Complete Oxidation of Methane on NiO Nanoclusters Supported on

Mar 5, 2018 - Here a nanocomposite catalyst (NiO/CeO2) consisting of CeO2 nanorods and supported NiO nanoclusters was prepared by a two-step ...
1 downloads 0 Views 1MB Size
Subscriber access provided by UNIV OF NEW ENGLAND ARMIDALE

Complete Oxidation of Methane on NiO Nanoclusters Supported on CeO2 Nanorods through Synergistic Effect Xiaoyan Zhang, Stephen D. House, Yu Tang, Luan Nguyen, Yuting Li, Adedamola A. Opalade, Judith Yang, Zaicheng Sun, and Franklin (Feng) Tao ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.8b00234 • Publication Date (Web): 05 Mar 2018 Downloaded from http://pubs.acs.org on March 8, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 32 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Complete Oxidation of Methane on NiO Nanoclusters Supported on CeO2 Nanorods through Synergistic effect Xiaoyan Zhang,abc Stephen House,e Yu Tang,c Luan Nguyen,c Yuting Li,c Adedamola A. Opalade,c Judith C. Yang,e Zaicheng Sun,d* Franklin (Feng) Taoc* a

State Key Laboratory of Luminescence and Applications, Changchun Institute of Optics, Fine Mechanics and Physics, Changchun, 130033 Jilin, P. R. China b University of Chinese Academy of Sciences, Beijing 100000, P. R. China c Department of Chemical and Petroleum Engineering and Department of Chemistry, University of Kansas, Lawrence, KS, 66045, USA d School of Chemistry, Beijing University of Technology, Beijing, 100080, P. R. China e Department of Chemical and Petroleum Engineering, University of Pittsburgh, PA, 15261, USA

Abstract Catalytic complete oxidation of CH4 at relative low temperatures is significant for removal of unburned CH4 in exhaust of combustion engines fueled with natural gas or liquefied petroleum gas. Here the nanocomposite catalyst (NiO/CeO2) consisting of CeO2 nanorods and supported NiO nanoclusters was prepared by a two-step wet-chemistry method. This nanocomposite catalyst exhibits high catalytic activity for complete oxidation of CH4 in the temperature range of 350-600 oC. CH3-like intermediate bound to Ni cations was observed at a relatively low temperature by ambient pressure Xray photoelectron spectroscopy under a catalytic condition. Parallel kinetic studies of NiO/SiO2, CeO2 and NiO/CeO2 catalysts show that the apparent barrier for complete oxidation of CH4 on NiO/CeO2 (69.4±4KJ/mol) is much lower than 95.1±5 kJ/mol of pure CeO2 and 98.4±5 kJ/mol of NiO/SiO2, supported by the turn-over frequency of NiO/CeO2 significantly higher than NiO and CeO2. These differences show a synergic effect between CeO2 nanorods and its supported NiO nanoclusters. This synergic effect results from the interface of NiO and CeO2 observed in TEM. The lattice oxygen atoms at the interface exhibits high activity based on the lower reduction temperature uncovered in the studies of temperature-programmed reduction of H2. *: To whom all correspondence should be addressed to. Email: [email protected] (FT) and [email protected] (SZ) KEYWORDS: NiO, CeO2, methane, complete oxidation, AP-XPS

ACS Paragon Plus Environment

1

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 32

Introduction CH4 is one of the main gas components in exhaust of vehicles using natural gas or liquefied petroleum gas as fuels of their combustion engines. Different from gasoline-fueled engines, the engines of vehicles using natural gas or liquefied petroleum gas perform combustions of light hydrocarbons at relatively low temperatures, typically