waals epitaxy in removing the limitations imposed by the substrate. For traditional epitaxy, the most successful story is the growth of single-crystalline GaN epifilms via buffer-layer mediation, which enables the revolution of blue light diodes.30,31 Markedly analogous to our case, it is claimed that high-quality Bi2Se3 epifilms can be achieved via van der Waals epitaxy on the buffer layer of Bi2Se3 itself, which also effectively removes the limitations imposed by substrates.16,32 So all the findings coherently confirm that our patternable growth method could remove the limitations imposed by substrates. Furthermore, these insulating substrates are compatible with modern electronics technologies. In addition, we note that the window for patternable growth is relatively narrow: the substrate temperature and the flow rate of carrier gas are identified to be critical parameters to achieve the patternable growth of 2D crystals. Low substrate temperature is more favorable to the formation of continuous films on both the modified and unmodified substrate regions, rather than discrete nanoplate arrays merely on modified substrates

ically lower nucleation energy barriers. Meanwhile, the general morphology evolution of Bi2Se3 nanoplate arrays during growth is clearly distinguished and presented in Figure 3d−f. The snapshot captured at the intermediate state of nucleation shows that uniform discrete nuclei about 2 QLs (∼2 nm) form within the modified domain (inset of Figure 3d). When the nuclei fully coalesce, as shown in Figure 3e, the growth proceeds in a layerby-layer growth mode, a well-established signature of 2D crystal growth (inset of Figure 3e).12,14,16,22,29 These observations further validate our postulation that discrete particles serve as the nucleation centers. Furthermore, the subsequent layer-bylayer growth scenario facilitates the thickness control of the aspatterned 2D-layered crystals, simply by tuning the growth duration (Figure S9). Notably, the thick patterned Bi2Se3 architectures typically exhibit approximately hexagonal morphology (Figure 3f and Figure S9c), deviating from the predesigned square relief structures. This phenomenon is putatively due to the anisotropic growth of Bi2Se3, which is in turn determined by its rhombohedral crystal lattice. Moreover, it is worth noting that this method is also applicable to other substrates. For example, nanoplate arrays of chalcogenide crystals can form on modified SiO2/Si and glass with considerably good crystallinity (Figure 3g and Figure S10). In particular, the 2D chalcogenide crystals are usually not aligned on SiO2/Si because of the amorphous property of SiO2.27 However, the patterned Bi2Se3 nanoplate arrays are 10320

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323

Article

ACS Nano

Figure 4. Patterned Bi2Se3 nanogrids for flexible transparent electrodes. (a) Digital micrograph of the patterned flexible Bi2Se3 nanogrids on mica. (b) OM image of large-area patterned Bi2Se3 2D nanogrids. Inset: Zoomed-in OM image of (b); scale bar is 20 μm. (c) Optical transmittance of the patterned Bi2Se3 nanogrids, continuous Bi2Se3 film, muscovite mica, and ITO. (d) Sheet resistance of patterned Bi2Se3 nanogrids with different thickness and continuous Bi2Se3 film.

excellent optical transmittance across the visible to nearinfrared regime with good electric conductivity. In comparison with ITO electrodes, the patterned Bi2Se3 nanogrids have comparable transmittance in the visible light regime and superior transmittance in the near-infrared regime (Figure 4c). The excellent optical transparency is attributed to two reasons: one is due to its grid structure; the other one is the exotic spin nondegenerate surface states of a topological insulator, which prohibits the carriers of surface states from the direct photoexcitation.34 The sheet resistances were measured on the large-area patterned Bi2Se3 nanogrids in a four-probe configuration. As presented in Figure 4d, the sheet resistance of Bi2Se3 nanogrids is larger than that of its continuous film counterpart because the “filling factor” of nanogrids is always less than 1 (in our case, as indicated in Figure 4b, the filling factor is ca. 55.56%).35 The sheet resistance of Bi2Se3 nanogrids can be tuned by its thickness. Obviously, for specific applications, the desired tradeoff between the optical transparency and sheet resistance can, in principle, be tuned by tailoring the grid structures (filling factor) and thickness of nanogrids. The preliminary results suggest that our patternable growth method is versatile and easy to scale up for batch production of topological insulator Bi2Se3 nanogrid-based flexible transparent electrodes for potential use in display windows, touch screens, and wearable electronics.

with minimal in-between crosstalks (Figure S11). The result can be elucidated by classic film growth theory. According to the film growth theory, the nucleation rate is co-determined by pressure, substrate temperature, and nucleation energy (Figure S11g).33 Because the specific substrate is always exposed to the same environment, it is therefore impossible to achieve patternable growth by tuning pressure P and substrate temperature T. However, extreme conditions of P or T can result in an ultrafast or ultraslow nucleation rate, which is destructive for patternable growth. In this case, low substrate temperature leads to ultrafast nucleation rate, and thereby continuous films tend to form. Meanwhile, a higher flow of carrier gas would result in a difficult coalescence of each nuclei into one single uniform epilayer within one modified domain. Discrete nanoplates tend to form within one modified domain (insets of Figure 3h). Moreover, the number of nuclei within one modified domain is positively correlated to the domain area, and a single nucleus was achieved by diminishing the domain size down to ∼2 μm (Figure 3h,i and Figure S12). This observation is in close analogy to the patternable growth of nonlayered inorganic nanocrystal arrays8 or organic semiconductor arrays9 by means of OTS-SAMs. The contrast highlights the layered structures of 2D crystals. Continuous nanosheets of topological insulator Bi2Se3 have been recognized by our group and others as a promising candidate for flexible transparent electrodes, which are immune to surface contaminations and bending.34−36 Compared to ITO electrodes, the Bi2Se3 electrode possesses extraordinary transmittance in the near-infrared regime and relatively lower transmittance in the visible light regime. In this work, we demonstrate the patterned large-area Bi2Se3 nanogrid-based flexible transparent electrodes (Figure 4a,b), which shows

CONCLUSION In summary, we exploit the chemical activities of the substrates and develop a scalable and versatile method for the patternable growth of 2D chalcogenide crystals. Remarkably, our method could remove the limitations imposed by substrates. Our 10321

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323

Article

ACS Nano findings may open an avenue to the integration and batch production of 2D crystal devices and inspire ongoing efforts dedicated to the fabrication of the in-plane or vertical van der Waals heterostructures.15,37

National Program for Support of Top-Notch Young Professionals.

REFERENCES (1) Novoselov, K. S.; Geim, A. K.; Morozov, S. V.; Jiang, D.; Zhang, Y.; Dubonos, S. V.; Grigorieva, I. V.; Firsov, A. A. Electric Field Effect in Atomically Thin Carbon Films. Science 2004, 306, 666−669. (2) Butler, S. Z.; Hollen, S. M.; Cao, L.; Cui, Y.; Gupta, J. A.; Gutierrez, H. R.; Heinz, T. F.; Hong, S. S.; Huang, J.; Ismach, A. F.; et al. Progress, Challenges, and Opportunities in Two-Dimensional Materials Beyond Graphene. ACS Nano 2013, 7, 2898−2926. (3) Zhang, H. Ultrathin Two-Dimensional Nanomaterials. ACS Nano 2015, 9, 9451−9469. (4) Fan, S. S.; Chapline, M. G.; Franklin, N. R.; Tombler, T. W.; Cassell, A. M.; Dai, H. J. Self-Oriented Regular Arrays of Carbon Nanotubes and Their Field Emission Properties. Science 1999, 283, 512−514. (5) Li, W. Z.; Xie, S. S.; Qian, L. X.; Chang, B. H.; Zou, B. S.; Zhou, W. Y.; Zhao, R. A.; Wang, G. Large-Scale Synthesis of Aligned Carbon Nanotubes. Science 1996, 274, 1701−1703. (6) Huang, M. H.; Mao, S.; Feick, H.; Yan, H. Q.; Wu, Y. Y.; Kind, H.; Weber, E.; Russo, R.; Yang, P. D. Room-Temperature Ultraviolet Nanowire Nanolasers. Science 2001, 292, 1897−1899. (7) Melosh, N. A.; Boukai, A.; Diana, F.; Gerardot, B.; Badolato, A.; Petroff, P. M.; Heath, J. R. Ultrahigh-Density Nanowire Lattices and Circuits. Science 2003, 300, 112−115. (8) Aizenberg, J.; Black, A. J.; Whitesides, G. M. Control of Crystal Nucleation by Patterned Self-Assembled Monolayers. Nature 1999, 398, 495−498. (9) Briseno, A. L.; Mannsfeld, S. C. B.; Ling, M. M.; Liu, S.; Tseng, R. J.; Reese, C.; Roberts, M. E.; Yang, Y.; Wudl, F.; Bao, Z. Patterning Organic Single-Crystal Transistor Arrays. Nature 2006, 444, 913−917. (10) Xiao, K.; Tao, J.; Puretzky, A. A.; Ivanov, I. N.; Retterer, S. T.; Pennycook, S. J.; Geohegan, D. B. Selective Patterned Growth of Single-Crystal Ag-TCNQ Nanowires for Devices by Vapor-Solid Chemical Reaction. Adv. Funct. Mater. 2008, 18, 3043−3048. (11) Huang, Y.; Duan, X. F.; Wei, Q. Q.; Lieber, C. M. Directed Assembly of One-Dimensional Nanostructures into Functional Networks. Science 2001, 291, 630−633. (12) Koma, A. Van der Waals Epitaxy - a New Epitaxial-Growth Method for a Highly Lattice-Mismatched System. Thin Solid Films 1992, 216, 72−76. (13) Lin, M.; Wu, D.; Zhou, Y.; Huang, W.; Jiang, W.; Zheng, W.; Zhao, S.; Jin, C.; Guo, Y.; Peng, H.; et al. Controlled Growth of Atomically Thin In2se3flakes by van der Waals Epitaxy. J. Am. Chem. Soc. 2013, 135, 13274−13277. (14) Dang, W.; Peng, H.; Li, H.; Wang, P.; Liu, Z. Epitaxial Heterostructures of Ultrathin Topological Insulator Nanoplate and Graphene. Nano Lett. 2010, 10, 2870−2876. (15) Tan, C.; Zhang, H. Epitaxial Growth of Hetero-Nanostructures Based on Ultrathin Two-Dimensional Nanosheets. J. Am. Chem. Soc. 2015, 137, 12162−12174. (16) Li, H. D.; Wang, Z. Y.; Kan, X.; Guo, X.; He, H. T.; Wang, Z.; Wang, J. N.; Wong, T. L.; Wang, N.; Xie, M. H. The van der Waals Epitaxy of Bi2Se3 on the Vicinal Si(111) Surface: An Approach for Preparing High-Quality Thin Films of a Topological Insulator. New J. Phys. 2010, 12, 103038. (17) Li, H.; Cao, J.; Zheng, W.; Chen, Y.; Wu, D.; Dang, W.; Wang, K.; Peng, H.; Liu, Z. Controlled Synthesis of Topological Insulator Nanoplate Arrays on Mica. J. Am. Chem. Soc. 2012, 134, 6132−6135. (18) Zhou, Y.; Nie, Y.; Liu, Y.; Yan, K.; Hong, J.; Jin, C.; Zhou, Y.; Yin, J.; Liu, Z.; Peng, H. Epitaxy and Photoresponse of TwoDimensional GaSe Crystals on Flexible Transparent Mica Sheets. ACS Nano 2014, 8, 1485−1490. (19) Han, G. H.; Kybert, N. J.; Naylor, C. H.; Lee, B. S.; Ping, J.; Park, J. H.; Kang, J.; Lee, S. Y.; Lee, Y. H.; Agarwal, R. Seeded Growth of Highly Crystalline Molybdenum Disulphide Monolayers at Controlled Locations. Nat. Commun. 2015, 6, 6128.

EXPERIMENTAL SECTION Chemical Modification of the Substrates. The procedure for the fabrication of the PDMS stamp was the same as that in our previous work.22 For the chemical modifications of the substrates, OTS/n-hexane solution (0.5−1 mmol/L) was first applied onto the PDMS stamp using a cotton swab several times. It could be seen that n-hexane evaporated very quickly. Then the PDMS stamp conformally contacted the substrates for 10−30 min. Lastly, the PDMS stamp was peeled off from the modified substrates with care. N-Octadecyltrichlorosilane (purity 95%, ∼5−10% branched isomers) was purchased from Alfa Aesar, stored in a glovebox in argon in ambient environment, and used as received. Patternable Growth of 2D Materials. The source powders of Bi2Se3 (purity 99.999%), Bi2Te3 (purity 99.999%), and In2Se3 (purity 99.99%) were purchased from Alfa Aesar and used as received. The source powders together with chemically modified substrates were loaded into a horizontal tube furnace (Lindberg/Blue M) with a 1 in. diameter quartz tube heated by a 12 in. long process tube. The substrates were typically placed sequentially from 6 to 13 cm away from the heat center of the furnace. The carrier gas was argon. Before the temperature was increased, the system was thoroughly purge with Ar several times. Typically, the temperature was increased to 470−500 °C for the patternable growth of Bi2Se3 and Bi2Te3 and 720−750 °C for the patternable growth of In2Se3. The increase rate of temperature was generally set ∼30 °C/min, and growth duration was tuned from 5 to 60 min. Characterization. The OTS self-assembled monolayer and patterned 2D chalcogenide crystals (Bi2Se3, Bi2Te3, and In2Se3) were characterized by optical microscopy (Olympus DX51 microscope), scanning electron microscopy (Hitachi S-4800, acceleration voltage 0.5−2 kV), and atomic force microscopy (Vecco Nanoscope IIIa and Bruker Dimension Icon, tapping mode). Transmission electron microscopy was performed on FEI Tecnai F30 (acceleration voltage 300 kV) equipped with an energy-dispersive X-ray spectrometer. X-ray diffraction spectroscopy was performed on Bruker D8 Advanced diffractometer in modified Debye−Scherrer geometry with Cu Kα1 radiation. Raman spectra and mapping were conducted on a Horiba HR800 Raman system using a 514 nm laser for excitation. Contact angle tests were measured on OCA 20. UV−vis−IR transmittance measurements were performed on PerkinElmer Lambda 950 spectrophotometer. Sheet resistances were measured on Res Map 178 (Creative Design Engineering Inc., Silicon Valley).

ASSOCIATED CONTENT S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsnano.6b06023. Supplementary text, Figures S1−S12, and additional references (PDF)

AUTHOR INFORMATION Corresponding Author

*E-mail: [email protected]. Notes

The authors declare no competing financial interest.

ACKNOWLEDGMENTS This work is financially supported by the National Natural Science Foundation of China (No. 21525310), the National Basic Research Program of China (No. 2014CB932500), and 10322

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323

Article

ACS Nano (20) Su, G.; Hadjiev, V. G.; Loya, P. E.; Zhang, J.; Lei, S.; Maharjan, S.; Dong, P.; Ajayan, P. M.; Lou, J.; Peng, H. Chemical Vapor Deposition of Thin Crystals of Layered Semiconductor SnS2 for Fast Photodetection Application. Nano Lett. 2015, 15, 506−513. (21) Yu, Q.; Jauregui, L. A.; Wu, W.; Colby, R.; Tian, J.; Su, Z.; Cao, H.; Liu, Z.; Pandey, D.; Wei, D.; et al. Control and Characterization of Individual Grains and Grain Boundaries in Graphene Grown by Chemical Vapour Deposition. Nat. Mater. 2011, 10, 443−449. (22) Zheng, W.; Xie, T.; Zhou, Y.; Chen, Y. L.; Jiang, W.; Zhao, S.; Wu, J.; Jing, Y.; Wu, Y.; Chen, G.; et al. Patterning Two-Dimensional Chalcogenide Crystals of Bi2Se3 and In2Se3 and Efficient Photodetectors. Nat. Commun. 2015, 6, 6972. (23) Xia, Y. N.; Whitesides, G. M. Soft Lithography. Angew. Chem., Int. Ed. 1998, 37, 550−575. (24) Zhang, H.; Liu, C.-X.; Qi, X.-L.; Dai, X.; Fang, Z.; Zhang, S.-C. Topological Insulators in Bi2Se3, Bi2Te3 and Sb2Te3 with a Single Dirac Cone on the Surface. Nat. Phys. 2009, 5, 438−442. (25) Xia, Y.; Qian, D.; Hsieh, D.; Wray, L.; Pal, A.; Lin, H.; Bansil, A.; Grauer, D.; Hor, Y. S.; Cava, R. J.; et al. Observation of a Large-Gap Topological-Insulator Class with a Single Dirac Cone on the Surface. Nat. Phys. 2009, 5, 398−402. (26) Island, J. O.; Blanter, S. I.; Buscema, M.; van der Zant, H. S. J.; Castellanos-Gomez, A. Gate Controlled Photocurrent Generation Mechanisms in High-Gain In2Se3 Phototransistors. Nano Lett. 2015, 15, 7853−7858. (27) Kong, D.; Dang, W.; Cha, J. J.; Li, H.; Meister, S.; Peng, H.; Liu, Z.; Cui, Y. Few-Layer Nanoplates of Bi2Se3 and Bi2Te3 with Highly Tunable Chemical Potential. Nano Lett. 2010, 10, 2245−2250. (28) Zhang, J.; Peng, Z.; Soni, A.; Zhao, Y.; Xiong, Y.; Peng, B.; Wang, J.; Dresselhaus, M. S.; Xiong, Q. Raman Spectroscopy of FewQuintuple Layer Topological Insulator Bi2se3 Nanoplatelets. Nano Lett. 2011, 11, 2407−2414. (29) Li, Y. Y.; Wang, G.; Zhu, X. G.; Liu, M. H.; Ye, C.; Chen, X.; Wang, Y. Y.; He, K.; Wang, L. L.; Ma, X. C.; et al. Intrinsic Topological Insulator Bi2te3 Thin Films on Si and Their Thickness Limit. Adv. Mater. 2010, 22, 4002−4007. (30) Amano, H.; Sawaki, N.; Akasaki, I.; Toyoda, Y. Metalorganic Vapor-Phase Epitaxial-Growth of a High-Quality GaN Film Using an AlN Buffer Layer. Appl. Phys. Lett. 1986, 48, 353−355. (31) Nakamura, S. GaN Growth Using GaN Buffer Layer. Jpn. J. Appl. Phys., Part 2 -Letters 1991, 30, L1705−L1707. (32) Taskin, A. A.; Sasaki, S.; Segawa, K.; Ando, Y. Manifestation of Topological Protection in Transport Properties of Epitaxial Bi2Se3 Thin Films. Phys. Rev. Lett. 2012, 109.06680310.1103/PhysRevLett.109.066803 (33) Ohring, M. Materials Science of Thin Films, 2nd ed.; Elsevier: Amsterdam, 2001. (34) Peng, H.; Dang, W.; Cao, J.; Chen, Y.; Wu, D.; Zheng, W.; Li, H.; Shen, Z.-X.; Liu, Z. Topological Insulator Nanostructures for nearInfrared Transparent Flexible Electrodes. Nat. Chem. 2012, 4, 281− 286. (35) Guo, Y.; Aisijiang, M.; Zhang, K.; Jiang, W.; Chen, Y.; Zheng, W.; Song, Z.; Cao, J.; Liu, Z.; Peng, H. Selective-Area Van Der Waals Epitaxy of Topological Insulator Grid Nanostructures for Broadband Transparent Flexible Electrodes. Adv. Mater. 2013, 25, 5959−5964. (36) Lin, Z.; Chen, Y.; Yin, A.; He, Q.; Huang, X.; Xu, Y.; Liu, Y.; Zhong, X.; Huang, Y.; Duan, X. Solution Processable Colloidal Nanoplates as Building Blocks for High-Performance Electronic Thin Films on Flexible Substrates. Nano Lett. 2014, 14, 6547−6553. (37) Geim, A. K.; Grigorieva, I. V. Van der Waals Heterostructures. Nature 2013, 499, 419−425.

10323

DOI: 10.1021/acsnano.6b06023 ACS Nano 2016, 10, 10317−10323