Environmental Processes

Concentration and Recovery of Dyes from Textile Wastewater using a Self-standing, Support-free Forward Osmosis Membrane Meng Li, Xi Wang, Cassandra J Porter, Wei Cheng, Xuan Zhang, Lianjun Wang, and Menachem Elimelech Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.9b00446 • Publication Date (Web): 25 Feb 2019 Downloaded from http://pubs.acs.org on February 25, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27

Environmental Science & Technology

1 2

Concentration and Recovery of Dyes from

3

Textile Wastewater using a Self-standing,

4

Support-free Forward Osmosis Membrane

5

Environmental Science & Technology 6 7 8 9

Meng Li,1 Xi Wang,2 Cassandra J. Porter,3 Wei Cheng,3 Xuan Zhang,1,3* Lianjun Wang,1 and Menachem Elimelech3*

10 11 12

1) Key Laboratory of New Membrane Materials, Ministry of Industry and Information Technology; School of Environmental and Biological Engineering, Nanjing University of Science & Technology, Nanjing 210094, China 2) School of Chemical Engineering, Nanjing University of Science & Technology, Nanjing 210094, China 3) Department of Chemical and Environmental Engineering, Yale University, New Haven, CT 06520-8286, USA 13 14 15 16 17

*Corresponding Author:

18

Xuan Zhang: [email protected];

19

Menachem Elimelech: [email protected].

20 1

ACS Paragon Plus Environment

Environmental Science & Technology

ABSTRACT 21

Forward osmosis (FO) can potentially treat textile wastewaters with less fouling than pressure-

22

driven membrane processes such as reverse osmosis and nanofiltration. However, conventional

23

FO membranes with asymmetric architecture experience severe flux decline caused by internal

24

concentration polarization and fouling as dye molecules accumulate on the membrane surface. In

25

this study, we present a new strategy for concentrating dye by using a self-standing, support-free

26

FO membrane with a symmetric structure. The membrane was fabricated by a facile solution-

27

casting approach based on a poly(triazole-co-oxadiazole-co-hydrazine) (PTAODH) skeleton. Due

28

to its dense architecture, ultra-smooth surface, and high negative surface charge, the PTAODH

29

membrane exhibits excellent FO performance with minimal fouling, low reverse salt flux, and

30

negligible dye passage to the draw solution side. Cleaning with a 40% alcohol solution, after

31

achieving a concentration factor of ~10, resulted in high flux recovery ratio (98.7%) for the

32

PTAODH membrane, whereas significant damage to the active layers of two commercial FO

33

membranes was observed. Moreover, due to the existence of cytotoxic oxadiazole and triazole

34

moieties in the polymer structure, our PTAODH membrane exhibited an outstanding antibacterial

35

property with two model bacteria. Our results demonstrate the promising application of the

36

symmetric PTAODH membrane for the concentration of textile wastewaters and its superior

37

antifouling performance compared to state-of-the-art commercial FO membranes.

38

2

ACS Paragon Plus Environment

Page 2 of 27

Page 3 of 27

Environmental Science & Technology

INTRODUCTION 39

Increasing stressors on water resources and growing concerns over pollution of aquatic

40

environments have revived an interest in achieving minimal or zero liquid discharge (ZLD) of

41

industrial wastewaters. Therefore, developing efficient, low-cost technologies for wastewater

42

treatment and reuse has become an important goal.1-3 Dyeing processes in the textile industry are

43

characterized by high water consumption and extremely polluted effluents containing high

44

concentrations of various dyes and salts.4,5 Through separation and concentration processes, useful

45

resources like dyes could be recycled or reused, reducing the risk to the environment and increasing

46

fresh water supply.4

47

Conventional wastewater treatment processes, such as biological degradation,6 adsorption,7

48

advanced oxidation,8 and coagulation-flocculation,9 are widely utilized in the textile industry.

49

However, possible wastewater toxicity to essential microorganisms used in biological reactors,

50

large quantities of chemicals needed for effective treatment, and toxic byproducts render the above

51

treatment techniques quite challenging and unsustainable.

52

Treating textile wastewaters by membrane-based technologies could potentially be simpler and

53

more environmentally friendly compared to conventional processes.4,10-18 The first step in treating

54

dye wastewaters via membrane processes is fractionation, whereby larger dye molecules are

55

selectively retained in the concentrate while smaller salt ions pass through more easily. Recently,

56

several efforts have been made to enable effective separation of inorganic components from textile

57

wastewaters by using commercial10-13 or self-made NF membranes13-18 with loose structures.

58

Following fractionation, retained solutions of valuable dyes undergo a concentration process

59

for their recovery and reuse.13 However, most dye concentration processes experience severe

60

fouling of membrane surfaces, particularly when conventional, pressure-driven membrane

61

processes are used (e.g., ultrafiltration19 and nanofiltration20), which results in rapid flux decline,

62

frequent chemical cleaning, and reduced membrane lifespan. Organic fouling, especially 3

ACS Paragon Plus Environment

Environmental Science & Technology

63

irreversible fouling caused by adsorption or deposition of dyes on the membrane surface,15 is

64

affected by the intrinsic hydrophobicity21-23 and the surface morphology of the membranes.24,25

65

Furthermore, thin-film composite polyamide nanofiltration membranes contain carboxyl groups,

66

which have been shown to enhance organic fouling.26

67

Biofouling is another major performance-limiting factor in nanofiltration,27-29 reverse

68

osmosis,30-33 and forward osmosis.34,35 To mitigate biofilm formation, membrane surfaces have

69

been grafted with biocidal nanomaterials,29-38 such as silver or copper nanoparticles30,32 and

70

graphene oxide (GO) nanosheets.37 However, the added costs and steps during fabrication pose

71

difficulties when manufacturing these hybrid membranes on larger scales, while the potential

72

leaching of nanomaterials may further hinder their commercialization.29,30 Hence, membranes

73

composed of an inherently bactericidal material could be a more commercially viable option.

74

Recently, we have presented a proof-of-concept of a self-standing, support-free FO membrane

75

using a novel poly(triazole-co-oxadiazole-co-hydrazine) (PTAODH) skeleton.39 Due to the

76

symmetric structure of the membrane, no internal concentration polarization was observed when

77

evaluating the FO membrane desalination performance. Uniquely, the membrane is extremely

78

smooth, and due to its robustness there is no need for membrane backing or a support layer. Despite

79

the initial promise, the use of this membrane in emerging FO applications has not previously been

80

demonstrated.

81

In this work, we systematically evaluate the use of the PTAODH thin film for dye

82

concentration in forward osmosis. For comparison, both the PTAODH symmetric membrane and

83

two commercially available asymmetric FO membranes were exposed to an artificial textile

84

wastewater effluent in which Congo Red was used as a model dye. Analyses of dye concentration

85

efficiency, membrane regeneration performance, fouling propensity, and anti-biofouling

86

properties provide insights into the membrane separation and antifouling mechanisms. Our work

87

highlights the potential application of the symmetric FO membranes for sustainable concentration 4

ACS Paragon Plus Environment

Page 4 of 27

Page 5 of 27

88

Environmental Science & Technology

and recovery of valuable dyes in the textile industry.

89

MATERIALS AND METHODS 90

Materials and Chemicals. Polyoxadiazole-co-hydrazide (PODH) and polytriazole-co-

91

oxadiazole-co-hydrazide were synthesized according to our previous report39 and used for the

92

fabrication of the self-standing, support-free FO membrane. The polymeric membrane is

93

composed of a random copolymer containing polytriazole, polyoxadiazole, and polyhydrazine

94

moieties at a controlled proportion. PTAODH-1.0 was used in the current study, where 1.0 denotes

95

the molar ratio of 4-aminobenzoic acid to the repeating unit of PODH during the synthesis.

96

Commercially available cellulose triacetate FO membrane (HTI-CTA) was provided by Hydration

97

Technology Innovations, and polyamide thin-film composite FO membrane (CSM-TFC) was

98

provided by Toray Chemical Korea, Inc. Congo Red (CR) and sodium sulfate (Na2SO4) were

99

procured from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Other reagents and

100

solvents were used as received. Deionized (DI) water with a minimum resistance of 18 MΩ-cm

101

(Millipore) was used throughout the work.

102

Membrane Characterization. Morphologies of the self-standing, support-free membrane

103

(PTAODH-1.0) as well as the commercial HTI-CTA and CSM-TFC membrane samples were

104

studied by field emission scanning electron microscopy (FESEM, S-4800, Hitachi, Japan). All

105

membrane samples were air-dried, fractured in liquid nitrogen, and sputter coated with gold prior

106

to imaging. Surface roughness of all membranes was measured by an Atomic Force Microscope

107

(AFM, Mutilmode8, Germany). At least three measurements were made at different locations for

108

each membrane surface.

109

Dye Concentration Process. In forward osmosis (FO) mode (active layer facing the feed

110

solution), 200 mL of 1.0 g L-1 CR solution and 150 mL of 1.5 M Na2SO4 solution were used as

111

feed solution and draw solution, respectively. The effective membrane area was 10 cm2, and the 5

ACS Paragon Plus Environment

Environmental Science & Technology

Page 6 of 27

112

crossflow velocity was fixed at 10.4 cm s-1, as described elsewhere.39 Reverse salt (Na2SO4)

113

concentration in the feed solution was measured by ion chromatography (Dionex ICS-2100, USA)

114

in terms of SO42- ion content; dye concentration was measured using a UV/VIS spectrometer

115

(Lambda 25, PerkinElmer, USA). Water weight loss of feed solution was recorded by a digital

116

balance to determine the water recovery. The concentration process was stopped at a water

117

recovery ratio of 90%, corresponding to a concentration factor (CF) of 10.

118

Analogously, in pressure-retarded osmosis (PRO) mode (active layer facing the draw solution),

119

the concentration process was the same as described above, except for the orientation of the active

120

layer in the cell. Because PTAODH-1.0 is symmetric, the two modes, denoted as FO-TF and FO-

121

BF, represent testing both sides of the membrane (top surface facing the feed, FO-TF, and bottom

122

surface facing the feed, FO-BF).

123

Membrane Cleaning Strategy. After the concentration stage (water recovery 90% or CF

124

= 10), various solutions were used to clean the fouled FO membranes in the FO setup for 30

125

minutes at room temperature. Pure water, 20%, 40%, 60%, and 80% alcohol solutions were used

126

in the feed side, and DI water was used in the draw side. Crossflow velocity on both the draw and

127

feed sides of the membrane was maintained at 10.4 cm s-1. The flux recovery ratio (FRR), used for

128

evaluating the effectiveness of cleaning the membranes, was calculated by13

FRR 

129

J w ,a J w,b

100%

(1)

130

where Jw,b and Jw,a represent the water flux of the CR solution (1.0 g L-1) before fouling and after

131

cleaning, respectively.

132

Evaluation of Antibacterial Properties of FO Membranes. Antibacterial properties

133

of PODH, PTAODH-1.0, HTI-CTA, and CSM-TFC FO membranes were tested against both

134

Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) by a viable cell counting method,

135

as described elsewhere.37,38,40 For both bacteria types, each membrane (HTI-CTA, CSM-TFC, 6

ACS Paragon Plus Environment

Page 7 of 27

Environmental Science & Technology

136

PODH, or PTAODH-1.0) with dimensions of 2.5 cm × 2.5 cm was installed in a sterile, specially

137

designed frame with clamps so that only the active surface was exposed and bacterial suspensions

138

could be contained within the frame. In this holder, the membrane top surfaces were sterilized for

139

30 minutes under UV radiation prior to the antibacterial tests. To prepare bacterial suspensions, E.

140

coli and S. aureus were grown overnight at 37oC in a Luria-Bertani (LB) medium. Cells were

141

collected by centrifugation, washed three times using sterile saline solution (NaCl, 0.9% (w/v)),

142

and diluted to the concentration of 1.0×108 colony-forming units per milliliter (CFU mL-1). A

143

quantity of 1.0 mL of bacterial suspension was poured onto the sterilized membrane surface. After

144

three hours of contact with the bacterial solution, the membrane was taken out and rinsed with a

145

sterile saline solution (NaCl, 0.9% (w/v)) to remove unattached cells on the membrane surface. To

146

detach the deposited cells, the membrane was mildly sonicated for five minutes in 10 mL of sterile

147

saline solution. The solutions were incubated overnight at 37oC and diluted by 100 times before

148

plating on the LB/Agar plates for plate counting.

149

RESULTS AND DISCUSSION 150

Membrane Properties. From our proof-of-concept study to develop a symmetric, support-free

151

membrane for FO,39 the best performing membrane in terms of water flux and salt retention,

152

referred to as PTAODH-1.0, was chosen for the present investigation. The water flux, Jw, and

153

reverse salt flux, Js, of the membrane were found to be 11.7±0.7 L m-2 h-1 and 27.5±2.1 mmol m-2

154

h-1, respectively, when using 1.5 M Na2SO4 as the draw solution. Other physicochemical properties

155

of the membrane, including mechanical robustness, were described in our recent proof-of-concept

156

study.39

157

The morphologies of the PTAODH-1.0 membrane as well as the two commercial membranes

158

used for comparison (HTI-CTA and CSM-TFC) were studied by FESEM. As shown in Figures

159

1A and 1B, the surface morphologies for both sides of the PTAODH-1.0 FO membrane are almost 7

ACS Paragon Plus Environment

Environmental Science & Technology

160

identical, and no visible pores were observed over the entire scanning area. In addition, the cross-

161

section image of PTAODH-1.0 (Figure 1C) portrays its symmetric structure. In contrast, both HTI-

162

CTA and CSM-TFC membranes exhibit typical asymmetric structures with a dense layer on top

163

of a polyester support mesh, as shown in Figures 1F and 1I. The surface roughness of the

164

membranes was analyzed using atomic force microscopy (AFM) (Figure S1 in Supporting

165

Information). The PTAODH-1.0 membrane is extremely smooth and exhibits a very small average

166

plane roughness (Ra) of 0.66±0.08 and 0.69±0.17 nm on each side of the symmetric membrane.

167

In contrast, much greater Ra values were found for both the HTI-CTA (top: 9.95±0.21 nm; bottom:

168

12.6±0.28 nm) and CSM-TFC (top: 30.3±1.84 nm; bottom: 9.6±5.78 nm) membranes. The overall

169

roughness can also be judged by inspecting the top or bottom surface in the SEM images (Figures

170

1D, 1E, 1G, and 1H).

171

Besides exhibiting smoothness on the nanoscale, the PTAODH-1.0 membrane is uniquely

172

smoother than both the HTI-CTA and CSM-TFC membranes on the microscale owing to its

173

robustness, which eliminates the need for a supportive membrane backing. As seen in Figures 1F

174

and 1I, the mesh support backings produce a regular pattern of microscale peaks and valleys on

175

both the top and bottom surfaces of the HTI-CTA and CSM-TFC membranes. Considering that

176

bacteria and aggregates of highly concentrated dyes 41 fall within the microscale range as opposed

177

to the nanoscale, perhaps microscale roughness may be more influential for both organic and

178

biofouling. Studies have shown that areas with the greatest fouling propensity are often dead zones,

179

especially in crossflow systems.42,43 Dead zones are caused more frequently by micro- and

180

macroscale structures, such as the presence of spacers,44 than by nanoscale roughness. In the case

181

of HTI-CTA and CSM-TFC membranes, such dead zones create near-stagnant flow, which

182

decreases mixing, thereby increasing concentration polarization (CP) and rates of organic and bio-

183

foulant deposition. Furthermore, such dead zones can also decrease the effectiveness of cleaning,

184

since cleaning relies on not only the foulant’s solubility in the cleaning solution but also on shear

185

forces. The positive impact of the extreme smoothness of the PTAODH-1.0 membrane at both the 8

ACS Paragon Plus Environment

Page 8 of 27

Page 9 of 27

Environmental Science & Technology

186

nano- and micro-scales is evident in the results of our dye concentration and membrane cleaning

187

studies, discussed in the following sections.

188

Figure 1

189 190 191

Desalination performance in FO (feed solution facing membrane active layer) and PRO (feed

192

solution facing membrane support layer) modes was investigated for all three types of membranes.

193

As shown in Figure 2, for the PTAODH-1.0 membrane, Jw and Js were consistent at both

194

orientations, which again is indicative of membrane symmetry. In contrast, both HTI-CTA and

195

CSM-TFC membranes exhibited markedly different desalination behaviors depending on their

196

orientation. The water flux for the HTI-CTA membrane in PRO mode (10.2±0.4 L m-2 h-1) was

197

slightly greater than that in FO mode (8.5±0.2 L m-2 h-1), whereas much greater Jw was found for

198

the CSM-TFC membrane in PRO mode (44.1±1.3 L m-2 h-1) than that in FO mode (21.0±2.5 L m-2

199

h-1). These results are attributed to the different extents of internal concentration polarization (ICP)

200

in FO (dilutive ICP) and PRO (concentrative ICP) modes.45,46 Although the pure water

201

permeability (A) value of our symmetric membrane (0.118 L m-2 h-1 bar-1) was lower than the

202

commercial membranes (0.375 L m-2 h-1 bar-1for HTI-CTA39,47 and 4.192 L m-2 h-1 bar-1 for CSM-

203

TFC

204

performance of a membrane,50 was still quite acceptable. Specifically, the reverse flux selectivities

205

of our symmetric membrane for FO-TF and FO-BF modes were 426.2±5.2 L mol-1 and 430.0±10.7

206

L mol-1, respectively, higher than those of the HTI-CTA membrane (FO mode: 384.9±20.8 L mol-1;

207

PRO mode: 397.8±22.0 L mol-1), but only slightly lower than those of the CSM-TFC membrane

208

(FO mode: 501.4±19.6 L mol-1; PRO mode: 579.8±53.6 L mol-1) (Figure 2B). The above Jw/Js

209

ratio of the PTAODH-1.0 membrane reflects a desalination efficiency comparable to that of the

210

commercial membranes.

48,49),

its reverse flux selectivity (Jw/Js), an essential parameter representing the FO

9

ACS Paragon Plus Environment

Environmental Science & Technology

211

Figure 2

212 213 214

Dye Concentration Performance. High salinities of up to ~6% (approximately 60,000 mg

215

L-1 TDS calculated as pure NaCl) in textile wastewaters present challenges for both conventional

216

and membrane-based treatment technologies.12,19 In conventional treatment, such high salt content

217

adversely impacts microorganisms that are used in biological reactors for degradation of dyes. For

218

FO dye concentration, high-salinity feed decreases the osmotic pressure driving force between the

219

feed and draw solution, thereby decreasing water flux. Therefore, separation of dyes from salt

220

seems a necessary prerequisite before degradation or concentration and reuse of dye. However,

221

state-of-the-art membranes still exhibit severe fouling caused by dye moleculeswhether treating

222

dye/salt mixtures or pure dye solutions,10,13,14 as discussed earlier. Particularly for high water

223

recovery ratios, frequent cleaning would be necessary to maintain the production rate, leading to

224

high energy consumption.

225

In contrast, PTAODH-1.0, a smooth, symmetric thin film, shows more promise for dye

226

concentration. Under periodic supplement of Na2SO4 to keep a constant draw solution osmotic

227

pressure, Jw remained relatively stable at 10.6±0.3 L m-2 h-1 over the entire concentration procedure

228

until CF ~10 (Figure 3A), which is directly related to minimal fouling at the feed side as well as

229

negligible ICP.39,51 Moreover, it was reported that membrane surface roughness can act as a

230

structural template for initial layers of foulant.52 Our membrane with an ultra-smooth surface

231

effectively prevents the adhesion of dye molecules, slowing fouling rates and extending membrane

232

life.

233

In marked contrast to the symmetric PTAODH-1.0 membrane, the HTI-CTA and CSM-TFC

234

membranes, with their asymmetric structure, exhibited significant Jw decline both in the FO and

235

PRO modes (Figures S2A, S3A, S4A, and S5A). Specifically, the Jw in FO decreased by 38.3% 10

ACS Paragon Plus Environment

Page 10 of 27

Page 11 of 27

Environmental Science & Technology

236

from 8.1 to 5.0 L m-2 h-1 and by 37.7% from 15.9 to 9.9 L m-2 h-1 for the HTI-CTA and CSM-TFC

237

membranes, respectively, over the time taken to reach CF ~10. The severe flux decline observed

238

for the commercial asymmetric FO membranes is attributed to significant fouling. With the more

239

porous support mesh layer of the commercial membranes facing the dye solution in PRO mode,

240

the Jw (PRO) suffered considerable flux decline due to accumulation of dye foulants in the porous

241

support layer:53 by 57.7% from the initial 9.7 to 4.1 L m-2 h-1 (HTI-CTA) and by 87.5% from the

242

initial 26.3 to 3.3 L m-2 h-1 (CSM-TFC). As evidenced by these results, the ultra-smooth PTAODH-

243

1.0 membrane, consisting of a symmetric architecture without a backing layer, could eliminate

244

ICP and minimize dye entrapment and cake layer formation during dye concentration.

245

The PTAODH-1.0 membrane also showed robust performance, achieving 10-fold dye

246

concentration within 18 hours (Figure 3D). In contrast, it took ~60% and ~40% more time for the

247

HTI-CTA membrane in FO and PRO modes, respectively (Figures S2 and S3) to achieve 10-fold

248

dye concentration. While the CSM-TFC membrane was able to achieve a 10-fold dye

249

concentration within 14 hours, slightly better than the PTAODH-1.0 membrane, the severe fouling

250

and need for chemical cleaning will be a major hindrance to practical application. Furthermore,

251

future improvement of the PTAODH-1.0 membrane fabrication, for example by reducing

252

membrane thickness and thus increasing water flux, could readily enhance the performance of the

253

membrane.

254

During the entire concentration process, all three membranes possessed rather high dye

255

retention and salt rejection (Figures 3B-3C, S2B-S2C, S3B-S3C, S4B-S4C, and S5B-S5C).

256

Specifically, the PTAODH-1.0 membrane only allows 0.37 mmol Na2SO4 to diffuse into the feed

257

solution until the end of operation, due to its inherently low Js values (23.9±2.8 mmol m-2 h-1).

258

Moreover, a tiny amount of the dye, linearly increasing over time, was found in the draw solution

259

with a final concentration of merely 2.2×10-3 mmol L-1 (Figure 3C), matching the final dye

260

concentration in the draw for both HTI-CTA and CSM-TFC membranes under FO operation mode.

11

ACS Paragon Plus Environment

Environmental Science & Technology

261

It is worth mentioning that the excellent retention of dye by the PTAODH-1.0 membrane is

262

also evident in the overlap between empirical and calculated dye concentration values, as shown

263

in Figure 3D. The actual concentration of CR was found to be 9.99 g L-1 when the CF reached ~10,

264

which was slightly lower than the theoretical value of 10.06 g L-1. Such a small discrepancy is

265

within the margin of error of our measurement method.

266 267

Figure 3

268 269

Membrane Cleaning and Regeneration. As seen in Figure S6, the images of the three

270

membrane types before and after the concentration process indicate differences in fouling

271

propensity. A very light red color could be seen on the surface of PTAODH-1.0, suggesting only

272

slight dye adsorption, while both the HTI-CTA and CSM-TFC membranes (PRO mode) developed

273

deep red color due to significant adsorption and accumulation of dye molecules.

274

In spite of insignificant fouling on the PTAODH-1.0 membrane during FO operation, a proper

275

cleaning strategy is necessary to maintain membrane desalination performance. The PTAODH-

276

1.0 membrane exhibits a relatively high FRR of 93±1.1% after rinsing with pure water, exceeding

277

the FRR of the HTI-CTA (at 86.3% and 76.7% for FO and PRO modes, respectively) and the

278

CSM-TFC (at 84.3% and 64.8% for FO and PRO modes, respectively) membranes (Figure 4A).

279

However, in order to maximize the FRR, it is advantageous to use a cleaning solution that better

280

dissolves the foulant of interest without damaging the membrane. Because dye molecules are

281

generally more soluble in organic solvents than in aqueous solution,13 alcohol solutions were

282

employed here. As shown in Figure 4B, the FRR of the PTAODH-1.0 membrane considerably

283

increases to 96.6% and 98.7% with a negligible increase in Js by cleaning with 20% or 40% of

284

ethanol/water solution, respectively, indicating the membrane good antifouling and solvent-

285

resistant properties. However, a sharp increase of Js up to 125.7 mmol m-2 h-1 was observed when 12

ACS Paragon Plus Environment

Page 12 of 27

Page 13 of 27

Environmental Science & Technology

286

cleaning with an 80% alcohol solution, which caused the FO performance to deteriorate. We

287

attribute this phenomenon to the physical expansion of the interstitial spaces within the membrane

288

matrix caused by excessive ethanol.13,52

289

Based on the above results, a 40% alcohol solution was chosen as the optimal cleaning medium

290

for comparing the performance of the three membrane types. As shown in Figure 4C, unlike the

291

superb performance of the PTAODH-1.0 membrane, after cleaning in FO mode, the HTI-CTA

292

membrane rejected Na2SO4 considerably less (Js increased to 75.2 mmol m-2 h-1) with an FRR of

293

106.3%, while only a moderate FRR of 92.2% was found for CSM-TFC membrane. Several

294

studies suggest that cellulose triacetate could swell or even degrade in the presence of ethanol by

295

a Claisen condensation reaction.54,55 Other studies suggested variation of pore size and pore density

296

of the polyamide layer in TFC membranes due to the contact with ethanol, causing severe volume

297

expansion or curling of the polymer matrix.56-58 Thus, the poor regeneration of both the HTI-CTA

298

and CSM-TFC membranes with alcohol solutions was probably due to the physical collapse of the

299

active layer, which hinders thorough cleansing in commercial applications.

300 301

Figure 4

302 303

Membrane Antibacterial Property. The antibacterial property of the PTAODH-1.0

304

membrane was investigated using two model bacteria, E. coli (Gram-negative) and S. aureus

305

(Gram-positive). To better understand the antibacterial mechanism, PODH (the precursor of

306

PTAODH without 1,2,4-triazole moiety) as well as the commercial FO membranes were included

307

in the investigation. The results, presented as percent of colony-forming units (CFU) compared

308

the control after three hours contact time, are shown in Figure 5. Based on their biocompatible

309

chemical structure,59,60 both the HTI-CTA and CSM-TFC membranes exhibit negligible

310

antibacterial activity against both bacteria types. Although the triazole moiety was found to 13

ACS Paragon Plus Environment

Environmental Science & Technology

311

comprise only ~10 mol% of the PTAODH-1.0 backbone (calculated from our previous study),39

312

significantly low cell viabilities of 14.0±1.4% and 18.0±12.6% were achieved against E. coli and

313

S. aureus, respectively. It has been reported that the hydrophilicity of oxadiazole and triazole

314

groups could disrupt the normal metabolism of bacterial cells by inhibiting the production of lipids

315

necessary for cell-wall biosynthesis, thus inhibiting bacterial reproduction.61-65 The triazole moiety

316

was even revealed to have cytotoxicity that may cause a fast cell deactivation.61 Moreover, the

317

smooth surface of the PTAODH-1.0 membrane could also prevent bacterial adhesion, growth,

318

proliferation, and subsequent formation of biofilm.66,67 Thus, both bacteriostatic/bactericidal

319

mechanisms and morphology contribute to the outstanding antibacterial properties of our

320

membrane PTAODH-1.0.

321

Figure 5

322 323

ASSOCIATED CONTENT 324

Supporting Information Available: Supporting figures include AFM morphology of PTAODH-

325

1.0, HTI-CTA, and CSM-TFC membranes (Figure S1); results of concentration experiment using

326

HTI-CTA membrane (FO mode) (Figure S2); results of concentration experiment using HTI-CTA

327

membrane (PRO mode) (Figure S3); results of concentration experiment using CSM-TFC

328

membrane (FO mode) (Figure S4); results of concentration experiment using CSM-TFC

329

membrane (PRO mode) (Figure S5); and images of all three membranes before dye concentration,

330

after dye concentration, and after physical cleaning (Figure S6). This material is available free of

331

charge via the internet at https://pubs.acs.org/.

332

AUTHOR INFORMATION 333

Corresponding Author 14

ACS Paragon Plus Environment

Page 14 of 27

Page 15 of 27

Environmental Science & Technology

334

* Xuan Zhang: [email protected].

335

* Menachem Elimelech: [email protected]. Notes

336

The authors declare no competing financial interest. ACKNOWLEDGMENTS

337

This work was supported by the National Natural Science Foundation of China (21774058,

338

51778292), the Natural Science Foundation of Jiangsu Province (BK20180072), and the

339

Postgraduate Research & Practice Innovation Program of Jiangsu Province (KYCX18_0480).

340

REFERENCES 341 342 343 344 345 346 347 348 349 350 351 352 353 354 355 356 357 358 359

(1) Werber, J. R.; Deshmukh, A.; Elimelech, M. The Critical Need for Increased Selectivity, Not Increased Water Permeability, for Desalination Membranes. Environ. Sci. Technol. Lett. 2016, 3, 112-120. (2) Tang, C. Y.; Yang, Z.; Guo, H.; Wen, J. J.; Nghiem, L. D.; Cornelissen, E. Potable Water Reuse through Advanced Membrane Technology. Environ. Sci. Technol. 2018, 52, 10215-10223. (3) Phuntsho, S.; Shon, H. K.; Majeed, T.; EI Saliby, I.; Viqneswaran, S.; Kandasamy, J.; Hong, S.; Lee, S. Blended fertilizers as draw solutions for fertilizer-drawn forward osmosis desalination. Environ. Sci. Technol. 2012, 46, 4567-4575. (4) Petrinić, I.; Bajraktari, N.; Hélix-Nielsen, C. Membrane Technologies for Water Treatment and Reuse in the Textile Industry. Advances in Membrane Technologies for Water Treatment. 2015, 2, 537-550. (5) Jiang, M.; Ye, K. F.; Deng, J. J.; Lin, J. Y.; Ye, W. Y.; Zhao, S. F.; Var der Bruggen, B. Conventional Ultrafiltration as Effective Strategy for Dye/Salt Fractionation in Textile Wastewater Treatment. Environ. Sci. Technol. 2018, 52, 10698-10708. (6) Gupta, V. K.; Bhushan, R.; Nayak, A.; Singh, P.; Bhushan, B. Biosorption and Reuse Potential of A Blue Green Alga for the Removal of Hazardous Reactive Dyes from Aqueous Solutions. Bioremediat. J. 2014, 18, 179-191. (7) Cardoso, N. F.; Lima, E. C.; Royer, B.; Bach, M. V.; Dotto, G. L.; Pinto, L. A.; Calvete, T. Comparison of Spirulina Platensis Microalgae and Commercial Activated Carbon as Adsorbents 15

ACS Paragon Plus Environment

Environmental Science & Technology

360 361 362 363 364 365 366 367 368 369 370 371 372 373 374 375 376 377 378 379 380 381 382 383 384 385 386 387 388 389 390 391 392 393 394

for the Removal of Reactive Red 120 Dye from Aqueous Effluents. J. Hazard. Mater. 2012, 241, 146-153. (8) Oller, I.; Malato, S.; Sánchez-Pérez, J. Combination of Advanced Oxidation Processes and Biological Treatments for Wastewater Decontamination: A Review. Sci. Total Environ. 2011, 409, 4141-4166. (9) Verma, A. K.; Dash, R. R.; Bhunia, P. A Review on Chemical Coagulation/Flocculation Technologies for Removal of Colour from Textile Wastewaters. J. Environ. Manage. 2012, 93, 154-168. (10)Lin, J.; Ye, W.; Zeng, H; Yang, J.; Shen.; Darvishmanesh, S.; Luis, P.; Sotto, A.; Van der Bruggen, B. Fractionation of Direct Dyes and Salts in Aqueous Solution using Loose Nanofiltration Membranes. J. Membr. Sci. 2015, 477, 183-193. (11)Ye, W. Y.; Lin, J. Y.; Borrego, R.; Tang, C. Y.; Van der Bruggen, B. Advanced Desalination of Dye/NaCl Mixtures by A Loose Nanofiltration Membrane for Digital Ink-jet Printing. Sep. Purif. Technol. 2018, 197, 27-35. (12) Lin, J. Y.; Tang, C. Y.; Ye, W. Y.; Sun, S. P.; Van der Bruggen, B. Unraveling Flux Behavior of Superhydrophilic Loose Nanofiltration Membranes during Textile Wastewater Treatment. J. Membr. Sci. 2015, 493, 690-702. (13)Li, M.; Yao, Y. J.; Zhang, W.; Zheng, J. F.; Zhang, X.; Wang, L J. Fractionation and Concentration of High-Salinity Textile Wastewater using an Ultra-Permeable Sulfonated Thinfilm Composite. Environ. Sci. Technol. 2017, 51, 9252-9260. (14)Lau, W. J.; Ismail, A. F. Polymeric Nanofiltration Membranes for Textile Dye Wastewater Treatment: Preparation, Performance Evaluation, Transport Modelling, and Fouling Control-A Review. Desalination 2009, 245, 321-348. (15)Zhao, S.; Wang, Z. A Loose Nanofiltration Membrane Prepared by Coating HPAN UF Membrane with Modified PEI for Dye Reuse and Desalination. J. Membr. Sci. 2017, 524, 214224. (16) Xing, L. X.; Guo, N. N.; Zhang, Y. T.; Zhang, H. Q.; Liu, J. D. A Negatively Charged Loose Nanofiltration Membrane by Blending with Poly(sodium 4-styrene sulfonate) Grafted SiO2 via SIATRP for Dye Purification. Sep. Purif. Technol. 2015, 146, 50-59. (17)Zhua, J. Y.; Tian, M. M.; Zhang, Y. T.; Zhang, H. Q.; Liu, J. D. Fabrication of A Novel “Loose” Nanofiltration Membrane by Facile Blending with Chitosan-Montmorillonite Nanosheets for Dyes Purification. Chem. Eng. J. 2015, 265, 184-193. (18)Chen, P.; Ma, X.; Zhong, Z.; Zhang, F.; Xing, W.; Fan, Y. Performance of Ceramic Nanofiltration Membrane for Desalination of Dye Solutions Containing NaCl and Na2SO4. Desalination 2017, 404, 102-111. 16

ACS Paragon Plus Environment

Page 16 of 27

Page 17 of 27

395 396 397 398 399 400 401 402 403 404 405 406 407 408 409 410 411 412 413 414 415 416 417 418 419 420 421 422 423 424 425 426 427

Environmental Science & Technology

(19)Lin, J. Y.; Ye, W. Y.; Baltaru, M. C.; Tang, Y. P.; Van der Bruggen, B. Tight Ultrafiltration Membranes for Enhanced Separation of Dyes and Na2SO4 during Textile Wastewater Treatment. J. Membr. Sci. 2016, 514, 217-228. (20)Chidambaram, T.; Oren, Y.; Noel, M. Fouling of Nanofiltration Membranes by Dyes during Brine Recovery from Textile Dye Bath Wastewater. Chem. Eng. J. 2015, 262, 156-168. (21)Qin, D. T.; Liu, Z. Y.; Liu, Z.; Bai, H. W.; Sun, D. D. Superior Antifouling Capability of Hydrogel Forward Osmosis Membrane for Treating Wastewaters with High Concentration of Organic Foulants. Environ. Sci. Technol. 2018, 52, 1421-1428. (22)Zhang, X. Y.; Tian, J. Y.; Gao, S. S.; Shi. W. X.; Liu, D. M. Surface Functionalization of TFC FO Membranes with Zwitterionic Polymers: Improvement of Antifouling and Salt-responsive Cleaning Properties. J. Membr. Sci. 2017, 544, 368-377. (23) Chen, S. F.; Li, L. Y.; Zhao, C.; Zheng, J. Surface Hydration: Principles and Applications Toward Low-fouling/Nonfouling Biomaterials. Polymer 2010, 51, 5283-5293. (24)Elimelech, M.; Zhu, X. H.; Childress, A. E.; Hong, S. K. Role of Membrane Surface Morphology in Colloidal Fouling of Cellulose Acetate and Composite Aromatic Polyamide Reverse Osmosis Membranes. J. Membr. Sci. 1997, 127, 101-109. (25)Vrijenhoek, E. M.; Hong, S.; Elimelech, M. Influence of Membrane Surface Properties on Initial Rate of Colloidal Fouling of Reverse Osmosis and Nanofiltration Membranes. J. Membr. Sci. 2001, 188, 115-128. (26)Mo, Y. H.; Tiraferri, A.; Yip, N. Y.; Adout, A.; Huang, X.; Elimelech, M. Improved Antifouling Properties of Polyamide Nanofiltration Membranes by Reducing the Density of Surface Carboxyl Groups. Environ. Sci. Technol. 2012, 46, 13253-13261. (27)Bottom, S.; Verliefde, A. R. D.; Quach, N. T.; Cornelissen, E. R. Influence of Biofouling on Pharmaceuticals Rejection in NF Membrane Filtration. Water Res. 2012, 46, 5848-5860. (28)Wang, J.; Wang, Z.; Liu, Y. Y.; Wang, J. X.; Wang, S. C. Surface Modification of NF Membrane with Zwitterionic Polymer to Improve Anti-biofouling Property. J. Membr. Sci. 2016, 514, 407-417. (29)Zheng, J. F.; Li, M.; Yao, Y. J.; Zhang, X.; Wang, L. J. Zwitterionic Carbon Nanotube Assisted Thin-film Nanocomposite Membranes with Excellent Efficiency for Separation of Mono/Divalent Ions from Brackish Water. J. Mater. Chem. A. 2017, 5, 13730-13739. (30)Ben-Sasson, M.; Zodrow, K. R.; Qi, G. G.; Kang, Y.; Gianelis, E. P.; Elimelech, M. Surface Functionalization of Thin-Film Composite Membranes with Copper Nanoparticles for Antimicrobial Surface Properties. Environ. Sci. Technol. 2014, 48, 384-393.

17

ACS Paragon Plus Environment

Environmental Science & Technology

428 429 430 431 432 433 434 435 436 437 438 439 440 441 442 443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 458 459 460

(31)Park, S. H.; Ko, Y. S.; Park, S. J.; Lee, J. S.; Cho, J. H.; Lee, J. H. Immobilization of Silver Nanoparticle-decorated Silica Particles on Polyamide Thin Film Composite Membranes for Antibacterial Properties. J. Membr. Sci. 2016, 499, 80-91. (32)Ben-Sasson, M.; Lu, X. L.; Bar-Zeev, E.; Zodrow, K. R.; Nejati, S.; Qi, G. G.; Giannelis, E. P.; Elimelech, M. In Situ Formation of Silver Nanoparticles on Thin-film Composite Reverse Osmosis Membranes for Biofouling Mitigation. Water Res. 2014, 62, 260-270. (33)Rahaman, M. S.; Thérien-Aubin, H.; Ben-Sasson, M.; Ober, C. K.; Nielsen, M.; Elimelech, M. Control of Biofouling on Reverse Osmosis Polyamide Membranes Modified with Biocidal Nanoparticles and Antifouling Polymer Brushes. J. Mater. Chem. B. 2014, 2, 1724-1732. (34)Faria, A. F.; Liu, C. H.; Xie, M.; Perreault, F.; Nghiem, L. D.; Ma, J.; Elimelech, M. Thinfilm Composite Forward Osmosis Membranes Functionalized with Graphene Oxide-silver Nanocomposites for Biofouling Control. J. Membr. Sci. 2017, 525, 146-156. (35)Bogler, A.; Lin, S. H.; Bar-Zeev, E. Biofouling of Membrane Distillation, Forward Osmosis and Pressure Retarded Osmosis: Principles, Impacts and Future Directions. J. Membr. Sci. 2017, 542, 378-398. (36)Diagne, F.; Malaisamy, R.; Boddie, V.; Holbrook, R. D.; Eribo, B.; Jones, K. L. Polyelectrolyte and Silver Nanoparticle Modification of Microfiltration Membranes to Mitigate Organic and Bacterial Fouling. Environ. Sci. Technol. 2012, 46, 4025-4033. (37)Perreault, F.; Tousley, M. E.; Elimelech, M. Thin-film Composite Polyamide Membranes Functionalized with Biocidal Graphene Oxide Nanosheets. Environ. Sci. Technol. Lett. 2014, 1, 71-76. (38)Lu, X. L.; Feng, X. D.; Werber, J. R.; Chu, C. H.; Zucker, I.; Kim, J. H.; Osuji, C. O.; Elimelech, M. Enhanced antibacterial activity through the controlled alignment of graphene oxide nanosheets. Proc. Natl. Acad. Sci. U. S. A. 2017, 114, 9793-9801. (39)Li, M.; Karanikola, V.; Zhang, X.; Wang, L. J.; Elimelech, M. A Self-standing, Support-Free Membrane for Forward Osmosis with No Internal Concentration Polarization. Environ. Sci. Technol. Lett. 2018, 5, 266-271. (40)Perreault, F.; de Faria, A. F.; Nejati S.; Elimelech, M. Antimicrobial Properties of Graphene Oxide Nanosheets: Why Size Matters. ACS Nano 2015, 9, 7226-7236. (41)Hillson, P. J.; McKay, R. B. Aggregation of Dye Molecules in Aqueous Solution A Polarographic Study. Trans. Faraday Soc. 1965, 61, 374-382. (42)Chen, K. L.; Song, L. F.; Ong, S. L.; Ng, W. J. The Development of Membrane Fouling in Full-scale RO Processes. J. Membr. Sci. 2004, 232, 63-72.

18

ACS Paragon Plus Environment

Page 18 of 27

Page 19 of 27

461 462 463 464 465 466 467 468 469 470 471 472 473 474

Environmental Science & Technology

(43)Lotfi, F.; Chekli, L.; Phuntsho, S.; Hong, S.; Choi, J. Y.; Shon, H. K. Understanding the Possible Underlying Mechanisms for Low Fouling Tendency of The Forward Osmosis and Pressure Assisted Osmosis Processes. Desalination 2017, 421, 89-98. (44)Vrouwenvelder, J. S.; Graf von der Schulenburg, D. A.; Kruithof, J. C.; Johns, M. L.; van Loosfrecht, M. C. Biofouling of Spiral-wound Nanofiltration and Reverse Osmosis Membranes: A feed spacer problem. Water Res. 2009, 43, 583-594. (45)Fang, L. F.; Cheng, L.; Jeon, S.; Wang, S. Y.; Takahashi, T.; Matsuyama, H. Effect of the Supporting Layer Structures on Antifouling Properties of Forward Osmosis Membranes in AL-DS Mode. J. Membr. Sci. 2018, 552, 265-273. (46)Gray, G.T.; McCutcheon, J.R.; Elimelech, M. Internal Concentration Polarization in Forward Osmosis: Role of Membrane Orientation. Desalination 2006, 197, 1-8. (47)Yip, N.Y.; Tiraferri, A.; Phillip, W. A.; Schiffman, J. D.; Elimelech, M. High Performance Thin-film Composite Forward Osmosis Membrane. Environ. Sci. Technol. 2010, 44, 38123818.

477

(48)Nguyen, T. P. N.; Jun, B. M.; Lee, J. H.; Kwon, Y. N. Comparison of Integrally Asymmetric and Thin Film Composite Structures for a Desirable Fashion of Forward Osmosis Membranes. J. Membr. Sci. 2015, 495, 457-470.

478

(49)Data Sheet CSM Forward Osmosis Membrane. Toray Chemical Korea Inc.

479

(50)Phillip, W. A.; Yong, J. S.; Elimelech, M. Reverse Draw Solute Permeation in Forward Osmosis: Modeling and Experiments. Environ. Sci. Technol. 2010, 44, 5170-5176.

475 476

480 481 482 483 484 485 486 487 488 489 490 491 492 493 494 495

(51)Shaffer, D. L.; Werber, J. R.; Jaramillo, H.; Lin, S. H.; Elimelech, M. Forward Osmosis: Where are we know? Desalination 2015, 356, 271-284. (52)Li, H. Y.; Chen, V. Membrane Fouling and Cleaning in Food and Bioprocessing. In Membrane Technology, A Practical Guide to Membrane Technology and Applications in Food and Bioprocessing; Cui, Z. F., Muralidhara, H. S., Eds.; Elsevier: Amsterdam, 2010: 213-254. (53)Yip, N. Y.; Elimelech, M. Influence of Natural Organic Matter Fouling and Osmotic Backwash on Pressure Retarded Osmosis Energy Production from Natural Salinity Gradients. Environ. Sci. Technol. 2013, 47, 12607-12616. (54)Wang, D. K.; Zhang, X. W.; Diniz da Costa, J. C. Claisen-type Degradation Mechanism of Cellulose Triacetate Membranes in Ethanol-Water Mixtures. J. Membr. Sci. 2014, 454, 119-125. (55)TENITETM Cellulose Acetate-Chemical Resistance. Eastman Chemical Company, 2012. www.eastman.com. (56)Geens, J.; Peeters, K.; Van der Bruggen, B.; Vandecasteele, C. Polymeric Nanofiltration of Binary Water-alcohol Mixtures: Influence of Feed Composition and Membrane Properties on Permeability and Rejection. J. Membr. Sci. 2005, 255, 255-264. 19

ACS Paragon Plus Environment

Environmental Science & Technology

496 497 498 499 500 501 502 503 504 505 506 507 508 509 510 511 512 513 514 515 516 517 518 519 520 521 522 523 524 525

(57)Geens, J.; Boussu, K.; Vandecasteele, C.; Van der Bruggen, B. Modelling of Solute Transport in Non-aqueous Nanofiltration. J. Membr. Sci. 2006, 281, 139-148. (58)Yang, X. J.; Livingston, A. G.; Freitas dos Santos, L. Experimental Observations of Nanofiltration with Organic Solvents. J. Membr. Sci. 2001, 190, 45-55. (59)Wang, J.; Wang, Z.; Wang, J. X.; Wang, S. C. Improving the Water Flux and Bio-fouling Resistance of Reverse Osmosis (RO) Membrane through Surface Modification by Zwitterionic Polymer. J. Membr. Sci. 2015, 493, 188-199. (60)Chang, Y.; Chen, S. F.; Yu, Q. M.; Zhang, Z.; Bernards, M.; Jiang, S. Y. Development of Biocompatible Interpenetrating Polymer Networks Containing a Sulfobetaine-Based Polymer and A Segmented Polyurethane for Protein Resistance. Biomacromolecules 2007, 8,122-127. (61)Suresh Kumar, G. V.; Rajendraprasad, Y.; Mallikarjuna, B. P.; Chandrashekar, S. M.; Kistayya, C. Synthesis of Some Novel 2-substituted-5-(isopropylthiazole) Clubbed 1,2,4-Triazole and 1,3,4-Oxadiazoles as Potential Antimicrobial and Antitubercular Agents. Eur. J. Med. Chem. 2010, 45, 2063-2074. (62)Singh, A. K.; Singh, P.; Mishra, S.; Shahi, V. K. Anti-biofouling Organic-inorganic Hybrid Membrane for Water Treatment. J. Mater. Chem. 2012, 22, 1834-1844. (63)Lopes, S. M. M.; Novais, J. S.; Costa, D. C. S.; Castro, H. C.; Figueiredo, A. M. S.; Ferreira, V. F.; Pinho E Melo, T. M. V. D.; da Silva, F. C. Hetero-Diels-Alder Reactions of Novel 3triazolyl-nitrosoalkenes as An Approach to Functionalized 1,2,3-Triazoles with Antibacterial Profile. Eur. J. Med. Chem. 2018, 143, 1010-1020. (64)Plech, T.; Kapron, B.; Penech, A.; Kosikowska, U. Search for Factors Affecting Antibacterial Activity and Toxicity of 1,2,4-Triazole-Ciprofloxacin Hybrids. Eur. J. Med. Chem. 2015, 97, 94103. (65)Singh, A. K.; Prakash, S.; Kulshrestha, V.; Shahi, V. K. Cross-Linked Hybrid Nanofiltration Membrane with Antibiofouling Properties and Self-Assembled Layered Morphology. ACS Appl. Mater. Interfaces 2012, 4, 1683-1692. (66)Mansouri, J.; Harrisson, S.; Chen, V. Strategies for Controlling Biofouling in Membrane Filtration Systems: Challenges and Opportunities. J. Mater. Chem. 2010, 20, 4567-4586. (67)Zhu, J. Y.; Wang, J.; Hou, J. W.; Zhang, Y. T.; Liu, J. D.; Van der Bruggen, B. Graphenebased Antimicrobial Polymeric Membranes: A Review. J. Mater. Chem. A. 2017, 5, 6776-6793.

20

ACS Paragon Plus Environment

Page 20 of 27

Page 21 of 27

Environmental Science & Technology

526 527 528 529 530

Figure 1. FESEM images of PTAODH-1.0 (top row), HTI-CTA (middle row), and CSM-TFC (bottom row) membranes: (A), (D), and (G) top surfaces; (B), (E), and (H) bottom surfaces; (C), (F), and (I) cross-sections.

21

ACS Paragon Plus Environment

Environmental Science & Technology

531

532 533 534 535 536 537 538 539 540 541 542 543 544 545

Figure 2. Performance of the PTAODH-1.0, commercial HTI-CTA, and commercial CSM-TFC membranes. (A) Water flux (Jw) and reverse salt flux (Js) for three membranes at different membrane orientations. For the symmetric PTAODH-1.0 membrane, FO-TF indicates that the top surface was facing the feed solution while FOBF indicates that the bottom surface was facing the feed solution. The asymmetric HTICTA and CSM-TFC membranes were evaluated in FO and PRO modes (feed solution facing the active layer and support layer, respectively). (B) Calculated reverse flux selectivities (Jw/Js) for the three types of membranes at the above membrane orientations. FO performance experiments were carried out with an effective membrane area of 10.0 cm2 and a crossflow velocity of 10.4 cm s-1, using 1.5 M Na2SO4 as a draw solution and DI water as feed solution. At least two parallel tests were conducted at 25oC for two hours, presented as average values with error bars. 22

ACS Paragon Plus Environment

Page 22 of 27

Page 23 of 27

Environmental Science & Technology

546 547 548 549 550 551 552 553 554 555 556

Figure 3. Dye concentration experiment using the PTAODH-1.0 membrane. Congo Red (CR) solution was used as the feed with an initial concentration of 1.0 g L-1. A constant draw solution concentration of 1.5 M Na2SO4 was maintained by adding salt as needed at every monitoring time. (A) Variation of water flux, Jw, with time. (B) Variation of Na2SO4 mass and concentration in feed with time due to reverse salt flux. (C) Variation of CR mass in draw solution with time. (D) Calculated and actual CR concentration in the feed and the corresponding FO concentration factor with time. The calculated CR concentration was obtained by the total mass balance of CR in the feed and the draw solution, assuming no adsorption of dye to the membrane.

23

ACS Paragon Plus Environment

Environmental Science & Technology

557

558 559 560 561 562 563 564 565 566

Figure 4. Comparison of membrane cleaning efficiency in terms of the flux recovery ratio (FRR) and variations in Js. (A) FRR and the variation of Js (ΔJs) for PTAODH1.0, HTI-CTA(FO), HTI-CTA(PRO), CSM-TFC(FO), and CSM-TFC(PRO) membranes after cleaning with pure water. (B) FRR and the variation of Js (ΔJs) for the PTAODH-1.0 FO membrane using pure water (PW) and various concentrations (%) of alcohol solutions. (C) FRR and the variation of Js (ΔJs) for the PTAODH-1.0, HTICTA(FO), HTI-CTA(PRO), CSM-TFC(FO), and CSM-TFC(PRO) membranes after washing with 40% alcohol solution. 24

ACS Paragon Plus Environment

Page 24 of 27

Page 25 of 27

Environmental Science & Technology

567 568 569 570 571 572 573 574 575 576 577 578 579

Figure 5. Antibacterial properties of PODH, PTAODH-1.0, HTI-CTA, and CSM-TFC membranes against E. coli and S. aureus. Membrane samples were cut to 2.5 cm × 2.5 cm squares and each contacted with 1.0 mL of bacterial solution (concentration of 1.0×108 CFU mL-1) for three hours. The membranes were taken out, rinsed with sterile saline solution (NaCl, 0.9% (w/v)) to remove unattached cells from the membrane surface, and each immersed in 10 mL of sterile saline solution to detach the deposited cells by mild sonication for five minutes. After cultivation overnight at 37oC, the solutions containing the detached cells were diluted and plated on LB/Agar plates for plate counting. The commercial HTI-CTA membrane was used as a control, and all results were normalized to the result of the HTI-CTA membrane. Four samples of each membrane type were tested against both species of bacteria. Error bars indicate the standard deviations from three independent replicates.

580

25

ACS Paragon Plus Environment

Environmental Science & Technology

581

For Table of Contents Use Only

582

583

26

ACS Paragon Plus Environment

Page 26 of 27

Page 27 of 27

Environmental Science & Technology

50x36mm (300 x 300 DPI)

ACS Paragon Plus Environment