Chapter 4

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

Photoinitiation of Acrylates via Sensitized Phthalimide Derivatives T. Brian Cavitt , Brian Phillips , Charles E. Hoyle , Chau K. Nguyen , Viswanathan Kalyanaraman , and Sonny Jönsson 1

1

1

1

2

3

1

School of Polymers and High Performance Materials, Department of Polymer Science, University of Southern Mississippi, 2609 West 4 Street, Hattiesburg, MS 39406 Becker-Acroma, Hattiesburg, MS 39406 Fusion UV-Curing Systems, Inc., 910 Clopper Road, Gaithersburg, MDd 20878-1357 th

2

3

When isopropylthioxanthone is used as a coinitiator for substituted N-phenylphthalimide photoinitiators, rapid rates of acrylate polymerization are attained if a tertiary amine is present as a hydrogen source. N-Phenylphthalimide with electron withdrawing substituents on the N-phenyl ring in the presence of a combination of isopropylthioxanthone and N­ -methyl-N,N-diethanolamine results in an increase in the maximum rate of polymerization of 1,6-hexanedioldiacrylate by a factor of as much as twice that attained when only the coinitiator and N-methyl-N,N-diethanolamine are present.

© 2003 American Chemical Society

In Photoinitiated Polymerization; Belfield, K., et al.; ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

41

42

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

Introduction As the EPA stipulates increasingly stringent regulations for coatings usage, industry has been forced to develop more "environmentallyfriendly"coatings (1). This has promoted steady growth in the UV-curable market over the last twenty years yielding novel technologies compliant to government regulations and consumer demand (2). Each of the major components of a UV-curable coating, monomers, reactive diluents, additives, and photoinitiators, have thus been investigated in detail to further the growth in this market. Being a vital component in photocurable formulations, photoinitiating systems are the subject of particularly extensive research. Most of this research has focused on Type I photoinitiators, which undergo an alpha cleavage process to form two radical species. An example of a Type I photoinitiator is 2,2dimethoxy-2-phenylacetophenone (DMPA), which undergoes cleavage alpha to the carbonyl to form a benzoyl radical and a tertiary carbon-centered radical. The benzoyl radical can subsequently initiate polymerization or abstract a hydrogen to form benzaldehyde. The second radical species rearranges to form methylbenzoate and a highly reactive methyl radical as an initiating species. Type II photoinitiators are a second class of photoinitiators and are based on compounds whose triplet excited states are reduced by a labile hydrogen transfer process thereby producing an initiating radical. Type II photoinitiators are exemplified by the traditional benzophenone/N-methyl-N,N-diethanolamine system where a hydrogen is transferred to the triplet excited state of benzophenone from the amine via an electron/proton transfer mechanism to yield a carbon-centered radical adjacent to the nitrogen capable of initiation and the semipinacol radical serving only to terminate propagating species. Recent work on new Type II photoinitiators has produced a system involving a maleimide or maleic anhydride, a tertiary amine such as N-methylΝ,Ν-diethanolamine, and a sensitizer (2, 3). Depending on the sensitizer and maleimide chosen for the initiating system, the resulting rate of polymerization can rival that of DMPA. The initiation process is probably based on a dual initiating mechanism involving an electron/proton transfer from the ketyl radical to the maleimide (e.g. chemical sensitization) and triplet energy transfer from the sensitizer to the maleimide. Phthalimide derivatives have electron affinities and reduction potentials that are comparable to those of maleimides, suggesting their use in three component photoinitiator systems (Table I). In this paper, phthalimide derivatives are evaluated for their viability in three component photoinitiators of acrylate polymerization.

In Photoinitiated Polymerization; Belfield, K., et al.; ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

43

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

Table L Electron affinities and reduction potentials of several electron acceptors

Maleimide N-Methylmaleimide N-Phenylmaleimide Phthalimide N-Phenylphthalimide

Electron AffinityiA)

Reduction Potential^)

1.16 1.12 1.36 1.01 1.16

... -1.45 -1.31

— —

NOTE: The units for electron affinity and reduction potential are electron volts and volts, respectively.

Experimental Materials N-methyl-N,N-diethanolamine (MDEA), N-phenylphthalimide (PPI), 4aminophthalonitrile, and 4-aminoveratrole were obtained from the Aldrich Chemical Company. UCB provided 1,6-hexanedioldiacrylate (HDDA). The Albemarle Corporation supplied isopropylthioxanthone. The Stepan Company furnished the phthalic anhydride used in the synthesis of N-(3,4dimethoxyphenyl) phthalimide, denoted DMPPI, and N-(3,4-dicyanophenyl) phthalimide, denoted DCPPI. Synthesis of DMPPI and DCPPI proceeded as given in the literature (d).

Photo-Differential Scanning Calorimetry Exotherms were measured on a Perkin-Elmer Differential Scanning Calorimeter 7 modified to accommodate a Canrad-Hanovia medium pressure mercury lamp source from Ace Glass. Light intensities were measured at the sample pans via a black body absorber. A mechanical shutter was placed between the light source and the sample chamber to provide control of exposure time. Sample pans were specially crimped and injected with 2 \3JL samples, giving a film thickness on the order of 200 μχη (about 8 mils).

In Photoinitiated Polymerization; Belfield, K., et al.; ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

44

Phosphorescence

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

Phosphorescence studies performed on a Spex Fluorolog 2fluorimeterwere used to estimate the triplet energies of the phthalimides for comparison to the sensitizers. An ethanol/methylene chloride glass (77 K) was used to observe phthalimide phosphorescence at 77 K. The triplet energies were taken as the energy corresponding to the phosphorescence intensity being 10% of the maximum peak intensity where no defined peak was discernable.

Laser Flash Photolysis Laser flash photolysis lifetime quenching data were obtained by using a system based upon a Continuum Nd-YAG laser as the excitation source and a pulsed xenon probe and data acquisition/analysis system from Applied Photophysics. The ultimate time resolution of the laser flash instrument was approximately 15-20 ns. Each sample was purged with nitrogen for fifteen minutes in the sealed quartz cell. The excitation wavelength was 355 nm where only the sensitizer appreciably absorbed. The analysis wavelength was 630 nm for isopropylthioxanthone.

Results and Discussion Photo-Differential Scanning Calorimetry (Photo-DSC) In the past, we have used several diaryl ketone sensitizers with maleimides in the presence of tertiary amines to initiate acrylate polymerization. Three of these diaryl ketones, benzophenone, 4-benzoylbiphenyl and isopropylthioxanthone, were studied in great detail (2,3). All of these sensitizers were also investigated in conjunction with various phthalimides in the presence of an amine. In all of these investigations, systems that incorporated isopropylthioxanthone (ΓΓΧ) gave higher polymerization rates than benzophenone or 4-benzoylbiphenyl. Selected results are highlighted herein for several N-phenylphthalimides. The trends found for ITX are also found when benzophenone and 4-benzoylbiphenyl are used, although the rates are slower with the latter two sensitizers. In Figure 1, results for the photopolymerization of 1,6-hexanedioldiaerylate (HDDA) in the presence of several N-phenylphthalimide derivatives and an ITX/MDEA mixture were compared to the standard ΓΓΧ/MDEA initiating

In Photoinitiated Polymerization; Belfield, K., et al.; ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

45 system. The results are as expected and show that the phthalimides with electron withdrawing substituents [i.e. N-(3,4-dicyanophenyl) phthalimide DCPPI and N-(3-trifluoromethylphenyl phthalimide - CF3PPI] yield the fastest rates of initiation as exemplified by the peak maxima. The Nphenylphthalimide substituted with an electron donating group [i.e. N-(3methoxy phenyl) phthalimide - MPPI] as well as unsubstituted Nphenylphthalimide (PPI) resulted in only moderate rate increases compared to those achieved with ITX/MDEA alone. The results in Figure 1 certainly demonstrate that there is a correlation between the electron affinity of the phthalimide and its ability to initiate polymerization in the presence of an ITX/MDEA combination.

T i m e (min)

Figure 1. Photo-DSC exotherms of Phthalimide/ITX/MDEA in nitrogen purged HDDA. I =64.3I mW cm . Full arc of medium pressure mercury lamp. A is 0.028wt% ΓΓΧ, lwt% MDEA; Β is 0.1wt% PPI 0.028wt% ΠΧ, Iwt% MDEA; C is 0.1wt% DCPPI, 0.028wt% ITX, lwt% MDEA; D is 0.1 wt% CF3PPI, 0.028% by weight ITX, lwt% MDEA; Ε is 0.1wt% MPPI, 0.028wt% ITX, lwt%MDEA. 0

Next we present results that describe the effect that the phthalimide concentration has on the rate of polmerization. This investigation is prompted

In Photoinitiated Polymerization; Belfield, K., et al.; ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

46 by the effect that maleimide concentration has on the rate of acrylate photopolymerization where due to self quenching/inhibition reactions a maximum rate is achieved at only 0.1 wt% maleimide. Although we have measured results for several N-substituted phthalimides with increasing concentration, only results for PPI are presented herein for demonstration purposes. The effect of PPI concentration on the exotherm for HDDA polymerization with ITX as the sensitizer and MDEA as coinitiator is shown in Figure 2. At these higher concentrations of PPI, the rates are even greater than recorded when 0.1 wt% PPI was used (Figure 1). The rate increases even up to a concentration of 1 wt% phthalimide. This dichotomy between phthalimides and maleimides (increased maleimide concentration greater than 0.1 wt% results in a decrease in the polymerization rate) holds true for each of the other phthalimides in this present investigation (although as already mentioned, only results for PPI are given here). Apparently, the high self-quenching and polymerization inhibition characteristic of maleimides are not operative for sensitized phthalimides. 170T

0.0

0.2

0.4

0.6

0.8

1.0

T i m e (min)

Figure 2. Photo-DSC exotherms of ΡΡΙ/ΓΓΧ/MDEA in nitrogen purged HDDA. l =69.52 mW cm . Full arc of a medium pressure mercury lamp. A is 0.028wt% ITX, lwt9c MDEA; Β is 0.5wt% PPI, 0.028wt% ΓΓΧ, lwt% MDEA; Cislwt%PPI, 0.028wt%TTX, lwtVbMDEA. 0

In Photoinitiated Polymerization; Belfield, K., et al.; ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

47 Recalling the exotherm results in Figure 1, there is an indication that an electron donating group substituted on the phenyl ring does not result in an enhancement in the polymerization rate. It might be expected that two electron donating groups would result in a reduction in the ability of a phthalimide/ITX/amine system to intiate acrylate polymerization, since as will be shown in the next few sections the initiation is thought to involve an electron transfer process to the N-arylphthalimide molecule. In Figure 3, the results for a phthalimide/ITX/MDEA system where the phthalimide is N-(3,4dimethoxyphenyl) phthalimide (DMPPI) clearly show that introduction of a second methoxy donating group on the phthalimide ring results in a system that exhibits little appreciable increase in polymerization rate over that achieved with the basic ITX7MDEA initiating system alone. From these results it is clear that the methoxy substituents decrease the ability of DMPPI to participate in the electron/proton transfer process that forms radicals capable of initiating polymerization. In order to interpret the results in Figures 1-3, we next present photophysical results for the phosphorescence and transient specta of three of the phthalimides in this investigation with significantly different electron affinities. The electron affinities decrease in the order: DCPPI > PPI > DMPPI. 120t

T i m e (min)

Figure 3. Photo-DSC exotherms of DMPPI/ITX/MDEA in nitrogen purged HDDA. I =61.21 mW cm' . Full arc of a medium pressure mercury lamp. A is 0.028% by weight ITX, 1% by weight MDEA, HDDA; Β is 0.1% by weight DMPPI, 0.028% by weight ITX, 1% by weight MDEA, HDDA. 2

0

American Chemical Society Library 1155 IBth St., N.W.

In Photoinitiated Polymerization; Belfield, K., et al.; Washington, DC 20036 ACS Symposium Series; American Chemical Society: Washington, DC, 2003.

48

Downloaded by UCSF LIB CKM RSCS MGMT on November 25, 2014 | http://pubs.acs.org Publication Date: March 3, 2003 | doi: 10.1021/bk-2003-0847.ch004

Phosphorescence of Substituted N-Phenylphthalimide Derivatives. The triplet energies of DMPPI, PPI, DCPPI were determined using low temperature phosphorescence as 61.1 kcal/mol, 67.6 kcal/mol, and 68.6 kcal/mol, respectively. From these data, it is obvious that efficient photosensitization of DCPPI and PPI by classical energy transfer from ITX (Et=64 kcal/mol as determined in our lab via phosphorescence at 77 Κ in a 1:1 ethanol/methylene chloride glass) is not feasible, suggesting that another process is responsible for enhancing the polymerization rate of phthalimides in the presence of ITX and an amine. Before proposing an exact mechanism, laser flash photolysis results are presented for DMPPI, PPI, and DCPPI.

Laser Flash Photolysis Laser flash photolysis was used to determine the extent of the interaction of the phthalimide derivatives with the excited triplet state of ΓΓΧ. The lifetime decay of the ITX triplet state monitored at 630 nm was determined at increasing concentrations of the phthalimide derivative in order to calculate the quenching constant, kq, of ΓΓΧ (Ei=64 kcal/mol) by the phthalimide (Table II).

Table Π. Quenching constants of ITX by phthalimide derivatives Sensitizer

Quencher

1

k (Μ· s') q

7

ITX

DCPPI