Correction to Measurements of Interdiffusion Coefficients of Transition Metals in Layered Li−Ni−Mn−Co Oxide Core−Shell Materials during Sintering Jing Li, Renny Doig, John Camardese, Kevin Plucknett, and Jeff R. Dahn* Chemistry of Materials 2015, 27 (22), 7765−7773. DOI: 10.1021/acs.chemmater.5b03499

I

Table 1. Summary of the Activation Energies for Diffusion Measured in This Work

n this article, Figure 10 is exactly the same as Figure 9. The correct figure is shown here. The caption and content are correct in the original paper.

activation energy diffusion couple

eV (±0.3)

kJ/mol (±30)

D0 (m2/s)

Ni/Mn Co/Mn Ni/Co

0.5 3.0 2.2

54 290 210

2.7 × 10−15 3.6 × 10−4 2.6 × 10−6

The Figure 6 discussion on page 7769 should be changed to “In order to maintain the charge balance of the compounds during diffusion, three Ni3+ ions need to exchange with one Li+ and two Mn4+ ions in the transition metal layer. Conversely, one Ni3+ can directly exchange with one Co3+ ion, which can explain why the Ni 3+ /Co 3+ couple shows the lowest interdiffusion coefficient at 900 and 1000 °C.” This correction will not change our final conclusion.

Figure 10.

In Table 1, the activation energy for Ni/Mn should be 0.55 eV and 54 kJ/mol instead of 5.5 eV and 540 kJ/mol, respectively. The correct table is shown here. The Ni/Mn couple has the lowest activation energy instead of the highest, but D0 of the Ni/Mn couple is the lowest, which is the reason why the Ni/Mn couple shows the lowest interdiffusivity even at 1000 °C. © XXXX American Chemical Society