Bond Scission and Bending-Induced Multicolor Switching

Subscriber access provided by University of Newcastle, Australia

Article

A Novel Reversible Mechanochromic Elastomer with High Sensitivity: the Bond Scission and Bending Induced Multi-Color Switching Taisheng Wang, Na Zhang, Jingwen Dai, Zili Li, Wei Bai, and Ruke Bai ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b00176 • Publication Date (Web): 14 Mar 2017 Downloaded from http://pubs.acs.org on March 16, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

A Novel Reversible Mechanochromic Elastomer with High Sensitivity: the Bond Scission and Bending Induced Multi-Color Switching Taisheng Wang,a Na Zhang,a Jingwen Dai,a Zili Li,a Wei Bai*b and Ruke Bai*a a

CAS Key Laboratory of Soft Matter Chemistry, Department of Polymer Science and

Engineering, University of Science and Technology of China, Hefei 230026, P. R. China. b

Department of Chemistry, University of Massachusetts-Amherst, 300 Massachusetts Ave,

Amherst, Massachusetts 01003, United States. KEYWORDS mechanochromic, broad-spectrum, bond scission, bond bending , rhodamine, high sensitivity

ABSTRACT

Although the rational designed mechanochromic polymer (MCP) materials have evoked major interest and experienced significant progress recently, but it is still a great challenge to develop a facile and effective strategy for preparation of reversible broad-spectrum MCP with a combination of wide-range color switch ability and high sensitivity, which thus make it possible to mimic the gorgeous color change as in nature. Herein, we designed and synthesized a novel

ACS Paragon Plus Environment

1


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 31

rhodamine-based mechanochromic elastomer. Our results demonstrated that the elastomer exhibited very promising and unique properties. Three primary-fluorescence colors were presented during continuous uniaxial extension and relaxing process and reversible broadspectrum fluorescence color change could be achieved consequently. The fluorescence quantum yield of the opened zwitterion of this new mechanophore was as high as 0.67. In addition, the elastomer showed very high sensitivity to stress with a detectable activation strain of about 0.24, which was much smaller than those reported in the previous literatures. Meantime, the easy-toget material, facile preparation and good mechanical property also made it suitable for potential practical applications.

INTRODUCTION

The ability of responding to mechanical strain and transducing mechanical stimulus into optical signal is one of the most attractive phenomenon developed by natural evolution.1,2 For example, cephalopod, such as cuttlefish, octopus, and squid, can take advantage of dazzling pattern of colors produced by contracting and releasing the muscles to improve the success rate in hunting and escaping.3,4 Inspired by their natural counterparts, the rational designed mechanochromic polymer (MCP) materials have also evoked major interest and experienced significant progress in recent years.5-11 The growing trend of MCP is believed to be mostly derived from its potential in developing sensing or displaying devices that can be used to measure or monitor the change of stress or strain, thus leading to various of latent applications such as memory chip, security communication and human motion monitoring.12-15 To fully take advantages of the MCP materials, the ability to display broad-spectrum optical signal, optical reversibility and high quantum yield are highly demanded besides general


2

Page 3 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


requirements such as good mechanical properties and weathering resistance. Currently, the most common method to prepare MCP materials is physical doping, in which dyes are generally dispersed in the polymer matrixes.16-20 However, most of these materials possess poor reversibility, thus limiting their applications. On the other hand, the mechanochromic polymers consisting of mechanophores have also been exploited. The conversion is often based on the transfer of mechanical forces along a polymer chain to a responsive unit, the mechanophore, of which the optical properties can be modulated by force-induced bond scission or isomerization of the mechanophores.5,6,8,21-31 Although very promising, these mechanochromic polymers as bio-inspired materials still suffer from some drawbacks. For instance, up to now, most of the mechanochromic polymers reported in literatures only display two colors switching due to their specific mechanistic models, which make them hard to mimic the gorgeous color change as in nature for wider applications. Although the spiropyran motif's merocyanine form has been widely employed as mechanophore in recent years,32-38 which exhibits secondary fluorescence color transition under force. However, besides of the extremely low fluorescence quantum yield of merocyanine form (ϕf < 0.02), which is also known as a crucial disadvantage,39,40 the color gamut produced in those cases was quite narrow. Therefore, it is still a challenging task to develop a facile and effective strategy for preparation of reversible broad-spectrum MCP with a combination of wide-range color switch ability and high sensitivity. In this paper, we work on using rhodamine-based single-mechanophore to develop new broadspectrum MCP elastomer with the ability to display three primary colors, which exhibit broadspectrum color switch ability and high quantum yield. Rhodamine derivates are widely used for chemical or biological sensors since they can be easily transformed from a twisted structure to a planar zwitterion which exhibits high quantum yield.41,42 The well-studied property and easy


3


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 31

accessibility make it an ideal candidate for practical broad-spectrum MCP materials. Nevertheless, the use of rhodamine as mechanophore for creating applicable polymers is still very rare. Notably, recent literature reported by Jia et al. was found that the rhodol fluorophore, a hybrid structure of fluorescein and rhodamine,43-45 could act as both a mechanophore and a photochromic compound when covalently linked in a polyurethane elastomeric matrix.25 However, only two primary fluorescence colors switching were observed for the elastomer under mechanical stimulus. In addition, it was subjected to a disadvantage of low sensitivity that the huge pressure used for activating the mechanophore was destructive to the elastomer, and no color change was found when stretching. Our results demonstrated that the elastomers as mechanochromic material exhibited very promising and unique properties. Firstly, they could exhibit three primary fluorescence colors during continuous uniaxial extension and relaxing process, and hence reversible broad-spectrum fluorescence color change ability could be achieved. The fluorescence quantum yield of the opened zwitterion of the new mechanophore was as high as 0.67. What’s more, high sensitivity to stress was achieved with a detectable activation strain of about 0.24, which was much smaller than those reported in the previous literatures.5,22 To the best of our knowledge, this is a first example of MCP elastomer that can enjoy the combined benefits of broad-spectrum fluorescent color switch ability, reversibility and high sensitivity. Meantime, the easy-to-get material, facile preparation and good mechanical property also make it suitable for potential practical applications.

RESULTS AND DISCUSSION


4

Page 5 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


As an initial step, a novel triacrylic ester of rhodamine (TAR) was designed and synthesized conveniently from commercial available rhodamine 6G. To increase the quantum yield of the ring-open zwitterion, two electron-donating tertiary amino groups were incorparated into the phenyl rings and trihydroxy rhodamine derivative (THR) (Scheme 1) was obtained. Then, TAR as crosslinker for photo-polymerization was prepared through the reaction of THR with acryloyl chloride (Scheme S1). The fluorescence quantum yield of the opened zwitterion of THR was determined to be ϕf = 0.67 which was almost two orders of magnitude higher than that of the widely employed merocyanine.

Scheme 1. Chemical structures of THR and TAR. In order to achieve high sensitivity and strength, we used TAR as the crosslinker to prepare the mechanochromic elastomers through three-step photo-polymerization process (Scheme S3). First, a crosslinked polymer film was obtained by photo-polymerization of ethyl acrylate (EA) and TAR in toluene under irradiation with ultraviolet light. This film was designated as “single network” or as first network (SNx, “x” represented the crosslinker concentration. For example, SN1 was crosslinked at 1.0 mole percent of monomer). Then the rhodamine-derived mechanophores contained SNx was stretched to prompt the sensitivity of the mechanochromic elastomers by swelling with EA, photo-initiator, and a certain amount of butanediol diacrylate (BDA). The double networks (DNx) were obtained by following photo-polymerization. The


5


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 31

triple networks (TNx) with higher level of prestretch were then prepared by repeating the swelling and photo-polymerization procedure. Mechanical properties of the elastomers were tested and the tunable mechanical performance could be achieved to satisfy the specific requirements in wide range of applications. The results in detail are presented in Table 1. By comparing the elastomers with different level of networks, i.e. SN1, DN1, and TN1 (Figure S1), both the elastic modulus and the tensile strength of them were increased in the order of SN1, DN1 and TN1. The modulus and the tensile strength of TN1 were respectively higher by a factor of up to 1.9 and 18.2, compared with that of SN1. These results indicated that the three-step polymerization process was a facile route to enhance the mechanical properties of the elastomer. Moreover, higher content of crosslinker resulted in lower breaking stress and elongation. For example, the TN1 elastomer exhibited a breaking stress of 27.4 MPa and a stretch ratio of 3.2, respectively, which were much larger than that of the TN3 elastomer. A 1% content of crosslinker resulted in the highest prestretch (λprestretch = 2.4) of the first networks in TN1 elastomer, which would greatly facilitate the force-induced isomerization process of the mechanophore when it was stretched (Table S1). DMA and DSC measurements were performed to test the thermal properties of the TNx elastomers. The glass transition temperature (Tg) of the TN1 elastomer was measured to be -18 oC, which was similar to that of polyethyl acrylate reported previously demonstrating its elastic character at room temperature.46 Moreover, a slight increase of Tg was observed when the concentration of TAR was varied from 1% to 3% as the polymer chain mobility would be restricted in higher cross-linking density (Figure S4, S5).


6

Page 7 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Table 1. The mechanical properties of elastomers. Shown are the Young’s modulus E (in MPa), true stress at break (in MPa), and stretch ratio at break (λbreak).

1% crosslinker TAR Sample

2% crosslinkerTAR

3% crosslinkerTAR

T (oC) E

σୠ୰ୣୟ୩ ்

λbreak

E


λbreak

E


λbreak

SN

25

0.9

1.5

2.5

1.5

1.9

1.9

2.1

1.0

1.4

DN

25

1.2

18.5

3.0

1.9

10.1

2.4

2.3

5.3

2.3

TN

25

1.7

27.4

3.2

4.0

27.0

2.9

5.4

8.6

1.5

Since the TN1 elastomer possessed the highest prestretch of the first networks, we qualitatively examined the mechano-responsive properties of it by stretching it with hand. Notably, the elastomer showed a vibrant fluorescent color change from pale blue to red with high contrast during stretching (Figure 1a). The transformation could be also observed by naked eye from colorless to dark-red. This fluorescent and visible color change could be ascribed to the forceinduced isomerization of the rhodamine-mechanophore from closed form to opened zwitterion, which dramatically red-shifted the absorption band and turned on the fluorescence emission. The dependence of fluorescence intensity on the stretch ratio is showed in Figure 1b. The initial TN1 elastomer showed an emission band at 420 nm with a weak blue color which was originated from the closed form of mechanophore (Figure S7). A very weak broad band ranging from 500 to 625 nm was also observed for the initial elastomer as a result of slightly isomerization of the mechanophore. When the stretch ratio continuously increased (Figure 1b), a new band at 600 nm emerged with a red emission. Similar changes were also observed in the absorption spectra. The pristine TN1 elastomer film was transparent without any absorption bands at above 450 nm. However, a broad absorption band at 564 nm appeared when the film was stretched (Figure S8). It was very interesting that the fluorescence color of the film immediately turned from red to


7


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 31

yellow when the stress was released. Actually, both absorption and fluorescence emission spectra were respectively blue-shifted by approximately 28 and 50 nm as soon as the stress was unloaded (Figure 1c, S9). The most important issue was that the fluorescence color change between yellow and red could be repeatedly switched back and forth by cycling stress-loading and stress-unloading, which could be spectroscopically quantified (Figure S10, S11). After unloading the stress, the elastomer could go back to the colorless state at room temperature within 5 hrs automatically (Figure 1d, S12) or 2 min by heating it at 70 oC, and this stretchinduced color change could be repeated over many cycles. What was beyond our expectation was that the TN1 elastomer could also return to the colorless state from the red state in 3 min under irradiation of 340 nm ultraviolet light (100 W) (Figure 1d).

Figure 1. (a) Fluorescent (left) and optical (right) images of manually stretched dumbbell-shaped TN1 elastomer. (b) Normalized FL intensity of TN1 elastomer during continuous extension. (c) Normalized FL intensity of TN1 elastomer under tensional and relax states. (d) Optical images of


8

Page 9 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


TN1 elastomer after unloaded at room temperature and on exposure of UV light (λex = 340 nm). (e) Chromaticity parameters of TN1 elastomer at different stretch ratios, and in relax state. Although the photo-induced transformation of the spirolactam to the open form was reported,47,48 we found that the newly synthesized compound THR was fairly stable under UV irradiation, which was proved by NMR spectroscopy (Figure S13). Figure 1e shows the sequential changes in the chromaticity parameters of the TN1 elastomer. As the stretch ratio increased, the overall chromaticity coordinates of the elastomer shifted from the blue region (x = 0.201, y = 0.165) to the red region. Once the stress was removed, the chromaticity coordinates moved to yellow region (x = 0.337, y = 0.395) immediately. This was a rather interesting and rare phenomenon that force can induce three primary fluorescence color transitions in single mechanophore. Since the three primary fluorescence colors were located in the blue, yellow, and red regions separately, the elastomer could produce rich fluorescence colors by rational tuning the stretch ratio, which was useful for various of purposes that require broad-spectrum colors (see movie S1 in Supporting Information). In order to understand the role of the mechanophores in the elastomers, we also prepared the control composite elastomers by simply doping THR into crosslinked polyethyl acrylate. No visible and fluorescence color change was observed when the composite elastomer was stretched (Figure S14). These results indicated that the force-induced ring-opening reaction of the the spirolactam would occur only when the mechanophore was incorporated in the polymer networks as a linking unit, thus endowing the elastomer with mechanochromic property. To gain more insights into the mechanochromic property of the elastomer, theoretical calculations were performed on the closed and open form of the mechanophore to optimize their molecular geometries (Figure 2a). To reduce computation time, the hydroxyls on the tertiary


9


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 31

amino groups were ignored. To our surprise, the zwitterion of the mechanophore did not adopt a planar conformation. The angle of C1-C2-O was calculated to be 134o. Although the positive charge on the opened zwitterions could be delocalized over the π extended xanthene rings, the negative charge was localized at nitrogen. Therefore, such zwitterions has a large dipole moment DM (DM = q × d) because of the relative long distance between charges which may lead to the formation of this bent geometry. The energy barrier for C-N bond scission reaction was simulated to be 96.2 KJ/mol (Figure S15, S16) which was much lower than the breaking energy for the C-C or C-O bond.49,50 During the continuous uniaxial extension, the stress was transferred to the mechanophores through the crosslinked network of the elastomer. Once the C-N bond of the twisted spirolactam was broken, the torque M (M = F3×d) applied by the polymer chains would lead to the bending of the C1-C2 bond (Figure 2c), which planarized the conformation of the zwitterions. This would facilitate the delocalization of the π electrons in the phenyl ring to that of the xanthene, resulting in red-shifts in both the absorption and fluorescence spectra. When the stress was removed, the zwitterions immediately went back to the bent geometry, leading to an obvious blue shift in fluorescence spectra (Figure 2b). Since the bending energy of C-C bond is around 30 KJ/mol, which is much lower than the breaking energy of C-N bond in spirolactam. As soon as the C-N bond broke, the zwitterion planarized instantaneously. This might explain why the emission band at 600 nm appeared at the early stage of uniaxial stretching. As is well known, the ring-opening reaction of the spirolactam could occur in the presence of acid such as trifluoroacetic acid.47,51 Because the negative charge (CF3COO-) was adjacent to the positive charge in this situation, we speculated that the dipole moment was dramatically decreased, which would planarize the open state. Therefore, in order to further confirm the mechanism of the secondary color transition, the fluorescence spectrum of TN1 elastomer saturated with CF3COOH


10

Page 11 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


gas was studied. It was found that the red fluorescence appeared at 600 nm after the reaction (Figure 2d) indicating that the planar zwitterions were formed in this situation. This result was further confirmed by the simulation data. As shown in Figure S17, the bond angle of C1-C2-O was calculated to be 175o for the zwitterions with trifluoroacetic anion, which was consistent with our hypothesis.

Figure 2. (a) Optimized molecular geometries of closed spirolactam (left) and opened zwitterion (right). (b) Mechanically triggered ring-open reaction and bond bending induced secondary fluorescent color transition. (c) Illustration of the torque M generated by the forces in three directions. The force was assumed to be equally distributed across all three junctions. (d) Fluorescence spectrum of TN1 elastomer saturated with CF3COOH. To determine whether the observed color change was dependent on linking positions or was the result of other factors, we also synthesized two control mechanophores with two crosslinking junctions (Figure 3a, Scheme S2) and then prepared the triple networks elastomers following the same procedures for TN1. These two elastomers were referred to as C-3 and C-6.


11


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 31

Both of the C-3 and C-6 exhibited a weak broad band at 550 nm before mechanical stretching (Figure 3b, 3c). This was because of a slightly isomerization of the mechanophore similar to that of TN1. Since the two cross-linking junctions of cross-linker 6 were located on the xanthenes, the force could not be transferred across the sensitive C-N spiro bond. Indeed, the fluorescent band at 550 nm almost remained the same with increasing stretch ratio (Figure 3c) indicating that the mechanophore was not been activated in C-6 elastomer. Unlike the mechanophore in C-6 elastomer, the cross-linker 3 was linked in a manner that the bond scission reaction was not hindered consequently. We could see an obvious increase in fluorescence band at 550 nm with a red shift of about 8 nm when the C-3 elastomer was stretched continuously (Figure 3b). The red shift in fluorescence was a result of bond bending induced by planarization of the mechanophore, which however was restricted in the cross-linker 3 with two linking junctions. Compared with the TN1 elastomer, the value of red shift for the C-3 elastomer was much smaller, which almost could not be detected by naked eye (see movie S2 in supporting information).


12

Page 13 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 3. (a) Chemical structures of control cross-linkers 3 and 6. Normalized FL intensity of C3 (b) and C-6 (c) elastomer during continuous extension. The insert showed the images of the elastomer before and after mechanical stretching (the stretch ratio was about 2.0). We plot the fluorescence intensity ratio I600/I420 versus λPrestretch to examine the influence of the prestretching level of the first network on the mechanochromic behaviour of the elastomer. Since the fluorescence signal output is ratiometric, this self-referencing two-band comparative method


13


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 31

possesses a great advantage over the other “turn on” MCP materials because of minimizing or eliminating external interference. The onset of detectable activation was defined as λ'. As seen in Figure 4b, in comparison with DN1, TN1 film showed a smaller value of λ' (1.24) and a greater activation under uniaxial deformation. Compared with most of the mechanochromic polymers reported which required high levels of strain to activate, often at the level of 5.0,5,29 the detectable activation strain for TN1 was much smaller. However, in the case of the SN1 film, no activation in fluorescence was found until it was broken into two pieces. These results suggested that high-level prestretching of the first network was crucial for producing high sensitivities in mechanochromic elastomers.


14

Page 15 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 4.The stress and fluorescence intensity ratio of I600/I420 as a function of stretch ratio for DN1 (a) and TN1 (b) elastomer. The TN1 elastomer for finger-motion detection: stretch the finger (c), bend the finger (d), and stretch the finger again (e). (f) A red apple was written on a thin film of the TN1 elastomer and it faded quickly in 3 min on exposure of UV light. In the basic action of making a fist, the skin on the finger joints repeatedly stretches and contracts by as much as 55%,52 which already exceeds the activation strain of TN1 elastomer (24%). A dumbbell-shaped TN1 elastomer was tightly attached to the middle of the finger by


15


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 31

scotch tape. As the finger bending, the fluorescence color in the middle of the elastomer sensor was changed from blue to red, while it turned to yellow with finger straightening (Figure 4c, 4d, 4e). Constantly bending and straightening the finger, the fluorescence color of the elastomer could change from red to yellow repeatedly. Therefore, it is promising to use the elastomer as a sensor for detection of changes related to stretching and contracting or as an inviting candidate for biomimic mechanochromic materials. In addition, the TN1 elastomer film coated onto white surface can be used as a mechanochemical writing/drawing tablet. Figure 4f shows an example made from TN1. A red apple was easy to be drawing on this thin film. When the colored film was irradiated with UV light (UV-340,100 W), the red color faded very quickly in 3 min without any trace. The fact that such colored patterns can be recorded by gently drawing the surface of film several times (Figure S18) indicates the easily writing and photo-erasing nature of the TN1 film.

CONCLUSION

In summary, we have designed and synthesized a novel rhodamine-based mechanochromic elastomer, which displays interesting and unique features. First, three-primary-color fluorescence emission stimulated by stress has been successfully achieved with single-mechanophorecontaining elastomer via combination of mechanochemistry and bond bending induced comformation change. Meanwhile, the fluorescence change in three primary colors was fast and reversible which made this MCP material suitable for strain sensor or drawing broad. Moreover, it not only possessed very high fluorescence quantum yield, but also showed very high sensitivity to stress because of its distinctive triple network structure. Due to these unique properties as well as the facile and convenient preparation of the mechanophore TAR, this


16

Page 17 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


elastomer will be a promising candidate for biomimic mechanochromic materials and other practical applications. The work may provide a new strategy for the development of broadspectrum MCP materials.

EXPERIMENTAL SECTION

Materials: Ethyl acrylate (EA) and butanediol diacrylate (BDA) were purchased and filtrated through a column of basic alumina to remove the inhibitor. All the other reagents were purchased and used without further purification. The UV-polymerizations were initiated by 2hydroxyethyl-2-methylpropiophenone (HMP) under a UV lamp (UV-340, 100 W) with wavelength ranging from 295 to 365 nm. Measurements: 1H NMR was recorded on 300 MHz (Bruker ARX300) and

13

C NMR

spectra were recorded on Bruker 100 MHz spectrometer at room temperature with CDCl3 as the solvents and tetramethylsilane (TMS) as the internal standard. Electrospray ionization (ESI) mass spectra were obtained on a Finnigan LCQ Advantage ion trap mass spectrometer (ThermoFisher Corporation). Differential scanning calorimetry (DSC) measurements were carried out on TA Instruments DSC Q2000. Fluorescence spectra measurements were performed on a Shimadzu RF-5301PC spectroflurophotometer. Absorption spectra were determined on a Pgeneral UV-Vis TU-1901 spectrophotometer. The DMA measurements were conducted in the three points mode with DMA Q800. Uniaxial tensile tests were performed on TMA Q400. Specimens were cut in a dumbbell shape using a normalized cutter with a central part of 15 mm in length, 2 mm in width. The photoluminescence quantum yields of the rhodamine derivatives in a ethanol solution were determined relative to a quinine sulfate solution in a 1 N H2SO4 at room-temperature, assuming a quantum yield of 0.546 when excited at 365 nm. All Density


17


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 31

Functional Theory (DFT) calculations were performed using the ORCA version 2.8 program package.53 Geometry optimizations were performed using B3LYP density functional while the final energy calculations were also performed with the B3LYP density functional. Synthesis of compound 1: Rhodamine 6G (10 g, 20.8 mmol) was dissolved in 160 mL acetonitrile. To this deep red solution was added monoethanolamine (3.7 mL, 62.6 mmol). The reaction mixture became gradually heterogeneous and lost color. After refluxing for 2 h, the reaction mixture was cooled to room temperature. The solid was filtered and washed thoroughly with water and dried under vacuum to give 9.1 g off-white product. Yield is 95 %. 1H NMR (300 MHz, CDCl3): δ 7.94 (m, 1H), 7.47 (m, 2H), 7.05 (m, 1H), 6.35 (s, 2H), 6.28 (s, 2H), 4.20 (br, 1H), 3.54 (br, 2H), 3.45 (t, 2H), 3.26 (m, 6H), 1.92 (s, 6H), 1.35 (t, 6H). 13C NMR (100 MHz, CDCl3): δ 170.1, 153.9, 151.7, 147.5, 132.8, 130.4, 128.2, 128.0, 123.8, 122.9, 118.1, 105.2, 96.6, 66.0, 62.6, 44.7, 38.4, 16.7, 14.7. ESI-MS (m/z): Calculated for C28H32O3N3 (M+H+): 458.24, found (M+H+): 458.32. Synthesis of THR: Compound 1 (4 g, 8.7 mmol) and K2CO3 (9.6 g, 69.8 mmol) were added into 40 mL ethylene chlorohydrin. The reaction mixture was heated at 100 oC for 24 h. Excessive ethylene chlorohydrin was evaporated under vacuum. The residue was poured into water and extracted with CH2Cl2 for three times. After drying it with Na2SO4, the organic solvent was evaporated. The pure product was obtained by column chromatography on silica gel (CH2Cl2 : ethanol = 35 : 1) to give 70 % THR. 1H NMR (300 MHz, CDCl3): δ 7.99 (m, 1H), 7.54 (m, 2H), 7.07 (m, 1H), 6.92 (s, 2H), 6.50 (s, 2H), 3.95 (br, 1H), 3.65 (t, 4H), 3.46 (t, 2H), 3.31 (t, 2H), 3.24 (t, 4H), 3.05 (q, 4H), 2.25 (br, 2H), 2.11 (s, 6H), 1.06 (t, 6H).

13

C NMR (100 MHz,

CDCl3): δ 170.2, 153.1, 150.8, 150.2, 133.1, 130.3, 130.0, 129.5, 128.7, 123.8, 123.3, 113.4,


18

Page 19 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


110.4, 65.4, 62.1, 59.1, 53.7, 48.2, 44.9, 17.9, 11.6. ESI-MS (m/z): Calculated for C32H40N3O5 (M+H+): 546.29, found (M+H+): 546.36. Synthesis of crosslinker TAR: THR (1.5 g, 2.7 mmol) and triethylamine (3.4 mL, 24.7 mmol) were dissolved in 60 mL CH2Cl2 in a 100 mL bottom flask. A solution of acryloyl chloride (0.87 mL, 10.7 mmol) in 10 mL CH2Cl2 was added dropwise into the flask at 0 oC. The mixture was allowed to warm to room temperature and stirred overnight. The solution was washed with diluted hydrochloric acid. After drying it with Na2SO4, the organic solvent was evaporated. The pure product was obtained by chromatography on silica gel using CH2Cl2 as eluent. Yield is 96 %. 1H NMR (300 MHz, CDCl3): δ 7.99 (m, 1H), 7.52 (m, 2H), 7.06 (m, 1H), 6.91 (s, 2H), 6.42 (s, 2H), 6.40-5.73 (m, 9H), 4.25 (t, 4H), 3.79 (t, 2H), 3.53 (t, 2H), 3.34 (t, 4H), 3.13 (q, 4H), 2.04 (s, 6H), 1.08 (t, 6H). 13C NMR (100 MHz, CDCl3): δ 168.7, 166.1, 165.5, 153.3, 151.0, 150.1, 130.8, 130.7, 130.1, 129.7, 128.3, 128.1, 123.9, 113.2, 109.9, 64.4, 62.2, 61.2, 53.4, 50.8, 47.9, 38.9, 17.8, 12.3. ESI-MS (m/z): Calculated for C41H46N3O8 (M+H+): 708.32, found (M+H+): 708.38. Synthesis of compound 2: Compound 1 (5.0 g, 10.9 mmol) and K2CO3 (12.1 g, 87.4 mmol) were added into 40 mL ethylene chlorohydrin. The reaction mixture was heated at 100 oC for 6 h. Excessive ethylene chlorohydrin was evaporated under vacuum. The residue was poured into water and extracted with CH2Cl2 for three times. After drying it with Na2SO4, the organic solvent was evaporated. The pure product was obtained by column chromatography on silica gel (CH2Cl2 : ethanol = 50 : 1). Yield is 51 %. 1H NMR (300 MHz, CDCl3): δ 7.95 (m, 1H), 7.49 (m, 2H), 7.04 (m, 1H), 6.91 (s, 1H), 6.47 (s, 1H), 6.33 (s, 1H), 6.29 (s, 1H), 4.08 (t, 1H), 3.61 (br, 2H), 3.45 (m, 2H), 3.25(m, 6H), 3.03 (q, 2H), 2.09 (s, 3H), 1.93 (s, 3H), 1.33 (t, 3H), 1.03 (t, 3H). 13

C NMR (100 MHz, CDCl3): δ 170.1, 153.5, 151.5, 150.6, 150.4, 147.7, 132.9, 130.2, 129.9,


19


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 31

129.5, 128.4, 128.0, 123.8, 123.1, 118.5, 113.7, 110.4, 104.8, 96.5, 65.7, 62.3, 59.1, 53.8, 48.3, 44.7, 38.3, 17.9, 16.7, 14.7, 11.7. ESI-MS (m/z): Calculated for C30H36N3O4 (M+H+): 502.26, found (M+H+): 502.36. Synthesis of control crosslinker 3: Acrylic acid (0.41 mL, 6.0 mmol) 2-chloro-1methylpyridinium iodide (1.52 g, 6.0 mmol) and triethylamine (1.66 mL, 12.0 mmol) were dissolved into 50 mL CH2Cl2 and stirred at room temperature for 30 min. Compound 2 (1.0 g, 2.0 mmol) was then added into the solution and stirred overnight. The solution was washed with diluted hydrochloric acid for three times. After drying it with Na2SO4, the organic solvent was evaporated. The pure product was obtained by column chromatography on silica gel (CH2Cl2 : ethanol = 50 : 1). Yield is 60 %. 1H NMR (300 MHz, CDCl3): δ 7.96 (m, 1H), 7.46 (m, 2H), 7.03 (m, 1H), 6.89 (s, 1H), 6.20-6.45 (m, 5H), 5.70-6.15 (m, 4H), 4.22 (t, 2H), 3.78 (t, 2H), 3.48 (t, 2H), 3.30 (t, 2H), 3.22 (q, 2H), 3.08 (q, 2H), 2.01 (s, 3H), 1.89 (s, 3H), 1.32 (t, 3H), 1.04 (t, 3H). 13

C NMR (100 MHz, CDCl3): δ 168.6, 166.0, 165.5, 153.6, 151.4, 150.8, 150.3, 147.6, 132.7,

130.8, 130.5, 130.4, 129.8, 129.6, 128.4, 128.3, 128.2, 123.8, 123.0, 118.3, 113.6, 109.9, 105.3, 96.5, 64.7, 62.2, 61.4, 53.4, 50.8, 47.9, 38.8, 38.3, 17.7, 16.7, 14.7, 12.3. ESI-MS (m/z): Calculated for C36H40N3O6 (M+H+): 610.28, found (M+H+): 610.32. Synthesis of compound 4: Rhodamine 6G (10 g, 20.8 mmol) was dissolved in 160 mL acetonitrile. To this deep red solution was added n-butylamine (6.1 mL, 62.6 mmol). The reaction mixture lost color gradually. After refluxing for 2 h, the reaction mixture was cooled to room temperature and poured into 150 mL methanol. The solid was filtered and washed thoroughly with water and dried under vacuum to give 8.8 g off-white product. Yield is 90 %. 1H NMR (300 MHz, CDCl3): δ 7.92 (m, 1H), 7.42 (m, 2H), 7.01 (m, 1H), 6.35 (s, 2H), 6.24 (s, 2H), 3.50 (br, 2H), 3.23 (t, 4H), 3.11 (t, 2H), 1.90 (s, 6H), 1.32 (t, 6H), 1.08 (br, 4H), 0.67 (t, 3H). 13C


20

Page 21 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


NMR (100 MHz, CDCl3): δ 168.1, 153.8, 151.7, 147.3, 132.2, 131.4, 128.7, 127.9, 123.7, 122.7, 117.8, 106.5, 96.5, 64.9, 40.1, 38.4, 30.3, 20.3, 16.7, 14.8, 13.6. ESI-MS (m/z): Calculated for C30H36N3O2 (M+H+): 470.27, found (M+H+): 470.40. Synthesis of compound 5: Compound 4 (5.0 g, 10.6 mmol) and K2CO3 (11.8 g, 85.2 mmol) were added into 40 mL ethylene chlorohydrin. The reaction mixture was heated at 100 oC for 24 h. Excessive ethylene chlorohydrin was evaporated under vacuum. The residue was poured into water and extracted with CH2Cl2 for three times. After drying it with Na2SO4, the organic solvent was evaporated. The pure product was obtained by column chromatography on silica gel (CH2Cl2 : ethanol = 70 : 1). Yield is 65 %. 1H NMR (300 MHz, CDCl3): δ 7.96 (m, 1H), 7.50 (m, 2H), 7.05(m, 1H), 6.91 (s, 2H), 6.43 (s, 2H), 3.61 (br, 4H), 3.21 (t, 4H), 3.11 (t, 2H), 3.03 (q, 4H), 2.08 (s, 6H), 1.04 (m, 10H), 0.63 (t, 3H). 13C NMR (100 MHz, CDCl3): δ 168.1, 152.7, 150.5, 150.2, 132.5, 131.3, 130.2, 130.0, 128.5, 123.7, 123.0, 114.5, 110.2, 64.4, 59.1, 53.9, 48.3, 40.3, 30.4, 20.2, 17.8, 13.5, 11.6. ESI-MS (m/z): Calculated for C34H44N3O4 (M+H+): 558.33, found (M+H+): 558.36. Synthesis of control crosslinker 6: Compound 5 (1.0 g, 1.8 mmol) and triethylamine (1.5 mL, 10.8 mmol) were dissolved in 50 mL CH2Cl2 in a 100 mL bottom flask. A solution of acryloyl chloride (0.44 mL, 5.4 mmol) in 5 mL CH2Cl2 was added dropwise into the flask at 0 o

C. The mixture was allowed to warm to room temperature and stirred overnight. The solution

was washed with diluted hydrochloric acid. After drying it with Na2SO4, the organic solvent was evaporated. The pure product was obtained by chromatography on silica gel using CH2Cl2 as eluent. Yield is 97 %. 1H NMR (300 MHz, CDCl3): δ 7.95 (m, 1H), 7.48 (m, 2H), 7.05 (m, 1H), 6.90 (s, 2H), 6.40 (s, 2H), 6.32 (d, 2H), 6.08 (q, 2H), 5.81(d, 2H), 4.21 (t, 4H), 3.30 (t, 4H), 3.09 (m, 6H), 2.04 (s, 6H), 1.03 (m, 10H), 0.62 (t, 3H). 13C NMR (100 MHz, CDCl3): δ 168.1, 166.1,


21


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 31

152.9, 150.7, 150.2, 132.4, 131.3, 130.8, 130.0, 128.3, 123.8, 123.0, 113.9, 109.8, 64.5, 62.1, 58.4, 50.9, 48.0, 40.3, 30.4, 20.2, 18.4, 17.6, 13.5, 12.2. ESI-MS (m/z): Calculated for C40H48N3O6 (M+H+): 666.35, found (M+H+): 666.38. Preparation of the first networks SNx: First networks were prepared by UV polymerization of a solution of EA (1 eq.), TAR crosslinker (1 % to 3 % mol) and photo-initiator HMP (1 % mol). A 50% solution of the reactants

in toluene was poured in a 0.36 mm thick

glass mold and exposed to UV light. The polymerization was then left to proceed for 1 h. Any unreacted species were extracted with a mixture of toluene and petroleum ether for two days. Swollen first networks were then dried under vacuum at 80 oC. At this point we quantified the fraction of unreacted species to be less than 2 wt % of the dry sample. Preparation of the double networks DNx: Double networks DNx were prepared starting from SNx. A piece of SNx was swollen in a bath composed of EA (40 mL) as monomer, BDA (28 µL, 0.04 % of monomer) as crosslinker and HMP (573 µL, 1 % of monomer) as UV initiator. The swollen reached equilibrium after 6 h. The sample was then carefully extracted from the solution and placed between glass sheets. A second step of UV polymerization was performed for 1 h. The DNx was then extracted with a mixture of toluene and petroleum ether for two days and dried under vacuum at 80 oC. Preparation of the triple networks TNx: Triple networks were prepared following the same procedure of swollen-UV polymerization process but starting from DNx. Preparation of the control triple networks C-3 and C-6: The C-3 and C-6 elastomers were prepared following the same procedure for TN1 except that the cross-linker used in first networks was compound 3 for C-3 and compound 6 for C-6.


22

Page 23 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


To determine the prestretch of the chains of first networks, we define a parameter λprestretch. Before swelling, the thickness (hSN) of the piece of first network was measured. The same data were collected from the final double/triple network sample (h). The prestretch of chains of the first network was then determined using the equation: λprestretch = h

hSN

.

Supporting Information The synthesis procedures and characterizations of organic compounds, fluorescent spectra, UVvis spectra, DSC and DMA profiles, 1H NMR,

13

C NMR, ESI-MS spectra, movie files. This

material is available free of charge via the Internet at http://pubs.acs.org.

AUTHOR INFORMATION

Corresponding Authors * E-mail: [email protected]. * E-mail: [email protected]. Notes T. Wang and N. Zhang contributed equally to this work. The authors declare no competing ﬁnancial interest.

ACKNOWLEDGMENT

We thank National Natural Science Foundation of China (No. 21474093 and No. 21674101) for financial support.


23


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 31

REFERENCES (1) Gillespie, P. G.; Walker, R. G. Molecular Basis of Mechanosensory Transduction. Nature 2001, 413, 194-202. (2) Friedland, J. C.; Lee, M. H.; Boettiger, D. Mechanically Activated Integrin Switch Controls Alpha5beta1 Function. Science 2009, 323, 642-644. (3) Mäthger, L. M.; Denton, E. J.; Marshall, N. J.; Hanlon, R. T. Mechanisms and Behavioural Functions of Structural Coloration in Cephalopods. J. R. Soc., Interface 2009, 6, 149-163. (4) Hanlon, R. Cephalopod Dynamic Camouflage. Curr. Biol. 2007, 17, 400-404. (5) Davis, D. A.; Hamilton, A.; Yang, J. L.; Cremar, L. D.; Gough, D. V.; Potisek, S. L.; Ong, M. T.; Braun, P. V.; Martinez, T. J.; White, S. R.; Moore, J. S.; Sottos, N. R. Force-Induced Activation of Covalent Bonds in Mechanoresponsive Polymeric Materials. Nature 2009, 459, 6872. (6) Göstl, R.; Sijbesma, R. P. π-Extended Anthracenes as Sensitive Probes for Mechanical Stress. Chem. Sci. 2016, 7, 370-375. (7) Balkenende, D. W. R.; Coulibaly, S.; Balog, S.; Simon, Y. C.; Fiore, G. L. and Weder, C. Mechanochemistry with Metallosupramolecular Polymers. J. Am. Chem. Soc. 2014, 136, 1049310498. (8) Chen, Y. L.; Spiering, A. J. H.; Karthikeyan, S.; Peters, G. W. M.; Meijer, E. W. and Sijbesma, R. P. Mechanically Induced Chemiluminescence from Polymers Incorporating a 1,2Dioxetane Unit in the Main Chain. Nat. Chem. 2012, 4, 559-562.


24

Page 25 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(9) Park, D. H.; Hong, J.; Park, I. S.; Lee, C. W.; Kim, J. M. A Colorimetric Hydrocarbon Sensor Employing a Swelling-Induced Mechanochromic Polydiacetylene. Adv. Funct. Mater. 2014, 24, 5186-5193. (10) Williams, G. A.; Ishige, R.; Cromwell, O. R.; Chung, J.; Takahara, A.; Guan, Z. B. Mechanically Robust and Self-Healable Superlattice Nanocomposites by Self-Assembly of Single-Component “Sticky” Polymer-Grafted Nanoparticles. Adv. Mater. 2015, 27, 3934-3941. (11) Imato, K.; Kanehara, T,; Nojima, S.; Ohishi, T.; Higaki, Y.; Takahara, A.; Otsuka, H. Repeatable Mechanochemical Activation of

Dynamic Covalent Bonds in Thermoplastic

Elastomers. Chem. Commun. 2016, E, 10482-10485. (12) Olson, C. E.; Previte, M. J. R. and Fourkas, J. T. Efficient and Robust Multiphoton Data Storage in Molecular Glasses and Highly Crosslinked Polymers. Nat. Mater. 2002, 1, 225-228. (13) Kishimura, A.; Yamashita, T.; Yamaguchi, K. and Aida, T. Rewritable Phosphorescent Paper by the Control of Competing Kinetic and Thermodynamic Self-Assembling Events. Nat. Mater. 2005, 4, 546-549. (14) Park, J.; Lee, Y.; Hong, J.; Lee, Y.; Ha, M.; Jung, Y.; Lim, H.; Kim, S. Y.; Ko, H. TactileDirection-Sensitive and Stretchable Electronic Skins based on Human-Skin-Inspired Interlocked Microstructures. ACS Nano 2014, 8, 12020-12029. (15) Ferrara, M.; Bengisu, M. Materials that Change Color, Springer, 2014. (16) Ciardelli, F.; Ruggeribc, G. and Pucci, A. Dye-Containing Polymers: Methods for Preparation of Mechanochromic Materials. Chem. Soc. Rev. 2013, 42, 857-870.


25


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 31

(17) Crenshaw, B. R. and Weder, C. Deformation-Induced Color Changes in Melt-Processed Photoluminescent Polymer Blends. Chem. Mater. 2003, 15, 4717-4724. (18) Lowe, C.; Weder, C. Oligo(p-phenylene vinylene) Excimers as Molecular Probes: Deformation-Induced Color Changes in Photoluminescent Polymer Blends. Adv. Mater. 2002, 14, 1625-1629. (19) Pucci, A.; Bertoldo, M.; Bronco, S. Luminescent Bis(benzoxazolyl)stilbene as a Molecular Probe for Poly(propylene) Film Deformation. Macromol. Rapid Commun. 2005, 26, 1043-1048. (20) Pucci, A. and Ruggeri, G. Mechanochromic Polymer Blends. J. Mater. Chem. 2011, 21, 8282-8291. (21) Chen, Y. L. and Sijbesma, R. P. Dioxetanes as Mechanoluminescent Probes in Thermoplastic Elastomers. Macromolecules 2014, 47, 3797-3805. (22) Ducrot, E.; Chen, Y. L.; Bulters, M.; Sijbesma, R. P.; Creton, C. Toughening Elastomers with Sacrificial Bonds and Watching Them Break. Science 2014, 344, 186-189. (23) Gossweiler, G. R.; Brown, C. L.; Hewage, G. B.; Sapiro-Gheiler, E.; Trautman, W. J.; Welshofer, G. W. and Craig, S. L. Mechanochemically Active Soft Robots. ACS Appl. Mater. Interfaces 2015, 7, 22431-22435. (24) Clough, J. M. and Sijbesma, R. P. Dioxetane Scission Products Unchanged by Mechanical Force. ChemPhysChem 2014, 15, 3565-3571.


26

Page 27 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(25) Wang, Z. J.; Ma, Z. Y.; Wang, Y.; Xu, Z. J.; Luo, Y. Y.; Wei, Y. and Jia, X. R. A Novel Mechanochromic and Photochromic Polymer Film: When Rhodamine Joins Polyurethane. Adv. Mater. 2015, 27, 6469-6474. (26) Imato, K.; Kanehara, T.; Ohishi, T.; Nishihara, M.; Yajima, H.; Ito, M.; Takahara, A.; Otsuka, H. Mechanochromic Dynamic Covalent Elastomers: Quantitative Stress Evaluation and Autonomous Recovery. ACS Macro Lett. 2015, 4, 1307−1311. (27) Kosuge, T.; Imato, K.; Goseki, R.; Otsuka, H. Polymer–Inorganic Composites with Dynamic Covalent Mechanochromophore. Macromolecules 2016, 49, 5903−5911. (28) Zhang, H.; Gao, F.; Cao, X. D.; Li, Y. Q.; Xu, Y. Z.; Weng, W. G. and Boulatov, R. Mechanochromism and Mechanical Force-Triggered Cross-Linking from a Single Reactive Moiety Incorporated into Polymer Chains. Angew. Chem. Int. Ed. 2016, 55, 3040-3044. (29) Beiermann, B. A.; Kramer, S. L. B.; May, P. A.; Moore, J. S.; White, S. R. and Sottos, N. R. The Effect of Polymer Chain Alignment and Relaxation on Force-Induced Chemical Reactions in an Elastomer. Adv. Funct. Mater. 2014, 24, 1529-1537. (30) Black, A. L.; Lenhardt, J. M. and Craig, S. L. From Molecular Mechanochemistry to Stress-Responsive Materials. J. Mater. Chem. 2011, 21, 1655-1663. (31) Li, J.; Nagamani, C. and Moore, J. S. Polymer Mechanochemistry: from Destructive to Productive. Acc. Chem. Res. 2015, 48, 2181-2190. (32) Gossweiler, G. R.; Hewage, G. B.; Soriano, G.; Wang, Q. M.; Welshofer, G. W.; Zhao, X. H. and Craig, S. L. Mechanochemical Activation of Covalent Bonds in Polymers with Full and Repeatable Macroscopic Shape Recovery. ACS Macro Lett. 2014, 3, 216-219.


27


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 31

(33) Jiang, S. C.; Zhang, L. X.; Xie, T. W.; Lin, Y. J.; Zhang, H.; Xu, Y. Z.; Weng, W. G. and Dai, L. Z. Mechanoresponsive PS-PnBA-PS Triblock Copolymers via Covalently Embedding Mechanophore. ACS Macro Lett. 2013, 2, 705-709. (34) Kim, J. W.; Jung, Y.; Coates, G. W. and Silberstein, M. N. Mechanoactivation of Spiropyran Covalently linked PMMA: Effect of Temperature, Strain Rate, and Deformation Mode. Macromolecules 2015, 48, 1335-1342. (35) Lee, C. K.; Diesendruck, C. E.; Lu, E.; Pickett, A. N.; May, P. A.; Moore, J. S. and Braun, P. V. Solvent Swelling Activation of a Mechanophore in a Polymer Network. Macromolecules 2014, 47, 2690-2694. (36) Peterson, G. I.; Larsen, M. B.; Ganter, M. A.; Storti, D. W. and Boydston, A. J. 3DPrinted Mechanochromic Materials. ACS Appl. Mater. Interfaces 2015, 7, 577-583. (37) Wang, Q. M.; Gossweiler, G. R.; Craig, S. L. and Zhao, X. H. Cephalopod-Inspired Design of Electro-Mechano-Chemically Responsive Elastomers for On-Demand Fluorescent Patterning. Nature Communications 2014, 5, 4899-4907. (38) Fang, X. L.; Zhang, H.; Chen, Y. J.; Lin, Y. J.; Xu, Y. Z.; Weng, W. G. Biomimetic Modular Polymer with Tough and Stress Sensing Properties. Macromolecules 2013, 46, 65666574. (39) Chibisov, A. K. and Görner, H. Singlet versus Triplet Photoprocesses in Indodicarbocyanine Dyes and Spiropyran-Derived Merocyanines. J. Photochem. Photobiol., A 1997, 105, 261–267.


28

Page 29 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(40) Chibisov, A. K. and Görner, H. Photoprocesses in Spiropyran-Derived Merocyanines. J. Phys. Chem. A 1997, 101, 4305–4312. (41) Willwohl, H.; Wolfrum, J.; Gleiter, R. Kinetics and Mechanism of the Photochromism of N-Phenyl-Rhodaminelactame. Laser Chem. 1989, 10, 63-72. (42) Kim, H. N.; Lee, M. H.; Kim, H. J.; Kim, J. S.; Yoon, J. A New Trend in Rhodaminebased Chemosensors: Application of Spirolactam Ring-Opening to Sensing Ions. Chem. Soc. Rev. 2008, 37, 1465-1472. (43) Ioffe, I. S.; Otten, V. F. Rhodamine Dyes and Compounds Related to Them. XIV. Interconversion of the Colorless and Colored Forms of Rhodamine and Rhodol. J. Org. Chem.USSR 1965, 1, 326-336. (44) Whitaker, J. E.; Haugland, R. P.; Ryan, D.; Hewitt, P. C.; Haugland, R. P.; Prendergast, F. G. Fluorescent Rhodol Derivatives: Versatile, Photostable Labels and Tracers. Anal. Biochem. 1992, 207, 267-279. (45) Peng, T.; Yang, D. Construction of a Library of Rhodol Fluorophores for Developing New Fluorescent Probes. Org. Lett. 2010, 12, 496-499. (46) Spahn, P.; Finlayson, C. E.; Etah, W. M.; D. Snoswell, R. E.; Baumberg, J. J. and Hellmann, G. P. Modification of the Refractive-Index Contrast in Polymer Opal Films. J. Mater. Chem. 2011, 21, 8893-8897. (47) Montenegro, H.; Paolo, M. D.; Capdevila, D.; Aramendía, P. F. and Bossi, M. L. The Mechanism of the Photochromic Transformation of Spirorhodamines. Photochem. Photobiol. Sci. 2012, 11, 1081-1086.


29


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 31

(48) Beija, M.; Afonso, C. A. M. and Martinho, J. M. G. Synthesis and Applications of Rhodamine Derivatives as Fluorescent Probes. Chem. Soc. Rev. 2009, 38, 2410-2433. (49) Gordy, W. Dependence of Bond Order and of Bond Energy upon Bond Length. J. Chem. Phys. 1947, 15, 305-310. (50) Nebbia, G. Bond Energy and Bond Order. J. Chem. Phys. 1950, 18, 1116-1117. (51) Belov, V. N.; Bossi, M. L.; Fölling, J.; Boyarskiy, V. P.; Hell, S. W. Rhodamine Spiroamides for Multicolor Single-Molecule Switching Fluorescent Nanoscopy. Chem. - Eur. J. 2009, 15, 10762-10776. (52) Yamada, T.; Hayamizu, Y.; Yamamoto, Y.; Yomogida, Y.; Najafabadi, A. L.; Futaba, D. N.; Hata, K. A Stretchable Carbon Nanotube Strain Sensor for Human-Motion Detection. Nat. Nanotechnol. 2011, 6, 296-301. (53) Neese, F.; ORCA-an ab initio, Density Functional and Semiempirical Program Package Version 2.8 2011, Universität Bonn, Bonn, Germany.


30

Page 31 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Graphic for manuscript