Correction to Combinatorial Study of Gradient Ag−Al Thin Films: Microstructure, Phase Formation, Mechanical and Electrical Properties Fang Mao,* Mamoun Taher, Oleksandr Kryshtal, Adam Kruk, Aleksandra Czyrska-Filemonowicz, Mikael Ottosson, Anna. M. Andersson, Urban Wiklund, and Ulf. Jansson* ACS Appl. Mater. Interfaces 2016, 8 (44), 30635−30643; DOI: 10.1021/acsami.6b10659 he title of x-axis of the right figure in the original Figure 2 is wrong. It was originally “Position on the substrate (mm)”, but should be “Ag concentration (at %)”. The corrected Figure 2 is shown below. The interpretation of the results and conclusions of the paper are not affected by this erratum. The authors apologize for the erratum.
T
Figure 2. Composition of the three gradient films A−C, as determined by EDX. (A) Ag-rich gradient; (B) intermediate gradient; (C) Al-rich gradient. Seven points, spaced 10 mm apart along the gradient direction on each gradient film, were studied. The center of the substrate is set as 0 mm.
Published: February 8, 2017 © 2017 American Chemical Society
6653
DOI: 10.1021/acsami.7b01155 ACS Appl. Mater. Interfaces 2017, 9, 6653−6653