Cost-effective Vertical Carbon Nanosheets/Iron-based Composites as Efficient Electrocatalysts for Water Splitting Reaction Yao Zhang, Kun Rui, Zhongyuan Ma, Wenping Sun, Qingqing Wang, Peng Wu, Qiao Zhang, Desheng Li, Min Du, Weina Zhang, Huijuan Lin, and Jixin Zhu Chem. Mater., Just Accepted Manuscript • DOI: 10.1021/acs.chemmater.8b01699 • Publication Date (Web): 27 Jun 2018 Downloaded from http://pubs.acs.org on June 27, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 9 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials

Cost-effective Vertical Carbon Nanosheets/Iron-based Composites as Efficient Electrocatalysts for Water Splitting Reaction Yao Zhang†, ‡, Kun Rui†, §, ‡, Zhongyuan Ma†, Wenping Sun§, *, Qingqing Wang†, Peng Wu†, Qiao Zhang†, Desheng Li†, Min Du†, Weina Zhang†, Huijuan Lin†, Jixin Zhu†, * †

Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (NanjingTech), 30 South Puzhu Road, Nanjing 211816, China

§

Institute for Superconducting and Electronic Materials, Australian Institute for Innovative Materials, University of Wollongong, NSW 2522, Australia ABSTRACT: Developing low cost and highly active catalysts is vital to achieve efficient electrochemical water splitting for hydrogen production, which is considered as a very promising approach for renewable energy storage. Herein, an efficient and cost-effective electrode architecture constructed by vertically aligned carbon nanosheets (VCNs) and iron oxyhydroxide/nitride (VCNs@FeOOH//VCNs@Fe4N) are designed and synthesized for water splitting in alkaline medium. Benefiting from the highly exposed active sites, accelerated mass and electron transport, and synergistic effect of multiple components, the composite electrodes deliver unprecedented catalytic performance with high activity and excellent durability. The VCNs@FeOOH composite electrode exhibits an overpotential of as low as 179 mV at 10 mA cm-2 for oxygen evolution reaction (OER), while VCNs@Fe4N shows a low overpotential of 172 mV for hydrogen evolution reaction (HER) at 10 mA cm-2. More significantly, a full electrolyzer cell with VCNs@Fe4N as the cathode and VCNs@FeOOH as the anode exhibits an appealing operation voltage of 1.6 V at 10 mA cm-2 with superior durability. The present results provide new insight into designing robust catalysts towards practical water splitting devices and metal-air batteries.

INTRODUCTION Due to the rapid growth of fossil fuel consumption and corresponding environmental degradation, developing green and renewable energy technologies such as fuel cells, rechargeable metal-air batteries and water splitting devices is of paramount importance.1-10 Among them, electrochemical water splitting coupled with efficient hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is widely regarded as a promising technology.11-17 Therefore, enormous efforts have been devoted to searching for highly efficient and robust electrocatalysts for the practical operation of overall water splitting.18-22 To date, noble metal-based catalysts remain the most efficient catalysts reported, e.g., Pt for HER, IrO2 and RuO2 for OER, whose scarcity and high cost considerably render water splitting of low economic appeal.23, 24 In this context, it is urgent to develop sustainable, nonnoble materials to effectively catalyze OER and HER in alkaline solutions. Over the past few years, transition metal compounds including oxides, sulfides, phosphides, etc., have emerged as alternative electrocatalysts.25-29 Specifically, iron (Fe)-based materials have been receiving increasing interest as promising electrocatalysts for both OER and HER owing to advantageous features of natural abundance, low cost and environmental friendliness.30, 31 However, application of Fe-based catalysts with poor in-

trinsic electrical conductivity and mass-transfer ability deserve more exploration, which were considered to be less electrocatalytically active previously.32, 33 Recently, considerable efforts have been focused on the direct growth of nanostructured catalysts on current collector as self-supported electroactive electrodes without using Nafion or other polymeric binders.34-37 Despite distinct advantages of enhanced electrical contact, enlarged active sites exposure, favored mass transport, etc., rational design of three-dimensional (3D) composite electrodes with desirable building blocks and controlled composition remains a critical challenge. As well known, twodimensional (2D) nanosheet materials with atomic thickness have shown great potential for electrocatalysis benefiting from their dramatically increased surface/volume ratio and abundant active sites, making them ideal as subunits in integrated 3D electrodes.38-42 In particular, vertically aligned 2D carbon architectures manifest superior chemical stability and good electrical conductivity, which is highly desirable to act as a backbone by integrating Fe-based catalysts for the construction of a 2D heterojunction.18, 42-44 Previously, OER performance of FeOOH was improved by constructing composite structures with Co, CeO2, CNTs with one-dimensional (1D) configurations on conductive substrates.45-47 Moreover, Fe-based nitrides derived from FeOOH also hold great potential for HER electrocatalysis with higher electrical conductivity.31, 48

ACS Paragon Plus Environment

Chemistry of Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nevertheless, facile incorporation of vertically aligned carbon nanosheet arrays with Fe-based oxyhydroxides/nitrides as self-supported catalysts has not been reported, to the best of our knowledge. Herein, vertically aligned carbon nanosheets iron-based composite architectures were synthesized by a facile approach suitable for large-scale production, and were demonstrated to be efficient electrocatalysts for water splitting in alkaline medium. The vertically aligned carbon nanosheets (VCNs) with nitrogen doping serve as highly conductive backbones to provide reliable electron transport for Fe-based catalysts. The strong bonding between the active materials (FeOOH/Fe4N) and VCNs also endows the composite electrodes with substantial stability. The VCNs@FeOOH and VCNs@Fe4N exhibited superior OER and HER catalytic activity in alkaline medium, respectively. Notably, the VCNs@FeOOH//VCNs@Fe4N couple also delivered exceptional performance in an alkaline electrolyzer for overall water splitting.

Page 2 of 9

and Figure S1, interconnected carbon nanosheets were aligned vertically on the surface of nickel foam. A highmagnification SEM image (Figure 1b) further revealed that these well-defined thin nanosheets with a thickness of 3-5 nm have a lateral dimension of up to hundreds of nanometers. These porous 2D arrays supported on the 3D macroporous nickel foam substrate possessed superior advantages due to high porosity and surface area, forming a large electrode-electrolyte interface and facilitating efficient charge transfer as well as rapid mass diffusion without any block of binder. According to the X-ray diffraction (XRD) result (Figure S2), one peak located at around 25.6 ° can be ascribed to the (002) peak of graphitic carbon.49, 50 Three well-resolved peaks at 1369, 1583, and 2721 cm-1 in the Raman spectrum corresponding to the D-band, G-band and 2D-band, respectively, further certified the formation of graphitic carbon nanosheets composed of layer graphene (Figure S3).51

RESULTS AND DISCUSSION

Scheme 1. Schematic illustration for the formation of vertically aligned carbon nanosheets (VCNs) and composite electrodes for overall water splitting.

The synthesis process of VCNs@FeOOH and VCNs@Fe4N mainly involves a room-temperature interfacial reaction followed by proper thermal treatment as illustrated in Scheme 1. First, VCNs were synthesized using our previously reported salt-templating method.8, 49 Specifically, ionic liquid (IL) carbon precursor 1-Ethyl-3methylimidazolium dicyanamide (Emim-dca) and salt mixture (ZnCl2/KCl) were thoroughly ground and uniformly casted to a pretreated commercial nickel foam. After carbonization under inert gas atmosphere at 900 °C for 3 h, VCNs were obtained strongly adhereing on nickel foam. Herein, VCNs were further employed as an ideal 3D conductive substrate with delicate 2D building blocks to support Fe-based catalytically active species. The in situ growth of FeOOH nanosheets on VCNs (VCNs@FeOOH) was then achieved by immersing VCNs in ferric nitrate solution at room temperature. Furthermore, VCNs@FeOOH was mildly transformed to VCNs@Fe4N via thermal treatment in NH3 flow at 500 °C for 2 h. The morphology and microstructure information of all samples were investigated by field emission scanning electron microscopy (FE-SEM). As seen from Figure 1a

Figure 1. Typical field emission scanning electron microscopy (FESEM) images. (a-b) Nitrogen doped vertically aligned carbon nanosheets (VCNs) on nickel foam. (c-d) Carbon nanosheets with FeOOH composites (VCNs@FeOOH) and (e-f) carbon nanosheets with Fe4N composites (VCNs@Fe4N).

Through a facile and mild interfacial reaction, VCNs@FeOOH composite nanosheets arrays were vertically grown on the 3D nickel foam substrate. No significant differences were observed between the FESEM images of VCNs and VCNs@FeOOH as evidenced in Figure 1c and Figure S4, indicating the uniform distribution of FeOOH nanosheets over the entire VCNs. At a higher magnification (Figure 1d), the thickness of these thin nanosheets barely increased as compared to VCNs, keeping a distance of around 200 nm with neighboring sheets. Meanwhile, 3D nickel foam substrates were less densely covered by these laterally extended composite nanosheets featured with more wrinkles and edge bending, beneficial to exposure of enriched active sites for catalytic reaction. After further heat treatment of VCNs@FeOOH under NH3 atmosphere, a 3D porous hierarchical composite structure constituted by highly branched assembly of interconnected fine nanoparticles (ca. 30 nm) was illustrated in Figure 1e and 1f. The as-obtained coral-like VCNs@Fe4N heterostructure on nickel foam substrate inherited structural merits from 2D VCNs@FeOOH template, exhibiting abundant void space within oriented self-assembly without severe aggregation. In addition, it is worth noting that VCNs acted as a structure-directing agent during the formation of desirable VCNs@FeOOH and VCNs@Fe4N het-

ACS Paragon Plus Environment

Page 3 of 9 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials erostructures, as indicated by the morphologies of controlled samples in the absence of VCNs, e.g., Ni@FeOOH and Ni@Fe4N (Figure S5).

loaded with nanoparticles as observed by TEM in Figure 2d. Additionally, the homogeneous distribution of C, N, and Fe was exhibited by EDS elemental mapping (Figure 2f) based on the corresponding dark-field image in Figure 2e. More importantly, the diffraction rings in selected area electron diffraction (SAED) pattern (Figure 2g) showed the polycrystalline structure of Fe4N nanoparticles. Meanwhile, the good crystallinity of Fe4N can be also confirmed by XRD with three strong diffraction peaks centered at around 42.1°, 48.8 ° and 71.5 ° (Figure S2), which belong to (111), (200) and (220) lattice planes of cubic Fe4N (JCPDS No. 86-0231) according to literatures.56 Furthermore, the lattice fringes with a d-spacing of 0.22 nm in the high-resolution TEM (HRTEM) image can be well indexed to the (111) plane of Fe4N (Figure S8).

Figure 2. Typical transmission electron microscopy (TEM) images of hybrid electrocatalysts. (a) TEM image of VCNs@FeOOH. (b-c) Dark-field TEM image and corresponding elemental mapping images of VCNs@FeOOH with orange for C, red for N, purple for Fe, and green for O. (d) TEM image of VCNs@Fe4N. (e-f) Dark-field TEM image and corresponding elemental mapping images of VCNs@Fe4N with purple for C, red for N, and green for Fe. (g) Corresponding SAED pattern for VCNs@Fe4N.

Further insight into the microstructure and composition of composite electrocatalysts was provided by conducting transmission electron microscopy (TEM). As shown in Figure 2a, these folding sheet-like composites displayed high transparency under the electron beam, indicating their ultrathin nature.52 At a higher magnification, asobserved lattice fringes (high-resolution TEM image in Figure S6) can be well indexed to (101) planes of hexagonal FeOOH (JCPDS No. 76-0123). Energy dispersive spectroscopy (EDS) elemental mapping images corresponding to the dark-field image of VCNs@FeOOH (Figure 2b) further revealed the uniform distribution of C, N, Fe and O (Figure 2c). Moreover, characteristic peaks located at around 467, 540 and 667 cm-1 in the Raman spectra of VCNs@FeOOH and Ni@FeOOH (Figure S7) can be well assigned to FeOOH in accordance with previous reports,53-55 while typical D-band, G-band and 2D-band features are ascribed to the presence of VCNs. In the case of VCNs@Fe4N, ultrathin carbon nanosheets were evenly

Figure 3. X-ray photoelectron spectroscopy (XPS) of (a-d) VCNs@FeOOH and (e-f) VCNs@Fe4N, indicating the presence of C, N, Fe, and O in the composite electrocatalysts.

X-ray photoelectron spectroscopy (XPS) was further carried out to examine the chemical composition and oxidation states of the as-prepared VCNs@FeOOH and VCNs@Fe4N. Figure 3a showed the high-resolution C 1s core level of VCNs@FeOOH, which can be deconvoluted into one dominant peak of graphitic (sp2 hybridized) carbon (C-C) at 284.7 eV as well as C-N bond (285.5 eV) and C-O bond (286.2 eV), respectively.57-59 Similar C 1s spectrum was also obtained for VCNs@Fe4N and presented in Figure S9 (Supporting Information). Besides, the detection of N in VCNs@FeOOH further revealed the N-doping feature of graphitic carbon nanosheets. According to the deconvolution of N 1s spectrum (Figure 3b), three resolved peaks at 398.6, 400.0 and 400.9 eV can be ascribed to pyridinic N, pyrrolic N and graphitic N, respectively.60,

ACS Paragon Plus Environment

Chemistry of Materials 61

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

As shown in Fe 2p spectrum (Figure 3c), two resolved peaks at 2p3/2 (713.5 eV), 2p1/2 (725.7 eV) and the satellite peak of 2p3/2 at 719.9 eV indicated the presence of Fe as Fe3+ in VCNs@FeOOH, which is consistent with previously reports.52, 62 The O 1s region spectrum of VCNs@FeOOH was also analyzed (Figure 3d), suggesting the existence of three distinct species, e.g., Fe-O-H bond (513.3 eV), C-O bond (532.0 eV), and C=O (533.2 eV).52, 55, 63 On the other hand, the valence state of Fe species in VCNs@Fe4N was carefully examined by high-resolution Fe 2p spectrum (Figure 3e). The coexistence of mixed oxidation states (+3 and +2) was revealed by the fitting, while the presence of Fe (0) can be attributed to the formation of trace metallic Fe by NH3 reduction. Moreover, a distinct peak corresponding to the Fe-N bond (397.8 eV) originating from Fe4N emerged in N 1s spectrum of VCNs@Fe4N (Figure 3f), in addition to three typical Ncontaining groups in N-doped VCNs.60, 64

Figure 4. Electrocatalytic activities for oxygen evolution reaction (OER). (a) Comparative polarization curves of Ni foam, Ni@FeOOH, VCNs, and VCNs@FeOOH (electrolyte: -1 0.1 M KOH, scan rate: 1 mV s ). (b) Corresponding overpo-2 tentials at a current density of 10 mA cm . (c) Tafel slopes of Ni foam, Ni@FeOOH, VCNs, and VCNs@FeOOH. (d) Chronopotentiometric curve for VCNs@FeOOH with a con-2 stant current density of 25 mA cm .

To explore the potential application of these as-prepared 3D electrodes in electrochemical water splitting, the electrocatalytic activity of VCNs@FeOOH toward OER was first evaluated in a three-electrode electrochemical system (see details in the Experimental Section). Figure 4a displays typical polarization curves obtained at 1 mV s-1 in 0.1 M KOH with VCNs@FeOOH, Ni@FeOOH, VCNs and nickel foam directly used as working electrodes. Significant oxygen evolution electrocatalytic activities were obtained for these samples. Among them, VCNs@FeOOH delivered the best electrocatalytic activity. To be more precise, overpotentials to achieve a current density of 10 mA cm-2 were summarized for these electrocatalysts (Figure 4b). As seen, VCNs@FeOOH requires the lowest overpotential of 179 mV, which is 110, 141 and 301 mV lower than those of Ni@FeOOH, VCNs, Ni foam, respectively. Superior OER performance of VCNs@FeOOH was also

Page 4 of 9

confirmed by its smaller Tafel slope (57 mV dec-1) derived from the linear sweep voltammetry (LSV) curve (Figure 4c) than other controlled samples, e.g., Ni@FeOOH (87 mV dec-1), VCNs (138 mV dec-1) and Ni foam substrate (357 mV dec-1), indicating a more favorable reaction kinetics of VCNs@FeOOH for OER. Here, the catalytic activity of VCNs@FeOOH can be further tuned by varying the content of FeOOH with altered deposition time (Table S1 and Figure S10). The optimal catalytic performance can be achieved with a deposition time of 24 h, which can be ascribed to the wise incorporation of moderate FeOOH active species. In addition, double-layer capacitance (Cdl) at the solid-liquid interface was measured to assess the electrochemically active surface area (ECSA) of different electrocatalysts. Cyclic voltammetry (CV) curves were obtained at different scan rates over a potential range of 1.05-1.15 V vs RHE without apparent faradaic processes (Figure S11). As expected, a much higher linear slope can be obtained for VCNs@FeOOH from current density difference (∆j) at 1.10 V vs RHE plotted against scan rate (Figure S12), e.g., a higher Cdl of 22.3 mF cm-2 as compared to VCNs (13.8 mF cm-2), Ni@FeOOH (2.4 mF cm-2), and bare Ni foam substrate (1.8 mF cm-2). Larger electrochemical active surface area of VCNs@FeOOH (ca. 10 times of pristine Ni@FeOOH) can be attributed to the porous architecture of self-supported electrode constructured by 2D ultrathin nanosheet building blocks, resulting in the enhanced OER activity. A comparison of VCNs@FeOOH with recently reported non-noble metalbased OER electrocatalysts was summarized in Table S2, demonstrating a comparably high catalytic performance under alkaline conditions. Additionally, the long-term electrochemical stability of VCNs@FeOOH was evaluated with chronopotentiometric measurements at a current density of 25 mA cm-2. As presented in Figure 4d, VCNs@FeOOH retained high catalytic activity over 12 h without evident voltage degradation. Specifically, only 37 mV overpotential increase was encountered over 12 h, corresponding to an activity loss of less than 13.8%. This result further demonstrated the desirable stability of VCNs@FeOOH for OER. The excellent stability of the VCNs@FeOOH electrode was further confirmed by exsitu XRD, Raman and SEM (Figure S13). Both the XRD pattern and Raman spectrum scarcely changed after the stability test, while the SEM images revealed the wellpreserved morphology of VCNs@FeOOH after OER, consistent with the stable performance of the VCNs@FeOOH electrode in alkaline media.

ACS Paragon Plus Environment

Page 5 of 9 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials VCNs@Fe4N for HER (Figure 5d). Ex-situ XRD and SEM measurements were also performed on VCNs@Fe4N after the stability test (Figure S17). As seen, the crystal phase was maintained after the cycling reaction. Meanwhile, well-preserved morphologies of porous 3D self-supported catalysts demonstrated the robust stability of as-prepared composite electrodes.

Figure 5. Electrocatalytic activities for hydrogen evolution reaction (HER). (a) Comparative polarization curves of Ni foam, VCNs, Ni@Fe4N, and VCNs@Fe4N (electrolyte: 0.1 M -1 KOH, scan rate: 1 mV s ). (b) Corresponding overpotentials -2 at a current density of 10 mA cm . (c) Tafel slopes of Ni foam, VCNs, Ni@Fe4N, and VCNs@Fe4N. (d) Chronopotentiometric curve of VCNs@ Fe4N with a constant current densi-2 ty of -10 mA cm .

In view of the cathode reaction of water splitting, HER performance of VCNs@Fe4N was further examined by carrying out corresponding electrochemical measurements under alkaline condition (0.1 M KOH) at room temperature. As shown in Figure 5a, a negligible catalytic activity was revealed for the bare Ni foam substrate according to the polarization curves, whereas current densities significantly increased for as-obtained self-supported 3D electrodes. A low overpotential of 172 mV was achieved for VCNs@Fe4N at a current density of 10 mA cm-2 (Figure 5b). In contrast, higher overpotentials of 331 and 319 mV were demanded for Ni@Fe4N and VCNs, respectively. Furthermore, the corresponding Tafel plots were derived to evaluate the HER kinetic process of 3D electrodes. VCNs@Fe4N delivered a Tafel slope of 80 mV dec-1, which is smaller than Ni@Fe4N (217 mV dec-1) and VCNs (220 mV dec-1), respectively (Figure 5c). As expected, VCNs@Fe4N catalyst derived from the VCNs@FeOOH with a deposition time of 24 h has the lowest overpotential and smallest Tafel slope, achieving the best electrochemical activity upon HER (Figure S14). This superior electrocatalytic performance is comparable to state-ofthe-art non-noble metal based HER catalysts (Table S3). Similarly, the effective ECSAs of VCNs@Fe4N, Ni@Fe4N, VCNs, and Ni foam toward HER were obtained according to CV scans from 0.08-0.18 V vs RHE (Figure S15), demonstrating a decrease in the order of VCNs@Fe4N > Ni@Fe4N > VCNs > Ni foam (Figure S16). Two times larger ECSA was achieved for VCNs@Fe4N than Ni@Fe4N, indicating a more advantageous 3D nanostructure provided by the presence of VCNs with enhanced electron transport along with increased active sites. Furthermore, prolonged chronopotentiometric experiment at a fixed current density of -10 mA cm-2 for 12 h showed a stable potential response, indicating remarkable durability of

Figure 6. (a) The water splitting performance of VCNs@FeOOH//VCNs@Fe4N couple in 0.1 M KOH solution in a two-electrode configuration. Inset: Optical photograph showing the generation of H2 and O2 bubbles. (b) The catalytic stability of VCNs@FeOOH//VCNs@Fe4N couple for -2 overall water splitting at 10 mA cm .

In order to approach the real application, the catalytic performance toward water splitting was measured in a two-electrode device by employing VCNs@FeOOH as anode and VCNs@Fe4N as cathode, respectively (Inset of Figure 6a). As shown in Figure 6a, the polarization curve of water electrolysis presented a current density of 10 mA cm-2 achieved with an external bias of 1.6 V, which was superior to most of the previously reported results for water splitting in alkaline solution (Table S4). Moreover, the long-term stability test of this two-electrode electrolyzer was also performed (Figure 6b), delivering a maintained voltage around 1.61 V at 10 mA cm-2 for 10 h. In addition, such VCNs@FeOOH//VCNs@Fe4N water electrolyzer can be driven by a single-cell AA battery with a voltage of 1.5 V in 1.0 M KOH (see corresponding movie in the Supporting Information). The evolution of numerous small bubbles near both electrodes can be clearly observed, indicating that produced O2 and H2 are readily released from the surface of catalysts. As discussed above, superior electrochemical performance of VCNs@FeOOH//VCNs@Fe4N can be attributed to the following aspects: (1) N-doped VCNs have the advantages of large electrode electrolyte interface, strong interaction with the current collector and low contact resistance. Simultaneously, the interconnected VCNs serve as growth templates for Fe-based catalytic components, ensuring the successful establishment and stability of 3D structure. (2) Both the VCNs@FeOOH nanosheets featured with wrinkles and curled-edges and the corallike VCNs@Fe4N nanoparticles endowed with large surface area have provided abundant active sites during electrocatalytic reactions, contributing to favorable catalytic reactions. (3) Successful construction of 3D VCNs@FeOOH//VCNs@Fe4N architectures on Ni foam substrates further enables synergistic effect from multiple components, resulting in the acceleration of both mass and electron transport as well as promoted electrical con-

ACS Paragon Plus Environment

Chemistry of Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ductivity, contributing to substantially boosted electrochemical activity. Therefore, N-doped vertically aligned carbon nanosheets coupled with iron oxyhydroxide/nitride (VCNs@FeOOH//VCNs@Fe4N) are promising electrocatalysts with high activity and excellent durability for electrochemical water splitting.

CONCLUSIONS In summary, vertically aligned carbon nanosheets/ironbased composite architectures were synthesized by a facile approach suitable for large-scale production, and were demonstrated to be efficient electrocatalysts for water splitting in alkaline medium. The composite architectures are enriched in active sites, and are also very beneficial for facilitating mass diffusion and charge transfer, all of which are of great significance to enhanced electrochemical water splitting. The VCNs@FeOOH and VCNs@Fe4N composite electrodes exhibited excellent electrocatalytic activity for OER (179 mV at 10 mA cm-2) and HER (172 mV at 10 mA cm-2), respectively. Notably, exceptional overall water-splitting performance was achieved in an alkaline electrolyzer employing the two composite electrodes. The present results open a new avenue to design efficient and cost-effective electrocatalysts for water splitting, and also shed light on the development of catalysts for metal-air batteries.

ASSOCIATED CONTENT The Supporting Information is available free of charge on the ACS Publications website at http://pubs.acs.org. Experimental details, additional figures, e.g. Lowmagnification SEM images and EDS mapping result for VCNs and VCNs@FeOOH, XRD patterns of all samples, Raman spectra of VCNs, VCNs@FeOOH and Ni@FeOOH, SEM images of Ni@FeOOH and Ni@Fe4N, HRTEM image of VCNs@FeOOH and VCNs@Fe4N, C1s XPS spectrum of VCNs@Fe4N, electrocatalytic activities of VCNs@FeOOH with different mass loading, cyclic voltammograms of all samples, structure and morphology analysis after OER/HER (XRD pattern, Raman spectrum and SEM images), comparison tables of the OER, HER and overall water splitting performance (PDF) and supporting movie (mp4).

AUTHOR INFORMATION Corresponding Author * Wenping Sun. Email: wenping@uow.edu.au * Jixin Zhu. Email: iamjxzhu@njtech.edu.cn

Author Contributions ‡ Y. Zhang and K. Rui contributed equally to this work.

Notes The authors declare no competing financial interest.

ACKNOWLEDGMENT This work was financially supported by the National Key R&D Program of China (2017YFA0207201), National Natural

Science Foundation of China (21501091), the NSF of Jiangsu Province (BK20170045), the Recruitment Program of Global Experts (1211019), the Six Talent Peak Project of Jiangsu Province (XCL-043), the National Key Basic Research Program of China (973) (2015CB932200). W. Sun acknowledges financial support from the Australian Research Council (ARC) DECRA Grant (DE160100596) and AIIM FOR GOLD Grant (2017, 2018). K. Rui acknowledges the fellowship from the China Scholarship Council (CSC), and the financial support from the China Postdoctoral Science Foundation (2016M600404, 2017T100360) and Jiangsu Postdoctoral Science Foundation (1701094C). Q. Zhang is grateful to the support from the Postgraduate Research & Practice Innovation Program of Jiangsu Province (KYCX17-0955).

REFERENCES (1) Yang, Y.; Zhang, K.; Lin, H.; Li, X.; Chan, H. C.; Yang, L.; Gao, Q. MoS2-Ni3S2 Heteronanorods as Efficient and Stable Bifunctional Electrocatalysts for Overall Water Splitting. ACS Catal. 2017, 7, 2357-2366. (2) Liang, K.; Guo, L.; Marcus, K.; Zhang, S.; Yang, Z.; Perea, D. E.; Zhou, L.; Du, Y.; Yang, Y. Overall Water Splitting with RoomTemperature Synthesized NiFe Oxyfluoride Nanoporous Films. ACS Catal. 2017, 7, 8406-8412. (3) Du, C.; Yang, L.; Yang, F.; Cheng, G.; Luo, W. Nest-Like NiCoP for Highly Efficient Overall Water Splitting. ACS Catal. 2017, 7, 4131-4137. (4) Wang, H.; Min, S.; Wang, Q.; Li, D.; Casillas, G.; Ma, C.; Li, Y.; Liu, Z.; Li, L. J.; Yuan, J.; Antonietti, M.; Wu, T. NitrogenDoped Nanoporous Carbon Membranes with Co/CoP JanusType Nanocrystals as Hydrogen Evolution Electrode in Both Acidic and Alkaline Environments. ACS Nano 2017, 11, 4358-4364. (5) Du, M.; Rui, K.; Chang, Y.; Zhang, Y.; Ma, Z.; Sun, W.; Yan, Q.; Zhu, J.; Huang, W. Carbon Necklace Incorporated Electroactive Reservoir Constructing Flexible Papers for Advanced Lithium-Ion Batteries. Small 2018, 14, 1702770. (6) Wang, Q.; Rui, K.; Zhang, C.; Ma, Z.; Xu, J.; Sun, W.; Zhang, W.; Zhu, J.; Huang, W. Interlayer-Expanded Metal Sulfides on Graphene Triggered by a Molecularly Self-Promoting Process for Enhanced Lithium Ion Storage. ACS Appl. Mater. Interfaces 2017, 9, 40317-40323. (7) Cheng, H.; Li, M.-L.; Su, C.-Y.; Li, N.; Liu, Z.-Q. Cu-Co Bimetallic Oxide Quantum Dot Decorated Nitrogen-Doped Carbon Nanotubes: A High-Efficiency Bifunctional Oxygen Electrode for Zn-Air Batteries. Adv. Funct. Mater. 2017, 27, 1701833. (8) Zhu, J.; Sakaushi, K.; Clavel, G.; Shalom, M.; Antonietti, M.; Fellinger, T.-P. A General Salt-Templating Method to Fabricate Vertically Aligned Graphitic Carbon Nanosheets and their Metal Carbide Hybrids for Superior Lithium Ion Batteries and Water Splitting. J. Am. Chem. Soc. 2015, 137, 5480-5485. (9) Li, D.; Wang, D.; Rui, K.; Ma, Z.; Xie, L.; Liu, J.; Zhang, Y.; Chen, R.; Yan, Y.; Lin, H.; Xie, X.; Zhu, J.; Huang, W. Flexible Phosphorus Doped Carbon Nanosheets/Nanofibers: Electrospun Preparation and Enhanced Li-Storage Properties as FreeStanding Anodes for Lithium Ion Batteries. J. Power Sources 2018, 384, 27-33. (10) Yu, Z.; Yun, Z.; Kun, R.; Hoon, H. H.; Kedar, H.; Jianwei, X.; Wenping, S.; Jixin, Z.; Qingyu, Y.; Wei, H. 2D Black Phosphorus for Energy Storage and Thermoelectric Applications. Small 2017, 13, 1700661. (11) Wu, X.; Zhu, C.; Wang, L.; Guo, S.; Zhang, Y.; Li, H.; Huang, H.; Liu, Y.; Tang, J.; Kang, Z. Control Strategy on Two/Four-Electron Pathway of Water Splitting by Multidoped Carbon Based Catalysts. ACS Catal. 2017, 7, 1637-1645.

ACS Paragon Plus Environment

Page 6 of 9

Page 7 of 9 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials (12) Spanos, I.; Auer, A. A.; Neugebauer, S.; Deng, X.; Tüysüz, H.; Schlögl, R. Standardized Benchmarking of Water Splitting Catalysts in a Combined Electrochemical Flow Cell/Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES) Setup. ACS Catal. 2017, 7, 3768-3778. (13) Chen, P.; Zhou, T.; Zhang, M.; Tong, Y.; Zhong, C.; Zhang, N.; Zhang, L.; Wu, C.; Xie, Y. 3D Nitrogen-Anion-Decorated Nickel Sulfides for Highly Efficient Overall Water Splitting. Adv. Mater. 2017, 29, 1701584. (14) Huang, Y.; Gong, Q.; Song, X.; Feng, K.; Nie, K.; Zhao, F.; Wang, Y.; Zeng, M.; Zhong, J.; Li, Y. Mo2C Nanoparticles Dispersed on Hierarchical Carbon Microflowers for Efficient Electrocatalytic Hydrogen Evolution. ACS Nano 2016, 10, 1133711343. (15) Aijaz, A.; Masa, J.; Rosler, C.; Xia, W.; Weide, P.; Botz, A. J.; Fischer, R. A.; Schuhmann, W.; Muhler, M. Co@Co3O4 Encapsulated in Carbon Nanotube-Grafted Nitrogen-Doped Carbon Polyhedra as an Advanced Bifunctional Oxygen Electrode. Angew. Chem. Int. Ed. 2016, 55, 4087-4091. (16) Cheng, H.; Su, C.-Y.; Tan, Z.-Y.; Tai, S.-Z.; Liu, Z.-Q. Interacting ZnCo2O4 and Au Nanodots on Carbon Nanotubes as Highly Efficient Water Oxidation Electrocatalyst. J. Power Sources 2017, 357, 1-10. (17) Kun, R.; Guoqiang, Z.; Yaping, C.; Yue, L.; Qian, Z.; Jiayi, C.; Jixin, Z.; Wenping, S.; Wei, H.; Xue, D. S. Hybrid 2D DualMetal-Organic Frameworks for Enhanced Water Oxidation Catalysis. Adv. Funct. Mater. 2018, doi:10.1002/adfm.201801554. (18) Hu, C.; Dai, L. Multifunctional Carbon-Based Metal-Free Electrocatalysts for Simultaneous Oxygen Reduction, Oxygen Evolution, and Hydrogen Evolution. Adv. Mater. 2017, 29, 1604942. (19) Zhao, X.; Zhang, H.; Yan, Y.; Cao, J.; Li, X.; Zhou, S.; Peng, Z.; Zeng, J. Engineering the Electrical Conductivity of Lamellar Silver-Doped Cobalt(II) Selenide Nanobelts for Enhanced Oxygen Evolution. Angew. Chem. Int. Ed. 2017, 56, 328-332. (20) Han, L.; Tang, P.; Reyes-Carmona, A.; Rodriguez-Garcia, B.; Torrens, M.; Morante, J. R.; Arbiol, J.; Galan-Mascaros, J. R. Enhanced Activity and Acid pH Stability of Prussian Blue-Type Oxygen Evolution Electrocatalysts Processed by Chemical Etching. J. Am. Chem. Soc. 2016, 138, 16037-16045. (21) Li, W.; Gao, X.; Xiong, D.; Wei, F.; Song, W.-G.; Xu, J.; Liu, L. Hydrothermal Synthesis of Monolithic Co3Se4 Nanowire Electrodes for Oxygen Evolution and Overall Water Splitting with High Efficiency and Extraordinary Catalytic Stability. Adv. Energy Mater. 2017, 7, 1602579. (22) Qu, K.; Zheng, Y.; Jiao, Y.; Zhang, X.; Dai, S.; Qiao, S.-Z. Polydopamine-Inspired, Dual Heteroatom-Doped Carbon Nanotubes for Highly Efficient Overall Water Splitting. Adv. Energy Mater. 2017, 7, 1602068. (23) Zhang, G.; Wang, G.; Liu, Y.; Liu, H.; Qu, J.; Li, J. Highly Active and Stable Catalysts of Phytic Acid-Derivative Transition Metal Phosphides for Full Water Splitting. J. Am. Chem. Soc. 2016, 138, 14686-14693. (24) Guo, Y.; Tong, Y.; Chen, P.; Xu, K.; Zhao, J.; Lin, Y.; Chu, W.; Peng, Z.; Wu, C.; Xie, Y. Engineering the Electronic State of a Perovskite Electrocatalyst for Synergistically Enhanced Oxygen Evolution Reaction. Adv. Mater. 2015, 27, 5989-5994. (25) Popczun, E. J.; Read, C. G.; Roske, C. W.; Lewis, N. S.; Schaak, R. E. Highly Active Electrocatalysis of the Hydrogen Evolution Reaction by Cobalt Phosphide Nanoparticles. Angew. Chem. Int. Ed. 2014, 126, 5531-5534. (26) Ling, T.; Yan, D. Y.; Wang, H.; Jiao, Y.; Hu, Z.; Zheng, Y.; Zheng, L.; Mao, J.; Liu, H.; Du, X. W.; Jaroniec, M.; Qiao, S. Z. Activating Cobalt(II) Oxide Nanorods for Efficient Electrocatalysis by Strain Engineering. Nat. Commun. 2017, 8, 1509.

(27) Zhuang, Z.; Li, Y.; Li, Z.; Lv, F.; Lang, Z.; Zhao, K.; Zhou, L.; Moskaleva, L.; Guo, S.; Mai, L. Schottky Catalysts Boost Hydrogen Evolution: the Case of MoB/g-C3N4 Interface Materials. Angew. Chem. Int. Ed. 2018, 57, 2697-2701. (28) Yin, J.; Li, Y.; Lv, F.; Lu, M.; Sun, K.; Wang, W.; Wang, L.; Cheng, F.; Li, Y.; Xi, P.; Guo, S. Oxygen Vacancies Dominated NiS2/CoS2 Interface Porous Nanowires for Portable Zn-Air Batteries Driven Water Splitting Devices. Adv. Mater. 2017, 29, 1704681. (29) Jianrui, F.; Fan, L.; Weiyu, Z.; Peihao, L.; Kai, W.; Chao, Y.; Bin, W.; Yong, Y.; Jinhui, Z.; Fei, L.; Gui-Chang, W.; Shaojun, G. Iridium-Based Multimetallic Porous Hollow Nanocrystals for Efficient Overall-Water-Splitting Catalysis. Adv. Mater. 2017, 29, 1703798. (30) Han, L.; Dong, S.; Wang, E. Transition-Metal (Co, Ni, and Fe)-Based Electrocatalysts for the Water Oxidation Reaction. Adv. Mater. 2016, 28, 9266-9291. (31) Jia, X.; Zhao, Y.; Chen, G.; Shang, L.; Shi, R.; Kang, X.; Waterhouse, G. I. N.; Wu, L.-Z.; Tung, C.-H.; Zhang, T. Ni3FeN Nanoparticles Derived from Ultrathin NiFe-Layered Double Hydroxide Nanosheets: An Efficient Overall Water Splitting Electrocatalyst. Adv. Energy Mater. 2016, 6, 1502585. (32) Chemelewski, W. D.; Lee, H. C.; Lin, J. F.; Bard, A. J.; Mullins, C. B. Amorphous FeOOH Oxygen Evolution Reaction Catalyst for Photoelectrochemical Water Splitting. J. Am. Chem. Soc. 2014, 136, 2843-2850. (33) Burke, M. S.; Enman, L. J.; Batchellor, A. S.; Zou, S.; Boettcher, S. W. Oxygen Evolution Reaction Electrocatalysis on Transition Metal Oxides and (Oxy)hydroxides: Activity Trends and Design Principles. Chem. Mater. 2015, 27, 7549-7558. (34) Yang, L.; Guo, Z.; Huang, J.; Xi, Y.; Gao, R.; Su, G.; Wang, W.; Cao, L.; Dong, B. Vertical Growth of 2D Amorphous FePO4 Nanosheet on Ni Foam: Outer and Inner Structural Design for Superior Water Splitting. Adv. Mater. 2017, 29, 1704574. (35) Li, J.; Wei, G.; Zhu, Y.; Xi, Y.; Pan, X.; Ji, Y.; Zatovsky, I. V.; Han, W. Hierarchical NiCoP Nanocone Arrays Supported on Ni Foam as an Efficient and Stable Bifunctional Electrocatalyst for Overall Water Splitting. J. Mater. Chem. A 2017, 5, 14828-14837. (36) Pi, Y.; Shao, Q.; Wang, P.; Lv, F.; Guo, S.; Guo, J.; Huang, X. Trimetallic Oxyhydroxide Coralloids for Efficient Oxygen Evolution Electrocatalysis. Angew. Chem. Int. Ed. 2017, 129, 45734577. (37) Zhu, Y. P.; Ma, T. Y.; Jaroniec, M.; Qiao, S. Z. SelfTemplating Synthesis of Hollow Co3O4 Microtube Arrays for Highly Efficient Water Electrolysis. Angew. Chem. Int. Ed. 2017, 56, 1324-1328. (38) Zhang, Z.; Lee, C.-S.; Zhang, W. Vertically Aligned Graphene Nanosheet Arrays: Synthesis, Properties and Applications in Electrochemical Energy Conversion and Storage. Adv. Energy Mater. 2017, 7, 1700678. (39) Mendoza-Sanchez, B.; Gogotsi, Y. Synthesis of TwoDimensional Materials for Capacitive Energy Storage. Adv. Mater. 2016, 28, 6104-6135. (40) Duan, J.; Chen, S.; Zhao, C. Ultrathin Metal-Organic Framework Array for Efficient Electrocatalytic Water Splitting. Nat. Commun. 2017, 8, 15341. (41) Ma, T. Y.; Cao, J. L.; Jaroniec, M.; Qiao, S. Z. Interacting Carbon Nitride and Titanium Carbide Nanosheets for HighPerformance Oxygen Evolution. Angew. Chem. Int. Ed. 2016, 55, 1138-1142. (42) Zhang, X.; Hou, L.; Ciesielski, A.; Samorì, P. 2D Materials Beyond Graphene for High-Performance Energy Storage Applications. Adv. Energy Mater. 2016, 6, 1600671. (43) Zhang, L.; Xiao, J.; Wang, H.; Shao, M. Carbon-Based Electrocatalysts for Hydrogen and Oxygen Evolution Reactions. ACS Catal. 2017, 7, 7855-7865.

ACS Paragon Plus Environment

Chemistry of Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(44) Xie, X.; Makaryan, T.; Zhao, M.; Van Aken, K. L.; Gogotsi, Y.; Wang, G. MoS2 Nanosheets Vertically Aligned on Carbon Paper: A Freestanding Electrode for Highly Reversible SodiumIon Batteries. Adv. Energy Mater. 2016, 6, 1502161. (45) Feng, J. X.; Xu, H.; Dong, Y. T.; Ye, S. H.; Tong, Y. X.; Li, G. R. FeOOH/Co/FeOOH Hybrid Nanotube Arrays as HighPerformance Electrocatalysts for the Oxygen Evolution Reaction. Angew. Chem. Int. Ed. 2016, 55, 3694-3698. (46) Zhang, Y.; Jia, G.; Wang, H.; Ouyang, B.; Rawat, R. S.; Fan, H. J. Ultrathin CNTs@FeOOH Nanoflake Core/Shell Networks as Efficient Electrocatalysts for the Oxygen Evolution Reaction. Mater. Chem. Front. 2017, 1, 709-715. (47) Feng, J. X.; Ye, S. H.; Xu, H.; Tong, Y. X.; Li, G. R. Design and Synthesis of FeOOH/CeO2 Heterolayered Nanotube Electrocatalysts for the Oxygen Evolution Reaction. Adv. Mater. 2016, 28, 4698-4703. (48) Zhang, Y.; Ouyang, B.; Xu, J.; Chen, S.; Rawat, R. S.; Fan, H. J. 3D Porous Hierarchical Nickel-Molybdenum Nitrides Synthesized by RF Plasma as Highly Active and Stable Hydrogen-Evolution-Reaction Electrocatalysts. Adv. Energy Mater. 2016, 6, 1600221. (49) Zhu, J.; Metzger, M.; Antonietti, M.; Fellinger, T. P. Vertically Aligned Two-Dimensional Graphene-Metal Hydroxide Hybrid Arrays for Li-O2 Batteries. ACS Appl. Mater. Interfaces 2016, 8, 26041-26050. (50) Coskun, M. B.; Qiu, L.; Arefin, M. S.; Neild, A.; Yuce, M.; Li, D.; Alan, T. Detecting Subtle Vibrations Using GrapheneBased Cellular Elastomers. ACS Appl. Mater. Interfaces 2017, 9, 11345-11349. (51) Shi, L.; Chen, K.; Du, R.; Bachmatiuk, A.; Rummeli, M. H.; Xie, K.; Huang, Y.; Zhang, Y.; Liu, Z. Scalable Seashell-Based Chemical Vapor Deposition Growth of Three-Dimensional Graphene Foams for Oil-Water Separation. J. Am. Chem. Soc. 2016, 138, 6360-6363. (52) Liu, J.; Zheng, M.; Shi, X.; Zeng, H.; Xia, H. Amorphous FeOOH Quantum Dots Assembled Mesoporous Film Anchored on Graphene Nanosheets with Superior Electrochemical Performance for Supercapacitors. Adv. Funct. Mater. 2016, 26, 919-930. (53) Padhi, D. K.; Parida, K. Facile Fabrication of α-FeOOH Nanorod/RGO Composite: A Robust Photocatalyst for Reduction of Cr(vi) Under Visible Light Irradiation. J. Mater. Chem. A 2014, 2, 10300-10312. (54) Wang, F.; Zeng, Y.; Zheng, D.; Li, C.; Liu, P.; Lu, X.; Tong, Y. Three-Dimensional Iron Oxyhydroxide/Reduced Graphene Oxide Composites as Advanced Electrode for Electrochemical Energy Storage. Carbon 2016, 103, 56-62. (55) Chen, J.; Xu, J.; Zhou, S.; Zhao, N.; Wong, C.-P. Amorphous Nanostructured FeOOH and Co-Ni Double Hydroxides for High-Performance Aqueous Asymmetric Supercapacitors. Nano Energy 2016, 21, 145-153. (56) Fan, X.; Kong, F.; Kong, A.; Chen, A.; Zhou, Z.; Shan, Y. Covalent Porphyrin Framework-Derived Fe2P@Fe4N-Coupled Nanoparticles Embedded in N-Doped Carbons as Efficient Trifunctional Electrocatalysts. ACS Appl. Mater. Interfaces 2017, 9, 32840-32850. (57) Jiang, F.-X.; Zhao, Y.; Zhou, G.-W.; Zhang, J.; Fan, J.-P.;

(59) Guan, Z.; Liu, H.; Xu, B.; Hao, X.; Wang, Z.; Chen, L. Gelatin-Pyrolyzed Mesoporous Carbon as a High-Performance Sodium-Storage Material. J. Mater. Chem. A 2015, 3, 7849-7854. (60) Yin, H.; Zhang, C.; Liu, F.; Hou, Y. Hybrid of Iron Nitride and Nitrogen-Doped Graphene Aerogel as Synergistic Catalyst for Oxygen Reduction Reaction. Adv. Funct. Mater. 2014, 24, 2930-2937. (61) He, C.; Zhang, J. J.; Shen, P. K. Nitrogen-Self-Doped Graphene-Based Non-Precious Metal Catalyst with Superior Performance to Pt/C Catalyst toward Oxygen Reduction Reaction. J. Mater. Chem. A 2014, 2, 3231-3236. (62) Peng, S.; Yu, L.; Sun, M.; Cheng, G.; Lin, T.; Mo, Y.; Li, Z. Bunched Akaganeite Nanorod Arrays: Preparation and HighPerformance for Flexible Lithium-Ion Batteries. J. Power Sources 2015, 296, 237-244. (63) Ma, Z.; Rui, K.; Zhang, Q.; Zhang, Y.; Du, M.; Li, D.; Wang, Q.; Huang, X.; Zhu, J.; Huang, W. Self-Templated Formation of Uniform F-CuO Hollow Octahedra for Lithium Ion Batteries. Small 2017, 13, 1603500. (64) Lei, X.; Ye, Z.; Zhao, N.; Lei, F.; Yang, H. Magnetic γ′Fe4N/Fe3C, χ-Fe5C2, and θ-Fe3C by a Simple Route for Application as Electrochemical Catalysts. Chem. Eur. J. 2017, 23, 17592-17597.

Xu, X.-H. Structure and Magnetic Properties of the γ′-Fe4N Films on Cu Underlayers. Chin. Phys. Lett. 2015, 32, 087501. (58) Wang, S.; Xia, L.; Yu, L.; Zhang, L.; Wang, H.; Lou, X. W. D. Free-Standing Nitrogen-Doped Carbon Nanofiber Films: Integrated Electrodes for Sodium-Ion Batteries with Ultralong Cycle Life and Superior Rate Capability. Adv. Energy Mater. 2016, 6, 1502217.

ACS Paragon Plus Environment

Page 8 of 9

Page 9 of 9 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials

For Table of Contents Only

ACS Paragon Plus Environment

9