Antifouling Properties of a Self-Assembling ... - ACS Publications

force microscopy (AFM), and contact angle measurements demonstrated that the block co- polymer self-assembled ... molecule (center to center). Once th...
0 downloads 5 Views 2MB Size
Subscriber access provided by UNIV OF SCIENCES PHILADELPHIA

Biological and Environmental Phenomena at the Interface

Antifouling Properties of a Self-Assembling Glutamic Acid-Lysine Zwitterionic Polymer Surface Coating Christopher Ziemba, Maria Khavkin, Dimitris Priftis, Handan Acar, Jun Mao, Maya Benami, Moshe Gottlieb, Matthew V. Tirrell, Yair Kaufman, and Moshe Herzberg Langmuir, Just Accepted Manuscript • DOI: 10.1021/acs.langmuir.8b00181 • Publication Date (Web): 11 Apr 2018 Downloaded from http://pubs.acs.org on April 12, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 39 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

Antifouling Properties of a Self-Assembling Glutamic Acid-Lysine Zwitterionic Polymer Surface Coating Christopher Ziemba1,2,3, Maria Khavkin1, Dimitris Priftis4, Handan Acar4, Jun Mao4, Maya Benami1, Moshe Gottlieb6, Matthew Tirrell4,5, Yair Kaufman1*, Moshe Herzberg1* 1

The Jacob Blaustein Institutes for Desert Research, Zuckerberg Institute for Water

Research, The Albert Katz International School of Desert Studies, Ben Gurion University of the Negev, Sede Boqer Campus, Midreshet Ben-Gurion, 84990 Israel 2

Current address: Eawag, Swiss Federal Institute of Aquatic Science and Technology,

Überlandstrasse 133, CH-8600 Dübendorf, Switzerland 3

Current address: Institute of Environmental Engineering, ETH Zürich, CH-8093, Zürich,

Switzerland 4

Institute for Molecular Engineering, University of Chicago, Chicago, Illinois 60637, United

States 5

Materials Science Division, Argonne National Laboratory, Argonne, Illinois 60439, United

States 6

Department of Chemical Engineering, Ben Gurion University of the Negev, Beer-Sheva

84105 Israel

Corresponding Authors *E-mail: [email protected], [email protected]

KEYWORDS: biofouling, extracellular polymeric substances, polymer brush, quartz crystal microbalance with dissipation, atomic force microscopy

ACS Paragon Plus Environment

Langmuir 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT There is a need for the development of antifouling materials to resist adsorption of biomacromolecules. Here we describe the preparation of a novel zwitterionic block co-polymer with the potential to prevent or delay the formation of microbial biofilms. The block copolymer comprised of a zwitterionic (hydrophilic) section of alternating glutamic acid (negatively-charged) and lysine (positively-charged) units and a hydrophobic polystyrene section. Cryo-TEM and dynamic-light-scattering (DLS) results showed that on average, the block co-polymer self-assembled into 7 nm diameter micelles in aqueous solutions (0 to 100 mM NaCl, pH 6). Quartz crystal microbalance with dissipation monitoring (QCM-D), atomic force microscopy (AFM), and contact angle measurements demonstrated that the block copolymer self-assembled into a brush-like monolayer on polystyrene surfaces. The brush-like monolayer produced from a 100 mg/L block co-polymer solution exhibited an average distance, d, of approximately 4 - 8 nm between each block co-polymer molecule (center to center). Once the brush-like monolayer self-assembled, it reduced EPS adsorption onto the polystyrene surface by ~70% (mass), reduced the rate of bacterial attachment by >80%, and inhibited the development of thick biofilms. QCM-D results revealed that the EPS molecules penetrate between the chains of the brush and adsorb onto the polystyrene surface. Additionally, AFM analyses showed that the brush-like monolayer prevents the adhesion of large (>d) hydrophilic colloids onto the surface via hydration repulsion; however, molecules or colloids small enough to fit between the brush polymers (