Cross-Linkable Fluorene-Diphenylamine Derivatives for

Oct 23, 2015 - Multicolor electrochromic systems based on heat cross-linkable arylamine-substituted fluorene derivatives, FD and FDOMe, are reported. ...
1 downloads 4 Views 1MB Size
Subscriber access provided by NEW YORK MED COLL

Article

Cross-linkable fluorene-diphenylamine derivatives for electrochromic applications Silja Abraham, Gayathri Prabhu T. Ganesh, Sunil Varughese, Biswapriya Deb, and Joshy Joseph ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.5b08218 • Publication Date (Web): 23 Oct 2015 Downloaded from http://pubs.acs.org on October 25, 2015

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Cross-linkable fluorene-diphenylamine derivatives for electrochromic applications Silja Abraham,† Gayathri Prabhu T. Ganesh,† Sunil Varughese,† Biswapriya Deb,†, ‡ and Joshy Joseph*, †, ‡ †

Photosciences and Photonics Section, Chemical Sciences and Technology Division, CSIR-

National Institute for Interdisciplinary Science and Technology, Thiruvananthapuram 695019, Kerala, India. E-mail: [email protected]

Academy of Scientific and Innovative Research (AcSIR), CSIR-NIIST Campus, Trivandrum,

India. KEYWORDS: electrochromism, cross-linkable small molecules, spectroelectrochemistry, triarylamine derivatives, Buchwald-Hartwig amination, electrochromic device.

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 31

ABSTRACT: Multicolor electrochromic systems based on heat cross-linkable arylamine substituted fluorene derivatives, FD and FDOMe are reported. These derivatives with pendant vinyl groups have been synthesized by Buchwald-Hartwig amination reaction and were well characterized using various analytical and spectroscopic techniques such as NMR, ESI-MS and single crystal X-ray diffraction analysis. FD and FDOMe exhibited thermally activated crosslinking above their melting temperatures, which was confirmed through absorption, differential scanning calorimetry (DSC), FT-IR, and wide angle X-ray diffraction (WAXD) techniques. Cross-linked FD films (FD-X) on ITO showed two reversible redox peaks at 0.74 V and 0.91 V (vs Ag/AgCl) which correspond to the formation of radical cations and dications, respectively. The corresponding redox peaks were observed at 0.6 V and 0.8 V for cross-linked FDOMe films (FDOMe-X). Spectroelectrochemical studies of the electrochromic films on ITO revealed multicolor electrochromism of FD-X (colorless - yellow - dark cyan) and FDOMe-X (colorless brick red - blue) with a color contrast of ~44% at 485 nm for FD-X and ~63% at 500 nm for FDOMe-X and good switching stability between neutral and oxidized states (>300 cycles) with low switching voltages (< 0.9 V for first oxidation and