Preparation and Characterization of Ultrarapidly Dissolving

Oct 25, 2015 - †School of Pharmacy and ‡School of Chemistry, University of East Anglia, Norwich, Norfolk, United Kingdom NR4 7TJ. J. Agric. Food C...
1 downloads 0 Views 1MB Size
Subscriber access provided by UNIV OF LETHBRIDGE

Article

Preparation and Characterisation of Ultra-Rapidly Dissolving Orodispersible Films for Treating and Preventing Iodine Deficiency in the Paediatric Population Cholpon RustemKyzy, Peter Belton, and Sheng Qi J. Agric. Food Chem., Just Accepted Manuscript • DOI: 10.1021/acs.jafc.5b03953 • Publication Date (Web): 25 Oct 2015 Downloaded from http://pubs.acs.org on October 31, 2015

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of Agricultural and Food Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 25

Journal of Agricultural and Food Chemistry

Preparation and Characterisation of Ultra-Rapidly Dissolving Orodispersible Films for Treating and Preventing Iodine Deficiency in the Paediatric Population

Cholpon Rustemkyzy1, Peter Belton2, Sheng Qi1*

1. School of Pharmacy, University of East Anglia, Norwich, Norfolk, UK, NR4 7TJ 2. School of Chemistry, University of East Anglia, Norwich, Norfolk, UK, NR4 7TJ

Correspondence: Sheng Qi, [email protected]

ACS Paragon Plus Environment

1

Journal of Agricultural and Food Chemistry

Page 2 of 25

Abstract: 1

Iodine deficiency is a public health problem that is easily prevented in many countries through

2

having a salt iodization programme. However, the World Health Organisation (WHO) recommends

3

that particular population groups including infants and young children have a higher daily iodine

4

dose than adults, whilst also reducing salt consumption in their diet. Whilst many iodine

5

supplements are available, swallowing tablet supplements is physically difficult for young children,

6

thus there is a need for the development of novel iodine delivery systems for paediatric patients. In

7

this study a novel, ultra-rapidly dissolving, nanofiber based orodispersible film formulation

8

containing iodine which is constructed from nanofibers was manufactured using an electrospinning

9

technique was developed. The potassium iodate (KIO3) loaded poly (ethylene oxide) (PEO) fibre

10

orodispersible films dissolve within seconds on wetting (applying on the tongue) without the need

11

for the consumption of water. The electrospinning process and KIO3 loading did not alter the

12

crystallinity and conformation of PEO. With high loading, KIO3 nanocrystals present in the fibers.

13

This formulation design allows easy administration of iodine for preventing childhood iodine

14

deficiency. It has also described a novel and easy method for producing and harvesting nanocrystals

15

of inorganic salts that can be potentially adopted for use in other relevant fields.

16

Keywords: iodine deficiency, electrospinning, solid dispersions, nanocrystals, ultra-rapidly

17

dissolving orodispersible film

18

Introduction

19

Iodine deficiency is one of the key factors responsible for mental impairment worldwide and is

20

easily preventable by supplementing the population using iodized salt.

1-3

Unfortunately, complete

21

elimination of iodine deficiency in the world has not been achieved.

4, 5

It is still a major health

22

problem in many developing countries and it can easily re-emerge anywhere because of the socio-

23

economic situation and/or circulation of iodine in the nature. This has happened in some iodine

24

sufficient countries.

6-11

In an attempt to address this, WHO and UNICEF urged all countries to ACS Paragon Plus Environment

2

Page 3 of 25

Journal of Agricultural and Food Chemistry

12

25

control and monitor iodine status every three years

26

medicaments/supplements for the most vulnerable groups in the population, such as children (90-

27

150 µg/d depending on the age group), prenatal, pregnant and lactating women (220-250 µg/d) in

28

order to meet their required daily dose. 13 Existing iodine medicaments and supplements are mostly

29

in tablet form, which often cause serious difficulties in swallowing for paediatric and elderly

30

patients. Although liquid iodine supplement formulations are available, there have a number of

31

drawbacks related with their reduced physical storage stability, increased manufacturing cost, and

32

increased contamination risk for multiple dose formulations.

7

33

developing

for

34

medicaments/supplements to meet paediatric population needs. This study reports the development

35

of ultra-rapidly dissolving orodispersible films as an alternative solid form of iodine delivery which

36

can meet this urgent need for tackling paediatric iodine deficiency.

37

The orodispersible films are made of an overlapping iodine loaded nanofiber network which

38

provides an ultra-rapid disintegration and dissolution once wetted. Additional water as is commonly

39

used when taking conventional tablets and capsules and swallowing of bulky solids are not required

40

for the administration of this orodispersible film. The child only needs to put the film on the tongue

41

and the formulation will dissolve rapidly in saliva and the iodine can be largely absorbed by

42

conventional gastrointestinal route. It is anticipated that a small proportion of the saliva-dissolved

43

iodine may also be absorbed via buccal mucosa within the oral cavity which has the advantages of

44

rapid uptake and by-passing the hepatic metabolism.

45

other unfulfilled therapeutic needs such as emergency medications for patients who are unable to

46

swallow conventional tablets and capsules, such as geriatric patients with dysphagia and

47

unconscious patients who are in seizure.

48

The nanofiber based orodispersible films were produced using electrospinning which has recently

49

gained an increased interests in the pharmaceutical, biomedical, food and tissue engineering fields.

50

16-21

countries,

there

is

an

increasing

demand

14, 15

and recommend oral iodine

Therefore and in particular for new

cost-effective

iodine

This delivery concept can also benefit

The main advantages of nanofibers as a delivery system are high surface to volume ratio, ACS Paragon Plus Environment

3

Journal of Agricultural and Food Chemistry

22-24

Page 4 of 25

51

enhanced drug loading capacity and relative cost-effectiveness.

However, characterisation of

52

the nanofibers can be challenging as a result of their sub-micron dimensions, but this

53

characterisation is crucial for understanding and thereby controlling the in vitro and in vivo

54

performance and stability of the formulations. In this study, potassium iodate (KIO3), which is the

55

most stable form of iodine source under stressed conditions, 25 was used as the active ingredient. In

56

order to maximise the stability of KIO3 and to be able to form easy-to-handle films with a uniform

57

distribution of a low dose of KIO3, poly (ethylene oxide) (PEO) was used to form a solid dispersion

58

with KIO3. PEO is easily processed by electrospinning and is water-soluble. 26, 27

59

Despite a rich literature base that have provided insight into solid dispersion based formulations,

60

there is a lack of information regarding using them to deliver inorganic molecules. This study

61

provides a thorough investigation into the behavior of such a system. The results reveal the

62

formation of nanocrystals of KIO3 within the nanofibers at relatively lower loading concentrations

63

than is the case with many organic, low molecular weight drugs. This study has demonstrated two

64

significant outcomes, 1) the development of a prototype form of a novel solid oral paediatric iodine

65

formulation which requires no water and swallowing for administration and 2) a considerable

66

contribution to the improving understanding of solid dispersions containing inorganic molecules

67

and the production of inorganic nanocrystals using a quick, simple and organic solve-free

68

electrospinning method.

69

70

Materials and method:

71

Materials

72

Poly (ethylene oxide) (Average Mw = 6×105 g/mol) and polydispersity below 1.10 28, KIO3 (ACS

73

grade – 99.5 % purity), KI (ACS grade - ≥99 % purity), H2SO4 (ACS grade – 95.0 - 98.0 % purity)

74

were all purchased from Sigma Aldrich (Pool, UK).

75

Electrospinning ACS Paragon Plus Environment

4

Page 5 of 25

Journal of Agricultural and Food Chemistry

76

PEO and KIO3 were dissolved in water in different w/w ratios in order to produce solid fibers

77

containing 0.4 % w/w to 86 % w/w KIO3. Overall, the solid content concentration of the

78

electrospun solution was 5-7 % w/v. The electrospinning processing parameters are as follow:

79

distance between the collector and the tip of the needle was 150 mm, 200 mm, and 250 mm; flow

80

rate was 0.5 ml/h and 0.1 ml/h; applied DC voltage was from 12kV to 25kV, was adjusted

81

accordingly during processing until a stable jet was observed. The electrospun PVP fibers

82

containing KIO3 or NaCl were prepared using 150mm as the distance between the collector and the

83

tip of the needle, 0.5 ml/h flow rate and 30kV DC voltage. PVP and the crystalline salt were

84

dissolved in water with solid salt concentration of 4 % to 14 % w/w. All samples were prepared

85

under room temperature at 50% relative humidity (RH), with the preparation process being repeated

86

at least three times to ensure the reproducibility of the process.

87

Scanning Electron Microscopy (SEM)

88

The morphology of the fibers was visualized using a JSM5900 LV SEM (JEOL Ltd, Japan). The

89

surfaces of the samples were pre-treated with Au/Pd.

90

SEM/Energy-dispersive X-ray spectroscopy (EDS)

91

The EDS (INCA Energy manufactured by Oxford Instruments) combined with the SEM is capable

92

of detecting chemical elements using a “spot mode”

93

Resolution: 131eV (Mn K alpha). Acquisition time: 30 to 60 sec. At least 5-10 spots at different

94

locations for each samples were examined.

95

Transmission Electron Microscopy (TEM)

96

The TEM instrument used was a Philips CM30 operating at 300kV. Samples were electrospun

97

directly onto TEM grids Support Film of holey-carbon on 300 mesh Cu.

98

Wetting, Disintegration and Dissolution testing

29

manually chosen in the scanned area.

ACS Paragon Plus Environment

5

Journal of Agricultural and Food Chemistry

Page 6 of 25

99

The wettability of the films was tested using a moist filter paper method describe previously in

100

literature. 30 In summary, a piece of cellulose filter paper (Sigma-Aldrich, Gillingham, Dorset, UK)

101

was wetted and saturated with distilled water. The filter paper was then placed in a petri dish and a

102

piece of the electrospun film was placed on top of the wetted filter paper. The time taken for the

103

film to transform from dry and opaque colour to invisible (indicating complete wetting) was

104

recorded. The tests were repeated at least three times.

105

The dissolution tests of the fast dissolving oral films were performed simply, because the

106

dissolution process was rapid. Placebo and KIO3 loaded films were dissolved in water in a petri dish

107

and by gentle stirring and the time taken for the film to dissolve was recorded. In order to see the

108

release of KIO3, an iodometric reaction was used. An excess amount of KIO3 and a small drop of

109

methylene blue dye were added to water. 1M H2SO4 was added after placing the fiber film in water

110

to see the immediate release of iodine to confirm fast release of active ingredient from carrier

111

material. Methylene blue dye was used as a colorant indicator to allow the identification of the

112

release of active ingredient. This is because that the fiber films were white colour and became

113

transparent and difficult to see in water. KIO3 is a good oxidising agent which oxidises iodide to

114

iodine in an acidic media and indicates the colour change via the reaction shown below:

115

KIO3 + 5KI + 3H2SO4 = 3I2 + 3K2SO4 + 3H2O

116

Attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR)

117

Infrared absorption peaks were measured with the IFS 66/S FT IR spectrometer Bruker Optics Ltd,

118

Coventy, UK fitted with a Golden Gate® ATR accessory with heated top plate (Orpington, UK)

119

equipped with diamond internal reflection element. The spectral resolution was 2 cm-1 with 64

120

scans taken for each measurement. Triplicate measurements for each sample were performed.

121

Powder X-Ray Diffraction (PXRD)

122

Diffraction peaks were measured with a Thermo-ARL Xtra diffractometer (Therumo scientific, UK)

123

with a step size of 0.01°, 0.5 sec time per step, from 3° - 60° 2θ. The wavelength was 1.54 angstrom ACS Paragon Plus Environment

6

Page 7 of 25

Journal of Agricultural and Food Chemistry

124

and the X-Ray source was Cu Kα1 with a power of 45 kV and current 40mA. Samples were

125

accurately folded and placed onto the sample holder with zero background and incorporated onto a

126

spinner stage.

127

Differential scanning calorimetry (DSC)

128

DSC measurements were conducted on a DSC Q2000 TA (New Castle, USA) instrument, equipped

129

with a RSC 90 cooling unit and which had been calibrated with Indium, Tin and N-Octadacon.

130

Samples weights were between 2-3 mg with a heating rate of 10°C/min over the temperature range

131

0-120°C. Triplicate measurements for each sample were performed.

132

Results and discussion

133

Processing optimisation

134

SEM images were used to characterise the dimensions and surface morphologies of the nanofiber.

135

PEO with molecular weight of 600K yielded smooth placebo nanofibers with a uniform diameter

136

range between 50 nm and 1.2 µm, as seen in Figure 1a and b. Addition of KIO3 up to 21% (w/w) led

137

to slightly reduced fiber diameter, but no change in the fiber morphology (Figure 1c and d). Using

138

the formation of nanofibers films which can be easily peeled off from the collector surface as the

139

key measure, the maximum loading of KIO3 was also studied. The optimal loading range to result

140

an elastic and easy-to-peel fiber film with smooth and uniform fibers was up to 21 % of KIO3

141

loading with a 0.2 ml/h feeding rate. Further increases in KIO3 content to and above 43% led to the

142

formation of beaded (formation of small beads on the fibers) nanofibers and brittle films (Figure 1e

143

and f). Nonetheless, it is possible to load up to 86 % (w/w) KIO3 into the fiber film, but the

144

morphology of the fibers would be beaded. For the fiber films with 13% KIO3 loading, delivering

145

0.5mg and 1.1 mg KIO3 require a piece of film with dimensions of approximately 1x1cm2 and 1x2

146

cm2, respectively, which meet the WHO recommended daily dose of 90 µg/d for children 0-5 years

147

and 200 µg/d for pregnant and lactating women, respectively. This low mass may be difficult to

148

handle, but with reducing the drug loading, the weight of oral film administrated can be easily ACS Paragon Plus Environment

7

Journal of Agricultural and Food Chemistry

Page 8 of 25

149

increased into easily manageable size. An alternative delivery method is to put the film on top of an

150

edible bulky item, such as conventional children’s snacks, which may also improve patient

151

adherence as they are appealing to paediatric population.

152

153

The EDS is able to detect elements with atomic number greater than 5. In combination with SEM, it

154

can be used to gain elemental distribution information. 31-33 As seen in Figure 2, the results revealed

155

that the KIO3 loaded fibre films consists of K, I, O, C and Au. The presence of Au is due to pre-

156

treatment of the SEM sample, C and O are polymer constituents and K, I, O constitutes of KIO3. As

157

the electrospun films were highly porous, the quantitative elemental composition assignment of the

158

EDS results would have limited reliability. Nevertheless, the atomic ratios between C, O, K and I

159

largely align with the molar ratios of these atoms within the formulations examined. The high

160

similarity of K and I peak intensities in different areas of the sample using the “spot mode”

161

indicates the homogeneity of the distribution of KIO3 in the nanofiber films. Overall the above

162

results confirmed that electrospinning is a suitable method for producing easy-to-use oral films for

163

delivery of iodine.

29

164

165

Ultra-rapid wetting, disintegration and dissolution

166

With the intention of providing rapid dissolution of these electrospun films on the tongue after

167

administration, these films should first demonstrate the ability to be wetted rapidly. The wetted

168

filter paper method reported in literature was adopted for simulating the moist surface of tongue. 30

169

As seen in Figure 3, the electrospun film wetted rapidly and transformed from an opaque dry film to

170

being invisible in less than 20 seconds. As indicated by the disappearance of the opaque films, both

171

the placebo and KIO3 loaded films, showed ultra-rapid disintegration and dissolution in the media

172

within less than a minute (Figure 4). The rate of dissolution of the KIO3 loaded films was tested

173

using sulphuric acid as an indicator. As seen in Figure 4, the dark brown colour of the media after ACS Paragon Plus Environment

8

Page 9 of 25

Journal of Agricultural and Food Chemistry

174

adding sulphuric acid indicates the liberation of I2, which appeared immediately after the fast

175

disintegration and dissolution of the nanofiber films. The total dissolution was within less than 30

176

seconds.

177 178

Formation of KIO3 nanocrystals in PEO nanofibers

179

As discussed earlier, the increases in KIO3 loading affected the mechanical properties of the formed

180

fiber films via converting the smooth fibers to beaded fibers as well as reducing the PEO content

181

which is responsible for the elasticity of the film. It was also suspected that the physical form of

182

KIO3 might be altered with increasing the loading. This assumption was made on the basis of the

183

existing literature of polymeric based solid dispersions for delivering organic molecules, in which

184

crystalline drug is expected if the loading is significantly exceeds the solubility limit of the organic

185

drug in the polymer.

186

reduce the mechanical strength of the fibers and result in weak and brittle fiber films. This

187

hypothesis was tested using PXRD. PXRD results confirm crystalline and semi-crystalline nature of

188

KIO3 and PEO, respectively. All of characteristic diffraction peaks match those ones reported in

189

literature.

190

KIO3 was formed with loadings at and above 1.2% w/w. This indicates that an inorganic salt such as

191

KIO3 has low solubility in solid PEO and instead of the formation of a solid solution or amorphous

192

solid dispersion KIO3 is likely to form crystalline solid dispersions with PEO after electrospinning.

36

34, 35

The generation of significant quantities of crystalline KIO3 could also

As seen in Figure 5, it is evident that with increasing the KIO3 loading, crystalline

193

194

However, no crystal or particulate feature were observed using SEM which is an imaging technique

195

that examines the surface of the fibers. Therefore TEM was applied to further investigate KIO3

196

crystal formation in the PEO fibers. As seen in Figure 6, darker, nano-size particles can be clearly

197

seen in the TEM images of the fiber films. These high-density nanoparticles are highly likely to be

198

the KIO3 crystals. It is interesting that these nanocrystals are distributed relatively evenly within the

ACS Paragon Plus Environment

9

Journal of Agricultural and Food Chemistry

Page 10 of 25

199

core of the fibers. This confirms the earlier EDS result, which suggested a uniform distribution of

200

KIO3 through the fibers. There appears to be no surface accumulation of the nanocrystals. This

201

finding is contrast to the surface and bulk crystallisation behaviour of other inorganic salts in

202

electrospun fibers reported in literature.

203

hydrophilic polymeric fibers was also observed in electrospun polyvinylpyrrolidone (PVP), a

204

widely used pharmaceutical hydrophilic and hygroscopic polymer,

205

or KIO3 (Figure 7). This indicates that the phenomenon of inorganic salt crystallisation in the bulk

206

of electrospun fibers is not PEO-KIO3 system specific. Although the mechanism of this

207

crystallisation behaviour is unclear and further investigation is required, it is noted that both PEO

208

and PVP are hydrophilic polymers which exhibit some hygroscopic behaviour. 40 The large surface

209

area and the hygroscopic nature of the polymer fibers may lead to a higher moisture content at the

210

surface layer of the fibers and this may be sufficient to solubilise the surface salts. The interior core

211

of the fibers are likely to be drier than the surface, with the low solubility of the salts in the dry

212

polymer interior driving the crystallisation.

213

With increasing the iodate loading, beading of the fibers can be seen and agglomeration of KIO3

214

nanocrystals at the beading sites is clearly evident (supplementary information). This indicates that

215

there are significantly higher KIO3 local concentrations at the beading sites. It is worth mentioning

216

that as the formation of the nanocrystals occurs at very low loading, it is reasonable to suggest that

217

presence of the nanocrystals per se is not the key factor responsible for the mechanical weakness of

218

the fiber films. The formation of highly concentrated KIO3 nanocrystal beads at higher iodine

219

loadings in combination with a low PEO content is more likely to be the underlying reason of the

220

poor mechanical properties of those fibers with high KIO3 loadings.

37-39

This interior-specific crystallisation behaviour in

40

fibers containing either NaCl

221

222

Effect of processing and KIO3 loading on the crystallisation behaviour of PEO

ACS Paragon Plus Environment

10

Page 11 of 25

Journal of Agricultural and Food Chemistry

223

PEO is a semi-crystalline polymer and the crystallinity of the polymer can be affected by the

224

electrospinning process and the incorporation of KIO3. These could potentially lead to stability

225

concerns in the finished product. Therefore the structural conformation and crystallinity of the

226

processed PEO in the fibers were studied in depth. ATR FT-IR spectroscopy was used in the first

227

instance to reveal the coexistence of helical (H) and trans (T) structure conformations of PEO. As

228

seen in Figure 8, IR peaks at 1358, 1278, 1235, 1060, 947, 842cm-1 have been specified as

229

indicators for the thermodynamically stable helical structure (H) and 1341, 1240, 961cm-1 for the

230

trans planar (T) conformation. Any changes in these peaks would indicate a change in T or H

231

conformation.

232

comparison to the placebo and are independent of KIO3 loading. This implies no significant change

233

in the overall PEO chain conformation occurred after incorporation of KIO3.

41-45

All absorption peaks due to the PEO polymer remained unchanged in

234

235

With 43 % of KIO3 loading, the absorption peak at 745 cm-1 was split into two bands at 756 and

236

738 cm-1. The band splitting at 745 cm-1 may indicate a subtle change of symmetry in the crystal

237

structure.

238

KIO3 crystal symmetry, 48 thus this change was not observed in the PXRD results. Nevertheless for

239

the purpose of this study, such subtle changes in KIO3 nanocrystal are not anticipated to impact the

240

dissolution behaviour of the formulation because of the high solubility of KIO3. The detailed

241

assignments of all detectable FT-IR peaks of the PEO samples can be found in the Supplementary

242

Material.

243

The crystallinity of the PEO after electrospinning and KIO3 incorporation was estimated using

244

DSC. As seen in Figure 9, the DSC results show no significant difference in the melting onset

245

temperature, crystallization onset and offset temperatures and the enthalpies of these transitions of

246

control sample and KIO3 loaded PEO fiber films. This confirms the ATR-FTIR spectroscopic and

247

PXRD results that there was no significant impact on polymer crystallinity after processing and

248

KIO3 loading. However, there are a minimal amount of subtle changes in diffraction peak shape that

46, 47

However, according to literature, PXRD is unable to detect such subtle changes in

ACS Paragon Plus Environment

11

Journal of Agricultural and Food Chemistry

Page 12 of 25

249

can be seen when comparing the PEO powder as the starting material and the placebo PEO

250

electrospun fibers. There subtle changes may be attributed to an orientation effect of the crystalline

251

PEO chains after electrospinning 16, 49, 50.

252

253

This study was conducted with a clear aim of finding an alternative low-cost and easy-to-use oral

254

iodine supplement formulation for the paediatric population who often have swallowing and

255

adherence difficulties. The formulation developed should fulfil the essential criteria of not requiring

256

swallowing large solids and has the potential to be easy and fun for children to take. The solution

257

proposed in this study is to use electrospinning to produce thin orodispersible films which can

258

instantly dissolve on the tongue for easy administration of nutritional supplements to children. The

259

key outcome reported for this proof-of-concept study is that this is achievable with low

260

requirements for operational optimisation and little effect on the structural conformation of PEO.

261

The formation of KIO3 nanocrystals in nearly all loaded fiber films indicates the low miscibility of

262

PEO with KIO3. This provides new insights into the research area of using polymeric based solid

263

dispersions for inorganic material delivery which is still significantly lacking. The fact that KIO3

264

forms nanocrystals in the PEO fibers and the PEO remains in its original stable conformation is

265

likely to ensure the physical stability of the finished product.

266

Conclusion

267

A novel ultra-rapidly dissolving oral film with high design flexibility was developed to deliver

268

iodine for children. These mas were PEO based electrospun fiber films containing nanofibers of

269

PEO loaded with KIO3 nanocrystals and showed good mechanical properties and fast disintegration

270

and dissolution behaviour in vitro. This novel formulation design allows easy administration of

271

iodine for preventing childhood iodine deficiency. Additionally it has also provided a novel and

272

easy method for producing and harvesting nanocrystals of inorganic salts that can be potentially

273

adopted for other relevant fields.

ACS Paragon Plus Environment

12

Page 13 of 25

Journal of Agricultural and Food Chemistry

274

Acknowledgement

275

Cholpon would like to thank the Islamic Development Bank Merit Scholarship Programme for High

276

Technology [grant number 600014339] to financially support her PhD. The authors would like to

277

acknowledge Dr Mark Eddleston, University of Cambridge, for carrying out the some of the TEM

278

experiments on the nanofibers.

279

Reference

280 281 282 283 284 285 286 287 288 289 290 291 292 293 294 295 296 297 298 299 300 301 302 303 304 305 306 307 308 309 310 311 312 313 314 315 316 317 318 319 320 321

1. Yen, P. M., Physiological and molecular basis of thyroid hormone action. Physiol. Rev. 2001, 81, 1097-1142. 2. Bürgi, H., Iodine excess. Best Pract. Res. Cl. En. 2010, 24, 107-115. 3. Hess, S. Y., Iodine: Physiology, Dietary Sources, and Requirements. In Encyclopedia of Human Nutrition (Third Edition), Caballero, B., Ed. Academic Press: Waltham, 2013; pp 33-38. 4. Andersson, M.; Karumbunathan, V.; Zimmermann, M. B., Global iodine status in 2011 and trends over the past decade. J. Nutr. 2012, 142, 744-750. 5. Zimmermann, M. B.; Jooste, P. L.; Pandav, C. S., Iodine-deficiency disorders. Lancet 2008, 372, 1251-1262. 6. Vanderpump, M. P. J.; Lazarus, J. H.; Smyth, P. P.; Laurberg, P.; Holder, R. L.; Boelaert, K.; Franklyn, J. A.; British Thyroid Association, U. K. I. S. G., Iodine status of UK schoolgirls: a cross-sectional survey. Lancet 2011, 377, 2007-2012. 7. Andersson, M.; De Benoist, B.; Darnton-Hill, I.; Delange, F., Iodine deficiency in Europe: a continuing public health problem. World Health Organization Geneva: 2007; p 3-61. 8. Bath, S. C.; Walter, A.; Taylor, A.; Wright, J.; Rayman, M. P., Iodine deficiency in pregnant women living in the South East of the UK: the influence of diet and nutritional supplements on iodine status. Brit. J. Nutr. 2014, 111, 1622-1631. 9. Williamson, C.; Lean, M. E. J.; Combet, E., Dietary recommendations and iodine awareness among mothers in the UK. P. Nutr. Soc. 2012, 71, E141. 10. Lampropoulou, M.; Lean, M. E. J.; Combet, E., Iodine status of women of childbearing age in Scotland. P. Nutr. Soc. 2012, 71, E143. 11. Bouga, M.; Layman, S.; Mullaly, S.; Lean, M. E. J.; Combet, E., Iodine intake and excretion are low in British breastfeeding mothers. P. Nutr. Soc. 2015, 74, E25. 12. WHO Assessment of iodine deficiency disorders and monitoring their elimination: a guide for programme managers; Geneva: World Health Organization: France, 2007; p 1. 13. World Health Organization.; Food and Agriculture Organization of the United Nations., Vitamin and mineral requirements in human nutrition. 2nd ed.; World Health Organization: Geneva, 2005; p 303-314. 14. Hearnden, V.; Sankar, V.; Hull, K.; Juras, D. V.; Greenberg, M.; Kerr, A. R.; Lockhart, P. B.; Patton, L. L.; Porter, S.; Thornhill, M. H., New developments and opportunities in oral mucosal drug delivery for local and systemic disease. Adv. Drug Deliver. Rev. 2012, 64, 16-28. 15. Madhav, N. V. S.; Shakya, A. K.; Shakya, P.; Singh, K., Orotransmucosal drug delivery systems: a review. J. Control. Release 2009, 140, 2-11. 16. Richard-Lacroix, M.; Pellerin, C., Molecular orientation in electrospun fibers: from mats to single fibers. Macromolecules 2013, 46, 9473-9493. 17. Huang, Z.-M.; Zhang, Y. Z.; Kotaki, M.; Ramakrishna, S., A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos. Sci. Technol. 2003, 63, 2223-2253. 18. Garg, K.; Bowlin, G. L., Electrospinning jets and nanofibrous structures. Biomicrofluidics 2011, 5, 013403. 19. Bhardwaj, N.; Kundu, S. C., Electrospinning: a fascinating fiber fabrication technique. Biotechnol. Adv. 2010, 28, 325-347. 20. Teo, W.-E.; Inai, R.; Ramakrishna, S., Technological advances in electrospinning of nanofibers. Sci. Tech. Adv. Mater. 2011, 12, 013002. ACS Paragon Plus Environment

13

Journal of Agricultural and Food Chemistry

322 323 324 325 326 327 328 329 330 331 332 333 334 335 336 337 338 339 340 341 342 343 344 345 346 347 348 349 350 351 352 353 354 355 356 357 358 359 360 361 362 363 364 365 366 367 368 369 370 371 372 373 374 375 376 377

Page 14 of 25

21. Frenot, A.; Chronakis, I. S., Polymer nanofibers assembled by electrospinning. Curr. Opin. Colloid. In. 2003, 8, 64-75. 22. Zamani, M.; Prabhakaran, M. P.; Ramakrishna, S., Advances in drug delivery via electrospun and electrosprayed nanomaterials. Int. J. Nanomedicine 2013, 8, 2997. 23. Bhushani, J. A.; Anandharamakrishnan, C., Electrospinning and electrospraying techniques: Potential food based applications. Trends Food Sci. Techn. 2014, 38, 21-33. 24. Ignatious, F.; Sun, L.; Lee, C.-P.; Baldoni, J., Electrospun nanofibers in oral drug delivery. Pharmaceut. Res. 2010, 27, 576-588. 25. Arroyave, G.; Pineda, O.; Scrimshaw, N. S., The stability of potassium iodate in crude table salt. Bull. World Health Organ. 1956, 14, 183. 26. Son, W. K.; Youk, J. H.; Lee, T. S.; Park, W. H., The effects of solution properties and polyelectrolyte on electrospinning of ultrafine poly (ethylene oxide) fibers. Polymer 2004, 45, 2959-2966. 27. Fong, H.; Chun, I.; Reneker, D. H., Beaded nanofibers formed during electrospinning. Polymer 1999, 40, 4585-4592. 28. Schmitt, A. L.; Mahanthappa, M. K., Polydispersity-driven shift in the lamellar mesophase composition window of PEO-PB-PEO triblock copolymers. Soft Matter 2012, 8, 2294-2303. 29. Kutchko, B. G.; Kim, A. G., Fly ash characterization by SEM–EDS. Fuel 2006, 85, 2537-2544. 30. Yu, D.-G.; Shen, X.-X.; Branford-White, C.; White, K.; Zhu, L.-M.; Bligh, S. W. A., Oral fastdissolving drug delivery membranes prepared from electrospun polyvinylpyrrolidone ultrafine fibers. Nanotechnology 2009, 20, 055104. 31. Piburn, G.; Barron, A. R., An introduction to energy dispersive X-ray spectroscopy. Physical methods in chemistry and nano science. Connexions/Rice University, Houston 2013, 90-98. 32. Wollman, D. A.; Irwin, K. D.; Hilton, G. C.; Dulcie, L. L.; Newbury, D. E.; Martinis, J. M., High‐resolution, energy‐dispersive microcalorimeter spectrometer for X‐ray microanalysis. Journal of Microscopy 1997, 188, 196-223. 33. Chang, H. H.; Cheng, C. L.; Huang, P. J.; Lin, S. Y., Application of scanning electron microscopy and X-ray microanalysis: FE-SEM, ESEM-EDS, and EDS mapping for studying the characteristics of topographical microstructure and elemental mapping of human cardiac calcified deposition. Analytical and bioanalytical chemistry 2014, 406, 359-66. 34. Janssens, S.; Van den Mooter, G., Review: physical chemistry of solid dispersions. J. Pharm. Pharmacol. 2009, 61, 1571-86. 35. Forster, A.; Hempenstall, J.; Tucker, I.; Rades, T., Selection of excipients for melt extrusion with two poorly water-soluble drugs by solubility parameter calculation and thermal analysis. Int. J. Pharm. 2001, 226, 147-61. 36. Yang, S.; Liu, Z.; Liu, Y.; Jiao, Y., Effect of molecular weight on conformational changes of PEO: an infrared spectroscopic analysis. J. Mater. Sci. 2015, 50, 1544-1552. 37. Zhang, C.; Yuan, X.; Wu, L.; Han, Y.; Sheng, J., Study on morphology of electrospun poly (vinyl alcohol) mats. Eur. Polym. J. 2005, 41, 423-432. 38. Barakat, N. A. M.; Kanjwal, M. A.; Sheikh, F. A.; Kim, H. Y., Spider-net within the N6, PVA and PU electrospun nanofiber mats using salt addition: novel strategy in the electrospinning process. Polymer 2009, 50, 4389-4396. 39. Singhal, R.; Kalra, V., Using common salt to impart pseudocapacitive functionalities to carbon nanofibers. Journal of Materials Chemistry A 2015. 40. Rumondor, A. C. F.; Marsac, P. J.; Stanford, L. A.; Taylor, L. S., Phase behavior of poly (vinylpyrrolidone) containing amorphous solid dispersions in the presence of moisture. Mol. Pharm. 2009, 6, 1492-1505. 41. Takahashi, Y.; Tadokoro, H., Structural studies of polyethers,(-(CH2) mO-) n. X. Crystal structure of poly (ethylene oxide). Macromolecules 1973, 6, 672-675. 42. Kim, G.-M.; Wutzler, A.; Radusch, H.-J.; Michler, G. H.; Simon, P.; Sperling, R. A.; Parak, W. J., One-dimensional arrangement of gold nanoparticles by electrospinning. Chem. Mater. 2005, 17, 4949-4957. 43. Gupta, R. K.; Rhee, H.-W., Plasticizing effect of K+ ions and succinonitrile on electrical conductivity of [poly (ethylene oxide)–succinonitrile]/KI–I2 redox-couple solid polymer electrolyte. J. Phys. Chem. B 2013, 117, 7465-7471. 44. Bergeron, C.; Perrier, E.; Potier, A.; Delmas, G., A study of the deformation, Network, and aging of polyethylene oxide films by infrared spectroscopy and calorimetric measurements. Int. J. Spectrosc 2012, 2012.

ACS Paragon Plus Environment

14

Page 15 of 25

378 379 380 381 382 383 384 385 386 387 388 389

Journal of Agricultural and Food Chemistry

45. Yoshihara, T.; Tadokoro, H.; Murahashi, S., Normal Vibrations of the Polymer Molecules of Helical Conformation. Iv. Polyethylene Oxide and Polyethylene‐D4 Oxide. J. Chem. Phys. 1964, 41, 2902-2911. 46. Nakamoto, K., Infrared and Raman spectra of inorganic and coordination compounds. Wiley Online Library: USA, 1986; p 115-121. 47. Dasent, W. E.; Waddington, T. C., 491. Iodine–oxygen compounds. Part I. Infrared spectra and structure of iodates. J. Chem. Soc. 1960, 2429-2432. 48. Lucas, B. W., Structure (neutron) of potassium iodate at 100 and 10 K. Acta Crystallogr. Sect. C: Cryst. Struct. Commun. 1985, 41, 1388-1391. 49. Deitzel, J. M.; Kleinmeyer, J. D.; Hirvonen, J. K.; Tan, N. C. B., Controlled deposition of electrospun poly (ethylene oxide) fibers. Polymer 2001, 42, 8163-8170. 50. Baji, A.; Mai, Y.-W.; Wong, S.-C.; Abtahi, M.; Chen, P., Electrospinning of polymer nanofibers: effects on oriented morphology, structures and tensile properties. Compos. Sci. Technol. 2010, 70, 703-718.

390

391

ACS Paragon Plus Environment

15

Journal of Agricultural and Food Chemistry

Page 16 of 25

392

Figure 1. SEM images of (a) the morphology and (b) diameter size distribution of placebo PEO

393

nanofibers, (c) the morphology and (d) diameter size distribution of PEO nanofibers loaded with

394

21% KIO3, and the beaded morphologies of PEO nanofibers loaded with (e) 43% and (f) 86% KIO3.

395 396

ACS Paragon Plus Environment

16

Page 17 of 25

Journal of Agricultural and Food Chemistry

397

Figure 2. Representative EDS results of PEO nanofibres loaded with 4% (w/w) KIO3 showing the

398

detection of K, O and I elements on the fibers.

399 400

ACS Paragon Plus Environment

17

Journal of Agricultural and Food Chemistry

Page 18 of 25

401

Figure 3. Demonstration of the rapid wetting of a piece of KIO3 loaded PEO nanofiber

402

orodispersible film. The blue area was used to provide the colour contrast to allow the easy

403

observation of the opaque film.

404

ACS Paragon Plus Environment

18

Page 19 of 25

Journal of Agricultural and Food Chemistry

405

Figure 4. Ultra-rapid dissolution of KIO3 loaded PEO nanofiber mats. The complete release of

406

KIO3 is demonstrated by the colour change of the dissolution medium containing the molecular

407

indicator, methylene blue, after adding small amount of H2SO4 solution.

408 409

ACS Paragon Plus Environment

19

Journal of Agricultural and Food Chemistry

410

Page 20 of 25

Figure 5. PXRD diffraction patterns of the starting materials and electrospun nanofibers.

411 412

ACS Paragon Plus Environment

20

Page 21 of 25

Journal of Agricultural and Food Chemistry

413

Figure 6. Representitive TEM image of PEO nanofibers loaded with 43% KIO3. KIO3 nanocrystals

414

can be seen as black dots in the fibers.

415 416

ACS Paragon Plus Environment

21

Journal of Agricultural and Food Chemistry

Page 22 of 25

417

Figure 7. Representitive TEM image of PVP nanofibers loaded with (a) 4% NaCl and (b) 14%

418

KIO3. Nanocrystals of NaCl and KIO3 (examples highlighted by arrows in the images) can be

419

osberved in the core of the fibers with the surfaces of the fibers being largely crystal-free.

420 421

ACS Paragon Plus Environment

22

Page 23 of 25

Journal of Agricultural and Food Chemistry

422

Figure 8. ATR-FTIR spectra of (a) pure PEO powder; (b) electrospun placebo PEO nanofibers and

423

PEO nanofibers loaded with (c) 4%, (d) 21% and 43% KIO3. The arrows indicate the position of

424

KIO3 signature absorbance peak.

425 426

ACS Paragon Plus Environment

23

Journal of Agricultural and Food Chemistry

Page 24 of 25

427

Figure 9. DSC thermographs of electrospun placebo PEO fibres and KIO3 loaded (4 and 13% w/w)

428

PEO fibres.

429 430

ACS Paragon Plus Environment

24

Page 25 of 25

431

Journal of Agricultural and Food Chemistry

TOC Graphic

432

ACS Paragon Plus Environment

25