Fundamental Insight into the Hierarchical Engineering of

modal pore topologies realized via facile convective co-assembly of ... supports, conductive glass), bridging processing & applications o Decoupli...
1 downloads 23 Views 532KB Size
Fundamental Insight into the Hierarchical Engineering of Nanoparticulate and Templated Porous Films for Molecular Separations Mark A. Snyder, Department of Chemical Engineering, Lehigh University, Bethlehem, PA 18015 Motivation: The ability to synthesize ultra-thin porous inorganic films with tunable, highly ordered pore topologies holds implications spanning molecular selectivity and flux as it relates to membrane-based gas, vapor, and liquid separations to efficient electrode technologies in solar cells. Goal: Establish a facile strategy for simultaneously tuning pore size and film thickness of porous inorganic films, the latter to the level of just tens to hundreds of nanometers by decoupling template assembly from chemistries of film formation.

Versatile C sources: Phenol-formaldehyde, resorcinol, furfuryl alcohol, sucrose, glucose,…

Robust substrate transfer

C film

Porous SS C film

Electrodes

Facile film morphology and pore topology control

Membranes

~130nm

Multi-step AND ‘One-pot’ hardtemplating for robust film formation

250nm

1µm

200nm

100nm

FTO-glass

500nm

Outcomes: o Realization of defect-free, mechanically flexible porous carbon and scaffolded zeolite films with ordered mesopore and mesopore-supported microporous thin films scalable to tens of nanometers in thickness o Novel, multi-modal pore topologies realized via facile convective co-assembly of binary nanoparticle solutions o Robust film transfer among substrates (e.g., porous supports, conductive glass), bridging processing & applications o Decoupling of template and film formation enabling versatility of carbon source as an additional independent handle for tuning film properties (e.g., molecular sieving, conductivity, mechanical robustness, etc.) o Realization of ‘one-pot’ hard-templating of three-dimensionally ordered mesoporous powders and thin films