Efficient and Stable Silicon Microwire Photocathodes with a Nickel

Apr 9, 2018 - The best-performing, all-earth-abundant microwire array devices exhibited, under AM 1.5G simulated solar illumination, an ideal regenera...
0 downloads 5 Views 1MB Size
Subscriber access provided by UNIV OF DURHAM

Efficient and Stable Silicon Microwire Photocathodes with a Nickel Silicide Interlayer for Operation in Strongly Alkaline Solutions Wouter Vijselaar, Roald M. Tiggelaar, Han J.G.E. Gardeniers, and Jurriaan Huskens ACS Energy Lett., Just Accepted Manuscript • DOI: 10.1021/acsenergylett.8b00267 • Publication Date (Web): 09 Apr 2018 Downloaded from http://pubs.acs.org on April 9, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Efficient and Stable Silicon Microwire Photocathodes with a Nickel Silicide Interlayer for Operation in Strongly Alkaline Solutions Wouter Vijselaar, Roald M.Tiggelaar, Han Gardeniers, Jurriaan Huskens* W. Vijselaar, Prof. J. Huskens Molecular NanoFabrication, MESA+ Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE, Enschede, The Netherlands E-mail: [email protected] Prof. H. Gardeniers Mesoscale Chemical Systems, MESA+ Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE, Enschede, The Netherlands Dr. R.M. Tiggelaar NanoLab cleanroom, MESA+ Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE, Enschede, The Netherlands

ACS Paragon Plus Environment

1

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 20

Abstract Most photoanodes commonly applied in solar fuel research (e.g., of Fe2O3, BiVO4, TiO2, or WO3) are only active and stable in alkaline electrolytes. Silicon (Si)-based photocathodes on the other hand are mainly studied under acidic conditions, due to their instability in alkaline electrolytes. Here, we show that the in-diffusion of nickel into a 3D Si structure, upon thermal annealing, yields a thin (sub-100-nm), defect-free nickel silicide (NiSi) layer. This has allowed us to design and fabricate a Si microwire photocathode with a NiSi interlayer between the catalyst and the Si microwires. Upon electrodeposition of the catalyst (here, nickel molybdenum) on top of the NiSi layer, an efficient, Si-based photocathode was obtained that is stable in strongly alkaline solutions (1 M KOH). The best performing, all earth-abundant microwire array devices exhibited, under AM 1.5G of simulated solar illumination, an ideal regenerative cell efficiency of 10.1%.

ACS Paragon Plus Environment

2

Page 3 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

In a complete photoelectrochemical cell, a photocathode and -anode are coupled together, preferably in one electrolyte, which is either acidic or alkaline. A major shortcoming of a photoelectrochemical (PEC) cells that operate in an acidic electrolyte is the limited range of materials for the oxygen evolution reaction (OER) catalyst.1-3 The vast majority of PEC cellcompatible OER catalysts in acidic electrolyte is based on oxides of ruthenium (Ru) and, especially, iridium (Ir) which are very scarce noble metals.4 Furthermore, McCrory et al. benchmarked the overpotential to produce 10 mA/cm2 for many known earth-abundant OER and HER catalysts for 2 h in both acidic (1 M H2SO4) and alkaline (1 M KOH) electrolytes.2 According to McCrory et al. the best earth-abundant HER/OER catalyst combination in acidic electrolyte (i.e. NiMo for the HER and Ni for the OER) requires an overpotential of 1.14 V, while the best HER/OER combination in alkaline electrolyte (i.e. NiMo for the HER and NiMoFe for the OER) only requires an overpotential of 430 mV.2 The latter overpotential is almost equal to that of the combination of the precious metals platinum (Pt) and Ru, that have an overpotential of 390 mV. Furthermore, McKone et al. showed that NiMo, which is the best performing earth-abundant HER catalyst in acidic electrolyte, is only stable up to 10 h of operation, while the same catalyst is stable >100 h in alkaline electrolyte.5 Therefore, there is a strong drive to produce HER photocathodes, based on earth-abundant materials, that are stable and active in alkaline medium.

Silicon (Si) is a widely investigated material as photoaborber in a photocathode. However crystalline Si has a high stability in acidic medium, but it is etched quickly (~2 µm/h) in alkaline solutions. Therefore the majority of research for Si as photocathode is conducted in acidic environment. This problem can potentially be overcome by introducing an intermediate closed layer between the catalyst and the n+-Si emitter. Both Kast and Bae et al. showed the necessity to

ACS Paragon Plus Environment

3

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 20

protect planar Si photocathodes with an intermediate layer of titanium oxide (TiO2).6,7 However, they employed a thin layer (~2 nm) of a precious metal catalyst (Ir or Pt) to overcome the light absorption limitations which are encountered with earth-abundant catalyst materials. Earthabundant catalysts require higher mass loadings of catalyst to achieve the same catalytic activity.8 High mass loadings of catalyst lead to parasitic optical absorption losses of the photon absorber (Si) underneath, limiting the photon current density (Jsc) and concomitantly the efficiency (η) of the device.8,9

Our previously fabricated n+/p-Si microwire array photocathodes, in part based on existing microwire research of others,8,9 with spatioselectively deposited nickel molybdenum (NiMo) surpassed the latter problem.10 By carefully adjusting the design parameters, we reported one of the highest reported efficiencies (i.e. ηirc = 10.8%) in acidic electrolyte. In the fabrication process of these photocathodes, the majority of the microwires is passivated by silicon-rich silicon nitride (SiNx) and protected from the harsh alkaline electrolyte.11 Unfortunately, spatioselectively deposited NiMo does not provide a conformal coverage over the Si structure, and thus the underlying Si substrate in the catalyst-covered areas will be etched in an alkaline electrolyte, reducing the lifetime of Si/NiMo microwire photocathodes substantially.10,12 Passivation techniques, as employed by Kast and Bae et al., are mostly limited to planar substrates, due to the limitations of sputtering or evaporation.6,7 Si microwire substrates require a deposition technique which is suitable for high-aspect-ratio structures. Atomic layer deposition (ALD) of TiO2 has been used successfully to coat micropillars conformally,13 but its applicability in spatioselective deposition has so far not been tested.

ACS Paragon Plus Environment

4

Page 5 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Therefore, the proposed intermediate has to meet several requirements, be (i) deposited spatioselectively only on the interface between the silicon and the NiMo overlayer, (ii) electrically conductive between the n+-Si emitter and the catalyst on top, (iii) stable in alkaline solution, (iv) defect free, and (v) deposition techniques are compatible with high aspect ratio structures. In order to comply with all requirements for defect-free interlayer formation, we envisaged the use of a spatioselectively electrodeposited Ni layer (stable between pH 5 and 14)14 that is transformed into nickel silicide (NiSi) at locations where it is in contact with Si, in a self-aligned and repairing process. NiSi is an effective and proven masking material for selective Si etching in KOH, in which it is not being etched at a noticeable rate, and NiSi is highly conductive.15,16 More importantly, the formation mechanism of NiSi provides the opportunity to repair possible defects introduced in the preceding step of the electrodeposition of Ni, since Ni diffuses into the Si substrate following Fick’s law of diffusion. Therefore NiSi as interlayer can comply with all four requirements stated above.

Both Pinaud and Shaner et al. have pointed out that PEC cells could become more efficient and commercially attractive than a PV-electrolyzer combination when the production cost can be reduced, which can be addressed by using earth-abundant materials and by improving the overall efficiency and the operational durability.17-18 The work described in our study addresses steps in all of these directions.

Here we show the chemical resistivity and applicability of NiSi as an interlayer for the protection of an efficient Si microwire photocathode in alkaline electrolyte for prolonged period of times. We apply the NiSi interlayer in a photocathode that is functional in alkaline medium, by the fabrication

ACS Paragon Plus Environment

5

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 20

of a Si microwire array with a radial n+/p-junction, the spatioselective formation of a conformal interlayer of NiSi, and the subsequent electrodeposition of NiMo as an active and stable HER catalyst in alkaline medium.2 By the spatioselective functionalization of the Si microwire with a catalyst, light blocking due to the catalyst is kept to a minimum.10 The activity and stability of the photocathode are assessed for prolonged periods of time under strong alkaline conditions.

Development of a NiSi interlayer The fabrication of silicon nitride (SiNx)-passivated microwires with a radial n+/p junction of ~900 nm, a diameter of 4 µm, a length of 40 µm, a pitch of 12 µm, and the spatioselective retracting of the SiNx layer was performed as previously reported (see Materials and Methods).1923

The fabrication scheme of the microwire arrays with spatioselectively deposited Ni or NiSi

interlayers is schematically depicted in Scheme 1.

Scheme 1 Fabrication scheme for alkaline-stable photocathodes, starting from a microwire array with a spatioselectively etched SiNx protection layer, which acts as a masking layer for (A) the electrodeposition of Ni on top of the wires, followed by either (B) direct electrodeposition of NiMo on top of the Ni-covered microwire array, or (C) formation of NiSi by RTA and removal of the remaining Ni by wet etching, followed by (D) electrodeposition of NiMo on top of the NiSi-covered microwire array.

ACS Paragon Plus Environment

6

Page 7 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

First, we fabricated microwire arrays with spatioselectively electrodeposited Ni (Scheme 1A). The deposition of conformal Ni caps is discussed in detail in the SI. These Ni caps were used as is, or the Ni cap was transformed into NiSi by means of rapid thermal annealing (RTA, 485 °C and a holding time of 120 s; see Scheme 1C and Figure S1). NiSi is a widely studied material in solid-state devices for electronic applications, owing to its properties: its ease in formation due to a broad temperature range (400 – 700 °C) (as opposed to other silicides, e.g., TiSi, CoSi, RhSi), its chemical resistivity in KOH, and a low resistivity (~10-18 µΩ cm).24,25 NiSi has been found to grow by a diffusion-controlled mechanism, whereby the Ni atoms diffuse through the growing NiSi layer with an activation energy between ~1.75 and 1.85 eV.25 The pre-exponential factor, D0, for the diffusion of Ni is mainly dependent on the pre-treatment of the Si sample before Ni deposition (e.g. with native oxide, or stripped in 1% HF) and is in the range of 1-2 cm2/s.26

In order to test the chemical resistivity of each material (i.e., Ni, SiNx, NiSi, and Si) separately, we used 1 M KOH (2 wt.%) at room temperature, which resemble the intended operating condition of a solar-to-fuel device. The etch rates in Table S1 clearly show the necessity of protecting Si: Si etches at a high rate, although doping of Si (which is required for the emitter formation) reduces the etch rate significantly.27 Even at these reduced etch rates, unprotected microwire arrays would be etched completely within a couple of hours. In contrast, both Ni and NiSi show a very high chemical resistivity under these conditions.

SEM images were acquired after immersing passivated microwire array samples in a 1 M KOH solution for 24 h, with either Ni or NiSi as the interlayer. Figure 1A and B show SEM images of a sample that was only protected by a spatioselective Ni layer on top of the microwire. Figure 1A

ACS Paragon Plus Environment

7

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 20

shows an overview of the array, and most of the microwires were affected, etched, or completely removed. Figure 1B shows a zoom-in of Figure 1A, and only hollow sleeves of SiNx are visible whereas the Ni caps are absent. For samples with a slightly larger Ni capping layer (upper ~2 µm), released Ni caps were found all over the substrate (see Figure S2). Scallops resulting from the fabrication process of the microwires are clearly visible within the caps, further indicating the stability of Ni under the alkaline test conditions (as also from Table S1), confirming that only Si has been etched while leaving the Ni structure intact. Furthermore, the SiNx layer showed great chemical resistance, as indicated in Table S1. Therefore, these results indicate that the instability of the Si structures occurs at the interface between SiNx and Ni, or at possible pinholes in the Ni layer.

Figure 1C shows an overview of microwires with a NiSi interlayer after 24 h in 1 M KOH. All of the microwires are still intact, which indicates that NiSi provides continuous protection of the underlying silicon under the harsh alkaline conditions. Figure 1D shows a close-up of the microwires in Figure 1C, clearly confirming that the microwires are undamaged.

ACS Paragon Plus Environment

8

Page 9 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Figure 1 SEM images of Si microwire arrays after 24 h in 1 M KOH: (A) with a Ni interlayer (without annealing to NiSi, scale bar is 250 µm; (B) a zoom-in of (A), which shows the remaining hollow SiNx sleeves (scale bar is 10 µm); (C) with a NiSi interlayer (scale bar is 100 µm); (D) a zoom-in of (C) (scale bar is 20 µm). (The white spots in (D) are alkaline residues formed after taking the sample out of solution). Defects within the Ni layer are clearly detrimental for the stability of the underlying Si microwire array. Pinholes are most likely still present within several of the millions of microwires/cm2. Even a single pinhole could eventually lead to dissolution of the complete silicon device, and should therefore be prevented. Annealing the sample by RTA does not only form a chemically resistive NiSi layer, it may also (i) repair defects within the layer and (ii) seal off the interface at the top

ACS Paragon Plus Environment

9

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 20

edge of the SiNx protection layer, both attributed to the diffusion process of the Ni atoms into the Si material at the Ni-Si interface. In order to show the above mentioned effects, we produced two test structures. Figure 2A and B shows SEM images in order to visualize the repair of defects (i) and Figure 2C to E to seal interface between the protective SiNx layer and underlying Si (ii).

Figure 2 SEM images of a cross-section of a microwire (broken wires visible on the left side in both images), with scallops resulting from the fabrication process: (A) After Ni sputtering, and (B) after subsequent annealing of the sample and stripping off the residual Ni layer (bright contrast implies a conductive layer). Scale bars are 300 nm. (C) Microwire with a spatioselective electrodeposited Ni layer. Scale bar is 2 µm. (D) Cross sectional image after Ni diffusion and stripping off the residual Ni layer. Scale bar is 2 µm. (E) Zoom-in of the interface between Si, SiNx and NiSi of (D). Scale bar is 200 nm.

ACS Paragon Plus Environment

10

Page 11 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Figure 2A shows a cross-section of a Si microwire with sputtered Ni and Figure 2B after annealing the sample by RTA. Sputtering of Ni (bright contrast in Figure 2A) resulted in a nonconformal layer over the Si microwire array, in particular at the side walls where scallops are present, thus providing induced defects. The top of a scallop causes a shadowing effect for the incoming sputtered material and, as a result of the high directionality of the material flux during sputtering, no material is found within the troughs of the scallops. After annealing and stripping the remaining Ni layer, a conformal NiSi layer is visualized by the SEM image in Figure 2B. Ni not only diffused orthogonally inward, but also into the troughs of the scallops where no Ni source was present at the Si interface, thereby forming a conformal and closed NiSi layer. The diffusion distance of ~100 nm is apparently sufficient to seal the defects induced by the scalloping.

Figure 2C shows a SEM image of a 5 µm long microwire, whereby the upper 2.5 µm was spatioselective functionalized with electrodeposited Ni, and the lower 2.5 µm is SiNx. Figure 2D shows a cross-sectional image of a spatioselective functionalized Si microwire after Ni diffusion, of which Figure 2E shows a zoom-in at the interface of Si, SiNx and NiSi. A conformal layer of NiSi is formed completely over the top of the microwire (light grey), as in Figure 2B. More importantly, the zoom-in (Figure 2E) clearly visualizes that a NiSi layer is formed in-between the Si and SiNx layer. To aid in the visualization, Figure S3A shows an EDX mapping of this interface in combination with a line scan (see Figure S3B). Furthermore, we performed X-ray diffraction which further supported the 1:1 stoichiometry of NiSi (see Figure S4).28 This indicates that Ni has diffused downward in-between the conformal SiNx layer and the Si microwire, thereby effectively protecting the underlying Si against the alkaline electrolyte. Generally, as long as the defects are

ACS Paragon Plus Environment

11

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 20

smaller than twice the diffusion distance of Ni during the RTA step, defects occurring in the preceding Ni deposition step will be repaired.

Photocathodes with a NiSi interlayer After the successful development of the NiSi interlayer for providing alkaline-stable Si microwire arrays, NiMo was deposited as a catalyst on top of microwire arrays with Ni as well as NiSi as interlayer. Electrodeposition was employed in order to cover all microwires with a catalyst layer. NiMo was deposited by contacting the n+-emitter, as was performed for the preceding Ni deposition step. Successful structures of NiMo-coated wires with Ni and NiSi interlayers are shown in Figure S5. The deposition of NiMo on both substrates (i.e. Figure S5A for Ni, Figure S5B for NiSi) resulted in an open granular structure. This highlights even further the necessity for a sealed interlayer, as NiMo alone is not adequate to protect the underlying Si microwire. Furthermore, Figure S6 shows that the spatioselective electrodeposition of NiMo is possible over large areas of microwires, as long as the interlayers are conductive.

The activity of functionalized substrates was assessed using dark JE measurements for HER electrocatalysis at planar Si substrates, tested in 1 M KOH (Figure 3). The influence of the doping level of n-Si is included, since Wong et al. showed the presence of a Schottky barrier at the interface of n-type Si and NiSi.29 This barrier can be reduced by increasing the doping level of ntype Si (see SI, Figure S7). Although the band edge position of Si straddles the H+/H2 redox couple, planar Si shows almost no catalytic activity over a large overpotential range (not shown in Figure 3), which underlines the requirement for a catalyst. Furthermore, unprotected n-Si is etched rapidly (~2 µm/h) under these conditions (see Table S1). The addition of a smooth Ni film on the

ACS Paragon Plus Environment

12

Page 13 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

surface improves the catalytic activity substantially, as shown in Figure 3. By electrodepositing NiMo on top of the already deposited Ni (Scheme 1C), the activity is increased even further (see Figure 3, NiMo-Ni on n++-Si). However, from the above mentioned KOH immersion experiments, it is known that Ni alone does not protect the interface of the Si microwires, and NiSi is required to preserve the microwires.

Figure 3. Plots of current density vs. potential for planar Si devices with and without NiMo catalyst on a Ni or NiSi interlayer, at different doping levels as stated. NiSi was prepared as described, on samples with different doping levels. After removal of the remaining Ni, NiMo was deposited on top (see Scheme 1D) and the resulting dark JE behavior was characterized (Figure 3). For n-Si and n+-Si, the activity was less than for the NiMo-Ni (on n++-Si) sample. This is due to the Schottky barrier formed at lower doping levels, as described in more detail in the SI. By increasing the doping level this barrier is overcome, and the activity of NiMo-NiSi on n++-Si appeared to be the same as NiMo on a metallic Ni layer. Therefore a doping level of 1021 cm-3 was applied for the n-emitters.

ACS Paragon Plus Environment

13

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 20

Previously, we optimized Si microwire photocathodes with respect to (optimum values between brackets): doping depth of the emitter (900 nm), microwire length (40 µm), pitch (12 µm), and catalyst coverage (upper ~100 nm).10,23 Here, we used these settings to fabricate a microwire array photocathode, but now with an emitter doping level of 1021 cm-3 to ensure Ohmic contact between the catalyst and the NiSi interlayer, while using NiMo as the HER catalyst. JE measurements for Si microwire arrays with spatioselectively deposited NiMo catalyst on a NiSi interlayer were performed in a 1 M KOH electrolyte under AM1.5G illumination, and the results are presented in Figure 4A. Here, the photocathode is characterized as an ideal regenerative cell (IRC).30

Figure 4 (A) JE measurements of microwire photocathodes with a NiSi interlayer and functionalized with NiMo catalyst, see Scheme 1D. The average of four different samples prepared with the same settings is shown and the standard deviation in light blue (the four individual graphs are given in Figure S8 and their characteristic parameters in Table S2). (B) Recorded current density under supplied potential of 500 mV vs. RHE of a Si microwire array photocathode under continuous AM 1.5G simulated sunlight. The values of FF, Voc and Jph(𝐸𝐻2 /𝐻 + ) in Equation 1 are referenced to the equilibrium potential of the half-reaction being performed at the photocathode, and Pin is the light power input (AM 1.5G, 100 mW/cm2). All relevant values of the photocathode are presented in Figure 4A. Although

ACS Paragon Plus Environment

14

Page 15 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

microwires are employed here, we do note that the planar bottom accounts for half of the generated photo-response (~15 mA/cm2), as was demonstrated in our previous study,10 where we studied the influence of catalyst coverage. To our knowledge this half-cell gave the highest Voc, Jsc and FF values reported so far for an all earth-abundant photocathode in alkaline conditions, with an overall efficiency of 10.1%.

The NiMo catalyst is expected to have long stability in alkaline conditions. To assess the durability of this catalyst in the microwire configuration, we measured the current density at a constant potential vs RHE. An applied bias of 500 mV vs RHE resulted in a current density of ~10 mA/cm2 and was maintained for 12 days under AM 1.5G light (see Figure 4B). These values for potential and current density are in good agreement with the JE measurement given in Figure 4A. The average recorded current density was stable over the entire period of time, and the current only oscillated slightly, which is most probably due to H2 bubble formation and detachment. The decrease in current density in the first day is most likely due to an increase of the temperature of the whole PEC cell, by the solar irradiation. This will lead to a negative shift of the Voc of the photocathode.31,32 The shift in Voc has been observed, by performing JE measurements at controlled cell temperatures (Figure S9A). Plotting the Voc as a function of the PEC cell temperature, revealed a shift of ~2.2 mV/°C (Figure S9B).31 Thereby, a small change of the Voc has a large effect on the current density at constant potential. Furthermore, the Si microwire arrays were unaffected by the immersion in 1 M KOH for prolonged periods of time (see Figure S10), which indicates the excellent passivation properties of the NiSi interlayer, positioned between the Si microwires and the NiMo catalyst.

ACS Paragon Plus Environment

15

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 20

In conclusion, we have designed, fabricated and experimentally validated a broadly applicable photoelectrode architecture that circumvents not only the trade-off between catalytic activity and optical absorption, but also provides stability in harsh alkaline electrolyte. For the latter reason, an interlayer of NiSi was developed to effectively shield the underlying Si microwire from the alkaline electrolyte, in which Si microwires normally are being etched rapidly. By annealing a sample with spatioselectively electrodeposited Ni, pinholes within the Ni layer were repaired effectively by Ni diffusion during the NiSi formation step. To ensure Ohmic behavior between the microwire array and the NiSi interlayer, a high doping level of the Si emitter layer is required to overcome an undesirable Schottky barrier. Lastly, by spatially decoupling light absorption and catalytic activity on high-aspect-ratio silicon microwires with a radial n++/p-junction, an efficient, i.e. ηIRC = 10.1%, solar-driven Si photocathode that is stable in alkaline electrolyte was achieved, which maintained a constant activity for several days of operation.

Furthermore, the etch rates of the materials exposed to KOH (i.e. SiNx, NiSi, and NiMo5) have been evaluated. This analysis indicates, together with known thicknesses of the SiNx and NiSi layers, that the device should be stable for at least 6 operating years. This lifetime is most likely limited by the SiNx layer, and its stability can potentially be further improved by using stoichiometric Si3N4 and/or a larger layer thickness.

Our future research will focus on the integration of these Si microwires with spatioselective catalyst deposition in a full solar-to-fuel device. The improved chemical resistivity of these Si microwires in alkaline electrolyte should enable the identification of a suitable combination with a higher bandgap photoanode.

ACS Paragon Plus Environment

16

Page 17 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

ASSOCIATED CONTENT Supporting Information The Supporting Information is available free of charge on the ACS Publications website at DOI: XXXX. Supporting information displaying the experimental section, additional SEM and EDX figures, cyclic voltammetry, XRD characterization, and supporting tables. Corresponding Author Prof. J. Huskens Molecular NanoFabrication, MESA+ Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE, Enschede, The Netherlands E-mail: [email protected] ACKNOWLEDGMENT This work is part of the research program of the Foundation for Fundamental Research on Matter (FOM, project 13CO12-2), which is part of the Netherlands Organization for Scientific Research (NWO). Dr. D. Dubbink is gratefully acknowledged for his insights, discussions, and expertise in characterizing the NiSi layer by XRD.

ACS Paragon Plus Environment

17

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 20

REFERENCES (1) Reier, T.; Nong, H. N.; Teschner, D.; Schlogl, R.; Strasser, P. Electrocatalytic Oxygen Evolution Reaction in Acidic Environments - Reaction Mechanisms and Catalysts. Adv. Energy Mater. 2017, 7, 1601275. (2) McCrory, C. C.; Jung, S.; Ferrer, I. M.; Chatman, S. M.; Peters, J. C.; Jaramillo, T. F. Benchmarking Hydrogen Evolving Reaction and Oxygen Evolving Reaction Electrocatalysts for Solar Water Splitting Devices. J. Am. Chem. Soc. 2015, 137, 4347-4357. (3) Carmo, M.; Fritz, D. L.; Merge, J.; Stolten, D. A Comprehensive Review on PEM Water Electrolysis. Int. J. Hydrogen Energy 2013, 38, 4901-4934. (4) Turekian, K. K.; Wedepohl, K. H. Distribution of the Elements in Some Major Units of the Earth's Crust. Geol. Soc. of Am. Bull. 1961, 72, 175-192. (5) McKone, J. R.; Sadtler, B. F.; Werlang, C. A.; Lewis, N. S.; Gray, H. B. Ni–Mo Nanopowders for Efficient Electrochemical Hydrogen Evolution. ACS Cat. 2013, 3, 166-169. (6) Kast, M. G.; Enman, L. J.; Gurnon, N. J.; Nadarajah, A.; Boettcher, S. W. Solutiondeposited F:SnO2/TiO2 as a Base-stable Protective Layer and Antireflective Coating for Microtextured Buried-junction H2-evolving Si Photocathodes. ACS Appl. Mater. Interfaces 2014, 6, 22830-22837. (7) Bae, D.; Shayestehaminzadeh, S.; Thorsteinsson, E. B.; Pedersen, T.; Hansen, O.; Seger, B.; Vesborg, P. C. K.; Ólafsson, S.; Chorkendorff, I. Protection of Si Photocathode Using TiO 2 Deposited by High Power Impulse Magnetron Sputtering for H2 Evolution in Alkaline Media. Sol. Energy Mater. Sol. Cells 2016, 144, 758-765. (8) Shaner, M. R.; McKone, J. R.; Gray, H. B.; Lewis, N. S. Functional Integration of Ni-Mo Electrocatalysts with Si Microwire Array Photocathodes to Simultaneously Achieve High Fill Factors and Light-limited Photocurrent Densities for Solar-driven Hydrogen Evolution. Energy Environ. Sci. 2015, 8, 2977-2984. (9) Boettcher, S. W.; Warren, E. L.; Putnam, M. C.; Santori, E. A.; Turner-Evans, D.; Kelzenberg, M. D.; Walter, M. G.; McKone, J. R.; Brunschwig, B. S.; Atwater, H. A.; Lewis, N. S. Photoelectrochemical Hhydrogen Evolution using Si Microwire Arrays. J. Am. Chem. Soc. 2011, 133, 1216-1219. (10) Vijselaar, W.; Westerik, P.; Veerbeek, J.; Tiggelaar, R. M.; Berenschot, E.; Tas, N. R.; Gardeniers, H.; Huskens, J. Spatial Decoupling of Light absorption and Catalytic Activity of NiMo-loaded High-aspect-ratio Silicon Microwire Photocathodes. Nature Energy 2018, 3, 185192. (11) Williams, K. R.; Gupta, K.; Wasilik, M. Etch Rates for Micromachining Processing - Part II. J. Microelectromech. Syst. 2003, 12, 761-778. (12) McKone, J. R.; Warren, E. L.; Bierman, M. J.; Boettcher, S. W.; Brunschwig, B. S.; Lewis, N. S.; Gray, H. B. Evaluation of Pt, Ni, and Ni-Mo Electrocatalysts for Hydrogen Evolution on Crystalline Si Electrodes. Energy Environ. Sci. 2011, 4, 3573-3583. (13) Shaner, M. R.; Hu, S.; Sun, K.; Lewis, N. S. Stabilization of Si Microwire Arrays for SolarDriven H2O Oxidation to O2(g) in 1.0 M KOH(aq) Using Conformal Coatings of Amorphous TiO2. Energy Environ. Sci. 2015, 8, 203-207. (14) Boubatra, M.; Azizi, A.; Schmerber, G.; Dinia, A. The Influence of pH Electrolyte on the Electrochemical Deposition and Properties of Nickel Thin Films. Ionics 2012, 18, 425-432.

ACS Paragon Plus Environment

18

Page 19 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

(15) Bhaskaran, M.; Sriram, S.; Sim, L. W. Nickel Silicide Thin Films as Masking and Structural Layers for Silicon Bulk Micro-machining by Potassium Hydroxide Wet Etching. J. Micromech. Microeng. 2008, 18, 095002. (16) Bhaskaran, M.; Sriram, S.; Holland, A. S.; Evans, P. J. Characterisation of Nickel Silicide Thin Films by Spectroscopy and Microscopy Techniques. Micron 2009, 40, 99-103. (17) Pinaud, B. A.; Benck, J. D.; Seitz, L. C.; Forman, A. J.; Chen, Z. B.; Deutsch, T. G.; James, B. D.; Baum, K. N.; Baum, G. N.; Ardo, S.; Wang, H. L.; Miller, E.; Jaramillo, T. F. Technical and Economic Feasibility of Centralized Facilities for Solar Hydrogen Production via Photocatalysis and Photoelectrochemistry. Energy Environ. Sci. 2013, 6, 1983-2002. (18) Shaner, M. R.; Atwater, H. A.; Lewis, N. S.; McFarland, E. W. A Comparative Technoeconomic Analysis of Renewable Hydrogen Production Using Solar Energy. Energy Environ. Sci. 2016, 9, 2354-2371. (19) Elbersen, R.; Tiggelaar, R. M.; Milbrat, A.; Mul, G.; Gardeniers, H.; Huskens, J. Controlled Doping Methods for Radial p/n Junctions in Silicon. Adv. Energy Mater. 2015, 5, 1401745. (20) Elbersen, R.; Vijselaar, W.; Tiggelaar, R. M.; Gardeniers, H.; Huskens, J. Fabrication and Doping Methods for Silicon Nano- and Micropillar Arrays for Solar-Cell Applications: A Review. Adv. Mater. 2015, 27, 6781-6796. (21) Elbersen, R.; Vijselaar, W.; Tiggelaar, R. M.; Gardeniers, H.; Huskens, J. Effects of Pillar Height and Junction Depth on the Performance of Radially Doped Silicon Pillar Arrays for Solar Energy Applications. Adv. Energy Mater. 2016, 6, 1501728. (22) Vijselaar, W.; Elbersen, R.; Tiggelaar, R. M.; Gardeniers, H.; Huskens, J. Photo-Electrical Characterization of Silicon Micropillar Arrays with Radial p/n Junctions Containing Passivation and Anti-Reflection Coatings. Adv. Energy Mater. 2017, 7, 1601497. (23) Westerik, P. J.; Vijselaar, W. J. C.; Berenschot, J. W.; Tas, N. R.; Huskens, J.; Gardeniers, J. G. E. Sidewall Patterning - a New Wafer-scale Method for Accurate Patterning of Vertical Silicon Structures. J. Micromech. Microeng. 2018, 28, 015008. (24) d’Heurle, F.; Petersson, C. S.; Baglin, J. E. E.; La Placa, S. J.; Wong, C. Y. Formation of Thin Films of NiSi: Metastable Structure, Diffusion Mechanisms in Intermetallic Compounds. J. Appl. Phys. 1984, 55, 4208-4218. (25) Wei, T.; Binh-Minh, N.; Renjie, C.; Shadi, A. D. Solid-state Reaction of Nickel Silicide and Germanide Contacts to Semiconductor Nanochannels. Semicond. Sci. Technol. 2014, 29, 054004. (26) Borel, J. P. La Diffusion Dans les Solides. physica status solidi (b) 1966, 13, 3-23. (27) Palik, E. D. Study of the Etch-Stop Mechanism in Silicon. J. Electrochem. Soc. 1982, 129, 2051-2059. (28) Detavernier, C.; Jordan-Sweet, J.; Lavoie, C. Texture of NiSi Films on Si(001), (111), and (110) Substrates. J. Appl. Phys. 2008, 103, 113526. (29) Wong, H. S.; Chan, L.; Sainudra, G.; Yeo, Y. C. Sub 0.1 eV Effective Schottky-barrier Height for NiSi on n-type Si (100) using Antimony Segregation. IEEE Electr. Device L. 2007, 28, 703-705. (30) Coridan, R. H.; Nielander, A. C.; Francis, S. A.; McDowell, M. T.; Dix, V.; Chatman, S. M.; Lewis, N. S. Methods for Comparing the Performance of Energy-conversion Systems for Use in Solar Fuels and Solar Electricity Generation. Energy Environ. Sci. 2015, 8, 2886-2901. (31) Chander, S.; Purohit, A.; Sharma, A.; Arvind; Nehra, S. P.; Dhaka, M. S. A Study on Photovoltaic Parameters of Mono-Crystalline Silicon Solar Cell with Cell Temperature. Energy Rep. 2015, 1, 104-109.

ACS Paragon Plus Environment

19

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 20

(32) Wen, C.; Fu, C.; Tang, J.; Liu, D.; Hu, S.; Xing, Z. The Influence of Environment Temperatures on Single Crystalline and Polycrystalline Silicon Solar Cell Performance. Sci. China Phys., Mech. Astron. 2012, 55, 235-241.

ACS Paragon Plus Environment

20