Insights into Sodium-ion Transfer at Na/NASICON Interface Improved by Uniaxial Compression Yasuhiro Uchida, George Hasegawa, Kazunari Shima, Miki Inada, Naoya Enomoto, Hirofumi Akamatsu, and Katsuro Hayashi ACS Appl. Energy Mater., Just Accepted Manuscript • DOI: 10.1021/acsaem.9b00250 • Publication Date (Web): 03 Apr 2019 Downloaded from http://pubs.acs.org on April 4, 2019
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Insights into Sodium-ion Transfer at Na/NASICON Interface Improved by Uniaxial Compression Yasuhiro Uchida,† George Hasegawa,†,* Kazunari Shima,† Miki Inada, ‡ Naoya Enomoto, § Hirofumi Akamatsu,† and Katsuro Hayashi†,*
† Department
of Applied Chemistry, Graduate School of Engineering, Kyushu University, 744 Motooka, Nishi-ku, Fukuoka, 819-0395, Japan
‡ Center
of Advanced Instrumental Analysis, Kyushu University, Kasuga, Fukuoka 8168580, Japan
§ National
Institute of Technology, Ariake College, Omuta, Fukuoka 836-8585, Japan
ACS Paragon Plus Environment
1
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 2 of 53
KEYWORDS: Na-ion battery; activation energy; charge transfer; solid electrolyte; allsolid-state battery
ACS Paragon Plus Environment
2
Page 3 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
ABSTRACT
A robust ceramic solid electrolyte with high ionic conductivity is a key component for all-solid-state batteries (ASSBs). In terms of the demand for high-energy-density storage, researchers have been tackling various challenges to use metal anodes, where a fundamental understanding on the metal/solid electrolyte interface is of particular importance. The Na+ super ionic conductor, so-called NASICON, has high potential for applying to ASSBs with a Na anode due to its high Na+ ion conductivity at room temperature, which has been, however, faced a daunting issue of the significantly large interfacial resistance between Na and NASICON. In this work, we have successfully reduced the interfacial resistance as low as 14 Ω cm2 at room temperature by a simple mechanical compression of a Na/NASICON assembly.
We also demonstrate a
fundamental study on the Na/NASICON interface in comparison with the Na/β”-alumina counterpart by means of the electrochemical impedance technique, which elucidates a stark difference between the activation energies for interfacial charge transfer: ~0.6 eV for Na/NASICON and ~0.3 eV for Na/β”-alumina. This result suggests the formation of
ACS Paragon Plus Environment
3
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 4 of 53
a Na+-conductive interphase layer in pressing Na metal on NASICON surface at room temperature.
1. Introduction Recent upsurge of research interest in all-solid-state batteries (ASSBs) as a nextgeneration energy storage device with high energy density and safety puts a worldwide spotlight on ceramic ionic conductors.1,2 As compared with the Li-ion secondary battery with a liquid electrolyte, the major drawbacks lie in the relatively low ionic conductivity of solid electrolytes and the significantly high interfacial resistance between solid electrolytes and electrode materials (solid/solid interface).3 With respect to the former point, extensive efforts to explore fast ionic conductors have developed a variety of solid electrolyte candidates to date.
As for the Li+ ion conductors, for example, their
conductivities at room temperature reach the order of 10–3 S cm–1 for oxide-based compounds4-6 while some sulfide ceramics exhibit beyond 10–2 S cm–1, which is comparable to the liquid electrolytes.7,8 On the other hand, the latter point still remains
ACS Paragon Plus Environment
4
Page 5 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
a formidable challenge especially for the ASSBs using a Li metal anode due to the poor stability of those electrolytes in contact with Li, forming a highly resistive solid electrolyte interphase (SEI).2,9,10 Although some strategies such as doping,11-14 coating15,16 and microstructural designing17-19 have been proposed for obtaining a solid electrolyte with improved stability in relation to the garnet-type Li7La3Zr2O12 (LLZO), another critical issue of the short-circuit plagued by dendrite formation is yet to be solved.20-25 In view of reducing battery cost, Na+-based ASSBs are fascinating due to the abundant Na resource, which boosts the demand for new Na+ ion conductors with superior conductivity.26-29 However, the emerging fast Na+ ion conductors again suffer from the interfacial problem in contact with Na metal, as is the case with the Li+ ion conductors.30 Meanwhile, the research on fast Na+ ion conductors has a longer history than the Li+ counterpart since the advent of β-alumina in 1960s followed by Na+ super ionic conductor (NASICON).31 A great deal of efforts were dedicated in the subsequent decades, which elucidated their stability against Na metal, ionic conduction pathways, effects of doping and so on.31-33 In this context, researchers have revisited the use of those well-investigated ceramics, in particular NASICON, which shows a higher
ACS Paragon Plus Environment
5
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 6 of 53
conductivity than β-alumina at room temperature. Nevertheless, only a few have been reported on the solid/solid interface between Na and NASICON because Na+ ion conductors were first developed as a solid electrolyte aiming at a rechargeable sodiumsulfur (NAS) battery operated at 300–350 °C, where both Na and S electrodes are in liquid form.34,35 Recently, Goodenough and co-workers documented that the NASICON surface is incompatible with Na metal at ambient condition, which is responsible for a large interface resistance between Na and NASICON.36 The poor contact also precludes a uniform Na+ flux across the interface, leading to severe dendrite formation and rapid short-circuit. They concluded that the fabrication of a good interlayer between Na and NASICON is a key to solve the overall issue and put forward the pretreatment of NASICON with Na melt to form a favorable SEI. In this study, we have tackled this crux by a direct approach: a uniaxial compression loaded on a Na/NASICON assembly. It was revealed that the high-pressure pressing can effectively reduce the resistance due to the improved interfacial contact. Here, we also discuss the activation energy of Na+ ion transfer at the solid/solid interface in comparison with Na/β”-alumina.
ACS Paragon Plus Environment
6
Page 7 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
2. Experimental 2.1 Synthesis of NASICON mother powder Reagent grade ZrO2, SiO2 and Na3PO412H2O (Purity of 98 %, 99.9 %, and 99 %, respectively; purchased from Kojundo Chemicals, Japan) were weighed to obtain a composition of Na3Zr2Si2PO12, and mixed by planetary ball milling with zirconia balls in ethanol using a Pulverisette 6 milling machine (Frichche, Germany) at 150 rpm for 1 h. The mixture was calcined at 1100 °C for 12 h. The calcined powder was pulverized by ball milling at 150 rpm for 18 h with zirconia balls and ethanol. The dried powder was screened with a sieve of 355 µm to obtain the fine NASICON mother powder. 2.2 Synthesis of sintered NASICON electrolyte The NASICON fine powder was pressed into a pellet followed by the cold isostatic pressing (CIP) at 200 MPa for 5 min.
Then, the pellet was placed in an alumina
crucible, covered with the NASICON mother powder, and calcined at 1270 °C for 12 h in air. Thus obtained NASICON sintered compact was cut into thin discs with a thickness
ACS Paragon Plus Environment
7
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 8 of 53
of ~1.1 mm. Both surfaces of the NASICON disc were polished into ~1 mm thick with a rotary polisher (MA-150, Musashinodenshi Corp., Japan) using 9 µm and 3 µm diamond pastes (Hyprez®, ENGIS Japan Corp., Japan) in sequence.
The mirror-polished
samples were finally annealed again at 1100 °C for 30 min in the NASICON mother powder.
2.3 Synthesis of sintered β”-alumina electrolyte The β”-alumina electrolyte was prepared by the solid-state reaction similar to the NASICON pellets. The β”-alumina (Na1.67Mg0.67Al10.33O17) fine powder was synthesized by firing the stoichiometric mixture of γ-Al2O3, Na2CO3 and Mg(OH)2 (Kojundo Chemicals, Japan) at 1500 °C for 2 h in air followed by ball-milling at 300 rpm for 10 h with zirconia balls and ethanol. The obtained fine powder was pressed into a pellet and subjected to CIP at 200 MPa for 5 min. Then, the pellet was placed in an alumina crucible filled with the β”-alumina powder and calcined at 1650 °C for 30 min in air.
2.4 Characterization
ACS Paragon Plus Environment
8
Page 9 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Microstructure on sintered surface and fractured cross-section of the NASICON pellet was observed by field-emission scanning electron microscopy (FE-SEM) using an S-5200 SEM (Hitachi Ltd., Japan).
Crystal phases of the sintered products were
identified by powder X-ray diffractometry (XRD) using a D8 ADVANCE (Bruker AXS GmbH, Germany).
Bulk density for the sintered pellets was calculated by
[weight]/[volume], which was used for obtaining the relative density.
Compressive
mechanical testing was performed using a uniaxial electromechanical testing device (EZGraph, Shimadzu Corp., Japan) at a crosshead speed of 1.0 mm min–1.
X-ray
photoelectron spectroscopy (XPS; AXIS-ULTRA; Shimadzu Corp.) was performed for the surface elemental analyses of NASICON samples. The Na metal adhered on the NASICON electrolytes was dissolved in ethanol (EtOH) followed by drying under vacuum. The monochromatized X-ray Al K radiation (1486.6 eV) was used. The core levels were calibrated by reference to the first component of the C ls core level peak (unfunctionalized hydrocarbons) set at 284.5 eV. In the case of EtOH-washed samples, the surface was slightly etched by Ar-sputtering to remove impurities like organic and carbonate species.
ACS Paragon Plus Environment
9
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 10 of 53
2.5 Electrochemical test conditions The NASICON solid electrolytes with a thickness of 1 mm were employed for the electrochemical tests. To obtain an Au | NASICON | Au cell, Au electrodes were put on to the both sides of the NASICON pellet with Au paste (No.8556, Tokuriki Honten Co., Ltd., Japan), which was heated at 200 °C to remove organic moieties. A Na | NASICON | Na cell was also prepared by sandwiching a NASICON plate between two Na foils, which was subjected to a uniaxial compression at 0–30 MPa using an oil hydraulic press (MS05-100, Riken Kiki Co., Ltd., Japan) in an Ar-filled glove box. The typical holding time for pressing was 5 sec.
Electrochemical impedance spectroscopy (EIS) was
recorded using a 1260A impedance/gain-phase analyzer (Solartron Analytical, UK) with a bias voltage of 100 mV in a frequency range from 1 MHz to 10 Hz at different temperatures. The impedance data were analyzed using a fitting program (ZView 2; Solartron Analytical, UK).
Galvanostatic cycling tests were performed on the Na|
NASICON | Na cell subjected to 30 MPa compression prior to assembling the cell using a potentiostat/galvanostat apparatus (S1287; Solartron Analytical, UK). The charge and
ACS Paragon Plus Environment
10
Page 11 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
discharge tests were conducted at varied current densities with 30 min-duration per each step. The activation energy for the charge transfer at Na/solid electrolyte interface was calculated according to the Arrhenius equation (1): 1 𝑅
𝐴
𝐸𝑎
= 𝑇 exp ( ― 𝑘𝐵𝑇)
(1)
where R is the interface resistance, A is the pre-exponential factor, T is the temperature,
Ea is the activation energy, and kB is the Boltzmann constant.
3. Results and Discussion 3.1 Characterization of sintered NASICON pellet The NASICON with a composition of x = 2 in Na1+xZr2SixP3–xO12 (0 < x < 3), where the electrical resistivity is reported to be minimum,37 was employed in this study. The NASICON mother powder with the corresponding composition (Na3Zr2Si2PO12) was first prepared by the conventional solid state reaction, which was pressed into a pellet followed by sintering to obtain a well-densified NASICON ceramic body. As the surface
ACS Paragon Plus Environment
11
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 12 of 53
properties such as roughness and impurity of a solid electrolyte influence on the charge transfer at the electrolyte and electrode interface,17-19 the surface of the NASICON electrolyte was mirror-polished followed by annealing to cure the surface damage during polishing in order to minimize the individual difference among the specimens. Figure 1 (a) shows the surface microstructure of the representative NASICON pellet, signifying the smooth surface composed of densely packed grains with a size of submicrons to a few microns containing only a few voids. The cross-sectional SEM image in Figure 1 (b) verifies the whole pellet was well-densified. The typical relative density of the NASICON specimens was assessed as 97–98% based on the theoretical density of 3.27 g cm–3 for Na3Zr2Si2PO12. The XRD pattern for the NASICON pellet in Figure 1 (c) can be assigned to Na3Zr2Si2PO12 with a trace of monoclinic ZrO2 phase. The quality of the NASICON pellet was also examined in terms of the electrical conductivity.
ACS Paragon Plus Environment
12
Page 13 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Figure 1. (a,b) SEM images of the NASICON pellet after mirror-polishing: (a) pellet surface and (b) cross-section. (c) XRD pattern and appearance (inset) of the NASICON pellet. (d) Nyquist plot of the NASICON pellet with the blocking electrodes measured at 25 °C.
The Nyquist diagram of the Au | NASICON | Au cell is presented in Figure 1 (d). The profile exhibits a depressed semicircle in the frequency range from 1 MHz to 100 kHz and a near-vertical line at the lower frequencies. The former is attributed to the grain
ACS Paragon Plus Environment
13
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 14 of 53
boundary resistance in the NASICON electrolyte, while the latter is predominantly derived from a capacitive component corresponding to the blocking nature of the Au electrodes.
As the total resistance (bulk and grain boundary resistances) of the
NASICON pellet can be obtained from the intercept of the semicircle with the real axis at low frequency, the total conductivity was determined as 1.1 × 103 S cm1 at 25 °C, which is comparable to the value reported previously.37
3.2 Effect of uniaxial compression on Na/NASICON interface resistance The electrochemical property of the Na/NASICON interface was probed by using a Na | NASICON | Na symmetric cell. The AC impedance profile of the cell without any intentional compression is displayed in Figure 2 (a). The cell configuration used for this study involved a spring, which applied ca. 20 N corresponding to the uniaxial stress of approximately 0.25 MPa.
The impedance spectrum comprises a high-frequency
semicircular component similar to the cell with Au blocking electrodes (Figure 1 (d)) and another large semicircle in the low frequency range. When the impedance data was fitted with the equivalent circuit illustrated in the inset of Figure 2 (a), the low-frequency
ACS Paragon Plus Environment
14
Page 15 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
semicircle resistance and capacity resulted in 1.3 × 103 Ω cm2 and 1.2 × 107 F, respectively. As the capacitance values of 107–105 F is generally interpreted as an interface resistance between electrode and electrolyte,38 this resistance can be ascribed to the two Na/NASICON interfaces in the symmetric cell.
It follows that the
Na/NASICON interface resistance was determined as 6.6 × 102 Ω cm2, which is 6 times higher than the total resistance of the 1 mm-thick NASICON electrolyte (110 Ω cm2). A mechanical pressing of a metal electrode/solid electrolyte assembly is simple yet effective to improve the interfacial contact.11,13
In this research, the uniaxial
compression was applied to the NASICON pellet sandwiched between a pair of Na foils, as schematically shown in Figure 2 (b). Note that the pressed pellet was placed in the same cell described above, which means that the pressure that the Na/NASICON/Na assemblies experienced during the electrochemical test came solely from the spring (~0.25 MPa). We have also confirmed by the mechanical test that the NASICON pellet shows a linear elastic behavior without any eternal strain after deloading within the pressure range in this study.
ACS Paragon Plus Environment
15
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 16 of 53
Figure 2. (a) Nyquist plot of the Na | NASICON | Na cell without compression prior to the cell assembly. The equivalent circuit for fitting is displayed in the inset. (b) Schematic illustration of the uniaxial compression of the Na/NASICON assembly.
(c) Nyquist plots for the Na |
NASICON | Na cells with pressing at varied pressures. (d) Variation of the areal resistances for the NASICON total resistance (RNASICON) and the Na/NASICON interface resistance (Rinterface) as a function of the uniaxial compression pressure.
Figure 2 (c) shows the Nyquist plots for the samples pressed with different uniaxial pressures. All the spectra consist of a small semicircular portion and a semicircle. The
ACS Paragon Plus Environment
16
Page 17 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
curve fitting was performed using the equivalent circuit as is the case with the spectrum in Figure 2 (a), and the capacitance values of 0.5–1.6 × 105 F were obtained for the low-frequency semicircle in each spectrum. Hence, the low-frequency semicircles are attributable to the Na/NASICON interface resistance. The fitting results are summarized in Figure 2 (d), where the NASICON total resistance (bulk and grain boundary) and the interface resistance are separately plotted as a function of the compressing pressure. The similar NASICON total resistivities testify that the electrical properties of the NASICON pellets for these measurements were almost identical. It is noteworthy that the interface resistance dramatically decreased by pressing the Na/NASICON/Na assembly. As a result, the interface resistance decreased to 14 Ω cm2 by pressing at 30 MPa, which is an order of magnitude smaller than the total resistance of the 1 mmthick NASICON electrolyte and thereby equivalent to that for a 100 µm-thick electrolyte. It should be also pointed out that the typical charge transfer resistance of Na anode in a carbonate-based organic electrolyte ranges from 700–1000 Ω cm2 due to the highly resistive SEI layer.39
ACS Paragon Plus Environment
17
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 18 of 53
Figure 3 (a) presents the impedance spectra recorded at different temperatures and the logarithmic interface resistances calculated from these impedance data are plotted as a function of temperature in Figure 3 (b). The activation energy for Na+ ion transfer at the Na/NASICON interface was evaluated from the corresponding Arrhenius plot (Figure 3 (c)), providing 0.60 eV, 0.67 eV, 0.53 eV and 0.63 eV for the Na/NASICON/Na assemblies pressed at 10 MPa, 14 MPa, 20 MPa and 30 MPa, respectively.
The
activation energy seems to be irrespective of the compression stress and amounts to approximately 0.6 eV.
ACS Paragon Plus Environment
18
Page 19 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Figure 3. (a,b) Temperature dependences of (a) the Nyquist plots and (b) the Na/NASICON interface resistances obtained by fitting for the Na | NASICON | Na cells with pressing at different pressures. (c) Arrhenius plots of the interface resistances for the Na | NASICON | Na cells with pressing at different pressures.
3.3 Insight into pressed Na metal on NASICON In the Li/LLZO system, it was reported that the heat-treatment at slightly below the melting point of Li (175 °C) can effectively reduce the interface resistance.19,21 However, it was found that the interface resistance of the Na | NASICON | Na cell at 25
ACS Paragon Plus Environment
19
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 20 of 53
°C after heating to 90 °C, which is slightly lower than the melting point of Na (98 °C), remained similar to the initial value as shown in Figure S1. This result indicates that the compression at > 10 MPa provides a better Na/NASICON interface in comparison with the pressing by the spring in the cell (~0.25 MPa) at 90 °C. In order to check the mechanical feature of a Na foil on pressing, the uniaxial compression test was performed on a Na plate at room temperature. A Na plate with a dimension of ca. (L) 12 mm × (W) 15 mm × (H) 4 mm was cut out from a Na block, which was sealedin a plastic bag in an Ar-filled glove box. The Na plate was taken out from the glove box and subjected to the compression test immediately. The same mechanical test was carried out on a Li plate as well for comparison. The metal surface maintained shiny after the mechanical tests. Figure S2 represents the load-strain curve for the representative Li and Na metal plates. Since the cross sectional area was substantially changed during pressing, the mechanical stress values based on the original plate dimension are presented in the graphs. Note that the loading curves might partially reflect the friction between the metal plate and a plastic bag. Both load-strain curves exhibit the similar mechanical
ACS Paragon Plus Environment
20
Page 21 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
behavior consisting of the initial elastic region followed by yielding and densification. As is well known, the Na plate was apparently softer than the Li plate in terms of elasticity and yield stress. Besides, the onset of the steep increase in loading force shifts to the larger strain for the Na metal, indicating that a Na electrode can deform to a larger extent in accordance with the surface microstructure of a solid electrolyte under the same compression pressure as compared with a Li electrode.
3.4 Insight into Na+ ion transfer at Na/NASICON interface Ion transfer at interfaces between two different electrolytes (solid/liquid or solid/polymer) were intensively investigated by Abe et al.40-43 They disclosed that the dominant factor changes depending not only on the type of electrolytes but also on the ion species (Li+ or Na+). In the case of Li+ ion transfer, the thorough desolvation of Li+ in an organic electrolyte is the rate-determining step for the both systems.40-42
By
contrast, in the case of Na+, the weaker Lewis acidity of Na+ than Li+ renders the activation barrier for desolvation smaller, and the extraction of Na+ ion from a solid electrolyte dominates the charge transfer at solid/liquid electrolyte interfaces.43
ACS Paragon Plus Environment
21
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 22 of 53
Nevertheless, regarding the Na+ ion transfer at a solid/poly(ethylene oxide)-based electrolyte interface, the desolvation process still remains rate-determining because of the strong interaction between Na+ and polymer. The activation energies associated with Na+ ion transfer are compiled in Table 1. In the present research, we have approximated the activation energy at Na/NASICON interface as about 0.6 eV, which lies between the activation energies of the NASICON/organic electrolyte and the NASICON/polymer electrolyte. In order to foster better understanding, we have also examined a different type of Na+-conducting ceramics, Na-β-alumina, which is renowned as a sustainable Na+ ion conductor33 and practically applied to the NAS battery developed by NGK Insulators Ltd. (Japan) and Tokyo Electric Power Co. (Japan) as well as the ZEBRA battery by FZ Sonick SA (Switzerland).34,35
Table 1. Activation energy for interfacial Na+ ion transfer.
Na
PEO
PC
DMSO
ACS Paragon Plus Environment
22
Page 23 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
NASICON
0.53–0.67 eV a
0.75 eV b,c
0.35 eV b,c
0.31 eV c,d
β”-Alumina
0.28 eV a
0.73 eV d
0.54 eV d
0.47 eV d
a
This study.
b
ref. 41.
c
NASICON with a composition of Na3Zr1.88Y0.12Si2PO12.
d
ref.
43.
A sintered pellet of the Mg2+-stabilized β”-alumina with a composition of Na1.67Mg0.67Al10.33O17 (1 mm thick) was employed for the electrochemical study as the aforementioned NASICON system. The XRD pattern in Figure 4 (a) evidences very few impurities in the sintered pellet. The relative density of the pellet was estimated as ca. 86%. As β”-alumina has good compatibility with Na metal,30 the pressure applied to the Na/β”-alumina assembly prior to the impedance tests was 2 MPa. Figure 4 (b) shows the Nyquist plots for the Na | β”-alumina | Na cells at different temperatures. Each spectrum is composed of two semicircles and the low-frequency portion with a capacitance of 2.5–5.1 × 105 F can be attributed to the interface resistance according to the fitting analysis similar to the NASICON system. Based on the semicircle at high frequencies, the total resistance (bulk and grain boundary) for β”-alumina was evaluated as 128 Ω cm2 at room temperature leading to the conductivity of 1.5 × 103 S cm–1. The
ACS Paragon Plus Environment
23
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 24 of 53
good agreement of the conductivity with the values reported previously30-34 assures the acceptable quality of the β”-alumina electrolyte. The small interface resistance of 21 Ω cm2 (25 °C) was observed, which is comparable to that at Na/NASICON with pressing at > 20 MPa.
Figure 4. (a) XRD pattern of the β”-alumina electrolyte. (b) Nyquist plots for the Na | β”alumina | Na cell measured at different temperatures.
(c,d) Arrhenius plots of the Na |
ACS Paragon Plus Environment
24
Page 25 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
NASICON | Na cells: (c) total conductivity of β”-alumina and (d) interface resistance at Na/β”alumina.
The Arrhenius plots for the Na | β”-alumina | Na are depicted in Figure 5 (c) and (d). The activation energy for the total conductivity of β”-alumina was calculated as 0.21 eV, which is in line with the reported value,33 while the value of 0.28 eV was obtained for the interfacial Na+ ion transfer at Na/β”-alumina, which is smaller than a half of that at Na/NASICON and similar to the interfacial Li+ ion transfer at Li/Nb-doped LLZO (0.31 eV).12 According to the previous report,43 the activation energies for Na+ ion transfer between solid and liquid electrolytes were reported to be higher for the β”-alumina solid electrolyte than for the NASICON (see Table 1).
This tendency is opposite to the
Na/solid electrolyte systems in this study. In addition, the activation energies at the NASICON/liquid electrolyte interfaces also lie in 0.31–0.35 eV.43 These systems with low activation energy were explained by the interfacial charge transfer free from the
ACS Paragon Plus Environment
25
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 26 of 53
desolvation process, which generally associates with high activation barrier (ca. 0.6 eV for the Li+ in typical organic electrolytes).40 One possible interpretation for the high activation energy at Na/NASICON is the constriction effect originated from the imperfect contacts between Na metal and NASICON.44,45 In this study, the mirror-polished NASICON plates were employed and high pressure was applied to make a good Na/NASICON contact.
However, it is
possible that the contact area gradually decreased during the repeated AC impedance tests.46 Fleig and Maier put forward that the similar activation energy values for the two semicircular components in the complex impedance plane signify the existence of geometrically imperfect contacts.45 In the present case, the activation energy for Na+ ion conduction in bulk and grain boundary of NASICON were evaluated as 0.22 eV and 0.75 eV, respectively (see Figure S3). These values are apparently different from the activation energy derived from the interfacial resistance at Na/NASICON, which indicates the small contribution of the ohmic constriction effect. As a different interpretation for the high activation energy at Na/NASICON interface obtained in this study, the presence of another barrier between Na and NASICON is
ACS Paragon Plus Environment
26
Page 27 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
proposed. As for the Li/solid electrolyte systems, the relatively high activation energy of ~0.63 eV was reported for the charge transfer at Li/lithium phosphorous oxynitride (LiPON).9 Although LiPON had been believed to be stable against Li metal for a long period,47 the formation of a thin passivation layer at the Li/LiPON interface was exemplified by Schwöbel et al.,48 which could be responsible for the high activation energy. We therefore came up with an assumption that NASICON outermost surface reacts with Na metal forming a sort of SEI layer, which might mediate the interface between Na and NASICON yet behaves as a barrier for the interfacial Na+ ion transfer. It is difficult to analyze the interphase because the Na metal stuck to the surface too strongly to be removed without chemical treatment. In this study, the Na metal was dissolved in EtOH followed by drying under vacuum for the XPS analysis. The obtained XPS spectra were displayed in Figure S4. The core-level spectra of the NASICON after Na-pressing are slightly different from those of the pristine NASICON; the peak shift to the lower binding energy is observed in the Na 1s, P 2p and Zr 3p spectra, whereas it is negligible in the Si 2p and O 1s spectra. In the case of Si 2p core-level spectrum, however, the band becomes broader by the Na-pressing. It is deduced that all the
ACS Paragon Plus Environment
27
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 28 of 53
changes in XPS spectra associates with the formation of reduced components by the reaction between NASICON and Na. Note that the EtOH washing and drying process probably changed the SEI layer, but the XPS results evidence the formation of Na/NASICON interphase. In addition, the similar XPS spectra for the samples before and after the AC impedance measurements prove that the activation energy of ~0.6 eV for the charge transfer at Na/NASICON is highly responsible for this SEI layer. The formation of interlayer species on NASICON surface has been already exemplified by Zhou et al.36
The literature reports that the NASICON surface was
hardly reacted with Na melt at 175 ºC because of the fairly low compatibility and thereby the non-wetting nature, while the reduction to form a black interlayer took place at 380 ºC. Comparing the XPS spectra of the interlayer species to our result in Figure S4, the larger peak shift to the lower energy is observed in the previous results. Hence, the SEI layer formed by Na-pressing at room temperature is less reduced than the interlayer formed by the reaction with Na melt at 380 ºC. We further examined the compatibility of Na and the SEI layer in heating beyond the solid/liquid phase transition of Na. Figure S5 shows the variation of electrical resistivity
ACS Paragon Plus Environment
28
Page 29 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
measured at 25 °C for the Na | NASICON | Na cell with a compression at 20 MPa before and after heating the Na/NASICON assembly at 150 °C for 30 min in an Ar atmosphere. It was found that the improved Na/NASICON interface resistance was completely spoiled. It follows that the SEI layer formed by Na-pressing is incompatible with Na melt and different from the interlayer reported previously.36 It is also noteworthy that this behavior is in stark contrast with the Li/Al-stabilized LLZO system demonstrated by Buschmann et al. previously,11 where the fusion of Li onto the solid electrolyte significantly decreased the interface resistance.
3.5 Cycling stability of NASICON electrolyte The improvement of Na/NASICON interface by pressing distinctly reduces the interface resistance between the Na electrode and NASICON solid electrolyte, which is expected to allow stable Na plating/stripping cycles. The DC cycling behavior of the Na | NASICON | Na cell was explored using a NASICON electrolyte with a thickness of 1 mm. We employed the similar method reported by Sharafi et al. to assess the critical current density (CCD), which is a benchmark current density for sustainability of a solid
ACS Paragon Plus Environment
29
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 30 of 53
electrolyte operated with metallic electrodes.21 It was confirmed that, without pressing, the cell shorting occurred at < 0.1 mA cm–2 due to the high cell voltage suffering from the high interface resistivity (see Figure S6). The higher resistivity enhances the local electric field at the tip of growing dendrites, which accelerates the metal propagation resulting in a more rapid short.36 Recent studies on Li metal electrode on various solid electrolytes validate that a shortcircuit takes place by the dendrite growth of metal both through transgranular pathway and between grain boundaries,22,49,50 which is hardly prevented by the Monroe and Newman strategy, where a solid electrolyte with adequately high mechanical strength can suppress the dendrite propagation.51
Porz et al. reported that Li filament can
penetrate even through a single-crystalline ceramic electrolyte by initial opening cracks against mechanical resistance followed by crack extension.49 It follows that the high mechanical stability and minimized surface roughness of a solid electrolyte are minimal requirements for blocking a short-circuit. This fact also underlines the importance of the metal/solid electrolyte interface; the key to use a metal anode is a stable interface that could minimize interfacial defects.49
ACS Paragon Plus Environment
30
Page 31 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
In this context, the nature of Na/NASICON interface formed by the uniaxial compression was examined by the galvanostatic cycling tests.
Figure 5 (a)
demonstrates the charge and discharge cycling results for the cell pressed at 30 MPa prior to the test at 25 °C.
By virtue of the small cell resistance with the reduced
interface resistivity,52 the cell was stably operated at up to 0.8 mA cm–2 (corresponding to the Na-plating/stripping capacity of 0.4 mAh cm–2). However, the gradual increase in voltage was observed at 0.9 mA cm–2, indicating the degradation of the Na | NASICON | Na cell probably due to the influence of Li dendrite propagation, and became out of order at 1.0 mA cm–2.
ACS Paragon Plus Environment
31
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 32 of 53
Figure 5. Galvanostatic cycling results of the Na | NASICON | Na cell with pressing at 30 MPa measured at (a) 25 °C and (b) 90 °C. The blue circle and arrow indicate the step where the large voltage change was observed.
In the Li | LLZO | Li system reported previously,21 the substantial increment of CCD by the elevation of operating temperature approaching the melting point of Li was demonstrated. This was explained by the improved Li/LLZO interfacial contact and the reduced charge transfer resistance. The galvanostatic cycling behavior at 90 °C in Figure 5 (b) signifies the further enhancement of CCD for the Na | NASICON | Na cell.
ACS Paragon Plus Environment
32
Page 33 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
The fairly small cell resistance at the elevated temperature allows the sustainable Na plating/stripping at up to 3 mA cm–2 corresponding to 1.5 mAh cm–2.52 However, these results indicate that the SEI layer formed by pressing Na on NASICON does not perfectly prevent forming Na filaments, and hence, more improvement of Na/NASICON interface is still necessary from a practical point of view.
4. Conclusions The mechanical compression of Na metal onto a NASICON solid electrolyte can effectively reduce the Na/NASICON interface resistance to 14 Ω cm2 by pressing at 30 MPa, which is comparable to the ionic conductivity for a 100 µm-thick NASICON electrolyte at room temperature.
The activation energy for the Na+ ion transfer at
Na/NASICON interface was evaluated as ca. 0.6 eV, which is fairly high as compared with those for Na/β”-alumina and NASICON/organic liquid electrolytes.
This result
suggests the formation of an interstitial layer between Na metal and NASICON by pressing Na metal even at room temperature.
ACS Paragon Plus Environment
33
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 34 of 53
As the reduced cell resistance results in the better short-circuit prevention, the Na | NASICON (1 mm thick) | Na cell experienced a short at < 1 mA cm–2. The further increase of critical current density is allowed by raising the operation temperature due to the enhancement of conductivity. From a practical viewpoint, the thickness of a solid electrolyte should be thinner than the NASICON plates used in this study (1 mm). It follows that the resistivity related to the bulk and grain boundary decreases, which is advantageous for the sustainability of Na plating/stripping. At the same time, however, the dendrite growth to short more readily occurs in the thinner electrolyte.
Hence,
further effort to block the dendrite formation is still required for high energy density ASSBs.
Supporting Information. The following files are available free of charge. Load-strain curves for the Li and Na metal plates; XPS spectra for the NASICON electrolytes before and after Na-pressing and impedance measurements; variation of
ACS Paragon Plus Environment
34
Page 35 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
the Nyquist plots for the Na | NASICON | Na cell during pressing followed by heating
AUTHOR INFORMATION
Corresponding Author * Dr. George Hasegawa E-mail:
[email protected] * Prof. Katsuro Hayashi E-mail: k.hayashi @cstf.kyushu-u.ac.jp
ACKNOWLEDGMENT
This work was supported by a Grant-in-Aid for Scientific Research (KAKENHI No. 26289235 and JP16H6440) from the Japan Society for the Promotion of Science (JSPS), and the Elements Strategy Initiative to Form Core Research Center, Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan. In addition, a part of this work was conducted in Kyushu University, supported by Nanotechnology Platform Program (Molecule and Material Synthesis) of MEXT.
ACS Paragon Plus Environment
35
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 36 of 53
REFERENCES
[1] Takada, K. Progress and prospective of solid-state lithium batteries. Acta Mater. 2013, 61, 759–770.
[2] Zhang, Z.; Shao, Y.; Lotsch, B.; Hu, Y.-S.; Li, H.; Janek, J.; Nazar, L. F.; Nan, C.-W.; Maier, J.; Armand, M.; Chen, L. New horizons for inorganic solid state ion conductors.
Energy Environ. Sci. 2018, 11, 1945–1976.
[3] Richards, W. D.; Miara, L. J.; Wang, Y.; Kim, J. C.; Ceder, G. Interface stability in solid-state batteries. Chem. Mater. 2016, 28, 266–273.
[4] Murugan, R.; Thangadurai, V.; Weppner, W. Fast lithium ion conduction in garnettype Li7La3Zr2O12. Angew. Chem. Int. Ed. 2007, 46, 7778–7781.
[5] Thangadurai, V.; Narayana, S.; Pinzaru, D. Garnet-type solid-state fast Li ion conductors for Li batteries: critical review. Chem. Soc. Rev. 2014, 43, 4714–4727.
ACS Paragon Plus Environment
36
Page 37 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
[6] Bachaman, J. C.; Muy, S.; Grimaud, A.; Chang, H.-H.; Pour, N.; Lux, S. F.; Paschos, O.; Maglia, F.; Lupart, S.; Lamp, P.; Giordano, L.; Shao-Horn, Y. Inorganic solid-state electrolytes for lithium batteries: mechanisms and properties governing ion conduction.
Chem. Rev. 2016, 116, 140–162.
[7] Kamaya, N.; Homma, K.; Yamakawa, Y.; Hirayama, M.; Kanno, R.; Yonemura, M.; Kamiyama, T.; Kato, Y.; Hama, S.; Kawamoto, K.; Mitsui, A. A lithium superionic conductor. Nat. Mater. 2011, 10, 682–686.
[8] Kato, Y.; Hori, S.; Saito, T.; Suzuki, K.; Hirayama, M.; Mitsui, A.; Yonemura, M.; Iba, H.; Kanno, R. High power all-solid-state batteries using sulphide superionic conductors.
Nat. Energy 2016, 1, 16030.
[9] Imanishi, N.; Hasegawa, S.; Zhang, T.; Hirano, A.; Takeda, Y.; Yamamoto O. Lithium anode for lithium-air secondary batteries. J. Power Sources 2008, 185, 1392–1397.
[10] Bron, P.; Roling, B.; Dehnen, S. Impedance characterization reveals mixed conducting interphases between sulfidic superionic conductors and lithium metal electrodes. J. Power Sources 2017, 352, 127–134.
ACS Paragon Plus Environment
37
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 38 of 53
[11] Buschmann, H.; Dölle, J.; Berendts, S.; Kuhn, A.; Bottke, P.; Milkening, M.; Heitjans, P.; Senyshyn, A.; Ehrenberg, H.; Lotnyk, A.; Duppel, V.; Kienle, L.; Janek, J. Structure and dynamics of the fast lithium ion conductor “Li7La3Zr2O12”. Phys. Chem.
Chem. Phys. 2011, 13, 19378–19392.
[12] Ohta, S.; Kobayashi, T.; Seki, J.; Asaoka, T. J. Power Sources 2012, 202, 332–335.
[13] Sudo, R.; Nakata, Y.; Ishiguro, K.; Matsui, M.; Hirano, A.; Takeda, Y.; Yamamoto, O.; Imanishi, N. Solid State Ionics 2014, 262, 151–154.
[14] Tsai, C.-L.; Roddatis, V.; Chandra, C. V.; Ma, Q.; Uhlenbruck, S.; Bram, M.; Heitjans, P.; Guillon, O. ACS Appl. Mater. Interfaces 2016, 8, 10617–10626.
[15] Han, X.; Gong, Y.; Fu, K.; He, X.; Hitz, G. T.; Dai, J.; Pearse, A.; Liu, B.; Wang, H.; Rubloff, G.; Mo, Y.; Thangadurai, V.; Wachsman, E. D.; Hu, L. Negating interfacial impedance in garnet-based solid-state Li metal batteries. Nat. Mater. 2017, 16, 572– 580.
ACS Paragon Plus Environment
38
Page 39 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
[16] Wang, C.; Gong, Y.; Liu, B.; Fu, K.; Yao, Y.; Hitz, E.; Li, Y.; Dai, J.; Xu, S.; Luo, W.; Wachsman, E. D.; Hu, L. Conformal, nanoscale ZnO surface modification of garnetbased solid-state electrolyte for lithium metal anodes. Nano Lett. 2017, 17, 565–571.
[17] Cheng, L.; Park, J. S.; Hou, H.; Zorba, V.; Chen, G.; Richardson, T.; Cabana, J.; Russo, R.; Doeff, M. Effect of microstructure and surface impurity segregation on the electrical and electrochemical properties of dense Al-substituted Li7La3Zr2O12. J. Mater.
Chem. A 2014, 2, 172–181.
[18] Cheng, L.; Chen, W.; Kunz, M.; Persson, K.; Tamura, N.; Chen, G.; Doeff, M. Effect of surface microstructure on electrochemical performance of garnet solid electrolytes.
ACS Appl. Mater. Interfaces 2015, 7, 2073–2081.
[19] Basappa, R. H.; Ito, T.; Yamada, H. Contact between garnet-type solid electrolyte and lithium metal anode: Influence on charge transfer resistance and short circuit prevention. J. Electrochem. Soc. 2017, 164, A666–A671.
[20] Ren, Y.; Shen, Y.; Lin, Y.; Nan, C.-W. Direct observation of lithium dendrites inside garnet-type lithium-ion solid electrolyte. Electrochem. Commun. 2015, 57, 27–30.
ACS Paragon Plus Environment
39
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 40 of 53
[21] Sharafi, A.; Meyer, H. M.; Nanda, J.; Wolfenstine, J.; Sakamoto, J. Characterizing the Li- Li7La3Zr2O12 interface stability and kinetics as a function of temperature and current density. J. Power Sources 2016, 302, 135–139.
[22] Cheng, E. J.; Sharafi, A.; Sakamoto, J. Intergranular Li metal propagation through polycrystalline Li6.25Al0.25La3Zr2O12 ceramic electrolyte. Electrochim. Acta 2017, 223, 85– 91.
[23] Raj, R.; Wolfenstine, J. Current limit diagrams for dendrite formation in solid-state electrolytes for Li-ion batteries. J. Power Sources 2017, 343, 119–126.
[24] Basappa, R. H.; Ito, T.; Morimura, T.; Bekarevich, R.; Mitsuishi, K.; Yamada, H. J.
Power Sources 2017, 343, 145–152.
[25] Yonemoto, F.; Nishimura, A.; Motoyama, M.; Tsuchimine, N.; Kobayashi, S.; Iriyama, Y. J. Power Sources 2017, 343, 207–215.
ACS Paragon Plus Environment
40
Page 41 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
[26] Hayashi, A.; Noi, K.; Sakuda, A.; Tatsumisago, M. Superionic glass-ceramic electrolytes for room-temperature rechargeable sodium batteries. Nat. Commun. 2012,
3, 856.
[27] Udovic, T. J.; Matsuo, M.; Tang, W. S.; Wu, H.; Stavila, V.; Soloninin, A. V.; Skoryunov, R. V.; Babanova, O. A.; Skripov, A.; Rush, J. J.; Unemoto, A.; Takamura, H.; Orimo, S. Exceptional superionic conductivity in disordered sodium decahydro-
closo-decaborate. Adv. Mater. 2014, 26, 7622–7626.
[28] Richards, W. D.; Tsujimura, T.; Miara, L. J.; Wang, Y.; Kim, J. C.; Ong, S. P.; Uechi, I.; Suzuki, N.; Ceder, G. Design and synthesis of the superionic conductor Na10SnP2S12.
Nat. Commun. 2015, 7, 11009.
[29] Banerjee, A.; Park, K. H.; Heo, J. W.; Nam, Y. J.; Moon, C. K.; Oh, S. M.; Hong, S.T.; Jung, Y. S. Na3SbS4: A soulution processable sodium superionic conductor for allsolid-state sodium-ion batteries. Angew. Chem. Int. Ed. 2016, 55, 1–6.
[30] Wenzel, S.; Leichtweiss, T.; Weber, D. A.; Sann, J.; Zeier, W. G.; Janek, J. Interfacial reactivity benchmarking of the sodium ion conductors Na3PS4 and sodium β-
ACS Paragon Plus Environment
41
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 42 of 53
alumina for protected sodium metal anodes and sodium all-solid-state batteries. ACS
Appl. Mater. Interfaces 2016, 8, 28216–28224.
[31] Anantharamulu, N.; Rao, K. K.; Rambabu, G.; Kumar, B. V.; Radha, V.; Vithal, M. A wide-ranging review on Nasicon type materials. J. Mater. Sci. 2011, 46, 2821–2837.
[32] Viswanathan, L.; Virkar, A. V. Wetting characteristics of sodium on β”-alumina and on nasicon. J. Mater. Sci. 1982, 17, 753–759.
[33] Lollongues, R.; Gourier, D.; Kahn, A.; Boilot, J. P.; Colomban, P.; Wicker, A. β alumina, a typical solid electrolyte: latest developments in fundamental approach and in battery utilization. J. Phys. Chem. Solids 1984, 45, 981–1013.
[34] Oshima, T.; Kajita, M.; Okuno, A. Development of sodium-sulfur batteries. Int. J.
Appl. Ceram. Technol. 2004, 1, 269–276.
[35] Hueso, K. B.; Armand, M.; Rojo, T. High temperature sodium batteries: status, challenges and future trends. Energy Environ. Sci. 2013, 6, 734–749.
ACS Paragon Plus Environment
42
Page 43 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
[36] Zhou, W.; Li, Y.; Xin, S.; Goodenough, J. B. Rechargeable sodium all-solid-state battery. ACS Cent. Sci. 2017, 3, 52–57.
[37] Goodenough, J. B.; Hong, H. Y-P.; Kafalas, J. A. Fast Na+-ion transport in skeleton structures. Mater. Res. Bull. 1976, 11, 203–220.
[38] Irvine, J. T. S.; Sinclair, D. C.; West, A. R. Electroceramics: characterization by impedance spectroscopy. Adv. Mater. 1990, 2, 132–138.
[39] Iermakova, D. I.; Dugas, R.; Palacín, Ponrouch, A. On the comparative stability of Li and Na metal anode interfaces in conventional alkyl carbonate electrolytes. J.
Electrochem. Soc. 2015, 162, A7060–A7066.
[40] Abe, T.; Sagane, F.; Ohtsuka, M.; Iriyama, Y.; Ogumi, Z. Lithium-ion transfer at the interface between lithium-ion conductive ceramic electrolyte and liquid electrolyte – A key to enhancing the rate capability of lithium-ion batteries. J. Electrochem. Soc. 2005,
152, A2151–A2154.
ACS Paragon Plus Environment
43
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 44 of 53
[41] Sagane, F.; Abe, T.; Iriyama, Y.; Ogumi, T. Li+ and Na+ transfer through interfaces between inorganic solid electrolytes and polymer or liquid electrolytes. J. Power
Sources 2005, 146, 749–752.
[42] Yamada, Y.; Sagane, F.; Iriyama, Y.; Abe, T.; Ogumi, Z. Kinetics of lithium-ion transfer at the interface between Li0.35La0.55TiO3 and binary electrolytes. J. Phys. Chem.
C 2009, 113, 14528–14532.
[43] Sagane, F.; Abe, T.; Ogumi, Z. Sodium-ion transfer at the interface between ceramic and organic electrolytes. J. Power Sources 2010, 195, 7466–7470.
[44] Fleig, J.; Maier, J. Point contacts in solid state ionics: finite element calculations and local conductivity measurements. Solid State Ionics 1996, 86–88, 1351–1356.
[45] Fleig, J.; Maier, J. The influence of laterally inhomogeneous contacts on the impedance of solid materials: A three-dimensional finite-element study. J. Electroceram. 1997, 1, 73–89.
ACS Paragon Plus Environment
44
Page 45 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
[46] Meyer, M.; Rickert, H.; Schwaitzer, U. Investigations on the kinetics of the anodic dissolution of lithium at the interface Li/Li3N. Solid State Ionics 1983, 9&10, 689–694.
[47] Yu, X.; Bates, J. B.; Jellison, Jr., G. E.; Hart, F. X. A stable thin-film lithium electrolyte: lithium phosphorus oxynitride. J. Electrochem. Soc. 1997, 144, 524–532.
[48] Schwöbel, A.; Hausbrand, R.; Jaegermann, W. Interface reactions between LiPON and lithium studied by in-situ X-ray photoemission. Solid State Ionics 2015, 273, 51–54.
[49] Porz, L.; Swamy, T.; Sheldon, B. W.; Rettenwander, D.; Frömling, T.; Thaman, H. L.; Berendts, S.; Uecker, R.; Carter, W. C.; Chiang, Y. -M. Mechanism of lithium metal penetration through inorganic solid electrolytes. Adv. Energy Mater. 2017, 7, 1701003.
[50] Manalastas Jr., W.; Rikarte, J.; Chater, R. J.; Brugge, R.; Aguadero, A.; Buannic, L.; Llordés, A.; Aguesse, F.; Kilner, J. Mechanical failure of garnet electrolytes during Li electrodeposition observed by in-operando microscopy. J. Power Sources 2019, 412, 287–293.
ACS Paragon Plus Environment
45
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 46 of 53
[51] Monroe, C.; Newman, J. The impact of elastic deformation on deposition kinetics at lithium/polymer interfaces. J. Electrochem. Soc. 2005, 152, A396–A404.
[52] Raj, R.; Wolfenstine, J. Current limit diagrams for dendrite formation in solid-state electrolytes for Li-ion batteries. J. Power Sources 2017, 343, 119–126.
ACS Paragon Plus Environment
46
Page 47 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Table of Contents (Graphical Abstract)
ACS Paragon Plus Environment
47
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Figure 1 128x105mm (300 x 300 DPI)
ACS Paragon Plus Environment
Page 48 of 53
Page 49 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Figure 2 129x120mm (300 x 300 DPI)
ACS Paragon Plus Environment
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Figure 3 176x107mm (300 x 300 DPI)
ACS Paragon Plus Environment
Page 50 of 53
Page 51 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Figure 4 129x128mm (300 x 300 DPI)
ACS Paragon Plus Environment
ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Figure 5 84x101mm (300 x 300 DPI)
ACS Paragon Plus Environment
Page 52 of 53
Page 53 of 53 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Energy Materials
Table of Contents 82x43mm (300 x 300 DPI)