Co Oxide Nanoparticle Embedded 3D

3 days ago - The nanocomposites were fully characterized and showed excellent ... very high power densities of 11358 W kg–1 to 748.6 W kg–1 were a...
0 downloads 0 Views 2MB Size
Subscriber access provided by BUFFALO STATE

Article

A Facile Green Route to Ni/Co Oxide Nanoparticle Embedded 3D Graphitic Carbon Nanosheets for High Performance Hybrid Supercapacitor Device Cuili Xiang, Yin Liu, Ying Yin, Pengru Huang, Yongjin Zou, Marcus Fehse, Zhe She, Fen Xu, Dipanjan Banerjee, Daniel Hermida-Merino, Alessandro Longo, Heinz-Bernhard Kraatz, Dermot F. Brougham, Bing WU, and Lixian Sun ACS Appl. Energy Mater., Just Accepted Manuscript • DOI: 10.1021/acsaem.9b00202 • Publication Date (Web): 15 Apr 2019 Downloaded from http://pubs.acs.org on April 16, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

A Facile Green Route to Ni/Co Oxide Nanoparticle Embedded 3D Graphitic Carbon Nanosheets for High Performance Hybrid Supercapacitor Device Cuili Xiang,† Yin Liu,† Ying Yin,† Pengru Huang,† Yongjin Zou,*,†,‡ Marcus Fehse,,§, Zhe She‡, Fen Xu†, Dipanjan Banerjee,║, Daniel Hermida Merino, Alessandro Longo, Heinz-Bernhard Kraatz‡, Dermot F. Brougham∏, Bing Wu*,‡,, Lixian Sun†

†Guangxi

Key Laboratory of Information Materials, Guilin University of Electronic Technology,

Guilin 541004, P.R. China ‡Department

of Physical and Environmental Science, University of Toronto, 1265 Military Trail,

Toronto, M1C 1A4, Canada, Dutch-Belgian

Beamline (DUBBLE), ESRF- The European Synchrotron Radiation Facility, CS

40220, 38043 Grenoble Cedex 9, France §Faculty

of Applied Sciences, Delft University of Technology, Mekelweg 5, 2628 CD Delft, the

Netherlands ║Department ∏School

of Chemistry, KU Leuven, Celestijnenlaan 200F box 2404, 3001 Leuven, Belgium

of Chemistry, University College Dublin, Belfield, Dublin 4, D04 V1W8, Ireland

1 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT: The demand for energy storage systems with superior performance has led to the creation of hybrid supercapacitor device. With proper designs, the hybrid supercapacitive materials can achieve high performance while reducing the overall cost. Herein, a novel method is developed for preparing three-dimensional hierarchical graphitic carbon nanocomposites with highly dispersed mixed Co-Ni oxide nanoparticles (Co–Ni–O/3DG) by a facile one-pot process involving carbonization and subsequent oxidation of metal ion doped biopolymer precursors. The mixed metal nanoparticles produced during carbonization enabled a top-down preparation of 3D graphitic carbon nanosheets. The nanocomposites were fully characterized and showed excellent electrochemical performance supported by the DFT calculation. Specific capacitance of 1586 F∙g–1 was achieved (current density 1.0 A∙g–1), with capacitance retention of 94.5% after 10,000 cycles demonstrating exceptional cycling stability. In an asymmetric full-cell system using a Co–Ni– O/3DG positive electrode, high energy densities of 32.8 to 54.7 Wh kg–1 associated with very high power densities of 11358 W kg–1 to 748.6 W kg–1 were obtained, comparable to the most advanced contemporary supercapacitive materials while also possesses an improved cyclability as well as using bio-sourced staring materials, underlining its potential application in hybrid supercapacitor devices. KEYWORDS: graphitic carbon nanosheets; hybrid supercapacitor; cobalt oxide; nickel oxide; pseudocapacitance

2 ACS Paragon Plus Environment

Page 2 of 33

Page 3 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

INTRODUCTION Rising global demands for new energy storage solutions has led to a wave of innovations in the materials and design of electrochemical energy storage devices. Hybrid supercapacitors (HSCs), consisting of carbon and pseudocapacitive materials, have attracted significant attention.16

These hybrid devices possess battery-level energy density together with a long cycle life and

short charging time as supercapacitors. Impressive progress has been achieved in the fundamental research of these hybrid devices in recent years.7-16 A milestone was the implementation/discovery of pseudocapacitive storage into carbon-based HSC systems which may provide a route to greatly enhanced electrochemical storage performance.17-20 Carbon-based materials doped with conducting polymers, transition metals, or heteroatoms which have multiple accessible oxidation states, have all demonstrated promising pseudocapacitance with an increase in capacitance on doping of typically of an order of magnitude, as compared to the undoped analogues.21,

22

However, poor conductivity and volume changes

during charge–discharge cycles limit their applications. A fully controlled synthesis of nanocomposite utilizing both electric double-layer capacitors (EDLC) and pseudocapacitor components would provide a new generation of hybrid supercapacitors holding the prospect of enhanced electrochemical performance. However, doping porous carbonaceous materials with pseudocapacitive components in a controlled manner remains a significant challenge.23, 24 Graphene is a layered graphitic material with extraordinary properties due to the high electronic charge mobility tailored by n- or p-type doping. The high electrochemical performance of this layered graphitic material strongly relies on the structural properties of the material. These materials can have a large number of applications including energy storage materials given that the irreversible aggregation of graphene nanosheets can be inhibited.25 In this regard, the formation

3 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

of three-dimensional (3D) graphitic networks is aspired as it can prevent the stacking between neighboring layers, thereby ensuring a large electrode-electrolyte interface that effectively reduce the charge-transfer resistance.26 Multiple synthetic routes to 3D graphitic carbon based electrodes for energy storage materials have been reported in the literature.27-29 Through procedures like templated chemical vapor deposition or controlled self-assembly, 3D graphitic carbon with hierarchical porous structures have been prepared in the form of sponges,30-32 aerogels,33, 34 frameworks35, 36 and hydrogels37-39. In other studies, spacers such as carbon nanotubes,40-42 metal oxides,27 and conducting polymers28, 29

were introduced to increase the inter-planar spacing and render both sides of the graphene

nanosheets accessible for charge storage. However, most of these synthesis routes are rather complex and expensive, often encompassing the preparation of graphene sheets followed by multiple modifications and processing steps. Furthermore, a common weakness in these materials is that the self-assembled materials are mostly derived from chemically exfoliated graphene, which has a partly restored graphitic structure and a relatively large O/C atomic ratio, resulting in poor conductivity and limited structural stability.25 One strategy to overcome these drawbacks is to produce conductive graphene materials from molecular carbon precursors by transition-metalbased catalytic routes such as the use of Ni substrates by templated chemical vapor deposition method.43 Compared to chemical exfoliation of graphite, the catalytic routes have distinct advantages such as increasing the electrochemical stability and conductivity of the final product, as chemically derived graphene sheets and inter-sheets have minimal contact resistance.43 However, removing the catalytic substrate from the 3D graphitic carbon is time-consuming and usually leads to loss of the 3D structure. Herein, a simple, scalable approach was reported to prepare metal-oxide nanoparticle-

4 ACS Paragon Plus Environment

Page 4 of 33

Page 5 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

embedded carbon nanosheets HSC materials. A 3D carbon nanosheets doped with highly dispersed Co-Ni nanoparticles was synthesized from environmental benign biopolymers persimmon tannin (PT) (Figure S1a) and chitosan (Figure S1b).44 Characterization of this composite material demonstrates that during the carbonization process, the doped chelating complex decomposed into a metal nanoparticle embedded carbon form, while these newly-formed nanoparticles simultaneously catalyzed the formation of 3D graphitic carbon with significant reduction in restacking. Subsequent treatment with H2O2 oxidized the metal nanoparticles imparting a very high pseudocapacitance to the nanocomposite arising from the highly dispersed metal oxide NPs (M– O). Furthermore, due to the beneficial combined effects of the porous carbon nanosheets structure45 and pseudocapacitive properties of mixed metal-oxide system46, the as-prepared CoNi-O/3DG has shown remarkable energy and power density, while retaining excellent cycling stability and rate performance.

MATERIALS AND METHODS Materials preparation. Persimmon tannin (extracts of astringent persimmon) was purchased from Huikun Company of Agricultural Products (China); cobalt (II) nitrate hexahydrate and chitosan extracted from crab shells (85% deacetylation, 200,000 Da) were obtained from commercial source and used as received. Reduced graphene oxide (rGO) was synthesized using Hummers’ method.47 Since persimmon tannin (PT) is water-soluble, it was cured before use. To cure the PT, 10 g of material was initially dissolved in 100 mL of water. Afterwards, the mixture was added with chitosan (5 g), and heated to 60 ºC under stirring for 1 h. The solution was later added with 25 mL of glutaraldehyde. This mixed solution was further reacted for 6 h under stirring

5 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

at 60 °C. Finally, the hydrogel was dried and milled into fine powder for use in the study; the mixed polymer powder is hereafter denoted as PTC. To prepare the precursor for carbonization, Co(NO3)2 (2 mmol), of Ni(NO3)2 (2 mmol), and PTC (1 g) were added to 100 mL of water. After 6 h of stirring to reach adsorption equilibrium, the suspension was filtered and dried at 80 ºC. The dried powder was then calcined at 800 ºC under a nitrogen atmosphere and for 6 h. The as-synthesized sample was further treated with a 30 wt% H2O2 solution for 12 h; hereafter it is denoted as Co–Ni–O/3DG. For comparison, we prepared two separate batches of the PTC biopolymer; Co ions alone were adsorbed on one batch of PTC, while only Ni ions (at the same metal concentration as for the mixed metal material) were adsorbed on the other. The carbonized samples of these two biopolymer complexes are denoted as CoO/3DG and NiO/3DG. Bare PTC was also carbonized under identical conditions, but was not treated with H2O2, this sample is hereafter denoted as PTC–C. Characterization of prepared carbon. The instrumental information can be found in our previous work5 including Fourier-transform infrared (FTIR) spectrometer, Thermogravimetric (TG) analysis, Brunauer−Emmett−Teller (BET) measurements, Powder X-ray diffraction (XRD), Field-emission scanning electron microscopy (SEM), transmission electron microscopy (TEM), select-area electron diffraction (SAED) and Raman spectra. The average conductivity of the samples was measured through the four-probe method with a Keithley 2602 digital electrometer. Before testing, the powder was pressed into pellet with a diameter of 0.5 cm. Each sample was measured for five times from different position. The X-ray absorption near-edge structure (XANES) analyses and the Extended X-ray Absorption Fine Structure (EXAFS) spectra of Co and Ni K edges (7709 eV and 8333 eV respectively) were collected for each sample at the Dutch-Belgian Beamline (DUBBLE, BM26A)

6 ACS Paragon Plus Environment

Page 6 of 33

Page 7 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

48

at the European Synchrotron Radiation Facility (ESRF). The detailed information can be found

in our previous work.49, 50 Electrochemical measurements. For the electrochemical tests, a three-electrode system was set up and connected to a potentiostat (IM6e, Zahner-Elektrik, Germany). Platinum foil was used as the counter and Ag/AgCl electrode was used as reference electrode. The working electrodes were prepared according our previous paper17 except replacing the active materials with the material prepared in this work. The active electrode was prepared as a uniform film with a typical areal mass of approximately 4 mg/cm2. All the electrochemical tests were carried out in a 6 M KOH electrolyte solution at room temperature (25 ± 1 ºC). An asymmetric two-electrode hybrid cell system was assembled by using Co–Ni–O/3DG as the positive electrode. RGO was employed as the negative electrode; hereafter, this cell is denoted as (Co–Ni–O/3DG)//rGO. The energy density (E) and power density (P) were calculated according to Eqs. (1) and (2), respectively: 1 𝐸 = ( 𝐶s∆𝑉2)/3.6 2

𝑃=

3600 × 𝐸 ∆𝑡

(1)

(2)

where 𝐸 is in units of Wh kg−1 and 𝑃 is in units of W kg−1, 𝐶𝑠 (F g−1) is the specific capacitance, ∆𝑉 is the potential window, and ∆𝑡 (s) is the discharging time. DFT calculations. Spin-polarized Density functional theory (DFT) calculations were performed using the Vienna ab initio simulation package (VASP) code with the projector augmented wave (PAW) pseudopotentials.51, 52 The configurations of the valence electrons of Co, Ni, H and O were (3d84s1), (3d94s1), (s1) and (2s2p4), respectively. Total energies and electron densities were

7 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

computed using the DFT+U approach of Dudarev et al., in which a Hubbard U-like term describing the onsite Coulomb interactions is added to the PBE functional.53, 54 We used an effective U-J value of 3.3 eV for Co atoms and 3.8 eV for Ni atoms. The energy cut-off for the plane-wave basis set was 500 eV. A (15× 15 × 3) Monkhorst–Pack k-point grid was used for the Brillouin-zone sampling. The unit cell of CoOOH containing two formula units was optimized to be (a=b=2.895 Å; c=8.781 Å). Similar cells were used for the calculations of NiOOH and CoNi(OOH)2 with lattice constants of (a=b=2.2.973 Å; c=8.732 Å), and (a=b=2.939 Å; c=8.794 Å), respectively. All considered structures were fully optimized with the force on each atom set to CoO/3DG > NiO/3DG > PTC–C, indicating that the Co–Ni–O/3DG electrode has a larger capacitance compared to single metal oxide electrode materials. While theoretically extremely high capacities can be obtained for CoO and NiO, experimental capacities are usually much lower and strongly depend on doping and morphology as shown in Table S2 and S3. The capacitances calculated from the galvanostatic charge–discharge (GCD) curves in Figure 6b were found to be 1538, 1028, 850, and 210 F g–1 at the current density of 1 A g–1 for Co–Ni–O/3DG, CoO/3DG, NiO/3DG, and PTC–C, respectively. Analogous to CV measurements, the electrode doped with the metal oxide composite showed higher capacitance than the electrodes doped with a single metal oxide. This superior storage performance of Co–Ni–O/3DG electrode as compared to the single metal oxide equivalents may arise from the mixed dual-transition metal redox reaction. Furthermore the 3D interconnected carbon nanosheets which shows highest degree of graphitization for the metal oxide composite provides an electronic wiring for fast charge.

19 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Moreover, the intimate confinement of the two transition-metal oxides in the composite is expected to yield a beneficial electron coupling effect, as demonstrated in the DFT calculation. This adequate tailoring of electronic structure in the metal oxide composite system results in unique properties and superior performance compared to single metal oxide system.73 The hetero-nanostructure can also effectively decrease the surface energy of the active nanomaterials that may lead to a high level of electrochemical reversibility.74

Figure 6. (a) CV curves of Co–Ni–O/3DG, CoO/3DG, NiO/3DG, and PTC–C electrodes at scan rates of 5 mV s–1. (b) GCD curves of Co–Ni–O/3DG, CoO/3DG, NiO/3DG and PTC–C 20 ACS Paragon Plus Environment

Page 20 of 33

Page 21 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

electrodes at a current density of 1 A g–1. (c) Nyquist plots obtained from electrochemical impedance spectroscopy (EIS) of Co–Ni–O/3DG, CoO/3DG, NiO/3DG and PTC–C electrodes; (d) CV curves of Co–Ni–O/3DG at various scan rates. (e) GCD curves of Co–Ni–O/3DG electrode at current densities ranging from 1 to 15 A g–1. (f) Plots of current density vs. specific capacitance of Co–Ni–O/3DG, obtained from GCD curves.

Figure 6c shows the results of the impedance study of the composite materials. The corresponding equivalent circuit of the electrode is shown in Figure S9 in SI, which consists of an electrolyte resistance (Rs) (the intercept at the real axis), a double layer capacitance (Cd), a Warburg impedance (Zw), and a charge-transfer resistance (Rct) (radius of the high frequency semicircle)75. The fitted Rct values for Co–Ni–O/3DG, CoO/3DG, NiO/3DG, and PTC–C electrodes were 0.2, 0.4, 0.5, and 0.7 Ω, respectively. Co–Ni– O/3DG shows lowest Rct, indicating a more efficient electron transfer. The Nyquist plots are nearly vertical for the Co–Ni–O/3DG electrode at low frequencies, revealing that the carbon exhibited ideal capacitive behavior and improved ion diffusion properties in the electrode. In any case it is clearly that Co–Ni–O/3DG electrode possesses higher capacitance and conductivity than those formed using single metal oxide. This enhanced conductivity of Co–Ni–O/3DG nanocomposite can be attributed to the electrical wiring of the 3DG network. The intimate contact between Co–Ni–O and 3DG facilitates the electron flow, whereas the channels formed by the 3D open scaffold structure provide short diffusion paths for rapid ionic transport. Compared with single phase oxide, metal oxides with complex hetero-nanostructure possesses several competitive advantages such as rich accessible electroactive sites, superior electronic conduction, higher degree of

21 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 33

graphitization as well as beneficial electronic structural properties, all of which improve its electrochemical performance. CV curves of the Co–Ni–O/3DG electrode were shown in Figure 6d. Oxidation and reduction peaks appear in the CV curves, and the peak currents increased with increasing scan rate. The shape of the CV curve is largely preserved upon 30 fold increase of scan rate and only a minor increase in overpotential (c. 1mV) was observed. These findings prove that Co–Ni–O/3DG has excellent transport properties which are the foundation for the highrate capability and hence elevated power density. This was further confirmed by the capacitance calculated from the GCD curves of Co–Ni–O/3DG (shown in Figure 6e) which decreases by only 40% from 1586 to 940 F g–1 upon a 15-fold increase in current density from 1 to 15 A g–1 (Figure 6f). This demonstrates an excellent rate capability along with a high specific capacitance outperforming many previously reported Co- and/or Nicompound-based electrodes, as shown in Table 1. Table 1 Comparison of specific capacitance of Co–Ni–O/3DG with reported data. Electrode material

Current

Specific

Electrolyte

Ref.

(loading mass)

density

capacitance

(A g–1)

(F g–1)

Ni/NiO/RGO (3 mg)

2

1027.27

6 M KOH

76

D-NiCo2O4 (0.8 mg)

5

667

2 M KOH

77

Co3O4 @MnO2 (4.3 mg)

2.67

480

1 MLiOH

78

NixCo3-xO4 (3 mg)

1

797

6 M KOH

79

Co3O4 tube (2 mg)

0.5

1498

6 M KOH

80

CoMoO4@Co3O4 (8 mg)

0.6

1168

2 M KOH

81

Co3O4@SrGO (0.12-2.27 mg)

1

406

1 M KOH

82

NCA/Co3O4 (4 mg)

1

616

6 M KOH

83

Co3O4@PPy@MnO2 (0.7 mg)

0.5

782

1 M KOH

84

MoS2–NiO (1 mg)

1

1080.6

6 M KOH

85

Co–Ni–O/3DG (4 mg)

1

1586

6 M KOH

This work

22 ACS Paragon Plus Environment

Page 23 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Finally, the cycling stability of the hybrid Co–Ni–O/3DG electrodes was tested at 1 A g–1 over 10000 cycles as shown in Figure S10 in SI, in which this hybrid electrode can retain 93.6% of its initial capacitance even after 10000 cycles, demonstrating outstanding long-term stability. Based on these results, we suggest that the graphitic carbon nanosheets provide a good matrix for the loading of the metal oxides. Besides preventing nanoparticles’ aggregation during extended use, this matrix also can preserve electrode integrity to mitigate the detrimental effects of volume changes, thus significantly enhancing the electrochemical performance stability of this nanocomposite.

Performance in asymmetric two-electrode hybrid supercapacitor cells. In order to explore the potential application of the Co–Ni–O/3DG in a complete cell and compare our material to previously reported devices, an asymmetric hybrid supercapacitor cell was assembled. The optimal mass loading for the Co–Ni–O/3DG and rGO electrodes was estimated to be to be 32.1 and 8 mg, respectively based on CV curves (Figure S11) and the equation reported elsewhere17. The GCD curves of the (Co–Ni–O/3DG)//rGO asymmetric cell have typical shapes of pseudocapacitor in different potential windows from 1 to 1.5 V (Figure 7a). Since no significant polarization effect was observed in the asymmetric hybrid supercapacitor cell up to 1.5 V, this value was chosen as upper voltage limit for further electrochemical investigation. The current density evolved within the above mentioned potential window at different scanning rates ranging from 5 to 150 mV s–1, are shown in Figure 7b. The general shape of the CV curves was maintained even at high scan rate of 150 mV s–1, indicating stable electrochemical cycling under high current load.

23 ACS Paragon Plus Environment

ACS Applied Energy Materials

a

01.0 V 01.1 V 01.2 V 01.3 V 01.4 V 01.5 V

0.9 0.6

0

c

Voltage (V)

1.5

1 A g 2 A g 5 A g 8 A g 10 A g 15 A g

1.2 0.9 0.6 0.3 0.0

50 40

0

100 200 300 400 500 600 Time (s)

e

30 20

This work CoMoO4@Co3O4/OMEP//AC MnO/NCA//Fe2O3/NCA

10

b

5 mV s1 10 mV s1 20 mV s1 50 mV s1 100 mV s1 150 mV s1

20 0

-40

100 200 300 400 500 600 Time (s)

Specific capacitance (F g1)

0.0

40

-20

0.3

2D-CMO//CNT CMMN-4//AC GF–CNT@NiO//G–CNT, CoO/ACT//ACT/graphene CoOx//graphene

100 1000 10000 Power density (W kg1)

Capacitance retention (%)

Voltage (V)

1.2

Current density (A g1)

1.5

Energy density (Wh kg1)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 33

180

0.0

0.4 0.8 1.2 Potential (V)

1.6

d

160 140 120 100 0 100

3 6 9 12 15 Current density (A g1)

f

90 80 70 60 50

0

1500 3000 4500 Number of cycles

Figure 7. (a) GCD curves of the (Co–Ni–O/3DG)//rGO asymmetric hybrid supercapacitor cell in different potential ranges at current density of 1 A g–1. (b) CV curves of the (Co–Ni– O/3DG)//rGO asymmetric hybrid supercapacitor cell at different scan rates. (c) GCD curves of the (Co–Ni–O/3DG)//rGO asymmetric hybrid supercapacitor cell at current densities from 1 to 15 A g–1. (d) Specific capacitance as a function of current density of the asymmetric cell. (e) Ragone plot of (Co–Ni–O/3DG)//rGO asymmetric hybrid supercapacitor cell and comparison with the reported data. (f) Cycling stability of (Co–Ni–O/3DG)//rGO asymmetric hybrid supercapacitor cell at current density of 1 A g–1. 24 ACS Paragon Plus Environment

Page 25 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Figure 7c shows the GCD curves of (Co–Ni–O/3DG)//rGO asymmetric cell at different current rates. It exhibits a high specific capacitance of 175.2 F g−1 (1 A g−1) (Figure 7d). The Ragone plot of (Co–Ni–O/3DG)//rGO asymmetric hybrid supercapacitor cell was shown in Figure 7e. The nanocomposite mixed metal electrode delivers the highest energy density of 54.7 Wh kg–1 at a corresponding power density of 748.6 W kg–1, while it can stilll retain an elevated energy density of 32.8 Wh kg–1 at an impressive 11358 W kg–1. Such high values of power density are far outperforming those of previously reported two-cell supercapacitors67,

74, 80, 81, 83.

Moreover, the (Co–Ni–O/3DG)//rGO

asymmetric cell demonstrated outstanding cycling stability. A gradual capacitance drop is observed, resulting in 86.3% of the original value retained after 5000 cycles (Figure 7f). This impressive electrochemical performances is again attributed to the open hybrid nanostructure of the Co–Ni–O/3DG electrode which provides an excellent electrolyteelectrode interface, enhanced the conductivity based on the 3D carbon electrical wiring network, and optimized electronic structure tailoring.

CONCLUSIONS In summary, three-dimensional graphitic carbon nanosheets embedded with highly dispersed Co–Ni oxides were obtained in a simple process from homogeneous biopolymer–metal complex monoliths. This approach represents a significant step forward in producing carbon-based batterysupercapacitor-hybrid materials using green resources. The resulting Co–Ni–O/3DG nanocomposite exhibits excellent electrochemical performance. A high capacitance of 1586 F g-1 was obtained at a current density of 1 A g-1 as well as remarkable cycling stability over 10000 cycles. By combining the Co–Ni–O/3DG positive electrode with a rGO

25 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

negative electrode, the resulting asymmetric hybrid supercapacitor delivered an energy density of 32.8 to 54.7 Wh kg–1 associated with very high power densities of 11358 to 748.6 W kg–1, which is beyond the recent state of the art and represents an important advancement in the HSC research field. Furthermore, the asymmetric hybrid supercapacitor showed a very stable cycling over thousands of cycles. Since the preparation of Co–Ni–O/3DG is simple, inexpensive and easy to implement in an industrial setup, the material has great potential to fill demands in future electrochemical storage applications.

26 ACS Paragon Plus Environment

Page 26 of 33

Page 27 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

ASSOCIATED CONTENT Supporting Information The Supporting Information is available free of charge on the ACS Publications website at DOI: XXXX XXX XXX-XXX [Figure S1 depicts the structure of PT and C; Figure S2 TG curve; Figure S3-S4 Fourier transformed EXAFS; Figure S5-S6 SEM/TEM images; Figure S7 XPS Spectrum; Figure S8 DFT model structure; Figure S9 Circuit illustration; Figure S10 Cycle stability test; Figure S11 additional CV curves; Table S1 lattice calculation; Table S2-S3 literature capacitance value comparison (PDF)] AUTHOR INFORMATION Corresponding Author *Email: [email protected] *Email: [email protected] ORCID Cuili Xiang: 0000-0001-8225-6568 Yongjin Zou: 0000-0002-9012-2639 Marcus Fehse: 0000-0001-8650-6974 Notes The authors declare no competing financial interest. ACKNOWLEGDMENTS The authors gratefully express their thanks to National Science Foundation of China (Grant No. 27 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

51861004), Guangxi Natural Science Foundation (Grant No. 2016GXNSFFA380012, 2017AD23029 and 2017GXNSFDA198018), the EU Horizon2020 Marie Curie Cofund project (Grant No. 713279) and NSERC (RGPIN-2016-06122), as well as the synchrotron beamtime granted on DUBBLE through the ESRF proposal (MA 4396).

28 ACS Paragon Plus Environment

Page 28 of 33

Page 29 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

REFERENCES: (1) (2) (3) (4) (5) (6) (7) (8) (9) (10) (11) (12) (13) (14) (15) (16) (17) (18) (19) (20) (21) (22)

Miller, J. R.; Simon, P. Materials Science - Electrochemical Capacitors for Energy Management. Science 2008, 321, 651–652. Tarascon, J. M.; Armand, M. Issues and Challenges Facing Rechargeable Lithium Batteries. Nature 2001, 414, 359–367. Dubal, D. P.; Gomez-Romero, P.; Sankapal, B. R.; Holze, R. Nickel Cobaltite as an Emerging Material for Supercapacitors: An Overview. Nano Energy 2015, 11, 377–399. El-Kady, M. F.; Ihns, M.; Li, M.; Hwang, J. Y.; Mousavi, M. F.; Chaney, L.; Lech, A. T.; Kaner, R. B. Engineering Three-dimensional Hybrid Supercapacitors and Microsupercapacitors for High-Performance Integrated Energy Storage. Proc. Natl. Acad. Sci. U.S.A. 2015,112, 4233–4238. Lee, D. U.; Kim, B. J.; Chen, Z. One-pot Synthesis of a Mesoporous NiCo2O4 Nanoplatelet and Graphene Hybrid and Its Oxygen Reduction and Evolution Activities as an Efficient Bi-Functional Electrocatalyst. J. Mater Chem. A 2013, 1, 4754–4762. Ma, F.-X.; Yu, L.; Xu, C.-Y.; Lou, X. W. Self-supported Formation of Hierarchical NiCo2O4 Tetragonal Microtubes with Enhanced Electrochemical Properties. Energy Environ. Sci. 2016, 9, 862–866. Kim, H.; Cho, M. Y.; Kim, M. H.; Park, K. Y.; Gwon, H.; Lee, Y.; Roh, K. C.; Kang, K. A Novel High-Energy Hybrid Supercapacitor with an Anatase TiO2-Reduced Graphene Oxide Anode and an Activated Carbon Cathode. Adv. Energy Mater. 2013, 3, 1500–1506. Qu, C.; Zhao, B. T.; Jiao, Y.; Chen, D. C.; Dai, S. G.; Deglee, B. M.; Chen, Y.; Walton, K. S.; Zou, R. Q.; Liu, M. L. Functionalized Bimetallic Hydroxides Derived from Metal-Organic Frameworks for High-Performance Hybrid Supercapacitor with Exceptional Cycling Stability. ACS Energy Lett. 2017, 2, 1263–1269. Li, B.; Zheng, M.; Xue, H.; Pang, H. High Performance Electrochemical Capacitor Materials Focusing on Nickel Based Materials. Inorg. Chem. Front. 2016, 3, 175–202. Li, L.; Cheah, Y.; Ko, Y.; Teh, P.; Wee, G.; Wong, C.; Peng, S.; Srinivasan, M. The Facile Synthesis of Hierarchical Porous Flower-Like NiCo2O4 with Superior Lithium Storage Properties. J. Mater. Chem. A 2013, 1, 10935–10941. Li, Z.; Xu, Z. W.; Wang, H. L.; Ding, J.; Zahiri, B.; Holt, C. M. B.; Tan, X. H.; Mitlin, D. Colossal Pseudocapacitance in a High Functionality-High Surface Area Carbon Anode Doubles the Energy of an Asymmetric Supercapacitor. Energy Environ. Sci. 2014, 7, 1708–1718. Wang, H.; Yi, H.; Chen, X.; Wang, X. Asymmetric Supercapacitors Based on Nano-Architectured Nickel Oxide/Graphene Foam and Hierarchical Porous Nitrogen-Doped Carbon Nanotubes with Ultrahigh-Rate Performance. J. Mater. Chem. A 2014, 2, 3223–3230. Wang, R.; Yan, X. Superior Asymmetric Supercapacitor Based on Ni-Co Oxide Nanosheets and Carbon nanorods. Sci. Rep. 2014, 4, 3712. Wu, Z.; Zhu, Y.; Ji, X. NiCo2O4-Based Materials for Electrochemical Supercapacitors. J. Mater. Chem. A 2014, 2, 14759–14772. Shen, L.; Yu, L.; Wu, H. B.; Yu, X.Y.; Zhang, X.; Lou, X. W., Formation of Nickel Cobalt Sulfide Ball-in-Ball Hollow Spheres with Enhanced Electrochemical Pseudocapacitive Properties. Nat. Commun. 2015, 6, 6694. Shen, L.; Yu, L.; Yu, X.Y.; Zhang, X.; Lou, X. W. Self-Templated Formation of Uniform NiCo2O4 Hollow Spheres with Complex Interior Structures for Lithium-Ion Batteries and Supercapacitors. Angew. Chem., Int. Ed. 2015, 54, 1868–1872. Zou, Y. J.; Cai, C. L.; Xiang, C. L.; Huang, P. R.; Chu, H. L.; She, Z.; Xu, F.; Sun, L. X.; Kraatz, H. B. Simple Synthesis of Core-Shell Structure of Co-Co3O4@Carbon-Nanotube-Incorporated Nitrogen-Doped Carbon for High-Performance Supercapacitor. Electrochim. Acta 2018, 261, 537–547. Xu, K.; Li, W.; Liu, Q.; Li, B.; Liu, X.; An, L.; Chen, Z.; Zou, R.; Hu, J. Hierarchical Mesoporous NiCo2O4@MnO2 Core-Shell Nanowire Arrays on Nickel Foam for Aqueous Asymmetric Supercapacitors. J. Mater. Chem. A 2014, 2, 4795–4802. Yu, X.; Lu, B.; Xu, Z. Super Long-Life Supercapacitors Based on the Construction of Nanohoneycomb-Like Strongly Coupled CoMoO-3D Graphene Hybrid Electrodes. Adv. Mater. 2014, 26, 1044–1051. Zhang, Y.; Li, L.; Su, H.; Huang, W.; Dong, X. Binary Metal Oxide: Advanced Energy Storage Materials in Supercapacitors. J. Mater. Chem. A 2015, 3, 43–59. Snook, G. A.; Kao, P.; Best, A. S. Conducting-Polymer-Based Supercapacitor Devices and Electrodes. J. Power Sources 2011, 196, 1–12. Xiang, C. L.; Wang, Q. Y.; Zou, Y. J.; Huang, P. R.; Chu, H. L.; Qiu, S. J.; Xu, F.; Sun, L. X. Simple Synthesis 29 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(23) (24) (25) (26) (27) (28) (29) (30) (31) (32) (33) (34) (35) (36) (37) (38) (39) (40) (41) (42) (43) (44) (45)

of Graphene-Doped Flower-Like Cobalt-Nickel-Tungsten-Boron Oxides with Self-Oxidation for HighPerformance Supercapacitors. J. Mater. Chem. A 2017, 5, 9907–9916. Hao, L.; Li, X. L.; Zhi, L. J. Carbonaceous Electrode Materials for Supercapacitors. Adv. Mater. 2013, 25, 3899– 3904. Shen, L.; Wang, J.; Xu, G.; Li, H.; Dou, H.; Zhang, X. NiCo2S4 Nanosheets Grown on Nitrogen-Doped Carbon Foams as an Advanced Electrode for Supercapacitors. Adv. Energy Mater. 2015, 5, 1400977. Li, Y. Y.; Li, Z. S.; Shen, P. K. Simultaneous Formation of Ultrahigh Surface Area and Three-Dimensional Hierarchical Porous Graphene-Like Networks for Fast and Highly Stable Supercapacitors. Adv. Mater. 2013, 25, 2474–2480. Kan, Y. F.; Ma, X. L.; Ning, G. Q.; Li, Y. F.; Zhou, Y. S. S, N Dual-Doped Graphene Fibers: A HighPerformance Electrode Material for Supercapacitors. ChemElectroChem 2017, 4, 2677–2682. Zhang, L.; Li, T. H.; Ji, X. L.; Zhang, Z. Y.; Yang, W. B.; Gao, J. J.; Li, H.; Xiong, C. Y.; Dang, A. Freestanding Three-Dimensional Reduced Graphene Oxide/MnO2 on Porous Carbon/Nickel Foam as a Designed Hierarchical Multihole Supercapacitor Electrode. Electrochim. Acta 2017, 252, 306–314. Liu, Z. S.; Li, D. H.; Li, Z. S.; Liu, Z. H.; Zhang, Z. Y. Nitrogen-Doped 3D Reduced Graphene Oxide/Polyaniline Composite as Active Material for Supercapacitor Electrodes. Appl. Surf. Sci. 2017, 422, 339–347. Ma, H. Y.; Li, C.; Zhang, M.; Hong, J. D.; Shi, G. Q. Graphene Oxide Induced Hydrothermal Carbonization of Egg Proteins for High-Performance Supercapacitors. J. Mater. Chem. A 2017, 5, 17040–17047. Li, B.; Yang, S. B.; Li, S. M.; Wang, B.; Liu, J. H. From Commercial Sponge Toward 3D Graphene-Silicon Networks for Superior Lithium Storage. Adv. Energy Mater. 2015, 5, 1500289. Zhao, L.; Sui, X. L.; Li, J. L.; Zhang, J. J.; Zhang, L. M.; Wang, Z. B. 3D Hierarchical Pt-Nitrogen-DopedGraphene-Carbonized Commercially Available Sponge as a Superior Electrocatalyst for Low-Temperature Fuel Cells. ACS Appl. Mater. Interfaces 2016, 8, 16026–16034. Marchena, M.; Song, Z.; Senaratne, W.; Li, C. N.; Liu, X. Y.; Baker, D.; Ferrer, J. C.; Mazumder, P.; Soni, K.; Lee, R.; Pruneri, V. Direct Growth of 2D and 3D Graphene Nano-Structures over Large Glass Substrates by Tuning a Sacrificial Cu-Template Layer. 2D. Mater. 2017, 4, 025088. Pan, Z. H.; Liu, M. N.; Yang, J.; Qiu, Y. C.; Li, W. F.; Xu, Y.; Zhang, X. Y.; Zhang, Y. G. High Electroactive Material Loading on a Carbon Nanotube@3D Graphene Aerogel for High-Performance Flexible All-Solid-State Asymmetric Supercapacitors. Adv. Funct. Mater. 2017, 27, 1701122. Zhang, W. L.; Xu, C.; Ma, C. Q.; Li, G. X.; Wang, Y. Z.; Zhang, K. Y.; Li, F.; Liu, C.; Cheng, H. M.; Du, Y. W.; Tang, N. J.; Ren, W. C. Nitrogen-Superdoped 3D Graphene Networks for High-Performance Supercapacitors. Adv. Mater. 2017, DOI: 10.1002/adma.201701677. Bao, L.; Li, T.; Chen, S.; Peng, C.; Li, L.; Xu, Q.; Chen, Y. S.; Ou, E. C.; Xu, W. J. 3D Graphene Frameworks/Co3O4 Composites Electrode for High-Performance Supercapacitor and Enzymeless Glucose Detection. Small 2017, 13, 1602677. Zhang, L. S.; Zhao, Z. J.; Xia, T. C.; Zhang, S. L.; Li, X. F.; Zhang, A. Q. Anchoring Bi2WO6 Nanoparticles on 3D Graphene Frameworks for Enhanced Lithium Storage. Mater. Lett. 2018, 210, 345–349. Wu, S. S.; Chen, W. F.; Yan, L. F. Fabrication of a 3D MnO2/Graphene Hydrogel for High-Performance Asymmetric Supercapacitors. J. Mater. Chem. A 2014, 2, 2765–2772. Lin, T. W.; Dai, C. S.; Tasi, T. T.; Chou, S. W.; Lin, J. Y.; Shen, H. H. High-Performance Asymmetric Supercapacitor Based on Co9S8/3D Graphene Composite and Graphene Hydrogel. Chem. Eng. J. 2015, 279, 241–249. Wu, J.; Tao, K.; Zhang, J.; Guo, Y. Y.; Miao, J. M.; Norford, L. K. Chemically Functionalized 3D Graphene Hydrogel for High Performance Gas Sensing. J. Mater. Chem. A 2016, 4, 8130–8140. Yan, Z.; Lin, J.; Peng, Z. W.; Sun, Z. Z.; Zhu, Y.; Li, L.; Xiang, C. S.; Samuel, E. L.; Kittrell, C.; Tour, J. M. Toward the Synthesis of Wafer-Scale Single-Crystal Graphene on Copper Foils. ACS Nano. 2012, 6, 9110–9117. Ozden, S.; Narayanan, T. N.; Tiwary, C. S.; Dong, P.; Hart, A. H. C.; Vajtai, R.; Ajayan, P. M. 3D Macroporous Solids from Chemically Cross-Linked Carbon Nanotubes. Small 2015, 11, 688–693. 42. Vinod, S.; Tiwary, C. S.; Machado, L. D.; Ozden, S.; Vajtai, R.; Galvao, D. S.; Ajayan, P. M. Synthesis of Ultralow Density 3D Graphene-CNT Foams Using a Two-Step Method. Nanoscale 2016, 8, 15857–15863. Chen, Z. P.; Ren, W. C.; Gao, L. B.; Liu, B. L.; Pei, S. F.; Cheng, H. M. Three-Dimensional Flexible and Conductive Interconnected Graphene Networks Grown by Chemical Vapour Deposition. Nat. Mater. 2011, 10, 424–428. Bacelo, H. A. M.; Santos, S. C. R.; Botelho, C. M. S. Tannin-Based Biosorbents for Environmental Applications - A Review. Chem. Eng. J. 2016, 303, 575–587. Fang, Y.; Lv, Y. Y.; Che, R. C.; Wu, H. Y.; Zhang, X. H.; Gu, D.; Zheng, G. F.; Zhao, D. Y. Two-Dimensional 30 ACS Paragon Plus Environment

Page 30 of 33

Page 31 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

(46) (47) (48)

(49) (50) (51) (52) (53) (54) (55) (56) (57) (58) (59) (60) (61) (62) (63) (64) (65) (66) (67) (68)

Mesoporous Carbon Nanosheets and Their Derived Graphene Nanosheets: Synthesis and Efficient Lithium Ion Storage. J. Am. Chem. Soc. 2013, 135, 1524–1530. Yuan, C. Z.; Wu, H. B.; Xie, Y.; Lou, X. W. Mixed Transition-Metal Oxides: Design, Synthesis, and EnergyRelated Applications. Angew. Chem. Int. Ed. 2014, 53, 1488–1504. Marcano, D. C.; Kosynkin, D. V.; Berlin, J. M.; Sinitskii, A.; Sun, Z. Z.; Slesarev, A.; Alemany, L. B.; Lu, W.; Tour, J. M. Improved Synthesis of Graphene Oxide. ACS Nano. 2010, 4, 4806–4814. Nikitenko, S.; Beale, A. M.; van der Eerden, A. M. J.; Jacques, S. D. M.; Leynaud, O.; O'Brien, M. G.; Detollenaere, D.; Kaptein, R.; Weckhuysen, B. M.; Bras, W. Implementation of a Combined SAXS/WAXS/QEXAFS Set-Up for Time-Resolved in situ Experiments. J. Synchrotron. Radiat. 2008, 15, 632– 640. Ressler, T. WinXAS: A New Software Package not Only for the Analysis of Energy-Dispersive XAS Data. J. Phys. Iv. 1997, 7, 269–270. Teo, B. K. EXAFS : Basic Principles and Data Analysis. Springer: Berlin; D.E., 1986. Kresse, G.; Hafner, J. Abinitio Molecular-Dynamics for Liquid-Metals. Phys. Rev. B 1993, 47, 558-561. Kresse, G.; Furthmuller, J. Efficiency of Ab-initio Total Energy Calculations for Metals and Semiconductors Using a Plane-Wave Basis Set. Comp. Mater. Sci. 1996, 6, 15–50. Perdew, J. P.; Burke, K.; Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 1996, 77, 3865–3868. Dudarev, S. L.; Botton, G. A.; Savrasov, S. Y.; Humphreys, C. J.; Sutton, A. P. Electron-Energy-Loss Spectra and the Structural Stability of Nickel Oxide: An LSDA+U Study. Phys. Rev. B 1998, 57, 1505–1509. Tessonnier, J. P.; Becker, M.; Xia, W.; Girgsdies, F.; Blume, R.; Yao, L. D.; Su, D. S.; Muhler, M.; Schlogl, R. Spinel-Type Cobalt-Manganese-Based Mixed Oxide as Sacrificial Catalyst for the High-Yield Production of Homogeneous Carbon Nanotubes. ChemCatChem 2010, 2, 1559–1561. Zhou, Z. D.; Liu, F. L.; Huang, Y.; Wang, Z. M.; Li, G. Y. Biosorption of Palladium(II) from Aqueous Solution by Grafting Chitosan on Persimmon Tannin Extract. Int. J. Biol. Macromol. 2015, 77, 336–343. Motahari, F.; Mozdianfard, M. R.; Salavati-Niasari, M. Synthesis and Adsorption Studies of NiO Nanoparticles in the Presence of H(2)acacen Ligand, for Removing Rhodamine B in Wastewater Treatment. Process Saf. Environ. Prot. 2015, 93, 282–292. Manteghi, F.; Kazemi, S. H.; Peyvandipour, M.; Asghari, A. Preparation and Application of Cobalt Oxide Nanostructures as Electrode Materials for Electrochemical Supercapacitors. Rsc Adv. 2015, 5, 76458-76463. Mishra, A. K.; Ramaprabhu, S. Carbon Dioxide Adsorption in Graphene Sheets. AIP Adv. 2011, 1, 032152. Duan, Z. J.; Zhang, H. Z.; Sun, L. X.; Cao, Z.; Xu, F.; Zou, Y. J.; Chu, H. L.; Qiu, S. J.; Xiang, C. L.; Zhou, H. Y. CaCl2 Center Dot 6H2O/Expanded Graphite Composite as Form-Stable Phase Change Materials for Thermal Energy Storage. J. Therm. Anal. Calorim. 2014, 115, 111–117. Li, Z. Q.; Lu, C. J.; Xia, Z. P.; Zhou, Y.; Luo, Z. X-ray Diffraction Patterns of Graphite and Turbostratic Carbon. Carbon 2007, 45, 1686–1695. Aijaz, A.; Masa, J.; Rosler, C.; Xia, W.; Weide, P.; Botz, A. J. R.; Fischer, R. A.; Schuhmann, W.; Muhler, M. Co@Co3O4 Encapsulated in Carbon Nanotube-Grafted Nitrogen-Doped Carbon Polyhedra as an Advanced Bifunctional Oxygen Electrode. Angew. Chem. Int. Ed. 2016, 55, 4087–4091. Zhang, L. J.; Hu, P.; Zhao, X. Y.; Tian, R. L.; Zou, R. Q.; Xia, D. G., Controllable Synthesis of Core-Shell Co@CoO Nanocomposites with a Superior Performance as an Anode Material for Lithium-ion Batteries. J. Mater. Chem. 2011, 21, 18279–18283. Long, H.; Shi, T. L.; Hu, H.; Jiang, S. L.; Xi, S.; Tang, Z. R. Growth of Hierarchal Mesoporous NiO Nanosheets on Carbon Cloth as Binder-free Anodes for High-Performance Flexible Lithium-ion Batteries. Sci. Rep. 2014, 4, 7413. Nossol, E.; Nossol, A. B. S.; Guo, S. X.; Zhang, J.; Fang, X. Y.; Zarbin, A. J. G.; Bond, A. M. Synthesis, Characterization and Morphology of Reduced Graphene Oxide-Metal-TCNQ Nanocomposites. J. Mater. Chem. C 2014, 2, 870–878. Zhang, L.; Zhang, F.; Yang, X.; Long, G. K.; Wu, Y. P.; Zhang, T. F.; Leng, K.; Huang, Y.; Ma, Y. F.; Yu, A.; Chen, Y. S. Porous 3D Graphene-Based Bulk Materials with Exceptional High Surface Area and Excellent Conductivity for Supercapacitors. Sci. Rep. 2013, 3, 1408. Zhang, X.; Luo, J. S.; Tang, P. Y.; Ye, X. L.; Peng, X. X.; Tang, H. L.; Sun, S. G.; Fransaer, J. A Universal Strategy for Metal Oxide Anchored and Binder-Free Carbon Matrix Electrode: A Supercapacitor Case with Superior Rate Performance and High Mass Loading. Nano Energy 2017, 31, 311–321. Kharissova, O. V.; Kharisov, B. I. Variations of Interlayer Spacing in Carbon Nanotubes. RSC Adv. 2014, 4, 30807–30815. 31 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(69) Wang, X.; Zhan, C.; Ding, Y.; Ding, B.; Xu, Y.; Liu, S.; Dong, H. Dual-Core Fe2O3@Carbon Structure Derived from Hydrothermal Carbonization of Chitosan as a Highly Efficient Material for Selective Adsorption. ACS Sustain. Chem. Eng. 2017, 5, 1457–1467. (70) Wang, X.; Sumboja, A.; Lin, M. F.; Yan, J.; Lee, P. S. Enhancing Electrochemical Reaction Sites in NickelCobalt Layered Double Hydroxides on Zinc Tin Oxide Nanowires: A Hybrid Material for an Asymmetric Supercapacitor Device. Nanoscale 2012, 4, 7266–7272. (71) Lyons, M. E. G.; Brandon, M. P. A Comparative Study of the Oxygen Evolution Reaction on Oxidised Nickel, Cobalt and Iron Electrodes in Base. J. Electroanal. Chem. 2010, 641, 119–130. (72) Yu, M. H.; Wang, W.; Li, C.; Zhai, T.; Lu, X. H.; Tong, Y. X. Scalable Self-Growth of Ni@NiO Core-Shell Electrode with Ultrahigh Capacitance and Super-Long Cyclic Stability for Supercapacitors. NPG. Asia Mater. 2014, 6, e129. (73) Long, X.; Wang, Z. L.; Xiao, S.; An, Y. M.; Yang, S. H. Transition Metal Based Layered Double Hydroxides Tailored for Energy Conversion and Storage. Mater. Today 2016, 19, 213–226. (74) Gao, Z.; Song, N. N.; Li, X. D. Microstructural Design of Hybrid CoO@NiO and Graphene Nano-Architectures for Flexible High Performance Supercapacitors. J. Mater. Chem. A 2015, 3, 14833–14844. (75) Li, X. L.; Pu, X.; Han, S. C.; Liu, M. M.; Du, C. H.; Jiang, C. Y.; Huang, X.; Liu, T.; Hu, W. G. Enhanced Performances of Li/Polysulfide Batteries with 3D Reduced Graphene Oxide/Carbon Nanotube Hybrid Aerogel as the Polysulfide Host. Nano Energy 2016, 30, 193–199. (76) Zhu, Y. C.; Chu, W.; Wang, N.; Lin, T.; Yang, W.; Wen, J.; Zhao, X. S. Self-Assembled Ni/NiO/RGO Heterostructures for High-Performance Supercapacitors. RSC Adv. 2015, 5, 77958–77964. (77) Veeramani, V.; Madhu, R.; Chen, S. M.; Sivakumar, M. Flower-Like Nickel-Cobalt Oxide Decorated DopamineDerived Carbon Nanocomposite for High Performance Supercapacitor Applications. ACS Sustain. Chem. Eng. 2016, 4, 5013–5020. (78) Liu, J. P.; Jiang, J.; Cheng, C. W.; Li, H. X.; Zhang, J. X.; Gong, H.; Fan, H. J. Co3O4 Nanowire@MnO2 Ultrathin Nanosheet Core/Shell Arrays: A New Class of High-Performance Pseudocapacitive Materials. Adv Mater. 2011, 23, 2076. (79) Chen, S. R.; Xue, M.; Li, Y. Q.; Pan, Y.; Zhu, L. K.; Qiu, S. L. Rational Design and Synthesis of NixCo3-xO4 Nanoparticles Derived from Multivariate MOF-74 for Supercapacitors. J. Mater. Chem. A 2015, 3, 20145–20152. (80) Zhang, Z. Q.; Zhang, H. D.; Zhang, X. Y.; Yu, D. Y.; Ji, Y.; Sun, Q. S.; Wang, Y.; Liu, X. Y. Facile Synthesis of Hierarchical CoMoO4@NiMoO4 Core-Shell Nanosheet Arrays on Nickel Foam as an Advanced Electrode for Asymmetric Supercapacitors. J. Mater. Chem. A 2016, 4, 18578–18584. (81) Li, M.; Wang, Y. H.; Yang, H. X.; Chu, P. K. Hierarchical CoMoO4@Co3O4 Nanocomposites on an Ordered Macro-Porous Electrode Plate as a Multi-Dimensional Electrode in High-Performance Supercapacitors. J. Mater. Chem. A 2017, 5, 17312–17324. (82) Qorbani, M.; Chou, T. C.; Lee, Y. H.; Samireddi, S.; Naseri, N.; Ganguly, A.; Esfandiar, A.; Wang, C. H.; Chen, L. C.; Chen, K. H.; Moshfegh, A. Z. Multi-Porous Co3O4 Nanoflakes@Sponge-Like Few-Layer Partially Reduced Graphene Oxide Hybrids: Towards Highly Stable Asymmetric Supercapacitors. J. Mater. Chem. A 2017, 5, 12569–12577. (83) Sun, G. L.; Ma, L. Y.; Ran, J. B.; Shen, X. Y.; Tong, H. Incorporation of Homogeneous Co3O4 into a NitrogenDoped Carbon Aerogel via a Facile in situ Synthesis Method: Implications for High Performance Asymmetric Supercapacitors. J. Mater. Chem. A 2016, 4, 9542–9554. (84) Wang, B.; He, X. Y.; Li, H. P.; Liu, Q.; Wang, J.; Yu, L.; Yan, H. J.; Li, Z. S.; Wang, P., Optimizing the Charge Transfer Process by Designing Co3O4@PPy@MnO2 Ternary Core-Shell Composite. J. Mater. Chem. A 2014, 2, 12968–12973. (85) Wang, K.; Yang, J.; Zhu, J. X.; Li, L.; Liu, Y.; Zhang, C.; Liu, T. X. General Solution-Processed Formation of Porous Transition-Metal Oxides on Exfoliated Molybdenum Disulfides for High-Performance Asymmetric Supercapacitors. J. Mater. Chem. A 2017, 5, 11236–11245.

32 ACS Paragon Plus Environment

Page 32 of 33

Page 33 of 33 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47

ACS Applied Energy Materials

ACS Paragon Plus Environment