Molecular Mass Distribution of Materials Solubilized by Xylanase

Canadian mills treated 750,000 tonnes of pulp with xylanase in 1994, representing 8% of Canada's bleached kraft pulp production. This paper describes ...
0 downloads 0 Views 2MB Size
Chapter 5

Molecular Mass Distribution of Materials Solubilized by Xylanase Treatment of Douglas-Fir Kraft Pulp 1

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

Ed de Jong, Ken Κ. Y. Wong , Lori A. Martin, Shawn D. Mansfield, F. M. Gama , and John N . Saddler 2

Chair of Forest Products Biotechnology, Department of Wood Science, University of British Columbia, 270-2357 Main Mall, Vancouver, British Columbia V6T 1Z4, Canada

Irgazyme, a commercial xylanase preparation from Trichoderma longibrachiatum, and xylanase D a purified enzyme from Trichoderma harzianum E58 were tested for their ability to enhance peroxide bleaching of Douglas-fir (Pseudotsuga menziesii) kraft pulp. A treatment with Irgazyme caused a much larger increase in brightness than did xylanase D. A double xylanase treatment with Irgazyme, before and after peroxide bleaching, resulted in the highest final brightness. Alkaline extraction increased the brightness of Douglas-fir brownstock. Treatment with Irgazyme released more lignin and carbohydrates than did xylanase D. The molecular mass of the lignin extracted from Irgazyme-treated brownstock was much larger than that from the control pulp. The lignin-like macromolecules directly solubilized from peroxide bleached pulps were substantially larger than those solubilized from the brownstock, irrespective of whether they were produced during xylanase or control treatments. This indicates that different kinds of materials were solubilized when a xylanase treatment was applied at different points in the bleaching sequence and raises concerns about the role of lignin entrapment in the mechanism by which xylanase enhances peroxide bleaching.

During the last few years the pulp and paper industry has rapidly moved away from using elemental chlorine as a bleaching agent. In a recent survey of Canadian pulp mills, 41 of the 51 bleach plants produced elemental chlorine free (ECF) grades in 1995, while prior to 1987 all of them used chlorine (7). However, to achieve the 1

Current address: PAPRO, NZ FRI Ltd., Private Bag 3020, Rotorua, New Zealand Current address: Department of Biological Engineering, University of Minho, Braga, Portugal

2

0097-6156/96/0655-0044$15.00/0 © 1996 American Chemical Society

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

5. DE JONG ET AL.

Xylanase Treatment of Doughs-Fir Kraft Pulp

45

desired brightness levels without elemental chlorine several changes have had to be implemented. The major changes included prolonged cooking regimes during the pulping stage to reach lower kappa values, as occurs in extended delignification, superbatch and extended modified continuous cooking. In the bleach plant, the benefits of chlorine dioxide, oxygen, ozone, peroxide and enzymes have also been shown. With oxygen based chemicals, desired brightness levels are often only reached at the expense of relatively high cost and/or low strength qualities, making the use of enzymes an interesting alternative. Two classes of enzymes have been shown to be useful in the bleaching of kraft pulp. Oxidative enzymes such as laccases and manganese peroxidases have been shown to bleach brownstocks to high brightnesses. However, this has only been recently demonstrated at the laboratory scale (2). In 1986 Viikari and co-workers (3) showed that xylanases can be used as a prebleaching step in conventional bleaching sequences. Xylanase treatment is effective on both softwood and hardwood kraft pulps (4, 5) and has been implemented in several kraft mills in North America and Europe (5-8). In 1994, six kraft mills in Canada treated at least 20% of their pulp with xylanase, totalling 7.5 million tonnes/year and representing 8% of the Canadian kraft pulp production (9). Xylanase pretreatment has a strong boosting effect on pulps being bleached with elemental chlorine and permits substantial reductions in both the chlorine charge required and the subsequent amounts of organochlorine generated (4, 5). Xylanase treatment is also effective on pulps produced with modern pulping processes such as superbatch and modified continuous cooking (10-13) and when it is incorporated into modern bleaching processes, including those that involve elemental chlorine-free (ECF) and totally chlorine-free (TCF) bleaching sequences (5, 12, 14-16). Xylanase treatment not only reduces the chemical loadings required to reach target brightness, certain reports also suggest that a xylanase treatment can improve the brightness ceiling of pulp bleached with peroxide (17, 18). As the enzyme appeared to be most effective at the beginning of the bleaching sequence where its application enhances subsequent chemical bleaching, the phenomenon has been coined 'bleach boosting' (19). Several mechanisms have been suggested to explain the bleach boosting effect of xylanase prebleaching. Kantelinen and co-workers (20) have proposed that the enzyme attacks xylan redeposited on the surface of the pulp at the end of the kraft cook. However, pulps from which the surface xylans had been removed with dimethyl sulfoxide still responded to xylanase prebleaching (19, 21). Similarly, xylanase prebleaching remained effective on pulps containing low amounts of redeposited xylan, such as those produced with flow-through and extended cooking methods (11, 12, 22). More recent work using mechanical peeling indicated that the outer surface of pine fibers was not enriched in xylan deposits and that its removal did not inhibit xylanaseaided bleaching (23, 24). A comparison of the outer and inner fractions of pulp fiber walls showed a surprisingly low bleachability of the outer layer during xylanaseaided peroxide bleaching (25). These authors suggested that bleachability depended on the composition of the lignin-carbohydrate complex (LCC) as well as the extent to which the outer layers were maintained during the pulping process. Other studies have indicated that xylanase treatments led to an extensive depolymerization of xylan

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

46

ENZYMES FOR PULP AND PAPER PROCESSING

without solubilization (26) and the liberation of lignin-carbohydrate complexes (27). Other evidence suggests that the release of chromophores may play an important role (28, 29). The exact mechanism of xylanase prebleaching thus remains unclear, although several hypotheses have been made concerning the nature of the target xylan (30). Possible substrates include: xylan in lignin-carbohydrate complexes; xylan that physically entraps residual lignin; xylan that modifies fiber porosity; and xylan that contains chromophoric carbohydrate units. Our research group has investigated the validity of these hypotheses. Our work with softwood and hardwood kraft pulps and model pulps, has shown that a xylanase treatment can cause both a bleach boosting as a direct brightening effect in peroxide bleaching sequences (31-34). Although xylan chromophores were formed under pulping conditions, they appeared to be of minor importance in xylanase bleaching (57, 35). Alternatively, L C C ' s could be isolated from kraft pulps and were shown to be hydrolysed by xylanases (36). Finally, a difference in the susceptibility of distinct fiber length fractions to xylanase bleaching was observed, with the smallest fibers showing the highest response (37). The research presented in this paper has focused on several aspects of xylanase bleaching of Douglas-fir kraft pulp. Size exclusion chromatography was used to assess the molecular mass distribution of the material solubilized by xylanase and that which becomes extractable in alkaline solutions. In addition, the bleaching activity of a purified 22 kDa β-1,4xylanase from Trichoderma harzianum E58 was compared with a commercial xylanase preparation from Trichoderma longibrachiatum.

Materials and Methods Enzymes. The commercial xylanase studied, Irgazyme 40S-4X (Genencor, San Fransisco, C A , USA), was an enzyme preparation from a selected strain of Trichoderma longibrachiatum. It contained a mixture of several extracellular enzymes but was essentially free of cellulases. The purified enzyme studied, xylanase D, was the 22 kDa, pi 9.4 xylanase from Trichoderma harzianum E58 (38). The assay described by Bailey et al. (39) was used with birchwood xylan as substrate to measure xylanase activity at pH 7 for Irgazyme and pH 5 for xylanase D. Each nkat of activity represents the release of 1 nmol xylose equivalent per second. Kraft Pulp. Brownstock (unbleached, never dried kraft pulp) derived from Douglasfir (Pseudotsuga menziesii) was prepared by Mr. Wai Gee in the pilot plant of the Pulp and Paper Research Institute of Canada (Vancouver, B.C.). A l l pulps were washed extensively by screening with a 200 mesh screen in the Bauer-McNett fiber length classifier. The composition of the pulp was determined as: glucose 83.1%; xylose 4.75%; mannose 3.99%; galactose 0.48%; arabinose 0.36%; acid insoluble lignin 4.00% and acid soluble lignin 0.42%. Bleaching Conditions. The bleaching sequence used was as described before (33). A l l bleaching and extraction stages were done in polyester bags, while enzyme treatments of partially bleached pulps were done in polyethylene (Ziploc) bags. The

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

5. DE JONG ET AL.

Xylanase Treatment of Dou$as-Fir Kraft Pulp 47

pulps were mixed vigorously by hand at the start of each stage, and before filtrate samples were taken after all enzyme (X) and alkaline extraction (E) stages. The pulps were washed at 1% consistency with de-ionized water after each stage. Each time a pulp was drained the filtrate was passed through the pulp cake three times to collect the fines. Pulps were treated with a high loading of 400 nkat xylanase g pulp" or with the same amount of heat inactivated enzyme at 10% consistency. The start pH was 7.0 for Irgazyme and 4.8 for xylanase D. The reaction was carried out for 60 min at 50 °C. The filtrate was analyzed for total sugars, and approximately 40 ml was brought to pH 7 and subsequently freeze-dried with a Speed Vac plus SC210A centrifuge (Savant, Farmindale, N Y , USA). The Ε-stage conditions were 10% pulp consistency, 2% NaOH for 1 hour at 80 °C. For chelation (Q-stage) the pulp was adjusted to pH 5.5 with sulphuric acid and brought to a 3% consistency. The pulp was then incubated with Na *EDTA-2H 0 (1% loading based on dry weight of pulp) for 30 min at 50 °C. For the peroxide bleaching (P-stage) the pulp was brought to 10 % consistency and bleached with 4% H 0 , 2% NaOH and 0.05% M g S 0 - 7 H 0 for 3 hours at 80 °C. The bleached pulp was adjusted to p H 4.5, thoroughly washed with de-ionized water, and used to prepare optical handsheets.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

1

2

2

2

4

2

2

Brightness. Handsheets for measuring brightness were made from 4 g dry weight pulp (CPPA standard C.5). ISO-brightness of handsheets was measured on a Technibrite TB-1C (Technidyne Corp., New Albany, IN, USA). Both sides of each handsheet were read five times, and the overall average values calculated. Lignin Determination. The residual lignin in pulp samples was determined in duplicate using the microkappa method (TAPPI Useful Methods U M 246, 1991) with 0.5 g dry weight of pulp in 25 ml. Lignin and chromophore content in filtrate samples was analyzed by measuring absorbance at 280 and 457 nm, respectively. These samples were diluted with 50 m M Na-phosphate buffer, p H 7.0, to give readings between 0.2 and 0.7 A U . Total Sugar in Pulp Filtrates. The total sugars in the liquid samples were determined using the phenol-sulphuric acid method (40). Samples were also spiked with a 0.2 m M xylose standard in order to verify the assay, and absorbance of the reaction mixture was measured at 490 nm. Size Exclusion Chromatography. The molecular mass distribution of lignins and xylans was analyzed with Toyopearl HW-55S and HW-50S resins (TosoHaas, Montgomeryville, PA, USA), packed in series in two 0.5 χ 20 cm H R columns (Pharmacia, Uppsala, Sweden). The resins have a separation range for dextrans from 0.34 to 40 kDa (41). Elution with 0.3 M NaOH was carried out at 3.6 ml hour" using a Dionex D X 500 HPLC system, and monitored using a Dionex ED40 electrochemical detector and a Dionex AD20 absorbance detector (280 nm, pathlength 6 mm, set at low) in series (41). The Pulsed Ampherometric Detector (PAD, electrochemical detector) is a sensitive detector for carbohydrates, although other oxidizable compounds also register (41). Immediately prior to injection, the 1

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

48

ENZYMES FOR PULP AND PAPER PROCESSING

sample of freeze-dried filtrate was diluted to 5% of its original volume with 0.3 M NaOH and a 900 μΐ aliquot was mixed with 100 μΐ of an internal standard (vanillin, 5 mg/ml). The sample was then filtered through a Millipore 0.45 μιη H V filter (Millipore, Bedford, M A ) and 20 μΐ was injected for chromatographic analysis.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

Results Pulp Brightness. To assess the effectiveness of the two enzymes with respect to their ability to enhance peroxide bleaching, the ISO-brightness of optical handsheets was measured (Table I). Handsheets were made after all xylanase and control treatments (X, C., X Q P X , XQPC, CQPX, CQPC, XQPPX, XQPPC, CQPPX, CQPPC), peroxide bleaching steps (XQP, CQP, XQPP, CQPP) and alkaline extraction steps (XE, C E , X Q P X E etc). The results clearly show that a treatment with Irgazyme, a commercial xylanase preparation from Trichoderma longibrachiatum, caused a much larger increase in brightness than the purified xylanase D from Trichoderma harzianum E58. It was also found that a double xylanase treatment with Irgazyme, before and after peroxide bleaching, resulted in the highest final brightness. This was not the case with xylanase D, which was only marginally beneficial to the bleaching of Douglas-fir kraft pulps when it was applied after peroxide bleaching. Alkaline extraction increased the brightness of Douglas-fir brownstock and of pulp bleached by one peroxide stage. A n Irgazyme treatment of the brownstock led to a relatively large increase in brightness after alkaline extraction. However, alkaline extraction of xylanase treated pulps bleached by one peroxide step resulted in a marginal brightness increase compared to the pulps treated with heat inactivated enzyme. Although alkaline extraction decreased the brightness of pulps bleached by two peroxide stages, it did not decrease the brightness gain of the xylanase treatments relative to the control treatments (Table I). Carbohydrate solubilization. A l l control treatments at pH 7 and pH 5 released sugars from pulp with 0.63 mg/g pulp and 0.42 mg/g pulp, respectively. Size exclusion chromatography of these samples showed that the molecular mass of apparent carbohydrates had abinodal distribution (Figures 1A, 2 and 4). The smaller component had a molecular mass of 0.4 kDa while the larger component had a molecular mass of 1 kDa. In all cases, an enzyme treatment increased the total amount of sugars solubilized. The Irgazyme treatment released much more sugars (2-4.4 mg/g) than did the xylanase D treatment (0.4-1 mg/g pulp). On average this was four times greater at each corresponding bleaching stage. Chromophore solubilization. The filtrates obtained after the enzyme treatment and alkaline extraction were analyzed for compounds absorbing in the U V (280 nm) and visible (457 nm) range of the spectrum (Table II). Irrespective of when and how often an Irgazyme treatment was applied this enzyme treatment jeleased more U V Vis absorbing material than did the xylanase D treatment. Another significant difference between the two enzymes was observed after subsequent alkaline extraction, where Irgazyme treatments led to increases in the total amount of

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

X

c

b

X

C

-0.5

29.1

-0.1

28.8

a

0.2

30.0

1.2

29.7

XE

0.1

51.2

0.5

52.0

XQP

1.1

XX

0.2 -0.4 -0.2

CX XC XX

50.9

0.5

xc

cc

0.9

52.2

cx

cc

XQPX

-0.1

-0.4

0.3

51.3

1.2

0.5

1.2

52.4

XQPXE

0.3

68.1

1.0

67.7

XQPP

0.1

-0.1

. 0.4

67.5

1.7

1.2

0.9

67.7

XQPPX

0.24

0.05

0.39

67.48

1.79

1.18

0.79

67.38

XQPPXE

The handsheets were made directly after xylanase (X) and control treatments (C), after subsequent chelation (Q) and peroxide bleaching (P) and after an alkaline extraction (E) step. The averages of replicate experiments are given. The ISO-brightness values for all the handsheets which had received one or two control (C and CC) treatments are given. Absolute increases (or decreases) are given for all the handsheets which had received one (X, X C and CX) or two (XX) xylanase treatments.

Xylanase D

Irgazyme

b

x

ISO-brightness values of xylanase bleached Douglas-fir kraft pulp handsheets.

Table I

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

50

ENZYMES FOR PULP AND PAPER PROCESSING

0.08

400 ΙΑ)

Xylanase treated

I r g X

300

Douglas-fir brownstock

0.06

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

200 0.04

3

ι

100 J 0.02 PAD data

0.00 102

103

104

105

Molecular Mass (Da) 1.6

400 frg X E Alkaline extracts of 300

Douglas-fir Brownstock

200

ι

100

UVdata 102

103

104

105

Molecular Mass (Da)

Figure 1. 1A) Size exclusion chromatograms showing the molecular mass distribution of material solubilized from Douglas-fir kraft pulps after xylanase and control treatments. Irgazyme was applied at pH 7 and xylanase D at pH 5. P A D = pulsed amperometric detector, U V = absorbance at 280 nm. IB) Size exclusion chromatograms showing the molecular mass distribution of alkaline extracts from pulp after xylanase or control treatment. For analytical details see the materials and methods section.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Xylanase Treatment of Douglas-Fir Kraft Pulp

51

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

5. DE JONG ET AL.

Figure 2. Size exclusion chromatograms showing the molecular mass distribution of material solubilized from Douglas-fir kraft pulps by xylanase (CX, X X ) or control (ÇC, X C ) treatments. The pulps were treated with two xylanase or control treatments that were separated by one peroxide bleaching stage. 2A) Pulp treated with Irgazyme 2B) Pulp treated with xylanase D.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

52

ENZYMES FOR PULP AND PAPER PROCESSING

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

material solubilized while xylanase D often led to a decrease (Table II). The ratio of absorbances at 280 and 457 nm for enzyme filtrates was basically the same as that for their corresponding alkaline extracts (Table II). However, this ratio was generally three times higher for the material solubilized from peroxide bleached pulp as compared to unbleached pulp. Molecular Mass Distribution of the Solubilized Material. Xylanase treatment of Douglas-fir brownstock and peroxide bleached pulps released UV-absorbing material of around 3-10 kDa, while there were as many as three distinct PAD-positive peaks (Figures 1A, 2 and 4). The UV-detector registers lignin and lignin-like material, while the PAD-detector is a sensitive detector for carbohydrates. The majority of the PAD-positive material was always of a much lower molecular mass, i.e. smaller than 2 kDa, than the UV-absorbing material. There were substantial differences in the amount of material solubilized by xylanase D and Irgazyme. The latter enzyme always released more UV-absorbing and more PAD-positive material. It was noticeable that both Irgazyme and xylanase D released substantially more U V absorbing material after the pulp had been bleached by one or two peroxide steps. In all cases, there was not much difference between the amount released after one or two peroxide stages (Figures 2 and 4). A l l of the chromatographic data were in agreement with the amounts of UV-absorbing material measured in the reaction filtrates (Table II). With both enzymes, a xylanase treatment after one or two peroxide bleaching steps released material with higher average molecular mass than was obtained with a xylanase treatment of the brownstock (Figures 1 A , 2 and 4). A xylanase treatment before one or two peroxide bleaching stages did not have much influence on the amount or molecular mass of the material solubilized during the control treatment of bleached pulps (CC versus X C , Figures 2 and 4). However, it is clear that one Irgazyme treatment (CX) released more material than the second of two xylanase treatments (XX). A n alkaline extraction of a xylanase treated pulp solubilized more U V absorbing and PAD-positive material than an extraction of a control treated pulp (Figures I B , 3, 5). There was a considerable difference between Irgazyme and xylanase D in the total amount of material and the molecular mass of PAD-positive material extracted after the enzyme treatment. Irgazyme released substantial amounts of higher molecular mass compounds (0.6-3 kDa) which were almost completely absent in the xylanase D filtrates. Similarly, after one and two peroxide bleaching steps much higher molecular mass, PAD-positive material was extracted from the Irgazyme samples with NaOH, although, the differences between Irgazyme and xylanase D were much smaller. If the molecular mass distribution of material solubilized directly by the enzyme treatment was compared with the material subsequently extracted with NaOH, the latter material always had a higher molecular mass, irrespective of how many times the pulp had been bleached with peroxide (Figures 1, 2, 3, 4 and 5). After two peroxide bleaching stages there was no significant difference between the amount of the high molecular mass (5-20 kDa) UV-absorbing material solubilized by alkaline extraction after an Irgazyme or xylanase D treatment (Figure 5). However, there were still differences in the amounts of UV-absorbing and P A D -

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

0.37/39

0.12/3

0.04/2

c

X

0.13/5

X

C

a

1.36/777

7.45/663

2.70/120

0.67/75 0.22/9 0.55/75

CX XC XX

1.52/29

XX 0.28/6

0.01/-2

XC

cc

2.20/56

CX

0.56/75

7.21/675 CC

XQPX

XE

0.0S/-44

-0.10/77

-0.54/-77

2.88/94

OAS/24

0.16/3

0.86/39

1.99/64

XQPXE

-0.01/-77

-0.15/-72

0.06/-3

0.50/77

0.82/7

-0.12/-9

1.35/7

0.48/77

XQPPX

-1.827-56

-1.95/-56

-0.SS/-45

2.15/94

0.32/23

-0.27/-3

0.59/35

1.76/32

XQPPXE

The amounts of U V (280 nm, AUFS) and visible (457nm, mAUFS, in italic) absorbing materials were measured directly after xylanase (X) and control treatments (C), and after a subsequent alkaline extraction (E) step. The averages of replicate experiments are given. The absolute amounts of solubilized materials are given for all the pulps which had only received one or two control (C and CC) treatments. Absolute increases (or decreases) are given for all the pulps which had received one (X, X C and CX) or two (XX) xylanase treatments.

Xylanase D

Irgazyme

b

x

UV/Vis absorbing materials solubilized after control and xylanase treatments of Douglas-fir kraft pulps.

Table II

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

ENZYMES FOR PULP AND PAPER PROCESSING

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

54

Figure 3. Size exclusion chromatograms showing the molecular mass distribution of material solubilized from Douglas-fir kraft pulps with an alkaline solution. The pulps were treated with two xylanase and/or control treatments that were separated by one peroxide bleaching stage. 3A) Pulp treated with Irgazyme 3B) Pulp treated with xylanase D.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Xylanase Treatment of Douglas-Fir Kraft Pulp

55

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

5. DE JONG ET AL.

Figure 4. Size exclusion chromatograms showing the molecular mass distribution of material solubilized from Douglas-fir kraft pulps by xylanase (CX, X X ) or control (CC, X C ) treatments. The pulps were treated with two xylanase or control treatments that were separated by two peroxide bleaching stages. 4A) Pulp treated with Irgazyme 4B) Pulp treated with xylanase D.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

ENZYMES FOR PULP AND PAPER PROCESSING

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

56

Figure 5. Size exclusion chromatograms showing the molecular mass distribution of material solubilized from Douglas-fir kraft pulps after alkaline extraction. The pulps were treated with two xylanase and/or control treatments separated by two peroxide bleaching stages. 5A) Pulp treated with Irgazyme 5B) Pulp treated with xylanase D.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

5. DE JONG ET AL.

Xylanase Treatment of Douglas-Fir Kraft Pulp

57

positive material of intermediate molecular mass (0.6-3 kDa). In contrast, an alkaline extraction of brownstock treated with Irgazyme showed a substantial increase in material solubilized over the whole molecular mass range (Figure IB).

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

Discussion Irgazyme showed both a much stronger bleach boosting effect on unbleached pulp and a stronger direct brightening effect on peroxide bleached pulp when compared to xylanase D (Table I). Indeed, xylanase D hardly showed any bleach boosting effect, and in fact, led to a loss in brightness when the bleached pulp was subjected to another enzyme control treatment (compare CQP(P) with CQP(P)C and XQP(P)C). Although direct brightening did occur with xylanase D, it was marginal and, contrary to the results obtained with Irgazyme, a second xylanase treatment was not beneficial. It is well documented that not every xylanase is as effective in biobleaching of kraft pulps (29, 42, 43). The activity of a xylanase preparation is usually measured by the hydrolysis of an isolated xylan in a short-term assay, such as that used in the present study (39). However, this study has shown that even when the two different xylanases were applied on pulp with the same amounts based on their determined activity, the total amount of sugars released differed considerably. A similar result was also observed using two xylanases purified from T. reesei (42). It would appear that conventional activity assays do not correlate well with hydrolysis rates occurring in pulps, nor with an enzyme's effectiveness in enhancing pulp bleaching. Two families of xylanases have now been distinguished according to their amino acid sequence (44). Most of the pulp bleaching work carried out with purified xylanases has used enzymes from family 11. In particular, two family 11 xylanases from Trichoderma reesei have been examined extensively (16, 42, 45, 46). The enzyme with the lower isoelectric point (pi 5.5) was much more effective in solubilizing sugars from pulp and in enhancing pulp brightness than was the one with a pi of 9. Interestingly, the optimal pH for the activity of these two enzymes on soluble xylan differed from that for their optimal activity on pulp (42). The two enzymes also differed in their response to the chelation stage, with the pi 9 enzyme being less tolerant (16). Part of this difference may be attributed to charge interactions between pulp and enzyme (16, 45). Two xylanases from Streptomyces sp. have also been compared for their bleaching effect on both softwood and hardwood kraft pulps. X y l l a is a low molecular mass, high pi xylanase and xyl 3 is a high molecular mass, low pi xylanase. At pH 9.0 the action patterns of the two enzymes were similar. However, xyl 3 released 12% more chromophores from hardwood and 30% more from softwood pulp than did xyl la. Both enzymes enhanced brightness while reducing chemical demand, although xyl 3 was more effective (29). Commercial xylanase preparations also vary in their effectiveness in pulp bleaching (13, 32, 34, 47-52) Although, this may be due to differences in their pH and temperature optima, the formulation of the enzyme preparations and contamination with other proteins would likely contribute to the observed differences. From our comparison of Irgazyme with Pulpzymes H B and H C at equal

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

58

ENZYMES FOR PULP AND PAPER PROCESSING

enzyme dosages (Novo Nordisk, Denmark) (32, 34), we hypothesized that the higher brightnesses obtained with Irgazyme may be explained by a synergistic action of different enzymes in this commercial preparation because the Pulpzymes were highly purified products of individual xylanases (32, 34). Synergism has been noted among distinct xylanases from Streptomyces sp. in the prebleaching of softwood but not of hardwood pulp (29). However, the differences between treatments with Irgazyme and xylanase D might also depend on whether Irgazyme is more tolerant to the reaction conditions, such as the requirements for metal ions (16) or the much lower pH used with the xylanase D enzyme. It was apparent that after one or two Irgazyme treatments, there was always an increase in the amount of UV-Vis absorbable material that could be extracted by alkali. This increase in lignin extractability has often been detected as an increase in absorbance of the extract at 280 nm and by a drop in the kappa number of the pulp (12, 33, 55-55). It has also been reported that the molecular mass of the lignin extracted after a xylanase treatment tends to be larger (12, 53, 54, 56). In our work the molecular mass of lignin extracted from Irgazyme-treated brownstock was much larger than that from the control pulp (Figure IB). However, the differences in molecular mass of the alkaline extracts of the control and enzyme treated pulps were already marginal after one peroxide bleaching stage (Figure 3) and were completely absent after two peroxide bleaching stages (Figure 5). The release of higher molecular mass, lignin-like material would apparently suggest that xylanase treatments affect the porosity of brownstock pulp. However, xylanases have been reported to decrease the water retention value of pulp (57, 58), with a corresponding increase in pulp freeness (58). These results therefore suggest there is a decrease in pulp swelling. However, since xylan is relatively hydrophillic, it is possible that its removal reduces the capacity of wood fibers to hold water. Therefore, the solute exclusion method (59) seems a more appropriate method for measuring fiber porosity because this method does not apply force on the fibers and relies on the diffusion of probes in the aqueous phase. To-date we have not been able to resolve any changes in the microporosity of pulp fibers as a result of xylanase treatment using this method (unpublished results). Another interesting point was that the lignin-like macromolecules directly solubilized from peroxide bleached pulps (Figures 3 and 5) were substantially larger than those solubilized from the brownstock (Figure IB), irrespective of whether they were produced during xylanase or control treatments. Since a xylanase treatment released higher molecular mass lignin from peroxide bleached pulps than from the brownstock, this is an indication that different kinds of materials were solubilized when a xylanase treatment was applied at different points in the bleaching sequence. However, this observation is probably not completely conclusive as the molecules could be subjected to all kinds of association/dissociation interactions and other modifications under alkaline conditions (41, 60). Nevertheless, it seems that the increased extractability of high molecular mass, lignin-like material after xylanase treatment of brownstock can also be achieved by peroxide bleaching. This result raises doubts concerning the role of lignin entrapment in the mechanism with which xylanase enhances peroxide bleaching. Thus it seems unlikely that the bleach boosting effect on peroxide bleaching

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

5. DE JONG ET AL.

Xylanase Treatment of Doug^as-Fir Kraft Pulp

59

is solely the result of high molecular mass compounds being made extractable by xylanase. Indeed our previous results have suggested that the role of high molecular mass lignin might be related to its abundance in shorter pulp fibers than to its entrapment underneath fiber surfaces (57). Other results suggested a role for lignincarbohydrate complexes (LCC's) (31, 36, 61). In the present work some P A D positive material did co-elute with UV-absorbing material during size exclusion chromatography, although the majority of the UV-absorbing material solubilized from Douglas-fir kraft pulp was larger than the PAD-positive material. This result would suggest that fragments of L C C ' s are present in the material solubilized during xylanase treatment and subsequent alkaline extraction. Other chromatographic and spectroscopic techniques should be used to verify this apparently close association between part of the lignin and carbohydrate components. Conclusion Although the mechanism of xylanase-aided bleaching is still unclear, a prevalent thought is that the enzymes act by enhancing pulp bleachability without directly brightening the pulp. This mechanism is generally accepted both because a xylanase treatment is not expected to directly modify lignin, which is the major contributor to pulp colour and because it permits chemical savings during subsequent pulp bleaching. Immediately after the enzyme stage there is nevertheless a drop in the kappa number of the pulp and an increase in the amounts of lignin that are solubilized and become extractable with alkali. The extractable lignin also tends to have a larger molecular mass after xylanase pretreatment of kraft pulp. However, the present work has shown that even larger fragments could be extracted from peroxide bleached pulp, with or without xylanase treatment. Therefore, it seems unlikely that a xylanase treatment would yield a bleach boosting effect only by increasing the extractability of high molecular mass compounds in a peroxide bleaching sequence. The presented work again showed that distinct xylanase preparations have quite different capacities to enhance pulp bleaching and that certain xylanases can be applied later in the bleaching sequence. Indeed, the final brightness achieved by xylanase post-treatment can be as high or higher than that achieved with xylanase prebleaching. Although bleach boosting could still be observed in the xylanase prebleached pulps where direct brightening is small or absent, its importance to pulp bleaching is now open to question. Acknowledgments We like to thank the Pulp and Paper Research Institute of Canada (Vancouver) for the preparation of the kraft pulp and the use of their handsheet making and testing laboratories. The work was partly financed by grants from the Science Council of British Columbia and the Natural Sciences and Engineering Research Council of Canada.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

60

ENZYMES FOR PULP AND PAPER PROCESSING

Literature Cited 1. 2. 3.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

4. 5. 6. 7. 8. 9. 10. 11. 12. 13. 14. 15.

16. 17. 18. 19. 20. 21. 22. 23. 24. 25. 26. 27.

Pryke, D.C.; McKenzie, D.J. Pulp Pap. Can. 1996, 97(1), 27-29. Paice, M.G.; Bourbonnais, R.; Reid, I.D. Tappi J. 1995, 78(9), 161-169. Viikari, L.; Ranua, M.; Kantelinen, Α.; Sundquist, J.; Linko, M. Proc. 3rd Int. Conf. Biotechnol. Pulp Pap. Ind. 1986, pp. 67-69. Senior, D.J.; Hamilton, J.; Bernier, R.L.; du Manoir, J.R. Tappi J. 1992, 75(11), 125-130. Viikari, L.; Kantelinen, Α.; Sundquist, J.; Linko, M. FEMS Microbiol. Rev. 1994, 13, 335-350. Jurasek, L.; Paice, M.G. Proc. Int. Symp. Poll. Prev. Manufac. Pulp Pap., 1992, pp. 105-107. Fastén, H. Proc. Non-Chlorine Bleach. Conf. 1993, paper 18. Kukkonen, K.; Reilama, I. Proc. Non-Chlorine Bleach. Conf. 1993, paper 20. Tolan, J.S., Olson, D. Dines, R.E. Pulp Pap. Can. 1995, 96(12), 107-110. Yang, J.L.; Cates, D.H.; Law, S.E.; Eriksson, K-E.L. Tappi J. 1994, 77(3), 243-250. Suurnäkki, Α.; Buchert, J.; Viikari, L. Proc. 48 Appita Annu Gen. Conf., 1994, pp. 169-172 Suurnäkki, Α.; Kantelinen, Α.; Buchert, J.; Viikari, L. Tappi J. 1994, 77(11), 111-116. Allison, R.W.; Clark, T.A.;Suurnäkki,A. Appita 1996, 49, 18-22. Scott, B.P.; Young, F.; Paice, M.G. Pulp Pap. Can. 1993, 94(3), 57-61. Lundgren, K.R.; Bergkvist, L.; Högman, S.; Jöves, H.; Eriksson, G.; Bartfai, T.; van der Laan, J.; Rosenberg, E.; Shoham, Y. FEMS Microbiol. Rev. 1994, 13, 365-368. Buchert, J.; Viikari, L. Paperi ja Puu 1995, 77(9), 582-587. Tolan, J.S. Proc. Non-Chlorine Bleach Conf. 1993, paper 40. Pham, P.L.; Alric, I.; Delmas, M. Appita 1995, 48, 213-217. Pedersen, L.S.; Kihlgren, P.; Nissen, A.M.; Munk, N.; Holm, H.C.; Choma, P.P. Tappi Proc. Pulp. Conf. 1992, pp. 31-37. Kantelinen, Α.; Hortling, B.; Ranua, M.; Viikari, L. Holzforschung 1993, 47, 29-35. Holm, H.C.; Skjold-Jørgensen, S.; Munk, N.; Pedersen, L.S. Proc. 1992 Pan-Pac Pulp Pap. Technol. Conf. 1992, Vol A, 53-57. Hortling, B.; Turunen, E.; Sundquist, J. Nord. Pulp Pap. Res. J. 1992, 7, 144151. Suurnäkki, Α.; Heijnesson, Α.; Buchert, J.; Westermark, U.; Viikari, L. Proc. 8th Int. Symp. Wood Pulp. Chem. 1995, Vol. III, pp. 237-242. Suurnäkki, Α.; Heijnesson, Α.; Buchert, J.; Viikari, L.; Westermark, U. J. Pulp Paper Sci. 1996, 22, J43-J47. Leite, M.; Eremeeva, T.; Treimanis, Α.; Egle, V.; Bykova, T.; Purina, L.; Viesturs, U. Acta Biotechnol. 1995, 15, 199-209. Paice, M.G.; Gurnagul, N.; Page, D.H.; Jurasek, L. Enzyme Microb. Technol. 1992, 14, 272-276. Yang, J.L.; Eriksson, K-E.L. Holzforschung 1992, 46, 481-488. th

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

5. DE JONG ET AL.

Xylanase Treatment of Douglas-Fir Kraft Pulp

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

28.

61

Patel, R.N.; Grabski, A.C.; Jeffries, T.W. Appl. Microbiol. Biotechnol. 1993, 39, 405-412. 29. Elegir, G.; Sykes, M.; Jeffries, T.W. Enzyme Microb. Technol. 1995, 17, 955-959. 30. Wong, K.K.Y.; Saddler, J.N. Crit. Rev. Biotechnol. 1992, 12, 413-435. 31. de Jong, E.; Wong, K.K.Y.; Saddler, J.N. Holzforschung 1996, in press. 32. Nelson, S.L.; Wong, K.K.Y.; Saddler, J.N.; Beatson, R.P. Pulp Pap. Can. 1995, 96(7), 42-45. 33. Wong, K.K.Y.; Martin, L.A.; Gama, F.M.; Saddler, J.N.; de Jong, E. 1996, Submitted. 34. Wong, K.K.Y.; Nelson, S.L.; Saddler, J.N. J. Biotechnol. 1996, in press. 35. Wong, K.K.Y.; Clarke, P.; Nelson, S.L. ACS Symp. Ser. 1995, 618, 352-362. 36. Wong, K.K.Y.; Yokota, S.; Saddler, J.N.; de Jong, E. J. Wood Chem. Technol. 1996, in press. 37. Mansfield, S.D.; Wong, K.K.Y.; de Jong, E.; Saddler, J.N. Appl. Microbiol. Biotechnol. 1996, in press. 38. Maringer, U.; Wong, K.K.Y.; Saddler, J.N.; Kubicek, C.P. Biotechnol. Appl. Biochem. 1995, 21, 49-65. 39. Bailey, M.J.; Biely, P.; Poutanen, K. J. Biotechnol. 1992, 23, 257-270. 40. Dubois, M.; Gilles, Κ.Α.; Hamilton, J.K.; Rebers, P.Α.; Smith, F. Anal. Chem. 1956, 28, 350-356. 41. Wong, K.K.Y.; de Jong, E. J. Chromatogr. A 1996, 737, 193-204. 42. Buchert, J.; Ranua, M.; Kantelinen, Α.; Viikari, L. Appl. Microbiol. Biotechnol. 1992, 37, 825-829. 43. Da Silva, R.; Yim, D.K.; Park, Y.K. Rev. Microbiol. 1994, 25, 112-118. 44. Henrissat, B.; Bairoch, A. Biochem. J. 1993, 293, 781-788. 45. Buchert, J.; Tenkanen, M.; Pitkänen, M.; Viikari, L. Tappi J. 1993, 76(11), 131-135. 46. Tenkanen, M.; Puls, J.; Poutanen, K. Enzyme Microb. Technol. 1992, 14, 566-574. 47. Allison, R.W.; Clark, T.A.; Ellis, M.J. Appita 1995, 48, 201-206. 48. Lavielle, P. Proc. EU CE PA Int. Environ. Symp. 1993, Vol. 1, 151-160. 49. Bajpai, P.; Bhardwaj, N.K.; Bajpai, P.K.; Jauhari, M.B. J. Biotechnol. 1994, 38, 1-6. 50. Brown, J.; Cheek, M.C.; Jameel, H.; Joyce, T.W. Tappi J. 1994, 77(11), 105-109. 51. Leduc, C.; Daneault, C.; Delauois, P.; Jaspers, C.; Pennickx, M. Appita 1995, 48, 435-439, 448. 52. Vicuña, R.; Oyarzún, E.; Osses, M. J. Biotechnol. 1995, 40, 163-168. 53. Buchert, J.; Siika-aho, M.; Ranua, M.; Kantelinen. Α.; Viikari, L.; Linko, A. Proc. 7th Int. Symp. Wood Pulp. Chem. 1993, Vol 2, 664-632. 54. Hortling, B.; Korhonen, M.; Buchert, J.; Sundquist, J.; Viikari, L. Holzforschung 1994, 48, 441-446. 55. Allison, R.W.; Clark, T.A. Tappi J. 1994, 77(7), 127-134. 56. Kantelinen, Α.; Suurnäkki, Α.; Buchert, J.; Hortling, B.; Viikari, L. Proc. 7th Int. Symp. Wood Pulp. Chem. 1993, Vol 2, 626-632.

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.

62 57. 58.

Saake, B.; Clark, T.;Puls,J. Holzforschung 1995, 49, 60-68. Siles, J.; Vidal, T.; Colom, J.F.; Torres, A. Proc. 8th Int. Symp. Wood Pulp. Chem. 1995, Vol. II, 391-396. Stone, J.E.; Scallan, A.M. Cellul. Chem. Technol. 1968, 2, 343-358. Dutta, S.; Garver Jr, T.M.; Sarkanen, S. ACS Symp. Ser. 1989, 397, 155-176. Yokota, S.; Wong, K.K.Y.; Saddler, J.N.; Reid, I.D. Pulp Pap. Can. 1995, 96(4), 39-41.

Downloaded by UNIV OF MASSACHUSETTS AMHERST on May 30, 2018 | https://pubs.acs.org Publication Date: November 21, 1996 | doi: 10.1021/bk-1996-0655.ch005

59. 60. 61.

ENZYMES FOR PULP AND PAPER PROCESSING

Jeffries and Viikari; Enzymes for Pulp and Paper Processing ACS Symposium Series; American Chemical Society: Washington, DC, 1996.