Direct Observation of the Band Gap Transition in ... - ACS Publications

Jul 31, 2017 - Peter Grünberg Institut PGI-1 and Institute for Advanced Simulation IAS-1, Forschungszentrum Jülich and JARA, 52425 Jülich,. Germany. §...
0 downloads 0 Views 3MB Size
Subscriber access provided by UNIVERSITY OF THE SUNSHINE COAST

Communication 2

Direct observation of the band gap transition in atomically thin ReS

Mathias Gehlmann, Irene Aguilera, Gustav Bihlmayer, Slavomir Nemsak, Philipp Nagler, Pika Gospodaric, Giovanni Zamborlini, Markus Eschbach, Vitaliy Feyer, Florian Kronast, Ewa Mlynczak, Tobias Korn, Lukasz Plucinski, Christian Schüller, Stefan Bluegel, and Claus M. Schneider Nano Lett., Just Accepted Manuscript • DOI: 10.1021/acs.nanolett.7b00627 • Publication Date (Web): 31 Jul 2017 Downloaded from http://pubs.acs.org on August 2, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Nano Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 10

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Direct observation of the band gap transition in atomically thin ReS2 Mathias Gehlmann,† Irene Aguilera,‡ Gustav Bihlmayer,‡ Slavomír Nemšák,† Philipp Nagler,¶ Pika Gospodarič,† Giovanni Zamborlini,† Markus Eschbach,† Vitaliy Feyer,† Florian Kronast,§ Ewa Młyńczak,†,k Tobias Korn,¶ Lukasz Plucinski,∗,† Christian Schüller,¶ Stefan Blügel,‡ and Claus M. Schneider† †PGI-6, Forschungszentrum Jülich GmbH, Germany ‡PGI-1/IAS-1, Forschungszentrum Jülich GmbH and JARA, Germany ¶Institut für Experimentelle und Angewandte Physik, Universität Regensburg, Germany §Abteilung Materialien für grüne Spintronik, Helmholtz-Zentrum Berlin, Germany kFaculty of Physics and Applied Computer Science, AGH University of Science and Technology, Poland E-mail: [email protected]

Abstract

vices and van der Waals heterostructures.

ReS2 is considered as a promising candidate for novel electronic and sensor applications. The low crystal symmetry of this van der Waals compound leads to a highly anisotropic optical, vibrational, and transport behavior. However, the details of the electronic band structure of this fascinating material are still largely unexplored. We present a momentum-resolved study of the electronic structure of monolayer, bilayer, and bulk ReS2 using k-space photoemission microscopy in combination with firstprinciples calculations. We demonstrate that the valence electrons in bulk ReS2 are – contrary to assumptions in recent literature – significantly delocalized across the van der Waals gap. Furthermore, we directly observe the evolution of the valence band dispersion as a function of the number of layers, revealing the transition from an indirect band gap in bulk ReS2 to a direct gap in the bilayer and the monolayer. We also find a significantly increased effective hole mass in single-layer crystals. Our results establish bilayer ReS2 as an advantageous building block for two-dimensional de-

Keywords ReS2 , band gap transition, photoemission spectroscopy, GW structure calculations, van der Waals materials. Introduction. Transition metal dichalcogenides (TMDs) hold a tremendous potential for novel electronic and sensoric applications. 1–3 Being van der Waals (vdW) compounds they can be thinned down to atomically thin sheets in the same fashion as graphene, but since they include several semiconducting materials with band gaps within the optical range 4,5 they pose a crucial addition to the available “atomic Legos” 6 as building blocks for two-dimensional devices and vdW heterostructures. 3,7–14 For several years the majority of research in this field focused on the classical TMDs: MoS2 , MoSe2 , WS2 , and WSe2 . The bulk crystals of these materials are indirect band gap semiconductors, but undergo a transition into a direct band gap when they are thinned down to the monolayer limit. 5,15–19 The direct band gap leads to a drastically increased performance of the mono-

ACS Paragon Plus Environment

1

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 ACS Paragon Plus Environment

Page 2 of 10

Page 3 of 10

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 ACS Paragon Plus Environment

Page 4 of 10

Page 5 of 10

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

cause the quantum confinement shifts the bulk VBM at the Γ point below the distinct valleys at the BZ edges, which do not exist in ReS2 in this form. The indirect character of the gap is by far less pronounced in ReS2 , which is a likely explanation why recent studies found indications for both an indirect and a direct gap. The fundamental band gaps predicted by the GW approximation are 1.85, 1.70, and 1.57 eV for the monolayer, bilayer, and bulk, respectively. In terms of the valence band structure our GW calculations are equivalent to our results from DFT. It is worth mentioning that the indirect character of the bulk band structure found in the GW calculations is a result of the many-body effects that are not incorporated in the GGA calculations. The conduction band structure in the GGA calculations is slightly different from GW and shows a direct band gap at the A-point of the bulk crystal (see supporting information for comparison). Another interesting aspect that is revealed by our results is that the thinning step from bilayer to monolayer, which enforces the complete confinement of the valence electrons within two dimensions, is accompanied by a significant decrease of the valence band dispersion in the xy-directions as well. This observation can be interpreted as an increased effective mass of the electrons close to the VBM. Recently, it was found in layer-dependent transport measurements that monolayers of ReS2 have a drastically reduced conductivity compared to bilayers or thicker crystals. 30 Apart from the larger band gap, this behavior was attributed to a significantly stronger influence of impurities and the interface. Our results rather suggest an intrinsic mechanism that suppresses the delocalization of VBM electrons within the x-y-plane. This behavior could significantly impact the electron mobility for single monolayer crystals. Recent studies using Raman spectroscopy have found indications for the existence of different polytypes in exfoliated ReS2 crystals. 22–25 Although the commercially available single crystals used in this study are grown in the distorted T1 phase 39 (see fig. 1), there is a chance that the stacking order of the bilayer sample was disturbed, e.g. by mechanical force

Page 6 of 10

during the exfoliation process. Therefore, we studied the influence of different stacking orders and structural relaxation on the band structure via DFT. The additional band structure calculations are included in the supporting information, and show that the band structure of bilayer ReS2 is not significantly altered by such effects. In particular, the direct band gap and the strong dispersion of the valence band close to the Γ point appear to be very robust properties. Conclusions. Using a combination of kspace photoemission microscopy and band structure calculations we have presented a thorough, momentum-resolved study of the electronic band structure of monolayer, bilayer, and bulk ReS2 . By showing a significant outof-plane delocalization of the valence electrons we have demonstrated that – contrary to assumptions in the recent literature – the layers of bulk ReS2 are not electronically decoupled. We identified the layer-dependent position of the VBM in our photoemission data, and in combination with our band structure calculations we concluded that only bilayer ReS2 has a direct band gap with well-dispersing band edges, although the indirect character of the gap for other crystal thicknesses is far less pronounced than in classical TMDs. Our results have shown that in monolayer ReS2 the valence electrons at the VBM suffer from a drastic increase of their effective mass, suggesting an intrinsic mechanism that could reduce the hole mobility in the in-plane directions compared to bilayers or thicker crystals. For many applications this feature in combination with the direct band gap would make ReS2 bilayers a preferred choice in comparison to monolayers or thicker crystals. Sample Preparation. The ReS2 single crystal was purchased from HQGraphene and cleaved in air with adhesive tape immediately before it was introduced into ultra-high vacuum and degassed at 250◦ C. Atomically thin ReS2 samples were produced ex situ by mechanical exfoliation from a bulk crystal. Using an all dry viscoelastic stamp method, which is described in Ref. (40), a ReS2 sample that simultaneously contained monolayer as well as bilayer areas

ACS Paragon Plus Environment

6

Page 7 of 10

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

was transfered onto HOPG. The thicknesses of the ultra-thin sample areas can be identified by the optical contrast in the transmission mode of an optical microscope, and were confirmed via atomic force microscopy (AFM) (see supporting information). The atomically thin samples were degassed in situ for one hour at 150◦ C. PEEM images of the samples and optical microscope images taken before and after the transfer process are shown in the supporting information. Photoemission Experiments. The photoemission experiments on the ReS2 bulk crystal were performed at the NanoESCA beamline of Elettra, Trieste, using a modified FOCUS NanoESCA. Homogeneous areas on the cleaved surface were identified using PEEM in real space mode and Hg lamp as excitation source. The lateral resolution of the k-resolved photoemission maps was limited by the beam size (10 µm × 10 µm) ruling out the influence of step edges and grain boundaries. The total energy resolution was better than 100 meV. Due to the highly focused synchrotron beam on the sample, the spectra suffered from charging effects, which were corrected in the data by an energy offset of 100 − 150 meV. The photoemission experiments on the atomically thin ReS2 samples were performed at the UE49 SPEEM endstation of BESSY II, Berlin. Using the field aperture of the PEEM the field of view in real space was limited to ≈ 5 µm. This way the monolayer and bilayer parts of the sample could be selectively measured in momentum mode. The total energy resolution was 300 meV. The orientation of the BZ was aligned by identifying the series of flat bands perpendicular to the baxis as they are visible in fig. 2 (a) and fig. 3 (d), as well as in our band structure calculations. Band structure calculations. Calculations were carried out with the DFT code Fleur 41 and the GW code spex, 42 which use the all-electron full-potential linearized augmented-plane-wave (FLAPW) formalism. The electron density was obtained with the Perdew-Burke-Ernzerhof (PBE) functional. We used the experimental lattice structure of Ref. (20). The calculations of the monolayer, bilayer, and 3-layer slab were performed with a tight-binding Hamiltonian with ab-initio

parameters obtained from the bulk GW calculation. Maximally localized Wannier functions, generated by the wannier90 library, 43 were used as a basis. Acknowledgement The authors thank the Helmholtz-Zentrum Berlin and Elettra Sincrotrone Trieste for providing synchrotron radiation. The financial support by the Helmholtz Association via the Initiative and Networking Fund and via the Virtual Institute for Topological Insulators, and by the DFG via GRK1570 is gratefully acknowledged. Supporting Information Available: Computational details of the band structure calculations. Comparison of the DFT and GW band structure calculations for bulk ReS2 . Optical microscope images of the exfoliated sample. AFM measurements of the exfoliated sample. Additional band structure calculations including structural relaxation and different stacking orders of bilayer crystals. This material is available free of charge via the Internet at http://pubs.acs.org/.

References (1) Ajayan, P.; Kim, P.; Banerjee, K. Phys. Today 2016, 69, 38. (2) Björkman, T.; Gulans, A.; Krasheninnikov, A. V.; Nieminen, R. M. Journal of Physics: Condensed Matter 2012, 24, 424218. (3) Geim, A. K.; Grigorieva, I. V. Nature 2013, 499, 419–425. (4) Splendiani, A.; Sun, L.; Zhang, Y.; Li, T.; Kim, J.; Chim, C.-Y.; Galli, G.; Wang, F. Nano Letters 2010, 10, 1271–1275. (5) Mak, K. F.; Lee, C.; Hone, J.; Shan, J.; Heinz, T. F. Phys. Rev. Lett. 2010, 105, 136805. (6) Geim, A. K. SciAm 2014, 311, 50–51. (7) Furchi, M. M.; Pospischil, A.; Libisch, F.; Burgdörfer, J.; Mueller, T. Nano Letters 2014, 14, 4785–4791.

ACS Paragon Plus Environment

7

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(8) Withers, F.; Pozo, D.; Mishchenko, A.; Rooney, A.; Gholinia, A.; Watanabe, K.; Taniguchi, T.; Haigh, S.; Geim, A.; Tartakovskii, A.; Novoselov, K. Nat. Mater. 2015, 14, 301–306.

Page 8 of 10

(19) Cappelluti, E.; Roldán, R.; SilvaGuillén, J. A.; Ordejón, P.; Guinea, F. Phys. Rev. B 2013, 88, 075409. (20) Murray, H.; Kelty, S.; Chianelli, R.; Day, C. Inorganic Chemistry 1994, 33, 4418.

(9) Cheng, R.; Li, D.; Zhou, H.; Wang, C.; Yin, A.; Jiang, S.; Liu, Y.; Chen, Y.; Huang, Y.; Duan, X. Nano Letters 2014, 14, 5590–5597.

(21) Aslan, O. B.; Chenet, D. A.; van der Zande, A. M.; Hone, J. C.; Heinz, T. F. ACS Photonics 2016, 3, 96–101.

(10) Jariwala, D.; Marks, T. J.; Hersam, M. C. Nat. Mater. 2017, 16, 170–181.

(22) Zhao, H.; Wu, J.; Zhong, H.; Guo, Q.; Wang, X.; Xia, F.; Yang, L.; Tan, P.; Wang, H. Nano Research 2015, 8, 3651– 3661.

(11) Coy Diaz, H.; Avila, J.; Chen, C.; Addou, R.; Asensio, M. C.; Batzill, M. Nano Letters 2015, 15, 1135–1140.

(23) Nagler, P.; Plechinger, G.; Schüller, C.; Korn, T. Phys. Status Solidi Rapid Res. Lett. 2016, 10, 185–189.

(12) Radisavljevic, B.; Radenovic, A.; Brivio, J.; Giacometti, V.; Kis, A. Nat. Nano 2011, 6, 147.

(24) He, R.; Yan, J.-A.; Yin, Z.; Ye, Z.; Ye, G.; Cheng, J.; Li, J.; Lui, C. H. Nano Letters 2016, 16, 1404–1409.

(13) Roy, T.; Tosun, M.; Cao, X.; Fang, H.; Lien, D.-H.; Zhao, P.; Chen, Y.-Z.; Chueh, Y.-L.; Guo, J.; Javey, A. ACS Nano 2015, 9, 2071–2079.

(25) Lorchat, E.; Froehlicher, G.; Berciaud, S. ACS Nano 2016, 10, 2752–2760.

(14) Man, M. K. L.; Deckoff-Jones, S.; Winchester, A.; Shi, G.; Gupta, G.; Mohite, A. D.; Kar, S.; Kioupakis, E.; Talapatra, S.; Dani, K. M. Sci. Rep. 2016, 6, 20890, Article.

(26) Lin, Y.-C.; Komsa, H.-P.; Yeh, C.-H.; Björkman, T.; Liang, Z.-Y.; Ho, C.-H.; Huang, Y.-S.; Chiu, P.-W.; Krasheninnikov, A. V.; Suenaga, K. ACS Nano 2015, 9, 11249–11257.

(15) Zhang, Y. et al. Nat Nano 2014, 9, 111– 115.

(27) Tongay, S. et al. Nat. Commun. 2014, 5 . (28) Gutiérrez-Lezama, I.; Reddy, B. A.; Ubrig, N.; Morpurgo, A. F. 2D Materials 2016, 3, 045016.

(16) Jin, W.; Yeh, P.-C.; Zaki, N.; Zhang, D.; Sadowski, J. T.; Al-Mahboob, A.; van der Zande, A. M.; Chenet, D. A.; Dadap, J. I.; Herman, I. P.; Sutter, P.; Hone, J.; Osgood, R. M. Phys. Rev. Lett. 2013, 111, 106801.

(29) Qiao, X.-F.; Wu, J.-B.; Zhou, L.; Qiao, J.; Shi, W.; Chen, T.; Zhang, X.; Zhang, J.; Ji, W.; Tan, P.-H. Nanoscale 2016, 8, 8324–8332.

(17) Wang, Q. H.; Kalantar,; Kis, A.; Coleman, J. N.; Strano, M. S. Nat. Nano 2012, 7, 699–712.

(30) Ovchinnikov, D.; Gargiulo, F.; Allain, A.; Pasquier, D. J.; Dumcenco, D.; Ho, C.H.; Yazyev, O. V.; Kis, A. Nat. Commun. 2016, 7, 12391.

(18) Han, S. W.; Kwon, H.; Kim, S. K.; Ryu, S.; Yun, W. S.; Kim, D. H.; Hwang, J. H.; Kang, J.-S.; Baik, J.; Shin, H. J.; Hong, S. C. Phys. Rev. B 2011, 84, 045409.

(31) Krömker, B.; Escher, M.; Funnemann, D.; Hartung, D.; Engelhard, H.; Kirschner, J. Review of Scientific Instruments 2008, 79, 053702.

ACS Paragon Plus Environment

8

Page 9 of 10

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

(32) Tusche, C.; Krasyuk, A.; Kirschner, J. Ultramicroscopy 2015, 159, Part 3, 520 – 529. (33) Wiemann, C.; Patt, M.; Krug, I. P.; Weber, N. B.; Escher, M.; Merkel, M.; Schneider, C. M. e-Journal of Surface Science and Nanotechnology 2011, 9, 395–399. (34) Kim, H.; Dumcenco, D.; Frégnaux, M.; Benayad, A.; Chen, M.-W.; Kung, Y.-C.; Kis, A.; Renault, O. Phys. Rev. B 2016, 94, 081401. (35) Seah, M. P.; Dench, W. A. Surface and Interface Analysis 1979, 1, 2–11. (36) Gehlmann, M.; Aguilera, I.; Bihlmayer, G.; Młyńczak, E.; Eschbach, M.; Döring, S.; Gospodarič, P.; Cramm, S.; Kardynał, B.; Plucinski, L.; Blügel, S.; Schneider, C. M. Sci. Rep. 2016, 6, 26197. (37) Cudazzo, P.; Tokatly, I. V.; Rubio, A. Phys. Rev. B 2011, 84, 085406. (38) Zhong, H.-X.; Gao, S.; Shi, J.-J.; Yang, L. Phys. Rev. B 2015, 92, 115438. (39) HQgraphene: ReS2 single crystals. http: //www.hqgraphene.com/ReS2.php, Accessed: 2017-06-01. (40) Castellanos-Gomez, A.; Buscema, M.; Molenaar, R.; Singh, V.; Janssen, L.; van der Zant, H. S. J.; Steele, G. A. 2D Materials 2014, 1, 011002. (41) FLEUR project homepage. http://www. flapw.de/, Accessed: 2016-10-03. (42) Friedrich, C.; Blügel, S.; Schindlmayr, A. Phys. Rev. B 2010, 81, 125102. (43) Mostofi, A. A.; Yates, J. R.; Lee, Y.S.; Souza, I.; Vanderbilt, D.; Marzari, N. Comput. Phys. Commun. 2008, 178, 685.

ACS Paragon Plus Environment

9

Nano Letters Page 10 of 10

1 2 3 Paragon Plus Environment ACS 4 5 6