A Nanopipette-based SERS Aptasensor for ... - ACS Publications

in cell silent region provided a versatile detection. 77 platform for single cell .... dissolved in 0.2 M NaOH) for 1 h at room temperature under cons...
0 downloads 0 Views 960KB Size
Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

A Nanopipette-based SERS Aptasensor for Subcellular Localization of Cancer Biomarker in Single Cells Sumaira Hanif, Hai-Ling Liu, Saud Asif Ahmed, Jin-Mei Yang, Yue Zhou, Jie Pang, Lina Ji, Xing-Hua Xia, and Kang Wang Anal. Chem., Just Accepted Manuscript • DOI: 10.1021/acs.analchem.7b02147 • Publication Date (Web): 21 Aug 2017 Downloaded from http://pubs.acs.org on August 22, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Analytical Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

1

A Nanopipette-based SERS Aptasensor for Subcellular

2

Localization of Cancer Biomarker in Single Cells

3

Sumaira Hanifa, Hai-Ling Liua, Saud Asif Ahmeda, Jin-Mei Yanga, Yue Zhoua, Jie Panga, Li-Na

4

Jib*, Xing-Hua Xiaa and Kang Wanga*

5

a: State Key Laboratory of Analytical Chemistry for Life Science, School of Chemistry and

6

Chemical Engineering, Nanjing University, Nanjing 210023, China.

7

b: State Key Laboratory of Pharmaceutical Biotechnology, School of Life Sciences, Nanjing

8

University, Nanjing 210023, China;

9

*Corresponding author: [email protected]; [email protected]

1 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

10

Abstract: Single cell analysis is essential for understanding the heterogeneity, behaviors of

11

cells, and diversity of target analyte in different subcellular regions. Nucleolin (NCL) is a

12

multifunctional protein that is markedly overexpressed in most of the cancers cells. The variant

13

expression levels of NCL in subcellular regions have marked influence on cancer proliferation

14

and treatments. However, the specificity of available methods to identify the cancer biomarkers

15

is limited because of the high level of subcellular matrix effect. Herein, we proposed a novel

16

technique to increase both the molecular and spectral specificity of cancer diagnosis by using

17

aptamers affinity based portable nanopipette with distinctive surface-enhanced Raman scattering

18

(SERS) activities. The aptamers-functionalized gold-coated nanopipette was used to capture

19

target, while p-mercaptobenzonitrile (MBN) and complementary DNA modified Ag

20

nanoparticles (AgNPs) worked as Raman reporter to produce SERS signal. The SERS signal of

21

Raman nanotag was lost upon NCL capturing via modified DNA aptamers on nanoprobe, which

22

further helped to verify the specificity of nanoprobe. For proof of concept, NCL protein was

23

specifically extracted from different cell lines by aptamers modified SERS active nanoprobe.

24

The nanoprobes manifested specifically good affinity for NCL with a dissociation constant Kd of

25

36 nM and provided a 1000-fold higher specificity against other competing proteins.

26

Furthermore, the Raman reporter moiety has vibrational frequency in the spectroscopically silent

27

region (1800-2300 cm-1) with a negligible matrix effect from cell analysis. The subcellular

28

localization and spatial distribution of NCL were successfully achieved in various types of cells

29

including MCF-7A, HeLa and MCF-10A cells. This type of probing technique for single cell

30

analysis could lead to develop a new perspective in cancer diagnosis and treatment at cellular

31

level.

2 ACS Paragon Plus Environment

Page 2 of 31

Page 3 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

32

Keywords: Aptasensor, nanopipette, nucleolin, SERS signal on/off, single cells, spatial

33

distribution

34

Single cell analysis is essential for unveiling the heterogeneity, behaviors of cells, and diversity

35

of target analyte localizations.1,2 The single cell heterogeneity dictates a multitude of functions

36

that could be helpful to investigate the development of disease states (prognosis and proliferation)

37

and get information of carcinogenic transformations.3-5 A number of different methods have been

38

developed for single cells analysis, including capillary electrophoresis (CE),6,7 mass

39

spectrometry,8, flow cytometry,9 and laser induced fluorescence (LIF)10,11 based assays. Besides

40

these well-developed techniques, a huge space is available due to some unsolved problems in

41

cancer diagnostics at cellular level.12-14

42

Surface-enhanced Raman scattering (SERS) has emerged as an appealing potential

43

detection tool for cell study due to its unprecedented optical properties.15 As well characterized

44

SERS substrates, metal nanoparticles16-18 undergo indocile aggregation in cells19,20 and usually

45

interferes with original SERS signal21. To overcome this issue, SERS substrates with fixed

46

configuration have been used, such as carbon nanopipettes, optical fibers and SERS-active glass

47

nanopipettes.

48

biomarkers in the single living cells.23 However, to the best of our knowledge, biocompatible and

49

portable aptamers based SERS nanoprobes have not been explored yet for subcellular

50

localization of biological targets in single cells.

22

Recently, SERS-active glass pipette has been successfully applied for probing

51

As a multifunctional protein associated with numerous biomolecules (DNA, RNA, and

52

other small molecules), nucleolin (NCL) plays an essential role in cell division.24 NCL is

53

localized at various parts of the cells including nucleus, cytoplasm and cell membrane with the

3 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 31

54

characteristic functionalities.25 More importantly, the altered expression levels of subcellular

55

NCL are found to be closely related to various types of cancers,26 including colorectal cancer,27

56

human breast and lung cancer cells.28 Usually, an immunofluorescence assay is used to examine

57

the various localization of NCL in cells.29 However, immunofluorescence technique can hardly

58

examine the spatial distribution of NCL at single cell level. Previously, a SERS-based analysis

59

was reported via a DNA barcode-assay for NCL detection at the cells surface while its

60

fabrication steps were complicated and it was not applicable for subcellular distribution.

61

Therefore, it is highly desirable to develop an alternative and non-invasive method for detecting

62

and mapping the expression of NCL at subcellular level.

30

63

To detect and inhibit the proliferation of cancer cells, several efforts have been put to

64

develop NCL binding molecules, such as aptamers (AS1411) and peptides.31-33 AS1411 is a 26-

65

mer G-rich DNA Aptamer, which is highly stable against nucleases.34,35 Herein, we developed a

66

simple SERS-based nanoprobe for subcellular localization of NCL in a single living cell via

67

aptamers based affinity. SERS-active glass nanopipette was functionalized with AS1411 then

68

hybridized with versatile Raman reporter and cDNA modified Ag nanotags for the recognization

69

of NCL. The principle and procedure of aptamers affinity SERS assay are illustrated in Scheme 1.

70

The thin layer of gold film coated on glass nanopipette with ~200 nm outer diameter was used as

71

based substrate, while thiolated NCL aptamers were modified on the surface of Au-coated

72

nanopipette. Meanwhile, Raman nanotags prepared by immobilizing thiolated complementary

73

DNA (cDNA) of AS1411 and MBN as Raman reporter on 55±5 nm AgNPs were used for the

74

detection. The developed SERS nanoprobe detection is relied on the SERS signal-off response of

75

MBN on the exposure of target molecule due to release of Raman nanotags from hybridized

76

SERS-active nanopipette. The bi-metallic nature of Au and Ag plasmon and MBN as Raman

4 ACS Paragon Plus Environment

Page 5 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

77

reporter with characteristic peak (2223 cm-1) in cell silent region provided a versatile detection

78

platform for single cell analysis. For proof of concept, the SERS nanoprobe was precisely

79

inserted into nucleus, cytoplasm and near cell surface in different living cell lines (MCF-7, MCF-

80

10A and HeLa cells). The nanoprobe exhibits astonishing results for subcellular localized study

81

and spatial distribution of biomarker in single cells. Thus, the burgeoning field of SERS active

82

nanopipettes can be further explored by applying various aptamer-affinity approaches for single

83

living cell study.

84 85

EXPERIMENTAL SECTION

86

Reagents and materials. Oligonucleotides used in the present study were purchased from

87

Shanghai

88

(China), and the sequences are given below:

89

Nucleolin Aptamer (AS1411):

90

5`-(CH2)6-S-S-(CH2)6-GGTGGTGGTGGTTGTGGTGGTGGTGG-3`

91

Complementary ssDNA:

92

3`-(CH2)6-S-S-(CH2)6-CCACCACCACCAACACCACCACCACC-5`

93

4-mercaptobenzonitrile (MBN, 95%) was purchased from Nanjing Norris Pharm Technology Co.

94

Ltd. Bovine serum albumin (BSA), horseradish peroxidase (HRP), β-Casein (β-Cas),

95

cytochrome-c (Cyt-c), transferrin (Trf), TE buffer (100-X, pH 7.4) and nucleolin (NCL) from

96

calf intestinal mucosa were all from Sigma-Aldrich (St. Louis, MO, USA). Hydrogen

97

tetrachloroaurate trihydrate (HAuCl4 3H2O, 99.9%) was purchased from Alfa-Aesar (Shanghai

98

China). Silver nitrate (AgNO3), Triton-X 100, trisodium citrate, NaOH, NaH2PO4, Na2HPO4,

99

glucose, potassium bicarbonate (KHCO3), NaOH, HCl (36%), NaCl, KCl, MgCl2, CaCl2,

Sangon

Biological

Engineering

Technology

5 ACS Paragon Plus Environment

&

Services

Co.,

Ltd.

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

100

KH2PO4, K2HPO4, EDTA, glycerol and anhydrous ethanol of analytical grade were purchased

101

from the Nanjing reagent company. All these reagents were used without further purification.

102

Water was purified with a Milli-Q Advantage A10 (Millipore, Milford, MA, USA), and was used

103

to prepare all solutions. Borosilicate glass capillaries with filament (0.58 mm I.D., 1.0 mm O.D.)

104

were purchased from Sutter Instrument Co.

105

Instrumentation. CO2-laser-based pipet puller (P-2000, Sutter Instrument Co.) was used to

106

fabricate the glass nanopipettes. Scanning electron microscopic (SEM) characterization was

107

carried out on a FE-SEM S-4800 system (Hitachi, Tokyo, Japan). Transmission electron

108

microscopy (TEM) characterization was performed on a JEM-1011 system (JEOL, Tokyo,

109

Japan). Raman and SERS experiments were conducted on a Renishaw InVia Reflex confocal

110

microscope (Renishaw, UK) equipped with a high-resolution grating with 1800 grooves/cm,

111

additional band-pass filter optics, and a CCD camera. All measurements were carried out using a

112

He-Ne laser (λ = 633 nm; laser power at spot, 1 mW; excitation laser line: 1s integration time

113

and 1 accumulation). The laser was focused onto the sample by using a ×50 objective lenses with

114

(N.A. 0.75), providing a spatial resolution of 1 µm. Wavelength calibration was performed by

115

measuring silicon wafers through a ×50 objective, assessing the first-order phonon band of

116

silicon (Si) at 520 cm-1. The spectra were recorded using the Renishaw's WiRE (Windows-based

117

Raman Environment) software and analyzed with Origin Pro 8.6 software. Each spectrum

118

baseline was corrected except noise test. A three-dimensional manipulator equipped on an

119

inverted microscope (Nikon Ti-E) was used to precisely insert extraction microprobes into single

120

cells under investigation.

121 122

Preparation of Raman nanotags

6 ACS Paragon Plus Environment

Page 6 of 31

Page 7 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

123

Synthesis of silver nanoparticles. Silver nanoparticles (AgNPs) with a diameter of 55±5 nm

124

were prepared according to a method by Lee and Meisel.36 In brief, AgNO3 (36 mg) was

125

dissolved in 200 mL water and brought to boil under continuous stirring. Then, 4 mL of 1% (w/v)

126

trisodium citrate was added. The mixture was boiled with stirring for about 1 h and then cooled

127

down to room temperature naturally. The solution was stored at 4 °C in refrigerator for further

128

use.

129 130

Immobilization of cDNA and Raman reporter on AgNPs. The cDNA of NCL aptamers and

131

Raman reporter was immobilized on AgNPs by using following procedure.26 10 µL of 100 µM

132

cDNA of aptamer(3’-thiol) were added to freshly prepared AgNPs (1 mL), and incubated at 4 °C

133

for 6 h. The obtained solution was centrifuged for 10 min at 10,000 rpm to remove the excess

134

reagents, the precipitate was washed and centrifuged repeatedly for three times. The resulting

135

cDNA-Ag nanoprobe was dispersed into 1 mL phosphate buffer solution (PBS, 0.01 M, pH 7.4).

136

To modify Raman reporter, 1mL cDNA-AgNPs were incubated with 1 µL of MBN (1 mM

137

dissolved in 0.2 M NaOH) for 1 h at room temperature under constant stirring. Then cDNA-

138

AgNPs were washed with 0.01 M PBS (pH 7.4) three times by centrifugation and re-suspended

139

in 1 mL PBS (pH 7.4) , stored at 4 °C for further use.

140 141

Fabrication of SERS nanoprobe

142

Fabrication of glass nanopipette. Borosilicate glass without filament (0.58 mm I.D., 1.0 mm

143

O.D., Sutter Instrument Co.) was fabricated by a CO2-laser-based pipette puller (P-2000, Sutter

144

Instrument Co.).

145

7 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

146

Preparation of Au coated nanoprobe. For the preparation of Au-coated nanopipette, a gold

147

layer was coated onto the surface of glass nanopipette by a previously reported chemo-deposition

148

method.37 Briefly, the nanopipettes (200 nm O.D.) were immersed in a solution containing 12

149

mM HAuCl4, 0.5 M KHCO3 and 25 mM glucose for 3-4 h at 45 °C until a clear gold layer

150

formed on the surface of each nanopipette. After washing with water and anhydrous ethanol 2-3

151

min for each, the Au-coated nanoprobes dried in air at room temperature.

152 153

Immobilization of aptamers on Au-nanoprobe. The aptamers modification on nanoprobe was

154

performed by immersing in 50 µL of 100 µM 5’-thiol aptamer in 0.01 M PBS and incubated at

155

4 °C in dark for 5 h. Then, excess reagent was removed by washing with 0.01 M PBS (pH 7.4)

156

for 2 min. The resulting aptamer-modified nanoprobes were stored in refrigerator at 4 °C for

157

further use.

158 159

NCL detection assay in solution

160

Hybridization of Raman nanotag on SERS nanoprobe. Au nanoprobes modified with

161

aptamers were immersed in 50 µL of Raman nanotag solution and incubated at room temperature

162

for 1 h. Then non-hybridized Raman nanotags were removed by washing with PBS (pH 7.4) for

163

2 min and air dried before Raman measurement.

164 165

Hybridized SERS nanoprobe for NCL detection. NCL was dissolved in protein binding buffer

166

(PBB) to at a concentration of 0.1 µM. PBB was prepared by adding 140 mM NaCl, 5 mM KCl,

167

1 mM MgCl2 and 1 mM CaCl2 in 1× TE Buffer (pH 7). The as prepared SERS nanoprobe was

8 ACS Paragon Plus Environment

Page 8 of 31

Page 9 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

168

immersed in NCL solution for 5 min at room temperature then washed with PBB and air dried

169

before Raman analysis.

170 171

Selectivity test. The selectivity of the SERS-nanoprobe was investigated against different

172

proteins including BSA, Trf, HRP, Cyt-c and β-casein. The SERS nanoprobes were incubated in

173

1 nM NCL or 1 µM interferants in PBB (pH 7) for 5 min each. Then nanoprobes were washed

174

with PBB (pH 7) for 2 min, dried at room temperature and detected by the Raman.

175 176

Cellular analysis

177

Cell culture. NCL-positive MCF-7, normal MCF-10A, HeLa cells were purchased from the Cell

178

Bank of Type Culture Collection of Chinese Academy of Sciences (Shanghai). The cells were

179

cultured in DMEM (Gibco) media containing 10% fetal bovine serum (Gibco), 100 mg/mL

180

streptomycin and 100 U/mL penicillin at 37 °C for 48 h under 5% CO2. Finally, cell culture

181

media were removed and the cells lingered on the cell culture dishes were washed with 1× PBS

182

buffer for three times then kept in 1× PBS buffer for further use.

183 184

SERS nanoprobe for single cells analysis. With the help of an inverted microscope (Nikon Ti-

185

E equipped with a three-dimensional manipulator), the nanoprobe was inserted into single cells

186

anchored on the bottom of a petri dish. The nanoprobe was precisely localized at different

187

regions (nucleus, cytoplasm and cell surface) of single cells under microscopy and kept still for 5

188

min for each measurement. Meanwhile, the cells were kept in 1× PBS at room temperature for all

189

measurements. After NCL extraction from each region of cells, the nanoprobes were washed

190

with 1× PBS for 2 min to remove unwanted matrix from the nanoprobe, then dried at room

9 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 31

191

temperature and measured for SERS signals. For spatial distribution study, the nanoprobe was

192

kept horizontal when it approached the nucleus of single cells by passing the cytoplasmic region.

193

Then the nanoprobe was washed with 1× PBS for 2 min after extraction, dried and measured for

194

SERS signals. All the experiments were repeated in triplicates to confirm the results. Meanwhile,

195

blank as negative control experiment was also conducted before each analysis.

196 197 198

RESULTS AND DISCUSSION

199

Characterization of the SERS nanoprobe and Raman nanotags. In this study, a smooth and

200

uniform gold layer on was coated the surface of glass nanopipettes in order to generate

201

plasmonic effect. The combination of bimetallic nanostructures (i.e. Au film and AgNPs) to

202

generate an enhanced plasmon has gained more interest in SERS based detection materials

203

because of its unique plasmon coupling effect and other physiochemical properties.38 With an

204

outer diameter of ~250 nm and a taper angle of 33˚, the Au coated glass nanopipette is sharp

205

enough to penetrate into the nucleus of a living cell. The SEM images of SERS nanoprobe before

206

and after its hybridization with Raman nanotag are shown in Figure 1A and 1B. For the

207

synthesis of Raman nanotags, AgNPs with an average diameter of 55±5 nm were prepared

208

(Figure S1A). The AgNPs were modified with MBN as Raman reporter and thiolated aptamers

209

complementary DNA as binding receptors for Raman nanotags. TEM images in Figure S1B and

210

S1C showed that the AgNPs retained its shape and dispersity before and after the modification

211

with MBN and cDNA. The localized surface plasmon resonance (LSPR) characterization of

212

MBN and cDNA modified AgNPs showed no apparent shifts in the LSPR spectrum, suggesting

213

that the modified AgNPs were well dispersed (Figure S2).

10 ACS Paragon Plus Environment

Page 11 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

214

The optical response of hybridized SERS nanoprobe against NCL is also presented by the

215

SEM images in Figure S3. The SERS response of aptamers modified Au-coated nanoprobe is

216

shown in Figure S4, which represents many characteristic peaks in DNA fingerprint region while

217

no peaks at cell silent region (highlighted in grey). The detailed characteristic peaks with

218

assigned vibrations are listed in Table S1. The sharp peak at 2223 cm-1 is assigned to

219

characteristic vibration of cyanide ν(-C≡N) functional group of MBN, and is selected for further

220

experimental characterizations. The MBN is a robust Raman reporter molecule for cell based

221

study due to its simple structure and sharp Raman peak at cell silent region (~2223 cm-1).39,40

222

The SERS response of Raman nanotags before and after modification is given in Figure S5,

223

which indicates a sharp and clear peak at 2223 cm-1 while the other cDNA characteristic peak

224

was overcome by MBN peaks in DNA fingerprint region.

225

The incubation time and concentration of thiolated aptamers and cDNA were optimized

226

before analysis. The 5’ labeled DNA sequences (MB labeled aptamers and alkyne labeled cDNA)

227

were used to optimize DNA concentrations on the surface of Au coated glass nanopipette and

228

AgNPs, respectively. The SERS response at peak 1623 cm-1 of MB labeled aptamers modified

229

nanoprobe is shown in Figure S6A with other characteristic peaks given in Table S1. The

230

optimized concentration and incubation time for aptamers modification on Au nanoprobe were

231

100 µM and 5 h, respectively (Figures S6B). Similarly, the alkyne tagged cDNA gave a

232

characteristic peak at 2010 cm-1 that was taken as a reference peak for optimization (Figure S7A).

233

The optimized concentration and incubation time for cDNA modification on AgNPs were 100

234

µM and 6h, respectively (Figures S7B). Meanwhile, the previously optimized concentration and

235

the maximum incubation time of MBN modification on metal surface were 1 mM and 1 h to get

236

a maximum saturation point.39 It is important to note that a consistent increase in SERS

11 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

237

intensities is observed with gradually increasing incubation time for the DNA sequences

238

modifications even for lower concentrations (10 and 50 µM for aptamers and cDNA). However,

239

higher concentrations have been chosen in order to get maximum Raman signal of modified

240

DNAs on the plasmonic surfaces of Au nanoprobe and Ag nanotag.

Page 12 of 31

241 242

NCL detection. The aptamer modified SERS nanoprobe was incubated with Raman nanotags to

243

form hybridization complex between complementary DNA sequences. This interaction between

244

Au surfaces of nanoprobe with MBN-attached Raman nanotags resulted in the amplification of

245

SERS signal at peak position of 2223 cm-1. The amplified signal within the hot spots of Au

246

nanoprobe and Raman nanotags was specifically lost if target protein NCL was present in the

247

solution as shown in Figure 1C. The binding tendency of modified aptamers towards the target

248

NCL was much higher as compared to complementary sequence hybridization.41 As shown in

249

Figure S8, the complete SERS spectra including DNA and protein fingerprint regions manifest

250

the alterations in characteristic peaks region of DNA after capturing protein. The reaction time of

251

SERS nanoprobe for NCL detection was also optimized to be 5 min (Figure S9). Similar

252

response of modified aptamers towards NCL was also observed in previous reports,42 indicating

253

that the binding efficiency of SERS nanoprobe modified aptamers for the target molecule can be

254

utilized for single cell analysis. Furthermore, SERS mapping image in Figure S10 indicates the

255

even distribution of Raman nanotags after hybridization on SERS nanoprobe. Therefore the

256

fabricated nanoprobe has the ability to provide quantitative information about the target analyte

257

(NCL) within complex biological samples.

258

12 ACS Paragon Plus Environment

Page 13 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

259

Binding affinity of SERS nanoprobe. The binding affinity of SERS nanoprobe in vitro was

260

determined by using increasing concentrations of NCL (0.5 to 500 nM). As shown in Figure 2A,

261

the SERS signal of MBN gradually decreased with the increasing concentration of NCL. Figure

262

2B showed that the decrease in SERS intensity at peak 2223 cm-1 became almost static when

263

NCL concentration was above 100 nM, suggesting the NCL capturing by SERS nanoprobe might

264

reach to saturation. The plot of SERS intensity at 2223 cm-1 against varying concentration of

265

NCL showed a significant binding affinity with an apparent Kd of 36 nM (the detailed is shown

266

in supporting information). The experimentally calculated limit of detection by using standard

267

deviation formula (S/N>3) was 0.8 nM for in vitro NCL with a linear range of 1-50 nM (inset of

268

Figure 2B), which was comparable to the previous report.42 Such a good binding affinity ensures

269

the formation of a stable complex between aptamers and NCL with significant detection limit to

270

release the hybridized Raman nanotags into the solution.43

271 272

Selectivity of the SERS nanoprobe. The selectivity of SERS nanoprobe was checked against a

273

variety of interfering proteins such as BSA, HRP, β-Cas, Cyt-C and Trf. As shown in Figure 3,

274

the SERS nanoprobe exhibited excellent specificity against the interfering proteins because no

275

SERS signal variation was observed for them as compared to blank. Even though the

276

concentration of interfering proteins was 1000-fold higher than that of NCL (especially for β-Cas

277

being phosphoprotein similar to NCL), the interfering proteins showed no or minimal SERS

278

response. Thus, the SERS nanoprobes are highly selective for the target molecule due to

279

aptamers based affinity.

280

13 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

281

Reproducibility of SERS nanoprobe. The SERS signal reproducibility of the SERS nanoprobe

282

was determined in terms of the coefficient of variation for hybridized nanoprobes before and

283

after NCL capturing. The SERS responses of 10 different Au nanoprobes were measured for

284

peak position at 2223 cm-1 before and after NCL detection (Figure S11). The relative standard

285

deviation (RSD) value of 8.6% manifested the good reproducibility of fabricated SERS-based

286

detection approach on Au coated glass nanopipette to work in sample with nanoliter volume.

Page 14 of 31

287 288

Subcellular localization and spatial distribution of NCL in single cells. To understand the

289

subcellular detection and spatial distribution of NCL, SERS nanoprobe was precisely inserted

290

within single cancer cells (MCF-7 and HeLa) and normal (MCF-10A) cells. For the subcellular

291

localizations of NCL, different SERS nanoprobes were individually inserted in perpendicular

292

way to the various cellular compartments as in nucleus, cytoplasm and kept near inner cell

293

membrane for 5 min at each region as shown in Figure 4A. The SERS spectra in Figure S12

294

depicted that the overexpressed NCL levels in cancer cells led to a tremendous decrease in SERS

295

signal of MBN at peak 2223 cm-1 in all regions including cytoplasm and cell surface. Meanwhile,

296

no significant decrease in SERS signal was observed in cytoplasmic and cell surface regions of

297

normal MCF-10A cells. Interestingly, due to the occurrence of SERS signal of MBN within

298

silent region of cell, negligible cell matrix effect and no SERS spectral overlapping were

299

observed as compared to blank. To further investigate the semi-quantitative analysis, percentage

300

loss in SERS spectra intensity was observed for NCL localization in different cell lines (Figure

301

4B). For instance, blank nanoprobes has 100% SERS signal and after NCL capturing the

302

intensity dropped to 11.2%, 12.5% and 12% in nucleus, cytoplasm and cell surface of MCF-7

303

cancer cell, respectively. For HeLa cells, the SERS intensity dropped to 11.8%, 34.6% and 47%

14 ACS Paragon Plus Environment

Page 15 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

304

for nucleus, cytoplasm and cell surface regions, respectively. Conversely, for normal cell (MCF-

305

10A) the drop of SERS intensity was not consistent in all regions. The SERS intensity of MCF-

306

10A dropped to 12.2% in nucleus, which is the native synthetic region for NCL in all normal

307

cells. The relatively higher percentage loss of SERS signal in cytoplasmic and cell surface

308

regions of cancer cells also verified the overexpressed level of NCL in these regions.

309

Furthermore, the expression levels of NCL in cancer and normal cells were also detected in

310

cytoplasmic and nuclear extracts of these cell lines (Figure S13). Figure S14 showed a low

311

degree of relative SERS intensity variations among different cellular regions, indicating that

312

NCL was homogenously distributed in cellular extracts and excessive free NCL molecules were

313

available for capturing. All these results for the subcellular detection of NCL and variation

314

within different cancer lines are in well agreement with previously published reports.44 Besides,

315

the spatial distribution of NCL on single nanoprobe was also investigated by inserting the Au

316

nanoprobe horizontally passing by the cytoplasm towards the nucleus of cell. After extraction the

317

SERS spectra were collected by starting from nucleus (N) inserted region towards the cell

318

surface (S) region of the nanoprobes with the total available surface area of 7-8 µm for Raman

319

measurements, and the schematic presentation is given in Figure S15. SERS spectral response in

320

Figure 5A showed a uniform distribution of SERS signal of MBN at peak position 2223 cm-1

321

before extraction of any NCL from the cells. The corresponding SERS spectra in Figure 5B, 5C

322

and 5D showed that the NCL was not evenly distributed in MCF-7 MCF-10A and HeLa cells.

323

Furthermore, the spatial distribution of NCL in various cell lines was also monitored via SERS

324

mapping technique as shown in Figure S16. Therefore, we can extract molecular information

325

about heterogeneously overexpressed NCL levels among different types of cancer cell lines (as

326

HeLa and MCF-7 are used in current study) which is highly important in cancer diagnosis.45

15 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 31

327

Hence, the SERS nanoprobes have the tendency to distinguish the subcellular NCL levels and

328

also can be implied for study of spatial distribution of any cancer biomarker with high precision

329

in individual cells. Moreover, our proposed approach with some alteration (cDNA modified

330

nanopipette and hybridization with aptamers attached nanoparticles) could be further useful to

331

develop an extended drug delivery setup or cancer therapy platform for localized region in

332

cancer cells. Such a simple, specific and sensitive probing strategy of cancer cells will also be

333

helpful for accessing biomolecular information at cellular level by merging it to in-situ SERS

334

detection platform.

335 336

Conclusion

337

In conclusion, we proposed a novel design of the SERS nanoprobe for cancer biomarker

338

detection at a subcellular level. The fabricated SERS nanoprobe has provided several beneficial

339

properties. First, the Raman reporter labeled AgNPs can aggregate on Au nanotip, and provide

340

significantly enhanced and reproducible SERS signal, which is selectively lost in the presence of

341

target. Second, the characteristic peak of MBN at 2223 cm-1 in the Raman silent region (cell and

342

other biomolecules) enables to detect the distribution of biomarker in single cells and reflect the

343

physiological and pathological states of the cancer cells. Third, the recognition nanoprobe

344

contains aptamers that can be easily replaced by the other types of aptamers to develop diverse

345

ranges of detecting platforms for different biological targets. Lastly, the design of fabricated

346

detection nanoprobe is highly flexible to be converted into the cancer treatment therapy setup

347

with a little variation, as our future perspective. Particularly, the successful detection of NCL at

348

subcellular level along the spatial distribution for the first time may provide a potential approach

16 ACS Paragon Plus Environment

Page 17 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

349

for detection of other proteins at low expression level in a single living cell and opens a new

350

horizon for cancer cell research.

351

17 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 31

352

ASSOCIATED CONTENT

353

Supporting Information

354

The Supporting Information is available free of charge on the ACS Publications website.

355

Synthesis routes, additional optimization, additional characterization and additional validation

356

are provided in the supporting information.

357 358

AUTHOR INFORMATION

359

* Corresponding Author: [email protected], [email protected]

360

Tel.: +86-25-89687436

361 362

ACKNOWLEDGEMENTS

363

This work was supported by the grants from the National Natural Science Foundation of China

364

(21575059 and 21627806) and the National Science Fund for Creative Research Groups

365

(21121091).

18 ACS Paragon Plus Environment

Page 19 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

366

REFERENCES

367

1 Schubert, C. Nature 2011, 480, 133-137.

368

2 Altschuler, S. J.; Wu, L. F. Cell 2010, 141, 559-563.

369

3 Chen, X.; Love, J. C.; Navin, N. E.; Pachter, L.; Stubbington, M. J.; Svensson, V.; Sweedler,

370

J. V.; Teichmann, S. A. Nat. Biotechnol. 2016, 34, 1111-1118.

371

4 Rubakhin, S. S.; Romanova, E. V.; Nemes, P.; Sweedler, J. V. Nat. Methods 2011, 8, 20-29.

372

5 Huang, B.; Wu, H.; Bhaya, D.; Grossman, A.; Granier, S.; Kobilka, B. K.; Zare, R. N.

373

Science 2007, 315, 81-84.

374

6 Xue, Q.; Yeung, E. S. Anal. Chem. 1994, 66, 1175-1178.

375

7 Valaskovic, G. A.; Kelleher, N. L.; McLafferty, F. W. Science 1996, 273, 1199-1202.

376

8 Rubakhin, S. S.; Sweedler, J. V. Nat. Protoc. 2007, 2, 1987-1997.

377

9 Irish, J. M.; Hovland, R.; Krutzik, P. O.; Perez, O. D.; Bruserud, Ø.; Gjertsen, B. T.; Nolan,

378

G. P. Cell 2004, 118, 217-228.

379

10 Cai, L.; Friedman, N.; Xie, X. S. Nature 2006, 440, 358-362.

380

11 Yu, J.; Xiao, J.; Ren, X.; Lao, K.; Xie, X. S. Science 2006, 311, 1600-1603.

381

12 König, K. J. Microsc. 2000, 200, 83-104.

382

13 Zipfel, W. R.; Williams, R. M.; Christie, R.; Nikitin, A. Y.; Hyman, B. T.; Webb, W. W.

383

Proc. Natl. Acad. Sci. U.S.A. 2003, 100, 7075-7080.

384

14 Widengren, J.; Rigler, R. Bioimaging 1996, 4, 149-157.

385

15 Lee, K.; Drachev, V. P.; Irudayaraj, J., ACS Nano 2011, 5, 2109-2117.

386

16 Kneipp, J.; Kneipp, H.; McLaughlin, M.; Brown, D.; Kneipp, K. Nano Lett. 2006, 6, 2225-

387

2231.

19 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

388

17 Kneipp, K.; Haka, A. S.; Kneipp, H.; Badizadegan, K.; Yoshizawa, N.; Boone, C.; Shafer-

389

Peltier, K. E.; Motz, J. T.; Dasari, R. R.; Feld, M. S. Appl. Spectrosc. 2002, 56, 150-154.

Page 20 of 31

390

18 Nabiev, I. R.; Morjani, H.; Manfait, M. J. Eur. Biophys. 1991, 19, 311-316.

391

19 Schatz, G. C. Proc. Natl. Acad. Sci. U.S.A. 2007, 104, 6885-6892.

392

20 Moskovits, M. J. Raman Spectrosc. 2005, 36, 485-496.

393

21 Kickhoefer, V. A.; Han, M.; Raval-Fernandes, S.; Poderycki, M. J.; Moniz, R. J.; Vaccari, D.;

394 395 396 397 398 399 400 401 402 403 404 405 406

Silvestry, M.; Stewart, P. L.; Kelly, K. A.; Rome, L. H., ACS Nano 2008, 3, 27-36. 22 Vitol, E. A.; Orynbayeva, Z.; Friedman, G.; Gogotsi, Y., J. Raman Spectrosc. 2012, 43, 817827. 23 Liu, J.; Yin, D.; Wang, S.; Chen, H. Y.; Liu, Z. Angew. Chem., Int. Ed. 2016, 55, 1321513218 24 Qiu, W.; Zhou, F.; Zhang, Q.; Sun, X.; Shi, X.; Liang, Y.; Wang, X.; Yue, L. APMIS 2013, 121, 919-925. 25 Fähling, M.; Steege, A.; Perlewitz, A.; Nafz, B.; Mrowka, R.; Persson, P. B.; Thiele, B. J. Biochim. Biophys. Acta 2005, 1731, 32-40. 26 Pichiorri, F.; Palmieri, D.; De Luca, L.; Consiglio, J.; You, J.; Rocci, A.; Talabere, T.; Piovan, C.; Lagana, A.; Cascione, L. J. Exp. Med. 2013, 210, 951-968. 27 Shen, N.; Yan, F.; Pang, J.; Wu, L.-C.; Al-Kali, A.; Litzow, M. R.; Liu, S. Oncotarget 2014, 5, 5494-5509.

407

28 Huang, Y.; Cai, D.; Chen, P. Anal. Chem. 2011, 83, 4393-4406.

408

29 Walling, M. A.; Shepard, J. R. Chem. Soc. Rev. 2011, 40, 4049-4076.

409

30 Li, Y.; Qi, X.; Lei, C.; Yue, Q.; Zhang, S. Chem. Commun. 2014, 50, 9907-9909.

20 ACS Paragon Plus Environment

Page 21 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

410 411

Analytical Chemistry

31 Bates, P. J.; Laber, D. A.; Miller, D. M.; Thomas, S. D.; Trent, J. O. Exp. Mol. Pathol. 2009, 86, 151-164.

412

32 Koutsioumpa, M.; Papadimitriou, E. Recent Pat. Anticancer Drug Discov. 2014, 9, 137-152.

413

33 Krust, B.; El Khoury, D.; Nondier, I.; Soundaramourty, C.; Hovanessian, A. G. BMC Cancer

414

2011, 11, 333.

415

34 Gao, H.; Yang, Z.; Zhang, S.; Pang, Z.; Liu, Q.; Jiang, X. Acta Biomater. 2014, 10, 858-867.

416

35 Lee, K. Y.; Kang, H.; Ryu, S. H.; Lee, D. S.; Lee, J. H.; Kim, S. J. Biomed. Biotechnol. 2010,

417

168306.

418

36 Lee, P.; Meisel, D. J. Phy. Chem. 1982, 86, 3391-3395.

419

37 Zhou, F.; Wang, M.; Yuan, L.; Cheng, Z.; Wu, Z.; Chen, H. Analyst 2012, 137, 1779-1784.

420

38 Muhammad, P.; Tu, X.; Liu, J., Wang, Y., Zhen, L. ACS Appl. Mater. Interfaces 2017, 9,

421 422 423 424 425 426 427

12082-12091. 39 Hanif, S.; Liu, H.; Chen, M.; Muhammad, P.; Zhou, Y.; Cao, J.; Ahmed, S. A.; Xu, J.; Xia, X.; Chen, H.; Wang, K., Anal. Chem. 2017, 89, 2522-2530. 40 Kennedy, D. C.; Tay, L. L.; Lyn, R. K; Rouleau, Y.; Hulse, J.; Pezacki, J. P., ACS Nano 2009, 3, 2329-2339. 41 Borghei, Y. S.; Hosseini, M.; Dadmehr, M.; Hosseinkhani, S.; Ganjali, M. R.; Sheikhnejad, R. Anal. Chim. Acta 2016, 904, 92-97.

428

42 Li, Y. R.; Liu, Q.; Hong, Z.; Wang, H. F., Anal. Chem. 2015, 87, 12183-12189.

429

43 Noaparast, Z.; Hosseinimehr, S. J.; Piramoon, M.; Abedi, S. M., J. Drug Targeting 2015, 23,

430 431 432

497-505. 44 Malik, M. T.; O'Toole, M. G.; Casson, L. K.; Thomas, S. D.; Bardi, G. T.; Reyes-Reyes, E. M,; Bates, P., Oncotarget 2015, 6, 22270-22281.

21 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

433 434

45 Tulchin, N.; Chambon, M.; Juan, G.; Dikman, S.; Strauchen, J.; Ornstein, L.; Monteiro, A. N., Am. J. Pathol. 2010, 176, 1203-1214.

22 ACS Paragon Plus Environment

Page 22 of 31

Page 23 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

435

FIGURE CAPTIONS

436

Scheme 1. Schematic illustration of aptamers affinity based SERS nanoprobe for probing NCL

437

in single cells.

438 439

Figure 1. SEM images of aptamers modified Au-nanoprobe before (A) and after hybridization

440

(B) with Raman nanotag. (C) SERS response of hybridized nanoprobe before and after nucleolin

441

(NCL) detection. SERS nanoprobe was incubated in 0.1 µM NCL solution for 5 min at room

442

temperature.

443 444

Figure 2. (A) Concentration-dependent SERS spectra of hybridized nanoprobe for NCL in PBB

445

(pH 7). (B) Plots of SERS intensity at 2223 cm-1 versus different concentrations of NCL. Binding

446

isotherm data was calculated with Hill fitting (R2 = 0.995). Inset graph indicates the linear fitting

447

for different NCL concentrations from 1 to 50 nM with value of R2 = 0.985. Error bars were

448

estimated from three repeated measurements.

449 450

Figure 3. Selectivity of SERS nanoprobe in the presence of different interferants. Bar chart

451

plotted for SERS intensity at 2223 cm-1 versus different proteins and blank (having no protein)

452

under similar conditions. Sample: 100 nM of target NCL protein and 100 µM of other competing

453

proteins dissolved in PBB (pH 7) while blank contain only buffer. Error bars were estimated

454

from three repeated measurements.

455 456

Figure 4. Optical images show the NCL extraction from (A) nucleus, (B) cytoplasm and (C) cell

457

surface of individual cell. The scale bar is 5 µm. (D) SERS intensities at 2223 cm-1 for each

23 ACS Paragon Plus Environment

Analytical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

458

nanoprobe inserted into different cell lines (MCF-7, MCF-10A and HeLa) within different

459

regions of cells (nucleus, cytoplasm and cell surface).

Page 24 of 31

460 461

Figure 5. SERS spectra for spatial distribution of NCL probing in different cell lines. (A) Blank

462

SERS nanoprobe (B) MCF-7 cells (C) MCF-10A cells and (D) HeLa cells. Raman analysis was

463

performed for 7-8 µm region of SERS nanoprobe with a roughly estimated step distance of 1 µm

464

for each measurement, while N and S referred as nucleus and surface regions of the cells,

465

respectively.

466

24 ACS Paragon Plus Environment

Page 25 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

467 468 469 470 471 472 473 474 475 476

Scheme 1

477

Scheme 1

478 479 480 481 482 483 484 485 486 487 488 489

25 ACS Paragon Plus Environment

Analytical Chemistry

490 491 492 493 494 495 496 497 498 499

C

Aptamer modified SERS nanoprobe

1000 counts

Raman nanotags hybridized SERS nanoprobe Hybridized SERS nanoprobe after NCL detection

SERS intensity

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 31

500 2000

2100

2200

2300

501

Raman Shift (cm )

502

Figure 1

-1

503 504 505 506 507 508 509 510 511 512

26 ACS Paragon Plus Environment

2400

Page 27 of 31

513

515

0 nM 0.5 nM 1 nM 10 nM 25 nM 50 nM 100 nM 200 nM 300 nM 400 nM 500 nM

516 517 518

2000

2100

2200

2300

2400

520

6000 4000

Raman Shift (cm )

7695 6840 5985 5130 4275 3420 0

2000

10 20 30 40 50 Conentration of NCL (nM)

Hill Fitting

0 0

-1

519

Sample Blank without NCL

8000

SERS intensity at 2223 cm-1

A

514

B10000 1000 counts

SERS intensity at 2223 cm-1

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

100

200

300

400

Concentration of NCL (nM)

Figure 2

521 522 523 524 525 526 527 528 529 530 531 532 533 534 535

27 ACS Paragon Plus Environment

500

Analytical Chemistry

536 537 538 539 540 541 542

10000 SERS intensity at 2223 cm-1

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

8000 6000 4000 2000 0

NCL Blank BSA HRP β-Cas Cyt-C Trf

543 544

Figure 3

545 546 547 548 549 550 551 552 553 554 555 556 557 558

28 ACS Paragon Plus Environment

Page 28 of 31

Page 29 of 31

559 560 561 562 563 564 565 566 567 568

D12000 SERS intensity at 2223 cm-1

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

Nucleus Cytoplasm Cell Surface

10000 8000 6000 4000 2000 0

569 570

Blank

MCF-10A

MCF-7

Figure 4

571 572 573 574 575 576 577 578 579 580 29 ACS Paragon Plus Environment

HeLa

Analytical Chemistry

581

8000 6000

584

4000 2000

585

5000

B

SERS Intensity

10000

A

583

4000 3000 2000 1000 0

0

S

2000

2100

2200

2300

on / it i

N 2000

2400

2100

2200

2300

Po s

N

587

Po si tio n/ µm

586

µm

S

2400

Raman Shift (cm-1)

Raman Shift (cm-1)

10000

C

8000 6000

590

4000 2000

591

10000

D

SERS Intensity

589

8000 6000 4000 2000 0

0

S

n/ µ t io N

593 2000

594

2100

2200

2300

N 2000

2400

2100

2300

Raman Shift (cm-1)

Raman Shift (cm-1)

595 596

2200

Figure 5

597 598 599 600 601

30 ACS Paragon Plus Environment

2400

Po si tio n/

m

µm

S

592

SERS Intensity

588

SERS Intensity

582

Po si

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 31

Page 31 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Analytical Chemistry

Table of Content

602

603 604

An aptamer modified gold nanopipette was decorated by Raman reporter-covered AgNPs to

605

form a signal-off nanoprobe. The subcellular localization and spatial distribution of NCL were

606

probed in various types of cells

31 ACS Paragon Plus Environment