Clustered-Microcapsule-Shaped Microporous Carbon-Coated Sulfur

Engineering, Harbin Institute of Technology, No. 92 West-Da Zhi Street, Harbin 150001, China. ACS Appl. Mater. Interfaces , 2017, 9 (51), pp 44512...
5 downloads 12 Views 1MB Size
Subscriber access provided by RMIT University Library

Article

Clustered-microcapsule-shaped Microporous Carbon Coated Sulfur Composite Synthesized via In-situ Oxidation Qian Wang, Honghong Liu, Rongrong Li, Minghui Yang, Zhen-Bo Wang, Li-Mei Zhang, Chao Li, and Da-Ming Gu ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b14467 • Publication Date (Web): 05 Dec 2017 Downloaded from http://pubs.acs.org on December 6, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Clustered-microcapsule-shaped Microporous Carbon Coated Sulfur Composite Synthesized via In-situ Oxidation Qian Wang, ‡ 1,2 Honghong Liu, ‡1 Rongrong Li,1 Minghui Yang, 1,* Zhen-Bo Wang, 2,* Limei Zhang,2 Chao Li, 2 Da-Ming Gu2 1

Ningbo Institute of Material Technology and Engineering, Chinese Academy of Sciences

No. 1219 Zhongguan West Road Zhenhai District, Ningbo, 315201 China 2

School of Chemistry and Chemical Engineering, Harbin Institute of Technology

No. 92 West-Da Zhi Street, Harbin, 150001 China KEYWORDS: clustered microcapsule structure, microporous carbon coated sulfur composite, high sulfur content, in-situ oxidation preparation, clustered ZnS precursor

ABSTRACT

Hollow materials as sulfur hosts, have been intensively investigated to address the poor cycling stabilities of Li-S batteries. Herein, we report an enhanced hollow framework to improve its applicability of the sulfur confinement. A clustered-microcapsule-shaped microporous carbon

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 24

encapsulating sulfur (CM-S@MPC) composite, is prepared from the clustered zinc sulfide (CZnS) precursor, through an in-situ oxidation process. The high specific surface area and the insitu preparation guarantee the uniform distribution of sulfur inside the carbon microcapsule, even under a higher sulfur content of 83 wt%. In addition, the interconnected frame constructed by the stacking of carbon microcapsules also mitigates the LPSs loss by setting interlayered hurdles on their pathway along the out-ward diffusion. Hence, these enable a fully demonstration of excellent cycling stability, compared to control sample obtained via physical sulfur infiltration. The outstanding decay rate of 0.039 % per cycle is achieved during 700 cycles at 1 C, even under high sulfur loading.

INTRODUCTION

As promising materials widely applied in the fields of catalysis,1-4 gas sensor,5-8 energy storage and conversion,9-15 hollow materials have also been researched as the hosts of sulfur in Li-S batteries for years, due to their special structures and functional characteristics.16-18 In the previous reports, Li-S battery is regarded as one of the prospective alternatives to the commercial Li-ion batteries, owing to its high theoretical energy density, cost-effective and environmental benignity.19-21 However, it is still plagued by three serious problems which are;22-24 (i) insulation of sulfur, (ii) volumetric change during cycling, and (iii) the dissolution of the intermediates. Hollow materials seem to be the right solution to the menaces. The inner void space can be employed to store the active sulfur and accommodate the large volumetric expansion (80 %) in the discharge process. And the considerable specific surface area provides full contact between the hollow host and the sulfur, enhancing the electron conductivity of sulfur and the discharge

ACS Paragon Plus Environment

2

Page 3 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

end-product Li2S. More notably, the shells are functionalized to block the dissolved intermediates of lithium polysulfides (LPSs) spreading out and shuttling to the anode, not only by space barrier, but also by chemical trap. The commonly researched hollow materials are; hollow carbon spheres,25-32 hollow carbon nanofibers/tubes,16,33-34 various hollow oxides,19,35-38 and their hybrids.39-43 The introduction of these hollow hosts overcomes the shortcomings of the sulfur cathode, which significantly improves the cycling stabilities of the Li-S batteries. It is hoped that sulfur is better to be loaded inside the hollow cavity rather than in the micro/meso-pores on the outer shell.27,28 Only in this way, the hollow cavity can be fully used as the buffer pool to accommodate volumetric expansion, and the micro/meso-pores on the outer shell can take their positive roles of lithium-ion transmission and LPSs blockage. Remorsefully, it has been shown that the hollow materials have insufficient internal surface areas, leading to failed deposition of sulfur and Li2S.29 Hence, the shortage needs to be supplemented by micro/meso-pores in the outer shell, which will enable free flow of dissolved LPSs. Furthermore, the loading position of sulfur is difficult to control by the existing method that involves filling sulfur by capillary adsorption in the gaseous or liquid state.27 This causes the distribution of the sulfur both inside and outside shell. In most cases, it also lead to the presence of sulfur at the micro and meso-pores of the outer-shell, which may results in the easy outflow of the LPSs. To solve these aforementioned issues, Loose and clustered ZnS (C-ZnS) was skillfully synthesized to be the self-sacrificial template and sulfur source, followed by microporous carbon coating to form clustered microporous carbon coated ZnS (C-ZnS@MPC) with core-shell structure. Then, the clustered-microcapsule shaped microporous carbon coated sulfur (CMS@MPC) composite was prepared via in-situ oxidation of the obtained C-ZnS@MPC. In the preparation process, the loose and clustered structure of C-ZnS, facilitated the carbon source to

ACS Paragon Plus Environment

3

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 24

access the interior of the C-ZnS and wrap each small ZnS particle homogeneously, forming the inter-connected carbon frame. Then, for the characteristic adsorption, iodine was easily distributed on the microporous carbon backbones, and served as the oxidizing agent to ensure insitu oxidation of the ZnS inside the carbon microcapsule. This approach guaranteed the generated sulfur to be precisely deposited on the inwall of the carbon microcapsule.44,45 Therefore, compared with the original hollow configuration, our improvement endowed the CMS@MPC composite with particular features: (i) Larger specific surface area provided possibility for accommodation of more sulfur and discharge end-product; (ii) The sulfur preparation of insitu oxidation enabled the sulfur to be deposited homogeneously inside every single carbon microcapsule, even under a higher sulfur content; (iii) The inter-connected carbon frame constructed by the clustered microcapsules, functioning as interlayered spatial barriers, effectively mitigated the out-ward diffusion of LPSs.

RESULTS AND DISCUSSION

ACS Paragon Plus Environment

4

Page 5 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 1. Schematic illustration of the synthesis of the CM-S@MPC composite. Figure 1 schematically illustrates the preparation process of CM-S@MPC. The loose and clustered ZnS (C-ZnS) precursor is synthesized through solvothermal reaction. In the preparation, the simultaneous additions of the two surfactants suppress the growth of the ZnS nanoparticles, and provide the primary particle with high surface energy that makes them aggregated to form a cluster shape, follow the principle of minimum energy. Resorcinol formaldehyde (RF) resin is employed as the carbon source precursor to coat the prepared C-ZnS. It is exactly the loose structure of the C-ZnS that enables the RF to access the interior and wrap every primary ZnS particle. RF resin is transformed to be the carbon layer, coating outside of every primary particle, after a calcination at 750 oC. The microporous carbon coated clustered

ACS Paragon Plus Environment

5

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 24

ZnS (C-ZnS@MPC) is obtained. And then, ZnS is oxidized inside every carbon microcapsule by the iodine that is enriched on the carbon shell.43 The generated sulfur is homogeneously orienteddeposited on the inwall of every carbon microcapsule, forming a single layer of sulfur. Hence, each microcapsule demonstrates double-hollow-sphere structure of sulfur and carbon. The whole structure looks like numerous microcapsules gathering together to form a cluster, so we name it clustered-microcapsule-shaped microporous carbon coated sulfur composite (CM-S@MPC).

Figure 2. TEM image of (a) overall, and (b) a single sphere of CM-S@MPC. (c) HRTEM image of CM-S@MPC. (d) Pore size distribution of CM-HCS, C-ZnS@MPC and CM-S@MPC. The STEM element mappings of (e) HAADF, (f) carbon, (g) sulfur, and (h) overlaying of the three. In order to verify whether the micro-morphologies of the prepared materials are consistent with the designs, SEM and TEM are performed. Figure S1a shows that the obtained C-ZnS is monodispersed, with a particle distribution of 162±30 nm. The cluster structure can be observed clearly to be formed by the accumulation of large amount of ZnS primary particles in the TEM image (Figure S2a). The HRTEM in Figure S2b reveals that interplanar d-spacings is 0.312 nm,

ACS Paragon Plus Environment

6

Page 7 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

corresponding to that of (0,0,60) lattice plane of the trigonal-type ZnS (JCPDS No. 01-0892192). This result matches up with the strongest peak located at 28.55

o

in the XRD pattern

(Figure S3). C-ZnS@MPC basically conserves the outline structure of C-ZnS, just slightly grows in size (Figure S1b and S2c). Every ZnS primary particle can be observed to be coated with a 2 nm thick carbon layer outside, in Figure S2d. The crystal type of ZnS is changed after the carbonization process (Figure S2d and S3). The CM-S@MPC composite, obtained via in-situ oxidation, maintains the original appearance and intact carbon configuration (Figure S1c and Figure 2a). Compared with C-ZnS@MPC precursor, the dimension of CM-S@MPC becomes smaller. The TEM image of CM-S@MPC demonstrates a spherical shape stacked by numerous hollow capsules (Figure 2b), which is in agreement with our material structure design. In comparison, without the use of the two surfactants, the ZnS ball gets bigger and closed packed, which enables the carbon source precursors only to coat outside (Figure S4a), rather than enter the interior. So, the different morphology of sulfur/carbon composite is achieved (Figure S4b). The HRTEM and STEM element mappings (Figure 2c and e-h) indicate that the distribution of sulfur is consistent with that of carbon, and the sulfur is homogeneously distributed without obvious aggregations, even under a sulfur content of higher than 80 wt% (Figure 3a). The HRTEM in Figure 2c shows that the average inner diameter of the microcapsule unit is approximate 12 nm. It is in highly agreement with the dominant pore size distribution at around 12 nm of CM-HCS (Figure 2d), which is obtained by removing the ZnS nano-particles in CZnS@MPC. Besides, the steep rises at P=Po in the isothermal curves (Figure S5) and the sharp peaks distributed in the micropore region (Figure 2d) of both CM-HCS and C-ZnS@MPC indicate the distribution of micropores on the carbon shells of microcapsules.42, 43 In the CMS@MPC composite, sulfur has occupied part of the micropores of the CM-HCS, as well as part

ACS Paragon Plus Environment

7

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 24

of mesopores, which can be observed from the pore size distribution (Figure 2d). According to the discussion aforementioned, the sulfur is verified to be distributed inside of the CM-S@MPC composite. The micropore volume (V﹤ 2

nm)

of 0.23 cm3 g-1 (Figure S6) can be calculated to

accommodate only 8.09 wt% of sulfur. Thereby, more than 74.91 wt% of sulfur could be deduced to be loaded on the inwall of carbon host, occupying the space of the hollow cavity. That is why the mesopore volume significantly decreases. In addition, the V﹤2 nm of 0.23 cm3 g-1 represents a relative small value, guaranteeing the suppression to the out-ward diffusion of LPSs. It can be calculated that the mesopore volume provided by the microcapsules is 1.4 times the volume that 83 wt% sulfur (Figure 3a) needed, based on the sulfur density of 2.07 g cm-3 and V2 ~22

nm

of 3.38 cm3 g-1. This suggests the volume inside the microcapsule is fairly enough for the

sulfur storage. In a similar way, the total pore volume of 4.36 cm3 g-1 can be calculated to be large enough to accommodate the corresponding Li2S, based on the Li2S density of 1.66 g cm-3.

ACS Paragon Plus Environment

8

Page 9 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 3. (a) TGA, (b) XRD patterns, (c) Raman, and (d) XPS of CM-S@MPC and S/CM-HCS. The visualization discharge experiments of (e) CM-S@MPC, and (f) S/CM-HCS. CM-HCS is employed as the host to be loaded with sulfur through melt-diffusion method, to obtain the S/CM-HCS composite (Figure S7). S/CM-HCS serves as the control sample, and is compared with CM-S@MPC using various techniques, to examine the structural characteristics of the CM-S@MPC composite and the advantages of in-situ oxidation approach. The TGA results in Figure 3a show that the weight loss temperature of S/CM-HCS is approximately 50 oC earlier than that of CM-S@MPC, under the similar sulfur content (about 82 wt.%), indicating

ACS Paragon Plus Environment

9

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 24

that the sulfur loaded in the same CM-HCS frame by the traditional physical method is easier to be lost than by the in-situ oxidation approach.33,46 The XRD pattern of S/CM-HCS displays obvious peaks mainly located at 23.12 o, 25.94

o

and 26.78 o, respectively, which matches up

with the characteristic peaks of S8 (JCPDS No.01-074-1465). The sulfur prepared directly from the oxidation of C-ZnS, also shows characteristic peaks of S8, suggesting that the sulfur synthesized via this approach is crystalline. While, no obvious sulfur characteristic peak appears in the XRD spectra of CM-S@MPC (Figure 3b), revealing that the sulfur introduced via in-situ oxidation method, is likely to attain uniform distribution, and does not exist outside the CM-HCS host.19,47 In the Raman spectra (Figure 3c), the characteristic peaks distributed at 472.0, 219.5, 155.6 and 85.5 cm-1 of S/CM-HCS indicate the presence of sulfur on the surface of CM-HCS host, further suggesting that it is difficult to load sulfur into the microporous carbon frame by the traditional melt-diffusion method.26 Comparatively, the much lower intensities of the sulfur characteristic peaks in the Raman spectra of CM-S@MPC also explain well confinement of sulfur in the CM-HCS host. Additionally, the lower ID/IG ratios of 0.85 and 0.90 show the relative higher graphitization extents, suggesting the superior electric conductivity of the carbon matrix. The surface of carbon frame may be oxidized partly by the iodic acid, resulting in the decreased graphitization degree of CM-S@MPC. That is why CM-S@MPC exhibits relative higher ID/IG ratio. This can be also verified by the higher oxygen atomic concentration of CMS@MPC in the XPS results, compared with S/CM-HCS (Figure 3d). The characteristic peaks of O 1s, C1s, S2s and S2p can be observed in the XPS pattern of Figure 3d. Therein, the inset table exhibits that the sulfur atomic concentration of CM-S@MPC is 7.86 %, much lower than that of S/CM-HCS, which exhibits less sulfur content on the surface of CM-S@MPC. This is consistence with the aforementioned test results. An off-line visualization experiment is

ACS Paragon Plus Environment

10

Page 11 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

performed under 0.5 current rate (based on the sulfur quantity on cathode). The cathode with CM-S@MPC as the active material demonstrates slight color change of the electrolyte during discharge (Figure 3e), explaining excellent LPSs confinement of the microporous walled carbon microcapsules. In contrast, the electrolyte color of S/CM-HCS becomes darker with time, which only indicates that the sulfur is not fully loaded inside the CM-HCS frames. From these results, it can be concluded that: in the CM-S@MPC, sulfur is well confined in the carbon microcapsule; and during the discharge process, CM-S@MPC also demonstrates superior space restriction to the dissolved LPSs. By comparison, it is difficult to infiltrate sulfur into the microporous CMHCS host. Therefore, in the case of outside-in sulfur loading approach, the sulfur confinement effect of microporous carbon shell and the accommodation function of the hollow space in the CM-HCS frame cannot be well realized.

ACS Paragon Plus Environment

11

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 24

Figure 4. (a) Rate performance of CM-S@MPC and S/CM-HCS, (b) charge/discharge voltage profiles of CM-S@MPC in rate test. (c) Cycling performances at current rate of 0.2 C, and (d) 0.5 C of the two sulfur/carbon composites. (e) Long-term cycling capacity and coulombic efficiency of CM-S@MPC at 1 C. The electrochemical performance of CM-S@MPC is evaluated to verify the sulfur confinement effect of the particular frame on the practical perspective. This is done based on a coin cell configuration with S/CM-HCS as the control sample. Figure 4a displays the discharge specific

ACS Paragon Plus Environment

12

Page 13 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

capacities and coulombic efficiencies under different current rates. The average capacities of CM-S@MPC reaches 1148, 940, 880, 831 and 758 mAh g-1 at 0.2, 0.4, 0.6, 0.8 and 1 C, respectively, even under the sulfur loading of 3.5 mg cm-2. Moreover, the capacity of 955 mAh g1

is recovered when the current density switches back to 0.4 C, a little higher than that of before,

suggesting excellent reversible rate cycling performance. In the S/CM-HCS composite, part of sulfur is inevitably loaded on the outside of the carbon frame, where the mass transmission is better than inside. That is why it delievers the higher discharge capacities at the 0.2 C and 0.4 C. However, this part of sulfur is easy to loss, thereby, S/CM-HCS exihibits faster decreased specific capacities in the following rate cycles. The charge/discharge profile of CM-S@MPC is provided in Figure 4b. On the discharge curve of 0.2 C (Figure 4b), there is a small discharge voltage plateau at the low potential, which is the unique discharge manifestation of the microporous materials.26,30,48 The sulfur generated by in-situ oxidation is tightly anchored on the inwall of the carbon microcapsule with uniform distribution, enabling the fast electron transfer. This is also reflected by the relative smaller charge transfer resistence (Rct) and ohmic impedance in EIS results (Figure S8). That is why the superior rate capability of CM-S@MPC is achieved. On account of the rate results, the galvanostatic cycling tests are performed at 0.1 C for activation,48-50 followed by 0.2 C and 0.5 C, respectively. The results are displayed in Figure 4c and d. The initial capacity of 882 mAh g-1 and retained capacity of 830 mAh g-1 are obtained by CM-S@MPC after 100 cycles at 0.2 C, corresponding to the capacity retention of 94 %. The control sample only delivers a capacity retention of 70 %, which is much lower than that of CMS@MPC. During the 0.5 C cycling (Figure 4d), the CM-S@MPC expresses an initial capacity of 859 mAh g-1 and the capacity retention of 72 % after 200 cycles. While, only 285 mAh g-1 is maintained by S/CM-HCS after 200 cycles. Then, the long-term cycling of CM-S@MPC is

ACS Paragon Plus Environment

13

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 24

carried out under 1 C-rate and sulfur loading of 3.03 mg cm-2. It delievers an intial peak capacity of 657 mAh g-1 and a capacity retention of 73 % after 300 cycles. The capacity is remained almost unchanged between 300 to 700 cycles. The caculated degradation ratio during the whole 700 cycles is 0.039 % per cycle. It is noted that such a long-term stability is a very attractive result for the cathode materials with similar frameworks (Table S1). The outstanding cycling stability is attributed to the special clustered-microcapsule structure that is stacked by a number of nano-scale double-hollow-spheres of carbon and sulfur. Every single microcapsule, as a miniature of hollow structure, possesses a hollow space for accommodating the volumetric expansion, and a microporous shell to serve as the LPSs hindrance. These are considered as the most prominent merits of hollow construction. Furthermore, it demonstrates several new advantages. Firstly, the relative thinner carbon walls facilitate fast transmission of lithium ions. Secondly, the larger specific surface area provides the higher content of sulfur with enough redeposition active sites. Thirdly, the big sphere after stacking not only improves the bulk density for easier process, but also sets multiple space hurdles on the diffusion path of LPSs, which significantly mitigates the loss of the active sulfur. Additionally, the intact microstructure is another cause to bring it high stabilities, which is confirmed by the STEM element mappings of CM-S@MPC after cycling (Figure S9). All of the abovementioned merits are beneficial to enhance the cycling stability at high sulfur areal loading.

CONCLUSION

In this work, a clustered-microcapsule-shaped microporous carbon coated sulfur (CM-S@MPC) composite with high sulfur content is synthesized through the in-situ oxidation of a loose clustered ZnS precursor. It is proved that the sulfur prepared by this approach is homogeneously

ACS Paragon Plus Environment

14

Page 15 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

deposited on the inwall of every single microcapsule, even under the sulfur content of 83 wt%, which is mainly attributed to: (i) The high specific surface area of 1668 m2 g-1, and pore volume of 4.36 cm3 g-1 of the CM-HCS host provide enough space for the deposition of sulfur and Li2S; (ii) The in-situ approach for loading sulfur enables accurate and reliable control of initial sulfur deposition. Furthermore, in the visualization experiment, CM-S@MPC demonstrates a more effective suppression to the out-ward diffusion of LPSs, compared with the control sample obtained by physical sulfur infiltration. Therefore, it achieves satisfactory electrochemical performance, with a remarkable low decay rate of 0.039 % per cycle during 700 cycles at 1Crate, under sulfur loading of 3.03 mg cm-2. In short sentence, this work provides an innovative preparation method and research strategy for the application of hollow materials in Li-S secondary batteries.

ASSOCIATED CONTENT Supporting Information. The Supporting Information is available free of charge on the Internet at http://pubs.acs.org. Material preparation, characterization and electrochemical measurements, SEM, TEM and HRTEM images of the prepared materials, XRD patterns, N2 adsorption/desorption isothermals, pore volume analyses, EIS pattern, and the performance comparison table of hollow structure cathode materials

AUTHOR INFORMATION Corresponding Author

ACS Paragon Plus Environment

15

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 24

*Email: [email protected] (M. Yang) *Email: [email protected] (Z.B. Wang) Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. ‡These authors contributed equally. Notes The authors declare no competing financial interest. ACKNOWLEDGMENT This work is supported by NSF China through grant 21471147,2014020087 Liaoning, and National Key Research and Development Program of China through grant 2016YFB0101200, 2016YFB0101205. M. Yang would like to thank for the National "Thousand Youth Talents" program of China and Ningbo 3315 program. This research is also financially supported by the National Natural Science Foundation of China (Grant No. 21273058 and 21673064), Harbin technological achievements transformation projects (2016DB4AG023) and HIT Environment and Ecology Innovation Special Funds (Grant No.HSCJ201620). REFERENCES (1) Zhang, Z.; Chen, Y.; He, S.; Zhang, J.; Xu, X.; Yang, Y.; Nosheen, F.; Saleem, F.; He, W.; Wang,

X.

Hierarchical

Zn/Ni-MOF

Nanosheet-Assembled

Hollow

Nanocubes

for

Multicomponent Catalytic Reactions. Angew. Chem., Int. Ed. 2014, 53, 12517-12521. (2) Zhang, Z.; Chen, Y.; Xu, X.; Zhang, J.; Xiang, G.; He, W.; Wang, X. Well-Defined MetalOrganic Framework Hollow Nanocages. Angew. Chem., Int. Ed. 2014, 53, 429-433.

ACS Paragon Plus Environment

16

Page 17 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(3) Dou, Y.; Zhang, S.; Pan, T.; Xu, S.; Zhou, A.; Pu, M.; Yan, H.; Han, J.; Wei, M.; Evans, D. G.; Duan, X. TiO2@Layered Double Hydroxide Core-Shell Nanospheres with Largely Enhanced Photocatalytic Activity Toward O2Generation. Adv. Funct. Mater. 2015, 25, 2243-2249. (4) Mezzavilla, S.; Baldizzone, C.; Mayrhofer, K. J.; Schuth, F. General Method for the Synthesis of Hollow Mesoporous Carbon Spheres with Tunable Textural Properties. ACS appl. mater. interfaces 2015, 7, 12914-12922. (5) Wang, W. W.; Zhu, Y. J.; Yang, L. X. ZnO–SnO2 Hollow Spheres and Hierarchical Nanosheets: Hydrothermal Preparation, Formation Mechanism, and Photocatalytic Properties. Adv. Funct. Mater. 2007, 17, 59-64. (6) Pan, J. H.; Wang, X. Z.; Huang, Q.; Shen, C.; Koh, Z. Y.; Wang, Q.; Engel, A.; Bahnemann, D. W. Large-scale Synthesis of Urchin-like Mesoporous TiO2 Hollow Spheres by Targeted Etching and Their Photoelectrochemical Properties. Adv. Funct. Mater. 2014, 24, 95-104. (7) Holken, I.; Neubuser, G.; Postica, V.; Bumke, L.; Lupan, O.; Baum, M.; Mishra, Y. K.; Kienle, L.; Adelung, R. Sacrificial Template Synthesis and Properties of 3D Hollow-Silicon Nano Microstructures. ACS appl. mater. interfaces 2016, 8, 20491-20498. (8) Yao, M. S.; Tang, W. X.; Wang, G. E.; Nath, B.; Xu, G. MOF Thin Film-Coated Metal Oxide Nanowire Array: Significantly Improved Chemiresistor Sensor Performance. Adv. Mater. 2016, 28, 5229-5234. (9) Qi, J.; Lai, X. Y.; Wang, J. Y.; Tang, H. J.; Ren, H.; Yang, Y.; Jin, Q.; Zhang, L. J.; Yu, R. B.; Ma, G. H.; Su, Z. G.; Zhao, H. J.; Wang, D. Multi-Shelled Hollow Micro-/Nanostructures. Chem. Soc. Rev. 2015, 44, 6749-6773.

ACS Paragon Plus Environment

17

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 24

(10) Zhao, Y.; Jiang, L. Hollow Micro/Nanomaterials with Multilevel Interior Structures. Adv. Mater. 2009, 21, 3621-3638. (11) Wu, H. B.; Chen, J. S.; Hng, H. H.; Lou, X. W. Nanostructured Metal Oxide-Based Materials as Advanced Anodes for Lithium-Ion Batteries. Nanoscale 2012, 4, 2526-2542. (12) Zhou, L.; Zhao, D.; Lou, X. LiNi0.5Mn1.5O4 Hollow Structures as High-Performance Cathodes for Lithium-Ion Batteries. Angew. Chem., Int. Ed. 2012, 51, 239-241. (13) Wu, X. W.; Xie, H.; Deng, Q.; Wang, H. X.; Sheng, H.; Yin, Y. X.; Zhou, W. X.; Li, R. L.; Guo, Y. G. Three-Dimensional Carbon Nanotubes Forest/Carbon Cloth as an Efficient Electrode for Lithium−Polysulfide Batteries. ACS appl. mater. interfaces 2017, 9, 1553-1561.

(14) Yu, X. Y.; Hu, H.; Wang, Y.; Chen, H.; Lou, X. W. Ultrathin MoS2 Nanosheets Supported on N-doped Carbon Nanoboxes with Enhanced Lithium Storage and Electrocatalytic Properties. Angew. Chem., Int. Ed. 2015, 54, 7395-7398. (15) Liu, Y.; Lan, K.; Bagabas, A. A.; Zhang, P.; Gao, W.; Wang, J.; Sun, Z.; Fan, J.; Elzatahry, A. A.; Zhao, D. Ordered Macro/Mesoporous TiO2 Hollow Microspheres with Highly Crystalline Thin Shells for High-Efficiency Photoconversion. Small 2016, 12, 860-867. (16) Zheng, G.; Yang, Y.; Cha, J. J.; Hong, S. S.; Cui, Y. Hollow Carbon NanofiberEncapsulated Sulfur Cathodes for High Specific Capacity Rechargeable Lithium Batteries. Nano lett. 2011, 11, 4462-4467.

ACS Paragon Plus Environment

18

Page 19 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(17) Zhang, K.; Zhao, Q.; Tao, Z.; Chen, J. Composite of Sulfur Impregnated in Porous Hollow Carbon Spheres as The Cathode of Li-S Batteries with High Performance. Nano Res. 2012, 6, 38-46. (18) Zhang, J.; Yang, C. P.; Yin, Y. X.; Wan, L. J.; Guo, Y. G. Sulfur Encapsulated in Graphitic Carbon Nanocages for High-Rate and Long-Cycle Lithium–Sulfur Batteries. Adv. Mater. 2016, 28, 9539-9544. (19) Zhang, Z.; Li, Q.; Jiang, S.; Zhang, K.; Lai, Y.; Li, J. Sulfur Encapsulated in a TiO2 Anchored Hollow Carbon Nanofiber Hybrid Nanostructure for Lithium-Sulfur Batteries. Chem. Eur. J. 2015, 21, 1343-1349. (20) Chen, C. Y.; Peng, H. J.; Hou, T. Z.; Zhai, P. Y.; Li, B. Q.; Tang, C.; Zhu, W.; Huang, J. Q.; Zhang, Q. A Quinonoid-Imine-Enriched Nanostructured Polymer Mediator for Lithium-Sulfur Batteries. Adv. Mater. 2017, 29, 1606802-1609808. (21) Yin, Y. X.; Xin, Se.; Guo, Y. G.; Wan, L. J. Lithium–Sulfur Batteries: Electrochemistry, Materials, and Prospects. Angew. Chem., Int. Ed. 2013, 52, 13186-13200. (22) Ahn, Wook.; Seo, M. H.; Jun, Y.S.; Lee, D. U.; Hassan, M. F.; Wang, X. L.; Yu, A. P.; Chen, Z. W. Sulfur Nanogranular Film-Coated Three-Dimensional Graphene Sponge-Based High Power Lithium Sulfur Battery. ACS Appl. Mater. Interfaces 2016, 8, 1984-1991. (23) Xin, S.; Gu, Li.; Zhao, N. H.; Yin, Y. X.; Zhou, L. J.; Guo, Y. G.; Wan, L. J. Smaller Sulfur Molecules Promise Better Lithium−Sulfur Batteries. J. Am. Chem. Soc. 2012, 134, 18510−18513.

ACS Paragon Plus Environment

19

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 24

(24) Wang, X. L.; Li, G.; Li, J. D.; Zhang, Y. N.; Wook, A.; Yua, A. P.; Chen, Z. W. Structural and Chemical Synergistic Encapsulation of Polysulfides Enables Ultralong-Life Lithium–Sulfur Batteries. Energy Environ. Sci. 2016, 9, 2533-2538. (25) Zhang, C.; Wu, H. B.; Yuan, C.; Guo, Z.; Lou, X. W. Confining Sulfur in Double-Shelled Hollow Carbon Spheres for Lithium-Sulfur Batteries. Angew. Chem., Int. Ed. 2012, 51, 95929595. (26) Lyu, Z.; Xu, D.; Yang , L.; Che, R.; Feng, R.; Zhao, J.; Li, Y.; Wu, Q.; Wang, X.; Hu, Z. Hierarchical Carbon Nano Confining High-Loading Sulfur for High-Rate Lithium–Sulfur Batteries. Nano Energ. 2015, 12, 657-665. (27) He, G.; Evers, S.; Liang, X.; Cuisinier, M.; Garsuch, A.; Nazar, L. F. Tailoring Porosity in Carbon Nanospheres for Lithium–Sulfur Battery Cathodes. ACS Nano 2013, 7, 10920-10930. (28) Yang, Z.-C.; Zhang, Y.; Kong, J.-H.; Wong, S. Y.; Li, X.; Wang, J. Hollow Carbon Nanoparticles of Tunable Size and Wall Thickness by Hydrothermal Treatment of αCyclodextrin Templated by F127 Block Copolymers. Chem. Mater. 2013, 25, 704-710. (29) Zhou, W. D.; Wang, C. M.; Zhang, Q. L.; Abruña, H. D.; He, Y.; Wang, J. W.; Mao, S. X.; Xiao, X. C. Tailoring Pore Size of Nitrogen-Doped Hollow Carbon Nanospheres for Confining Sulfur in Lithium-Sulfur Batteries. Adv. Energ. Mater. 2015, 5, 1401752-141759. (30) Zheng, J.; Guo, G.; Li, H.; Wang, L.; Wang, B.; Yu, H.; Yan, Y.; Yang, D.; Dong, A. Elaborately Designed Micro−Mesoporous Graphitic Carbon Spheres as Efficient Polysulfide Reservoir for Lithium−Sulfur Batteries. ACS Energ. Lett. 2017, 2, 1105-1114.

ACS Paragon Plus Environment

20

Page 21 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(31) Li, Z.; Wu, H. B.; Lou, X. W. Rational Designs and Engineering of Hollow Micro anostructures as Sulfur Hosts for Advanced Lithium-Sulfur Batteries. Energ. Environ. Sci. 2016, 9, 3061-3070. (32) Li, Z.;Jiang, Y.;Yuan, X. L.;Yi, Z. Q.; Wu, C.; Liu, Y.; Strasser, P.; Huang, Y. H. A Highly Ordered Meso@Microporous Carbon-Supported Sulfur@Smaller Sulfur Core–Shell Structured Cathode for Li–S Batteries. ACS Nano 2014, 8, 9295-9303. (33)Zhao, Y.; Wu, W.; Li, J.; Xu, Z.; Guan, L. Encapsulating MWNTs into Hollow Porous Carbon Nanotubes: A Tube-In-Tube Carbon Nanostructure for High-Performance LithiumSulfur Batteries. Adv. Mater. 2014, 26, 5113-5118. (34) Mao, Y.Y.; Li, G. R.; Guo, Y.; Li, Z. P.; Liang, C. D.; Peng, X. S.; Lin, Z. Foldable Interpenetrated Metal-Organic Frameworks/Carbon Nanotubes thin Film for Lithium–Sulfur Batteries. Nat. Comm. 2017, 8, 14628. (35) Guo, J. L.; Zhang, X. L.; Du, X. Y.; Zhang, F. X. A Mn3O4 Nano-Wall Array Based BinderFree Cathode for High Performance Lithium–Sulfur Batteries. J. Mater. Chem. A 2017, 5, 6447– 6454. (36) Cao, B.; Li; Hou, B.; Mo, Y.; Yin, L.; Chen, Y. Synthesis of Double-Shell SnO2@C Hollow Nanospheres as Sulfur/Sulfide Cages for Lithium-Sulfur Batteries. ACS Appl. Mater. Interfaces 2016, 8, 27795−27802. (37) Liang, X.; Nazar, L. F. In Situ Reactive Assembly of Scalable Core-Shell Sulfur-MnO2 Composite Cathodes. ACS nano 2016, 10, 4192-4198.

ACS Paragon Plus Environment

21

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 24

(38) Chen, T.; Ma, L.; Cheng, B.; Chen, R.; Hu, Y.; Zhu, G.; Wang, Y.; Liang, J.; Tie, Z.; Liu, J.; Jin, Z. Metallic and Polar Co9S8 Inlaid Carbon Hollow Nanopolyhedra as Efficient Polysulfide Mediator for Lithium−Sulfur Batteries. Nano Energ. 2017, 38, 239-248. (39) Li, Z.; Zhang, J.; Guan, B.; Wang, D.; Liu, L. M.; Lou, X. W. A Sulfur Host Based on Titanium Monoxide@Carbon Hollow Spheres for Advanced Lithium-Sulfurbatteries. Nat. commun. 2016, 7, 13065. (40) Strubel, P.; Thieme, S.; Biemelt, T.; Helmer, A.; Oschatz, M.; Brückner, J.; Althues, H.; Kaskel, S. ZnO Hard Templating for Synthesis of Hierarchical Porous Carbons with Tailored Porosity and High Performance in Lithium-Sulfur Battery. Adv. Funct. Mater. 2015, 25, 287297. (41) Lee, J. T.; Zhao, Y.; Thieme, S.; Kim, H.; Oschatz, M.; Borchardt, L.; Magasinski, A.; Cho, W. I.; Kaskel, S.; Yushin, G. Sulfur-Infiltrated Micro- and Mesoporous Silicon Carbide-Derived Carbon Cathode for High-Performance Lithium Sulfur Batteries. Adv. Mater. 2013, 25, 45734579. (42) Zhang, J.; Hu, H.; Li, Z.; Lou, X. W. Double-Shelled Nanocages with Cobalt Hydroxide Inner Shell and Layered Double Hydroxides Outer Shell as High-Efficiency Polysulfide Mediator for Lithium-Sulfur Batteries. Angew. Chem., Int. Ed. 2016, 55, 3982-3986. (43) Wang, X.; Gao, T.; Fan, X.; Han, F.; Wu, Y.; Zhang, Z.; Li, J.; Wang, C. Tailoring Surface Acidity of Metal Oxide for Better Polysulfide Entrapment in Li-S Batteries. Adv. Funct. Mater. 2016, 26, 7164-7169.

ACS Paragon Plus Environment

22

Page 23 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

(44) Wang, Q.; Wang, Z. B.; Li, C.; Gu, D. M. High Sulfur Content Microporous Carbon Coated Sulfur Composites Synthesized via In Situ Oxidation of Metal Sulfide for High-Performance Li/S Batteries. J. Mater. Chem. A 2017, 5, 6052-6059. (45) Wang, Q.; Wang, Z. B.; Li, C.; Gu, D. M. A Novel Synthetic Route to Cathode Materials for Li–S Batteries: from Organic Sulfides to Sulfur/Nitrogenous Carbon Composites. J. Mater. Chem. A 2017, 5, 16796–16802. (46) Wang, D. L.; Yu, Y. C.; Zhou, W. D.; Chen, H.; DiSalvo, F. J.; Muller, D. A.; Abruna, H. D.

Infiltrating

Sulfur

in

Hierarchical

Architecture

MWCNT@Meso

C

Core-Shell

Nanocomposites for Lithium-Sulfur Batteries. Phys. Chem. Chem. Phys. 2013, 15, 9051-9057. (47) Du, W. C.; Yin, Y. X.; Zeng, X. Xi.; Shi, J. L.; Zhang, S. F.; Wan, L. J.; Guo, Y. G. Wet Chemistry Synthesis of Multidimensional Nanocarbon−Sulfur Hybrid Materials with Ultrahigh Sulfur Loading for Lithium−Sulfur Batteries. ACS Appl. Mater. Interfaces 2016, 8, 3584−3590.

(48) Li, M.; Zhang, Y. N.; Wang, X. L.; Ahn, W.; Jiang, G. P.; Feng, K.; Lui, G.; Chen, Z. W. Gas Pickering Emulsion Templated Hollow Carbon for High Rate Performance Lithium Sulfur Batteries. Adv. Funct. Mater. 2016, 26, 8408–8417. (49) Pei, F.; An, T. H.; Zang, J.; Zhao, X. J.; Fang, X. L.; Zheng, M. S.; Dong, Q. F.; Zheng, N. F. From Hollow Carbon Spheres to N-Doped Hollow Porous Carbon Bowls: Rational Design of Hollow Carbon Host for Li-S Batteries. Adv. Energ. Mater. 2016, 6, 1502539.

ACS Paragon Plus Environment

23

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 24

(50) Chen, C. Y.; Peng, H. J.; Hou, T. Z.; Zhai, P. Y.; B. Li, Q.; Tang, C.; Zhu, W. C.; Huang, J. Q.; Zhang, Q. A Quinonoid-Imine-Enriched Nanostructured Polymer Mediator for Lithium– Sulfur Batteries. Adv. Mater. 2017, 29, 1606802. (51) Liang, X.; F Nazar, L. In Situ Reactive Assembly of Scalable Core−Shell Sulfur−MnO2 Composite Cathodes. ACS Nano 2016, 10, 4192-4198.