NOVEL NANOPOROUS gold material prepared
by removing silver from a gold-silver alloy selectively catalyzes production of an industrially important compound under mild conditions, according to a team of researchers in Germany and the U.S. (Science 2010, 327, 319). The study further broadens gold’s rapidly growing repertoire of catalytic reactions. It also could help efforts to replace industrial chemical processes with less hazardous and “greener” ones. In just the past few years, gold’s reputation as an inert noncatalytic metal has undergone a complete makeover, as several research groups have found a number of reactions—including various types of oxidations—that are catalyzed by gold in nanostructured form. Nonetheless, commercial applications have been impeded by gold’s slowness to dissociate oxygen—a key step in oxidations—and the tendency of nanoparticles to agglomerate under typical reaction conditions. That process quickly shortens the lifetimes of supported catalysts such as gold, which is usually dispersed on the surfaces of solid oxides. The new catalyst may provide a way around those problems. By treating a gold-silver alloy with nitric acid, the researchers formed a stable, unsupported monolithic gold catalyst composed of a three-dimensional network of nanoscale ligaments. The team, which includes
CHEMOTAXIS Acidic droplet solves maze In the scientific world, solving mazes used to be the dominion of experimental psychologists. Now chemists are getting in on the action, but they’ve swapped the traditional lab rat for a drop of liquid. A team led by Northwestern University chemistry professor Bartosz A. Grzybowski has shown that an acidic droplet can successfully navigate a complex maze (J. Am. Chem. Soc., DOI: 10.1021/ja9076793). “I personally find most exciting that such a simple system can exhibit apparently
‘intelligent’ behavior,” Louisiana State University chemistry professor John A. Pojman comments. “This approach may be useful as a pumping method for microfluidics or a way to convert chemical energy to mechanical motion in small devices. I am eager to see if they can generalize it to other types of gradients,” he says. The droplet, composed of 2-hexyldecanoic acid in either dichloromethane or mineral oil, travels several centimeters through a maze with a pH gradient. The pH is high
WWW.CEN-ONLINE.ORG
at the maze entrance and low at its exit. Once in the maze, the droplet travels toward the lower pH, and in doing so, Grzybowski notes, it always finds the shortest path through the maze. Acid-base chemistry and surface tension are what drive the drop. “The interfacial reaction between the acid in the drop and the base in the channel creates convection rolls or ‘swirls,’ ” Grzybowski explains. “The fluid mechanics plays out such that the swirl facing lower pH is more pronounced, and so the drop is effectively pushed in this direction.”— BETHANY HALFORD
9
JANUARY 1 8, 20 10
Treatment with acid converts a silver-gold alloy into the nanoporous gold catalyst shown in this SEM image.
MAZE MANEUVERS
A droplet travels through a maze with a pH gradient. In the overlaid image, black drops show early times, red ones are later. Watch the droplet solving the maze at C&EN Online.
J. AM. CHEM. SOC.
MATERIALS: Precious metal in nanostructured form mediates oxidations selectively
Arne Wittstock, Volkmar Zielasek, and Marcus Bäumer of Bremen University, in Germany; Harvard University’s Cynthia M. Friend; and coworkers, found that at low temperature and 1 atm of oxygen, the nanoporous material catalyzes oxidative coupling of methanol to yield methyl formate. That compound is used commercially as a solvent and blowing agent and as a precursor to formic acid and dimethylformamide. It is prepared industrially in a process that uses carbon monoxide, methanol, caustic base, and metallic sodium. At room temperature, the gold-catalyzed reaction is 100% selective but runs sluggishly, the team reports. Raising the temperature to just 80 °C speeds up the reaction, increases methanol conversion severalfold, and only slightly reduces selectivity—producing about 3% CO2, according to the researchers. They note that the catalyst remained stable and active during tests that ran continuously for periods ranging from days to weeks. In addition, on the basis of experiments comparing a series of de-alloyed samples, the team concludes that a small fraction of residual silver enhances the gold catalyst’s reactivity by promoting oxygen dissociation. “It is tempting to assume” that results from this type of gold catalyst with residual silver may be better than those from pure gold catalysts used before in oxidation reactions, Claus H. Christensen of Danish catalyst manufacturer Haldor Topsøe and Jens K. Nørskov of the Technical University of Denmark note in a commentary about the work. Further research is needed, but this advance may move green gold catalysis closer to industrial applications, they say.—MITCH JACOBY AR N E WIT TSTO CK /BR EM EN U
FINDING GREEN IN GOLD