Research Article pubs.acs.org/journal/ascecg
Fabricating the Robust g‑C3N4 Nanosheets/Carbons/NiS Multiple Heterojunctions for Enhanced Photocatalytic H2 Generation: An Insight into the Trifunctional Roles of Nanocarbons Jiuqing Wen,†,‡,§ Jun Xie,†,‡,§ Zhuohong Yang,†,§ Rongchen Shen,†,‡,§ Huiyi Li,†,‡,§ XingYi Luo,†,§ Xiaobo Chen,∥ and Xin Li*,†,‡,§ †
College of Materials and Energy, South China Agricultural University, Guangzhou 510642, P. R. China College of Forestry and Landscape Architecture, South China Agricultural University, Guangzhou 510642, P. R. China § Key Laboratory of Energy Plants Resource and Utilization, Ministry of Agriculture, Key Laboratory of Biomass Energy of Guangdong Regular Higher Education Institutions, Institute of New Energy and New Materials, South China Agricultural University, Guangzhou 510642, P. R. China ∥ Department of Chemistry, University of Missouri − Kansas City, Kansas City, Missouri 64110, United States
Downloaded via LA TROBE UNIV on July 4, 2018 at 19:03:43 (UTC). See https://pubs.acs.org/sharingguidelines for options on how to legitimately share published articles.
‡
ABSTRACT: In this work, robust nanocarbons, including graphite (G), carbon nanotube (CNT), reduced graphene oxide (rGO), carbon black (CB), and acetylene black (AB), have been successfully coupled into the interfaces between g-C3N4 and NiS using a facile precipitation method. The results demonstrated that nanocarbons played trifunctional roles in boosting the photocatalytic H2 evolution over g-C3N4, which can not only act as effective H2-evolution co-catalysts but can also serve as conductive electron bridges to collect photogenerated electrons and boost the H2-evolution kinetics over the NiS co-catalysts. More interestingly, the nanocarbons can also result in the downshift of valence band of g-C3N4, thus facilitating the fast oxidation of triethanolamine and charge-carrier separation. Particularly, in all five ternary multiheterostructured systems, the g-C3N4-0.5%CB-1.0% NiS (weight ratio) and g-C3N4-0.5%AB-1.0%NiS photocatalysts exhibited the highest H2-evolution rates of 366.4 and 297.7 μmol g−1 h−1, which are 3.17 and 2.57 times higher than that of g-C3N4-1.0%NiS, respectively. Apparently, the significantly enhanced H2-evolution activity of multiheterostructured g-C3N4/carbon/NiS composite photocatalysts can be mainly ascribed to the trifunctional nanocarbons, which serve as the conductive electron bridges rather than the general co-catalysts. More importantly, it is revealed that the amorphous carbons with higher electrical conductivity and weaker electrocatalytic H2-evolution activity are more suitable interfacial bridges between g-C3N4 and NiS co-catalysts for maximizing the H2 generation. This work may give a new mechanistic insight into the development of multiheterostructured g-C3N4-based composite photocatalysts using the combination of trifunctional nanocarbon bridges and earth-abundant co-catalysts/semiconductors for various photocatalytic applications. KEYWORDS: Photocatalytic hydrogen evolution, NiS co-catalysts, g-C3N4, Trifunctional nanocarbons, Graphene
1. INTRODUCTION As is well known, heterogeneous semiconductor photocatalytic hydrogen production driven by renewable solar energy could simultaneously achieve the directly sustained solar-to-fuel conversion and solve environmental pollution, thus gaining a significant amount of research interest around the world.1,2 Since Fujishima and Honda first discovered the photoelectrochemical overall water splitting over a n-TiO2 cell,3 numerous efforts have been devoted to exploit a wide variety of semiconductors for photocatalytic H2 generation from water splitting in the past decades.2,4−10 Among various types of heterogeneous semiconductors, the metal-free polymeric g-C3N4, with a medium band gap of 2.7 eV has been identified as one of the exciting visible-light-driven photocatalysts for solar fuel production11−16 because it possesses the favorable conduction band bottom and the proper valence band top (−1.3 and 1.4 V vs NHE at pH 7) © 2017 American Chemical Society
for reduction of H2O and CO2 and oxygen evolution, respectively. Clearly, it has promptly become a shining star in photocatalytic hydrogen production since the first report in 2009,17 owing to its unique chemical and thermal stability, easy fabrication from the condensation of simple nitrogen-rich precursors, low toxicity, and low cost.15,18 Nevertheless, the photocatalytic H2-evolution efficiency of g-C3N4 is mainly constrained by several typical challenges, including the rapid carrier recombination rate, moderate water oxidation ability, sluggish kinetics, insufficient active sites, and visible-light absorption, which greatly restrict its practical applications in photocatalytic H2 generation.19 Thus, it is highly desirable to develop some new Received: October 14, 2016 Revised: December 15, 2016 Published: January 16, 2017 2224
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering
also could reveal the rate-determining steps, which is favorable for the design and optimization of highly efficient g-C3N4-based composite photocatalysts. Therefore, in this study, the robust conductive nanocarbons, including graphite (G), carbon nanotube (CNT), rGO, carbon black (CB), and acetylene black (AB), will serve as efficient co-catalysts and electron transfer bridges for enhancing the photocatalytic H2-evolution activity over the g-C3N4/NiS hybrids. The ternary hybrids are synthesized by a simple and facile wet-chemistry method: ultrasonic dispersion treatments and the subsequent precipitation process (as shown in Scheme 1).
modification strategies to address these problems and improve the photocatalytic H2-evolution efficiency of g-C3N4. To this end, efficient engineering of the structure, composition, texture, surface, and interface of g-C3N4 has been demonstrated to be crucial to design high-performance g-C3N4-based photocatalysts for hydrogen generation under visible-light irradiation.2,15,20−26 It is well known that the charge separation and transfer and surface charge utilization play major roles in determining efficient photocatalysis.2,27,28 However, simultaneous optimization of the charge carrier separation, migration, and utilization of g-C3N4 is still very challenging. To date, it is well known that loading suitable co-catalysts on g-C3N4 has extensively proven to be one of the most promising strategies for accelerating its sluggish surface H2-elvolution rate. Considering the sustainable development and related economic issues, it is well accepted that the search for earth-abundant H2-evolution electrocatalysts, such as nonprecious metal-based, metal-free, and hybrid materials, have been found to be extremely important for achieving robust electrocatalytic hydrogen generation.29−34 More importantly, these electrocatalysts could be selectively deposited onto various nanostructured heterogeneous semiconductors as water-reduction co-catalysts to significantly boost the H2-evolution activity in aqueous solutions containing proper electron donors.2,35,36 Thus, far, various noble metal-free (such as N-doped graphitic carbon,37 CoS,38 Cu(OH)2,39 NiSx,27,40−45 Ni(dmgH)2,46 Ni(OH)2,47,48 NiO,49 MoS2,50,51 WS2,52,53 and FeOx54) H2-evolution electrocatalysts have been employed as co-catalysts to enhance the photocatalytic H2 generation over g-C3N4.55 However, for these earth-abundant co-catalysts, there have been also two obvious disadvantages: one is their weak electrical conductivity and low work function, as compared to the famous noble metal Pt, thus unfavorable for their effective collection and utilization of photogenerated electrons; the other is their well-known p-type semiconductor characteristics with much smaller band gaps, leading to the formation of typical p−n heterojunctions after the band-structure alignment under irradiation, which are specifically unfavorable for the transfer of photoexcited electrons from the conduction band of n-type g-C3N4 to the p-type co-catalysts. Therefore, to further enhance the activity and stability of the g-C3N4/noble metal-free co-catalysts hybrids, it is of great significance to improve the interfacial coupling to maximize the charge separation and transfer of hot electrons and the H2-evolution efficiency over p-type co-catalysts. More interestingly, despite the significant advances in the promoted photocatalytic H2 evolution over CdS and TiO2 semiconductors through combing the rGO, other various kinds of earthabundant co-catalysts such as MoS2,56,57 WS2,58 Ni(OH)2,59 and NiS,60 limited studies have been reported on the photocatalytic H2 evolution over the ternary hybrids of g-C3N4/ conductive carbons/earth-abundant co-catalysts.40,44 Thus, it would be of great interest to enhance the photocatalytic H2 evolution over the ternary g-C3N4/carbon/earth-abundant co-catalysts by using various nanocarbons with different structures and conductivity properties. To the best of our knowledge, the effects of nanocarbons with different surface physicochemical properties on the photocatalytic H2 evolution over the g-C3N4/NiS hybrids have been rarely reported, especially for some conductive amorphous carbons such as carbon black (CB) and acetylene black (AB). Importantly, more detailed studies on the mechanisms of charge-separation and photocatalytic activity enhancement over the ternary multiheterostructured hybrids with different carbon bridges
Scheme 1. Schematic Illustration for Fabrication of Ternary g-C3N4/Carbon/NiS Composites
The trifunctional roles of nanocarbons in boosting the photocatalytic H2 evolution over g-C3N4 are carefully investigated. The results demonstrated that all nanocarbons can greatly boost the photocatalytic H2-evolution activity over the g-C3N4/ NiS hybrids. More interestingly, it was also revealed that the amorphous AB and CB as solid-state electron mediators could lead to much larger enhancements in the H2-evolution activity of the binary g-C3N4/NiS composite photocatalysts, as compared to the highly crystallized G, CNTs, and rGO, under visible-light irradiation from an aqueous solution containing triethanolamine (TEOA). A possible photocatalytic enhancement mechanism for the improved photocatalytic activity of ternary g-C3N4/carbon/NiS photocatalysts was also proposed. It is believed that the activity enhancement can be attributed to the enhanced charge separation and the improved H2-evolution and TEOA oxidation kinetics. It is hoped that the combination of trifunctional nanocarbon materials and earth-abundant co-catalysts could provide a general strategy to enhance the photocatalytic H2 evolution over different semiconductors under visible-light illumination.
2. EXPERIMENTAL SECTION 2.1. Preparation of Photocatalysts. All chemicals were of analytical grade and used without any further purification. The pure g-C3N4 photocatalyst was synthesized via the pyrolysis (or thermal polycondensation) of urea under ambient pressure without the use of any additives, according to the previously reported procedure.61,62 In a typical synthesis, 10 g of urea was put in a crucible with a cover and heated under static air a muffle furnace at 550 °C for 4 h with a ramping rate of 5 °C min−1. After cooling to room temperature, g-C3N4 was obtained in a powder form. The binary g-C3N4/0.5%CB (weight ratio) hybrid was synthesized by a simple sonochemical approach. A typical experimental procedure was as follows: 3 g of g-C3N4 and 15 mg of carbon black were dissolved in 100 mL of absolute ethyl alcohol. The suspension was ultrasonicated for approximately 2 h. The resultant product was filtered and dried at 80 °C in an oven overnight. The binary g-C3N4/NiS was 2225
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering
Figure 1. XRD patterns of (a) six photocatalysts and (b) five carbon materials. 2.4. Photoelectrochemical Measurements. The working electrodes were prepared as follows: 5 mg of photocatalyst powder was added into 2 mL of ethanol make a slurry, and the powders were dispersed using ultrasonication. Here, 500 uL of the solution was injected onto a 2 cm × 3.5 cm fluorine-doped tin-oxide (FTO) glass substrate by a drop casting method. The resulting electrodes were then dried in an oven and calcined at 150 °C for 1 h in a N2 gas flow. Transient photocurrent measurements were performed on an electrochemical analyzer (CHI660E, CHI Shanghai, Inc.) in a standard three-electrode configuration, using the as-prepared working electrodes as the working electrodes, a Pt wire as the counter electrode, and Ag/AgCl (saturated KCl) as a reference electrode. A 300 W Xe arc lamp with a sharp cut-off filter served as a visible-light source (λ ≥ 420 nm). The electrochemical impedance spectroscopy (EIS) of the above-mentioned working electrodes in a three-electrode system were also recorded via a computer controlled IM6e impedance measurement unit (Zahner Elektrik, Germany) over a frequency range of 0.01−105 Hz with an ac amplitude of 2 mV in the dark. Also, 0.1 M Na2SO4 aqueous solutions were used as the electrolyte. The same electrochemical system was also used to determine the flat-band potential of the working electrodes by the Mott−Schottky (MS) method. The measurements were performed in darkness by scanning the electrodepotential from −0.5 to 1.0 V at a scan rate of 25 mV/s, and the impedance-potential characteristics were recorded at a frequency of 1 kHz. 2.5. Electrocatalytic Hydrogen Evolution. The electrocatalytic hydrogen evolution was tested using a three-electrode cell. Linear sweep voltammetry with a 5 mV−1 scan rate was performed in a 0.5 M H2SO4 electrolyte solution using a Pt plate as the counter electrode and Ag/AgCl (saturated KCl) as a reference electrode. The working electrodes were prepared as follows: 6 mg of photocatalyst power was ultrasonically dispersed in 2 mL of deionized water (for >2 h) and then deposited on a glassy carbon electrode with 3 μL of the solution. After drying, 3 μL of 0.5% Nafion solution (contain 10 vol % ethanol) was then added on top of the catalyst layer.
prepared via the direct precipitation method at room temperature, using Ni(NO3)2 and Na2S as the precursors for NiS. Following the same procedure described above, the ternary g-C3N4/CB/NiS hybrid was prepared using Ni(NO3)2 and Na2S as the precursors for NiS. In a typical synthesis, 600 mg of binary g-C3N4/CB was dispersed in 40 mL of deionized water by ultrasound, and then, 3.30 mL of 0.02 M Ni(NO3)2 solution was dropped in the dispersion. The suspension was ultrasonicated for 30 min, and then 3 mL of 0.05 M Na2S solution was dropped into the above mixed solution. After 1 h stirring at room temperature, the powder samples were filtered, rinsed with distilled water, and dried at 80 °C for 24 h. The obtained g-C3N4/CB/NiS composites with 0.5 wt % of carbon black and 1.0 wt % of NiS were denoted as g-C3N4-0.5% CB-1.0%NiS. The other ternary composites with percentages of G, CNTs, rGO, and AB at 0.5 wt % and with percentages of NiS at 1.0 wt % were prepared according to the above method and were denoted as g-C3N4-0.5%G-1.0%NiS, g-C3N4-0.5%CNT-1.0%NiS, g-C3N4-0.5% rGO-1.0%NiS, and g-C3N4-0.5%AB-1.0%NiS, respectively. 2.2. Characterization. The X-ray diffraction (XRD) patterns were obtained at room temperature using a MSAL-XD2 diffractometer with Cu Kα radiation (operated at 36 kV and 30 mA, λ = 0.15406 nm). Transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) images were performed on a JEM-2100HR (200 kV, Japan), using an accelerating voltage of 120 kV. X-ray photoelectron spectroscopy (XPS) was performed with a VG ESCALAB250 surface analysis system using a monochromatized Al Kα X-ray source (300 W, 5 mA, and 15 kV). The base pressure was about 3 × 10−9 mbar. The UV−vis spectroscopy in the 200−800 nm was measured with a Daojin UV-2550PC diffuse reflectance spectroscope. Nitrogen adsorption−desorption isotherms were measured on a Gemini-2360 analyzer (Micromeritics Co., U.S.A.) at 77 K. The Brunauer−Emmett−Teller (BET) method was used to determine the specific surface area. The pore-size distributions were derived from the desorption branches of the isotherms using the Barrett−Joyner− Halenda (BJH) method. Raman spectra were recorded at room temperature using a Renishaw InVia micro-Raman spectrometer with laser excitation at 785 nm. The photoluminescence (PL) spectra were measured using a LS 50B (PerkinElmer, Inc., U.S.A.) with an excitation wavelength of 385 nm at room temperature. 2.3. Photocatalytic Reaction Procedures. Photocatalytic water splitting was carried out in a LabSolar H2 photocatalytic hydrogen evolution system (Perfectlight, Beijing) including a 300 W Xe lamp (PLS-SXE300, Beijing Trusttech). In a typical reaction, 50 mg of powder sample was dispersed in a Pyrex glass reactor containing the mixed solution of 85 mL water and 15 mL TEOA. Then, the system was sealed and vacuumized to keep the pressure at −0.1 MPa. Afterward, a circular cooling water system was turned on, and the reactor was irradiated with Xe lamp (300 W) under magnetic stirring. The gases evolved were analyzed online with a gas chromatograph (GC-7900, TCD, with N2 as carrier gas) after 1 h of illumination. The reaction was continued for 3 h. A cyclic experiment was carried out to investigate the photocatalytic stability of the g-C3N4/AB/NiS composite. After 3 h of reaction, H2 produced was evacuated and then run for another 3 h.
3. RESULTS AND DISCUSSION 3.1. Phase Structure, Morphology, and Composition. The crystal phase structure of the as-prepared hybrid photocatalysts was first studied by powder XRD measurements. Figure 1a displays the XRD patterns of the binary g-C3N4/NiS and the ternary g-C3N4/carbon/NiS hybrid photocatalysts. As shown in Figure 1a, all obtained powder samples exhibited two distinct diffraction peaks centered at around 27.4° and 13.1°, which are consistent with the previously reported values for the hexagonal phase of polymeric g-C3N4 (JCPDS #87-1526), confirming the formation of the graphitic-like packing layer structure.17,27 It is known that the bulk g-C3N4 stacks like graphite with 2D nanosheets, which consist of tri-s-triazines interconnected via tertiary amines.18 The strong diffraction peak at 2θ values of 27.4° typically corresponds to the (002) crystal plane of g-C3N4 with interplanar distance of 0.326 nm, which is well known for the melon networks.61 Another weak 2226
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering
Figure 2. TEM images of (a) g-C3N4-1.0%NiS, (b) g-C3N4-0.5%G-1.0%NiS, (c) g-C3N4-0.5%CNT-1.0%NiS, (d) g-C3N4-0.5%rGO-1.0%NiS, (e) g-C3N4-0.5%AB-1.0%NiS, and (f) g-C3N4-0.5%CB-1.0%NiS.
Figure 3. TEM (a−-d) and HRTEM (e) images, and the corresponding EDX elemental mapping images (f−j) of the ternary g-C3N4-0.5%CB-1.0% NiS nanohybrids.
due to their low concentration and highly selective dispersion of carbon and NiS species in the composites. Moreover, it is shown in Figure 1b that graphite and carbon nanotubes exhibit a distinct diffraction peak at 26.3°, which can be attributed to the (002) plane of its hexagonal graphitic structure,65 while the broad diffraction peak of CB or AB around at 25° is indicative of an amorphous carbon material.48 The pattern of rGO displayed a broad diffraction peak at around 24.5°, corresponding to the (002) interlayer d-spacing of 0.388 nm.66 All results confirm that the loading of nanocarbons and NiS nanoparticles has no significant influence on the crystalline structure of g-C3N4. The morphology and nanostructures of the as-prepared photocatalysts were further identified by TEM measurements. Figure 2 shows the TEM images of the as-prepared samples with different nanocarbons. Figure 2a displays the TEM image of the g-C3N4-1.0%NiS photocatalyst, confirming that small NiS nanoparticles with an average diameter of 420 nm) are displayed in Figure 9B. As observed in Figure 9B, it is obvious that the ternary composite photocatalysts exhibit higher photocurrent density than the binary composite photocatalysts, indicating that the metal-free carbon materials as co-catalysts could more efficiently boost the interfacial charge transfer. The enhanced photocurrent over ternary composites implies more efficient separation and transfer of photoexcited electron−hole pairs, which is greatly beneficial for the photoactivity enhancements. More importantly, g-C3N4/CB/NiS exhibits the highest photocurrent density among all ternary samples, indicating the best charge separation and transfer caused by the introduction 2231
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering
Figure 10. Polarization curves of NiS and different photocatalysts (A) and nanocarbons (B) were measured in 0.5 M H2SO4 acidic solution.
sample (−0.796 V vs NHE, in 0.5 M H2SO4 acidic solution), indicating that amorphous CB and AB as interfacial mediators are better than rGO for effectively improving the H2-evolution kinetics over the g-C3N4/NiS hybrids due to their higher electrical conductivity. Meanwhile, Figure 10B shows the electrocatalytic H2-evolution activity for five types of nanocarbons. As observed in Figure 10B, it is clear that these five carbons could also act as the electrocatalytic H2-evolution active sites, despite that their electrocatalytic activities (or onset potentials) are obviously smaller than those of the famous NiS co-catalysts. Further observation demonstrates that the electrocatalytic H2-evolution activities of these five carbons decrease in the following order: CNT > rGO > AB ≈ CB > G. Through a more careful and deliberate comparison between Figure 10A and B, it could be revealed that the nanocarbons with higher electrical conductivity and weaker electrocatalytic H2-evolution activities, such as AB and CB, are more suitable for being utilized as interfacial mediators to improve the H2-evolution activity of NiS co-catalysts. In other words, the nanocarbons with higher conductivity and weaker electrocatalytic H2-evolution activities as interfacial mediators could more efficiently collect and enrich the photogenerated electrons from g-C3N4 semicondcutor, which could be further utilized to significantly boost the electroncatlytic H2 evolution over the adjacent NiS co-catalysts. The weaker electrocatalytic H2-evolution activities of nanocarbons could effectively reduce the loss of collected electrons, thus maximizing their potential utilization in driving the electrocatalytic H2 evolution over more active NiS co-catalysts. As a result, the excellent synergistic effects of NiS and nanocarbons achieve the significantly enhanced charge separation and photocatalytic H2 evolution. In order to better understand the intrinsic electronic properties of the film electrode in contact with the electrolyte solution, the differences in the flat-band positions of the g-C3N4-1.0%NiS and g-C3N4-0.5%CB-1.0%NiS film electrodes were examined by using the MS analysis, which is based on the assumption that the capacitance of the space charge layer is much smaller than that of the Helmholtz layer.87 Figure 11 shows MS plots, 1/C2 versus E, for g-C3N4-1.0%NiS and g-C3N4-0.5%CB-1.0%NiS. The positive slope of the straight lines indicates that g-C3N4 is an n-type semiconductor, whose lowest potential of CB can be very close to the flat-band potential. The flat band potential can be obtained from the intercept of the tangents of linear potential curves on the horizontal axis, which can be approximately estimated to be −1.12 and −1.05 V versus RHE for g-C3N4-1.0%NiS and g-C3N4-0.5%CB-1.0%NiS, respectively. Clearly, g-C3N4-0.5% CB-1.0%NiS displays a positive shift of the flat-band potential as compared with that of g-C3N4-1.0%NiS. According to the value of the band gap, it has been demonstrated that
of CB, which are supported by the highest photocatalytic H2-evolution activity. To further confirm the enhanced charge separation rate, the EIS Nyquist plot of all samples in the dark were also performed, which is one of the most powerful techniques to study the interfacial charge transfer and recombination rates occurring in the three-electrode systems.85,86 The EIS Nyquist plots of six different samples are shown in Figure 9C. As displayed in Figure 9C, the photocatalysts exhibit semicircles in the middlefrequency region, and the arc radius on the Nyquist plot of ternary hybrids samples are smaller than that of g-C3N4-1.0% NiS, suggesting that a slower recombination and a more efficient separation of photogenerated electron−hole pairs for them. Thus, it is clear that G, CNT, rGO, AB, and CB in the ternary hybrids could lead to accelerated charge transport and separation, thus resulting in significantly improved photocatalytic H2-production activity. In addition, it is also observed that ternary g-C3N4-0.5%AB-1.0%NiS and g-C3N4-0.5%CB1.0%NiS exhibit a smaller arc radius than the other three kinds of ternary hybrids, which are in good agreement with the highest H2-evolution activity, further confirming the outstanding roles of AB and CB in improving charge separation and transfer. Obviously, the improvements of charge-separation performances for these nanocarbons increased in the following order: G < CNT < rGO < AB ≈ CB. In a word, the similar results from transient photocurrent responses and PL and EIS spectra strongly indicated that the amorphous semimetals CB and AB are much better than rGO, CNT, and G for applications in the ternary composite photocatalysts, due to much higher electric conductivity and smaller particle sizes. 3.5. Photocatalytic Mechanism. It is known that the photogenerated electrons and holes cause reduction and oxidation reactions on surface active sites, respectively, which are similar to those in electrolysis.2,27 To further identify the key roles of NiS and nano carbon co-catalysts in improving the H2 evolution during the photocatalytic process, the polarization curves of NiS, different photocatalysts, and nanocarbons were also performed. Figure 10A shows the electrocatalytic H2-evolution activity for NiS and four kinds of nanocomposites using a standard three-electrode configuration in 0.5 M H2SO4 acidic solution. Clearly, the binary samples exhibited the proper onset potential for H2 evolution (−0.901 V vs NHE, in 0.5 M H2SO4 acidic solution, obtained by the intercept of the tangents on horizontal axis), indicating that NiS plays an important role in acting as active sites to decrease the onset potential and improve the kinetics for H2 evolution.27 More importantly, it is noteworthy from Figure 10A that the onset potentials of g-C 3 N 4 -0.5%CB-1.0%NiS and g-C 3 N 4 -0.5%AB-1.0%NiS (−0.698 and −0.704 V vs NHE, in 0.5 M H2SO4 acidic solution) are slightly smaller than that of the g-C3N4-0.5%rGO-1.0%NiS 2232
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering
of g-C3N4 could be excited and injected into its conduction band to drive the H2 evolution reaction, leaving the holes in the valence band for TEOA oxidation. However, the photogenerated electron−hole pairs will quickly recombine at the bulk and surface of g-C3N4 without co-catalyst loading, thus leading to its poor H2-evolution activity. Previous studies have demonstrated that the NiS co-catalysts could act as active sites to promote charge separation and decrease the overpotential of H2-evolution reaction on g-C3N4 semiconductor photocatalysts, thus achieving the significantly enhanced H2-evolution activity.27,42,43 Unfortunately, the poor electrical conductivity and P-type character of NiS co-catalysts are unfavorable for accepting and storing the electrons to drive the H2-evolution reaction. On the contrary, when inserting the carbon layer between the g-C3N4 photocatalyst and NiS co-catalysts, the photoinduced electrons in the conduction band of g-C3N4 can rapidly transfer to carbon materials due to their excellent electronic conductivity, which could hinder the fast charge recombination.40,44 More importantly, the enriched photoinduced electrons on the surface of carbon materials could accelerate the photocatalytic H2 evolution on the NiS co-catalysts as active sites. Additionally, the loaded nanocarbons can also slightly increase the oxidation ability of TEOA driven by photogenerated holes, thus leading to the improved TEOAoxidation kinetics.87,89 In a word, the boosted photocatalytic H2 evolution over gC3N4/NiS photocatalysts could be well supported by the trifunctional roles of nanocarbons: acting as effective H2-evolution co-catalysts and conductive electron bridges and increasing the oxidation ability of TEOA driven by photogenerated holes due to the lowered valance band position. Accordingly, it is clear that the combined effects of improved charge transfer and separation and H2-evolution kinetics and TEOA-oxidation capacity could directly achieve the significantly enhanced co-catalyst-assisted photocatalytic H2 evolution activity over the ternary multiheterostructured hybrid photocatalysts.
Figure 11. MS plots of two different photocatalysts film electrodes. MS plots were obtained at a frequency of 1 kHz in an aqueous solution of Na2SO4 (0.1 M).
g-C3N4-1.0%NiS and g-C3N4-0.5%CB-1.0%NiS exhibit a similar band gap of ca. 2.71 eV. Thus, the calculated positions of the valence band maximum (VBM) are 1.59 and 1.66 V versus RHE for g-C3N4-1.0%NiS and g-C3N4-0.5%CB-1.0%NiS, respectively. The VBM of g-C3 N 4 -0.5%CB-1.0%NiS is lower than that of g-C3N4-1.0%NiS by 0.07 V, suggesting that g-C3N4-0.5%CB-1.0%NiS has a stronger oxidation ability for TEOA theoretically. More recently, the enhanced H2 evolution has also been realized by improved water oxidation kinetics.88 It was believed that the metal-free carbon nanodots could promote the decomposition of H2O2 generated on the proximity active sites on the surface of g-C3N4, thus achieving the highest overall water splitting so far.88 According to the photocatalytic mechanism, the improved TEOA oxidation ability will further accelerate the separation efficiency of electron−hole pairs, thus directly contributing to the enhancement of photocatalytic H2-evolution activity. The results were also well supported by the improved photocurrent and EIS and PL spectra. On the basis of the above-mentioned observations and results, it is clear that the nanocarbons are typically trifunctional materials in these interestingly ternary systems. On the one hand, nanocarbons could obviously serve as H2-evolution co-catalysts due to their much lower electrocatalytic H2-evolution overpotentials than that of pure g-C3N4 nanosheets. At this point, the nanocarbons themselves could play an important role in increasing the surface H2-evolution active sites over g-C3N4 nanosheets. On the other hand, nanocarbons could also act as conductive bridges to significantly boost the H2 evolution over NiS co-catalysts. The possible mechanisms for separation and transport of the electron−hole pairs in the binary g-C3N4/NiS and ternary g-C3N4/carbon/NiS composites under visible-light irradiation are illustrated in Scheme 2A and B, respectively. Under visible-light irradiation, the electrons in the valence band
4. CONCLUSIONS In summary, a series of semimetallic nanocarbons, including G, CNT, rGO, AB, and CB, have been successfully coupled into the interface between g-C3N4 and earth-abundant NiS co-catalysts using a facile precipitation method. The resulting ternary multiheterostructured g-C3N4/carbon/NiS photocatalysts exhibit excellent photocatalytic activity and stability for H2 generation from a 15 vol % TEOA aqueous solution under visible-light irradiation. The results showed that the g-C3N4-0.5%CB-1.0% NiS and g-C3N4-0.5%AB-1.0%NiS photocatalysts exhibited the highest H2-evolution rates of 366.4 and 297.7 μmol g−1 h−1,
Scheme 2. Schematic Diagram of Photocatalytic H2 Evolution over (A) Binary g-C3N4/NiS Co-Catalyst and (B) Ternary g-C3N4/Carbon/NiS Co-Catalyst Composites under Visible-Light Irradiation
2233
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering
Photocatalytic H-2 Production. ACS Sustainable Chem. Eng. 2014, 2, 1446−1452. (11) Xiang, Q.; Cheng, B.; Yu, J. Graphene-Based Photocatalysts for Solar-Fuel Generation. Angew. Chem., Int. Ed. 2015, 54, 11350−11366. (12) Low, J.; Yu, J.; Ho, W. Graphene-Based Photocatalysts for CO2 Reduction to Solar Fuel. J. Phys. Chem. Lett. 2015, 6, 4244−4251. (13) Ye, S.; Wang, R.; Wu, M.-Z.; Yuan, Y.-P. A review on g-C3N4 for photocatalytic water splitting and CO2 reduction. Appl. Surf. Sci. 2015, 358, 15−27. (14) Li, X.; Wen, J.; Low, J.; Fang, Y.; Yu, J. Design and fabrication of semiconductor photocatalyst for photocatalytic reduction of CO2 to solar fuel. Science China Materials 2014, 57, 70−100. (15) Cao, S.; Yu, J. g-C3N4-Based Photocatalysts for Hydrogen Generation. J. Phys. Chem. Lett. 2014, 5, 2101−2107. (16) Wen, J.; Xie, J.; Chen, X.; Li, X. A review on g-C3N4-based photocatalysts. Appl. Surf. Sci. 2017, 391, 72−123. (17) Wang, X.; Maeda, K.; Thomas, A.; Takanabe, K.; Xin, G.; Carlsson, J.; Domen, K.; Antonietti, M. A metal-free polymeric photocatalyst for hydrogen production from water under visible light. Nat. Mater. 2009, 8, 76−80. (18) Cao, S.; Low, J.; Yu, J.; Jaroniec, M. Polymeric Photocatalysts Based on Graphitic Carbon Nitride. Adv. Mater. 2015, 27, 2150−2176. (19) Zhang, J.; Sun, J.; Maeda, K.; Domen, K.; Liu, P.; Antonietti, M.; Fu, X.; Wang, X. Sulfur-mediated synthesis of carbon nitride: Band-gap engineering and improved functions for photocatalysis. Energy Environ. Sci. 2011, 4, 675−678. (20) Chuang, P.-K.; Wu, K.-H.; Yeh, T.-F.; Teng, H. Extending the pi-Conjugation of g-C3N4 by Incorporating Aromatic Carbon for Photocatalytic H2 Evolution from Aqueous Solution. ACS Sustainable Chem. Eng. 2016, 4, 5989−5997. (21) Zhang, X.; Peng, B.; Zhang, S.; Peng, T. Robust Wide VisibleLight-Responsive Photoactivity for H2 Production over a Polymer/ Polymer Heterojunction Photocatalyst: The Significance of Sacrificial Reagent. ACS Sustainable Chem. Eng. 2015, 3, 1501−1509. (22) Lang, J.; Liu, M.; Su, Y.; Yan, L.; Wang, X. Fabrication of the heterostructured CsTaWO6/Au/g-C3N4 hybrid photocatalyst with enhanced performance of photocatalytic hydrogen production from water. Appl. Surf. Sci. 2015, 358, 252−260. (23) Zhang, J.; Huang, F. Enhanced visible light photocatalytic H2 production activity of g-C3N4 via carbon fiber. Appl. Surf. Sci. 2015, 358, 287−295. (24) Han, C.; Wu, L.; Ge, L.; Li, Y.; Zhao, Z. AuPd bimetallic nanoparticles decorated graphitic carbon nitride for highly efficient reduction of water to H2 under visible light irradiation. Carbon 2015, 92, 31−40. (25) Li, X.; Yu, J.; Jaroniec, M. Hierarchical photocatalysts. Chem. Soc. Rev. 2016, 45, 2603−2636. (26) Lin, Z.; Lin, L.; Wang, X. Thermal nitridation of triazine motifs to heptazine-based carbon nitride frameworks for use in visible light photocatalysis. Chinese. J. Catal. 2015, 36, 2089−2094. (27) Yuan, J.; Wen, J.; Zhong, Y.; Li, X.; Fang, Y.; Zhang, S.; Liu, W. Enhanced photocatalytic H2 evolution over noble-metal-free NiS cocatalyst modified CdS nanorods/g-C3N4 heterojunctions. J. Mater. Chem. A 2015, 3, 18244−18255. (28) Yuan, Y.-P.; Ruan, L.-W.; Barber, J.; Joachim Loo, S. C.; Xue, C. Hetero-nanostructured suspended photocatalysts for solar-to-fuel conversion. Energy Environ. Sci. 2014, 7, 3934−3951. (29) Duan, J.; Chen, S.; Jaroniec, M.; Qiao, S. Z. Porous C3N4 Nanolayers@N-Graphene Films as Catalyst Electrodes for Highly Efficient Hydrogen Evolution. ACS Nano 2015, 9, 931−940. (30) Zou, X.; Zhang, Y. Noble metal-free hydrogen evolution catalysts for water splitting. Chem. Soc. Rev. 2015, 44, 5148−5180. (31) Han, A.; Jin, S.; Chen, H.; Ji, H.; Sun, Z.; Du, P. A robust hydrogen evolution catalyst based on crystalline nickel phosphide nanoflakes on three-dimensional graphene/nickel foam: high performance for electrocatalytic hydrogen production from pH 0−14. J. Mater. Chem. A 2015, 3, 1941−1946.
which are 3.17 and 2.57 times higher than that of g-C3N4-1.0% NiS, respectively. It is believed that the enhanced photocatalytic activity can be attributed to the combined effects of improved charge transfer and separation, accelerated H2-evolution kinetics, and enhanced oxidation ability of holes due to the lowerd valance band position. Through the thorough discussion of trifunctional roles of nanocarbons, the possible co-catalystassisted photocatalytic mechanisms have been proposed to well explain the enhanced photocatalysis in the ternary g-C3N4/ carbon/NiS composites. This work demonstrated that the amorphous semimetal CB and AB as interfacial mediators are much better than rGO, CNT, and G for enhancing the charge transfer and separation from g-C3N4 to NiS and significantly boosting the H2-evolution activity of NiS co-catalysts, which may give a new mechanistic insight into the development of multiheterostructured g-C3N4-based composite photocatalysts for various applications.
■
AUTHOR INFORMATION
Corresponding Author
*Tel.: +86 20 85282633. Fax: +86 20 85285596. E-mail: Xinliscau@yahoo.com (X. Li). ORCID
Xin Li: 0000-0002-4842-5054 Notes
The authors declare no competing financial interest.
■
ACKNOWLEDGMENTS The work was supported by National Natural Science Foundation of China (51672089), the industry and research collaborative innovation major projects of Guangzhou (201508020098), and the State Key Laboratory of Advanced Technology for Material Synthesis and Processing (Wuhan University of Technology) (2015-KF-7).
■
REFERENCES
(1) Turner, J. A. A Realizable Renewable Energy Future. Science 1999, 285, 687−689. (2) Li, X.; Yu, J.; Low, J.; Fang, Y.; Xiao, J.; Chen, X. Engineering heterogeneous semiconductors for solar water splitting. J. Mater. Chem. A 2015, 3, 2485−2534. (3) Fujishima, A.; Honda, K. Electrochemical photolysis of water at a semiconductor electrode. Nature 1972, 238, 37−38. (4) Chen, X.; Shen, S.; Guo, L.; Mao, S. S. Semiconductor-based photocatalytic hydrogen generation. Chem. Rev. 2010, 110, 6503− 6570. (5) Chao, K.-J.; Cheng, W.-Y.; Yu, T.-H.; Lu, S.-Y. Large enhancements in hydrogen production of TiO2 through a simple carbon decoration. Carbon 2013, 62, 69−75. (6) Liu, J.; Xu, S.; Liu, L.; Sun, D. D. The size and dispersion effect of modified graphene oxide sheets on the photocatalytic H2 generation activity of TiO2 nanorods. Carbon 2013, 60, 445−452. (7) Wang, X.; Yao, X. Photocatalytic hydrogen generation of ZnO rod-CdS/reduced graphene oxide heterostructure prepared by Ptinduced oxidation and light irradiation-assisted methods. Carbon 2014, 77, 667−674. (8) Li, Q.; Li, X.; Wageh, S.; Al-Ghamdi, A. A.; Yu, J. CdS/Graphene Nanocomposite Photocatalysts. Adv. Energy Mater. 2015, 5, 1500010. (9) Hsu, M.-H.; Chang, C.-J.; Weng, H.-T. Efficient H-2 Production Using Ag2S-Coupled ZnO@ZnS Core-Shell Nanorods Decorated Metal Wire Mesh as an Immobilized Hierarchical Photocatalyst. ACS Sustainable Chem. Eng. 2016, 4, 1381−1391. (10) Zhang, L.; Jing, D.; Guo, L.; Yao, X. In Situ Photochemical Synthesis of Zn-Doped Cu2O Hollow Microcubes for High Efficient 2234
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering (32) Zheng, Y.; Jiao, Y.; Zhu, Y.; Li, L. H.; Han, Y.; Chen, Y.; Du, A.; Jaroniec, M.; Qiao, S. Z. Hydrogen evolution by a metal-free electrocatalyst. Nat. Commun. 2014, 5, 3783. (33) Li, X.; Yu, J.; Wageh, S.; Al-Ghamdi, A. A.; Xie, J. Graphene in Photocatalysis: A Review. Small 2016, 12, 6640. (34) Zheng, Y.; Jiao, Y.; Jaroniec, M.; Qiao, S. Z. Advancing the Electrochemistry of the Hydrogen-Evolution Reaction through Combining Experiment and Theory. Angew. Chem., Int. Ed. 2015, 54, 52−65. (35) Xu, Y.; Xu, R. Nickel-based co-catalysts for photocatalytic hydrogen production. Appl. Surf. Sci. 2015, 351, 779−793. (36) Ran, J.; Zhang, J.; Yu, J.; Jaroniec, M.; Qiao, S. Z. Earthabundant co-catalysts for semiconductor-based photocatalytic water splitting. Chem. Soc. Rev. 2014, 43, 7787−7812. (37) Zhou, Y.; Zhang, L.; Huang, W.; Kong, Q.; Fan, X.; Wang, M.; Shi, J. N-doped graphitic carbon-incorporated g-C3N4 for remarkably enhanced photocatalytic H-2 evolution under visible light. Carbon 2016, 99, 111−117. (38) Zhu, Y.; Xu, Y.; Hou, Y.; Ding, Z.; Wang, X. Cobalt sulfide modified graphitic carbon nitride semiconductor for solar hydrogen production. Int. J. Hydrogen Energy 2014, 39, 11873−11879. (39) Zhou, X.; Luo, Z.; Tao, P.; Jin, B.; Wu, Z.; Huang, Y. Facile preparation and enhanced photocatalytic H2-production activity of Cu(OH)2 nanospheres modified porous g-C3N4. Mater. Chem. Phys. 2014, 143, 1462−1468. (40) Zhong, Y.; Yuan, J.; Wen, J.; Li, X.; Xu, Y.; Liu, W.; Zhang, S.; Fang, Y. Earth-abundant NiS co-catalyst modified metal-free mpgC3N4/CNT nanocomposites for highly efficient visible-light photocatalytic H2 evolution. Dalton Trans. 2015, 44, 18260−18269. (41) Yin, L.; Yuan, Y.-P.; Cao, S.-W.; Zhang, Z.; Xue, C. Enhanced visible-light-driven photocatalytic hydrogen generation over g-C3N4 through loading the noble metal-free NiS2 cocatalyst. RSC Adv. 2014, 4, 6127−6132. (42) Chen, Z.; Sun, P.; Fan, B.; Zhang, Z.; Fang, X. In Situ TemplateFree Ion-Exchange Process to Prepare Visible-Light-Active g-C3N4/ NiS Hybrid Photocatalysts with Enhanced Hydrogen Evolution Activity. J. Phys. Chem. C 2014, 118, 7801−7807. (43) Hong, J.; Wang, Y.; Wang, Y.; Zhang, W.; Xu, R. Noble-MetalFree NiS/C3N4 for Efficient Photocatalytic Hydrogen Evolution from Water. ChemSusChem 2013, 6, 2263−2268. (44) Wen, J.; Li, X.; Li, H.; Ma, S.; He, K.; Xu, Y.; Fang, Y.; Liu, W.; Gao, Q. Enhanced visible-light H2 evolution of g-C3N4 photocatalysts via the synergetic effect of amorphous NiS and cheap metal-free carbon black nanoparticles as co-catalysts. Appl. Surf. Sci. 2015, 358, 204−212. (45) Yuan, Y.-P.; Cao, S.-W.; Yin, L.-S.; Xu, L.; Xue, C. NiS2 Cocatalyst decoration on CdLa2S4 nanocrystals for efficient photocatalytic hydrogen generation under visible light irradiation. Int. J. Hydrogen Energy 2013, 38, 7218−7223. (46) Cao, S.-W.; Yuan, Y.-P.; Barber, J.; Loo, S. C. J.; Xue, C. Noblemetal-free g-C3N4/Ni(dmgH)2 composite for efficient photocatalytic hydrogen evolution under visible light irradiation. Appl. Surf. Sci. 2014, 319, 344−349. (47) Yu, J.; Wang, S.; Cheng, B.; Lin, Z.; Huang, F. Noble metal-free Ni(OH)2-g-C3N4 composite photocatalyst with enhanced visible-light photocatalytic H-2-production activity. Catal. Sci. Technol. 2013, 3, 1782−1789. (48) Bi, G.; Wen, J.; Li, X.; Liu, W.; Xie, J.; Fang, Y.; Zhang, W. Efficient visible-light photocatalytic H2 evolution over metal-free gC3N4 co-modified with robust acetylene black and Ni(OH)2 as dual co-catalysts. RSC Adv. 2016, 6, 31497−31506. (49) Zhang, G.; Li, G.; Wang, X. Surface Modification of Carbon Nitride Polymers by Core-Shell Nickel/Nickel Oxide Cocatalysts for Hydrogen Evolution Photocatalysis. ChemCatChem 2015, 7, 2864− 2870. (50) Ge, L.; Han, C.; Xiao, X.; Guo, L. Synthesis and characterization of composite visible light active photocatalysts MoS2-g-C3N4 with enhanced hydrogen evolution activity. Int. J. Hydrogen Energy 2013, 38, 6960−6969.
(51) Hou, Y.; Laursen, A. B.; Zhang, J.; Zhang, G.; Zhu, Y.; Wang, X.; Dahl, S.; Chorkendorff, I. Layered Nanojunctions for HydrogenEvolution Catalysis. Angew. Chem., Int. Ed. 2013, 52, 3621−3625. (52) Hou, Y.; Zhu, Y.; Xu, Y.; Wang, X. Photocatalytic hydrogen production over carbon nitride loaded with WS2 as co-catalyst under visible light. Appl. Catal., B 2014, 156-157, 122−127. (53) Akple, M. S.; Low, J.; Wageh, S.; Al-Ghamdi, A. A.; Yu, J.; Zhang, J. Enhanced visible light photocatalytic H2-production of gC3N4/WS2 composite heterostructures. Appl. Surf. Sci. 2015, 358, 196−203. (54) Cheng, R.; Zhang, L.; Fan, X.; Wang, M.; Li, M.; Shi, J. One-step construction of FeOx modified g-C3N4 for largely enhanced visiblelight photocatalytic hydrogen evolution. Carbon 2016, 101, 62−70. (55) Yin, S.; Han, J.; Zhou, T.; Xu, R. Recent progress in g-C3N4 based low cost photocatalytic system: activity enhancement and emerging applications. Catal. Sci. Technol. 2015, 5, 5048−5061. (56) Lang, D.; Shen, T.; Xiang, Q. Roles of MoS2 and Graphene as Cocatalysts in the Enhanced Visible-Light Photocatalytic H-2 Production Activity of Multiarmed CdS Nanorods. ChemCatChem 2015, 7, 943−951. (57) Xiang, Q.; Yu, J.; Jaroniec, M. Synergetic Effect of MoS2 and Graphene as Cocatalysts for Enhanced Photocatalytic H2 Production Activity of TiO2 Nanoparticles. J. Am. Chem. Soc. 2012, 134, 6575− 6578. (58) Xiang, Q.; Cheng, F.; Lang, D. Hierarchical Layered WS2/ Graphene-Modified CdS Nanorods for Efficient Photocatalytic Hydrogen Evolution. ChemSusChem 2016, 9, 996−1002. (59) Yan, Z.; Yu, X.; Han, A.; Xu, P.; Du, P. Noble-Metal-Free Ni(OH)2-Modified CdS/Reduced Graphene Oxide Nanocomposite with Enhanced Photocatalytic Activity for Hydrogen Production under Visible Light Irradiation. J. Phys. Chem. C 2014, 118, 22896−22903. (60) Zhang, J.; Qi, L.; Ran, J.; Yu, J.; Qiao, S. Z. Ternary NiS/ ZnxCd1‑xS/Reduced Graphene Oxide Nanocomposites for Enhanced Solar Photocatalytic H2-Production Activity. Adv. Energy Mater. 2014, 4, 1301925. (61) Dong, F.; Wu, L.; Sun, Y.; Fu, M.; Wu, Z.; Lee, S. C. Efficient synthesis of polymeric g-C3N4 layered materials as novel efficient visible light driven photocatalysts. J. Mater. Chem. 2011, 21, 15171− 15174. (62) Liu, J.; Zhang, T.; Wang, Z.; Dawson, G.; Chen, W. Simple pyrolysis of urea into graphitic carbon nitride with recyclable adsorption and photocatalytic activity. J. Mater. Chem. 2011, 21, 14398−14401. (63) Guo, Y.; Li, J.; Yuan, Y.; Li, L.; Zhang, M.; Zhou, C.; Lin, Z. A Rapid Microwave-Assisted Thermolysis Route to Highly Crystalline Carbon Nitrides for Efficient Hydrogen Generation. Angew. Chem., Int. Ed. 2016, 55, 14693−14697. (64) Schwinghammer, K.; Mesch, M. B.; Duppel, V.; Ziegler, C.; Senker, J.; Lotsch, B. V. Crystalline Carbon Nitride Nanosheets for Improved Visible-Light Hydrogen Evolution. J. Am. Chem. Soc. 2014, 136, 1730−1733. (65) Chen, Y.; Li, J.; Hong, Z.; Shen, B.; Lin, B.; Gao, B. Origin of the enhanced visible-light photocatalytic activity of CNT modified gC3N4 for H2 production. Phys. Chem. Chem. Phys. 2014, 16, 8106− 8113. (66) Xie, X.; Lin, L.; Liu, R.-Y.; Jiang, Y.-F.; Zhu, Q.; Xu, A.-W. The synergistic effect of metallic molybdenum dioxide nanoparticle decorated graphene as an active electrocatalyst for an enhanced hydrogen evolution reaction. J. Mater. Chem. A 2015, 3, 8055−8061. (67) Razzaq, A.; Grimes, C. A.; In, S.-I. Facile fabrication of a noble metal-free photocatalyst: TiO2 nanotube arrays covered with reduced graphene oxide. Carbon 2016, 98, 537−544. (68) Xu, T.; Zhang, L.; Cheng, H.; Zhu, Y. Significantly enhanced photocatalytic performance of ZnO via graphene hybridization and the mechanism study. Appl. Catal., B 2011, 101, 382−387. (69) Chen, Y.; Li, J.; Hong, Z.; Shen, B.; Lin, B.; Gao, B. Origin of the enhanced visible-light photocatalytic activity of CNT modified gC3N4 for H2 production. Phys. Chem. Chem. Phys. 2014, 16, 8106− 8113. 2235
DOI: 10.1021/acssuschemeng.6b02490 ACS Sustainable Chem. Eng. 2017, 5, 2224−2236
Research Article
ACS Sustainable Chemistry & Engineering (70) Zhang, Z.; Li, X.; Wang, C.; Fu, S.; Liu, Y.; Shao, C. Polyacrylonitrile and Carbon Nanofibers with Controllable Nanoporous Structures by Electrospinning. Macromol. Mater. Eng. 2009, 294, 673−678. (71) Wu, M.; Yan, J.-M.; Tang, X.-n.; Zhao, M.; Jiang, Q. Synthesis of Potassium-Modified Graphitic Carbon Nitride with High Photocatalytic Activity for Hydrogen Evolution. ChemSusChem 2014, 7, 2654−2658. (72) Pawar, R. C.; Kang, S.; Ahn, S. H.; Lee, C. S. Gold nanoparticle modified graphitic carbon nitride/multi-walled carbon nanotube (gC3N4/CNTs/Au) hybrid photocatalysts for effective water splitting and degradation. RSC Adv. 2015, 5, 24281−24292. (73) Zhu, B.; Xia, P.; Ho, W.; Yu, J. Isoelectric point and adsorption activity of porous g-C3N4. Appl. Surf. Sci. 2015, 344, 188−195. (74) Shi, L.; Liang, L.; Wang, F.; Liu, M.; Chen, K.; Sun, K.; Zhang, N.; Sun, J. Higher Yield Urea-Derived Polymeric Graphitic Carbon Nitride with Mesoporous Structure and Superior Visible-LightResponsive Activity. ACS Sustainable Chem. Eng. 2015, 3, 3412−3419. (75) Akple, M. S.; Low, J.; Wageh, S.; Al-Ghamdi, A. A.; Yu, J.; Zhang, J. Enhanced visible light photocatalytic H2-production of gC3N4/WS2 composite heterostructures. Appl. Surf. Sci. 2015, 358, 196−203. (76) Huang, Q.; Yu, J.; Cao, S.; Cui, C.; Cheng, B. Efficient photocatalytic reduction of CO2 by amine-functionalized g-C3N4. Appl. Surf. Sci. 2015, 358, 350−355. (77) Sing, K.; Everett, D.; Haul, R.; Moscou, L.; Pierotti, R.; Rouquerol, J.; Siemieniewska, T. Reporting physisorption data for gas/ solid systems with special reference to the determination of surface area and porosity. Pure Appl. Chem. 1985, 57, 603−619. (78) Li, X.; Liu, H.; Luo, D.; Li, J.; Huang, Y.; Li, H.; Fang, Y.; Xu, Y.; Zhu, L. Adsorption of CO2 on heterostructure CdS(Bi2S3)/TiO2 nanotube photocatalysts and their photocatalytic activities in the reduction of CO2 to methanol under visible light irradiation. Chem. Eng. J. 2012, 180, 151−158. (79) Li, X.; Xia, T.; Xu, C.; Murowchick, J.; Chen, X. Synthesis and photoactivity of nanostructured CdS-TiO2 composite catalysts. Catal. Today 2014, 225, 64−73. (80) Ikeda, S.; Takata, T.; Kondo, T.; Hitoki, G.; Hara, M.; Kondo, J. N.; Domen, K.; Hosono, H.; Kawazoe, H.; Tanaka, A. Mechanocatalytic overall water splitting. Chem. Commun. 1998, 2185−2186. (81) Gao, G.; Jiao, Y.; Ma, F.; Jiao, Y.; Waclawik, E.; Du, A. Metalfree graphitic carbon nitride as mechano-catalyst for hydrogen evolution reaction. J. Catal. 2015, 332, 149−155. (82) Wang, X.; Hong, M.; Zhang, F.; Zhuang, Z.; Yu, Y. Recyclable Nanoscale Zero Valent Iron Doped g-C3N4/MoS2 for Efficient Photocatalysis of RhB and Cr(VI) Driven by Visible Light. ACS Sustainable Chem. Eng. 2016, 4, 4055−4062. (83) Chen, D.; Wang, K.; Hong, W.; Zong, R.; Yao, W.; Zhu, Y. Visible light photoactivity enhancement via CuTCPP hybridized gC3N4 nanocomposite. Appl. Catal., B 2015, 166-167, 366−373. (84) Gu, Q.; Liao, Y.; Yin, L.; Long, J.; Wang, X.; Xue, C. Templatefree synthesis of porous graphitic carbon nitride microspheres for enhanced photocatalytic hydrogen generation with high stability. Appl. Catal., B 2015, 165, 503−510. (85) Yu, J.; Jin, J.; Cheng, B.; Jaroniec, M. A noble metal-free reduced graphene oxide-CdS nanorod composite for the enhanced visible-light photocatalytic reduction of CO2 to solar fuel. J. Mater. Chem. A 2014, 2, 3407−3416. (86) Xiao, X.; Wei, J.; Yang, Y.; Xiong, R.; Pan, C.; Shi, J. Photoreactivity and Mechanism of g-C3N4 and Ag Co-Modified Bi2WO6 Microsphere under Visible Light Irradiation. ACS Sustainable Chem. Eng. 2016, 4, 3017−3023. (87) Bai, X.; Wang, L.; Wang, Y.; Yao, W.; Zhu, Y. Enhanced oxidation ability of g-C3N4 photocatalyst via C-60 modification. Appl. Catal., B 2014, 152-153, 262−270. (88) Liu, J.; Liu, Y.; Liu, N.; Han, Y.; Zhang, X.; Huang, H.; Lifshitz, Y.; Lee, S.-T.; Zhong, J.; Kang, Z. Metal-free efficient photocatalyst for stable visible water splitting via a two-electron pathway. Science 2015, 347, 970−974.
(89) Wan, W.; Yu, S.; Dong, F.; Zhang, Q.; Zhou, Y. Efficient C3N4/ graphene oxide macroscopic aerogel visible-light photocatalyst. J. Mater. Chem. A 2016, 4, 7823−7829.
2236