Diblock copolymers attached to homopolymer surfaces and interfaces

May 1, 1993 - Dong Han Kho, Seung Hun Chae, Unyong Jeong, Hwang Yong Kim, and Jin Kon Kim. Macromolecules 2005 38 (9), 3820-3827. Abstract | Full ...
0 downloads 0 Views 2MB Size
Macromolecules 1993,26, 2410-2418

2470

Diblock Copolymers Attached to Homopolymer Surfaces and Interfaces Andrzej Budkowski,tJ Jacob Klein,*lt Ullrich Steiner,t and Lewis J. Fetters$ Department of Materials and Interfaces, Weizmann Institute of Science, Rehovot 76100, Israel, and Corporate Research Laboratories, Exxon Research and Engineering Company, Annandale, New Jersey 08801 Received November 18, 1992; Revised Manuscript Received February 2, 1993

ABSTRACT: Nuclear reaction analysis (NRA) was used to study the segregation of an asymmetric diblock copolymer,consisting of polyisoprene (PI, molecular weight M = lV)/deuterated polystyrene (dPS, M = 105) blocks, to the interfaces formed by polystyrene (PS) homopolymer with various phases. PS/vacuum, PSI silicon, and PS/PI homopolymer interfaces were investigated for different M values of the PS matrix ( M = 1.7 X lo3-330 X lo3),and segregation isotherms were established as a function of temperature and of diblock concentration within the PS homopolymer. In all cases the diblocks attach to the interfaces by their PI moieties alone, to form brushlike structures of end-attached PS tails. The high spatial resolution of the NRA technique enabled studies of the brush conformation as a function of the attachment density at the PS/ vacuum surface and was used to characterize the extent of penetration of the PS matrix chains into the diblock brushes. Detailed analysis of the brush conformation and of the segregation isotherms, mainly in terms of a Flory-type mean field model based on those due to de Gennes and to Leibler, provided a consistent description of our data, it enabled the extraction of the PI/PS segmental interaction parameter XPIPS, yielding values in accord with scattering studies, and of the attachment energies of the PI diblock moiety to the PS/air and PS/silicon interfaces. The values of xpps extracted from our data using this Flory-type model were found to increase at lower M values of the PS matrix, in qualitative accord with previous results.

I. Introduction Polymers attached at surfaces or at interfaces can profoundly modify surface interactions and related behavior, an effect deriving from their large size and their flexibility. Thus polymers at the solid-liquid interface can modify fluid flow or lubrication properties at these surfaces,lwhile polymers attached at solid-air or at solidsolid interfaces can control friction and wear properties,2 a d h e s i ~ n , and ~ . ~ load transfer characteristic^.^ Chains attached densely by one end only (for example, via a polar head-group or by a covalent bond) at an otherwise nonadsorbing interface form so-called polymer brushes; in the context of understanding steric stabilizationof colloidal dispemions,69'the properties and structure of such brushes at the solid-liquid interface, and in particular the way in which they modify long-ranged interactions between the surfaces immersed in a liquid, have been intensively studied.sl1 A-B block copolymers in which one of the blocks (of polymer A say) selectively attaches to a surface or at an interface between two phases while the other (polymer B) dangles out to form a brushlike layer provide a simple means for the realization of polymeric brushes. In particular, such A-B diblocks are intuitively attractive as modifiers of interfacialproperties between incompatible A and B polymers, where one expects anatural segregation of the diblocks at the A/B interface, with each block dangling into ita respective homopolymer. Brushlike layers formed by such diblocks at the phase boundary can reduce the interfacial tension between A and B.12 This in turn can significantly modify the mechanical properties of adhesive joints between them3 and the rheological properties, stability, and domain size in phase-separated A/B mixtures. Brush layers at solidlpolymer interfaces can also lead to stabilizationof thin polymeric films against rupture and breakup.13J4 A number of theoretical models +

Weizmann Institute of Science.

* On leave of absence from Jagellonian University of Cracow,

Cracow, Poland. 8 Exxon Research and Engineering Co.

0024-9291/93~2226-2470$04.00/0

have dealt specifically with the case of brush layers in polymer melt matrices, either grafted on a surface or formed by A-B diblock copolymers at A/B interfaces. These include scaling approaches,15J6simple Flory-type models of the brush 1ayers,16J7and more detailed selfconsistent mean field c a l c u l a t i ~ n s ~ (generally ~J~ requiring numerical evaluation). In contrast to the case of polymeric brushes at solidliquid interfaces there have been relatively few direct experimental studies of polymeric brushes formed by diblock copolymers in melt matrices, whether at a polymer/ air20or polymer/solidinterface21or at the interfacebetween two incompatible polymer^.^^-^^ Brown and co-workers22 deposited a layer of an A-B diblock copolymer at the interface between an A and a C polymer, where C and B were compatible (i.e., the segmental interaction parameter XBC < 0); using secondary ion mass spectrometry for deuterium depth profiling, they demonstrated the enthalpic swelling of the B moieties of the diblock in the C homopolymer. Shull, Kramer, and ~ o - w o r k e r s ~and 3~~~ Green and R ~ s s e 1 1studied ~ ~ ~ ~the ~ segregation of A-B diblock copolymers to the interface between incompatible A and B homopolymers (and between A and a solid substrate), where a thin film of A homopolymer incorporating the A-B diblock was laid on top of a B homopolymer film which was spin-cast onto a silicon wafer. The A-B copolymers were polystyrene (PS)-poly(2vinylpyridine)(PVP) and PS-poly(methy1 methacrylate), respectively, in the two studies. These investigations utilized elastic ion beam scattering methods to determine the excess of diblocks attached to the A/B interfaces as a function of diblock concentration in the bulk of the A homopolymer and as a function of the molecular weight of the A homopolymer. Formation of polymeric micelles can occur readily in diblock/homopolymer mixtures above the critical micelle concentration (cmc),and such micelles were in clear evidence in the PS-PVP case,23124 where they segregated strongly both at the AIB and at the Alair interfaces, leading to interesting interfacial structures combining both brushes and micelles.26 0 1993 American Chemical Society

Dihlock Copolymers Attached to Homopolymer Surfaces 2471

Macromolecules, Vol. 26, No. 10, 1993

airlPS

PSISi

PIlPS

Figure 2. Schematic illustration of the different interfaces in the present study.

I

10-2

surface coverage

0

Figure 1. Variation of the mean brush height L with surface coverage (expressed in terms of areal density) a of the PI-PS diblocks at the air interface of polystyrene films of degree of polymerizationP (taken from ref 20): (0) P = 88; ( 0 )P = 3173. The broken line is the relation L &, while the solid curve is a guide to the eye: its linear portion corresponds to L &%.

-

-

In a recent studyz0 related to the present report, we used a depth-profiling technique based on nuclear reaction analysis (NRA) to determine the structure of a polyisoprene (PI)-PS diblock copolymer (PI-PS) segregating to form a PS brush at the air interface of PS films of varying molecular weight. The high spatial resolution of the NRA method20~27-~-comparablewith the unperturbed dimensions of the PS diblock moiety (of molecular weight M = 105)-enabled the mean PS brush heights L(u) to be determined as a function of the density u of diblock chains at the interface, as described in detail in ref 20; here u = aZ/sZ is the areal density of the end-tethered PS chains, where n (=0.66nm for polystyrene) and s are the segment size and the mean spacing of the copolymers at the interface, respectively. Both Flory-type16J7 and selfconsistent mean-field18 models give similar predictions for the variation of the brush heightL with u;these depend on the density of the diblocks at the interface and on the relative degrees of polymerization N a n d P of the brushforming chains and of the matrix chains, respectively. In the regime N > P > NLlz the P-mer matrix chains may penetrate the brush (the so-called “wet-brush” regime), and in this case the brush thickness is predicted to vary as L = const X NaP1’3u1/3 (wet-brush regime) (1) A t high values of the surface coverage by the tethered N-mer, progressive exclusion of the P-mer matrix chains from within the brush layer occurs (leading to the socalled “dry-brush” regime), while at high values of P (P 2 N) essentially complete exclusion of the P-mers from within the brush is predicted. In this dry-brush regime the brush height becomes independent of P and is then a function of the surface coverage alone: L u. The variation of brush height with areal density of the PI-PS diblocks was determined at the air interface of two of the homopolystyrenes used in the present study and is reproduced in Figure 1. For the PS matrix with M = 9.2 X lo3there is some scatter in the data (open circles), but it is consistent with the wet-brush behavior, shown as the broken line, predicted by eq 1,as is also expected in this case for which N > P > iW2.For the PS matrix with M = 3.3 X 105 (solid circles) the brush height in the region u 2 3 X 10-3varies as L C+ (solid line in Figure 1)where theexponentn = 0.54. Thevalueoftheexponentissmaller than that expected for a dry brush ( L u), indicating’ that despite the fact that P > N, the behavior is still in transition to the limiting dry-brush behavior. (We also

-

-

-

Table 1. Molecular Weights and Polydispersities (Expressed As the Ratio of Weight to Numher Average) of Materials Used in This Studv

oolvmer

’%a

1700 9200

dPS(929) dPS(174ll)

PI(5182) PI-PS

Mw/Mnb 1.06 1.03

51500

1.04

100ooO 330000

1.06

104000 195oooO

1.02

374000 PI = 1030b dPS = 1o(xxxI

1.05

1.04 1.14

1.03

1.03

Via lowangle laser light scattering. Via size exclusion chromatography.

note that both seta of data approach the value L = R,,the radius of gyration of the PS moiety of the diblock, at the lowest u values studied, as expected for isolated chains.) We shall find these indications useful when examining our data in the light of theoretical models. In the present study we extend o w investigation of the segregation of PI-PS diblocks from PS homopolymer matrices in which they are incorporated to interfaces of these matrices with air (or vacuum) (henceforth PS/air), with a silicon substrate (PS/Si), and with a PI homopolymer (PS/PI). The respective geometries are shown schematically in Figure 2. In section I1 we describe the experimental approach and materials used; in section 111 we present results of control experiments, typical profiles of the PI-PS brushes at the various interfaces, and of the segregation isotherms as a function of PS host-matrix molecular weight and the hulk concentration of the PIPS diblocks in the homopolystyrene host. In section IV we consider our data mainly in terms of the Flory-type m~dels,’~J~ with some modifications due to the particular conditions of our experiments. 11. Experimental Section

The copolymer used was a monodisperse, highly asymmetric polyisoprenedeuterated polystyrene diblock (PI-PS, with the respective blocks having M values of ca.

lo4 and lo5).

Mono-

disperse homopolystyrene samples covering a range of (weight average) molecular weights M = 1.7 X lO“3.3 X lo5 (with correspondingdegreesof polymerization P = 163173)and designated PS(P) were used as the matrix polymers, while a monodisperse homopolyisoprene sample (M 4 X lo5)was used for the PS/PI interfacialsegregationmeasurements. Inadditioqperdeuterated homopolystyrene samples (dPS(P))were used in control measurements. All molecular characteristics are given in Table I. Polished silicon (Si)wafers were purchased from Aurel GmbH, Germany, and from Intel Electronics, Israel, and degreased in toluene (hut not otherwise pretreated) prior to use. All solvents used were analytical grade. Films of the PS incorporating different PI-PS concentrations

were prepared by spin-casting a toluene solution containingthe

Macromolecules, Vol. 26, No. 10, 1993

2472 Budkowski e t al.

-

R

* 20-

T=160°C

Y

t 4

e

* i

0

. c) I

u

C

m

t

10

loL r

6

*

L

t=63h

t=35h

1

i

01 +J 100

0

0

400

depth z [nm] Figure 3. Composition-depth profiles of the (deuterated) PS moiety of the PI-PS diblock, illwtrating the resolution/depth range trade-off using NRA in the present study. The profiles are for the PI-PS diblocks at volume fraction = 4.9% in a layer of PS(3173) mounted on a silicon wafer, following 1 day of annealing at 180 O C . Profile a: incident 3He energy E3.0 = 700 keV; profile b E3,0= 1.2 MeV. The shaded areas are the surface excess values r as defined in eq 2; the air interface is at z = 0, while the Si interface is at z = 470 nm. appropriate homopolymer/diblock ratios onto the Si wafers (cut to dimensions ca. 1 x 2 cm2)to thicknesses in the range 400-600 nm. Where segregation to the PS/PI interface was studied, a layer of the PI (thickness in the range 100-200 nm) was spin-cast onto freshly cleaved mica, floated off on distilled water, and mounted on the precast PS film on the Si wafer to form a bilayer. Samples were sealed in glass ampules under vacuum (