Letter Cite This: ACS Macro Lett. 2019, 8, 205−212
pubs.acs.org/macroletters
Photoinitiated Polymerization-Induced Self-Assembly via Visible Light-Induced RAFT-Mediated Emulsion Polymerization Jianbo Tan,*,†,‡ Xiaocong Dai,† Yuxuan Zhang,† Liangliang Yu,† Hao Sun,§ and Li Zhang*,†,‡ †
Downloaded via EASTERN KENTUCKY UNIV on February 4, 2019 at 08:44:41 (UTC). See https://pubs.acs.org/sharingguidelines for options on how to legitimately share published articles.
Department of Polymeric Materials and Engineering, School of Materials and Energy, Guangdong University of Technology Guangzhou 510006, China ‡ Guangdong Provincial Key Laboratory of Functional Soft Condensed Matter, Guangzhou 510006, China § Department of Chemistry, Northwestern University, Evanston, Illinois 60208, United States S Supporting Information *
ABSTRACT: Aqueous emulsion polymerization is one of the most commonly used techniques in industry for the production of polymer latexes. In this contribution, we present photoinitiated polymerization-induced self-assembly (photo-PISA) based on aqueous visible light-induced reversible addition−fragmentation chain transfer (RAFT)-mediated emulsion polymerization at room temperature. A wide range of morphologies including spheres, worms, and vesicles have been achieved at room temperature by modulating reaction parameters. Additionally, this method enables access to inorganic nanoparticles-loaded vesicles by adding inorganic nanoparticles at the beginning of the polymerization. Finally, an oxygen-tolerant RAFT-mediated emulsion polymerization has been developed, allowing the synthesis of polymer nanoobjects at low volumes (e.g., in a 96-well plate). This study is expected to expand the scope of photo-PISA for the preparation of various block copolymer nano-objects in water at room temperature.
S
insoluble monomers are employed as the core-forming monomers and hydrophilic macromolecular RAFT (macroRAFT) agents are employed as the stabilizers. Charleux and co-workers,29−31 Davis and co-workers,32 and D’Agosto and co-workers33 reported that higher order morphologies, including worms and vesicles, were accessible by RAFTmediated emulsion polymerization employing statistic copolymers as macro-RAFT agents and styrene as the core-forming (co)monomer. The preparation of higher order morphologies by RAFT-mediated emulsion polymerization of methacrylic or acrylic monomers has rarely been reported. To overcome these limitations, temperature-directed morphology transformation method has been developed using thermoresponsive macroRAFT agents.34,35 Thermal initiation is usually employed to initiate the RAFT-mediated emulsion polymerization at high temperatures (e.g., 70 °C). Upon heating the thermoresponsive macro-RAFT agent above the lower critical solution temperature (LCST), the macro-RAFT agent becomes insoluble and additional surfactant is required to ensure the colloidal stability. It should be noteworthy that the presence of surfactant is not beneficial for applications in many areas (e.g., drug delivery). Moreover, the high reaction temperature hinders the preparation of thermosensitive or biorelated polymer nano-objects. While the method of aqueous RAFTmediated dispersion polymerization has been popular for the
olution self-assembly of amphiphilic block copolymers is a versatile method for the preparation of polymer nanoobjects with a diverse set of morphologies. The obtained polymer nano-objects have broad applications in different areas including catalysis, nanoreactor, biomineralization, drug delivery, and so on.1−4 Typically, the block copolymers are fully solubilized in a good solvent (for both blocks) and then a bad solvent (for one block) is added to drive the self-assembly. However, this cosolvent self-assembly method is typically performed in a diluted solution (solids 98%) was observed in each case when the reaction volume was gradually reduced to 1000, 500, or even 200 μL (Figure 5d). PPEGMA6-PtBA100 diblock copolymer nano-objects prepared at different volumes were then characterized by TEM. Mixed morphologies containing vesicles and worms were obtained in all studied cases (Figure S4), which is consistent with the sample prepared in a 10 mL round-bottom flask (Figure 1f). It should be noteworthy that magnetic stirring is critical for maintaining the colloidal stability during the polymerization. This oxygen-tolerant RAFT-mediated emulsion polymerization provides a promising strategy for nonexperts to prepare polymer nano-objects in a high-throughput manner. In conclusion, a novel photo-PISA method via visible lightinduced RAFT-mediated emulsion polymerization has been established for the synthesis diblock copolymer nano-objects. For the first time, higher order morphologies (including worms, vesicles and vesicles loaded with silica nanoparticles) were prepared by RAFT-mediated emulsion polymerization at room temperature. Furthermore, an oxygen-tolerant photoPISA strategy was also developed by adding GOx and glucose into the reaction, allowing the preparation of polymer nanoobjects in open air or multiwell plates. This method not only extends the application of polymerization-induced selfassembly, but also facilitates the formation of functional polymer nano-objects that are challenging to prepare by conventional RAFT-mediated emulsion polymerization.
■
(2) Hu, X.; Zhang, Y.; Xie, Z.; Jing, X.; Bellotti, A.; Gu, Z. StimuliResponsive Polymersomes for Biomedical Applications. Biomacromolecules 2017, 18 (3), 649−673. (3) Blackman, L. D.; Varlas, S.; Arno, M. C.; Fayter, A.; Gibson, M. I.; O’Reilly, R. K. Permeable Protein-Loaded Polymersome Cascade Nanoreactors by Polymerization-Induced Self-Assembly. ACS Macro Lett. 2017, 6 (11), 1263−1267. (4) Hu, X.; Hu, J.; Tian, J.; Ge, Z.; Zhang, G.; Luo, K.; Liu, S. Polyprodrug Amphiphiles: Hierarchical Assemblies for ShapeRegulated Cellular Internalization, Trafficking, and Drug Delivery. J. Am. Chem. Soc. 2013, 135 (46), 17617−17629. (5) Mai, Y.; Eisenberg, A. Self-Assembly of Block Copolymers. Chem. Soc. Rev. 2012, 41 (18), 5969−5985. (6) Charleux, B.; Delaittre, G.; Rieger, J.; D’Agosto, F. Polymerization-Induced Self-Assembly: From Soluble Macromolecules to Block Copolymer Nano-Objects in One Step. Macromolecules 2012, 45 (17), 6753−6765. (7) Sun, J.-T.; Hong, C.-Y.; Pan, C.-Y. Recent Advances in RAFT Dispersion Polymerization for Preparation of Block Copolymer Aggregates. Polym. Chem. 2013, 4 (4), 873−881. (8) Warren, N. J.; Armes, S. P. Polymerization-Induced SelfAssembly of Block Copolymer Nano-Objects via RAFT Aqueous Dispersion Polymerization. J. Am. Chem. Soc. 2014, 136 (29), 10174− 10185. (9) Canning, S. L.; Smith, G. N.; Armes, S. P. A Critical Appraisal of RAFT-Mediated Polymerization-Induced Self-Assembly. Macromolecules 2016, 49 (6), 1985−2001. (10) Wang, X.; Shen, L.; An, Z. Dispersion Polymerization in Environmentally Benign Solvents via Reversible Deactivation Radical Polymerization. Prog. Polym. Sci. 2018, 83, 1−27. (11) He, W.-D.; Sun, X.-L.; Wan, W.-M.; Pan, C.-Y. Multiple Morphologies of PAA-b-PSt Assemblies throughout RAFT Dispersion Polymerization of Styrene with PAA Macro-CTA. Macromolecules 2011, 44 (9), 3358−3365. (12) Wan, W.-M.; Pan, C.-Y. One-Pot Synthesis of Polymeric Nanomaterials via RAFT Dispersion Polymerization Induced SelfAssembly and Re-Organization. Polym. Chem. 2010, 1 (9), 1475− 1484. (13) Wan, W.-M.; Hong, C.-Y.; Pan, C.-Y. One-Pot Synthesis of Nanomaterials via RAFT Polymerization Induced Self-Assembly and Morphology Transition. Chem. Commun. 2009, 39, 5883−5885. (14) Derry, M. J.; Fielding, L. A.; Armes, S. P. PolymerizationInduced Self-Assembly of Block Copolymer Nanoparticles via RAFT Non-Aqueous Dispersion Polymerization. Prog. Polym. Sci. 2016, 52, 1−18. (15) Lowe, A. B. RAFT Alcoholic Dispersion Polymerization with Polymerization-Induced Self-Assembly. Polymer 2016, 106, 161−181. (16) Wang, X.; An, Z. New Insights into RAFT Dispersion Polymerization-Induced Self-Assembly: From Monomer Library, Morphological Control, and Stability to Driving Forces. Macromol. Rapid Commun. 2019, 40 (2), 1800325. (17) Zhou, W.; Qu, Q.; Xu, Y.; An, Z. Aqueous PolymerizationInduced Self-Assembly for the Synthesis of Ketone-Functionalized Nano-Objects with Low Polydispersity. ACS Macro Lett. 2015, 4 (5), 495−499. (18) Zhang, Y.; Han, G.; Cao, M.; Guo, T.; Zhang, W. Influence of Solvophilic Homopolymers on RAFT Polymerization-Induced SelfAssembly. Macromolecules 2018, 51 (11), 4397−4406. (19) Gao, C.; Wu, J.; Zhou, H.; Qu, Y.; Li, B.; Zhang, W. SelfAssembled Blends of AB/BAB Block Copolymers Prepared through Dispersion RAFT Polymerization. Macromolecules 2016, 49 (12), 4490−4500. (20) Huo, M.; Zeng, M.; Wu, D.; Wei, Y.; Yuan, J. Topological Engineering of Amphiphilic Copolymers via RAFT Dispersion Copolymerization of Benzyl Methacrylate and 2-(Perfluorooctyl)Ethyl Methacrylate for Polymeric Assemblies with Tunable Nanostructures. Polym. Chem. 2018, 9 (7), 912−919.
ASSOCIATED CONTENT
S Supporting Information *
The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsmacrolett.9b00007.
■
Full experimental section and additional results (PDF).
AUTHOR INFORMATION
Corresponding Authors
*E-mail:
[email protected]. *E-mail:
[email protected]. ORCID
Jianbo Tan: 0000-0002-5635-7178 Hao Sun: 0000-0001-9153-4021 Notes
The authors declare no competing financial interest.
■
ACKNOWLEDGMENTS The authors acknowledge support from the National Natural Science Foundation of China (Grant 21504017), Science and Technology Planning Project of Guangdong Province (Grant 2017A010103045), and Science and Technology Program of Guangzhou (Grant 201707010420). J.T. acknowledges the support from Pearl River Young Scholar.
■
REFERENCES
(1) Ning, Y.; Fielding, L. A.; Ratcliffe, L. P. D.; Wang, Y.-W.; Meldrum, F. C.; Armes, S. P. Occlusion of Sulfate-Based Diblock Copolymer Nanoparticles within Calcite: Effect of Varying the Surface Density of Anionic Stabilizer Chains. J. Am. Chem. Soc. 2016, 138 (36), 11734−11742. 210
DOI: 10.1021/acsmacrolett.9b00007 ACS Macro Lett. 2019, 8, 205−212
Letter
ACS Macro Letters (21) Huo, M.; Ye, Q.; Che, H.; Wang, X.; Wei, Y.; Yuan, J. Polymer Assemblies with Nanostructure-Correlated Aggregation-Induced Emission. Macromolecules 2017, 50 (3), 1126−1133. (22) Figg, C. A.; Simula, A.; Gebre, K. A.; Tucker, B. S.; Haddleton, D. M.; Sumerlin, B. S. Polymerization-Induced Thermal SelfAssembly (PITSA). Chem. Sci. 2015, 6 (2), 1230−1236. (23) Figg, C. A.; Carmean, R. N.; Bentz, K. C.; Mukherjee, S.; Savin, D. A.; Sumerlin, B. S. Tuning Hydrophobicity To Program Block Copolymer Assemblies from the Inside Out. Macromolecules 2017, 50 (3), 935−943. (24) Wright, D. B.; Touve, M. A.; Adamiak, L.; Gianneschi, N. C. ROMPISA: Ring-Opening Metathesis Polymerization-Induced SelfAssembly. ACS Macro Lett. 2017, 6 (9), 925−929. (25) Tan, J.; Xu, Q.; Li, X.; He, J.; Zhang, Y.; Dai, X.; Yu, L.; Zeng, R.; Zhang, L. Enzyme-PISA: An Efficient Method for Preparing WellDefined Polymer Nano-Objects under Mild Conditions. Macromol. Rapid Commun. 2018, 39 (9), 1700871. (26) Cunningham, V. J.; Alswieleh, A. M.; Thompson, K. L.; Williams, M.; Leggett, G. J.; Armes, S. P.; Musa, O. M. Poly(Glycerol Monomethacrylate)−Poly(Benzyl Methacrylate) Diblock Copolymer Nanoparticles via RAFT Emulsion Polymerization: Synthesis, Characterization, and Interfacial Activity. Macromolecules 2014, 47 (16), 5613−5623. (27) Hatton, F. L.; Lovett, J. R.; Armes, S. P. Synthesis of WellDefined Epoxy-Functional Spherical Nanoparticles by RAFT Aqueous Emulsion Polymerization. Polym. Chem. 2017, 8 (33), 4856−4868. (28) Canning, S. L.; Cunningham, V. J.; Ratcliffe, L. P. D.; Armes, S. P. Phenyl Acrylate Is a Versatile Monomer for the Synthesis of Acrylic Diblock Copolymer Nano-Objects via Polymerization-Induced SelfAssembly. Polym. Chem. 2017, 8, 4811−4821. (29) Boissé, S.; Rieger, J.; Belal, K.; Di-Cicco, A.; Beaunier, P.; Li, M.-H.; Charleux, B. Amphiphilic Block Copolymer Nano-Fibers via RAFT-Mediated Polymerization in Aqueous Dispersed System. Chem. Commun. 2010, 46 (11), 1950−1952. (30) Zhang, X.; Boissé, S.; Zhang, W.; Beaunier, P.; D’Agosto, F.; Rieger, J.; Charleux, B. Well-Defined Amphiphilic Block Copolymers and Nano-Objects Formed in Situ via RAFT-Mediated Aqueous Emulsion Polymerization. Macromolecules 2011, 44 (11), 4149−4158. (31) Zhang, W.; D’Agosto, F.; Boyron, O.; Rieger, J.; Charleux, B. Toward a Better Understanding of the Parameters That Lead to the Formation of Nonspherical Polystyrene Particles via RAFT-Mediated One-Pot Aqueous Emulsion Polymerization. Macromolecules 2012, 45 (10), 4075−4084. (32) Khor, S. Y.; Truong, N. P.; Quinn, J. F.; Whittaker, M. R.; Davis, T. P. Polymerization-Induced Self-Assembly: The Effect of End Group and Initiator Concentration on Morphology of Nanoparticles Prepared via RAFT Aqueous Emulsion Polymerization. ACS Macro Lett. 2017, 6 (9), 1013−1019. (33) Lesage de la Haye, J.; Zhang, X.; Chaduc, I.; Brunel, F.; Lansalot, M.; D’Agosto, F. The Effect of Hydrophile Topology in RAFT-Mediated Polymerization-Induced Self-Assembly. Angew. Chem., Int. Ed. 2016, 55 (11), 3739−3743. (34) Kessel, S.; Urbani, C. N.; Monteiro, M. J. Mechanically Driven Reorganization of Thermoresponsive Diblock Copolymer Assemblies in Water. Angew. Chem., Int. Ed. 2011, 50 (35), 8082−8085. (35) Truong, N. P.; Quinn, J. F.; Anastasaki, A.; Haddleton, D. M.; Whittaker, M. R.; Davis, T. P. Facile Access to Thermoresponsive Filomicelles with Tuneable Cores. Chem. Commun. 2016, 52 (24), 4497−4500. (36) Jasinski, F.; Zetterlund, P. B.; Braun, A. M.; Chemtob, A. Photopolymerization in Dispersed Systems. Prog. Polym. Sci. 2018, 84, 47−88. (37) Burridge, K. M.; Wright, T. A.; Page, R. C.; Konkolewicz, D. Photochemistry for Well-Defined Polymers in Aqueous Media: From Fundamentals to Polymer Nanoparticles to Bioconjugates. Macromol. Rapid Commun. 2018, 39 (12), 1800093. (38) Tan, J.; Sun, H.; Yu, M.; Sumerlin, B. S.; Zhang, L. Photo-PISA: Shedding Light on Polymerization-Induced Self-Assembly. ACS Macro Lett. 2015, 4 (11), 1249−1253.
(39) Tan, J.; Bai, Y.; Zhang, X.; Zhang, L. Room Temperature Synthesis of Poly(Poly(Ethylene Glycol) Methyl Ether Methacrylate)Based Diblock Copolymer Nano-Objects via Photoinitiated Polymerization-Induced Self-Assembly (Photo-PISA). Polym. Chem. 2016, 7 (13), 2372−2380. (40) Tan, J.; Liu, D.; Bai, Y.; Huang, C.; Li, X.; He, J.; Xu, Q.; Zhang, X.; Zhang, L. An Insight into Aqueous Photoinitiated Polymerization-Induced Self-Assembly (Photo-PISA) for the Preparation of Diblock Copolymer Nano-Objects. Polym. Chem. 2017, 8 (8), 1315−1327. (41) Tan, J.; Liu, D.; Bai, Y.; Huang, C.; Li, X.; He, J.; Xu, Q.; Zhang, L. Enzyme-Assisted Photoinitiated Polymerization-Induced Self-Assembly: An Oxygen-Tolerant Method for Preparing Block Copolymer Nano-Objects in Open Vessels and Multiwell Plates. Macromolecules 2017, 50 (15), 5798−5806. (42) Tan, J.; Liu, D.; Huang, C.; Li, X.; He, J.; Xu, Q.; Zhang, L. Photoinitiated Polymerization-Induced Self-Assembly of Glycidyl Methacrylate for the Synthesis of Epoxy-Functionalized Block Copolymer Nano-Objects. Macromol. Rapid Commun. 2017, 38 (15), 1700195. (43) Tan, J.; Xu, Q.; Zhang, Y.; Huang, C.; Li, X.; He, J.; Zhang, L. Room Temperature Synthesis of Self-Assembled AB/B and ABC/BC Blends by Photoinitiated Polymerization-Induced Self-Assembly (Photo-PISA) in Water. Macromolecules 2018, 51 (18), 7396−7406. (44) Tan, J.; Li, X.; Zeng, R.; Liu, D.; Xu, Q.; He, J.; Zhang, Y.; Dai, X.; Yu, L.; Zeng, Z.; Zhang, L. Expanding the Scope of Polymerization-Induced Self-Assembly: Z-RAFT-Mediated Photoinitiated Dispersion Polymerization. ACS Macro Lett. 2018, 7 (2), 255−262. (45) Yeow, J.; Xu, J.; Boyer, C. Polymerization-Induced SelfAssembly Using Visible Light Mediated Photoinduced Electron Transfer−Reversible Addition−Fragmentation Chain Transfer Polymerization. ACS Macro Lett. 2015, 4 (9), 984−990. (46) Yeow, J.; Chapman, R.; Xu, J.; Boyer, C. Oxygen Tolerant Photopolymerization for Ultralow Volumes. Polym. Chem. 2017, 8 (34), 5012−5022. (47) Xu, S.; Ng, G.; Xu, J.; Kuchel, R. P.; Yeow, J.; Boyer, C. 2(Methylthio)Ethyl Methacrylate: A Versatile Monomer for Stimuli Responsiveness and Polymerization-Induced Self-Assembly in the Presence of Air. ACS Macro Lett. 2017, 6 (11), 1237−1244. (48) Zaquen, N.; Yeow, J.; Junkers, T.; Boyer, C.; Zetterlund, P. B. Visible Light-Mediated Polymerization-Induced Self-Assembly Using Continuous Flow Reactors. Macromolecules 2018, 51 (14), 5165− 5172. (49) Jiang, Y.; Xu, N.; Han, J.; Yu, Q.; Guo, L.; Gao, P.; Lu, X.; Cai, Y. The Direct Synthesis of Interface-Decorated Reactive Block Copolymer Nanoparticles via Polymerisation-Induced Self-Assembly. Polym. Chem. 2015, 6 (27), 4955−4965. (50) Gao, P.; Cao, H.; Ding, Y.; Cai, M.; Cui, Z.; Lu, X.; Cai, Y. Synthesis of Hydrogen-Bonded Pore-Switchable Cylindrical Vesicles via Visible-Light-Mediated RAFT Room-Temperature Aqueous Dispersion Polymerization. ACS Macro Lett. 2016, 5 (12), 1327− 1331. (51) Ding, Y.; Cai, M.; Cui, Z.; Huang, L.; Wang, L.; Lu, X.; Cai, Y. Synthesis of Low-Dimensional Polyion Complex Nanomaterials via Polymerization-Induced Electrostatic Self-Assembly. Angew. Chem., Int. Ed. 2018, 57 (4), 1053−1056. (52) Blackman, L. D.; Doncom, K. E. B.; Gibson, M. I.; O’Reilly, R. K. Comparison of Photo- and Thermally Initiated PolymerizationInduced Self-Assembly: A Lack of End Group Fidelity Drives the Formation of Higher Order Morphologies. Polym. Chem. 2017, 8 (18), 2860−2871. (53) Varlas, S.; Blackman, L. D.; Findlay, H. E.; Reading, E.; Booth, P. J.; Gibson, M. I.; O’Reilly, R. K. Photoinitiated PolymerizationInduced Self-Assembly in the Presence of Surfactants Enables Membrane Protein Incorporation into Vesicles. Macromolecules 2018, 51 (16), 6190−6201. (54) Couturaud, B.; Georgiou, P. G.; Varlas, S.; Jones, J. R.; Arno, M. C.; Foster, J. C.; O’Reilly, R. K. Poly(Pentafluorophenyl Methacrylate)-Based Nano-Objects Developed by Photo-PISA as 211
DOI: 10.1021/acsmacrolett.9b00007 ACS Macro Lett. 2019, 8, 205−212
Letter
ACS Macro Letters Scaffolds for Post-Polymerization Functionalization. Macromol. Rapid Commun. 2019, 40 (2), 1800460. (55) Jung, K.; Boyer, C.; Zetterlund, P. B. RAFT Iniferter Polymerization in Miniemulsion Using Visible Light. Polym. Chem. 2017, 8 (27), 3965−3970. (56) Blanazs, A.; Madsen, J.; Battaglia, G.; Ryan, A. J.; Armes, S. P. Mechanistic Insights for Block Copolymer Morphologies: How Do Worms Form Vesicles? J. Am. Chem. Soc. 2011, 133 (41), 16581− 16587. (57) Blanazs, A.; Ryan, A. J.; Armes, S. P. Predictive Phase Diagrams for RAFT Aqueous Dispersion Polymerization: Effect of Block Copolymer Composition, Molecular Weight, and Copolymer Concentration. Macromolecules 2012, 45 (12), 5099−5107. (58) Tan, J.; He, J.; Li, X.; Xu, Q.; Huang, C.; Liu, D.; Zhang, L. Rapid Synthesis of Well-Defined All-Acrylic Diblock Copolymer Nano-Objects via Alcoholic Photoinitiated Polymerization-Induced Self-Assembly (Photo-PISA). Polym. Chem. 2017, 8 (44), 6853−6864. (59) Zehm, D.; Ratcliffe, L. P. D.; Armes, S. P. Synthesis of Diblock Copolymer Nanoparticles via RAFT Alcoholic Dispersion Polymerization: Effect of Block Copolymer Composition, Molecular Weight, Copolymer Concentration, and Solvent Type on the Final Particle Morphology. Macromolecules 2013, 46 (1), 128−139. (60) Yeow, J.; Chapman, R.; Gormley, A. J.; Boyer, C. Up in the Air: Oxygen Tolerance in Controlled/Living Radical Polymerisation. Chem. Soc. Rev. 2018, 47 (12), 4357−4387. (61) Chapman, R.; Gormley, A. J.; Herpoldt, K.-L.; Stevens, M. M. Highly Controlled Open Vessel RAFT Polymerizations by Enzyme Degassing. Macromolecules 2014, 47 (24), 8541−8547. (62) Chapman, R.; Gormley, A. J.; Stenzel, M. H.; Stevens, M. M. Combinatorial Low-Volume Synthesis of Well-Defined Polymers by Enzyme Degassing. Angew. Chem. 2016, 128 (14), 4576−4579.
212
DOI: 10.1021/acsmacrolett.9b00007 ACS Macro Lett. 2019, 8, 205−212