Microbial Transformation of Multiwalled Carbon Nanotubes by

Jan 12, 2017 - Department of Natural Resources and Environmental Science, University of ... Department of Geological Sciences & Engineering, Universit...
0 downloads 0 Views 3MB Size
Subscriber access provided by Fudan University

Article

Microbial Transformation of Multi-walled Carbon Nanotubes by Mycobacterium vanbaalenii PYR-1 Yaqi You, Kamol K. Das, Huiyuan Guo, Che-Wei Chang, Maria Navas-Moreno, James W. Chan, Paul Verburg, Simon R. Poulson, Xilong Wang, Baoshan Xing, and Yu Yang Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.6b04523 • Publication Date (Web): 12 Jan 2017 Downloaded from http://pubs.acs.org on January 12, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 32

Environmental Science & Technology

1

Microbial Transformation of Multi-walled Carbon Nanotubes by Mycobacterium

2

vanbaalenii PYR-1

3 4 5

Yaqi You1*, Kamol Das1, Huiyuan Guo2, Che-Wei Chang3, Maria Navas-Moreno3, James W.

6

Chan3, Paul Verburg4, Simon R. Poulson5, Xilong Wang6, Baoshan Xing2, Yu Yang1*

7 8 9

1

Department of Civil and Environmental Engineering, University of Nevada Reno, MS258, 1664

10 11

N. Virginia Street, Reno, Nevada 89557, USA; 2

Stockbridge School of Agriculture, University of Massachusetts Amherst, 410 Paige Laboratory,

12

Amherst, MA 01003, USA; 3

13

Center for Biophotonics, University of California Davis Medical Center, 2700 Stockton Blvd

14

Suite 1400, Sacramento, CA 95817, USA; 4

15 16

Department of Natural Resources and Environmental Science, University of Nevada Reno, MS186, 1664 N. Virginia Street, Reno, Nevada 89557, USA;

5

17 18

Department of Geological Sciences & Engineering, University of Nevada Reno, MS172, 1664 N. Virginia Street, Reno, Nevada 89557, USA;

6

19 20

Laboratory for Earth Surface Processes, College of Urban and Environmental Sciences, Peking University, Beijing 100871, China.

21 22

*To whom correspondence should be addressed:

23

[email protected] or [email protected]; phone: 775-682-6609.

24



1

ACS Paragon Plus Environment

Environmental Science & Technology

25

ABSTRACT

26

Carbonaceous nanomaterials are widely used in industry and consumer products, but

27

concerns have been raised regarding their release into the environment and subsequent impacts

28

on ecosystems and human health. Although many efforts have been devoted to understanding the

29

environmental fate of carbonaceous nanomaterials, information about their microbial

30

transformation is still rare. In this study, we found that within 1 month a polycyclic aromatic

31

hydrocarbon-degrading bacterium, Mycobacterium vanbaalenii PYR-1, was able to degrade both

32

pristine and carboxyl-functionalized multi-walled carbon nanotubes (p-MWCNT and c-

33

MWCNT), as demonstrated by consistent results from high resolution transmission electron

34

microscopy, Raman spectroscopy, and confocal Raman microspectroscopy. Statistical analysis of

35

Raman spectra identified significant increase in the density of disordered or amorphous carbon in

36

p-MWCNT and c-MWCNT after biodegradation. Microbial respiration further suggested

37

potential mineralization of MWCNTs within about 1 month. All of our analyses consistently

38

showed higher degradation or mineralization of c-MWCNT compared to p-MWCNT. These

39

results highlight the potential of using bacteria in engineered systems to remove residual

40

carbonaceous nanomaterials and reduce risk of human exposure and environmental impact.

41

Meanwhile, our finding suggests possible transformation of carbonaceous nanomaterials by

42

polycyclic aromatic hydrocarbon-degrading bacteria in the natural environment, which should be

43

accounted for in predicting environmental fate of these emerging contaminants and in

44

nanotechnology risk regulation.

45



2

ACS Paragon Plus Environment

Page 2 of 32

Page 3 of 32

46

Environmental Science & Technology

INTRODUCTION

47

Due to their unique physicochemical properties, carbon nanotubes (CNTs) have attracted

48

worldwide commercial interests in diverse applications for both industry and consumer

49

products.1-2 Current global production capacity of CNTs has surpassed 5,000,000 kg per year,

50

and is increasing by about 500,000 kg annually.2 Such rapid growth in production and

51

widespread use of CNTs has raised concerns about their impact on human and environmental

52

health following their release into the environment.3-6

53

Although many efforts have been made to understand their environmental fate,

54

information about biotransformation of CNTs in the environment is still scarce.7 Several studies

55

have reported in vitro transformation of single-walled carbon nanotubes (SWCNTs) and multi-

56

walled carbon nanotubes (MWCNTs), catalyzed by plant-derived horseradish peroxidase,8-10

57

manganese peroxidase from white-rot fungus,11 and human myeloperoxidase and eosinophil

58

peroxidase.12,13 Given the extremely high abundance and diversity of microbes in the

59

environment and their versatile metabolic potentials, microbial degradation of CNTs is very

60

likely the major biotransformation process in the environment, and deserves more

61

investigation.14 Recently, Zhang et al.15 reported mineralization of as much as 6.8% of

62

MWCNTs within 7 days by a bacterial community through co-metabolism with extra carbon

63

sources, and identified Burkholderia kururiensis, Delftia acidovorans and Stenotrophomonas

64

maltophilia as three potential key players. Parks et al.16 reported that after 6 months, less than

65

0.1% of SWCNTs were mineralized by the white-rot fungus Trametes versicolor or by

66

microbiota from polychlorinated biphenyl-contaminated sediments or aerated wastewater

67

treatment plant sludge. These dissimilar degradation rates warrant more efforts toward a better

68

understanding of microbial transformation of CNTs.



3

ACS Paragon Plus Environment

Environmental Science & Technology

69

A promising group of candidate microbes for CNT biodegradation are bacteria capable of

70

degrading polycyclic aromatic hydrocarbons (PAHs), which share similar structural skeletons

71

with CNTs. Previous studies have unambiguously demonstrated that species of Mycobacterium

72

can utilize PAHs as the sole source of carbon and energy.14,17 It is possible that those bacteria can

73

also transform CNTs, and even utilize CNTs as their carbon and energy source. To address this

74

question, we utilized a model PAH-degrading bacterium, Mycobacterium vanbaalenii PYR-1,

75

and studied its interaction with pristine (p-MWCNT) or carboxyl-functionalized MWCNT (c-

76

MWCNT) under various incubation conditions. Multiple analytical methods, including

77

transmission electron microscopy (TEM), Raman spectroscopy and confocal Raman

78

microspectroscopy, were applied to characterize physicochemical changes in MWCNTs after

79

reaction with this bacterium. Potential mineralization of MWCNTs was investigated using a

80

variety of conditions. By comparing results from p-MWCNT and c-MWCNT, we explored the

81

role of surface functionalization in biodegradation of MWCNTs by PYR-1.

82 83

MATERRIALS AND METHODS

84

MWCNTs preparation

85

Research-grade MWCNTs were used in this study: 1) pristine MWCNT (p-MWCNT)

86

(Nanocyl NC3150); 2) carboxyl-functionalized MWCNT (c-MWCNT) (Nanocyl NC3151).

87

According to the manufacturer (http://www.nanocyl.com/product/), both MWCNTs have an

88

average diameter of 9.5 nm and an average length of 95.0%

89

carbon and 80.0% carbon, 30 spectra.

156

A point-scan confocal Raman system25,26 was utilized to construct Raman maps of D- and

157

G-bands, from which the distribution of ID/IG ratios were calculated. Samples were prepared as

158

aforementioned, and 20 µL aliquots were drop-casted on 70% ethanol-cleaned quartz cover slips



7

ACS Paragon Plus Environment

Environmental Science & Technology

159

(0.2 mm thick, Technical Glass Products) and air-dried overnight. A 785 nm diode laser beam

160

(0.3 mW power) was used for excitation, with an acquisition time of 1 sec per spectrum. Each

161

map was generated by scanning a 6 µm × 6 µm region, which resulted in 400 Raman spectra (1

162

spectrum per 0.3 µm × 0.3 µm). For each sample, 3-6 regions were examined.

163 164

Measurement of CO2 from different incubations

165

We measured CO2 evolved from bacteria incubated with different external carbon

166

sources. After M. vanbaalenii PYR-1 cultures (MSM + 1% glucose + 5 mM pyerne) reached a

167

density of 109 cell/mL, they were harvested, washed three times with phosphate-buffered saline

168

(pH 7.0), and re-suspended in autoclaved MilliQ water for respiration measurement. Respiration

169

experiments were set up in duplicate or triplicate in 473 mL polypropylene jars, with each jar

170

containing approximately 4×109 bacterial cells and 111.17 mL one of the following media: 1)

171

MSM (pH 7.0), 2) MSM + 10 mg p-MWCNT, 3) MSM + 10 mg c-MWCNT, 4) MSM + 1%

172

glucose and 5 mM pyrene + 1 mg p-MWCNT, 5) MSM + 1% glucose and 5 mM pyrene + 1 mg

173

c-MWCNT. Medium (1) served as a negative control without external carbon source; medium

174

(2) or (3) represented a condition with MWCNTs being the only external carbon source; medium

175

(4) or (5) represented a positive control containing both energetic carbon sources and low-dose

176

MWCNTs. Respiration jars were wrapped with aluminum foil and incubated aerobically at

177

20−25°C for about 32 days. The jar lids were then tightened and sealed with parafilm to keep

178

gas-tight; headspace CO2 level was continuously monitored for 3 days using a Vaisala GMP343

179

probe that was inserted through the lid. CO2-based estimation of mineralization is detailed in the

180

SI.

181



8

ACS Paragon Plus Environment

Page 8 of 32

Page 9 of 32

182

Environmental Science & Technology

Data analyses and statistics

183

Bacterial growth kinetics was analyzed by fitting experimental data to the modified

184

Logistic or Gompertz equations27 using R (3.2.4). Raman spectra were analyzed using R and

185

MATLAB (more details in the SI). Statistical analyses were performed with R. Levene’s test was

186

conducted to check homogeneity of variance, after which data were compared using ANOVA or

187

Welch t-test, as well as Mann-Whitney U test.

188 189

RESULTS AND DISCUSSION

190

M. vanbaalenii PYR-1 growth

191

For each medium condition and each concentration of both p- and c-MWCNT, growth

192

trends from two independent batches were consistent (Figure S3). Contrast to other reports on

193

CNT’s concentration-dependent cytotoxicity on microorganisms,22 the presence of either p-

194

MWCNT or c-MWCNT stimulated M. vanbaalenii PYR-1 growth, when glucose alone or both

195

glucose and pyrene served as the primary carbon source. For instance, after 312-h growth,

196

bacterial cultures in the glucose medium containing 25 ppm p-MWCNT or c-MWCNT reached

197

an OD600 reading 3.0 or 1.7 times that of cultures grown in the same medium without MWCNTs,

198

respectively (Figure S3, A1 and B1). Similarly, after 312-h growth, bacterial cultures in the

199

glucose plus pyrene medium containing 5 ppm p-MWCNT or c-MWCNT reached an OD600

200

reading 1.4 or 1.6 times that of cultures grown in the same medium without MWCNTs,

201

respectively (Figure S3, A1 and B1). The addition of MWCNTs triggered earlier exponential

202

growth of bacterial cultures. Growth kinetics was fitted with the Logistic model (eq. 1) or the

203

modified Logistic model incorporating population decline (eq. 2) that are commonly used for

204

proliferating populations:27



9

ACS Paragon Plus Environment

Environmental Science & Technology

205

206

y=

y=

Page 10 of 32

A ⎧⎪ ⎡ 4µ ⎤⎫⎪ ⎨1+ exp⎢ m (λ −t)+2⎥⎬ ⎢⎣ A ⎥⎦⎪⎭ ⎪⎩

(eq. 1)

Aexp(−dt) ⎧⎪ ⎡ 4µ ⎤⎫⎪ ⎨1+ exp⎢ m (λ −t)+2⎥⎬ ⎢⎣ A ⎥⎦⎭⎪ ⎩⎪

(eq. 2)

207

where A (-) is the maximal population size, µm (h-1) is the maximum specific growth rate, λ (h) is

208

the lag time, and d (h-1) is the decline rate (fitted parameters shown in Table S2). Using cultures

209

grown in each medium without MWCNTs as reference, we assessed the impact of MWCNTs on

210

PYR-1’s lag time. As shown in Figure 1, the addition of 25 ppm p-MWCNT or c-MWCNT to

211

the glucose medium resulted in a 46.20% or 39.05% decrease in the lag time, respectively.

212

Similar patterns were observed for cultures in the glucose plus pyrene medium and for cultures

213

exposed to MWCNTs at other concentrations (Figure 1 and Table S2). When PYR-1 was

214

incubated without glucose or pyrene, no significant growth was observed within 2 months, no

215

matter whether MWCNTs were present or not (Figure S3). These results indicate that MWCNTs

216

could stimulate M. vanbaalenii PYR-1 growth when more labile carbon source(s) was present,

217

but MWCNTs alone were insufficient to support population proliferation.

218

Several recent studies have shown enhanced cellular growth of Escherichia coli,

219

Staphylococcus aureus and Bacillus subtilis by 10 ppm SWCNTs or MWCNTs, and suggested

220

that bacterial cells attached on CNT bundles could produce extracellular polymeric substances

221

(EPS) and form biofilms mitigating CNT toxicity.28-30 Carbonaceous nanomaterials other than

222

CNTs, such as graphene oxide, have also been reported to enhance bacterial growth through

223

promoting cell attachment, proliferation and biofilm formation.31 EPS as a protective barrier was

224

also reported for Shewanella oneidensis under the stress of metal nanoparticles.23 In this study,



10

ACS Paragon Plus Environment

Page 11 of 32

Environmental Science & Technology

225

M. vanbaalenii PYR-1 cells aggregated with MWCNTs (Figure S4 and Figure S5) and formed

226

biofilms encapsulating MWCNTs (Figure S6), a phenomenon previously observed for

227

Salmonella exposed to SWCNT.22 Mycobacterial strains are known to attach and form biofilms

228

on PAH particles with their extremely hydrophobic rigid cell envelope, and can modify their cell

229

wall composition in response to carbon sources.32 We thus speculate that MWCNTs may induce

230

biofilm formation by PYR-1 (SEM images shown in Figure S6) and consequently shorten the lag

231

time of its exponential growth, although more research is needed. The small amount of

232

amorphous carbon on the surface of MWCNTs (Table S1), although insufficient to serve as the

233

sole carbon/energy source, might also contribute to the observed growth stimulation.

234

Alternatively, MWCNTs can potentially up-regulate key genes involved in this bacterium’s

235

growth. For example, MWCNTs are known to promote plant growth through up-regulating genes

236

for cell division/cell wall formation and water transport.33 Similar mechanisms could have

237

enhanced M. vanbaalenii PYR-1 growth (e.g., up-regulation of DNA metabolism shown in

238

Figure S7), but to determine the exact mechanism needs further investigation. In any case, a

239

majority of PYR-1 cells attached on MWCNTs remained alive with intact cellar integrity (green

240

cells in Figure S5) and cell morphology (Figure S6), whereas losing cellular integrity is believed

241

to be one major mechanism for CNT’s bacterial cytotoxicity.7,34

242 243

Biotransformation of MWCNTs

244

TEM imaging of initial p- and c-MWCNT revealed sharp-edge tubular structures and

245

crystal lattices (10 layers on average according to HRTEM; Table S1), without substantial

246

amorphous materials on the surface (Figure 2 and Figure S8; Table S1). The same morphology

247

was observed for MWCNTs after abiotic incubation (Figure 2 and Figure S8). In contrast, a



11

ACS Paragon Plus Environment

Environmental Science & Technology

248

variety of drastic morphological changes were detected in both p-MWCNT and c-MWCNT

249

incubated with M. vanbaalenii PYR-1 for 25 days, regardless of the growth medium (containing

250

glucose or both glucose and pyrene). We observed shorter and thinner nanotubes and highly

251

disordered tubular structure with kinks and bends (Figure S8, A3-D3), as well as nanotubes with

252

broken ends (Figure S9). Moreover, we observed exfoliated graphitic flakes with substantial

253

amorphous materials on the surface, likely residues from incomplete degradation of graphite

254

lattices (Figure 2, A2, A5, B2, B5; Figure S8, A4-D4). These TEM observations indicated

255

degradation of MWCNTs by PYR-1, likely through oxidization of crystal lattices and subsequent

256

exfoliation of graphitic walls. Similar structural transformations were observed in degradation of

257

CNTs by horseradish peroxidase, microglial cells, and a microbial consortium, where CTNs

258

were broken down to shorter nanotubes or deformed through a layer-by-layer mode.9,15,35

259

As another line of evidence for degradation, Raman spectra were analyzed for MWCNTs

260

incubated with M. vanbaalenii PYR-1, and compared to initial and abiotically incubated

261

MWCNTs. Incubations using the glucose medium (Figure 3 and Figure 4) or the glucose plus

262

pyrene medium (Figure S10 and Figure S11) yielded similar results. As shown in Figure 3,

263

Raman spectra were similar for initial p- and c-MWCNT, displaying two fingerprint peaks as the

264

tangential-mode G-band (∼1580 cm-1) and the disorder-induced D-band (∼1340 cm-1).36 The

265

intensity ratio of D-band to G-band (ID/IG) for p- and c-MWCNT was measured as 1.07±0.05

266

(n=67) and 1.16±0.11 (n=48) (Figure 4), consistent with other report on the same MWCNTs.37

267

Surface functionalization of p-MWCNT with carboxylic functional groups (Table S1) slightly

268

increases the ID/IG value (p