Subscriber access provided by READING UNIV
Article
In-Situ Observation of Light Illumination-Induced Degradation in Organometal Mixed-Halide Perovskite Films Rui-Peng Xu, Yanqing Li, Teng-Yu Jin, Yue-Qi Liu, Qin-Ye Bao, Conor O’Carroll, and Jian-Xin Tang ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b18389 • Publication Date (Web): 01 Feb 2018 Downloaded from http://pubs.acs.org on February 2, 2018
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 34 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Materials & Interfaces
In-Situ Observation of Light Illumination-Induced Degradation in Organometal Mixed-Halide Perovskite Films
Rui-Peng Xu,1 Yan-Qing Li,1,* Teng-Yu Jin,1 Yue-Qi Liu,1 Qin-Ye Bao, 2,* Conor O’Carroll,3 and Jian-Xin Tang1,*
1
Institute of Functional Nano & Soft Materials (FUNSOM), Jiangsu Key Laboratory for Carbon-Based Functional Materials & Devices, Joint International Research Laboratory of Carbon-Based Functional Materials and Devices, Soochow University, Suzhou 215123, China. E-mail:
[email protected],
[email protected] 2
Key Laboratory of Polar Materials and Devices, Ministry of Education, East China Normal
University,
200241,
Shanghai,
P.R.
China.
E-mail:
[email protected] 3
School of Physics, Trinity College Dublin, The University of Dublin, Dublin 2, Ireland.
* Corresponding authors. E-mail addresses:
[email protected] (J.X. Tang),
[email protected] (Y.Q. Li),
[email protected] (Q.Y. Bao)
1 ACS Paragon Plus Environment
ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ABSTRACT Organometal mixed-halide perovskite materials hold great promise for nextgeneration solar cells, light-emitting diodes, lasers as well as photodetectors. Except for the rapid progress in efficiency of perovskite-based devices, the stability issue over prolonged light illumination has severely hindered their practical application. The deterioration mechanism of organometal halide perovskite materials under light illumination has seldom been conducted to date, which is indispensable to the understanding and optimization of photon harvesting process inside perovskite-based optoelectronic devices. Here, explicit degradation pathways and comprehensive microscopic understandings of white light-induced degradation have been put forward for two organometal mixed-halide perovskite materials (e.g., MAPbI3-xClx and MAPbBr3-xClx) under high vacuum conditions. In-situ compositional analysis and real-time film characterizations reveal that the decomposition of both mixed-halide perovskites starts at the grain boundaries, leading to the formation of hydrocarbons and ammonia gas with the residuals of PbI2(Cl), Pb or PbClxBr2-x in the films. The degradation has been correlated to the localized trap states that induce strong coupling between photo-excited carriers and the crystal lattice.
KEYWORDS: organometal halide perovskites, in-situ characterization, light illumination, electronic structures, degradation
2 ACS Paragon Plus Environment
Page 2 of 34
Page 3 of 34 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Materials & Interfaces
1. INTRODUCTION Organometal halide perovskites have been attracting tremendous attention in optoelectronic devices due to their excellent optical and electrical properties, such as large absorption coefficients, broad wavelength tunability, long carrier diffusion length, and ambipolar charge transport characteristics.1-3 These excellent properties enable perovskites to be promising for applications in solar cells,4-7 light-emitting diodes (LEDs),8-10 lasers,2 photodetectors,11 etc. Among various perovskite materials, methylammonium lead mixed-halide (MAPbX3, MA=CH3NH3, X = Cl, Br, or I) with two of Cl-, Br- and I- halide anions (e.g., MAPbI3-XClx) are widely used as solar energy harvesters in the field of solar cells, since their bandgap can be continuously tuned over a large range of wavelengths and their carrier diffusion length can be greatly enhanced with the substitution of halide anions, delivering good device performance.12,13 Therefore, the development of MAPbX3-based solar cells has rapidly intensified with a power conversion efficiency beyond 22%.14-16 Besides excellent photovoltaic properties, MAPbX3, particularly MAPbBr3-XClx perovskites holds great promise in the fabrication of high-efficiency LEDs due to the desirable features such as direct-bandgap nature and high photoluminescence quantum efficiencies.17-19 Despite tremendous process in device efficiency that is comparable even with that of the conventional silicon-based ones, operational lifetime and long-term stability of MAPbX3 perovskite-based optoelectronic devices are still low,20 which is the current benchmark for practical applications. Indeed, MAPbX3 perovskites are sensitive to moisture,21 oxygen,22,23 heat,24 light,25 and ion migration,26,27 which could cause the severe property degradation and thus the stability deterioration. Worse still, these factors not only work alone, but also intertwine with each other, thus doing
3 ACS Paragon Plus Environment
ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
harm to the film property and device performance. For instance, it was found that moisture could induce the formation of hydrated intermediate phases in MAPbI3 (e.g., MAPbI3·H2O and (MA)4PbI6·2H2O), which would ultimately decompose to HI, CH3NH2 and PbI2 as observed in a process typically accelerated by heat and light.28,29 Exposure of MAPbI3 films to light and oxygen could lead to the formation of reactive superoxide species O2-, which can deprotonate the MA cation and decompose the photo-excited perovskite to PbI2, H2O, CH3NH2, and I2.30 Clearly, these multiple factors make the stability issue extremely complicated, and further blur the mechanism of how single factor affects the decomposition of MAPbX3 perovskites. Therefore, a comprehensive understanding of the degradation pathway under one sole factor and the corresponding degradation mechanism for MAPbX3 perovskites has undoubtedly become the most imperative issue for future development of more robust perovskite materials and devices. The degradation factors of moisture, oxygen and heat can be circumvented through optimized encapsulation schemes, while the issue of stability against light illumination is inevitable for MAPbX3 perovskite-based materials and devices (e.g., solar cells and photodetectors). It was initially believed that MAPbI3 films only degraded in the presence of both light and oxygen.31 Latterly, several reports shown that full-spectrum light soaking in an inert atmosphere or under primary vacuum conditions will also induce performance degradation in MAPbI3 perovskite solar cells.25,32-34 It has demonstrated that high-energy laser irradiation will cause the partial decomposition of MAPbI3 films with the appearance of a new metallic Pb component, while the decomposition will achieve a saturation level after several hours of continuous illumination.35 Recent work further revealed that significant changes of electronic and chemical structures of perovskites films occur upon white-light
4 ACS Paragon Plus Environment
Page 4 of 34
Page 5 of 34 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Materials & Interfaces
illumination with a formation of PbI2 defects.36 Regardless of these preliminary results on pure MAPbX3 perovskites, it is indispensable to unravel the exact process and pathways of light illumination-induced degradation in mixed-halide MAPbX3 perovskites with dual halide anions so as to explain the complex dynamic phenomena and ultimately obtain photo-stable perovskite optoelectronic devices. In this regard, only few pertinent studies have been conducted to date. Here, we investigate the dynamic degradation process and explore the underlying mechanism of two mixed-halide perovskite films (i.e., MAPbI3-XClx and MAPbBr3XClx)
under white-light illumination in an ultrahigh vacuum (UHV) environment
(base pressure