Enhancing the Mobilization of Native Phosphorus in the Mung Bean

Apr 7, 2016 - The level of resultant P uptake in mung bean increased by 10.8%. In ... P mobilization using ZnO nanoparticles in the life cycle of mung...
0 downloads 0 Views 3MB Size
Subscriber access provided by UNIV OF CALIFORNIA SAN DIEGO LIBRARIES

Article

Enhancing the mobilization of native phosphorous in mung bean rhizosphere using ZnO nanoparticles synthesized by soil fungi Ramesh Raliya, Jagadish Chandra Tarafdar, and Pratim Biswas J. Agric. Food Chem., Just Accepted Manuscript • DOI: 10.1021/acs.jafc.5b05224 • Publication Date (Web): 07 Apr 2016 Downloaded from http://pubs.acs.org on April 8, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of Agricultural and Food Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

Journal of Agricultural and Food Chemistry

Enhancing the mobilization of native phosphorous in mung bean rhizosphere using ZnO nanoparticles synthesized by soil fungi

ǁ



†, *

Ramesh Raliya , Jagadish Chandra Tarafdar and Pratim Biswas



Washington University in St. Louis, St. Louis, MO-63130, USA ǁ

Central Arid Zone Research Institute, Jodhpur – 342003, India

Manuscript ID jf-2015-05224n.R1 Submitted to Journal of Agricultural and Food Chemistry March 13, 2016

S

*Corresponding Author Phone: +1 314-936-5548. Fax: 314-935-5464. Email: [email protected]

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

2

Enhancing the mobilization of native phosphorous in mung bean rhizosphere using ZnO nanoparticles synthesized by soil fungi

3

S

4

ABSTRACT: Phosphorous (P) is a limiting factor to plant growth and productivity in almost

5

half of the world’s arable soil, and its uptake in plants is often constrained due to low solubility

6

in the soil. To avoid repeated and large quantity application of rock phosphate as a P fertilizer

7

and enhance the availability of native P acquisition by the plant root surface, in this study

8

biosynthesized ZnO nanoparticle was used. Zn acts as a cofactor for P-solubilizing enzymes

9

such as phosphatase and phytase and nano ZnO increased their activity between 84 and 108%.

10

Resultant P uptake in mung bean increased by 10.8%. In addition, biosynthesized ZnO also

11

improves plants phenology such as stem height, root volume, biochemical indicators such as leaf

12

protein and chlorophyll contents. In the rhizosphere, increased chlorophyll and root volume

13

attract microbial populations that maintain soil biological health. ICP-MS results exhibited ZnO

14

nanoparticles were distributed in all plant parts including seeds. However, the concentration of

15

Zn was within the limit of the dietary recommendation. To the authors’ knowledge, this is the

16

first holistic study focusing on native P mobilization using ZnO nanoparticles in the life cycle of

17

mung bean plants.

18

KEYWORDS: native P mobilization, ZnO nanoparticle, phosphatase, phytase, mung bean

1

19

ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29

Journal of Agricultural and Food Chemistry

20



21

Low utilization of native-P by crops and high fixation of applied P had been a major concern in

22

crop production for over three decades.1 Different approaches viz. phosphorus solubilizing

23

bacteria (PSB), phosphatase and phytase producing fungi (PPF), organic acid producing

24

microorganisms, and Vesicular-arbuscular mycorrhiza (VAM) have been tried in past to address

25

these problems.2-4 But success of these phosphorus mobilizing micro-organisms (PMM) had

26

been limited for two reasons (a) Low Soil Organic Carbon (SOC) which limit the energy supply

27

to PMM (b) High evaporation from surface soils which adversely affect the survivability of

28

PMM. Plants exude about 25 to 30% of the photosynthates through roots. These exudates consist

29

of low molecular weight amino acids, amino sugars, organic acids and polysaccharides,

30

enzymes, and can provide energy to PMM and C skeleton for synthesis of nutrient mobilization

31

and uptake.5-7 Any attempt to increase the proportion of root exudates would logically result in

32

more symbiosis with microbial community, and enhance the activity of soil nutrient mobilizing

33

enzymes. Therefore, in this study, we aim to enhance P mobilization enzyme activity, soil

34

microbial population as a result of photosynthesis in mung bean plants. In this study, we select

35

mung bean because of its nutritional value for the essential nutrients. It is well established that

36

increased activity of phosphatase and phytase enzyme play a role in native P mobilization and

37

enhance acquisition by root surface.8 To enhance P availability and uptake, various attempts has

38

been developed such as direct application of phosphate rock,9 P fertilization10 and foliar

39

application.11, 12

INTRODUCTION

40

In the recent years, many applications of nanotechnology have been explored across the

41

whole spectrum of economic sectors, including agriculture, food, forest, and the environment,

42

with demonstrated societal benefits.13 Scientific community agrees that nanoscale technology is

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Page 4 of 29

43

promising for food and agriculture, the development must be done in a sustainable manner.14 In

44

the context of P mobilization, best of our knowledge, there are only two reports, one from our

45

group in which, we reported ZnO effect on P-mobilizing enzyme secretion and gum contents in

46

clusterbean15 and recently by Zahra et al.,16 reported that the application of TiO2 and Fe3O4

47

nanoparticles increased phyto-availability of P in Lactuca sativa. In the present study, we used

48

ZnO nanoparticles for native P mobilization in the rhizosphere and acquisition by mung bean.

49

Zinc is the structural component, a cofactor of P mobilizing enzymes (phosphatases and

50

phytase) and microbial enzyme dehydrogenase.17 They are known to stabilize the enzyme

51

complexes in plants. We aim on utilizing nanoscale property of zinc for enhancing native P

52

mobilization by increasing P mobilizing enzyme activity in soil, and boosting plant metabolism

53

that would most likely lead to enhance photosynthesis and higher root exudation which in turn

54

would increase the energy supply and supply of C skeleton compounds to PMM. This approach

55

would enable in breaking of existing barriers to utilization of native P and reduce dependence on

56

conventional P fertilizers, expensive and limited natural mineral resources all over the world.

57

To synthesize zinc (in the form of ZnO) nanoparticles, a variety of chemical methods

58

are available.18, 19 However, to minimize the risk and use of harmful chemicals, we used ZnO

59

nanoparticles synthesized from the rhizospheric fungi with a fungal protein coating,15,

60

making this an environmentally benign process. Nanoparticles were applied on the foliage part

61

of mung bean to avoid direct contact with the soil ecosystem. Wang et al.,21 developed an

62

approach that could be used to deliver nanoparticles precisely by an aerosol route. The aim of

63

this study was to explore the use of biologically synthesized ZnO nanoparticles to increase

64

rhizosphere soil P availability for plant acquisition by minimizing the risk of nanoparticle

ACS Paragon Plus Environment

20

Page 5 of 29

Journal of Agricultural and Food Chemistry

65

toxicity. Physiological response, phenological impact and quantification of ZnO nanoparticle

66

biodistribution in mung bean was investigated.

67



68

Synthesis and Characterization of ZnO Nanoparticles. The ZnO nanoparticles were

69

synthesized from the soil fungus, Aspergillus fumigatus TFR-8 by following the method reported

70

earlier.15 In brief, Aspergillus fumigatus TFR-8 mycelial fungal balls (NCBI GenBank Accession

71

No. JQ675291) were grown up in broth medium (composed of 0.3 % malt extract, 1 % sucrose,

72

0.3 % yeast extract, and 0.5 % peptone). After incubation, the cell-free filtrate was obtained by

73

separating the fungal biomass using 0.45-microsize membrane filter. Using cell-free filtrate, salt

74

solution of zinc nitrate was prepared with final concentration of 0.1 mM. The biotransformed

75

product was collected periodically for characterization of particle size. Biosynthesized ZnO

76

nanoparticles were characterized by UV-Vis spectroscopy, Dynamic Light Scattering (DLS)

77

analysis (Zetasizer Nano ZS) to determine the hydrodynamic particle size that is useful to predict

78

particle size distribution in the solvent. Transmission Electron Microscopy (TEM, JEM-2100F)

79

measurements were carried out at 200 kV accelerating voltage to confirm the size and

80

morphology, and selective area electron diffraction (SAED) pattern of the synthesized ZnO

81

nanoparticles. Elemental analysis was carried out using X-Ray Photoelectron Spectrometer

82

(Physical Electronics® 5000 VersaProbe II Scanning ESCA (XPS) Microprobe). Crystal nature

83

of the particles were characterized by X-Ray Diffraction (Bruker D8).

84

Characterization of Experimental Soil and Plant Growth. The experimental soil was

85

collected from farm field of Central Arid Zone Research Institute. The soil was air dried and

86

sieved through a 2 mm mesh prior to experimental use. The soil type was classified as sandy-

87

loam soil, in which percentage of sand, slit and clay of 85.6%, 6.9% and 7.5% respectively. The

MATERIAL AND METHODS

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

88

organic matter of the soil was 0.3%. Therefore, organic farm manure was mixed with soil (1:10)

89

before use. Resulting soil properties were: pH 8.1±0.2, Zinc 0.6 µg/g, nitrogen 462±18.5 mg/kg,

90

P 733±23.5 mg/kg and potassium 695±21.9 mg/kg. Bacteria, fungi and actinomycetes counts

91

(colony forming unit; CFU/ml) of 12×10-6, 8×10-4 and 6×10-5 correspondingly.

92

Five seeds of mung bean were sown in each pot, was thinned to three at a later stage of

93

germination. The pots were placed (in a random block design and exchanged their position every

94

alternate day to avoide environmental impact) in a greenhouse with 16h photoperiod, 34/25 ºC

95

day/night temperature, 65% relative humidity and 360 µmol m-2S-1 light intensity. Each

96

treatment including control and bulk ZnO was set in five replicates. No additional fertilizer and

97

pesticides were used through the life cycle. Alternate day, watering was carried out.

98

Nanoparticles Exposure to Mung bean Foliage. Two weeks old mung bean plants’ foliage was

99

exposed with ZnO nanoparticles and bulk ZnO. Concentration of ZnO suspension was 10 mg/L,

100

found an optimum in screening experiment. The solution was homogenized by sonication for 45

101

minutes before use. A total of 25 mL suspension, each of bulk and nano ZnO was sprayed on

102

each plant by an atomizer, generate 250-300 µ size droplets. Samples were collected after 14

103

days of treatment for phenotypic analyzes, plant – soil, biochemical analyzes and rhizosphere

104

microbial population count.

105

Plant-Rhizosphere Response to ZnO Nanoparticles.

106

Phenotype. Plant phenotype is a comprehensive assessment of growth and development. In this

107

study, plant height, root length, root area, root diameter and number of root nodules were

108

recorded. After 28 days, plants of each treatment was uprooted, stems were cut at the soil

109

surface, and height were measured using meter scale. Roots were carefully shaken to remove

110

excess soil, and clumps of soil trapped between roots were taken out. The roots were transferred

ACS Paragon Plus Environment

Page 6 of 29

Page 7 of 29

Journal of Agricultural and Food Chemistry

111

to a beaker and cleaned by gentle shaking of the beaker after adding 0.2 mM CaCl2 solution. The

112

roots were taken out of the soil extract and processed further for root length, area, and diameter

113

measurement using Delta T-Scan Software (Delta-T Devices, UK).

114

Representative leaves were used further for protein and chlorophyll measurement.

115

Rhizospheric soil sample of each treatment was taken out (100 g) from the bulk soil of the pots

116

in which plants were grown, as well as from absolute control pot in which no plants were grown

117

and frozen at 4 °C for further analysis.

118

Rhizosphere Soil Enzyme. All the studied enzyme activities were calculated based on the

119

changes of absorbance and Beer’s Law. In this study, P mobilizing and microbial activity

120

enzymes, as an indicator of biological activity in rhizospheric soil were investigated.

121

Acid and Alkaline Phosphates Activity. The acid and alkaline phosphatase was assayed by the

122

method reported earlier.22 In short, 1 g of sieved soil (< 2 mm) mixed in 0.2 mL of toluene, 4 mL

123

of p-nitrophenyl phosphate (PNP) solution prepared in acetate buffer (pH 4.5, for acid

124

phosphatase) and borax-NaOH buffer (pH 9.2, for alkaline phosphatase). Further, samples were

125

incubated at 30 °C in the dark for 1 h, followed by 1 mL of 0.5 M CaCl2 and 4 mL of 0.5 M

126

NaOH were added. Swirled the test tube for a few seconds, and filtered the soil suspension

127

through a Whatman no 42 filter paper. The yellow color intensity of the filtrate was measured at

128

420 nm wavelength. The p-nitrophenol content of the filtrate was calculated from the standard

129

curve obtained with standards containing 0, 10, 20, 30, 40 and 50 µg of p-nitrophenol.

130

Phytase Activity. Phytase activity was assayed by Ames’ method.23 Two gram of sieved soil

131

sample mixed with 4 mL of 100 M sodium acetate buffer (pH 4.5), and 1 mL of 1µM sodium

132

phytate. The sample was incubated at 37° C for 1 h in the dark. After 1 h incubation, the reaction

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

133

was terminated by the addition of 0.5 mL of 10% TCA. Liberated inorganic P was analyzed by

134

spectrophotometer analyzes at 660 nm using chlorostannous reduced molybdophosphoric

135

hydrochloric acid. One unit of phytase activity was defined as the amount of enzyme, which

136

liberated 1 µM Pi (inorganic P) per second.

137

Dehydrogenase Activity. Dehydrogenase activity was measured in soils immediately after soil

138

sampling that was assayed by the method of Tabatabai.24 In summary, 1 g soil mixed with, 0.2

139

mL of 3% 2,3,5-Triphenyl-2H-tetrazolium chloride (TTC) and 0.5 mL of 1% glucose. After a

140

gentle shake, the sample was incubated for 24 h at 37 °C in dark, followed by addition of 10 mL

141

of methanol. The sample was further incubated at 4 °C for 3 h. The production of

142

triphenylformazan (TPF) was determined by measuring absorbance at 485 nm.

143

Microbial Population Count. Microorganisms play an essential role in maintaining biological

144

soil health. In this study, foliar application of ZnO nanoparticle effect on rhizospheric bacteria,

145

fungi and actinomycetes populations were assessed. Serial dilution technique25 was used to

146

count microbial CFU.

147

Plant P. Grinded and sieved (2 mm size) plant samples were digested using a tri-acid mixture

148

(HNO3: H2SO4: HClO4; 9:2:1) as described by Jackson.26 To estimate 10 mL of digested plant

149

material was diluted with 25 mL DI water and add 15 mL added HNO3, ammonium molybdate

150

(5%) and ammonium metavanadate (0.25%) in equal proportions (1:1:1). Phosphorous was

151

quantified by measuring absorption at 485 nm and calculated according to the formula described

152

elsewhere.27

153

Soluble Leaf Protein. Total soluble proteins were quantified using the method suggested by

154

Lowry et al.28 with certain modification. In short, fresh leaves were crushed in 5 mL of 10%

ACS Paragon Plus Environment

Page 8 of 29

Page 9 of 29

Journal of Agricultural and Food Chemistry

155

trichloroacetic acid to precipitate the total soluble proteins and purified using centrifugation at

156

8×103 g for 10 minutes at 4 °C. In this method, folin reagent (a mixture of sodium tungstate,

157

molybdatye and phosphate) together with a copper sulfate mixed with isolated protein. The

158

resultant, blue-purple color produced due to the reduction of phosphomolybdotungstate to

159

hetero-polymolybdenum blue by the copper catalyzed the oxidation of amino acids, was

160

quantified by absorbance at 660 nm using a spectrophotometer.

161

Chlorophyll Pigment Content. To measure the chlorophyll content, plant leaves were collected

162

on the 28th day and washed with tap water followed by DI water. One gram of fresh plant leaves

163

were cut into small pieces and dipped in absolute acetone for 12h under dark. After incubation,

164

the extracted chlorophyll was recorded at 661.6 nm, 664.8 nm, and 470 nm wavelength. Total

165

chlorophyll content was calculated according to the formula described elsewhere.29

166

Biodistribution and Transport of ZnO Nanoparticles. To investigate nanoparticles movement in

167

mung bean plant, quantitative estimation was carried out by ICP-MS by following the sample

168

digestion method describing elsewhere.21 Anatomical study of root, stem, leaf and mung bean

169

seed was carried out by TEM. Root, stem, and leaf were collected on the 28th day, whereas, seeds

170

were collected at 78th day. Small pieces of the tissue was immersed in 2.5% phosphate buffered

171

glutaraldehyde for 4 h followed by rinsed with 0.1 M phosphate buffer and subjected to

172

secondary fixation using 2% osmium tetroxide. Dehydration was carried out in a series (30 –

173

100%) of five ethanol washes. The tissues were then infiltrated with a mixture of epoxy resin

174

and propylene oxide as a transitional solvent, followed by complete infiltration with resin.

175

Finally, the resin was polymerized in the oven at 60 ⁰C and the of plant tissues were ultra-

176

sectioned using a microtome, followed by staining of sections with 4% uranyl acetate before

177

imaging by TEM at 120 KV.

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

178

Statistical analysis.

The data obtained from pot and field experiments were subjected to

179

Statistical analysis by the analysis of variance method.30 The significance of different sources of

180

variance was tested by “Error Mean Square” method of Fisher’s at probability level of 0.05 for

181

appropriate degree of freedom. The standard of means (SEM ±) and the value of least

182

significance difference (LSD) were calculated as described by Gomez and Gomez.31

183 184



185

Physico-chemical Characterization of ZnO Nanoparticles. The morphology of ZnO

186

nanoparticles was investigated by TEM and HR-TEM analyzes. Nearly spherical ZnO

187

nanoparticles of 22.4±1.8 nm were more or less homogenously distributed as revealed by TEM

188

micrograph (Figure. 1 A).

189

agreement with a hydrodynamic diameter (inset of Figure. 1A) of the particles dispersed in DI

190

water. Aqueous dispersion of ZnO nanoparticles was fairly stable up to 24 h under experimental

191

condition. The stability of particles is possible due to in situ corona formation by fungal

192

extracellular protein used in synthesis procedure.15 Negative surface zeta potential (-31.4 mV) of

193

the particles play a role in nano-biointeraction with plant cell and keep them radially dispersed

194

due to Coulomb repulsion.32 Crystal property of synthesized ZnO nanoparticles can be revealed

195

by plane structure observed in HR-TEM micrograph, which is further supported by SAED

196

pattern (Figure. 1B). In addition, crystal nature of particles were confirmed by X-Ray diffraction

197

peaks (Fig. S1), match with characteristic zincite crystal plane.33 The chemical composition of

198

the nanoparticles was determined by XPS analyzes (Figure. 2), where characteristic peaks for Zn

199

(2p1 and 2p3) and O (1s) were observed. From the higher resolution XPS spectra of Zn 2p1 and

200

2p3, it can be seen that the photoelectron peak of the sample appears at the binding energy of

RESULTS AND DISCUSSION

The physical diameter of synthesized nanoparticles is in well

ACS Paragon Plus Environment

Page 10 of 29

Page 11 of 29

Journal of Agricultural and Food Chemistry

201

1043.6 eV and 1020.5 eV. Dominated peak of Zn 2p3 at 1020.5 and oxygen at 529.2 is

202

associated with the binding of Zn2+ in ZnO zincite structure.34 Low-intensity carbon peak

203

observed in the XPS survey spectrum is due to substrate used to mount sample powder for the

204

XPS analyzes.

205

The impact of ZnO Nanoparticles on the Physiological Growth. Zinc is a known as an

206

essential micronutrient for all plants.35 The bulk counterpart either zinc sulfate or zinc oxide has

207

been extensively applied in the field to abate Zn deficiency.36 To avoid the sulfate interference,

208

in this study, we used bulk ZnO to compare the effect of ZnO nanoparticles. The concentration

209

of applied nanoparticles were 10 mg/L, an optimal concentration of any micronutrient element

210

for plant growth.37 Above the concentration limit, it imparts toxicity to the plants. Both, bulk

211

and nano ZnO were tested for mung bean plants and several growth parameters were checked

212

thereafter. Figure 3 shows that both bulk and nano ZnO had a significant positive effect in terms

213

of stem height and root length. However, no significant difference were observed in root

214

diameter and nodule with respect to control. Stem height of plants treated with ZnO

215

nanoparticles was observed 32.8% higher than control. Similarly, root length, area, and nodule

216

was increased by 29.9%, 53.3% and 58.9%, respectively. Plants phenotypic characteristic is

217

crucial to determine plant biomass and extensive effect on root directly co-relate with water and

218

nutrient absorption by plants. An important feature of legume root, is nodulation, a site for

219

nitrogen fixation bacterial species.38

220

The response of Zno Nanoparticles Mung bean Plants to Soil Enzyme of Native P

221

Mobilization in Rhizosphere and Soil Biological Health. A large portion of the P in soil can

222

exist in an organic form, must be converted to inorganic P before it can be utilized by plants.39

223

The cycling of organic P and externally applied P fertilizer has a large impact on P availability in

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Page 12 of 29

224

agricultural ecosystem.40 Phosphorous is very stable element in soils because they are very

225

reactive with other compounds and bound as ester phosphate such as Ca-P, Al-P or Fe-P, become

226

increasingly insoluble in the soil.1 Resultant P is unavailable to plants either due to runoff with

227

excess rainfall or due to complex structure of P with other compounds. Phosphorous is taken up

228

by plants wither in the form of H2PO4- or HPO42-. The mineralization of organic P is mediated by

229

phosphatase and phytase enzyme, also known as P mobilizing enzymes that hydrolyzes C-O-P

230

ester bonds.6, 40 Plants roots and rhizospheric microbes, produces or secrets phosphatases and

231

phytase.41 Phosphatase and phytase enzyme play an important role in acquisition of P by plant

232

roots and a significant factor of nutritional efficiency.5,

233

enzymes including phytase and phosphatase that assist in performing reaction to mobilize native

234

P.17,

235

alkaline) and phytase as a result of ZnO nanoparticle exposure to plants is well complement with

236

the previous studies as discussed above. ZnO nanoparticles of 23 nm having an improved

237

catalytic property than bulk counterpart, significantly increased acid phosphatase (98.07%),

238

alkaline phosphatase (93.02%), phytase (108%) and dehydrogenase (84.21%) activity in

239

rhizosphere soil with respect to control (Figure 4). Although bulk ZnO also increased the

240

enzyme activity but almost half of the nanoparticle efficiency, because of several reason such as

241

(a) availability/internalization (b) surface zeta potential (c) surface area to volume size ratio and

242

(d) intra cellular transport and reach out to various plants parts and subsequently to rhizospheric

243

zone. Increase phosphatase and phytase activity is also complement with an increased in P

244

acquisition in plants by 10.85% in nano ZnO treated plants and 2.04% in bulk ZnO treated plants

245

(Figure. 5). Results of increased availability in soil and acquisition of P by plants due to nano

246

ZnO can also be verified from increased rhizospheric zone by significantly increased root

24

42-44

Zinc is the cofactor for various

In this study, experimental results of increased activity in soil phosphatase (acid and

ACS Paragon Plus Environment

Page 13 of 29

Journal of Agricultural and Food Chemistry

247

volume (Figure. 3) and soil microbial (fungi, bacteria and actinomycetes) population (Figure. 6)

248

and dehydrogenase enzyme activity (Figure. 5), an indicator of microbial activity in soil.

249

Enhanced microbial population help to maintain soil structure and soil biological health, an

250

important phenomenon for various nutrient cycle.

251

Biodistribution and Phytoaccumulation of Zn in Exposed Plant. ICP-MS data showed the

252

presence of Zn in leaf, stem, root and shoot after foliar treatment with 10 mg/kg ZnO

253

nanoparticles and its bulk counterpart (Figure. 7). The concentration of Zn in mung bean tissues

254

followed the sequence leaf > stem > seed > root. Trends of Zn accumulation was similar for nano

255

and bulk ZnO. The presence of Zn in mung bean seed indicate the possibility of introducing Zn

256

ions/ZnO nanoparticles into the food chain. However, the amount of Zn (