Novel Photoalignment Method Based on Low-Molecular-Weight

Subscriber access provided by UNIV OF SCIENCES PHILADELPHIA

Article

A Novel Photoalignment Method Based on Low-molecular-weight Azobenzene Dyes and its Application for High-dichroic-ratio Polarizers Su Pan, Jacob Yeuk-Lung Ho, and Hoi Sing Kwok ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.8b00104 • Publication Date (Web): 14 Feb 2018 Downloaded from http://pubs.acs.org on February 16, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

A Novel Photoalignment Method Based on Lowmolecular-weight Azobenzene Dyes and its Application for High-dichroic-ratio Polarizers Su Pan*, Jacob Y. Ho, Vladimir G. Chigrinov and Hoi Sing Kwok State Key Lab on Advanced Displays and Optoelectronics, Department of Electronic and Computer Engineering, Hong Kong University of Science and Technology, Clear Water Bay, Kowloon, Hong Kong, China KEYWORDS: photoalignment, azobenzene dye, polarizer, dichroic ratio, order parameter

ABSTRACT: Photoalignment is a simple tecnique for manipulation of molecular orientations, which has been widely used in liquid crystal displays. Here we propose a novel photoalignment method, in which an azobenzene dye thin film is deposited by thermal evaporation and in situ exposed to linear polarized light simultaneously. We obtain polarizers with a dichroic ratio up to 62, which is the highest value ever realized by a photoalignment method. Moreover, the polarizing thin film has a thickness of just 200 nm, compatible with flexible substrates, making it perfect for use as a dichroic polarizer in ultra-thin and flexible displays.

1. INTRODUCTION

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 20

Dichroic polarizers are indispensable elements in flat panel displays, which are ubiquitous in modern life. Conventional polarizing thin films are based on mechanically stretching polyvinyl alcohol (PVA) doped with iodine; such polarizers are low cost and have a high dichroic ratio (N>60).1 The dichroic ratio (N) is the key parameter to evaluate the optical performance of a dichroic polarizer, which is defined as N=A⊥/A∥, where A⊥ and A∥ are the absorbances perpendicular and parallel to the transmission axis of the polarizer, respectively. For highperformance liquid crystal displays (LCDs), polarizers with a dichroic ratio of more than 50 are required.2 Besides the optical performance, the thickness of the elements in the displays is also a crucial selection criterion. With the rapid development of ultra-thin displays, the demand for ultra-thin polarizers is urgent, as the thickness of conventional polarizers is around 25 µm, which is not satisfactory for such displays. Polarizers of a thickness at 5 µm have been developed by the stretching method recently,3 but further reduction of the thickness is very challenging because ultra-thin PVA films are fragile to handle during the stretching process. Besides the reduction of the thickness and weight, ultra-thin polarizers have an overwhelming advantage in flexible LCDs because they are able to be placed inside the liquid crystal cells to eliminate the light leakage problem resulting from the birefringence of the flexible substrates.4 Furthermore, there is a serious concern with using conventional polarizers in thin and flexible displays. The shrinkage force generated in the stretching process will cause panel bending and display distortion when there is little rigid support in the device.5 Therefore, a novel technique capable of producing an ultra-thin polarizer without this shrinkage issue is highly anticipated for ultra-thin and flexible displays. A thin polarizer with a thickness less than 1 µm and based on lyotropic liquid crystalline (LLC) molecules has been reported.6 However, the dichroic ratio of this LLC polarizer is smaller


2

Page 3 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


than 25, which cannot satisfy the requirements of high-performance displays. Additionally, a high-contrast polarizer with a thickness of 5 µm and based on the guest-host effect has been demonstrated by Peeters et al.,2 but the film is not sufficiently thin and the fabrication process is complicated. The photoalignment method is a simple way to manipulate the orientation of molecules in a non-contact way by exposure to linearly polarized light.7 Photoalignment is advantageous because it can avoid mechanical damage and electrostatic charges, which are inevitably generated by the rubbing technique. Moreover, photoalignment offers great convenience to realize complex orientations.8-11 Therefore, it has wide applications in liquid crystal alignment,7, 12-14

optical actuators,10 polarized light emission15, 16 and polarizers.17-19 Azobenzene dye

molecules are common materials applied for dichroic polarizers by photoalignment.18, 20, 21 The dichroic ratios previously achieved by photoalignment are around 20,17, 18, 22 except the value of 50 obtained by photosensitive ionic self-assembly complexes.19 Further improvement to achieve a dichroic ratio for high-performance LCDs (N>50) has never been realized by using existing photoalignment methods before. In this paper, we introduce a novel in situ photoalignment technique and demonstrate an ultra-thin high-dichroic-ratio polarizer with a dichroic ratio of 62. This high-dichroic ratio polarizer can fulfill the requirement of high-performance displays. Moreover, the polarizer is 200 nm thick, which can reduce the thickness of the displays and also makes the polarizer suitable to be placed inside the liquid crystal cells to improve the optical performance. Additionally, the in situ photoalignment method eliminates the shrinkage problem, and the polarizing thin films produced are highly compatible with flexible displays.


3


Page 4 of 20

2. RESULTS AND DISCUSSION In the in situ method, we deposit and simultaneously irradiate an azobenzene dye thin film with linear polarized light, as shown in Figure 1(a). The thermal evaporation technique is intensively employed in thin film deposition due to its low cost, minimal damage to the surface of functional materials and low tendency to unintentional heat to the substrate. Low-molecularweight molecules are suitable for thermal evaporation because their melting temperature is relatively low. The chemical structure of the low-molecular-weight azobenzene dye 4,4’-([1,1’Biphenyl]-4,4’-diylbis(diazene-2,1- diyl))bis(N,N-dibutylaniline) (AD-1) we use, which is synthesized and additionally purified by preparative column chromatography and recrystallization23, 24, is shown in Figure 1(b). The AD-1 material is melted at 144 °C and shows good thermal stability until 320 °C. (Thermo gravimetric analysis data is shown in Figure S1.) The molecular orbitals of AD-1 are highly anisotropic, which is critical to obtain high dichroism. The UV-vis absorption spectrum of AD-1 in toluene solution is shown in Figure 1(c). The absorption peaks are located at 321 nm and 464 nm.


4

Page 5 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 1. (a) Schematic diagram of the in situ photoalignment technique. The linear polarized light is guided into the vacuum chamber with a small oblique angle to the substrate. The AD-1 source is put at the bottom of the chamber, right below the glass substrate. The deposition rate is controlled by the heating temperature. The irradiation of the AD-1 molecules starts and stops synchronously with the deposition process. (b) Chemical structure of the AD-1 molecule. (c) The


5


Page 6 of 20

UV-vis absorption spectrum of AD-1 in toluene solution. The absorption peaks are located at 321 nm and 464 nm. During the deposition of AD-1 thin film, the vacuum in the chamber is kept as low as 10-6 Torr. The deposition rate is controlled by the heating temperature of AD-1 powders. The absorption spectrum of a 200-nm thick deposited AD-1 film (without alignment) is shown in Figure 2(a). The absorbance band in visible region is broadened and the peak is slightly blueshifted to 439 nm, which is due to the molecular aggregation and π−π stacking.23, 25 Besides, the optical density of the 200-nm thick thin film is quite large, which is beneficial to realize an ultrathin polarizer. The surface morphology of the thin film is measured by atomic force microscope (AFM) is exhibited in Figure 2(b). The root mean square of the roughness in a 10 µm × 10 µm area is 2.327 nm, which indicates a smooth surface of the AD-1 thin film.

Figure 2. (a) Absorption spectrum of this AD-1 thin film deposited by vacuum evaporation. Two absorption peaks are located at 322 nm and 439 nm. (b) Surface topography of the evaporated


6

Page 7 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


AD-1 thin film with a thickness of 200 nm. The root mean square of the roughness in a 10 µm × 10 µm area is 2.327 nm.

To align the AD-1 molecules, the thin film is illuminated by linear polarized light. The absorption of the molecules is proportional to cos2 θ, where θ is the angle between the absorption oscillator of the AD-1 molecules and the polarization of the pump light. The molecules located at the smaller θ are more able to be excited and rotate via iterative isomerization and diffusion. Finally, the molecules will reach a steady anisotropic angular distribution, and an orientation perpendicular to the polarization is preferred.7 In the in situ photoalignment method, the irradiation starts and stops synchronously with the thermal evaporation process of the AD-1 thin film. A linear polarized He-Cd laser (442 nm) is expanded and guided to the glass substrate in a vacuum chamber through an optical window. The light is uniformly distributed around a 15 mm × 15 mm area, and its intensity is fixed at 5 mW cm-2. The exposure dosage is varied by changing the exposure time, and the exposure time is the same as the deposition time, which is changed according to the deposition rate for thin films of a given thickness. In our experiments, the 200-nm thickness of the AD-1 film is a result of balancing the transmission and contrast ratio of the polarizer. We firstly compare the polarizers produced by the in situ method and the conventional photoalignment method, in which all the conditions are kept the same as for the in situ method, except that the irradiation starts after the thin film has been completely deposited. Polarizing optical microscopy pictures of the AD-1 thin films obtained by the two methods are demonstrated in Figure 3. With the conventional method, the AD-1 molecules are randomly


7


Page 8 of 20

oriented and show birefringence in domains under cross polarizers, which is shown in Figure 3(a). The domains disappear after the photoalignment (Figure 3(b)), which indicates the homogenous alignment direction of the AD-1 molecules. The microscopy image of the AD-1 polarizer produced by the in situ photoalignment is shown in Figure 3(c), and there are no domains because the AD-1 is photoaligned during the deposition. Moreover, the crystalline properties of the AD-1 powders and films are investigated by the X-ray diffraction (XRD) technique. The AD-1 powders show several obvious diffraction peaks, as exhibited in Figure 4(a), which indicates that the AD-1 molecules in powders are packed with strong crystalline properties. The XRD results of the AD-1 thin films produced by both the conventional and in situ photoalignment methods show a sharp peak and a broad amorphous peak with several small peaks, as shown in Figure 4(b). The small peaks of the AD-1 thin film by in situ photoalignment is more obvious than those by conventional photoalignment, which may indicate a stronger semicrystalline property of the AD-1 polarizer by in situ method and favorability to achieve a higher order parameter. The order parameter (S) is a parameter describing the degree of order of the molecules, and it can be calculated by the dichroic ratio ( 1 / 2 ) under the assumption that the transition dipole moment is parallel to the molecular long axis.26

Figure 3. Polarizing optical microscopy images of the AD-1 thin films (200 nm) produced by both conventional photoalignment and in situ photoalignment techniques. (a) Vacuum deposited AD-1 thin films. (b) AD-1 thin films by conventional photoalignment. (c) AD-1 thin films by in situ photoalignment. The scale bars are 100 µm.


8

Page 9 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 4. (a) X-ray diffraction of AD-1 powders. The three main peaks appear at 2θ=8.1º, 20.1º and 24.6º, which indicates the strong crystalline property of the AD-1 powders. (b) XRD results of the AD-1 thin films by both the conventional photoalignment and in situ photoalignment methods.

Polarized UV-vis absorption spectra parallel and perpendicular to the polarization of the pump light are measured. The calculated dichroic ratios (at 450 nm) of the polarizers produced by both methods are demonstrated in Figure 5. The dichroic ratio achieved by the in situ method is much larger than that produced by the conventional method under the same exposure energy. During the photoalignment process, the free volume surrounding the excited molecules is significant for the molecular reorientation. It is generally known that a minimum local free volume is essential for the isomerization of azobenzene dyes.27, 28 What’s more, it has been reported that the order parameter of azobenzene dyes after photoalignment is improved with more free volume.29 For the conventional photoalignment method, the AD-1 thin films are deposited first and the molecular aggregation is completed before the photoalignment, so there is not much free volume for the molecular movement, which results in a low dichroic ratio. However, in the in situ method, the azobenzene molecules are evaporated and irradiated when the molecular packing is not very strong because the surrounding molecules have not settled down and the upper


9


Page 10 of 20

molecules have not yet been evaporated. Therefore, there are large free volumes for the freshly evaporated AD-1 molecules and they can easily rotate with small steric hindrance when they are excited by the pump light, and are finally oriented with a high order parameter.

Figure 5. Comparison of dichroic ratios (at 450 nm) achieved by the in situ and conventional photoalignment methods. The substrate temperature is room temperature (23 °C). The light intensity of the linear polarized He-Cd laser (442 nm) is fixed at 5 mW cm-2 and the film thickness is 200 nm. In the conventional photoalignment method, the irradiation starts after the thin film has been completely deposited and the other conditions are kept the same as in the in situ method. The maximum dichroic ratios realized by the in situ and conventional photoalignment methods are 62 and 15 at a dosage of 33 J cm-2, respectively.


10

Page 11 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


The dichroic ratios achieved by both methods grow as the exposure energy increases. The maximum dichroic ratios realized by the in situ and conventional photoalignment methods are 62 and 15 at a dosage of 33 J cm-2, respectively. It should be noted that for the in situ photoalignment method, the dichroic ratio decreases to 35 when the exposure energy increases to 50 J cm-2. This is because there are more free volumes during the photo-reorientation in this method, which may result in out-of-plane alignment under a very high excitation energy, reducing the dichroic ratio. The value of 62 is the highest dichroic ratio achieved by a photoalignment method so far and satisfies the requirement for high-performance LCDs. The absorption spectra parallel and perpendicular to the polarization of the pump light are exhibited in Figure 6(a), and the wavelength-dependent dichroic ratio is shown in Figure 6(b). The photos of the produced AD-1 polarizer on a polarized lighting device are shown in Figure 6(c), and its video is demonstrated in supporting information (Video S1). Moreover, the energy consumed at the maximum dichroic ratio is just 33 J cm-2. This is much lower than for the photosensitive ionic self-assembly complexes method, in which a dosage of 850 J cm-2 is required to obtain a dichroic ratio of 50.19 Consequently, this in situ technique is the most efficient and economical photoalignment method.


11


Page 12 of 20

Figure 6. (a) The measured absorbance parallel and perpendicular to the polarization of the pump laser after in situ photoalignment at a dosage of 33 J cm-2. (b) The calculated dichroic ratio. The peak is located around 450 nm. (c) Photos of the produced AD-1 polarizer on a polarized lighting device. In the left-hand picture, the polarization axis of the AD-1 polarizer is placed parallel to the polarization of the light box. The sample rotated 90◦ is shown in the righthand picture. The size of the sample is 20 mm × 20 mm. An area of around 15 mm × 15 mm in the center is exposed to the linear polarized He-Cd laser (442 nm), while the surrounding area


12

Page 13 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


corresponds to unexposed AD-1. The blank spaces at two corners are the sites at which we fixed the glass substrate, so there are no AD-1 molecules.

Next we investigate the effect of the substrate temperature, which is an influential factor in the photo-isomerization and diffusion process.30, 31 We change the substrate temperature during the in situ photoalignment and preserve the other conditions of the process in which the dichroic ratio of 62 is achieved. The dependence of the dichroic ratio on substrate temperature is demonstrated in Figure 7. It is found that the dichroic ratio decreases rapidly to 20 when the substrate temperature rises to 50 °C. The rise of the temperature will accelerate the thermal diffusion towards isotropy.32 Besides, the trans isomers are more stable at an elevated temperature, which decelerates the molecular reorientation by trans-cis-trans isomerization.33 Therefore, a high temperature is not favorable in the photoalignment process. However, the dichroic ratio is not improved further under lower temperatures, and is reduced to 35 at 5 °C because the rotational mobility of the molecules decreases when the temperature decreases.34 What’s more, it is reported that no reorientation is observed when the temperature is below a threshold. Therefore, room temperature (23 °C) is optimal to obtain the highest dichroic ratio by balancing the photo-reorientation process and thermal diffusion. This in situ photoalignment is advantageous to integrate with flexible display manufacturing because no extra heating is necessary and the flexible substrates’ tolerance to heat is of no concern.


13


Page 14 of 20

Figure 7. The influence of the substrate temperature on dichroic ratios (at 450 nm) in the in situ photoalignment method at a dosage of 33 J cm-2. The optimal substrate temperature is room temperature (23 °C). Finally, the compatibility of this in situ photoalignment technique with flexible substrates is investigated. We bond a piece of 150-µm thick polyethylene terephthalate (PET) film on a glass substrate to ensure a flat surface during the evaporation because curved substrates can cause nonuniformity of the incident angle and light distribution. After the in situ photoalignment process, a flexible polarizer with a dichroic ratio around 50 at 450 nm is obtained under the previous optimal conditions. The optical performance is exhibited in Figure S2, and the video of it on a polarized lighting device is shown in the supporting information (Video S2). The small drop in the dichroic ratio may be due to the change of surface tension and roughness. The thickness of the polarizing thin film is just 200 nm, which makes it able to be inserted inside liquid crystal


14

Page 15 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


cells to avoid optical performance deterioration resulting from the birefringence of flexible substrates. Photoalignment is a simple and low-cost way to produce dichroic polarizers, and it shows advantages for flexible displays because the polarizers it produces are ultra-thin, able to be integrated inside liquid crystal cells and free from the shrinkage issue. The main hindrance to the practical application of dichroic polarizers produced by photoalignment is the insufficient dichroic ratio. In this work, a polarizer with a dichroic ratio of more than 60 is, for the first time, achieved by a photoalignment method. By in situ photoaligning the dye molecules simultaneously with the thin film deposition process, the molecules rotate under unfastened circumstances and are free to orient themselves with a high order parameter. They can therefore show a much higher dichroic ratio than in the conventional photoalignment processes. This in situ photoalignment technique paves a new way to realize high-performance polarizing thin films that can rival commercial PVA/iodine polarizers. Moreover, this technique achieves molecules with an order parameter as large as 0.95 and may be applied in polarized emission to double the optical efficiency of displays. Finally, the photoalignment based on azobenzene dyes is a reversible process, and additional passivation is necessary to stabilize the molecules after the alignment.35 This means that we can reorient the direction of the molecules by additional exposure, and the method possesses particular advantages in realizing patterned alignments, which show great potential in photonic applications.8 3. CONCLUSION In conclusion, we have proposed an in situ photoalignment method and successfully demonstrated an ultra-thin high-dichroic-ratio polarizer. Compared with conventional photoalignment methods, this novel technique has realized oriented dye molecules with a large


15


Page 16 of 20

order parameter, which show a very high dichroic ratio, up to 62. Moreover, the energy consumption is low, which is more economical for practical manufacturing. Furthermore, the thickness of the produced polarizer is only 200 nm and the fabrication process is highly compatible with flexible substrates, which is urgently demanded for ultra-thin and flexible displays. We believe this polarizer has overwhelming advantages for next-generation displays, and the superior photoalignment technique has promising applications in manipulation of molecular orientation. Supporting information Experimental details including material characterization, fabrication process, atomic force microscopy and spectroscope measurement; thermo gravimetric analysis result of AD-1 molecules; measured absorbance and dichroic ratio of 200-nm AD-1 polarizing thin film on 150µm thick PET substrate after the in situ photoalignment; optical performance of the commercial PVA/iodine polarizer; video of the AD-1 polarizers on a polarized lighting device.

Corresponding Author Su Pan*, Email address: [email protected] ACKNOWLEDGMENT This work was mainly supported by the State Key Laboratory on Advanced Displays and Optoelectronics Technologies of The Hong Kong University of Science and Technology. The characterizations were performed in the Materials Characterization and Preparation Facility of


16

Page 17 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


The Hong Kong University of Science and Technology. The authors acknowledge Dr. Vashchenko V. V. and Krivoshey A. I. for preparation of AD-1 according to HKUST-STCU project #P641a.

References (1) Land, E. H. Some Aspects of the Development of Sheet Polarizers*. JOSA 1951, 41, 957-963. (2) Peeters, E.; Lub, J.; Steenbakkers, J. A.; Broer, D. J. High‐Contrast Thin‐Film Polarizers by Photo‐Crosslinking of Smectic Guest–Host Systems. Adv Mater 2006, 18, 2412-2417. (3) Izaki, A.; Kitagawa, T.; Goto, S.; Kamijo, T.; Mori, T.; Miyatake, M. Thin polarizing film, optical laminate with thin polarizing film, and production method for thin polarizing film, US patent 9227222 B2 2016. (4) Crawford, G. Flexible Flat Panel Displays; John Wiley & Sons: 2005. (5) Lin, T.; Chen, A.; Chen, S.; Leu, J. Effects of thermomechanical properties of polarizer components on light leakage in thin-film transistor liquid-crystal displays. Japanese Journal of Applied Physics 2015, 54, 076701. (6) Khan, I. G.; Belyaev, S.; Malimonenko, N.; Kleptsyn, V.; Kukushkina, M.; Masanova, N.; Solovei, V.; Vorozhtsov, G. 46.4: Ultra‐Thin O‐Polarizers' Superiority over E‐Polarizers for LCDs. SID Symposium Digest of Technical Papers. 2004, 35, 1316-1319. (7) Chigrinov, V. G.; Kozenkov, V. M.; Kwok, H. Photoalignment of liquid crystalline materials: physics and applications; John Wiley & Sons: 2008. (8) Guo, Y.; Jiang, M.; Peng, C.; Sun, K.; Yaroshchuk, O.; Lavrentovich, O.; Wei, Q. High‐ Resolution and High‐Throughput Plasmonic Photopatterning of Complex Molecular Orientations in Liquid Crystals. Adv Mater 2016, 28, 2353–2358. (9) Du, T.; Fan, F.; Tam, A. M. W.; Sun, J.; Chigrinov, V. G.; Sing Kwok, H. Complex nanoscale‐ordered liquid crystal polymer film for high transmittance holographic polarizer. Adv Mater 2015, 27, 7191-7195. (10) de Haan, L. T.; Sánchez‐Somolinos, C.; Bastiaansen, C. M.; Schenning, A. P.; Broer, D. J. Engineering of complex order and the macroscopic deformation of liquid crystal polymer networks. Angewandte Chemie International Edition 2012, 51, 12469-12472. (11) Morikawa, Y.; Kondo, T.; Nagano, S.; Seki, T. Photoinduced 3D ordering and patterning of microphase-separated nanostructure in polystyrene-based block copolymer. Chemistry of Materials 2007, 19, 1540-1542.


17


Page 18 of 20

(12) Ichimura, K.; Furumi, S.; Morino, S.; Kidowaki, M.; Nakagawa, M.; Ogawa, M.; Nishiura, Y. Photocontrolled orientation of discotic liquid crystals. Adv Mater 2000, 12, 950-953. (13) Fukuhara, K.; Fujii, Y.; Nagashima, Y.; Hara, M.; Nagano, S.; Seki, T. Liquid‐Crystalline Polymer and Block Copolymer Domain Alignment Controlled by Free‐Surface Segregation. Angewandte Chemie International Edition 2013, 52, 5988-5991. (14) Obi, M.; Morino, S.; Ichimura, K. Factors affecting photoalignment of liquid crystals induced by polymethacrylates with coumarin side chains. Chemistry of materials 1999, 11, 656664. (15) Contoret, A. E.; Farrar, S.; Jackson, P.; Khan, S.; May, L.; O'Neill, M.; Nicholls, J.; Kelly, S.; Richards, G. Polarized Electroluminescence from an Anisotropic Nematic Network on a Non‐contact Photoalignment Layer. Adv Mater 2000, 12, 971-974. (16) Furumi, S.; Janietz, D.; Kidowaki, M.; Nakagawa, M.; Morino, S.; Stumpe, J.; Ichimura, K. Polarized photoluminescence from photopatterned discotic liquid crystal films. Chemistry of materials 2001, 13, 1434-1437. (17) Yip, W.; Kwok, H. S.; Kozenkov, V. M.; Chigrinov, V. G. Photo-patterned e-wave polarizer. Displays 2001, 22, 27-32. (18) Matsumori, M.; Takahashi, A.; Tomioka, Y.; Hikima, T.; Takata, M.; Kajitani, T.; Fukushima, T. Photoalignment of an azobenzene-based chromonic liquid crystal dispersed in triacetyl cellulose: single-layer alignment films with an exceptionally high order parameter. ACS applied materials & interfaces 2015, 7, 11074-11078. (19) Zakrevskyy, Y.; Stumpe, J.; Faul, C. F. A Supramolecular Approach to Optically Anisotropic Materials: Photosensitive Ionic Self‐Assembly Complexes. Adv Mater 2006, 18, 2133-2136. (20) Chigrinov, V.; Kwok, H. S.; Takada, H.; Takatsu, H. Photo‐aligning by azo‐dyes: Physics and applications. Liquid Crystals Today 2005, 14, 1-15. (21) Advincula, R. C.; Fells, E.; Park, M. Molecularly ordered low molecular weight azobenzene dyes and polycation alternate multilayer films: aggregation, layer order, and photoalignment. Chemistry of materials 2001, 13, 2870-2878. (22) Kozenkov, V. M.; Yip, W. C.; Chigrinov, V. G.; Kwok, H. S. Photo-induced dichroic polarizers and fabrication methods thereof , US patent 576485 B2 2013. (23) Zhang, Y.; Zhuang, H.; Yang, Y.; Xu, X.; Bao, Q.; Li, N.; Li, H.; Xu, Q.; Lu, J.; Wang, L. Thermally stable ternary data-storage device based on twisted anthraquinone molecular design. The Journal of Physical Chemistry C 2012, 116, 22832-22839.


18

Page 19 of 20 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(24) Lewis, G.; Reiss, J. Photochemical reactions of azo compounds. XI. Formation and characterization of 2-Dimethylaminobenzo [c] cinnoline. Aust. J. Chem. 1967, 20, 1451-1455. (25) Surin, M.; Sonar, P.; Grimsdale, A. C.; Müllen, K.; De Feyter, S.; Habuchi, S.; Sarzi, S.; Braeken, E.; Ver Heyen, A.; Van der Auweraer, M. Solid-state assemblies and optical properties of conjugated oligomers combining fluorene and thiophene units. Journal of Materials Chemistry 2007, 17, 728-735. (26) Ivashchenko, A. V. Dichroic dyes for liquid crystal displays; CRC Press: 1994. (27) Xie, S.; Natansohn, A.; Rochon, P. Recent developments in aromatic azo polymers research. Chemistry of Materials 1993, 5, 403-411. (28) Paik, C. S.; Morawetz, H. Photochemical and thermal isomerization of azoaromatic residues in the side chains and the backbone of polymers in bulk. Macromolecules 1972, 5, 171-177. (29) Shi, Y.; Zhao, C.; Ho, J. Y.; Vashchenko, V. V.; Srivastava, A. K.; Chigrinov, V. G.; Kwok, H.; Song, F.; Luo, D. Exotic Property of Azobenzenesulfonic Photoalignment Material Based on Relative Humidity. Langmuir 2017, 33, 3968-3974. (30) Fischer, E. Temperature dependence of photoisomerization equilibria. Part I. Azobenzene and the azonaphthalenes. J. Am. Chem. Soc. 1960, 82, 3249-3252. (31) Chigrinov, V.; Pikin, S.; Verevochnikov, A.; Kozenkov, V.; Khazimullin, M.; Ho, J.; Huang, D. D.; Kwok, H. Diffusion model of photoaligning in azo-dye layers. Physical Review E 2004, 69, 061713. (32) Hore, D.; Natansohn, A.; Rochon, P. Irradiance and temperature dependence of photoinduced orientation in two azobenzene-based polymers. Canadian journal of chemistry 1998, 76, 1648-1653. (33) Malkin, S.; Fischer, E. TEMPERATURE DEPENDENCE OF PHOTOISOMERIZATION. PART II. 1 QUANTUM YIELDS OF cis⇆ trans ISOMERIZATIONS IN AZO-COMPOUNDS. J. Phys. Chem. 1962, 66, 2482-2486. (34) Schönhoff, M.; Mertesdorf, M.; Lösche, M. Mechanism of photoreorientation of azobenzene dyes in molecular films. J. Phys. Chem. 1996, 100, 7558-7565. (35) Tseng, M.; Yaroshchuk, O.; Bidna, T.; Srivastava, A. K.; Chigrinov, V.; Kwok, H. Strengthening of liquid crystal photoalignment on azo dye films: passivation by reactive mesogens. RSC Advances 2016, 6, 48181-48188. (36) Matsumori, M.; Takahashi, A.; Tomioka, Y.; Hikima, T.; Takata, M.; Kajitani, T.; Fukushima, T. Photoalignment of an azobenzene-based chromonic liquid crystal dispersed in triacetyl cellulose: single-layer alignment films with an exceptionally high order parameter. ACS applied materials & interfaces 2015, 7, 11074-11078.


19


Page 20 of 20

For Table of Contents Only


20

Novel Photoalignment Method Based on Low-Molecular-Weight

Recommend Documents