Contrast of the Biological Activity of Negatively and Positively

Nov 17, 2011 - Quantum dots (QDs) are semiconductor nanocrystals that have found use in bioimaging, cell tracking, and drug delivery. This article com...
2 downloads 0 Views
Article pubs.acs.org/crt

Contrast of the Biological Activity of Negatively and Positively Charged Microwave Synthesized CdSe/ZnS Quantum Dots Amber Nagy,† Andrew Zane,‡ Sara L. Cole,§ Michael Severance,‡ Prabir K. Dutta,*,‡ and W. James Waldman*,† †

Department of Pathology, The Ohio State University, Columbus, Ohio, United States Department of Chemistry, The Ohio State University, Columbus, Ohio, United States § Campus Microscopy and Imaging Facility, The Ohio State University, Columbus, Ohio, United States ‡

S Supporting Information *

ABSTRACT: Quantum dots (QDs) are semiconductor nanocrystals that have found use in bioimaging, cell tracking, and drug delivery. This article compares the cytotoxicity and cellular interactions of positively and negatively charged CdSe/CdS/ZnS QDs prepared by a microwave method using a murine alveolar macrophage-like cell culture model. Keeping the core semiconductor the same, QD charge was varied by altering the surface capping molecule; negatively charged QDs were formed with mercaptopropionic acid (MPA-QDs) and positively charged QDs with thiocholine (THIO-QDs). The size and charge of these two QDs were investigated in three types of media (RPMI, RPMI + FBS, and X-VIVO serum-free media) relevant for the biological studies. MPA-QDs were found to have negative zeta potential in RPMI, RPMI + FBS, and serum-free media and had sizes ranging from 8 to 54 nm. THIO-QDs suspended in RPMI alone were 250 nM). Both types of QDs were internalized via clathrin-dependent endocytosis. Using real-time, live cell imaging, we found that MPA-QDs interact with the cell surface within minutes and progress through the endocytic pathway to the lysosomes upon internalization. With the THIO-QDs, the internalization process was slower, but the pathways could not be mapped because of spectroscopic interference caused by QD aggregates. Finally, MPA-QDs were found to associate with cell surface scavenger receptors, while the THIO-QDs did not. This study indicates that the surface charge and aggregation characteristics of QDs change drastically in biological culture conditions and, in turn, influence nanoparticle and cellular interactions.



receptor mediated signal transduction18 and neuronal glycine receptors.12 Studies have been conducted that investigate the cytotoxicity of QDs with particular focus on QDs with Cd cores. One early study showed that differences in CdSe QD toxicity in Vero cells, HeLa cells, and human primary hepatocytes were concentration and time dependent.19 Size dependent cytotoxicity in rat pheochromocytoma cells and murine microglial cells was confirmed by Lovrić et al.20 using CdTe QDs. The mechanism of QD cytotoxicity in MCF-7 breast cancer cells has been attributed to the formation of reactive oxygen species (ROS).21 Others22 showed that QD internalization by hippocampal neurons resulted in calcium deregulation and sodium channel disruption, both of which can affect the role of ROS mediated protective responses.

INTRODUCTION The emergence of nanotechnology has ushered in many new and exciting applications. The use of nanoparticles in biomedicine has already proved to be quite useful as demonstrated by the increase of FDA-approved treatments that have incorporated the use of nanosized drug carriers. Quantum dots (QDs) are fluorescent semiconductor nanoparticles that have several advantages over traditional organic fluorophores. Because they are resistant to photobleaching, size tunable, and have the ability to be multiplexed, they are already being used in both clinical and basic sciences as tools for microbial detection,1−4 bioimaging,5−7 drug delivery,8−10 and tracking.11−14 One of the most interesting and effective applications of QDs is their use in imaging. Because of their size and robust fluorescence, they can be used in single molecule tracking.11,12,14−16 Cancer cell lines were among the first live cells that were successfully imaged,6,17 and QDs have been used to visualize receptor interactions, specifically erb2/HER © 2011 American Chemical Society

Received: August 2, 2011 Published: November 17, 2011 2176

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

and was stored at 4 °C. Nucleation of CdSe dots occurred when the NaHSe stock was injected into Cd-MPA solution. This mixture was stirred for one hour prior to the addition of the Zn(NH3)42+ stock solution. These contents were then microwave irradiated (MARS5 microwave system, CEM Corp.) for 90 min at 150 °C. THIO-QDs were prepared through a ligand exchange using MPA-QDs. A 25 mM thiocholine solution was prepared by a hydrolysis reaction of acetylthiocholine chloride with 1 M NaOH. Progress of the hydrolysis reaction was monitored with an Accumet AB15 pH Meter (Fisher Scientific). Five hundred milligrams of acetylthiocholine chloride was dissolved in 80 mL of water and stirred. NaOH was added dropwise until the pH reached between 10 and 11. The pH decreased as hydroxide ions were consumed in the reaction, and more NaOH was added. This process continued until the pH stabilized. The final pH was adjusted to 9 using 1 M NaOH or HCl, and the final volume was adjusted to 100 mL. The MPA-QDs were placed in 12,000 molecular weight cutoff regenerated cellulose dialysis tubing (Fisher Scientific) and dialyzed in 3 L of water for several hours to remove MPA from the solution. The removal of MPA caused the quantum dots to aggregate and settle. The supernatant solution was removed and replaced by the thiocholine solution. This process was repeated twice, resulting in particles which had a positive zeta potential. Characterization. Spectroscopic Measurements. All absorption measurements were obtained using a Shimadzu UV-2501PC UV−visible spectrometer. All emission measurements were obtained using a Horiba Jobin Yvon Fluorolog 3 fluorimeter. The as-prepared quantum dot solutions (930 nM; concentration calculations were done using an extinction coefficient of 2.9 × 106 cm−1 M−1 at 488 nm) was diluted 10:1 with purified water and placed in a quartz cuvette to measure the optical spectra. The excitation wavelength used for the emission spectrum was 375 nm, and all slits were set for a 2.5 nm band-pass. To obtain a quantum yield measurement, the quantum dot solution was compared to a solution of rhodamine 6G. Both solutions were diluted to have an absorbance of 0.020 at a wavelength of 480 nm. At this wavelength and concentration, rhodamine 6G is known to have a quantum yield of 95%.26 The peak emissions of both samples were measured with 480 nm excitation and the quantum yield calculated. To determine possible time-dependent leaching of cadmium at a pH of 4.5, solutions of QDs (final concentration 466 nM) were adjusted to this pH using 1 M hydrochloric acid and left standing for different times. The samples were centrifuged using a Thermo-Fisher Scientific MX-150 ultracentrifuge at 150,000 rpm for 1 h, and the emission of the supernatant indicated that there were no QDs in solution. The cadmium concentration was determined using inductively coupled plasma mass spectroscopy (ICP-MS) by Galbraith Laboratories. Size and Charge Measurements. Titrations of zeta potential and size vs pH were obtained using a Malvern Zetasizer Nano and an attached Malvern MPT-2 autotitrator. Zeta potential measurements were made using the method of phase analysis light scattering. Measurements were conducted at 25 °C at a forward scattering angle of 15°. Zeta potentials were calculated from the measured electrophoretic mobility using the Henry equation with a value of 1.5 for Henry’s constant according to the Smoluchowski approximation. This approximation is consistent with the high dielectric constant of water. Measurements were conducted at 25 °C with a backscattering angle of 273°. Dynamic light scattering results were analyzed using several algorithms. The data presented were analyzed using the constrained regularization method, CONTIN.27 A quartic weighting scheme was used for multimodal analysis. CONTIN analysis provided the distribution of particle radii based on scattering intensity. In some cases, these were converted to relative volume distribution according to Mie theory and the known properties of the scattering material. The refractive index was set to 2.351, the value for ZnS at these conditions.28 Cell Culture. The murine alveolar macrophage cell line (MH-S) was purchased from the American Type Culture Collection (Manassas,

The mechanism by which nontargeted nanoparticles enter cells is not well understood, and there is evidence that multiple pathways may be used. One recent study reported that commercially available negatively charged QDs can use scavenger receptors and lipid raft-mediated endocytosis for cellular entry in epidermal keratinocytes.23 Modified low density lipids and negatively charged inorganic nanoparticles have the propensity to bind scavenger receptors which supports the role of these receptors in QD uptake. Little research has been conducted regarding the internalization mechanism of positively charged QDs. The intracellular destination of QDs has been shown to range from the cytoplasm and nucleus24,25 to lysosomes.23 Although nanoparticles have shown great promise for use in biomedical applications, there is an urgent need to understand the implications, cellular interactions, and toxicity of nanoparticles harboring different physicochemical properties. In this study, using QDs as a model nanoparticle system, we address this problem by investigating how the physical properties of as-synthesized positive and negative QDs change in biologically relevant media and the influence of these resulting particles on cytotoxicity, inflammation, cellular uptake, and cell surface interactions in an alveolar macrophage cell line. Large quantities of double shelled CdSe/CdS/ZnS QDs were prepared using an inexpensive, rapid, microwave-based protocol, and surface charges were altered by capping QDs with mercaptopropionic acid (MPA-QDs) or thiocholine (THIOQDs) to produce negative and positively charged QDs, respectively.26 Because of the ability of nanoparticles in general to traverse the pulmonary system and reach alveoli after intentional or incidental exposure, we chose the murine alveolar macrophage-like cell line, MH-S, for our exposure studies due to their relevance in pulmonary uptake and respiratory toxicology. A profound difference of the charge and aggregation characteristics of QDs was also revealed in biologically relevant media. MPA-QD and THIO-QD induced cell death, apoptosis, and tumor necrosis factor-alpha (TNF-α) secretion in macrophages after exposure to high concentrations. Both types of QDs appear to utilize clathrin-coated pits for cell entry. The internalization of MPA-QDs was captured in real time, and intracellular fate was found to be confined to lysosomes. Differences in the molecular level interaction of positively and negatively charged QDs with cell surface scavenger receptors are reported for the first time.



EXPERIMENTAL PROCEDURES

Chemicals for QD Synthesis. Cadmium chloride hemipentahydrate, CdCl2·2.5 H2O (≥98%), and sodium borohydride, NaBH4 (99%), were purchased from Aldrich. Zinc chloride, ZnCl 2 (99.99%), mercaptopropionic acid (MPA), and Se powder (>99.5%, 200 mesh) were obtained from Acros. Sodium hydroxide, NaOH, and ammonium hydroxide, NH4OH (28−30%), were purchased from Mallinckrodt Chemicals. All chemicals were used without further purification. The H2O used for QD synthesis was purified by a Barnstead NANOpure Infinity ultrapure water system. Quantum Dot Preparation. MPA-QDs were prepared using a previously published protocol.26 Briefly, fresh solutions of NaHSe were prepared by mixing NaBH4 with H2O followed by the addition of Se powder under an inert environment (N2). The components reacted for ∼3.5 h, and then supernatants containing NaHSe were diluted to 20 mM using N2-saturated H2O. A solution of Cd-MPA was created by mixing MPA in H2O with 5.0 mM CdCl2·2.5 H2O stock solution, adjusting the pH to 9.5 using 1 M NaOH, and held at room temperature until needed. Last, a 60 mM Zn(NH3)42+ stock solution was prepared by dissolving ZnCl2 in H2O and titrating with NH4OH, 2177

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

nontoxic to the cells over a 24 h period as assayed by LDH release and Annexin V staining. QDs were suspended in fresh media containing 100 μg/mL Poly-I and then applied to macrophages. Unexposed cells and cells treated with Poly-I only served as controls. Cells were incubated for 6 h, then harvested and analyzed for fluorescence by flow cytometry using a FACScalibur flow cytometer at an excitation wavelength of 488 nm. Endocytosis Inhibition. Cells were pretreated for 30 min with fresh media (RPMI + FBS) containing cytochalasin D (2.5 μg/mL), which inhibits actin polymerization, 50 μM of chlorpromazine, a clathrin inhibitor, or 50 μM nystatin, a caveolae inhibitor. All inhibitors were purchased from Sigma and diluted to nontoxic (as tested by LDH release and Annexin V staining) working concentration using PBS. Cells that were not exposed to QDs and cells treated with inhibitors only served as controls. After pretreatment, media were removed and replaced with media containing the inhibitor and increasing concentrations of QDs. Cells were incubated with or without inhibitor and with or without QDs for 2 h, then washed 3 times with PBS. Cells were harvested by trypsinization, suspended in HBSS and analyzed by flow cytometry using a FACS calibur flow cytometer at an excitation wavelength of 488 nm. Live Cell Imaging. Cells were plated on glass coverslips situated in 35 mm Petri dishes at a density of 5 × 104 cells/coverslip and incubated overnight. Prior to live cell imaging and QD addition, cells were incubated with phenol red-free, serum-free X-VIVO media containing 25 nM LysoTracker Red (Invitrogen) for at least 15 min. QDs (final concentration of 75 nM) were added following 3 min of image collection. Images were acquired sequentially at an excitation of 442 nm, dichroic 442/488/565/643 and emission (barrier) 488/565/ 643 for QDs, while LysoTracker Red was detected using an excitation wavelength of 561 nm, a dichroic setting of 442/488/565/643 and a barrier setting of 488/565/643 every 6 s for a total of 20 min. In additional experiments, cells were incubated with LysoTracker Red and QDs for 45 min prior to image collection. Images were acquired using a Hamamatsu C9100 EM-13 camera connected to a Visitech Infinity3 2D array scanning multibeam confocal scanner and an IX81 microscope equipped with a 100×, 1.40 N.A. UPlanApo objective lens. Movies were constructed using MetaMorph software (Molecular Devices) using image stacks that were background subtracted with the statistical correction option of the “Background and Shading Correction” application. Out of focus images were removed prior to the production of movies. See Supporting Information for information regarding colocalization analyses. Statistical Analysis. Comparisons between QD treatments were analyzed for statistical significance using One-way ANOVA performed with SigmaPlot software.

Va), and propagated using RPMI cell culture media (Gibco) supplemented with 10% fetal bovine serum (FBS, Atlanta Biologicals) and 0.1% penicillin−streptomycin (Gibco). Cells were passaged every 3−4 days and incubated at 37 °C with 5.0% CO2. Cells were acclimated to these conditions for at least 12 h prior to QD exposure. Biological Characterization and Internalization Mechanistic Assays. Cytotoxicity and ELISA Experiments. Cells were plated in 24 well plates at a density of 1 × 105 cells/well. Old media were aspirated, and QDs diluted to working concentrations using appropriate cell culture media were applied to the cell cultures and incubated for 24 h. Cells treated with 1% Triton-100 (Sigma) in complete culture media served as a positive control for lactate dehydrogenase (LDH) release assays, while cells treated with E. coli lipopolysaccharide (Sigma) served as the positive control for tumor necrosis factor-alpha (TNF-α) and interleukin-1beta (IL-1β) ELISAs. Additionally, to determine if toxicity was driven by the QDs themselves or residual ligand, QD suspensions were centrifuged at 150,000 rpm for 1 h, and QD supernatants were diluted 2-fold a total of 5 times using RPMI + 10% FBS cell culture media. Diluted supernatants were applied to macrophages, and the cells were incubated for 24 h. Cell supernatants were collected and assayed for necrosis using the LDH assay as a measurement of cell membrane permeability. The compatibility of QDs and QD supernatants in a cellfree system were also tested using the LDH assay to determine if the materials themselves interfere with the assay. In cellular exposure experiments, cell supernatants were collected from each well and clarified by centrifugation and transferred to clean microfuge tubes and stored at −80 °C until analysis for cytokine secretion or LDH release. All experiments were performed at least 3 times. LDH Cell Viability Assays. Cellular supernatants were pipetted in duplicate into flat bottom 96-well plates and assayed for LDH activity using kits from Clontech per manufacturer’s instructions. Optical densities (ODs) representing enzyme activity were measured colormetrically using a BMG LabTech Omega plate reader at an absorbance wavelength of 490 nm and a reference wavelength of 600 nm. Cell viability was calculated using the following equation:

ELISAs. TNF-α and IL-1β secretion was measured via ELISAs using DuoSets purchased from R&D Systems according to the manufacturer’s recommendations. Supernatants were assayed in duplicate, and plates were read using a BMG LabTech Omega plate reader at an absorbance wavelength of 450 nm with a correction wavelength of 570 nm. Experimental sample concentrations were calculated with Omega software using a four parameter logistic standard curve. Flow Cytometry. All flow cytometry experiments were performed in triplicate. Cells were seeded in 6-well plates (Corning) at a density of 1.5 × 106 cells/well and allowed to adhere overnight prior to QD exposure. Flow cytometry staining procedures are described below. Annexin V Staining. Cells were exposed to QDs for 24 h. Cells were then washed with PBS three times prior to being harvested by trypsinization. Cell concentration was adjusted to 1 × 106 cells per tube, and cells were resuspended in 100 μL of Annexin binding buffer (Invitrogen); 5 μL of Annexin V-APC (BD Biosciences) was then added to each tube. Tubes were incubated in the dark at room temperature for 15 min before an additional 400 μL of binding buffer was added. Cells were analyzed for fluorescence using a FACScalibur flow cytometer at an excitation wavelength of 488 nm for detection of QDs and 635 nm for Annexin-APC. Scavenger Receptor Competition Assay. Three types of culture media were used: RPMI only, RPMI containing 10% FBS and X-VIVO 15 serum-free, phenol red-free media (Lonza). Culture media were removed and replaced with each of the fresh media listed above containing 100 μg/mL of Poly /inosinic acid (Poly-I), a nonspecific scavenger receptor ligand, for 30 min. This concentration of Poly-I was



RESULTS QD Characteristics. The microwave-based synthesis procedure for the QDs used in this study has been reported previously.26 These QDs contain a CdSe core with a CdS intermediate shell followed by a ZnS outer shell. MPA-QDs were capped with 3-mercapatopropionic acid (3-MPA). Detailed chemical and physical characterization of these MPA-QDs has been reported, including composition, size, and morphology.26 THIO-QDs were derived from the same core−shell QDs as the MPA-QDs by a ligand exchange process where MPA was replaced with thiocholine. Since the THIO-QDs were derived from the same core−shell QDs as the MPA-QDs and capped by a ligand exchange process, they had comparable, emission, absorption spectra, and quantum yields as the previously reported MPA-QDs.26 Figure 1A illustrates the particle sizes and zeta potential of the MPA-QDs as a function of pH in aqueous solution. The size data in this figure are reported as average diameters based on the intensity distribution (later we use volume distributions for the media dispersed samples; our purpose in Figure 1 was to 2178

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

Figure 1. Chemical characterization of QDs. Plots of MPA-QD (top panel) and THIO-QD (bottom panel) Z-average diameter and zeta potential as a function of pH. QD concentrations for size titration were 931 nM and 186 nM for zeta potential.

Three media types were examined in this study: RPMI without supplements, RPMI + fetal bovine serum (FBS), and X-VIVO serum-free, phenol red-free media. Dynamic light scattering and zeta potential of all three media were examined and reported in Table 1, and the raw data is in the Supporting Information. The analysis of light scattering data used the volume distribution rather than the intensity since large particles scatter more, and volume (or number) distribution is a better measurement of size. All three media had particles with diameters ranging from 1 to 8 nm. Additionally, in all three media types, the zeta potential data was noisy (Supporting Information) due to the small size of the particles

examine the aggregation characteristics in water as a function of pH). The hydrodynamic diameter for MPA-QDs is relatively constant between pH 5.5−11 and shows a marked increase below pH ∼6, indicating aggregation. The zeta potential remains negative throughout the pH titration, with a gradual increase in the zeta potential from −48 mV at pH 10 to −34 at pH 4.5. The behavior of the THIO-QDs in water is shown in Figure 1B. The zeta potential was found to remain positive over pH of 2−7 and decreased at higher pH. Thus, as synthesized, the MPA-QDs and THIO-QDs maintain a negative and positive charge, respectively, over biologically relevant pH ranges in water. 2179

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

Table 1. Volume-Based Diameters and Zeta Potentials for MPA-QDs and THIO-QDs in Media with and without Poly-I a MPA-QDs

THIO-QDs

− Poly I

a

+ Poly I

− Poly I

+ Poly I

size (nm)

charge (mV)

size (nm)

charge (mV)

size (nm)

charge (mV)

size (nm)

charge (mV)

8, 26 54 12, 39

−34 −15 −24

17 25 30

−26.6 −20.3 −14.8

20, 62 140, 1200 3000

15 −11 0

18, 42, 77, 450, 2700 62, 504 1300

−24.6 −17.3 0

RPMI RPMI + FBS X-VIVO

All of the experimental data corresponding to numbers in this table are provided in the Supporting Information, Figures 1−34.

that 20 nM concentration is suitable for imaging.23,26 At a concentration of 500 nM MPA-QDs, greater than 40% of cells were found to be necrotic, (Figure 34, Supporting Information), so for detailed necrosis and apoptosis measurements, we limited the concentration of QDs to 125 nM. These experiments were carried out in RPMI + FBS since it closely simulates physiological conditions. Both MPA-QDs and THIOQDs are stabilized by ligands, an excess of which is present in the QD suspension. For the LDH assay, which is a measure of necrosis, both the supernatants of the QDs and the entire QD suspension were examined. It is also relevant to point out that the supernatant from the THIO-QDs interfered with the LDH assay at 250 nM and higher concentrations. Figure 2 shows the

and not readily amenable to interpretation. The size and charge of the two QDs were examined in these three media types, in the presence and absence of Poly-I, and the data are summarized in Table 1. Also, the Supporting Information shows the actual distribution curves obtained from the light scattering and the raw zeta potential data for QDs in all media. The THIO-QDs and MPA-QDs behaved differently in each media. As synthesized, MPA-QDs had a diameter of ∼26 nm and charge of −44 mV (pH 9). Note that these sizes differ slightly from Figure 1 since it is the volume-based number that is being used henceforth. Also, our previous TEM studies show that the QDs are about 5.3 nm in diameter, so the light scattering data indicates that there is some aggregation even in water.26 Upon replacing MPA with thiocholine, the size was 17 nm with a charge of +34 mV (pH 9). When suspended in all three media types, the MPA-QDs exhibited a stable, optically clear dispersion. In RPMI, the size distribution was bimodal: ∼8 and 26 nm with a charge of −34 mV. Smaller sized particles of ∼1 nm were present in RPMI alone. It is unclear if these contribute to the ∼8 nm particles. In RPMI + FBS, the size of the MPA-QDs was 54 nm, and the charge was −15 mV. In X-VIVO media, the size distribution for MPA- QDs was also bimodal: ∼12 and 39 nm, with a negative charge of −24 mV. The X-VIVO media by itself had particles with sizes of ∼7 nm and is possibly the contributor to the smaller of the two sizes in the bimodal distribution. Thus, in both RPMI + FBS and XVIVO media, the QDs are increasing significantly in size, more so in the former, possibly by association with proteins, which also leads to lowering in the surface charge. A stable, optically clear dispersion of THIO-QDs was achieved only with RPMI. The size distribution in RPMI was bimodal with ∼20 and ∼62 nm particles, and the surface charge was +15 mV. In RPMI + FBS, the solution turned cloudy with time (15−30 min) and is reflected in the broad particle size distribution with peaks at 140, 1200 nm, and also larger aggregates. The zeta potential of THIO-QDs in RPMI + FBS was −11 mV. With the X-VIVO media, aggregation for THIOQDs was more marked with sizes over a range of 1000−6000 nm (average around 3000 nm), and the particles had a neutral charge of ∼0 mV, also indicating association of negatively charged species from the media with THIO-QDs. To simulate the acidic environment of the lysosome, QDs were incubated at a pH of 4.5 in water (466 nM) under ambient conditions, and the concentration of free Cd2+ in solution was determined by ICP-MS. In the case of MPA-QDs, the concentration of Cd2+ was not detectable after 15 min and increased to 1.8 μM over 24 h, whereas for the THIO-QDs, the Cd2+ content increased from 0.9 μM after 15 min to 3.6 μM after 24 h at pH 4.5. Cytotoxicity and Proinflammatory Response of QD Exposed Cells. We incubated cells with QDs with concentrations as high as 500 nM, though previous studies have shown

Figure 2. Necrosis induced by MPA-QDs, THIO-QDs, and QD supernatants in murine alveolar macrophages. Cells were incubated with increasing concentrations of MPA-QDs, THIO-QDs, and equivalent QD supernatants containing excess ligand. QDs and QD supernatants were diluted in RPMI + FBS and exposed to macrophages for 24 h before cellular necrosis was measured via LDH release. THIO-QDs were significantly more toxic (p < 0.01, indicated by **) than MPA-QDs at 125 nM. MPA QDs were significantly more toxic than MPA-QD supernatants at 125 nM (p < 0.05 indicated by *), and THIO-QDs were significantly more toxic than THIO-QD supernatants at 125 nM (p < 0.05, indicated by *). Error bars are the standard deviation from 3 independent experiments.

LDH assay data for both MPA-QD, THIO-QD, and their supernatants. Dose-dependent necrosis of cells is observed for the QD suspensions, while the supernatants exhibited little toxicity, at the level of ∼5% death of cells. The THIO-QDs were significantly more cytotoxic at 125 nM (p < 0.01), with 30% cell death as compared to MPA-QDs. Annexin V staining was performed after a 24 h exposure to examine the apoptotic response of cells exposed to QDs suspended in RPMI + FBS media. Macrophages exposed to 250 nM of MPA-QDs or less were observed to have between a 10 to 15% increase in the number of apoptotic cells compared to that of unexposed cells (Figure 3A), while cells treated with 2180

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

Figure 3. Apoptotic effects of MPA-QDs and THIO-QDs in murine alveolar macrophages after 24 h. (A) Macrophages were incubated with increasing concentrations of MPA-QDs suspended in RPMI + FBS, and apoptosis was measured via flow cytometry. The number of apoptotic cells approximately doubled for concentrations up to 250 nM. (B) Macrophages were incubated with increasing concentrations of THIO-QDs suspended in RPMI + FBS, and apoptosis was measured via flow cytometry. Numbers of apoptotic cells increased in a dose dependent manner. Figures are representative of three independent experiments for each QD type.

500 nM were found to have ∼3.5 times (56.8%) as many apoptotic cells, indicating that the mechanism of cytotoxicity is apoptosis (Figure 35, Supporting Information). A dose dependent increase in Annexin V staining for cells incubated with THIO-QDs was observed, where macrophages exposed to 62.5, 125, or 250 nM THIO-QDs resulted in 6.7%, 13.3%, and 24.3% Annexin V positive cells, respectively (Figure 3B). Levels of secreted TNF-α and IL-1β in supernatants recovered from macrophages exposed to MPA-QDs and THIO-QDs suspended in RPMI + FBS were quantified by ELISA. Macrophages treated with 100 ng/mL of lipopolysaccharide alone resulted in TNF-α levels greater than 175 pg/mL (data not shown) indicating that these cells are capable of producing a proinflammatory response. Supernatants derived from cells incubated with QDs for short periods (2 h) did not result in proinflammatory cytokine induction (data not shown); thus, samples were collected after 24 h exposures. TNF-α levels range from undetectable for untreated cells and cells treated with 62.5 and 125 nM of MPA-QDs. The amounts of TNF-α secreted from macrophages after exposure to MPA-QDs were significantly different from amounts secreted from cells exposed to THIO-QDs (Figure 4). Supernatants from cells treated with 500 nM of MPA-QDs show an increase of 33 ± 8 pg/mL of TNF-α compared to 23 ± 4 pg/mL from cells treated with 250 nM of MPA-QDs. These same supernatants were also analyzed for IL-1β, which was undetectable (data not shown). Supernatants collected from cells treated with 250 nM of THIO-QDs secreted 51 ± 12 pg/mL of TNF-α but only 6 ± 11 pg/mL after exposure to 500 nM of THIO-QDs (40% cell death at these high concentrations). Internalization, Intracellular Localization, and Mechanism of QD Uptake. There are several possible mechanisms that facilitate endocytosis, including internalization through caveolae and clathrin coated pits. We used an inhibitor

Figure 4. Secretion of TNF-α from macrophages exposed to MPAQDs and THIO-QDs. Significant differences (p < 0.001, n = 3, as indicated by *) in TNF-α secretion levels were measured using ELISA from cell supernatants after exposure to MPA-QDs and THIO-QDs suspended in RPMI + FBS for 24 h.

approach to block internalization of MPA-QDs, all experiments being carried out in RPMI + FBS media. Initially, cells were pretreated with cytochalasin D (inhibits actin polymerization and phagocytosis), nystatin (binds cholesterol and disrupts caveolae coat structure), or chlorpromazine (prevents clathrin recycling) prior to the addition of MPA-QDs suspended in media containing inhibitors. Neither nystatin treated cells nor cytochalasin D treated cells displayed a reduction in fluorescence after exposure of cells to MPA-QDs suspended in the corresponding inhibitor (data not shown). However, in cells treated with chlorpromazine, fluorescence is substantially reduced at all concentrations tested (Figure 5A and B). 2181

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

Macrophages exposed to 150 nM MPA-QDs in the presence of chlorpromazine exhibited approximately 66% less fluorescent positive cells. Likewise, when macrophages were exposed to 125 nM THIO-QDs in the presence of chlorpromazine, ∼60% less fluorescent cells was observed compared to that in controls. Differences in fluorescence after treatment with the clathrin inhibitor are summarized in Figure 5 and Table 2.

Figure 6. MPA-QD compartmentalization in macrophages. (A) Macrophages stained with LysoTracker Red just prior to the addition of MPA-QDs suspended in serum free, phenol red-free X-VIVO media. (B) MPA-QDs form a halo around the outside of the cell within 2 min. (C) Yellow vesicles indicative of colocalization are apparent after ∼9 min. (D) MPA-QDs are clearly in acidic compartments by 12 min. (E) Vesicles begin to track in the cell by 17 min postexposure. In panel F, macrophages were incubated with LysoTracker followed by the addition of 150 nM MPA-QD (final concentration = 75 nM) for 45 min prior to imaging. The majority of QDs are found within lysosomes. r is the correlation between MPAQDs and LysoTracker.

Figure 5. Role of clathrin-coated pits in QD internalization. (A) Macrophages were exposed to MPA-QDs alone suspended in RPMI + FBS (left panel) or pretreated with chlorpromazine (50 μM) for 30 min prior to exposure to MPA-QDs suspended in RPMI + FBS containing chlorpromazine (right panel). (B) Macrophages were exposed to THIO-QDs alone suspended in RPMI + FBS (left panel) or pretreated with chlorpromazine (50 μM) for 30 min prior to exposure to THIO-QDs suspended in RPMI + FBS containing chlorpromazine (right panel).

performed in X-VIVO serum-free, phenol red free media due to the interference of phenol red with imaging. We stained acidic organelles using LysoTracker Red to visualize the late endosomal pathway and were able to localize MPA-QDs in the lysosomes within 20 min of their introduction into live cultures (Supporting Information). The image presented in Figure 6F is representative of QD/lysosomal colocalization after 45 min of incubation from the second movie file in Supporting Information. We quantified the amount of colocalization in this cell over time, and MPA-QDs were found to have a correlation coefficient (r value) of 0.577 ± 0.066, indicating that the majority of QDs are retained in acidic compartments. Colocalization of MPA-QDs and LysoTracker is consistent with transport through the endosomal pathway to the lysosomes. THIO-QDs were also observed to be internalized. However, flow cytometry data collected from the clathrin inhibition assays indicate cellular association occurred within 2 h, in contrast to MPA-QDs which were internalized in approximately 20 min. Their compartmentalization in lysosomes could not be definitively established since the aggregated QDs in serum free media scatter the laser light (561 nm), making it difficult to distinguish from the LysoTracker Red signal. This phenomenon was not apparent for MPA-QDs, which remained dispersed in the media. To identify a possible mechanism of QD internalization in all three media types, we evaluated the molecular relationship between scavenger receptors and charged QDs using a competition assay using Poly-I, a nonspecific scavenger receptor ligand. When cells were incubated with MPA-QDs suspended in all media types containing 100 μg/mL Poly-I, a

Table 2. Percent Fluorescent Cells Exposed to Negative and Positive QDs Suspended in RPMI + FBS in the Absence and Presence of the Clathrin Inhibitor, Chlorpromazinea % fluorescent cells MPA-QD concentration (nM) 0 25 75 150

− chlorpromazine

+ chlorpromazine

0.8 ± 0.0 9.5 ± 2.3 63.1 ± 2.5 87.4 ± 2.5 % fluorescent

0.5 ± 0.4 0.4 ± 0.1 3.2 ± 0.3 29.9 ± 6.1 cells

THIO-QD concentration (nM)

− chlorpromazine

+ chlorpromazine

0 31.2 62.5 125

1.0 ± 0.2 65.6 ± 2.4 85.1 ± 1.6 91.5 ± 1.5

1.4 ± 0.3 2.8 ± 0.5 9.9 ± 1.4 26.8 ± 3.6

a

Values are the average of 3 independent experiments ± standard deviation.

Using live cell confocal imaging, we observed MPA-QDs localizing to the cell membrane within minutes (3 min) after they were introduced to the culture, followed by their appearance in intracellular vesicles (9 min) and mature vesicles at 12 and 17 min (Figure 6A−E). All experiments were 2182

dx.doi.org/10.1021/tx2003195 | Chem. Res. Toxicol. 2011, 24, 2176−2188

Chemical Research in Toxicology

Article

Figure 7. Comparisons in QD charge and macrophage scavenger receptor association. (A) Macrophages were treated with increasing concentrations of MPA-QDs suspended in RPMI (left panel), RPMI + FBS (middle panel), or X-VIVO media (right panel) for 6 h prior to analyses of cellular fluorescence by flow cytometry. (B) Macrophages were pretreated with RPMI (left panel), RPMI + FBS (middle panel), or X-VIVO media containing Poly-I (100 μg/mL) for 30 min. MPA-QDs suspended in each media type containing Poly-I were added to the cells and incubated for 6 h prior to analyses of cellular fluorescence by flow cytometry. (C) Macrophages were treated with increasing concentrations of THIO-QDs suspended in RPMI (left panel), RPMI + FBS (middle panel), or X-VIVO media (right panel) for 6 h prior to analyses of cellular fluorescence by flow cytometry. (D) Macrophages were pretreated with RPMI (left panel), RPMI + FBS (middle panel), or X-VIVO media containing Poly-I (100 μg/mL) for 30 min. THIO-QDs suspended in each media type containing Poly-I were added to the cells and incubated for 6 h prior to analyses of cellular fluorescence by flow cytometry.

Table 1 shows that the MPA-QDs do not have major interactions with Poly-I, and the QDs remain negatively charged and with sizes