Distribution of Total Sulfur in Acidic, Basic, and Neutral Fractions on

Feb 24, 2015 - ... and Neutral Fractions on Brazilian Asphalt Cements and Its Relationship to the ..... studies of sulfur compounds and its relationsh...
0 downloads 0 Views 442KB Size
Subscriber access provided by NEW YORK MED COLL

Article

Distribution of Total Sulfur in Acidic, Basic and Neutral Fractions on Brazilian Asphalt Cements and its Relationship to the Aging Process Leandro M. de Carvalho, Paulo C. do Nascimento, Denise Bohrer, Luis E. Claussen, Luis Ferraz, Carla Grassmann, Hugo T. S. Braibante, Daiane Dias, Margareth Cravo, and Leni F. Mathias Leite Energy Fuels, Just Accepted Manuscript • DOI: 10.1021/ef5025643 • Publication Date (Web): 24 Feb 2015 Downloaded from http://pubs.acs.org on February 28, 2015

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Energy & Fuels is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

1

Distribution of Total Sulfur in Acidic, Basic and Neutral Fractions on

2

Brazilian Asphalt Cements and its Relationship to the Aging Process

3 4

Leandro M. de Carvalho*a, Paulo C. do Nascimentoa, Denise Bohrera, Luís E. Claussena, Luis Ferraza,

5

Carla Grassmann a, Hugo T. S. Braibantea, Daiane Diasb, Margareth Cravoc and Leni F. M. Leitec

6 7

a

8

Brazil

9

b

10

c

11

PETROBRAS, Rio de Janeiro, RJ, Brazil

Departamento de Química, Universidade Federal de Santa Maria, 97110-970, CP 5051, Santa Maria, RS,

Departamento de Química, Universidade Federal do Rio Grande, Rio Grande, RS, Brazil Centro de Pesquisas e Desenvolvimento “Leopoldo Américo Miguez de Mello” (CENPES),

12 13 14 15 16

AUTHOR INFORMATION:

17

Phone/FAX: +55-32208870. E-mail:[email protected]

18 19

ACS Paragon Plus Environment

1

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 28

20 21

ABSTRACT: In this work, studies were performed in Brazilian asphaltic cements by

22

separating fractions of maltenes and asphaltenes using non-aqueous ion exchange liquid

23

chromatography (NIELC). Initially, three different aging processes (RTFOT, PAV and

24

SUNTEST) were applied to 23 different asphaltic cements for evaluating the changing of

25

asphaltenic (12.7±2.5 %) and maltenic

26

process was studied in a comparative way for 5 asphalt cements samples, since it caused the more

27

pronounced changes in maltenes and asphaltenes among the asphaltic cements supplied by

28

different Brazilian refineries. Asphaltenes presented the highest amount of polar compounds in all

29

the studied samples, herein attributed to compounds of acidic and basic character that contain

30

sulfur. It was also found that the aging of asphalt cement leads to an increase of the more reactive

31

acidic (9.5−18.9%) and basic (14.6−30.9%) fraction in both asphaltenes and maltenes. As a result,

32

a reactivity index (Ir) for asphaltic cements was calculated and proposed for classifying the studied

33

samples regarding their aging susceptibility. It was also observed that the less reactive asphaltic

34

cement presented the highest amount (>80%) of neutral sulfur compounds in maltenic fraction.

35

Lastly, it was concluded that a higher content of total sulfur in asphalts does not imply necessarily

36

in a higher chemical reactivity (susceptibility to aging) of the cement, as observed for 5 studied

37

samples having total sulfur ranging from 1.8 to 3.4% (w/w). The presence of functional groups

38

related to their specific heteroatoms, such as sulfur, suggest a possible way to explain a greater or

39

lesser susceptibility of asphalts to aging.

(90.6±5.0 %) compounds. The RTFOT+SUNTEST

40 41

Keywords: Asphalt cements; total sulfur distribution; aging processes, SUNTEST, reactivity

42

index.

43 44

ACS Paragon Plus Environment

2

Page 3 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

45

Energy & Fuels

1.

INTRODUCTION

46 47

The speciation of sulfur in asphalt cements has becoming an important issue from

48

scientific and technological viewpoints, since sulfur compounds are considered precursors of

49

asphalt oxidation reactions. In this context, it is already known that changes in the

50

physicochemical and rheological properties of asphalt cements are caused mainly by alteration in

51

the chemistry of sulfured functional groups, the viscosity and the balance of polar/nonpolar

52

groups.1 Among the processes involved in the asphalt aging, oxidation is considered the most

53

significant one, since it takes place during the application of the wearing course and continues

54

slowly during its pavement service.2 Beyond the formation of oxygenated compounds, the polar

55

groups present in the asphalt cement tend to associate, forming micelles and agglomerates of high

56

molecular weight and higher viscosity (asphaltenes).

57

It is well known that oxidation processes in asphalts involve mainly the heteroatom sulfur

58

by oxidation of e.g. sulfides to sulfoxides.1,2 Beyond oxidation processes involving sulfur

59

compounds, carbonyl formation associated to e.g. naphthenes are involved in the chemical

60

transformations taking place during asphalt aging.1 Chemical transformation of polar fractions in

61

asphalts involve also the formation of ketones and alcohols concurrently with sulfoxides, being

62

alcohols the main contributors to oxidative aging of asphalts with high content of sulfur.3

63

Furthermore, ketones are formed primarily from the oxidation of benzyl carbons in side chains

64

attached to highly condensed aromatic ring systems, which exist largely in the polar aromatics

65

fraction of asphalts.4,5 Beyond the organic compounds containing basically sulfur, nitrogen and

66

oxygen as heteroatoms, metallorganic compounds, such as vanadyl porphyrins, have been also

67

described for asphaltic matrices and are also involved in the aging processes.6,7

68

ACS Paragon Plus Environment

3

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 28

69

In this context, chemical transformations involving specific classes of sulfur compounds,

70

such as thiophenes, sulfides, sulfoxides and sulfones of acidic, basic and neutral character were

71

studied by Green, Payzant and co-workers.8−13 According to these work, there is a distribution of

72

species according to their acid-base character in each respective class of sulfur compounds. These

73

species characterize the more polar and, consequently, more reactive fraction of asphalt cements

74

and can be directly involved in the aging mechanism. However, the understanding of the

75

mechanisms associated with specific sulfur classes and their transformations during the aging has

76

been investigated so little depth up to date.

77

Speciation studies of sulfur compounds in asphalt have been described in the literature for

78

asphaltic matrices produced in different countries.8−13 Although Brazil is one of the important

79

producers of petroleum and petroleum-derived products worldwide, systematic studies focused on

80

the physicochemical characterization of the asphalt cements produced in the refineries spread over

81

the country have not been performed in depth up to date. Furthermore, the knowledge of sulfur

82

species as markers of aging and quality indicators of asphalt cement is highly relevant, since it can

83

contribute to establishing of criteria for the production of more resistant asphaltic mixtures and

84

their additives as well.

85

The aging process of asphalt cements have been evaluated by different analytical methods,

86

which use techniques merely for specification studies or elucidation/understanding of the asphalt

87

cement behavior. A typical method used for the characterization of asphalt cements is the liquid

88

chromatography using silica columns (IATROSCAN), which identifies and quantifies the more

89

generic chemical fractions (SARA: Saturates, Aromatics, Resins and Asphaltenes). Gel

90

permeation chromatography (GPC) is used for separating the compounds according to the

91

apparent molecular weight and the infrared spectroscopy (FTIR) identifies some functional groups

92

(e.g. carbonyls and sulfoxides) formed after oxidation.14−17 Atomic force microscopy (AFM) has

ACS Paragon Plus Environment

4

Page 5 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

93

been recently applied to studies of physical properties of asphalts submitted to aging processes.18,

94

19

95

In this work, studies were performed in asphalt cements by separating different fractions in

96

order to understand their formation, especially regarding sulfur compounds. Initially, the

97

separation of virgin asphalt cements was carried out for asphaltenes and maltenes by using the

98

method described in ASTM D 4124.20 The next step consisted in a second fractionation, where

99

both maltenes as asphaltenes were separated into acidic, basic and neutral fractions. For this

100

purpose, the method described by Green and co-workers9 was adapted and applied to samples of

101

Brazilian asphalt cements. The separations based on both the mentioned methods were made

102

comparatively for virgin and aged asphalt cements. Thus, total sulfur was determined in the acidic,

103

basic, and neutral asphalt fractions submitted to the different aging processes. Thus, the

104

distribution of the compound classes in asphaltenic and maltenic fractions was obtained. The

105

distribution profile for these compound classes was observed in asphaltenes and maltenes, which

106

gave information on chemical transformations occurring during the aging process of asphalt

107

cements. Considering the studied total sulfur distribution, a reactivity index (Ir) for 5 different

108

asphaltic cements was calculated and proposed for classifying the studied samples regarding their

109

aging susceptibility.

110 111

2.

EXPERIMENTAL SECTION

112 113

2.1 Instrumentation and Apparatus

114 115

All asphalt cement samples were heated at 100 ° C for 60 minutes in an oven provided of

116

air circulation (Q314 M - Quimis) before sampling the matrix for separations in order to keep the

ACS Paragon Plus Environment

5

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 28

117

sample in a homogeneous form. The sample was then weighted for applying in the separation

118

systems by NIELC.9

119 120

2.2 Reagents

121 122

Ion-exchange resins MP-1 (anionic) and PM-50 (cationic) were obtained from Biorad

123

Laboratories (Richmond, CA, USA) with particle sizes of 200-400 mesh (37-75 µm). These resins

124

were used for separation of acidic, basic and neutral sulfur compounds by non-aqueous ion

125

exchange liquid chromatography (NIELC).9 Methanol, isooctane, benzene, cyclohexane, ethyl

126

ether, propanol, toluene, n-pentane, sulfuric acid, dichloromethane, sodium hydroxide were

127

obtained from Merck (Damrstadt, Germany). Propylamine was obtained from Sigma-Aldrich (St.

128

Louis, MO, USA).

129 130

2.3 Samples

131 132

A total of 23 samples of asphaltic cements were analyzed in this work for asphaltenes and

133

maltenes content. Five samples of asphalt cements were studied before and after the three aging

134

processes (described below) and analyzed in a comparative way for speciation purposes. The

135

samples were supplied by five different refineries in Brazil and analyzed as received.

136 137 138 139 140 141

ACS Paragon Plus Environment

6

Page 7 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

142

Energy & Fuels

2.4 Analytical procedures

143 144

2.4.1 Separation of asphaltenes and maltenes

145 146

The separation of asphaltenic and maltenic fractions was carried out according to the

147

ASTM D4124.20 Briefly, the sample was weighted and refluxed in isooctane (100 mL for each

148

gram of sample). The mixture was heated and stirred once the reflux was initiated. The

149

temperature was maintained at 99 °C by stirring for 1-2 h, until no observation of adherence of the

150

asphalt matrix at the glassware. Once the asphalt cement was dissolved, the solution was stirred

151

for 1 h longer. The solution was cooled and stirred for 2 h and the condensator was washed from

152

top to bottom with 10-20 mL isooctane. After, this step, the solution was kept at resting for 2 h

153

before filtration. The solution was filtered using vacuum and the residues of asphaltenes adhered

154

to the glassware was washed with 100 mL isooctane by refluxing for 30 min. The filtration cake

155

was washed with isooctane until it became colorless. The filtrate represents the soluble fraction

156

(maltenes) and the residue of the funnel represents the insoluble fraction (asphaltenes). The

157

obtained filtrate (maltenes) was evaporated in order to eliminate the solvent residue. Both the solid

158

fractions (asphaltenes and maltenes) were weighted for calculating the mass balance of the

159

process.

160 161

2.4.2 Separation of acidic, basic and neutral compounds by NIELC

162 163

The fractionation of asphalt matrix in acidic, basic and neutral compounds was carried out

164

by using the NIELC method developed by Green et al.9 Briefly, 2.5 g of virgin asphalt cement was

165

dissolved in ciclohexane and applied to a separation system containing two columns composed of

166

a cationic and an anionic ion-exchange stationary phase connected in series. The columns were

ACS Paragon Plus Environment

7

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 28

167

previously cleaned and activated according to the procedure. After applying the sample to the two

168

column systems, ciclohexane (100 mL) was added and the neutral fraction was obtained. The

169

columns were disconnected and treated separately. 10 mL of methanol was added to each

170

disconnected columns and the aliquots were collected separately for using in the respective

171

extraction procedure. The column containing the cation exchange resin was extracted in a Soxhlet

172

system for 10 h with benzene and formic acid (10 mL) in order to obtain the acidic fraction. The

173

column containing the anionic exchange resin was extracted in another Soxhlet system for 10 h

174

with benzene and propylamine (10 mL) in order to obtain the basic fraction. After the extraction

175

processes, the products were evaporated and weighted for determining the mass of the fraction.

176 177

2.4.3 Aging process of asphaltic cements

178 179

Three different procedures were used for simulating the aging process of asphalt cements.

180

The Rolling Thin Film Oven Test (RTFOT) simulates the short term aging of asphalt during the

181

hot mix, truck and silo storage, spray and compaction process, which takes place during its

182

application. For this purpose, the assay is carried out at high temperatures and in the presence of

183

oxygen (ASTM D 2872).21 The Pressure Aging Vessel (PAV) test was developed by the Strategic

184

Highway Research Program (SHRP) and simulates the aging of the asphaltic binder in situ, i.e.,

185

during its use as a road pavement at service temperatures. In the long term procedure, the asphalt

186

sample is normally first conditioned using the RTFOT method. Thus, the residue from the RTFOT

187

is placed in standard stainless steel pans and aged at the specified conditioning temperature for 20

188

h in a vessel pressurized with air to 2.10 MPa. The conditioning temperature is selected according

189

to the grade of asphalt cement. The residue is lastly vacuum degassed (ASTM D 6521).22 The

190

SUNTEST aging procedure simulates a natural weathering of the asphalt cements under influence

ACS Paragon Plus Environment

8

Page 9 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

191

of UV radiation in pavement service.2 Herein, asphalt cements were also first conditioned using

192

the RTFOT method and then submitted to UV radiation test (48 hours at 60ºC).

193 194

2.4.4 Determination of total sulfur

195 196

In order to approach the possible role of sulfur compounds present in acidic, basic and

197

neutral asphalt fractions, the determination of total sulfur in the obtained fractions were carried out

198

by combustion of the samples based on the determination of SO2 performed by infrared

199

spectroscopy (ASTM D1552).23 All the samples of asphalt cements and its fractions were

200

dissolved in toluene prior to the analysis.

201 202 203

3. RESULTS AND DISCUSSION

204 205

The chemical characterization of asphalt cements is a very important issue, since it is

206

directly related to the physical performance of asphalts. However, the chemical speciation of

207

sulfur compounds in maltenic and asphaltenic fractions and its relationship with the mechanisms

208

that take place during the aging of asphalts has been little explored up to date. Thus, the

209

distribution of sulfur compounds in different samples of asphalt cements produced by different

210

Brazilian refineries was investigated. In a first step, 23 samples were characterized according to

211

the distribution of asphaltenes and maltenes. In a second step, five samples were randomly

212

selected for speciation studies of sulfur compounds and its relationship with the aging processes.

213

The 23 samples investigated in this work showed a distribution of asphaltenes and

214

maltenes with a significant higher amount of maltenes (90.6±5.0%) compared to asphaltenes

215

(12.7±2.5%), as expected and previously reported for other asphaltic products.1,15,24,25 Thus, after

ACS Paragon Plus Environment

9

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 28

216

characterizing the samples according to their asphaltenic and maltenic fractions, the speciation

217

studies were conducted in order to elucidate the distribution of sulfur compounds within these

218

fractions.

219 220

3.1 Speciation of acidic, basic and neutral sulfur compounds in asphaltenes and maltenes

221 222

According to Green,8−11 the fractionation of asphalt cements by ion exchange liquid

223

chromatography

in

non-aqueous

medium

(NIELC)

is

based

on

the

obtaining

of

224

positively/negatively charged and neutral compounds using cationic and anionic exchange resins.

225

According to Payzant,12,13 the fractionation of dissolved asphalt cements in the ion exchange

226

resins lead to the obtaining of acidic, basic and neutral fractions, which consist of the following

227

majority sulfur compound classes: sulfoxides, sulfones, sulfides, thiophenes, mercaptans, and

228

sulfonic acids. Even being present in a variety of structures, the conditions during formation and

229

maturation of a petroleum reservoir can lead to the existence of some preferential forms. All these

230

species can also be present as aliphatic or aromatic forms. Regardless the form they are present,

231

sulfur compounds can be associated with three different oxidation states in asphalts: S(−2):

232

sulfides, disulfides, thiols and thiophenes; S(+2): sulfoxides; and S(+4): sulfones and sulfonic

233

acids. Therefore, the chemical speciation of sulfur in asphalt cements can involve both their

234

oxidation states (redox speciation) and their binding forms (surrounding chemical environment).

235

The sulfur charged structures separated in the ion exchange resins9 may be defined as the

236

most reactive fraction, which is more susceptible to undergo oxidation, agglomeration, and

237

condensation reactions.15,24,25-28 As shown in Table 1, both the asphaltenic and maltenic fractions

238

in Brazilian asphalts are composed mostly of neutral compounds containing sulfur. After

239

fractionation of maltenes and asphaltenes into acidic, basic and neutral subfractions, we observed

240

a similar pattern in the total sulfur distribution. Despite the observed measurement deviations, the

ACS Paragon Plus Environment

10

Page 11 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

241

neutral fraction was found to be the majority fraction in maltenes and asphaltenes. This behavior

242

was observed for a total of 23 samples analyzed, considering merely the gravimetric determination

243

of the solid products obtained after fractionating the acids, bases and neutral species.

244 245

TABLE 1

246 247

The acidic, basic and neutral compounds containing sulfur present in asphalts allows us to

248

establish that: (1) most of the compounds present in asphalt cements (in both asphaltenes and

249

maltenes) are of neutral character (less reactive species); (2) acidic and basic compounds (more

250

reactive species) represent a minority fraction of asphalt cements. Furthermore, asphaltenes

251

presented the highest amount of polar compounds (25.3−50.9%) in the studied samples, herein

252

attributed to acidic and basic compounds that contain sulfur.

253

Considering a mechanistic approach based on the established sulfur organic chemistry, the

254

compounds of acidic and basic character found in asphaltenes and maltenes may have in their

255

structures the heteroatoms sulfur, nitrogen and oxygen. Possible structures of sulfur-containing

256

acidic compounds are associated mainly to aliphatic and aromatic positively charged species.

257

Besides sulfur, the presence of nitrogen in these structures may also contribute to the acidic

258

character of these compounds as a protonated group.29 Regarding the compounds of basic

259

character, possible structures may be associated mainly to aliphatic and aromatic negatively

260

charged species. Besides sulfur, the presence of nitrogen and oxygen in these structures should

261

also contribute to the basic character of the compounds. Thus, the basic character may be linked

262

directly to the sulfur heteroatom (e.g. sulfoxides, sulfonates, thiols and mercaptans) as well as the

263

concomitant presence of sulfur and nitrogen/oxygen heteroatoms in the structure of each

264

individual speciated compound.8,30−32

ACS Paragon Plus Environment

11

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 28

265

By making a rationalization from the sulfur organic chemistry and previous work reporting

266

data from other asphalts,8, 30−32 one can postulate that sulfur and nitrogen containing compounds of

267

amphoteric character may also be present in both separated acidic and basic forms, depending on

268

the apparent pH of the media and pKa of each species. As hypothetical example, sulfur structures

269

such as sulfilimines and sulfoximines29 may be formed depending on the environmental

270

conditions. Likewise, compounds of acidic and basic character can be protonated or deprotonated

271

and, consequently, acquire the majority neutral form depending on the medium conditions. All

272

these possible acid-base equilibriums occurring in the medium of dissolved asphalt cement may

273

explain why sulfur functionalities defined as e.g. sulfides, thiophenes, and sulfoxides are almost

274

omnipresent in acidic, basic and neutral fractions.8 Additionally, acidic and basic funcionalities

275

such as carboxylic acids, phenols, indoles, carbazoles, amides, pyrroles, pyrimidines, pyridines,

276

quinolines, acridines, and phenazines may be present in these fractions30−32 separated by NIELC.

277

Moreover, the knowledge of the chemical speciation associated with sulfur and its surrounding

278

heteroatoms (N and O) is well recognized as the key to understanding the processes of conversion

279

and migration that take place during the aging of asphalts.9,10,26

280 281

3.2

Aging of asphalt cements and the speciation of sulfur compounds

282 283

The aging process of asphalt cements occurs mainly due to loss of mass by volatilization and

284

oxidation.1,9 These processes can significantly vary depending on the different sources of asphalt

285

cements. Other factors such as temperature, light effect, chemical reactions with aggregates may

286

also contribute to this process.1 According to some authors,8,24 asphalts should have a balanced

287

amount of polar and nonpolar molecules, which would lead to the homogeneity of the binder.

288

Furthermore, the balance of these compound classes plays a key role in the aging susceptibility

289

and performance of the asphalt binder, so that any chemical imbalance in this mixture may

ACS Paragon Plus Environment

12

Page 13 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

290

Energy & Fuels

influence on its final quality.1

291

It is also well known that the aging of asphalts influences and alters the composition of

292

asphaltenes and maltenes in different ways.1,9,14,15,26 So an increased asphaltenic fraction and a

293

decreased maltenic fraction are expected after aging. Thus, the distribution of asphaltenic and

294

maltenic fractions in 5 virgin asphalt samples submitted to three aging processes (RTFOT,

295

RTFOT+PAV and RTFOT+SUNTEST) was investigated, which were lately studied for the

296

speciation involving sulfur compounds. As expected (figure 1), all the studied aging processes

297

lead to an increase in the asphaltenic fraction (figure 1A) in all the 5 samples of asphaltic cements.

298

These changes involve the formation of compounds high apparent molecular weight from

299

processes such as agglomeration and condensation.1,28 Furthermore, these new high apparent

300

molecular weight compounds may contain sulfur mainly in their higher oxidation states (+II and

301

+IV) forming sulfoxides and sulfones.9,33 For maltenes (figure 1B), it was observed that the

302

behavior was almost constant in the RTFOT aging, causing a small decrease in the RTFOT+PAV

303

aging and a more pronounced decrease in the RTFOT+SUNTEST process.

304 305

FIGURE 1

306 307

The subsequent separation of acidic (AF), basic (BF) and neutral (NF) fractions was

308

performed in maltenes and asphaltenes in order to identify the variations involving these classes

309

during the aging process. Taking into account that the RTFOT+SUNTEST process lead to the

310

more pronounced alteration in asphalt cements (figure 1), the 5 investigated samples were

311

analyzed in a comparative way for total sulfur distribution considering this process. It should be

312

also pointed out that the RTFOT+SUNTEST process takes into consideration also the effect of

313

sunlight in the asphalt aging, what is relevant for asphaltic cements used in pavements of tropical

314

countries. Figure 2 shows the behavior of sulfur compounds in virgin and RTFOT+SUNTEST

ACS Paragon Plus Environment

13

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 28

315

aged samples in a comparative way for asphaltenes. As can be seen, the average percentage of

316

acidic, basic and neutral fractions showed an increase of acid (AF) and basic (BF) sulfur

317

compounds, while the neutral compounds (NF) decreased.

318 319

FIGURE 2

320 321

Furthermore, an overall increase of about 22% of the most reactive fractions (AF + BF) in

322

asphaltenes after aging is probably related to the oxidation, condensation and agglomeration

323

reaction of sulfur compounds, which may also partially migrate from maltenes. In contrast, the

324

neutral fraction (FN) decreased by about 23%. In the case of maltenes (figure 3), the behavior of

325

sulfur compounds after aging is similar to that shown for asphaltenes. As can be seen, the average

326

percentage of acidic, basic and neutral fractions for 5 samples showed an overall increase of ~32%

327

in the more reactive fractions, while the neutral fraction (NF) decreased ~30% after aging by the

328

RTFOT+SUNTEST process.

329 330

FIGURE 3

331 332

The loss of neutral compounds in both the asphaltenic and maltenic fractions may be also

333

associated with volatilization, agglomeration and condensation reactions forming sulfur, carbon

334

and nitrogen compounds of higher polarity.14,28 These reactions can lead also to the transformation

335

of aromatics into resins and the resins into asphaltenes, resulting in a continuing increase of heavy

336

fractions14,28 and the consequent hardening of the asphalt cement. However, the aging of asphalts

337

according to these well-known majority processes was not yet specifically explained in terms of

338

distribution of sulfur compounds of acid-base character in asphaltenes and maltenes. Furthermore,

339

the observed transformations of neutral aromatics into polar compounds (resins) may be related to

ACS Paragon Plus Environment

14

Page 15 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

340

ring-open reactions observed for thiophenic fractions within the studied samples. For supporting

341

this hypothesis, a dominant process was observed in this work involving thiophenes separated by

342

the method proposed by Payzant and co-workers.13 After performing these experiments in 5

343

different asphaltic cements, a decrease of thiophenic compounds in the range 24.3−48.2% after

344

aging by RTFOT+PAV process22 was observed.

345 346

3.3 Speciation of sulfur compounds and the aging susceptibility of asphalt cements

347 348

The aforementioned and discussed results for acidic, basic and neutral fractions of

349

maltenes and asphaltenes may also be approached in terms of chemical reactivity of the sample.

350

Herein, polar compounds may confer a higher reactivity to the asphalt involving their more active

351

sites (acidic and basic functionalities). Therefore, the sum of the most reactive fractions (AF + BF)

352

divided by the less reactive fraction (NF) is proposed as a calculation index for reactivity of the

353

asphaltic cements. Thus, the sample that presents the highest reactive fraction will be the one,

354

which is more susceptible to aging. This calculation can be expressed according to the equation:

355 356 357

Ir = AFa + BFa + AFm + BFm NFa + NFm

358 359

where Ir is the reactivity index, AFa and BFa the basic and acidic fractions of asphaltenes;

360

AFm and FBm are the acidic and basic fractions of maltenes; and NFm and NFa the neutral fractions

361

of asphaltenes and maltenes, respectively. This calculation considers the sum of the more reactive

362

fractions divided by the sum of the less reactive fractions of the whole asphalt (maltenes +

363

asphaltenes). Table 2 summarizes the results in terms of reactivity of the asphalt cement compared

364

to the content of total sulfur and asphaltenes for the 5 studied virgin and aged asphalt samples. The

365

reactivity index can be also calculated specifically to each fraction of asphaltenes and maltenes

ACS Paragon Plus Environment

15

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 28

366

containing AF, BF and NF. Herein, a similar distribution of the samples was achieved concerning

367

their reactivity and aging susceptibility.

368

As can be seen, a higher concentration of total sulfur in asphalts does not imply necessarily

369

in a higher reactivity (susceptibility to aging) of the cement. Therefore, the chemical speciation

370

regarding the classes of sulfur compounds in the asphalt structure play a more important role and

371

may count lastly for a higher or lower resistance of the asphalt to the aging. Herein, compounds of

372

acidic and basic character seem to be crucial for understanding these processes and for quantifying

373

the chemical stability of the asphalt cement according to chemical parameters as well. So these

374

results suggest a classification of asphalt cements in terms of their susceptibility to aging

375

(reactivity) based on the chemical speciation of sulfur compounds, which is normally based on

376

physical parameters. Furthermore, this knowledge would allow the production of more stable

377

binder mixtures.

378 379

The classification of the studied samples considering their susceptibility to aging based on the chemical reactivity (calculated as Ir) can be expressed as follows:

380 381 382

Asphalt cement samples:

A1 < A3 < A2 < A4 < A5 Reactivity

383 384

According to the reactivity classification regarding the total sulfur distribution and

385

asphaltenes in virgin asphalt samples, there is a high similarity between asphaltene composition

386

and reactivity based on sulfur compounds. So sample A1 presented a lower reactivity and lower

387

content of asphaltenes, whereas sample A5 is the one with higher reactivity and higher content of

388

asphaltenes (table 2). However, it can vary from sample to sample. This situation suggests that a

389

higher content of asphaltenes may be related, but not necessarily imply in a higher reactivity of the

390

asphalt cement, as can be observed for samples A4 and A5 (table 2). This would depend on the

391

sample, which has specific functional groups related to their heteroatoms (S, N and O),

ACS Paragon Plus Environment

16

Page 17 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

392

characterizing a greater or lesser susceptibility of the cement to aging. Furthermore, it was

393

observed that the less reactive sample (A1) presented the highest amount (>80%) of neutral sulfur

394

compounds in maltenic fraction of asphalt. Considering that this sample suffered the higher

395

variation of Ir after aging (table 2), one can infers that the most important chemical transformation

396

in the asphaltic cement occurred in maltenes involving all neutral compounds. Considering that

397

oxidative aging is also a time-dependent process, asphalt cements having neutral compounds as a

398

majority class seem to be more resistant to aging by RTFOT+SUNTEST process. Additionally,

399

the neutral fraction of maltenes has probably amphoteric compounds that may be involved in the

400

chemical transformations taking place during aging. Furthermore, sample A1 presented the higher

401

variation of asphaltene content (+3.0%) after aging (table 2). Since this sample presented the

402

lower asphaltene content (virgin sample), the higher variation of Ir after aging is related mostly to

403

the increasing of acidic and basic sulfur compounds in this fraction, which may partially migrate

404

from maltenes as oxidized compounds (e.g. sulfoxides and sulfones). As can be also observed in

405

table 2, sample A5 suffered less pronounced transformations in asphaltenic fraction (+0.1%), what

406

is probably related to a high initial concentration of polar compounds (Ir = 1.18) present as

407

asphaltenes in this cement. Beyond compounds containing sulfur, ketone formation has been also

408

identified as a major factor that lead to asphaltene formation, being asphaltenes the primary

409

responsible for viscosity increase on asphalt aging.34,35 In addition, it is already known that the

410

formation of ketone functional groups changes the polarity and solubility of the associated

411

condensed aromatic ring compounds, so that they can agglomerate and become part of the

412

asphaltene fraction.3

413 414 415 416

ACS Paragon Plus Environment

17

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

417

4.

Page 18 of 28

CONCLUSIONS

418 419

Asphalt cement is a matrix of highly complex constitution, which depends also on their

420

origin. The results discussed in this work were important for deepening the knowledge about the

421

influence of sulfur chemical speciation on the asphalt quality. Thus, the RTFOT+SUNTEST

422

process was studied in a comparative way for 5 asphalt cements samples, since it was the process

423

that caused the more pronounced changes in maltenes and asphaltenes among 23 different samples

424

supplied by different refineries. It was found that the aging of asphalt cement leads to an increase

425

of the more reactive fractions of sulfur (acidic and basic) in both asphaltenes and maltenes. In

426

addition, a decrease in the less reactive fraction (neutral) was observed in both asphaltenes and

427

maltenes. This study also showed the importance of other heteroatoms, such as nitrogen and

428

oxygen, bound to sulfur (or surrounding it) in the asphalt chemical structure, what may influence

429

on the susceptibility of the asphalt cement to aging. It was observed that sulfur appears in larger

430

amounts in the less reactive fraction (neutral) in both maltenes and asphaltenes. Herein, a

431

classification of the studied samples was proposed taking into account the reactivity calculated in

432

terms of acidic, basic and neutral compounds. It was also observed that the less reactive sample

433

(A1) presented the highest amount (>80%) of neutral sulfur compounds in maltenic fraction of

434

asphalt. Therefore, the presence of functional groups related to their specific heteroatoms seemed

435

to be definitive to explain a greater or lesser susceptibility of asphalts to aging.

436

Lastly, this study contributed to a greater understanding on the aging processes in asphalt

437

cements regarding the speciation of sulfur compounds. This understanding is necessary to improve

438

the quality of the final product, allowing the production of cements that could be more resistant to

439

aging as well as the development of processes to retard it. Moreover, the establishment of specific

440

markers within the sulfur compounds (e.g. aryl/alkyl sulfidic or tiophenic acids and bases) that

ACS Paragon Plus Environment

18

Page 19 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Energy & Fuels

441

could define an asphalt binder of greater or lesser aging resistance might be studied from this

442

approach on.

443 444

ACKNOWLEDGEMENTS

445 446

The authors acknowledge the financial support provided by the foundations CNPq and

447

CAPES. The authors also greatly acknowledge the financial support from PETROBRAS through

448

the Center of Research and Development “Leopoldo Américo Miguez de Mello” (CENPES).

449 450 451

REFERENCES

452 453

(1)

Siddiqui, M. N; Ali, M. F. Studies on the aging behavior of the Arabian asphalts. Fuel 1999, 78, 1005−1015.

454 455

(2)

Whiteoak, D. SHELL Bitumen handbook. SHELL, England, 1990.

456

(3)

Petersen, J. C.; Glaser, R. Asphalt oxidation mechanisms and the role of oxidation products on age hardening revisited. Road Mat. Pav. Design 2011, 12, 795−819

457 458

(4)

asphalts. Anal. Chem. 1974, 46, 2242−2246.

459 460

(5)

Petersen, J. C. A dual, sequential mechanism for the oxidation of petroleum asphalts. Petrol. Sci. Technol. 1998, 16, 1023−1051.

461 462

Dorrence, S. M.; Barbour, F. A.; Petersen, J. C. Direct evidence for ketones in oxidized

(6)

Aleshin, G. N.; Altukhova, Z. P.; Antipenko, V. R.; Marchenko, S. P.; Kam’yanov, V. F.

463

Distribution of vanadium and vanadyl porphyrins in petroleum distillates of different

464

chemical types. Petrol. Chem. U.S.S.R. 1984, 24, 191-195.

ACS Paragon Plus Environment

19

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

465

(7)

Page 20 of 28

Zhao, X.; Liu, Y.; Xu, C.; Yan, Y.; Zhang, Y.; Zhang, Q.; Zhao, S.; Chung , K.; Gray, M. R.;

466

Shi, Q. Separation and characterization of vanadyl porphyrins in Venezuela Orinoco heavy

467

crude oil. Energ. Fuels 2013, 27, 2874–2882.

468

(8)

Types in Asphalt. Energ. Fuel 1993, 7, 119−126.

469 470

Green, J. B.; Yu, S. K. T.; Pearson, C. D.; Reynolds, J. W. Analysis of Sulfur Compound

(9)

Green, J. B.; Hoff, J.; Woodward, P. W.; Stevens, L. L. Separation of liquid fossil fuels

471

into acid, base and neutral concentrates: 1. An improved nonaqueous ion exchange method.

472

Fuel 1984, 63,1290− −1301.

473

(10)

Green, J. A.; Green, J. B.; Grigsby, R. D.; Pearson, C. D.; Reynolds, J. W.; Shay, J. Y.;

474

Sturm Jr., G. P.; Thomson, J. S.; Vogh, J.W.; Vrana, R. P.; Yu, S. K-T.; Diehl, B. H.;

475

Grizzle, P. L.; Hirsch, D. E.; Hornung, K. W.; Tang, S-Y.; Carbognani, L.; Hazos, M.;

476

Sanchez, V. Analysis of Heavy Oils: Method Development and Application to Cerro Negro

477

Heavy Petroleum. Topical Report NIPER-452, NTIS No. DE90000201; NTIS: Springfield,

478

VA, 1989; Chapter 4.

479

(11)

Green, J. A.; Green, J. B.; Grigsby, R. D.; Pearson, C. D.; Reynolds, J. W.; Shay, J. Y.;

480

Sturm Jr., G. P.; Thomson, J. S.; Vogh, J. W.; Vrana, R. P.; Yu, S. K-T.; Diehl, B. H.;

481

Grizzle, P. L.; Hirsch, D. E.; Hornung, K. W.; Tang, S-Y.; Carbognani, L.; Hazos, M.;

482

Sanchez, V. Analysis of Heavy Oils: Method Development and Application to Cerro Negro

483

Heavy Petroleum. Topical Report NIPER-452, NTIS No. DE90000200; NTIS: Springfield,

484

VA, 1989; Chapter 3.

485

(12)

1986, 9, 357−369.

486 487

Payzant, J. D.; Montgomery, D. S.; Strausz O. P.. Sulfides in petroleum. Org. Geochem.

(13)

Payzant, J. D.; Mojelsky, T. W.; Strausz, O. P. Improved Methods for the Selective

488

Isolation of the Sulfide and Thiophenic Classes of Compounds from Petroleum. Energ.

489

Fuels 1989, 3, 449−454.

ACS Paragon Plus Environment

20

Page 21 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

490

Energy & Fuels

(14)

Mat. 2002, 16, 15−22.

491 492

Lu, X.; Isacsson, U. Effect of ageing on bitumen chemistry and reology. Constr. Build.

(15)

Qin, Q.; Schabron, J. F.; Boysen, R. B.; Farrar, M. J. Field aging effect on chemistry and

493

rheology of asphalt binders and rheological predictions for field aging. Fuel 2014, 121,

494

86−94.

495

(16)

of environmental aging on Colombian asphalts. Fuel 2014, 115, 321–328.

496 497

Fernández-Gómez, W. D.; Quintana, H. A. R.; Daza, C. E.; Lizcano, F. A. R. The effects

(17)

Lee, S. J.; Amirkhanian, S. N.; Shatanawi, K.; Kim, K. W. Short-term aging

498

characterization of asphalt binders using gel permeation chromatography and selected

499

Superpave binder tests. Constr. Build. Mater. 2008, 22, 2220−2227.

500

(18)

Introducing two new techniques. Fuel 2014, 118, 365–368.

501 502

Fischer, H. R.; Dillingh, E. C. On the investigation of the bulk microstructure of bitumen –

(19)

Rebelo, L. M.; de Sousa, J. S.; Abreu, A. S.; Baroni, M. P. M. A.; Alencar, A. E. V.;

503

Soares, S.A.; Mendes Filho, J.; Soares, J. B. Aging of asphaltic binders investigated with

504

atomic force microscopy. Fuel 2014, 117, 15–25.

505

(20)

ASTM D4124-09. Standard Test Method for Separation of Asphalt into Four Fractions.

506

(21)

ASTM D2872. Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin Film Oven Test).

507 508

(22)

Pressurized AgingVessel (PAV).

509 510

(23)

ASTM D1552. Standard Test Method for Sulfur in Petroleum Products (High-Temperature Method).

511 512

ASTM D6521-08. Standard Pratice for Accelerated Aging of Asphalt Binder Using a

(24)

Zhang, F.; Yu, J.; Han, J. Effects of thermal oxidative aging on dynamic viscosity,

513

TG/DTG, DTA and FTIR of SBS- and SBS/sulfur-modified asphalts. Constr. Build. Mater.

514

2011, 25,129−137.

ACS Paragon Plus Environment

21

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

515

(25)

Mastrofini, D.; Scarsella, M. The application of rheology to the evaluation of bitumen ageing. Fuel 2000, 79, 1005-1015.

516 517

Page 22 of 28

(26)

Michalica, P.; Daucik, P.; Zanzotto, L. Monitoring of compositional changes occurring

518

during the oxidative aging of two selected asphalts from different sources. Petroleum &

519

Coal 2008, 50, 1−10.

520

(27)

asphaltenes from heavy petroleum feedstocks. Fuel 1984, 63, 141−146.

521 522

Spheight, J. G.; Long, R. B.; Trowbridge, T. D. Factors influencing the separation of

(28)

Sugano, M.; Kajita, J.; Ochiai, M.; Takagi, N.; Iwai, S.; Hirano, K. Mechanisms for

523

chemical reactivity of two kinds of polymer modified asphalts during thermal degradation.

524

Chem. Eng. J. 2011, 176-177, 231−36.

525

(29)

York, 1977, p. 232−602.

526 527

(30)

Dutta, P. K.; Holland, R. J. Acid-base characteristics of petroleum asphaltenes as studied by non-aqueous potentiometric titrations. Fuel 1984, 63, 197−201.

528 529

Oae, S. Organic Chemistry of Sulfur. University of Tsukuba, Japan. Plenum Press, New

(31)

Okuno, I.; Latham, D. R.; Haines, W. E. Type Analysis of Nitrogen in Petroleum Using

530

Nonaqueous Potentiometric Titration and Lithium Aluminum Hydride Reduction. Anal.

531

Chem. 1965, 37, 54−57.

532

(32)

asphaltite and oil shale pyrolysis products. J. Anal. Appl. Pyrol. 1990, 17, 227−235.

533 534

Önen, A.; Sarac, A. S. Nonaqueous potentiometry for analyses of nitrogen bases from

(33)

Waldo, G. S.; Mullins, O. C.; Penner-Hahn, J. E.; Cramer, S. P.; Determination of the

535

chemical environment of sulphur in petroleum asphaltenes by X-ray absorption

536

spectroscopy. Fuel 1992, 71, 53−57.

537

(34) Petersen, J. C. A review of the fundamentals of asphalt oxidation – chemical,

538

physicochemical,

physical

property

and

durability

539

Transportation Research Board, Washington, DC, October 2009.

ACS Paragon Plus Environment

relationships,

No.

E-C140,

22

Page 23 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

540

Energy & Fuels

(35)

Lin, M. S.; Linsford, K. M.; Glover, C. J.; Davidson, R. R.; Bullin, J. A. The effects of

541

asphaltenes on the chemical and physical characteristics of asphalts, Asphaltenes:

542

Fundamentals and Applications, E.Y. Shen and O.C. Mullins, eds., Plenum Press, N.Y.,

543

1995, p. 155-176.

544 545 546

Captions to the figures

547 548

Figure 1 – Distribution pattern (n = 3) of asphaltenes (A) and maltenes (B) in asphalts submitted

549

to the aging processes RTFOT, RTFOT+PAV and RTFOT+SUNTEST compared to a virgin

550

cement sample.

551 552

Figure 2 – Distribution pattern (n = 3) of sulfur in acidic, basic and neutral compounds in

553

asphaltenes of virgin and aged asphalts (N = 5). AF: Acidic fraction; BF: Basic fraction; NF:

554

Neutral fraction. All the results are expressed as the average values related to 5 different asphalt

555

cements (described in section 2.3).

556 557

Figure 3 – Distribution pattern (n = 3) of sulfur in acidic, basic and neutral compounds in

558

maltenes of virgin and aged asphalts (N = 5). AF: Acidic fraction; BF: Basic fraction; NF: Neutral

559

fraction. All the results are expressed as the average values related to 5 different asphalt cements

560

(described in section 2.3).

ACS Paragon Plus Environment

23

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48

561

Page 24 of 28

Table 1. Total sulfur distribution regarding acidic, basic and neutral compounds in asphalt fractions (maltenes and asphaltenes) Sulfur distribution (%) a

Sample Acidic compounds b

Basic compounds c

Neutral compounds d

Asphaltenes

Maltenes

Asphaltenes

Maltenes

Asphaltenes

Maltenes

A1

14.6

6.6

22.1

5.1

63.3

88.3

A2

10.8

24.1

14.5

22.4

74.7

53.5

A3

12.3

13.9

15.8

24.6

71.9

61.5

A4

23.5

15.7

24.1

20.5

52.4

63.8

A5

17.9

26.6

33.0

30.4

49.1

43.0

562

a

Mean values (n=3); b RSD (Relative standard deviation; n=3): 21.8−28.3%; c RSD (Relative standard deviation; n=3): 25.0−31.0%;

563

d

RSD (Relative standard deviation; n=3): 18.9−30.8%

564

24 ACS Paragon Plus Environment

Page 25 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48

Energy & Fuels

565

Table 2. Characterization of virgin and aged asphaltic cements regarding the content of total sulfur, reactivity index (Ir) and asphaltenes.

566

Sample

Total S (%) a

567

Ir

Asphaltene content (%)

Virgin asphalt

Aged asphalt b

Virgin asphalt

Aged asphalt b

568

A1

2.2

0.32

2.23

8.6

11.6

569

A2

3.4

0.56

2.09

10.2

12.7

570

A3

3.1

0.50

1.46

11.0

13.8

571

A4

1.8

0.72

1.27

14.5

15.0

572

A5

3.1

1.18

1.72

13.4

13.5

573

a

RSD (Relative standard deviation; n=3): 8.0−15.0%

574

b

Asphalt cements aged by RTFOT+SUNTEST methods

25 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48

Page 26 of 28

575 576 577

Figure 1

578

579 580

26 ACS Paragon Plus Environment

Page 27 of 28

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48

Energy & Fuels

581 582 583

Figure 2

584

585 586 587

27 ACS Paragon Plus Environment

Energy & Fuels

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48

Page 28 of 28

588 589 590 591

Figure 3

592

593

28 ACS Paragon Plus Environment