Correction to Insights into the Performance Limits of the Li7P3S11 Superionic Conductor: A Combined First-Principles and Experimental Study Iek-Heng Chu, Han Nguyen, Sunny Hy, Yuh-Chieh Lin, Zhenbin Wang, Zihan Xu, Zhi Deng, Ying Shirley Meng,* and Shyue Ping Ong* ACS Appl. Mater. Interfaces 2016, 8 (12), pp 7843−7853. DOI: 10.1021/acsami.6b00833
P
age 7847. The authors regret that one mistake was made in their paper. In Figure 4b, the “Endo-Exo” direction was
Figure 4. (b) Experimental DSC curve of 70Li2S·30P2S5 glass. Blue dashed lines denote the glass-transition temperature (Tg) and crystallization temperature (Tc).
supposed to be reversed. When the orientation is corrected, Tg is assigned an endothermic process and Tc is assigned an exothermic process. A corrected Figure 4b (along with its original caption) is provided. Although the error was present, it does not affect the interpretation and conclusions of the manuscript as a whole. The authors apologize for any inconvenience this may have caused the readers.
© XXXX American Chemical Society
A
DOI: 10.1021/acsami.8b03438 ACS Appl. Mater. Interfaces XXXX, XXX, XXX−XXX