Co4N Nanosheet Assembled Mesoporous Sphere as a Matrix for

Subscriber access provided by UNIV OF ARIZONA

Article

Co4N Nanosheets Assembled Mesoporous Sphere as a Matrix for Ultrahigh Sulfur Content Lithium-Sulfur Batteries Ding-Rong Deng, Fei Xue, Yue-Ju Jia, Jian-Chuan Ye, Cheng-Dong Bai, Ming-Sen Zheng, and Quan-Feng Dong ACS Nano, Just Accepted Manuscript • Publication Date (Web): 01 Jun 2017 Downloaded from http://pubs.acs.org on June 1, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Co4N Nanosheets Assembled Mesoporous Sphere as

a

Matrix

for

Ultrahigh

Sulfur

Content

Lithium−Sulfur Batteries Ding-Rong Deng, Fei Xue, Yue-Ju Jia, Jian-Chuan Ye, Cheng-Dong Bai, Ming-Sen Zheng* and Quan-Feng Dong*

State Key Laboratory for Physical Chemistry of Solid Surfaces, Department of Chemistry, College of Chemistry and Chemical Engineering, iChem (Collaborative Innovation Center of Chemistry for Energy Materials) Xiamen, Fujian, 361005, China

KEYWORDS : Li-S battery, mesoporous sphere, cobalt nitride, adsorb, catalyze, high sulfur loading

ABSTRACT

High utilization and loading of sulfur in cathode holds the key in realization of Li-S batteries. We here synthesized a Co4N mesoporous sphere, which was made up of nanosheets via an easy

ACS Paragon Plus Environment

1

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 30

and convenient method. This material presents high affinity, speedy trapping and absorbing capacity for polysulfides, and acts as a bifunctional catalysis for sulfur redox processes, therefore it is an ideal matrix for S active material. With such a mesoporous sphere used as a sulfur host in Li-S batteries, extraordinary electrochemistry performance has been achieved. With a sulfur content of 72.3 wt% in the composite, the Co4N@S delivered a high specific discharge capacity of 1659 mAh g-1 at 0.1 C, almost reaching its theoretic capacity. Also, the battery exhibited large reversible capacity about 1100 mAh g-1 at 0.5 C and 1000 mAh g-1 at 1 C after 100 cycles. At a high rate of 2 C and 5C, after 300 cycles, the discharge capacity finally stabilized at 805 mAh g-1 and 585 mAh g-1. Even at the 94.88% sulfur content, the cathode can still deliver an extremely high specific discharge capacity of 1259 mAh g-1 with good cycle performance.

There is no doublt that the energy demand increases steadily with time because of the global population increase and the economic growth. The search of advanced energy storage systems with higher energy densities is very important for powering our future communities.1-5 Lithium−sulfur (Li−S) battery has been one of the best devices for next generation high energy storage systems as a result of its high theoretical capacity. The lithium−sulfur battery has a high energy density and theoretical capacity of 2500 kW kg-1 and 1675 mAh g-1, respectively, far superior to the current lithium-ion batteries.6-11 However, with years of development, Li-S battery is still not primed for commercialization due to its incomplete sulfur utilization, capacity attenuation, poor cycling life and low Coulombic efficiency. These drawbacks are attributed to the poor conductivity of sulphur and the emergence of the discharging products (Li2S and Li2S2) and the dissoluble lithium polysulfide (Li2Sn) in the charging and discharging processes.8,12,13 During back and forth shuttling in the electrolyte between the cathode and anode, polysulfide


2

Page 3 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

lithium triggers a polysulphide-shuttle process, which leads to battery capacity attenuation, poor cycling life and low Coulombic efficiency.14-16 To deal with these challenges, great efforts have been made to optimize the composition and the structure of the sulfur cathode, most of those managed to combine sulfur with different kinds of host materials.17-29 However, with the accretion of the host materials, the content of S in the active material of cathode decreases accordingly, therefore how to find a balance between the content of S and good electrochemical performance plays a significant role in the study of the Li−S battery. Most of the host materials attach S with different kinds of conductive additives, such as various types of carbonous materials. Nazar et al. used the porous carbon materials (CMK3) as the sulfur host materials, which improved the cycling life and specific capacity for their lithium−sulfur battery.17 When the content of S at active material of cathode was about 70%, the discharge capacity of the first cycle was 1380 mAh g-1 at a current density of 0.1 C (1C=1675 mA g-1). Carbon materials can promote the electrical conductivity of the cathode and act as good buffers for the large volume expansion of sulfur during the charge-discharge process.17-23 On the other hand, host materials that bind polysulfides through chemical interactions have been discovered and applied as cathode electrodes for Li-S batteries.24-31 Nazar et al. reported that Ti4O7 can be used as the effective LiPS absorbents.24 When the content of S in Ti4O7/S composite was about 60%, the discharge capacity of the 1st cycle was 1200 mAh g-1 at the rate of 0.05 C. And it exhibited a reversible capacity about 850 mAh g-1 at 0.5 C after 100 cycles. After that, polar materials like metal oxides, metal nitride including Ti4O7,24,25 TiO2,26 MnO2,27,28 MnO,30 TiN

31,32

and functionalized carbon materials such as nitrogen doped

carbon/graphene15,29 have been reported to be used as the effective lithium polysulfides (LiPSs)


3

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 30

absorbents. These host materials in cathode will reduce the “shuttle effect” and improve the cycle stability of the lithium-sulfur battery. Unfortunately, according to the results of existing reports, the sulfur content of active material in Li-S battery cathodes is below 70 wt%, which is difficult to achieve commercialization. In order to achieve higher sulfur content, some host materials have been employed in recent study.33-36 However, the high loading of elemental S will lead to more serious shuttle effect, rapid capacity loss, lower specific capacity, and poor rate properties. Zheng et al. used the hierarchical porous carbon rods as sulfur host materials, when the sulfur content was increased to 80%, it showed a first cycle discharge capacity of 972 mAh g-1 at 0.5 C and 800 mAh g-1 after 30 cycles at 1 C.36 And in recent papers, the high area loadings S about 10 mg cm-2 have been reported.37-41 Therefore, increasing the utilization of sulfur in cathode at high S content continues to be a great challenge for Li-S battery. Here, a simple and efficient method for synthesizing Co4N mesoporous sphere which was composed by nanosheets was reported. The Co4N mesoporous spheres were uniform distribution and displayed porous structure. In comparison with the Co3O4 mesoporous sphere which has similar pore size distribution and specific surface area, the Co4N mesoporous sphere exhibited not only higher affinity for polysulfide, but also stronger capability for polysulfide adsorbtion than Co3O4 sphere. Furthermore, the Co4N mesoporous sphere demonstrated bifunctional catalytic activities for Li-S battery. The Co atoms in Co4N can promote the discharge process and N atoms can improve the charge process of lithium-sulfur battery (Scheme1). As the Co4N mesoporous sphere used as sulfur host materials for Li-S battery, they displayed remarkable cycling performance, especially in the very high sulfur content regime. When the weight ratio of elemental S and Co4N spheres was 3:1 (S content is as high as 72.3 wt%), the battery exhibited


4

Page 5 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

large reversible capacity above 1100 mAh g-1 at 0.5 C and 1000 mAh g-1 at 1 C after 100 cycles. At a high rate of 2 C, it showed a high capacity retention of above 94% and with a capacity decay of 0.01% per cycle. After 300 cycles, the discharge capacity finally stabilized at 805 mAh g-1. Even with a weight ratio increased to 9:1 (S content of 89.64 wt%), the Co4N-S composite still delivered a outstanding rate performance and cycling stability (801 mAh g−1 after 100 cycles at 1 C and 670 mAh g-1 after 300 cycles at 2C). More importantly, even after the high weight ratio of S and Co4N spheres was adjusted to 19:1, the Co4N/S composite maintained a high cycling stability (640 mAh g-1 after 100 cycles at 1 C). RESULTS AND DISCUSSION XRD analysis were used to characterize the as-prepared samples and the results are shown in Figure S1. Figure S1a shows that the sample is pure Co3O4, all the peaks can be assigned to the standard Co3O4, no any other contaminations were observed, indicating a high purity of the Co3O4 crystalline phase. The XRD patterns achieved after a simple nitridation reaction in Figure S1b match well with those of the pure Co4N phase with a face centered cubic (fcc) structure, indicating that the Co3O4 can be successfully converted into Co4N product.42 And the Energy Dispersive Spectrometer (EDS) in Figure S2 show that the atomic ratio of Co and N is about 4:1. Field-emission scanning electron microscopy (FESEM) images provide insight into the structure and morphology of the as-prepared Co3O4 and Co4N. Figure 1a and b are the SEM images of overall view of Co3O4 power; it shows a uniform distribution of spherical morphology with diameter of 2-3 µm. Figure 1b shows that the Co3O4 spheres display porous structure consisting of Co3O4 nanosheets with 10-20 nm in thickness. Figure 1c and d illustrate the SEM images of the products obtained after thermal treatment of Co3O4 at 400 °C for 4 h in ammonia


5

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 30

atmosphere. The images reveal that most of the spheres are retained, and the surface morphology of porous structure is mostly maintained after calcination, except for part of the nanosheets becoming nanoparticles with diameter of 20-30 nm. This can be clearly seen in the transmission electron microscopy (TEM) images in Figure S3. And the TEM images also show that both the Co3O4 and Co4N spheres are porous structure. The high crystallinity of Co4N spheres is corroborated by the high-resolution (HRTEM) image in Figure 1d. The fringe spacing of 0.203 nm corresponds to the (111) spacing (0.205nm) of Co4N.43 The pore size distribution and specific surface area of the Co3O4 spheres and Co4N spheres were used by N2 adsorption-desorption isotherms. As shown in Figure 2, both samples reflect quite similar N2 sorption isotherms and pore size distribution curves. The Brunauer-EmmettTeller (BET) specific surface areas of Co3O4 spheres and Co4N spheres are 51.2 m2 g-1 and 48.4 m2 g-1, and the pore volume are 0.254 cm3 g-1 and 0.237 cm3 g-1, respectively. The specific surface areas and pore volume of Co3O4 spheres is slightly higher than Co4N spheres. The high specific surface area and large pore volume can provide abundant pore structure to stockpile sulphur, more adsorption and catalytic sites for polysulphide, thus significantly improving the specific capacity and cycling stability for lithium-sulfur battery. Many metal oxides and metal nitride were reported to have strong adsorption for polysulfide and would "trap" the lithium polysulfides (LiPSs) in the cathodes instead of shuttling to the anode. This will reduce the “shuttle effect” and improve the cycle stability of lithium-sulfur battery. To further illustrate the affinity for polysulfide, a visual discrimination has been used and the Li2S6 was utilized as the representative polysulphide. Co3O4 spheres, Co4N spheres and super P with the same quality were first added into a solution of Li2S6 in DOL/DME solvent. As shown in Figure 3a, the excellent intrinsic capability of Co4N spheres to adsorb Li2S6 was


6

Page 7 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

obvious. After adding Co4N spheres, the yellow Li2S6 solution was completely changed to colourless after 1 h. And after 3h, the colour of Li2S6 solution added with Co3O4 spheres became lighter but not complete obliteration. Whereas the one after adding Sup P remained yellow, indicating that there is still a large amount of Li2S6 in the solution. It showed that although the Co3O4 spheres have higher specific surface area than Co4N spheres, Co4N spheres exert a stronger and faster adsorption for polysulfide. Raman spectroscopy was used to measure the blank solution (DOL&DME), Li2S6 solution, Li2S6 solution added Sup P, Li2S6 solution added Co3O4 spheres and Li2S6 solution added Co4N spheres after 3 h, respectively. According to the comparative analysis of Li2S6 solution and blank one in Figure 3b, the former has two additional peaks at 218 cm-1 and 478 cm-1, which are characteristics of Li2S6. The Raman spectra of Li2S6 solution added with Sup P are similar to that of Li2S6 solution, which still have two peaks at 218 cm-1 and 478 cm-1. In the spectra of Li2S6 solution with Co3O4 spheres, the peaks of Li2S6 are weaker than that of Sup P, but the peak at 218 cm-1 still exists. And on the spectra of that added with Co4N spheres, there are no obvious peaks appearing at 218 cm-1 or 478 cm-1. That is because Li2S6 in the solution is almost completely adsorbed by the Co4N spheres and there is no Li2S6 species in the solution, indicating that Co4N spheres have a high affinity for LiPSs. In terms of kinetics, not only the affinity but also the trapping speed, which has not been paid attention to yet, is crucial for sulfur redox processes. So the trapping speed was also investigated here. Figure 3c and d were the visual discrimination by taking Li2S6 and Raman spectroscopy after 12h. Both the Li2S6 solution added with Co3O4 spheres and Co4N spheres became colourless; the peak at 218 cm-1 in the Raman spectra of Li2S6 solution with Co3O4 spheres disappeared. It proved Co3O4 spheres have stronger affinity for polysulfide than carbon materials, but compared with Co4N spheres, the Co4N spheres showed higher adsorption rate for LiPSs. The stronger and


7

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 30

faster adsorption for LiPSs may make Co4N sphere become a promising host material of S cathode for Li-S battery. Sulfur was incorporated into the Co4N spheres by melt diffusion under 155°C. Thermogravimetric analysis (TGA) in Figure S4 shows that all of the sulfur is retained in the Co4N/S sample after melting diffusion treatment, yielding a 72.32 wt% composite. Figure S6 shows the characterization of the Co4N/70S sample. The XRD results shown in Figure S6 prove the presence of sulphur in the sample. As the SEM images in Figure S6 b and c illustrated, the surface of Co4N/70S become smoother than that of Co4N spheres, and there are a few additional sulfur particles in the sample, most of the sulphur is distributed in the framework of Co4N spheres. In order to further confirm the distribution pattern of S in the sample, the SEM corresponding element mapping of Co, N and S are revealed in Fig. S5 d-g. The elemental distribution maps on a single Co4N/70S spheres clearly reveal the distribution of elemental S is on the Co4N spheres surface. To evaluate the electrochemical properties of the Co4N/70S composites with 72.3 wt% sulphur, the cell was cycled from 1.7 to 2.7 V versus Li/Li+ (Figure 4). The galvanostatic discharge and charge curves of the first cycle at 0.1 C show that such composites could deliver a very high specific discharge capacity of 1659 mAh g-1 at this rate, which is very close to the theoretical capacity of sulphur (1675 mAh g-1). Then the Co4N/70S shows excellent rate performance and high specific capacity as shown in Figure 4a. Under the current densities of 0.1 C, 0.2 C, 0.5 C, 1 C, 2 C and 5 C, the Co4N/70S shows first cycle discharge specific capacities of 1659 mAh g-1, 1441 mAh g-1, 1342 mAh g-1, 1280 mAh g-1, 1213 mAh g-1 and 1144 mAh g-1, respectively. Even the current density is as high as 8.4 A g-1 (5 C), the first cycle discharge specific capacity can still maintain at 1144 mAh g-1, equivalent 68.3% to the theoretical capacity of sulphur.


8

Page 9 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Fig.4b shows the rate properties of Co4N/70S electrode at different current rates. When the current densities increase from 0.1C to 0.2 C, 0.5 C, 1 C and 2 C, the reversible capacities are 1657 mAh g-1, 1299 mAh g-1, 1141 mAh g-1, 1010 mAh g-1 and 882 mAh g-1, respectively. After the high rate cycling, the current density returns to 0.1 C. An extremely high specific discharge capacity of 1334 mAh g-1 is recovered, which is close to that in the beginning. Besides the good rate performance and high specific capacity, the Co4N/70S also shows excellent cycling stability at various rates. When the current density was 0.1 C, the discharge capacity was above 1300 mAh g-1 after 20 cycles. The charge/discharge capacity and Coulombic efficiency versus cycle number at current density of 0.5 C and 1 C is shown in Figure 4d. At the current density of 0.5 C, the Coulombic efficiency of the first cycle was above 99.5% and finally remains at nearly 100%. Co4N/70S delivered a discharge capacity above 1100 mAh g-1 at 0.5 C and above 1000 mAh g-1 at 1 C after 100 cycles. And after 500 cycles, the discharge capacity can still stabilized at about 930 mAh g-1 at 1C (as shown in Figure S6). Figure 4e shows an excellent cycling stability at high current densities of 2 C and 5 C, the discharge capacity finally stabilized at 805 mAh g-1 and 585 mAh g-1 after 300 cycles, respectively. Even the cycle number was upgrade to 1000, the capacity can still keep at 761 mAh g-1 and 494 mAh g-1, respectively. The discharge capacity, rate capability and cycling stability of Co4N/S is very rare in the current studies of Li-S batteries (as shown in Table S1 and S2). In order to further study the effects of Co4N for lithium−sulfur batteries, we compared the 1st cycle charge and discharge processes of the Co4N/S, Co3O4/S, Co/S and sup P/S. Figure S4 shows the TGA curves of these composites, the sulfur content of these composites were about 73%. Figure 5a and b are the 1st charge and discharge voltage profiles for the first cycle at 0.1 C and 1 C for the four composites, respectively. Each of the composites shows a typical voltage


9

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 30

and capacity profile for Li-S batteries. There are two voltage plateaus in the discharge process. The first plateau at 2.35 V is attributed to the reduction of cyclo-S8 to solvable long-chain Li2Sn (4≤n≤8), and the second plateau at 2.1 V corresponds to the further reduction of the high-order Li2S4 to Li2S2 and eventually to Li2S. The first process of discharge occurs relatively fast, the four composites performed similar discharge capacity at this process. But at the second plateau, they exhibit distinct differences. The first cycle discharge capacity of Co4N/S, Co3O4/S, Co/S and sup P/S at 0.1C were 1657 mAh g-1, 1292 mAh g-1, 1584 mAh g-1 and 1405 mAh g-1, respectively. The discharge capacity of Co4N/S is close to the theoretical capacity of S, and Co/S also shows a rather high capacity of the 1st cycle at 0.1 C. They are all much higher than the capacity of sup P/S and Co3O4/S. And at high current densities such as 1C, this phenomenon is more distinct. So it can be inferred that in comparison with carbon materials, Co4N spheres could more effectively improve the initial discharge capacity of Li-S battery. What is more, this significant improvement mainly depends on the promote of the capacity of the lower plateau, which suggests that Co4N sphere can catalyze the process of reduction the Li2S4 to Li2S2 and eventually, to Li2S. The Co element of low valence in the Co4N play a major role in this catalytic process. This may be attributed to the valence state of the Co ions in Co4N not at the full oxidation valence +3; they are highly capable of donating electrons which leads to a strong affinity for sulfur atoms/ions in the LiPSs. In order to study the chemical composition in the Co4N, X-ray photoelectron spectroscopy (XPS) was used. Figure 5c is the XPS of Co 2p3/2 in Co4N and Co4N/Li2S6, respectively. The spectrum showed that Co 2p3/2 in Co4N can be divided into two characteristic peaks located at 780.3 eV and 778.3 eV, respectively. The peak located at 778.3 eV is corresponding to metallic cobalt, confirming the existence of cobalt with 0 valency. And the peak at 780.3 eV could be assigned to the Co-N bond. After adsorbing Li2S6, the Co


10

Page 11 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

2p3/2 spectrum has an additional peak at 778.9 eV, indicative of Co-S bond,44 and the intensity of former peaks recede, especially the peak around 778.5 eV. This suggests that the cobalt with low valency in Co4N has a strong chemical affinity for sulfur in the LiPSs. Figure 5d shows the 1st cyclic voltammetric curve of the Co4N/S, Co3O4/S and sup P/S cell in the range of 1.7–2.7 V at a scan rate of 0.05 mV s-1. All the samples show similar charge and discharge profiles: two characteristic reduction peaks observed are attributed to the reduction of the cyclo-S8 to long-chain Li2Sn, then formation of Li2S2 and Li2S, respectively. On forward scan, broad oxidation peak at about 2.5 V is attributed to the conversion of short-chain to longchain LiPSs. The CV of Co4N/S is compared with that of sup P/S; there is nearly no obvious shift in reduction peak, but the distinguishable negative shift in oxidation peak indicates that the Co4N sphere can facilitate the oxidation of short-chain to long-chain LiPS, thus improving the S utilization and increasing the capacity of charge process. And there is almost no obvious shift in oxidation peak compared with Co/S and Sup P/S. This result indicates better redox reactions taking place at the Co4N electrode. As the first discharge and charge voltage profiles shown in Figure 5b, the same situation can be seen: the oxidation plateau of Co4N/S electrode is much lower than that of Sup P/S electrode. It can be attributed to Co4N sphere that has a stronger adsorption ability than LiPSs, which catalyzes the reactions from short-chain to long-chain LiPSs and then to S8. It was reported in our previous work that one electron lone pair of the N atom can serve as a conductive Lewis base “catalyst” matrix to enhance the adsorption energy of Li in the Li2Sn (n = 4–8), which facilitates the oxidization of LiPSs.9,15,31 The fast oxidation process could lead to a better charge capacity, then improves the Coulombic efficiency. The charge capacity of Co4N/S cell at 0.1 C was 1655 mAh g-1, nearly the theoretical capacity of S. And the Coulombic efficiency of the 1st cycle was as high as 99.9%. On the other hand, the charge


11

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 30

capacity of Co/S and sup P/S was 1470 mAh g-1 and 1315 mAh g-1, respectively. The Coulombic efficiency was only 92.8% and 93.6%. The Co and N in Co4N have strong adsorption capacity for both S and Li in LiPSs, respectively. So the bifunctional catalytic activities of Co4N spheres can both increase the discharge and charge capacity for lithium−sulfur battery, and improve the Coulombic efficiency. The fast and strong affinity of Co4N spheres for polysulfide can reduce the “shuttle effect” during the discharge/charge process, so the Co4N/S electrode exhibits high capacity, good rate performance and excellent cycling stability. Compared with the discharge capacity of Co3O4/S and Co/S composites under the current density of 1C, as shown in Figure 5e, the capacity of Co4N/S is about 1000 mAh g-1 and there is nearly no obvious capacity fading from 4 to 100 cycles. Because the Co3O4 spheres have relatively strong affinity for polysulfide in comparison with carbon materials, it shows a satisfactory cycling stability for Li-S battery. But the capacity is much lower than Co4N/S; it stabilizes at about 650 mAh g-1. The Co/S composite shows a higher discharge capacity than Co3O4/S at first, but the weak Coulombic efficiency leads to worse cycling stability-the capacity fell fast and after 100 cycles there was only less than 600 mAh g-1 left. Figure S7 shows that the rate performance of Co4N/S cathode is far superior than the other composite cathodes. And the XPS of S element in the metal lithium anode and electrolyte after 100 cycles (Figure S8 and S9) shows that the Co4N can efficient reduce the “shuttle effect” during the discharge and charge process. The Co4N spheres not only have stronger affinity for polysulfide than Co3O4, but can also adsorb more polysulfide than Co3O4. Figure 6a and b show the visual discrimination by comparing 5 mg, 10 mg, 20 mg, 30 mg of Co4N spheres and Co3O4 spheres, respectively, added in the Li2S6 solution. After 12 h, all the Li2S6 solution containing Co4N spheres become almost


12

Page 13 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

colourless, but only the solution added with 30 mg Co3O4 spheres become colourless. The color of other solution only became shallow, indicating that there were still leftover of Li2S6 species in the solution. The excellent adsorb capacity of Co4N spheres for polysulfide may lead a good electrochemical performance for Li-S battery even at a high loading of insulating sulfur. When the weight ratio of elemental S and Co4N spheres was set to 9:1, the TGA curve showed the S content in this sample is 89.64 wt% (Figure S10, named as Co4N/90S). However, as was expected, the Co4N/90S electrode also exhibited an outstanding electrochemical property (as shown is Figure 6). At the rate of 0.1 C, the initial discharge capacity of the Co4N/90S electrode could achieve at 1428 mAh g−1. When the rate increase to 2C, the Co4N/90S electrode still can release a high discharge specific capacity of 720 mAh g−1, and this is an excellent result comparing to the recent reports. In addition to good rate performance, the Co4N/90S cathode also shows excellent cycling stability and high specific capacity at various rates. At the current rate of 0.5 C, the Co4N/90S cathode could deliver a high initial discharge capacity of 1201 mAh g−1, and this capacity was still remained at 920 mAh g−1 after 100 cycles. And at a large rate of 1 C, after 100 cycles, the reversible specific capacity was as high as 801 mAh g−1. Even the current densities increase to 2 C and 5 C, there was still a discharge capacity finally stabilizing at 670 mAh g-1 and 520 mAh g-1 after 300 cycles. Even the cycle number was upgrade to 800, the capacity can still keep at 690 mAh g-1 and 440 mAh g-1, respectively. Compared with the discharge capacity of Co3O4/90S composite (the same melt-diffusion process as Co4N/90S) under the current density of 1C, (when the sulfur content was 70%wt, the Co3O4/S shows the satisfactory cycling stability) when sulfur content was increased to 90%wt, cycling stability of Co3O4/S became worse, the capacity decreased rapidly and after 100 cycles there was only about


13

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 30

450 mAh g-1remained. This indicates the hollow Co4N mesoporous sphere is conducive to immobilize sulfur and assuage the dissolve of polysulfide at ultrahigh sulfur content. Even after increasing the weight ratio of elemental sulfur and Co4N spheres to 19:1 (sulfur content is 94.88%, named as Co4N/95S), the Co4N/S cathode still exhibited excellent electrochemical properties. As shown in Figure 5, the Co4N/95S cathode could exhibit an extremely high specific discharge capacity of 1259 mAh g-1 at 0.1C. After 100 cycles at 1C, the Co4N/S cathode also maintained a high specific capacity of 640 mAh g-1 and after 800 cycles at 2 C, the discharge capacity still remained at 540 mAh g-1. Compared with the Co3O4/90S cathode, there is a greatly improvement in the specific capacity and cycling stability, and this is a very high level at present researches (Table S3). CONCLUSIONS In summary, Co4N mesoporous sphere presents a uniform distribution and the displayed porous structure has been successfully synthesized via an easy and convenient method. With high affinity, speedy trapping, much absorbing capacity for polysulfides as well as the bifunctional catalyzing for sulfur redox processes, this Co4N sphere has proven to be an ideal matrix for sulfur active material. When Co4N sphere composited with 72.32 wt% sulfur is evaluated as a cathode material for lithium−sulfur battery, it exhibited large specific discharge capacity of 1659 mAh g-1 at 0.1 C, high Coulombic efficiency, good rate capability, and excellent cycling performance with reversible capacity of 1000 mAh g-1 at 1 C after 100 cycles. Even at increased 9:1 and 19:1 weight ratio of elemental sulfur and Co4N spheres (90% and 95 wt% S loadings), the discharge capacity of first cycle is still as high as 1428 mAh g-1 and 1259 mAh g-1, respectively. The reversible capacity at 2C after 800 cycles were above 690 mAh g-


14

Page 15 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

1

and 540 mAh g-1, respectively. The facile approach and its results could be used to guide the

realization of S-based high energy density batteries. EXPERIMENTAL SECTION Synthesis of Co3O4 Spheres: All chemicals were analytical grade and used without further purification. 2 g Co(CH3COO)2 and 0.2g PVP (Mw=18000 g mol-1) was dissolved into 160 mL ethylene glycol. After stirred for 3 h, the mixture was then transferred into an autoclave and maintained at 200°C for 12 h. Then the reactant was cooled to room temperature. The precipitate was collected by centrifugation, then washed with ethanol and distilled water several times. Subsequently dried at 50 °C, then calcined at 550 °C in a temperature-programmed muffle furnace for 4 h in air to get the Co3O4 Spheres. Synthesis of Co4N Spheres: The as-prepared Co3O4 Spheres were heated to 400 °C in ammonia atmosphere for 4 h with a slow heating ramp (room temperature to 300 °C, 5 °C min-1; 300 to 400 °C, 1 °C min-1). After being cooled to room temperature, mesoporous Co4N Spheres were thus obtained. Synthesis of Co nanoparticles: The Co3O4 Spheres were heated to 700 °C in ammonia atmosphere for 4 h with a slow heating ramp (room temperature to 600 °C, 5 °C min-1; 600 to 700 °C, 1 °C min-1). After being cooled to room temperature, Co nanoparticles were thus obtained. Preparation of the Sulphur composites: The Co4N/S composite was prepared via the classical melt-diffusion method. First, the required amount of elemental sulfur and mesoporous Co4N spheres (3:1 by mass) were mixed thoroughly by grinding. Then the mixture was heated at


15

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 30

155 °C for 6 h and cooled to room temperature. The Co3O4/S, Co/S, Sup P/S composite was prepared by the same method as Co4N/S one. Polysulphide adsorption sample preparation: The 5 mM Li2S6 solutions were prepared by dissolving appropriate amounts Li2S6 into 5 ml DOL/DME solvent in five vials with same volume. 30 mg Sup P, mesoporous Co4N and Co3O4 spheres were then added to there different vials, respectively. All procedures were completed in an Ar-filled glovebox. Characterization of the materials: X-ray diffraction (XRD) patterns of the samples were recorded on a Philips analytical X-pert diffractometer with Cu Ka radiation (λ = 0.1548 nm) at 40 kV and 30 mA and a step of 0.02. Data were recorded ranging from 20 to 80 degree. Scanning electron microscopy (SEM) was performed on a Hitachi S-4800 scanning electron microscope at an accelerating voltage of 15 kV. Transmission electron microscopy (TEM) observations were carried out FEI Tecnai F30 microscopes at 300 kV. Thermogravimetric (TG) analysis was carried out on a Perkin Elmer instrument. Nitrogen adsorption and desorption isotherms at 77 K were characterized by a Micromeritics Tristar 3020 analyzer surface area and pore-size analyzer. Raman spectra were performed using a XploR Raman microscope with an excitation wavelength of 785 nm. Electrochemical measurements: To evaluate the electrochemical properties of the Co4N/S composite as a cathode material, its electrochemical testing was constructed. The cathode electrode consists of 70 wt% active material (sulfur composites), 20 wt% super P, and 10 wt% binder (LA). All test cells were assembled in an Ar-filled glove box. Celgard 2400 as the separator, Li foils were used as the counter electrode, and the electrolyte was 0.5 M LiCF3SO3 & 0.5 M LiNO3 (dissolved in 1,2-dimethoxyethane and dioxolane with a 1:1 volume ratio). The


16

Page 17 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

areal mass loading of sulfur in electrode was about 1.5-2 mg cm-2 (70% wt S loading) and 2.4-2.8 mg cm-2 (90% wt S loading), and 40 µL electrolyte was added into the CR2016 type coin cells. These cells were cycled on a NEWARE BTS-5 V/20 mA type battery chargers (Shenzhen, China) testing system at room temperature, and the galvanostatic charge-discharge cycling with a voltage window of 1.7–2.7 V. The cell without any activation when current densities blew 1 C. And the cell wll be a activation at a 0.1 C rate for 3 cycles when the current densities were 1 C, 2 C and 5 C. FIGURES

Scheme1 ： Schematic illustration of Co4N sphere and its interaction with LiPSs during discharge/charge process of the lithium-sulfur battery.


17

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 30

Figure 1. SEM images of Co3O4 phase (a, b), and Co4N phase (c, d). HRTEM image of the Co4N is presented in the inset of 1d.

Figure 2. N2 adsorption-desorption isotherm loop and pore-size distribution plot of Co3O4 phase and Co4N phase.


18

Page 19 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Figure 3. Sealed vials of a lithium polysulfides solution (Li2S6 dissolved in DOL/DME solvents) containing Sup P, Co3O4 phase, Co4N phase and blank electrolyte quiescence after 3h (a) and 12h (c). The Raman spectra of solution of blank solution without Li2S6, Li2S6 solution, Li2S6 solution added Sup P, Co3O4 phase and Co4N phase after 3 h (b) and 12 h (d), respectively.


19

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 30

Figure 4. (a) Charge and discharge voltage profiles for the first cycle at current densities of 0.1 C, 0.2 C, 0.5 C, 1 C, 2 C, and 5 C. (b) Rate capability of Co4N/70S at different current rates. (c) (d) the charge and discharge capacity and Coulombic efficiency versus cycle number at current densities of 0.1 C, 0.5 C and 1 C (e) The charge and discharge capacity versus cycle number at current densities of 2 C and 5 C.


20

Page 21 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Figure 5. First charge and discharge voltage profiles of Co4N/S, Co3O4/S, Co/S and sup P/S electrodes at 0.1 C (a) and 1 C (b). (c) Co 2p3/2 X-ray photoelectron spectroscopy (XPS) of the Co4N phase and Co4N/Li2S6, respectively. (d) First CV Co4N/S, Co3O4/S, Co/S and sup P/S at a scan rate of 0.05 mV s −1. (e) The discharge capacity of Co4N/S, Co3O4/S, Co/S versus cycle number at a current density of 1 C.


21

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 30

Figure 6. Sealed vials of a lithium polysulfides solution (Li2S6 dissolved in DOL/DME solvents) containing 5 mg, 10 mg, 20 mg, 30 mg Co4N phase (a) and Co3O4 phase (b) after 12 h, respectively.


22

Page 23 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Figure 7. (a) Rate capability of Co4N/90S and Co4N/95S at different current rates. (b) The discharge capacity of Co4N/90S at 0.5C and Co4N/90S, Co4N/95S, Co3O4/90S versus cycle number at a current density of 1 C. (c) the charge and discharge capacity of Co4N/90S versus cycle number at current densities of 2 C and 5 C, Co4N/95S at 2 C.

ASSOCIATED CONTENT Supporting Information. The Supporting Information is available free of charge on the ACS Publication website.


23

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 30

Additional XRD,TEM, XPS,EDX, TG and electrochemical performance (PDF)

AUTHOR INFORMATION Corresponding Author *E-mail: [email protected], [email protected] Notes The authors declare no competing financial interest. ACKNOWLEDGMENT We acknowledge financial support from the National 973 Program (2015CB251102), the Key Project of NSFC (U1305246, 21321062) and the NFFTBS (No. 20720150042).

REFERENCES (1)

Owen, J. R. Rechargeable Lithium Batteries. Chem. Soc. Rev. 1997, 26, 259–267.

(2)

Tarascon, J. M.; Armand, M. Issues and Challenges Facing Rechargeable Lithium

Batteries. Nature 2001, 414, 359–367. (3)

Ellis, B. L.; Lee, K. T.; Nazar, L. F. Positive Electrode Materials for Li-Ion and Li-

Batteries. Chem. Mater. 2010, 22, 691–714. (4)

Etacheri, V.; Marom, R.; Elazari, R.; Salitra, G.; Aurbach, D. Challenges in the

Development of Advanced Li-Ion Batteries: a Review. Energy Environ. Sci. 2011, 4, 3243–3262. (5)

Goodenough, J. B.; Park K.-S. The Li-Ion Rechargeable Battery: A Perspective. J. Am.


24

Page 25 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Chem. Soc. 2013, 135, 1167–1176. (6)

Peled, E.; Gorenshtein, A.; Segal, M. S.; Sternberg, Y. Rechargeable Lithium-Sulfur

Battery (Extended Abstract). J. Power Sources 1989, 26, 269–271. (7)

Yang, Y.; Zheng, G. Y.; Cui Y. Nanostructured Sulfur Cathodes. Chem. Soc. Rev. 2013,

42, 3018–3032. (8)

Manthiram, A.; Fu, Y.; Su, Y.-S. Challenges and Prospects of Lithium-Sulfur Batteries.

Acc. Chem. Res. 2012, 46, 1125–1134. (9)

Li, Y. J.; Fan, J. M.; Zheng, M. S.; Dong, Q. F. A Novel Synergistic Composite with

Multi-Functional Effects for High-Performance Li-S Batteries. Energy Environ. Sci. 2016, 9, 1998–2004. (10)

Li, Z.; Zhang, J. T.; Chen, Y. M.; Lou, X. W. Pie-Like Electrode Design for High-Energy

Density Lithium-Sulfur Batteries. Nat. Commum. 2015, 6, 8850. (11)

Yin, Y. X.; Xin, S.; Guo, Y. G.; Wan, L. J. Lithium-Sulfur Batteries: Electrochemistry,

Materials, and Prospects. Angew. Chem. Int. Ed. 2013, 52, 13186–13200. (12)

Bresser, D.; Passerini, S.; Scrosati, B. Recent Progress and Remaining Challenges in

Sulfur-Based Lithium Secondary Batteries-a Review. Chem. Commun. 2013, 49, 10545–10562. (13)

Mikhaylik, Y. V.; Akridge, J. R. Polysulfide Shuttle Study in the Li/S Battery System. J.

Electrochem. Soc. 2004, 151, A1969 –A1976. (14)

Su, Y. S.; Manthiram, A. Lithium-Sulphur Batteries with a Microporous Carbon Paper as

a Bifunctional Interlayer. Nat. Commun. 2012, 3, 1166. (15)

Chen, J.-J.; Yuan, R.-M.; Feng, Fu, G.; Zheng, M.-S.; Ren, B.; Dong, Q.-F., Conductive

Lewis Base Matrix to Recover the Missing Link of Li2S8 during the Sulfur Redox Cycle in Li-S Battery. Chem. Mater. 2015, 27, 2048–2055.


25

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(16)

Page 26 of 30

Wang, Z.; Dong, Y.; Li, H.; Zhao, Z.; Lou, X. W. Enhancing Lithium-Sulphur Battery

Performance by Strongly Binding the Discharge Products on Amino-Functionalized Reduced Graphene Oxide. Nat. Commun. 2014, 5, 5002. (17)

Ji, X. L.; Lee, K. T.; Nazar, L. F. A Highly Ordered Nanostructured Carbon–Sulphur

Cathode for Lithium-Sulphur Batteries. Nat. Mater. 2009, 8, 500–506. (18)

Schuster, J.; He, G.; Mandlmeier, B.; Nazar, L. F. Spherical Ordered Mesoporous Carbon

Nanoparticles with High Porosity for Lithium-Sulfur Batteries. Angew. Chem. Int. Ed. 2012, 51, 3591–3595. (19)

Chung, S. H.; Chang, C. H.; Manthiram, A Carbon-Cotton Cathode with Ultrahigh

Loading Capability for Statically and Dynamically Stable Lithium-Sulfur Batteries. ACS Nano 2016, 10, 10462–10470. (20)

Chen, H. W.; Wang, C. H.; Chen, L. W. Monodispersed Sulfur Nanoparticles for Lithium-

Sulfur Batteries with Theoretical Performance. Nano. Lett. 2015, 15, 798–802. (21)

He, G.; Ji, X. L.; Nazar. L. F. High “C” Rate Li-S Cathodes: Sulfur Imbibed Bimodal

Porous Carbons. Energy Environ. Sci. 2011, 4, 2878–2883. (22)

Liang, C. D.; Dudney, N. J.; Howe, J. Y. Hierarchically Structured Sulfur/Carbon

Nanocomposite Material for High-Energy Lithium Battery. Chem. Mater. 2009, 21, 4724–4730. (23)

Zhou, W.; Xiao, X.; Cai, M.; Yang, L. Polydopamine-Coated, Nitrogen-Doped, Hollow

Carbon-Sulfur Double-Layered Core-Shell Structure for Improving Lithium-Sulfur Batteries. Nano Lett. 2014, 14, 5250–5256. (24)

Pang, Q.; Kundu, D.; Cuisinier, M; Nazar, L. F. Surface-Enhanced Redox Chemistry of

Polysulphides on a Metallic and Polar Host for Lithium-Sulphur Batteries. Nat. Commun. 2014, 5, 4795.


26

Page 27 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

(25)

Tao, X.; Wang, J.; Ying, Z.; Cai, Q.; Zheng, G.; Zhang, W.; Cui, Y. Strong Sulfur

Binding with Conducting Magnéli-Phase TinO2n-1 Nanomaterials for Improving Lithium-Sulfur Batteries. Nano Lett. 2014, 14, 5288–5294. (26)

Seh, Z. W.; Li, W. Y.; Cha, J. J.; Cui, Y. Sulphur-TiO2 Yolk-Shell Nanoarchitecture with

Internal Void Space for Long-Cycle Lithium-Sulphur Batteries. Nat. Commum. 2013, 4, 1331. (27)

Liang, X.; Hart, C.; Pang, Q.; Garsuch, A.; Weiss, T.; Nazar, L. F. A Highly Efficient

Polysulfide Mediator for Lithium-Sulfur Batteries. Nat. Commun. 2015, 6, 5682. (28)

Li, Z.; Zhang, J.; Lou, X. W. Hollow Carbon Nanofibers Filled with MnO2 Nanosheets as

Efficient Sulfur Hosts for Lithium-Sulfur Batteries. Angew. Chem. Int. Ed. 2015, 54, 12886– 12890. (29)

Zhang, J. T.; Hu, H.; Li, Z.; Lou, X. W. Double-Shelled Nanocages with Cobalt

Hydroxide Inner Shell and Layered Double Hydroxides Outer Shell as High-Efficiency Polysulfide Mediator for Lithium-Sulfur Batteries. Angew. Chem. Int. Ed. 2016, 55, 3982–3986. (30)

An. T. H.; Deng, D. R.; Wu, Q. H.; Zheng, M. S.; Q. F. Dong, MnO Modified Carbon

Nanotubes as a Sulfur Host with Enhanced Performance in Li/S Batteries. J. Mater. Chem. A 2016, 4, 12858–12864. (31)

Deng, D. R.; An, T. H.; Zheng, M. S.; Dong, Q. F. Hollow Porous Titanium Nitride

Tubes as a Cathode Electrode for Extremely Stable Li-S Batteries. J. Mater. Chem. A 2016, 4, 16184–16190. (32)

Cui, Z. M.; Zu, C. X.; Zhou, W. D.; Goodenough, J. B. Mesoporous Titanium Nitride-

Enabled Highly Stable Lithium-Sulfur Batteries. Adv. Mater. 2016, 28, 6926–6931.


27

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(33)

Page 28 of 30

Lyu, Z.; Xu, D.; Yang, L.; Che, R.; Feng, R.; Hu, Z. Hierarchical Carbon Nanocages

Confining High-Loading Sulfur for High-Rate Lithium-Sulfur Batteries. Nano Energy 2015, 12, 657–665. (34)

Du, W. C.; Yin, Y. X.; Zeng, X. X.; Shi, J. L.; Zhang, S. F.; Wan, L. J.; Guo, Y. G. Wet

Chemistry Synthesis of Multidimensional Nanocarbon-Sulfur Hybrid Materials with Ultrahigh Sulfur Loading for Lithium-Sulfur Batteries. ACS Appl. Mater. Interfaces 2016, 8, 3584–3590. (35)

Zhou, G.; Li, L.; Ma, C.; Wang, S.; Shi, Y.; Koratkar, N.; Ren, W.; Li, F.; Cheng, H. A

Graphene Foam Electrode with High Sulfur Loading for Flexible and High Energy Li-S Batteries. Nano Energy 2015, 11, 356–365. (36)

Zheng, Z. M.; Guo, H. C.; Fang, X. L.; Zheng, N. F., High Sulfur Loading in Hierarchical

Porous Carbon Rods Constructed by Vertically Oriented Porous Graphene-Like Nanosheets for Li-S Batteries. Adv. Funct. Mater. 2016, 26, 8952–8959. (37)

Fang, R. P.; Zhao, S. Y.; Liu, C.; Li, F. 3D Interconnected Electrode Materials with

Ultrahigh Areal Sulfur Loading for Li-S Batteries. Adv. Mater. 2016, 28, 3374–3382. (38)

Qie, L.; Zu, C. X.; Manthiram, A. A High Energy Lithium-Sulfur Battery with Ultrahigh-

Loading Lithium Polysulfide Cathode and its Failure Mechanism. Adv. Energy Mater. 2016, 6, 1502459. (39)

Yuan, Z; Peng, H.-J.; Huang, J.-Q.; Zhang, Q. Hierarchical Free-Standing Carbon-

Nanotube Paper Electrodes with Ultrahigh Sulfur-Loading for Lithium–Sulfur Batteries. Adv. Funct. Mater. 2014, 24, 6105–6112.


28

Page 29 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

(40)

Li, M. Y.; Carter, R.; Douglas, A.; Oakes, L.; Pint, C. L. Sulfur Vapor-Infiltrated 3-D

Carbon Nanotube Foam for Binder-Free High Areal Capacity Lithium Sulfur Battery Composite Cathodes. ACS Nano 2017, 11, DOI: 10.1021/acsnano.7b01437. (41)

Sun, K.; Cama, C. A.; Takeuchi, E. S.; Gan, H. Effect of Carbon and Binder on High

Sulfur Loading Electrode for Li-S Battery Technology. Electrochim. Acta 2017, 235, 399–408. (42)

Chen, P. Z.; Xu, K.; Fang, Z. W.; Wu, C. Z.; Xie, Y. Rapid Synthesis of Cobalt

Nitride Nanowires: Highly Efficient and Low-Cost Catalysts for Oxygen Evolution. Angew. Chem. Int. Ed. 2015, 54, 14923–14927. (43)

Theerthagiri, J.; Dalavi, S. B.; Panda, R. N., Magnetic Properties of Nanocrystalline ɛ-

Fe3N and Co4N Phases Synthesized by Newer Precursor Route. Materials Research Bulletin. 2013, 48, 4444–4448. (44)

Alstrup, I.; Chorkendorff, I.; Candia, R.; Clausen, B.; Topsoe, H. A Combined X-Ray

Photoelectron and Mössbauer Emission Spectroscopy Study of the State of Cobalt in Sulfided, Supported, and Unsupported Co/Mo Catalysts. J. Catal. 1982, 77, 397–399.


29

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 30

For Table of Contents Only


30