Concentration and Recovery of Dyes from Textile Wastewater using a Self-standing, Support-free Forward Osmosis Membrane Meng Li, Xi Wang, Cassandra J Porter, Wei Cheng, Xuan Zhang, Lianjun Wang, and Menachem Elimelech Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.9b00446 • Publication Date (Web): 25 Feb 2019 Downloaded from http://pubs.acs.org on February 25, 2019
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 27
Environmental Science & Technology
1 2
Concentration and Recovery of Dyes from
3
Textile Wastewater using a Self-standing,
4
Support-free Forward Osmosis Membrane
5
Environmental Science & Technology 6 7 8 9
Meng Li,1 Xi Wang,2 Cassandra J. Porter,3 Wei Cheng,3 Xuan Zhang,1,3* Lianjun Wang,1 and Menachem Elimelech3*
10 11 12
1) Key Laboratory of New Membrane Materials, Ministry of Industry and Information Technology; School of Environmental and Biological Engineering, Nanjing University of Science & Technology, Nanjing 210094, China 2) School of Chemical Engineering, Nanjing University of Science & Technology, Nanjing 210094, China 3) Department of Chemical and Environmental Engineering, Yale University, New Haven, CT 06520-8286, USA 13 14 15 16 17
*Corresponding Author:
18
Xuan Zhang:
[email protected];
19
Menachem Elimelech:
[email protected].
20 1
ACS Paragon Plus Environment
Environmental Science & Technology
ABSTRACT 21
Forward osmosis (FO) can potentially treat textile wastewaters with less fouling than pressure-
22
driven membrane processes such as reverse osmosis and nanofiltration. However, conventional
23
FO membranes with asymmetric architecture experience severe flux decline caused by internal
24
concentration polarization and fouling as dye molecules accumulate on the membrane surface. In
25
this study, we present a new strategy for concentrating dye by using a self-standing, support-free
26
FO membrane with a symmetric structure. The membrane was fabricated by a facile solution-
27
casting approach based on a poly(triazole-co-oxadiazole-co-hydrazine) (PTAODH) skeleton. Due
28
to its dense architecture, ultra-smooth surface, and high negative surface charge, the PTAODH
29
membrane exhibits excellent FO performance with minimal fouling, low reverse salt flux, and
30
negligible dye passage to the draw solution side. Cleaning with a 40% alcohol solution, after
31
achieving a concentration factor of ~10, resulted in high flux recovery ratio (98.7%) for the
32
PTAODH membrane, whereas significant damage to the active layers of two commercial FO
33
membranes was observed. Moreover, due to the existence of cytotoxic oxadiazole and triazole
34
moieties in the polymer structure, our PTAODH membrane exhibited an outstanding antibacterial
35
property with two model bacteria. Our results demonstrate the promising application of the
36
symmetric PTAODH membrane for the concentration of textile wastewaters and its superior
37
antifouling performance compared to state-of-the-art commercial FO membranes.
38
2
ACS Paragon Plus Environment
Page 2 of 27
Page 3 of 27
Environmental Science & Technology
INTRODUCTION 39
Increasing stressors on water resources and growing concerns over pollution of aquatic
40
environments have revived an interest in achieving minimal or zero liquid discharge (ZLD) of
41
industrial wastewaters. Therefore, developing efficient, low-cost technologies for wastewater
42
treatment and reuse has become an important goal.1-3 Dyeing processes in the textile industry are
43
characterized by high water consumption and extremely polluted effluents containing high
44
concentrations of various dyes and salts.4,5 Through separation and concentration processes, useful
45
resources like dyes could be recycled or reused, reducing the risk to the environment and increasing
46
fresh water supply.4
47
Conventional wastewater treatment processes, such as biological degradation,6 adsorption,7
48
advanced oxidation,8 and coagulation-flocculation,9 are widely utilized in the textile industry.
49
However, possible wastewater toxicity to essential microorganisms used in biological reactors,
50
large quantities of chemicals needed for effective treatment, and toxic byproducts render the above
51
treatment techniques quite challenging and unsustainable.
52
Treating textile wastewaters by membrane-based technologies could potentially be simpler and
53
more environmentally friendly compared to conventional processes.4,10-18 The first step in treating
54
dye wastewaters via membrane processes is fractionation, whereby larger dye molecules are
55
selectively retained in the concentrate while smaller salt ions pass through more easily. Recently,
56
several efforts have been made to enable effective separation of inorganic components from textile
57
wastewaters by using commercial10-13 or self-made NF membranes13-18 with loose structures.
58
Following fractionation, retained solutions of valuable dyes undergo a concentration process
59
for their recovery and reuse.13 However, most dye concentration processes experience severe
60
fouling of membrane surfaces, particularly when conventional, pressure-driven membrane
61
processes are used (e.g., ultrafiltration19 and nanofiltration20), which results in rapid flux decline,
62
frequent chemical cleaning, and reduced membrane lifespan. Organic fouling, especially 3
ACS Paragon Plus Environment
Environmental Science & Technology
63
irreversible fouling caused by adsorption or deposition of dyes on the membrane surface,15 is
64
affected by the intrinsic hydrophobicity21-23 and the surface morphology of the membranes.24,25
65
Furthermore, thin-film composite polyamide nanofiltration membranes contain carboxyl groups,
66
which have been shown to enhance organic fouling.26
67
Biofouling is another major performance-limiting factor in nanofiltration,27-29 reverse
68
osmosis,30-33 and forward osmosis.34,35 To mitigate biofilm formation, membrane surfaces have
69
been grafted with biocidal nanomaterials,29-38 such as silver or copper nanoparticles30,32 and
70
graphene oxide (GO) nanosheets.37 However, the added costs and steps during fabrication pose
71
difficulties when manufacturing these hybrid membranes on larger scales, while the potential
72
leaching of nanomaterials may further hinder their commercialization.29,30 Hence, membranes
73
composed of an inherently bactericidal material could be a more commercially viable option.
74
Recently, we have presented a proof-of-concept of a self-standing, support-free FO membrane
75
using a novel poly(triazole-co-oxadiazole-co-hydrazine) (PTAODH) skeleton.39 Due to the
76
symmetric structure of the membrane, no internal concentration polarization was observed when
77
evaluating the FO membrane desalination performance. Uniquely, the membrane is extremely
78
smooth, and due to its robustness there is no need for membrane backing or a support layer. Despite
79
the initial promise, the use of this membrane in emerging FO applications has not previously been
80
demonstrated.
81
In this work, we systematically evaluate the use of the PTAODH thin film for dye
82
concentration in forward osmosis. For comparison, both the PTAODH symmetric membrane and
83
two commercially available asymmetric FO membranes were exposed to an artificial textile
84
wastewater effluent in which Congo Red was used as a model dye. Analyses of dye concentration
85
efficiency, membrane regeneration performance, fouling propensity, and anti-biofouling
86
properties provide insights into the membrane separation and antifouling mechanisms. Our work
87
highlights the potential application of the symmetric FO membranes for sustainable concentration 4
ACS Paragon Plus Environment
Page 4 of 27
Page 5 of 27
88
Environmental Science & Technology
and recovery of valuable dyes in the textile industry.
89
MATERIALS AND METHODS 90
Materials and Chemicals. Polyoxadiazole-co-hydrazide (PODH) and polytriazole-co-
91
oxadiazole-co-hydrazide were synthesized according to our previous report39 and used for the
92
fabrication of the self-standing, support-free FO membrane. The polymeric membrane is
93
composed of a random copolymer containing polytriazole, polyoxadiazole, and polyhydrazine
94
moieties at a controlled proportion. PTAODH-1.0 was used in the current study, where 1.0 denotes
95
the molar ratio of 4-aminobenzoic acid to the repeating unit of PODH during the synthesis.
96
Commercially available cellulose triacetate FO membrane (HTI-CTA) was provided by Hydration
97
Technology Innovations, and polyamide thin-film composite FO membrane (CSM-TFC) was
98
provided by Toray Chemical Korea, Inc. Congo Red (CR) and sodium sulfate (Na2SO4) were
99
procured from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Other reagents and
100
solvents were used as received. Deionized (DI) water with a minimum resistance of 18 MΩ-cm
101
(Millipore) was used throughout the work.
102
Membrane Characterization. Morphologies of the self-standing, support-free membrane
103
(PTAODH-1.0) as well as the commercial HTI-CTA and CSM-TFC membrane samples were
104
studied by field emission scanning electron microscopy (FESEM, S-4800, Hitachi, Japan). All
105
membrane samples were air-dried, fractured in liquid nitrogen, and sputter coated with gold prior
106
to imaging. Surface roughness of all membranes was measured by an Atomic Force Microscope
107
(AFM, Mutilmode8, Germany). At least three measurements were made at different locations for
108
each membrane surface.
109
Dye Concentration Process. In forward osmosis (FO) mode (active layer facing the feed
110
solution), 200 mL of 1.0 g L-1 CR solution and 150 mL of 1.5 M Na2SO4 solution were used as
111
feed solution and draw solution, respectively. The effective membrane area was 10 cm2, and the 5
ACS Paragon Plus Environment
Environmental Science & Technology
Page 6 of 27
112
crossflow velocity was fixed at 10.4 cm s-1, as described elsewhere.39 Reverse salt (Na2SO4)
113
concentration in the feed solution was measured by ion chromatography (Dionex ICS-2100, USA)
114
in terms of SO42- ion content; dye concentration was measured using a UV/VIS spectrometer
115
(Lambda 25, PerkinElmer, USA). Water weight loss of feed solution was recorded by a digital
116
balance to determine the water recovery. The concentration process was stopped at a water
117
recovery ratio of 90%, corresponding to a concentration factor (CF) of 10.
118
Analogously, in pressure-retarded osmosis (PRO) mode (active layer facing the draw solution),
119
the concentration process was the same as described above, except for the orientation of the active
120
layer in the cell. Because PTAODH-1.0 is symmetric, the two modes, denoted as FO-TF and FO-
121
BF, represent testing both sides of the membrane (top surface facing the feed, FO-TF, and bottom
122
surface facing the feed, FO-BF).
123
Membrane Cleaning Strategy. After the concentration stage (water recovery 90% or CF
124
= 10), various solutions were used to clean the fouled FO membranes in the FO setup for 30
125
minutes at room temperature. Pure water, 20%, 40%, 60%, and 80% alcohol solutions were used
126
in the feed side, and DI water was used in the draw side. Crossflow velocity on both the draw and
127
feed sides of the membrane was maintained at 10.4 cm s-1. The flux recovery ratio (FRR), used for
128
evaluating the effectiveness of cleaning the membranes, was calculated by13
FRR
129
J w ,a J w,b
100%
(1)
130
where Jw,b and Jw,a represent the water flux of the CR solution (1.0 g L-1) before fouling and after
131
cleaning, respectively.
132
Evaluation of Antibacterial Properties of FO Membranes. Antibacterial properties
133
of PODH, PTAODH-1.0, HTI-CTA, and CSM-TFC FO membranes were tested against both
134
Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) by a viable cell counting method,
135
as described elsewhere.37,38,40 For both bacteria types, each membrane (HTI-CTA, CSM-TFC, 6
ACS Paragon Plus Environment
Page 7 of 27
Environmental Science & Technology
136
PODH, or PTAODH-1.0) with dimensions of 2.5 cm × 2.5 cm was installed in a sterile, specially
137
designed frame with clamps so that only the active surface was exposed and bacterial suspensions
138
could be contained within the frame. In this holder, the membrane top surfaces were sterilized for
139
30 minutes under UV radiation prior to the antibacterial tests. To prepare bacterial suspensions, E.
140
coli and S. aureus were grown overnight at 37oC in a Luria-Bertani (LB) medium. Cells were
141
collected by centrifugation, washed three times using sterile saline solution (NaCl, 0.9% (w/v)),
142
and diluted to the concentration of 1.0×108 colony-forming units per milliliter (CFU mL-1). A
143
quantity of 1.0 mL of bacterial suspension was poured onto the sterilized membrane surface. After
144
three hours of contact with the bacterial solution, the membrane was taken out and rinsed with a
145
sterile saline solution (NaCl, 0.9% (w/v)) to remove unattached cells on the membrane surface. To
146
detach the deposited cells, the membrane was mildly sonicated for five minutes in 10 mL of sterile
147
saline solution. The solutions were incubated overnight at 37oC and diluted by 100 times before
148
plating on the LB/Agar plates for plate counting.
149
RESULTS AND DISCUSSION 150
Membrane Properties. From our proof-of-concept study to develop a symmetric, support-free
151
membrane for FO,39 the best performing membrane in terms of water flux and salt retention,
152
referred to as PTAODH-1.0, was chosen for the present investigation. The water flux, Jw, and
153
reverse salt flux, Js, of the membrane were found to be 11.7±0.7 L m-2 h-1 and 27.5±2.1 mmol m-2
154
h-1, respectively, when using 1.5 M Na2SO4 as the draw solution. Other physicochemical properties
155
of the membrane, including mechanical robustness, were described in our recent proof-of-concept
156
study.39
157
The morphologies of the PTAODH-1.0 membrane as well as the two commercial membranes
158
used for comparison (HTI-CTA and CSM-TFC) were studied by FESEM. As shown in Figures
159
1A and 1B, the surface morphologies for both sides of the PTAODH-1.0 FO membrane are almost 7
ACS Paragon Plus Environment
Environmental Science & Technology
160
identical, and no visible pores were observed over the entire scanning area. In addition, the cross-
161
section image of PTAODH-1.0 (Figure 1C) portrays its symmetric structure. In contrast, both HTI-
162
CTA and CSM-TFC membranes exhibit typical asymmetric structures with a dense layer on top
163
of a polyester support mesh, as shown in Figures 1F and 1I. The surface roughness of the
164
membranes was analyzed using atomic force microscopy (AFM) (Figure S1 in Supporting
165
Information). The PTAODH-1.0 membrane is extremely smooth and exhibits a very small average
166
plane roughness (Ra) of 0.66±0.08 and 0.69±0.17 nm on each side of the symmetric membrane.
167
In contrast, much greater Ra values were found for both the HTI-CTA (top: 9.95±0.21 nm; bottom:
168
12.6±0.28 nm) and CSM-TFC (top: 30.3±1.84 nm; bottom: 9.6±5.78 nm) membranes. The overall
169
roughness can also be judged by inspecting the top or bottom surface in the SEM images (Figures
170
1D, 1E, 1G, and 1H).
171
Besides exhibiting smoothness on the nanoscale, the PTAODH-1.0 membrane is uniquely
172
smoother than both the HTI-CTA and CSM-TFC membranes on the microscale owing to its
173
robustness, which eliminates the need for a supportive membrane backing. As seen in Figures 1F
174
and 1I, the mesh support backings produce a regular pattern of microscale peaks and valleys on
175
both the top and bottom surfaces of the HTI-CTA and CSM-TFC membranes. Considering that
176
bacteria and aggregates of highly concentrated dyes 41 fall within the microscale range as opposed
177
to the nanoscale, perhaps microscale roughness may be more influential for both organic and
178
biofouling. Studies have shown that areas with the greatest fouling propensity are often dead zones,
179
especially in crossflow systems.42,43 Dead zones are caused more frequently by micro- and
180
macroscale structures, such as the presence of spacers,44 than by nanoscale roughness. In the case
181
of HTI-CTA and CSM-TFC membranes, such dead zones create near-stagnant flow, which
182
decreases mixing, thereby increasing concentration polarization (CP) and rates of organic and bio-
183
foulant deposition. Furthermore, such dead zones can also decrease the effectiveness of cleaning,
184
since cleaning relies on not only the foulant’s solubility in the cleaning solution but also on shear
185
forces. The positive impact of the extreme smoothness of the PTAODH-1.0 membrane at both the 8
ACS Paragon Plus Environment
Page 8 of 27
Page 9 of 27
Environmental Science & Technology
186
nano- and micro-scales is evident in the results of our dye concentration and membrane cleaning
187
studies, discussed in the following sections.
188
Figure 1
189 190 191
Desalination performance in FO (feed solution facing membrane active layer) and PRO (feed
192
solution facing membrane support layer) modes was investigated for all three types of membranes.
193
As shown in Figure 2, for the PTAODH-1.0 membrane, Jw and Js were consistent at both
194
orientations, which again is indicative of membrane symmetry. In contrast, both HTI-CTA and
195
CSM-TFC membranes exhibited markedly different desalination behaviors depending on their
196
orientation. The water flux for the HTI-CTA membrane in PRO mode (10.2±0.4 L m-2 h-1) was
197
slightly greater than that in FO mode (8.5±0.2 L m-2 h-1), whereas much greater Jw was found for
198
the CSM-TFC membrane in PRO mode (44.1±1.3 L m-2 h-1) than that in FO mode (21.0±2.5 L m-2
199
h-1). These results are attributed to the different extents of internal concentration polarization (ICP)
200
in FO (dilutive ICP) and PRO (concentrative ICP) modes.45,46 Although the pure water
201
permeability (A) value of our symmetric membrane (0.118 L m-2 h-1 bar-1) was lower than the
202
commercial membranes (0.375 L m-2 h-1 bar-1for HTI-CTA39,47 and 4.192 L m-2 h-1 bar-1 for CSM-
203
TFC
204
performance of a membrane,50 was still quite acceptable. Specifically, the reverse flux selectivities
205
of our symmetric membrane for FO-TF and FO-BF modes were 426.2±5.2 L mol-1 and 430.0±10.7
206
L mol-1, respectively, higher than those of the HTI-CTA membrane (FO mode: 384.9±20.8 L mol-1;
207
PRO mode: 397.8±22.0 L mol-1), but only slightly lower than those of the CSM-TFC membrane
208
(FO mode: 501.4±19.6 L mol-1; PRO mode: 579.8±53.6 L mol-1) (Figure 2B). The above Jw/Js
209
ratio of the PTAODH-1.0 membrane reflects a desalination efficiency comparable to that of the
210
commercial membranes.
48,49),
its reverse flux selectivity (Jw/Js), an essential parameter representing the FO
9
ACS Paragon Plus Environment
Environmental Science & Technology
211
Figure 2
212 213 214
Dye Concentration Performance. High salinities of up to ~6% (approximately 60,000 mg
215
L-1 TDS calculated as pure NaCl) in textile wastewaters present challenges for both conventional
216
and membrane-based treatment technologies.12,19 In conventional treatment, such high salt content
217
adversely impacts microorganisms that are used in biological reactors for degradation of dyes. For
218
FO dye concentration, high-salinity feed decreases the osmotic pressure driving force between the
219
feed and draw solution, thereby decreasing water flux. Therefore, separation of dyes from salt
220
seems a necessary prerequisite before degradation or concentration and reuse of dye. However,
221
state-of-the-art membranes still exhibit severe fouling caused by dye moleculeswhether treating
222
dye/salt mixtures or pure dye solutions,10,13,14 as discussed earlier. Particularly for high water
223
recovery ratios, frequent cleaning would be necessary to maintain the production rate, leading to
224
high energy consumption.
225
In contrast, PTAODH-1.0, a smooth, symmetric thin film, shows more promise for dye
226
concentration. Under periodic supplement of Na2SO4 to keep a constant draw solution osmotic
227
pressure, Jw remained relatively stable at 10.6±0.3 L m-2 h-1 over the entire concentration procedure
228
until CF ~10 (Figure 3A), which is directly related to minimal fouling at the feed side as well as
229
negligible ICP.39,51 Moreover, it was reported that membrane surface roughness can act as a
230
structural template for initial layers of foulant.52 Our membrane with an ultra-smooth surface
231
effectively prevents the adhesion of dye molecules, slowing fouling rates and extending membrane
232
life.
233
In marked contrast to the symmetric PTAODH-1.0 membrane, the HTI-CTA and CSM-TFC
234
membranes, with their asymmetric structure, exhibited significant Jw decline both in the FO and
235
PRO modes (Figures S2A, S3A, S4A, and S5A). Specifically, the Jw in FO decreased by 38.3% 10
ACS Paragon Plus Environment
Page 10 of 27
Page 11 of 27
Environmental Science & Technology
236
from 8.1 to 5.0 L m-2 h-1 and by 37.7% from 15.9 to 9.9 L m-2 h-1 for the HTI-CTA and CSM-TFC
237
membranes, respectively, over the time taken to reach CF ~10. The severe flux decline observed
238
for the commercial asymmetric FO membranes is attributed to significant fouling. With the more
239
porous support mesh layer of the commercial membranes facing the dye solution in PRO mode,
240
the Jw (PRO) suffered considerable flux decline due to accumulation of dye foulants in the porous
241
support layer:53 by 57.7% from the initial 9.7 to 4.1 L m-2 h-1 (HTI-CTA) and by 87.5% from the
242
initial 26.3 to 3.3 L m-2 h-1 (CSM-TFC). As evidenced by these results, the ultra-smooth PTAODH-
243
1.0 membrane, consisting of a symmetric architecture without a backing layer, could eliminate
244
ICP and minimize dye entrapment and cake layer formation during dye concentration.
245
The PTAODH-1.0 membrane also showed robust performance, achieving 10-fold dye
246
concentration within 18 hours (Figure 3D). In contrast, it took ~60% and ~40% more time for the
247
HTI-CTA membrane in FO and PRO modes, respectively (Figures S2 and S3) to achieve 10-fold
248
dye concentration. While the CSM-TFC membrane was able to achieve a 10-fold dye
249
concentration within 14 hours, slightly better than the PTAODH-1.0 membrane, the severe fouling
250
and need for chemical cleaning will be a major hindrance to practical application. Furthermore,
251
future improvement of the PTAODH-1.0 membrane fabrication, for example by reducing
252
membrane thickness and thus increasing water flux, could readily enhance the performance of the
253
membrane.
254
During the entire concentration process, all three membranes possessed rather high dye
255
retention and salt rejection (Figures 3B-3C, S2B-S2C, S3B-S3C, S4B-S4C, and S5B-S5C).
256
Specifically, the PTAODH-1.0 membrane only allows 0.37 mmol Na2SO4 to diffuse into the feed
257
solution until the end of operation, due to its inherently low Js values (23.9±2.8 mmol m-2 h-1).
258
Moreover, a tiny amount of the dye, linearly increasing over time, was found in the draw solution
259
with a final concentration of merely 2.2×10-3 mmol L-1 (Figure 3C), matching the final dye
260
concentration in the draw for both HTI-CTA and CSM-TFC membranes under FO operation mode.
11
ACS Paragon Plus Environment
Environmental Science & Technology
261
It is worth mentioning that the excellent retention of dye by the PTAODH-1.0 membrane is
262
also evident in the overlap between empirical and calculated dye concentration values, as shown
263
in Figure 3D. The actual concentration of CR was found to be 9.99 g L-1 when the CF reached ~10,
264
which was slightly lower than the theoretical value of 10.06 g L-1. Such a small discrepancy is
265
within the margin of error of our measurement method.
266 267
Figure 3
268 269
Membrane Cleaning and Regeneration. As seen in Figure S6, the images of the three
270
membrane types before and after the concentration process indicate differences in fouling
271
propensity. A very light red color could be seen on the surface of PTAODH-1.0, suggesting only
272
slight dye adsorption, while both the HTI-CTA and CSM-TFC membranes (PRO mode) developed
273
deep red color due to significant adsorption and accumulation of dye molecules.
274
In spite of insignificant fouling on the PTAODH-1.0 membrane during FO operation, a proper
275
cleaning strategy is necessary to maintain membrane desalination performance. The PTAODH-
276
1.0 membrane exhibits a relatively high FRR of 93±1.1% after rinsing with pure water, exceeding
277
the FRR of the HTI-CTA (at 86.3% and 76.7% for FO and PRO modes, respectively) and the
278
CSM-TFC (at 84.3% and 64.8% for FO and PRO modes, respectively) membranes (Figure 4A).
279
However, in order to maximize the FRR, it is advantageous to use a cleaning solution that better
280
dissolves the foulant of interest without damaging the membrane. Because dye molecules are
281
generally more soluble in organic solvents than in aqueous solution,13 alcohol solutions were
282
employed here. As shown in Figure 4B, the FRR of the PTAODH-1.0 membrane considerably
283
increases to 96.6% and 98.7% with a negligible increase in Js by cleaning with 20% or 40% of
284
ethanol/water solution, respectively, indicating the membrane good antifouling and solvent-
285
resistant properties. However, a sharp increase of Js up to 125.7 mmol m-2 h-1 was observed when 12
ACS Paragon Plus Environment
Page 12 of 27
Page 13 of 27
Environmental Science & Technology
286
cleaning with an 80% alcohol solution, which caused the FO performance to deteriorate. We
287
attribute this phenomenon to the physical expansion of the interstitial spaces within the membrane
288
matrix caused by excessive ethanol.13,52
289
Based on the above results, a 40% alcohol solution was chosen as the optimal cleaning medium
290
for comparing the performance of the three membrane types. As shown in Figure 4C, unlike the
291
superb performance of the PTAODH-1.0 membrane, after cleaning in FO mode, the HTI-CTA
292
membrane rejected Na2SO4 considerably less (Js increased to 75.2 mmol m-2 h-1) with an FRR of
293
106.3%, while only a moderate FRR of 92.2% was found for CSM-TFC membrane. Several
294
studies suggest that cellulose triacetate could swell or even degrade in the presence of ethanol by
295
a Claisen condensation reaction.54,55 Other studies suggested variation of pore size and pore density
296
of the polyamide layer in TFC membranes due to the contact with ethanol, causing severe volume
297
expansion or curling of the polymer matrix.56-58 Thus, the poor regeneration of both the HTI-CTA
298
and CSM-TFC membranes with alcohol solutions was probably due to the physical collapse of the
299
active layer, which hinders thorough cleansing in commercial applications.
300 301
Figure 4
302 303
Membrane Antibacterial Property. The antibacterial property of the PTAODH-1.0
304
membrane was investigated using two model bacteria, E. coli (Gram-negative) and S. aureus
305
(Gram-positive). To better understand the antibacterial mechanism, PODH (the precursor of
306
PTAODH without 1,2,4-triazole moiety) as well as the commercial FO membranes were included
307
in the investigation. The results, presented as percent of colony-forming units (CFU) compared
308
the control after three hours contact time, are shown in Figure 5. Based on their biocompatible
309
chemical structure,59,60 both the HTI-CTA and CSM-TFC membranes exhibit negligible
310
antibacterial activity against both bacteria types. Although the triazole moiety was found to 13
ACS Paragon Plus Environment
Environmental Science & Technology
311
comprise only ~10 mol% of the PTAODH-1.0 backbone (calculated from our previous study),39
312
significantly low cell viabilities of 14.0±1.4% and 18.0±12.6% were achieved against E. coli and
313
S. aureus, respectively. It has been reported that the hydrophilicity of oxadiazole and triazole
314
groups could disrupt the normal metabolism of bacterial cells by inhibiting the production of lipids
315
necessary for cell-wall biosynthesis, thus inhibiting bacterial reproduction.61-65 The triazole moiety
316
was even revealed to have cytotoxicity that may cause a fast cell deactivation.61 Moreover, the
317
smooth surface of the PTAODH-1.0 membrane could also prevent bacterial adhesion, growth,
318
proliferation, and subsequent formation of biofilm.66,67 Thus, both bacteriostatic/bactericidal
319
mechanisms and morphology contribute to the outstanding antibacterial properties of our
320
membrane PTAODH-1.0.
321
Figure 5
322 323
ASSOCIATED CONTENT 324
Supporting Information Available: Supporting figures include AFM morphology of PTAODH-
325
1.0, HTI-CTA, and CSM-TFC membranes (Figure S1); results of concentration experiment using
326
HTI-CTA membrane (FO mode) (Figure S2); results of concentration experiment using HTI-CTA
327
membrane (PRO mode) (Figure S3); results of concentration experiment using CSM-TFC
328
membrane (FO mode) (Figure S4); results of concentration experiment using CSM-TFC
329
membrane (PRO mode) (Figure S5); and images of all three membranes before dye concentration,
330
after dye concentration, and after physical cleaning (Figure S6). This material is available free of
331
charge via the internet at https://pubs.acs.org/.
332
AUTHOR INFORMATION 333
Corresponding Author 14
ACS Paragon Plus Environment
Page 14 of 27
Page 15 of 27
Environmental Science & Technology
334
* Xuan Zhang:
[email protected].
335
* Menachem Elimelech:
[email protected]. Notes
336
The authors declare no competing financial interest. ACKNOWLEDGMENTS
337
This work was supported by the National Natural Science Foundation of China (21774058,
338
51778292), the Natural Science Foundation of Jiangsu Province (BK20180072), and the
339
Postgraduate Research & Practice Innovation Program of Jiangsu Province (KYCX18_0480).
340
REFERENCES 341 342 343 344 345 346 347 348 349 350 351 352 353 354 355 356 357 358 359
(1) Werber, J. R.; Deshmukh, A.; Elimelech, M. The Critical Need for Increased Selectivity, Not Increased Water Permeability, for Desalination Membranes. Environ. Sci. Technol. Lett. 2016, 3, 112-120. (2) Tang, C. Y.; Yang, Z.; Guo, H.; Wen, J. J.; Nghiem, L. D.; Cornelissen, E. Potable Water Reuse through Advanced Membrane Technology. Environ. Sci. Technol. 2018, 52, 10215-10223. (3) Phuntsho, S.; Shon, H. K.; Majeed, T.; EI Saliby, I.; Viqneswaran, S.; Kandasamy, J.; Hong, S.; Lee, S. Blended fertilizers as draw solutions for fertilizer-drawn forward osmosis desalination. Environ. Sci. Technol. 2012, 46, 4567-4575. (4) Petrinić, I.; Bajraktari, N.; Hélix-Nielsen, C. Membrane Technologies for Water Treatment and Reuse in the Textile Industry. Advances in Membrane Technologies for Water Treatment. 2015, 2, 537-550. (5) Jiang, M.; Ye, K. F.; Deng, J. J.; Lin, J. Y.; Ye, W. Y.; Zhao, S. F.; Var der Bruggen, B. Conventional Ultrafiltration as Effective Strategy for Dye/Salt Fractionation in Textile Wastewater Treatment. Environ. Sci. Technol. 2018, 52, 10698-10708. (6) Gupta, V. K.; Bhushan, R.; Nayak, A.; Singh, P.; Bhushan, B. Biosorption and Reuse Potential of A Blue Green Alga for the Removal of Hazardous Reactive Dyes from Aqueous Solutions. Bioremediat. J. 2014, 18, 179-191. (7) Cardoso, N. F.; Lima, E. C.; Royer, B.; Bach, M. V.; Dotto, G. L.; Pinto, L. A.; Calvete, T. Comparison of Spirulina Platensis Microalgae and Commercial Activated Carbon as Adsorbents 15
ACS Paragon Plus Environment
Environmental Science & Technology
360 361 362 363 364 365 366 367 368 369 370 371 372 373 374 375 376 377 378 379 380 381 382 383 384 385 386 387 388 389 390 391 392 393 394
for the Removal of Reactive Red 120 Dye from Aqueous Effluents. J. Hazard. Mater. 2012, 241, 146-153. (8) Oller, I.; Malato, S.; Sánchez-Pérez, J. Combination of Advanced Oxidation Processes and Biological Treatments for Wastewater Decontamination: A Review. Sci. Total Environ. 2011, 409, 4141-4166. (9) Verma, A. K.; Dash, R. R.; Bhunia, P. A Review on Chemical Coagulation/Flocculation Technologies for Removal of Colour from Textile Wastewaters. J. Environ. Manage. 2012, 93, 154-168. (10)Lin, J.; Ye, W.; Zeng, H; Yang, J.; Shen.; Darvishmanesh, S.; Luis, P.; Sotto, A.; Van der Bruggen, B. Fractionation of Direct Dyes and Salts in Aqueous Solution using Loose Nanofiltration Membranes. J. Membr. Sci. 2015, 477, 183-193. (11)Ye, W. Y.; Lin, J. Y.; Borrego, R.; Tang, C. Y.; Van der Bruggen, B. Advanced Desalination of Dye/NaCl Mixtures by A Loose Nanofiltration Membrane for Digital Ink-jet Printing. Sep. Purif. Technol. 2018, 197, 27-35. (12) Lin, J. Y.; Tang, C. Y.; Ye, W. Y.; Sun, S. P.; Van der Bruggen, B. Unraveling Flux Behavior of Superhydrophilic Loose Nanofiltration Membranes during Textile Wastewater Treatment. J. Membr. Sci. 2015, 493, 690-702. (13)Li, M.; Yao, Y. J.; Zhang, W.; Zheng, J. F.; Zhang, X.; Wang, L J. Fractionation and Concentration of High-Salinity Textile Wastewater using an Ultra-Permeable Sulfonated Thinfilm Composite. Environ. Sci. Technol. 2017, 51, 9252-9260. (14)Lau, W. J.; Ismail, A. F. Polymeric Nanofiltration Membranes for Textile Dye Wastewater Treatment: Preparation, Performance Evaluation, Transport Modelling, and Fouling Control-A Review. Desalination 2009, 245, 321-348. (15)Zhao, S.; Wang, Z. A Loose Nanofiltration Membrane Prepared by Coating HPAN UF Membrane with Modified PEI for Dye Reuse and Desalination. J. Membr. Sci. 2017, 524, 214224. (16) Xing, L. X.; Guo, N. N.; Zhang, Y. T.; Zhang, H. Q.; Liu, J. D. A Negatively Charged Loose Nanofiltration Membrane by Blending with Poly(sodium 4-styrene sulfonate) Grafted SiO2 via SIATRP for Dye Purification. Sep. Purif. Technol. 2015, 146, 50-59. (17)Zhua, J. Y.; Tian, M. M.; Zhang, Y. T.; Zhang, H. Q.; Liu, J. D. Fabrication of A Novel “Loose” Nanofiltration Membrane by Facile Blending with Chitosan-Montmorillonite Nanosheets for Dyes Purification. Chem. Eng. J. 2015, 265, 184-193. (18)Chen, P.; Ma, X.; Zhong, Z.; Zhang, F.; Xing, W.; Fan, Y. Performance of Ceramic Nanofiltration Membrane for Desalination of Dye Solutions Containing NaCl and Na2SO4. Desalination 2017, 404, 102-111. 16
ACS Paragon Plus Environment
Page 16 of 27
Page 17 of 27
395 396 397 398 399 400 401 402 403 404 405 406 407 408 409 410 411 412 413 414 415 416 417 418 419 420 421 422 423 424 425 426 427
Environmental Science & Technology
(19)Lin, J. Y.; Ye, W. Y.; Baltaru, M. C.; Tang, Y. P.; Van der Bruggen, B. Tight Ultrafiltration Membranes for Enhanced Separation of Dyes and Na2SO4 during Textile Wastewater Treatment. J. Membr. Sci. 2016, 514, 217-228. (20)Chidambaram, T.; Oren, Y.; Noel, M. Fouling of Nanofiltration Membranes by Dyes during Brine Recovery from Textile Dye Bath Wastewater. Chem. Eng. J. 2015, 262, 156-168. (21)Qin, D. T.; Liu, Z. Y.; Liu, Z.; Bai, H. W.; Sun, D. D. Superior Antifouling Capability of Hydrogel Forward Osmosis Membrane for Treating Wastewaters with High Concentration of Organic Foulants. Environ. Sci. Technol. 2018, 52, 1421-1428. (22)Zhang, X. Y.; Tian, J. Y.; Gao, S. S.; Shi. W. X.; Liu, D. M. Surface Functionalization of TFC FO Membranes with Zwitterionic Polymers: Improvement of Antifouling and Salt-responsive Cleaning Properties. J. Membr. Sci. 2017, 544, 368-377. (23) Chen, S. F.; Li, L. Y.; Zhao, C.; Zheng, J. Surface Hydration: Principles and Applications Toward Low-fouling/Nonfouling Biomaterials. Polymer 2010, 51, 5283-5293. (24)Elimelech, M.; Zhu, X. H.; Childress, A. E.; Hong, S. K. Role of Membrane Surface Morphology in Colloidal Fouling of Cellulose Acetate and Composite Aromatic Polyamide Reverse Osmosis Membranes. J. Membr. Sci. 1997, 127, 101-109. (25)Vrijenhoek, E. M.; Hong, S.; Elimelech, M. Influence of Membrane Surface Properties on Initial Rate of Colloidal Fouling of Reverse Osmosis and Nanofiltration Membranes. J. Membr. Sci. 2001, 188, 115-128. (26)Mo, Y. H.; Tiraferri, A.; Yip, N. Y.; Adout, A.; Huang, X.; Elimelech, M. Improved Antifouling Properties of Polyamide Nanofiltration Membranes by Reducing the Density of Surface Carboxyl Groups. Environ. Sci. Technol. 2012, 46, 13253-13261. (27)Bottom, S.; Verliefde, A. R. D.; Quach, N. T.; Cornelissen, E. R. Influence of Biofouling on Pharmaceuticals Rejection in NF Membrane Filtration. Water Res. 2012, 46, 5848-5860. (28)Wang, J.; Wang, Z.; Liu, Y. Y.; Wang, J. X.; Wang, S. C. Surface Modification of NF Membrane with Zwitterionic Polymer to Improve Anti-biofouling Property. J. Membr. Sci. 2016, 514, 407-417. (29)Zheng, J. F.; Li, M.; Yao, Y. J.; Zhang, X.; Wang, L. J. Zwitterionic Carbon Nanotube Assisted Thin-film Nanocomposite Membranes with Excellent Efficiency for Separation of Mono/Divalent Ions from Brackish Water. J. Mater. Chem. A. 2017, 5, 13730-13739. (30)Ben-Sasson, M.; Zodrow, K. R.; Qi, G. G.; Kang, Y.; Gianelis, E. P.; Elimelech, M. Surface Functionalization of Thin-Film Composite Membranes with Copper Nanoparticles for Antimicrobial Surface Properties. Environ. Sci. Technol. 2014, 48, 384-393.
17
ACS Paragon Plus Environment
Environmental Science & Technology
428 429 430 431 432 433 434 435 436 437 438 439 440 441 442 443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 458 459 460
(31)Park, S. H.; Ko, Y. S.; Park, S. J.; Lee, J. S.; Cho, J. H.; Lee, J. H. Immobilization of Silver Nanoparticle-decorated Silica Particles on Polyamide Thin Film Composite Membranes for Antibacterial Properties. J. Membr. Sci. 2016, 499, 80-91. (32)Ben-Sasson, M.; Lu, X. L.; Bar-Zeev, E.; Zodrow, K. R.; Nejati, S.; Qi, G. G.; Giannelis, E. P.; Elimelech, M. In Situ Formation of Silver Nanoparticles on Thin-film Composite Reverse Osmosis Membranes for Biofouling Mitigation. Water Res. 2014, 62, 260-270. (33)Rahaman, M. S.; Thérien-Aubin, H.; Ben-Sasson, M.; Ober, C. K.; Nielsen, M.; Elimelech, M. Control of Biofouling on Reverse Osmosis Polyamide Membranes Modified with Biocidal Nanoparticles and Antifouling Polymer Brushes. J. Mater. Chem. B. 2014, 2, 1724-1732. (34)Faria, A. F.; Liu, C. H.; Xie, M.; Perreault, F.; Nghiem, L. D.; Ma, J.; Elimelech, M. Thinfilm Composite Forward Osmosis Membranes Functionalized with Graphene Oxide-silver Nanocomposites for Biofouling Control. J. Membr. Sci. 2017, 525, 146-156. (35)Bogler, A.; Lin, S. H.; Bar-Zeev, E. Biofouling of Membrane Distillation, Forward Osmosis and Pressure Retarded Osmosis: Principles, Impacts and Future Directions. J. Membr. Sci. 2017, 542, 378-398. (36)Diagne, F.; Malaisamy, R.; Boddie, V.; Holbrook, R. D.; Eribo, B.; Jones, K. L. Polyelectrolyte and Silver Nanoparticle Modification of Microfiltration Membranes to Mitigate Organic and Bacterial Fouling. Environ. Sci. Technol. 2012, 46, 4025-4033. (37)Perreault, F.; Tousley, M. E.; Elimelech, M. Thin-film Composite Polyamide Membranes Functionalized with Biocidal Graphene Oxide Nanosheets. Environ. Sci. Technol. Lett. 2014, 1, 71-76. (38)Lu, X. L.; Feng, X. D.; Werber, J. R.; Chu, C. H.; Zucker, I.; Kim, J. H.; Osuji, C. O.; Elimelech, M. Enhanced antibacterial activity through the controlled alignment of graphene oxide nanosheets. Proc. Natl. Acad. Sci. U. S. A. 2017, 114, 9793-9801. (39)Li, M.; Karanikola, V.; Zhang, X.; Wang, L. J.; Elimelech, M. A Self-standing, Support-Free Membrane for Forward Osmosis with No Internal Concentration Polarization. Environ. Sci. Technol. Lett. 2018, 5, 266-271. (40)Perreault, F.; de Faria, A. F.; Nejati S.; Elimelech, M. Antimicrobial Properties of Graphene Oxide Nanosheets: Why Size Matters. ACS Nano 2015, 9, 7226-7236. (41)Hillson, P. J.; McKay, R. B. Aggregation of Dye Molecules in Aqueous Solution A Polarographic Study. Trans. Faraday Soc. 1965, 61, 374-382. (42)Chen, K. L.; Song, L. F.; Ong, S. L.; Ng, W. J. The Development of Membrane Fouling in Full-scale RO Processes. J. Membr. Sci. 2004, 232, 63-72.
18
ACS Paragon Plus Environment
Page 18 of 27
Page 19 of 27
461 462 463 464 465 466 467 468 469 470 471 472 473 474
Environmental Science & Technology
(43)Lotfi, F.; Chekli, L.; Phuntsho, S.; Hong, S.; Choi, J. Y.; Shon, H. K. Understanding the Possible Underlying Mechanisms for Low Fouling Tendency of The Forward Osmosis and Pressure Assisted Osmosis Processes. Desalination 2017, 421, 89-98. (44)Vrouwenvelder, J. S.; Graf von der Schulenburg, D. A.; Kruithof, J. C.; Johns, M. L.; van Loosfrecht, M. C. Biofouling of Spiral-wound Nanofiltration and Reverse Osmosis Membranes: A feed spacer problem. Water Res. 2009, 43, 583-594. (45)Fang, L. F.; Cheng, L.; Jeon, S.; Wang, S. Y.; Takahashi, T.; Matsuyama, H. Effect of the Supporting Layer Structures on Antifouling Properties of Forward Osmosis Membranes in AL-DS Mode. J. Membr. Sci. 2018, 552, 265-273. (46)Gray, G.T.; McCutcheon, J.R.; Elimelech, M. Internal Concentration Polarization in Forward Osmosis: Role of Membrane Orientation. Desalination 2006, 197, 1-8. (47)Yip, N.Y.; Tiraferri, A.; Phillip, W. A.; Schiffman, J. D.; Elimelech, M. High Performance Thin-film Composite Forward Osmosis Membrane. Environ. Sci. Technol. 2010, 44, 38123818.
477
(48)Nguyen, T. P. N.; Jun, B. M.; Lee, J. H.; Kwon, Y. N. Comparison of Integrally Asymmetric and Thin Film Composite Structures for a Desirable Fashion of Forward Osmosis Membranes. J. Membr. Sci. 2015, 495, 457-470.
478
(49)Data Sheet CSM Forward Osmosis Membrane. Toray Chemical Korea Inc.
479
(50)Phillip, W. A.; Yong, J. S.; Elimelech, M. Reverse Draw Solute Permeation in Forward Osmosis: Modeling and Experiments. Environ. Sci. Technol. 2010, 44, 5170-5176.
475 476
480 481 482 483 484 485 486 487 488 489 490 491 492 493 494 495
(51)Shaffer, D. L.; Werber, J. R.; Jaramillo, H.; Lin, S. H.; Elimelech, M. Forward Osmosis: Where are we know? Desalination 2015, 356, 271-284. (52)Li, H. Y.; Chen, V. Membrane Fouling and Cleaning in Food and Bioprocessing. In Membrane Technology, A Practical Guide to Membrane Technology and Applications in Food and Bioprocessing; Cui, Z. F., Muralidhara, H. S., Eds.; Elsevier: Amsterdam, 2010: 213-254. (53)Yip, N. Y.; Elimelech, M. Influence of Natural Organic Matter Fouling and Osmotic Backwash on Pressure Retarded Osmosis Energy Production from Natural Salinity Gradients. Environ. Sci. Technol. 2013, 47, 12607-12616. (54)Wang, D. K.; Zhang, X. W.; Diniz da Costa, J. C. Claisen-type Degradation Mechanism of Cellulose Triacetate Membranes in Ethanol-Water Mixtures. J. Membr. Sci. 2014, 454, 119-125. (55)TENITETM Cellulose Acetate-Chemical Resistance. Eastman Chemical Company, 2012. www.eastman.com. (56)Geens, J.; Peeters, K.; Van der Bruggen, B.; Vandecasteele, C. Polymeric Nanofiltration of Binary Water-alcohol Mixtures: Influence of Feed Composition and Membrane Properties on Permeability and Rejection. J. Membr. Sci. 2005, 255, 255-264. 19
ACS Paragon Plus Environment
Environmental Science & Technology
496 497 498 499 500 501 502 503 504 505 506 507 508 509 510 511 512 513 514 515 516 517 518 519 520 521 522 523 524 525
(57)Geens, J.; Boussu, K.; Vandecasteele, C.; Van der Bruggen, B. Modelling of Solute Transport in Non-aqueous Nanofiltration. J. Membr. Sci. 2006, 281, 139-148. (58)Yang, X. J.; Livingston, A. G.; Freitas dos Santos, L. Experimental Observations of Nanofiltration with Organic Solvents. J. Membr. Sci. 2001, 190, 45-55. (59)Wang, J.; Wang, Z.; Wang, J. X.; Wang, S. C. Improving the Water Flux and Bio-fouling Resistance of Reverse Osmosis (RO) Membrane through Surface Modification by Zwitterionic Polymer. J. Membr. Sci. 2015, 493, 188-199. (60)Chang, Y.; Chen, S. F.; Yu, Q. M.; Zhang, Z.; Bernards, M.; Jiang, S. Y. Development of Biocompatible Interpenetrating Polymer Networks Containing a Sulfobetaine-Based Polymer and A Segmented Polyurethane for Protein Resistance. Biomacromolecules 2007, 8,122-127. (61)Suresh Kumar, G. V.; Rajendraprasad, Y.; Mallikarjuna, B. P.; Chandrashekar, S. M.; Kistayya, C. Synthesis of Some Novel 2-substituted-5-(isopropylthiazole) Clubbed 1,2,4-Triazole and 1,3,4-Oxadiazoles as Potential Antimicrobial and Antitubercular Agents. Eur. J. Med. Chem. 2010, 45, 2063-2074. (62)Singh, A. K.; Singh, P.; Mishra, S.; Shahi, V. K. Anti-biofouling Organic-inorganic Hybrid Membrane for Water Treatment. J. Mater. Chem. 2012, 22, 1834-1844. (63)Lopes, S. M. M.; Novais, J. S.; Costa, D. C. S.; Castro, H. C.; Figueiredo, A. M. S.; Ferreira, V. F.; Pinho E Melo, T. M. V. D.; da Silva, F. C. Hetero-Diels-Alder Reactions of Novel 3triazolyl-nitrosoalkenes as An Approach to Functionalized 1,2,3-Triazoles with Antibacterial Profile. Eur. J. Med. Chem. 2018, 143, 1010-1020. (64)Plech, T.; Kapron, B.; Penech, A.; Kosikowska, U. Search for Factors Affecting Antibacterial Activity and Toxicity of 1,2,4-Triazole-Ciprofloxacin Hybrids. Eur. J. Med. Chem. 2015, 97, 94103. (65)Singh, A. K.; Prakash, S.; Kulshrestha, V.; Shahi, V. K. Cross-Linked Hybrid Nanofiltration Membrane with Antibiofouling Properties and Self-Assembled Layered Morphology. ACS Appl. Mater. Interfaces 2012, 4, 1683-1692. (66)Mansouri, J.; Harrisson, S.; Chen, V. Strategies for Controlling Biofouling in Membrane Filtration Systems: Challenges and Opportunities. J. Mater. Chem. 2010, 20, 4567-4586. (67)Zhu, J. Y.; Wang, J.; Hou, J. W.; Zhang, Y. T.; Liu, J. D.; Van der Bruggen, B. Graphenebased Antimicrobial Polymeric Membranes: A Review. J. Mater. Chem. A. 2017, 5, 6776-6793.
20
ACS Paragon Plus Environment
Page 20 of 27
Page 21 of 27
Environmental Science & Technology
526 527 528 529 530
Figure 1. FESEM images of PTAODH-1.0 (top row), HTI-CTA (middle row), and CSM-TFC (bottom row) membranes: (A), (D), and (G) top surfaces; (B), (E), and (H) bottom surfaces; (C), (F), and (I) cross-sections.
21
ACS Paragon Plus Environment
Environmental Science & Technology
531
532 533 534 535 536 537 538 539 540 541 542 543 544 545
Figure 2. Performance of the PTAODH-1.0, commercial HTI-CTA, and commercial CSM-TFC membranes. (A) Water flux (Jw) and reverse salt flux (Js) for three membranes at different membrane orientations. For the symmetric PTAODH-1.0 membrane, FO-TF indicates that the top surface was facing the feed solution while FOBF indicates that the bottom surface was facing the feed solution. The asymmetric HTICTA and CSM-TFC membranes were evaluated in FO and PRO modes (feed solution facing the active layer and support layer, respectively). (B) Calculated reverse flux selectivities (Jw/Js) for the three types of membranes at the above membrane orientations. FO performance experiments were carried out with an effective membrane area of 10.0 cm2 and a crossflow velocity of 10.4 cm s-1, using 1.5 M Na2SO4 as a draw solution and DI water as feed solution. At least two parallel tests were conducted at 25oC for two hours, presented as average values with error bars. 22
ACS Paragon Plus Environment
Page 22 of 27
Page 23 of 27
Environmental Science & Technology
546 547 548 549 550 551 552 553 554 555 556
Figure 3. Dye concentration experiment using the PTAODH-1.0 membrane. Congo Red (CR) solution was used as the feed with an initial concentration of 1.0 g L-1. A constant draw solution concentration of 1.5 M Na2SO4 was maintained by adding salt as needed at every monitoring time. (A) Variation of water flux, Jw, with time. (B) Variation of Na2SO4 mass and concentration in feed with time due to reverse salt flux. (C) Variation of CR mass in draw solution with time. (D) Calculated and actual CR concentration in the feed and the corresponding FO concentration factor with time. The calculated CR concentration was obtained by the total mass balance of CR in the feed and the draw solution, assuming no adsorption of dye to the membrane.
23
ACS Paragon Plus Environment
Environmental Science & Technology
557
558 559 560 561 562 563 564 565 566
Figure 4. Comparison of membrane cleaning efficiency in terms of the flux recovery ratio (FRR) and variations in Js. (A) FRR and the variation of Js (ΔJs) for PTAODH1.0, HTI-CTA(FO), HTI-CTA(PRO), CSM-TFC(FO), and CSM-TFC(PRO) membranes after cleaning with pure water. (B) FRR and the variation of Js (ΔJs) for the PTAODH-1.0 FO membrane using pure water (PW) and various concentrations (%) of alcohol solutions. (C) FRR and the variation of Js (ΔJs) for the PTAODH-1.0, HTICTA(FO), HTI-CTA(PRO), CSM-TFC(FO), and CSM-TFC(PRO) membranes after washing with 40% alcohol solution. 24
ACS Paragon Plus Environment
Page 24 of 27
Page 25 of 27
Environmental Science & Technology
567 568 569 570 571 572 573 574 575 576 577 578 579
Figure 5. Antibacterial properties of PODH, PTAODH-1.0, HTI-CTA, and CSM-TFC membranes against E. coli and S. aureus. Membrane samples were cut to 2.5 cm × 2.5 cm squares and each contacted with 1.0 mL of bacterial solution (concentration of 1.0×108 CFU mL-1) for three hours. The membranes were taken out, rinsed with sterile saline solution (NaCl, 0.9% (w/v)) to remove unattached cells from the membrane surface, and each immersed in 10 mL of sterile saline solution to detach the deposited cells by mild sonication for five minutes. After cultivation overnight at 37oC, the solutions containing the detached cells were diluted and plated on LB/Agar plates for plate counting. The commercial HTI-CTA membrane was used as a control, and all results were normalized to the result of the HTI-CTA membrane. Four samples of each membrane type were tested against both species of bacteria. Error bars indicate the standard deviations from three independent replicates.
580
25
ACS Paragon Plus Environment
Environmental Science & Technology
581
For Table of Contents Use Only
582
583
26
ACS Paragon Plus Environment
Page 26 of 27
Page 27 of 27
Environmental Science & Technology
50x36mm (300 x 300 DPI)