Chapter 1

Solid-State NMR Spectroscopy of Inorganic Materials: An Overview 1

2,3

John J. Fitzgerald and Susan M. DePaul 1

Department of Chemistry and Biochemistry, South Dakota State University, Brookings, SD 57007 Materials Sciences Division, E. O. Lawrence Berkeley National Laboratory and Department of Chemistry, University of California, Berkeley, CA 94720

Downloaded by 87.242.144.86 on May 21, 2014 | http://pubs.acs.org Publication Date: March 18, 1999 | doi: 10.1021/bk-1999-0717.ch001

2

Advances in solid-state nuclear magnetic resonance (NMR) investigations of a diverse range of important inorganic materials are reviewed. Fundamental and new solid-state NMR methods including magic-angle spinning, cross-polarization, multiple-quantum and various two-dimensional techniques that are applicable to both spin-1/2 and quadrupolar nuclides are discussed. An overview of the successful applications of these solid-state NMR methods to obtain new information about the salient chemical, structural and dynamical features of several important classes of inorganic materials is given. Key literature pertaining to selected solid-state NMR studies of refractory metal oxides, catalysts, zeolites and layered materials, ceramics and glasses, biomaterials, semiconductors, ion conductors, superconductors and inorganic composites is discussed. Various chemical issues that have been addressed by these investigations suggest that in the future solid-state NMR will play an important role in expanding our detailed atomic-level understanding of the chemical behavior of these and other advanced inorganic materials. Solid-State NMR of Inorganic Materials During the pastfivedecades, nuclear magnetic resonance (NMR) spectroscopy has been one of the most important spectroscopic approaches for obtaining physical and chemical information about a diverse range of complex chemical systems (1-7). The last two decades, in particular, have experienced significant advances in the study of the atomic-level structure and dynamics of both organic and inorganic materials using solid-state nuclear magnetic resonance spectroscopy (8-13). In the case of inorganic materials, such studies have often provided crucial insight into the chemistry of complicated systems. The complexity of inorganic materials has its origins in their 3

Current address: Max-Planck-Institut fur Polymerforschung, Postfach 3148, D-55021 Mainz, Germany.

2

©1998 American Chemical Society In Solid-State NMR Spectroscopy of Inorganic Materials; Fitzgerald, J.; ACS Symposium Series; American Chemical Society: Washington, DC, 1999.


3 diverse three-dimensional structures and in the presence in many cases of multiple solid phases, interfaces, surface sites or impurities. Advanced inorganic materials exhibit a wide range of functional dynamics and structural features that underlie properties such as catalytic activity, electronic and ionic conductivity, superconductivity and dielectric behavior. Applications of modern inorganic materials includes uses such as specialized industrial catalysts, molecular sieves and adsorbents, high-temperature structural ceramics, electrooptic and laser materials, electronic ceramics, semiconductors, specialized glasses and amorphous fibers, cements, and, most notably, high-temperature superconductors. The emerging demands for inorganic composite materials and multilayered electronic devices requires a new atomic-level understanding of interfacial interactions at organic-inorganic and inorganic-inorganic interfaces. Other interesting inorganic materials, such as those arising from biomineralization, have also stimulated study of processes at the atomic-level by solid-state NMR. In geochemistry and mineralogy, important geological problems involving the high-temperature structural chemistry of mineral phases, mineral surface adsorption and ion exchange reactions in natural geochemical processes, and the migration and deposition chemistry of inorganic ion (e.g., Pb , Cd ) and organic (e.g., pesticides) pollutants are presently the subject of intense solid-state NMR study. Recent advances in the development and understanding of inorganic materials have occurred in parallel with major advances in solid-state NMR methods and approaches. Increased resolution in NMR spectra of solids has resulted from the use of line-narrowing techniques such as magic-angle spinning (MAS) NMR for most NMR-active spin-1/2 nuclei in the Periodic Table. In addition, methods such as DOuble Rotation (DOR) and Dynamic Angle Spinning (DAS) have allowed highresolution spectra of many quadrupolar (spin / > 1/2) nuclides to be obtained. The use of DOR and DAS for improved NMR spectral resolution of quadrupolar broadened signals has recently been augmented by major developments in multiplequantum MAS (MQMAS) NMR to obtain detailed descriptions of atomic sites in a variety of inorganic materials. Research investigations of inorganic solids have also benefited from the selectivity and signal enhancement characteristics of cross-polarization MAS (CP/MAS), which in the last decade led to major advances in understanding organic polymers and biomass materials. Multidimensional NMR techniques (e.g., isotropic/anisotropic correlations, heteronuclear shift correlations, COSY and INADEQUATE experiments) are being used to extract new information about local metal and oxygen atom environments in metal oxides and zeolites. Recent solid-state NMR experiments such as REDOR, TEDOR, SEDOR, TRAPDOR and REAPDOR reveal internuclear distances, while two-dimensional exchange experiments provide insight into molecular mobility. This introductory chapter will review the major classes of inorganic materials and their NMR nuclide compositions, including the most significant spin-1/2 and quadrupolar nuclides currently being used to study solid inorganic materials. The important interactions in solid-state NMR will then be discussed, followed by a review of NMR approaches that can be used to provide detailed, site-specific structural and dynamical information about inorganic materials. Finally, this chapter will give an overview of important past and current solid-state NMR studies of various classes of inorganic materials, focusing on the types of information obtainable and using selected 2+

2+

In Solid-State NMR Spectroscopy of Inorganic Materials; Fitzgerald, J.; ACS Symposium Series; American Chemical Society: Washington, DC, 1999.

4 examples from the literature. These NMR investigations have provided a major impetus for the organization of the recent ACS symposium on "Solid-State NMR Spectroscopy of Inorganic Materials".


I. COMPOSITION O F INORGANIC MATERIALS Inorganic materials exhibit a enormously diverse range of functional properties due to their complex catalytic, adsorptive, ion exchange, magnetic, electronic, optical, thermal, photochemical, and structural behavior. Several categories of inorganic materials are summarized in Table I. The use of solid-state NMR spectroscopy to examine the structural nature, reactivity and physico-chemical properties of these materials is based on the ability of NMR to obtain nuclide-specific information about these solids. The most important criterion is the presence of a nucleus that possesses a non-zero nuclear magnetic moment since only such nuclei are observable by NMR spectroscopy. Because nearly all of the stable elements of the Periodic Table have at least one isotope with a non-zero magnetic moment, NMR can be used to study a wide variety of inorganic substances. In particular, diamagnetic materials containing the nuclides such as Ή, B , C, N, F, Na, A1, Si and P (Tables Π and ΙΠ) have been extensively studied in systems such as silicon and aluminum oxides; silicon carbides and nitrides; zeolites; alkali silicate, borosilicate and fluoride-containing glasses; and aluminum phosphates. Recent interest in the study of metal oxide catalysts, geomaterials, ceramics, electronic materials, semiconductors and superconductors has motivated solid-state NMR studies of both low abundance nuclides ( 0, Mg, - Ti and Mo) and high abundance nuclides ( V, Ga and Nb) with more complex NMR characteristics. For the low-abundant nuclei, isotopiclabelling approaches are increasingly being used both for signal enhancement and for site selectivity. The solid-state NMR spectra of many of these less-studied nuclides, however, can be extremely complex due to their NMR relaxation processes, to chemical shift anisotropy and quadrupolar effects, and to the possible presence of paramagnetic oxidation states in many materials that contain these nuclides. Although only elements in diamagnetic states are typically studied by NMR, the presence of paramagnetic species (e.g., due to free radicals, oxygen defect sites, or intermediate or minor species containing paramagnetic metal ions) in copper, vanadium and molybdenum systems has provided significant solid-state NMR challenges. Systems where these situations occur include metal oxide catalysts, high-T copper oxide superconductors, complex perovskite-type ion conductors, and high-temperature ceramics. In many systems, however, paramagnetic effects are negligible, and the NMR spectra are dominated by the interactions of a given nucleus with its neighboring nuclei and electrons. The following section describes a few of these interactions, the information they provide, and how they are manifested in solid-state NMR spectra. n

17

25

47

49

13

15

95

!9

23

27

29

31

51

69

93

c

II. NMR INTERACTIONS IN INORGANIC SOLIDS A. Spin-1/2 Nuclei. Nuclei with a spin quantum number, /, equal to 1/2 have been extensively studied by NMR spectroscopy. Some of the most widely examined spin-1/2 nuclides in inorganic In Solid-State NMR Spectroscopy of Inorganic Materials; Fitzgerald, J.; ACS Symposium Series; American Chemical Society: Washington, DC, 1999.

5 Several major categories of inorganic materials

Table

Metal Oxides (Catalysts/Supports/Reagents) Si0 , Si0 nH 0 Al 0 nH 0 Na^-SiOj (Sodium Silicates) Na20Al 0 (Sodium Aluminates) Si0 /Al 0 (Sihca/Alumina) Ti0 , ZrO, (Titania, Zirconia) V 0 , Nb 0 Mo0 2

2

2

3

2

2

2

2

3

2

3

2

2

5

2

3

5;


Open Framework and Layered Materials Zeolites (Si/Al-Containing) A1PO (Zeolitic Al/P-Containing) SAPO (Zeolitic Si/Al/P-Containing) Si/Al Minerals (Kaolin, Pyrophyllite, Montmorillonite) Ti/Si Layered Materials Zr(HP0 ) , ZrHP0 nH 0 4

2

4

Glasses

2

Cements/Adhesives

Si0 Al 0 Si0 Si0 B 0 ~ (Na )(K 0)-2SiOo L i O A l 0 Si0

CaOAl 0 *Si0 (Portland Cements) A1P0 (Aluminophosphates) Ca (P0 ) nH 0

2

2

3

2

2

2

2

3

2

3

2

4

3

4

2

2

2

2

2

3

2

Structural Ceramics TiB , ZrB SiC, TiC, ZrC BN, Si N , TiN 2

Zr0 , Zr0 /Al 0 SiAlON BaSiAlON

2

3

2

4

2

2

3

Electronic/Magnetic Materials BaTi0 PbTi0 PZT PLZT

3 3

Fe 0 CoFe 0 LiFe0 LaMn0 YMnO,

PMN PZN PMN/PT TiO,

2

3

2

4

2

3

Ion Conductors

Semiconductors

Superconductors

LaCr0 MgCr 0 BaÔ, β-Α1 0

AIN, GaN A1P, GaP, InP Ga.Al.P GaAs

Bi Sr CaCu 0 YBa2Cu 0 . Tl Ba2CaCu 0 La Sr Cu0 .

3

2

2

3

4

2

2

2

3

2

8+x

7 x

2

L85

015

8+x

4

x


6

Table il.


Nucleus

% Abundance

Properties of selected spin-1/2 nuclei.

Frequency Examples of Receptivity (Relative to Ή) (MHz) Inorganic Materials at 11.7 Τ

Ή

99.985

1.000

"C

1.10

1.76 χ 10"

,5

0.37

F

Si

500.0

Hydrates, Sol-gel Intermediates

4

125.7

Metal Carbides Chelated Metal Oxides

3.85 χ 10'

6

50.7

Nitride Ceramics

100

0.834

470.4

Fluoridated Hydroxyapatites

4.70

3.69 χ 10"

99.3

Glasses, Zeolites Silicon Nitride Silicon Carbide

100

0.0665

202.4

Glasses, Catalysts Semiconductors

7.6

5.30 χ 10'

4

95.3

Semiconductors

100

1.19 χ 10'

4

24.5

Laser Materials, Ceramics Superconductors

12.26

1.35 χ 10°

110.9

Semiconductors Photovoltaic Oxides

" Sn

8.58

4.51 χ 10

186.4

Oxides, Ion Conductors Photovoltaics

,25

6.99

2.24 χ 10"

3

158.0

Semiconductors

33.8

3.39 χ 10"

3

107.5

Catalysts

22.60

2.10 χ 10"

3

104.6

Oxides, Sulfides Electronic Materials

N

19

29

3lp

77

Se

89γ

3

" Cd 9

Te

195

Pt

207p

b

4

3

3

Receptivity equals I γ 1 · (% abundance) · 1(1+1)


7

Table III.

ncleus

Spin

2

H Li Li B "B N 0 Na Mg A1

6

7


10

14

,7

23

25

27

47

49

Ti Ti

51

v

63

Cu Cu Ga Ga As Rb Rb Zr Nb Mo In " In Cs Ba

65

69

71

75

85

87

91

93

95

,l3

5

l33

137

Properties of selected quadrupolar nuclei.

% Abundance

1 1 3/2 3 3/2 1 5/2 3/2 5/2 5/2 3/2 5/2 7/2 7/2 3/2 3/2 3/2 3/2 3/2 5/2 3/2 5/2 9/2 5/2 9/2 9/2 7/2 3/2

0.015 7.42 92.58 19.58 80.42 99.63 0.037 100 10.1 100 93.1 7.3 5.5 99.76 69.09 30.91 60.4 39.6 100 72.14 27.85 11.2 100 15.7 4.28 95.72 100 11.3

Receptivity (Relative to Ή)

-6

1.45 χ ΙΟ 6.31 χ 10 0.272 3.89 χ 10" 0.133 1.00 χ 10 1.08 χ 10" 1.3 χ ΙΟ" 2.72 χ 10" 0.207 4.75 χ 10 1.53 χ ΙΟ 2.08 χ 10 0.383 6.45 χ 10" 3.54 χ ΙΟ" 4.19 χ 10 60.4 0.11 2.3 χ 10 4.92 χ 10 1.06 χ 10" 0.487 5.14 χ 10 1.48 χ ΙΟ" 0.337 4.82 χ 10" 7.89 χ 10 4

3

3

5

2

4

4

-4

4

2

2

2

2

2

3

4

2

2

4

Frequency (MHz) at 11.7 Τ 76.8 72.6 194.3 53.7 160.4 36.1 67.8 132.3 30.6 130.3 23.3 28.2 28.2 131.4 137.6 142.0 120.2 152.5 85.9 48.4 164.1 46.7 122.2 32.6 109.3 109.6 65.6 55.6

3

Receptivity equals | γ | · (% abundance) · 1(1+1)


8 materials are listed in Table Π together with some of their relevant parameters, including natural abundances, receptivities (relative to H), Larmor frequencies at 11.7 Τ (corresponding to 500 MHz for H), and examples of important inorganic systems containing these nuclides. The most important interactions for spin-1/2 nuclei in solids include the Zeeman interaction, the chemical shift interaction, and the dipolar interaction. L Zeeman Interaction. By the laws of angular momentum, a nucleus with spin-quantum number 7 has 27+1 states. These states are labeled by the quantum number m where m has one of the following values: {-7, -7+1, ... 7-1, 7}. Thus, a spin- 1/2 nucleus is a two-level system with states m = +1/2 and m = -1/2. In the presence of an externally applied magnetic field, these states become non-degenerate due to the Zeeman interaction, and the application of electromagnetic radiation (in the form of radio waves) of the appropriate frequency can induce transitions between them. The splitting between successive levels is given by the Larmor frequency ω = yB where γ is the gyromagnetic ratio, which is nuclide dependent (cf. the fourth column of Table Π), and B is the strength of the applied magnetic field. Note the wide variation in the Larmor frequencies of different nuclides (see Tables Π and ΙΠ). Since pulsed NMR techniques typically excite spectral ranges on the order of tens to hundreds of kilohertz, signals due to a single isotope can (in most cases) be selectively observed, making NMR a powerful technique for obtaining site-specific information. For spin-1/2 nuclei and magnetic field strengths of several Tesla (typical for NMR spectrometers), the Zeeman interaction dominates the NMR Hamiltonian, and all other interactions can be considered as small perturbations relative to it. 2. Chemical-Shift Interaction. The chemical shift (δ) reflects the magnetic shielding of a nucleus by neighboring electron clouds and is the most commonly used NMR parameter. Like the Zeeman interaction, the chemical shift is proportional to the strength of the applied magnetic field. Both diamagnetic and paramagnetic effects contribute to the chemical shift, which is an orientation-dependent (tensor) quantity. In solution-state NMR spectroscopy, rapid molecular tumbling averages out this orientation-dependence and produces a narrow line at a position known as the isotropic chemical shift (δ^), which reflects the average electronic environment of the nucleus. In spectra of powdered solid samples, however, all orientations of a given site with respect to the B field are present. When the local symmetry is less than cubic, most of these orientations have slightly different resonance frequencies. This leads to a broad lineshape known as a "powder pattern" (cf. Figures 1A and IB) from which the eigenvalues of the chemical-shielding tensor in its diagonal representation (σ ,σ ,σ ) can be extracted. The eigenvalues are referred to as the principal values of the chemical-shielding anisotropy (CSA), and they can often be correlated with site symmetry, chemical bonding and next-nearest neighbor effects. An equivalent set of linear combinations of these parameters is also frequently used and consists of the previously mentioned isotopic chemical shift (δ^), the anisotropy parameter (Δδ), and an asymmetry parameter (rj ). !


!

0

0

0

Q

π

22

33

cs

3. Direct Magnetic Dipolar Interaction.

Another important interaction in

solid-state NMR is the through-space interaction between the magnetic moments of two nuclei. The strength of this interaction is directly proportional to the product of the gyromagnetic ratios of each nucleus and inversely proportional to the cube of the



9

-3000-2000-1000

0

1000 2000 3000

Frequency [Hz]

-3000-2000-1000

0

1000 2000 3000

Frequency [Hz] Figure 1.

Simulated static powder patterns due to various NMR interactions for a spin1/2 nucleus. (A) Axially symmetric chemical-shielding powder pattern. (B) Asymmetric chemical-shielding powder pattern. (C) Dipolar Pake pattern for an isolated spin pair. Note that the principle values of CSA ( σ ^ , σ ^ ^ ) correspond to the "singularities" in the powder spectra while the separation between the horns in the dipolar powder pattern is related to the internuclear distance.


10

distance between them. As in the case of the chemical shift interaction, the direct dipolar interaction is anisotropic; it depends on the orientation of the internuclear vector with respect to the static B field. Thus, for a powder sample, a broad lineshape will be generated. However, this pattern can contain singularities which allow the average internuclear distance to be directly determined. Figure 1C shows a powder (Pake) pattern for an isolated pair of spins. In this idealized case, the chemical shielding anisotropy is negligible, and since the separation between the peaks in Hz is given by (jiJA^y^^x^Îln) for a pair of unlike spins, the internuclear distance can be extracted directly from the peak separation. In larger spin systems, the spectra become more complicated and the distance information correspondingly harder to extract. 4. Other Interactions, A few other interactions can also potentially affect the solid-state NMR spectra of spin-1/2 nuclei. In addition to the direct dipolar interaction mentioned above, there is also an indirect dipolar-coupling mechanism which involves bonding electrons. This through-bond interaction, also known as the scalar interaction, is characterized by a coupling constant J . It is an important interaction in solution-state spectroscopy where motional averaging removes the effects of the direct dipolar interaction on the positions of the resonances. In solids the J-coupling is often neglected since it is typically much smaller than the direct dipolar coupling, but it can be significant in highly crystalline samples. Another interaction which can influence the spectra of spin-1/2 nuclei is the hyperfme coupling between nuclear magnetic moments and the magnetic moments of conduction electrons in a metal. This produces a shift of the NMR resonance frequency which is known as the Knight shift. Although the Knight shift has the same functional form as the chemical shift, it arises from a different physical mechanism, and the two effects can be distinguished using a combination of experiment and theory. Measurements of the temperature-dependence of the Knight shift have been used to test theories of high-T superconductivity (14). While the above interactions contain a wealth of structural and dynamical information, the presence of more than one of them in a sample (as is generally the case) can lead to spectra too complex to interpret. Fortunately, a wide range of NMR experiments (see Section III) have been developed to selectively enhance or suppress given interactions and thus permit the extraction of chemically relevant information.


Q

c

B. Quadrupolar Nuclei. Nuclei with a spin-quantum number J greater than 1/2 are known as quadrupolar nuclei. Over two-thirds of the NMR-active nuclei in the Periodic Table are quadrupolar nuclei (15,16), but many of them have not yet been widely utilized. Several quadrupolar nuclides used for studies of inorganic materials are listed in Table III, together with relevant NMR parameters, including nuclear spin (/), natural abundance, Larmor frequencies at 11.7 Tesla and receptivities relative to *H. In this overview, we will focus on quadrupolar nuclei with odd half-integer spin quantum numbers (J = 3/2, 5/2, 7/2 . . . etc.) since they are abundant in inorganic materials and have been the focus of much technique development during the past decade. As in the case of spin-1/2 nuclei, the levels of a quadrupolar nucleus undergo



11

Zeeman splitting when placed in a large external magnetic field (see Figure 2A), and the presence of the chemical shift, direct dipolar coupling, scalar coupling, or Knight shift interaction will further perturb them. Since there are now more than two energy levels, multiple transitions (and hence multiple resonances for a single nucleus) are possible (see Figures 2A and 2B). A nucleus with I > 111 also has a non-spherically symmetric charge distribution and hence a non-zero nuclear electric quadrupole moment, eQ. Such a moment will interact with an electric field gradient (EFG) present in the sample due to an asymmetric distribution of electrons around the nucleus. This interaction is known as the quadrupolar interaction; like the chemical shift and direct dipolar interactions, it is anisotropic (orientation-dependent) and leads to powder patterns in polycrystalline samples. The widths and shapes of these powder patterns are strongly influenced by two parameters, respectively: (1) the quadrupolar coupling constant, C = e qQ/h, which is proportional to the product of the nuclear electric quadrupole moment, eQ, and the magnitude of the electric field gradient along its principal axis, eq [note that there are alternative definitions of the quadrupolar coupling constant in the literature which involve scaling factors that are functions of the spin-quantum number /]; and (2) the asymmetry parameter, r| , which reflects the deviation of the electric field gradient from cylindrical symmetry. The quadrupolar coupling constant can have a wide range of values. When C is very small relative to the Zeeman splitting, the quadrupolar interaction can be treated by first-order perturbation theory. Figure 2B shows an example of a static powder pattern for a spin-5/2 nucleus subject to the first-order quadrupolar interaction. This pattern is a superposition of the powder patterns for the five allowed transitions. The narrowest peak in the center of the spectrum corresponds to the central transition (m = +1/2 ο m = -1/2) which is unaffected by the quadrupolar interaction to first order, while the wings on the side correspond to anisotropic powder patterns for the four satellite transitions (m = +5/2 ο m = +3/2), {m = +3/2 ο m = +1/2), (m = -1/2

HOSi(OSi) -99.8 ppm 3

v

χ

^/Si(OSi) -109.3 ppm


4

1

1

1

~~i—«— —·—·—ι— — —»—»—ι—«— -100

-50

- 1 5 0 PPM

(B)

5

10

15

20

25

30

35

CONTACT TIME, MS Figure 8.

29

CP/MAS Si NMR spectrum (A) of a silica gel (hydrated silica) showing three different types of surface and internal silicon sites, including Q-type geminal silanols, Q-type single silanols and Q-type siloxane sites; and (B) plot of Si signal intensity versus contact time (msec) for the three different silicon sites (41). The solid-lines represent fits of the cross-polarization dynamics (7), parameterized by H and S i rotating-frame relaxation times (T ) and the rate of cross-polarization (T ). From these fits, T equalled 20.3, 22.1 and 21 msec, and T , equalled 2.3, 2.9 and 12.7 msec, for the Si peaks at -90.6, -99.8 and -109.3, respectively. 2

3

4

29

1

1p

29

HSj

HS

29


1 p

26 requires approximate knowledge of the J-couplings, which are often difficult to measure in solids. Since the scalar coupling interaction is a through-bond interaction, sequences incorporating INEPT-type transfer will yield information about connectivities rather than distances. B. Special Techniques for High-Resolution of Quadrupolar Nuclei. As Figure 3B shows, magic-angle spinning alone does not fully eliminate the quadrupolar anisotropy which can make resolution of multiple sites in the spectrum of a quadrupolar nucleus difficult. Fortunately, several techniques have been developed to produce high-resolution spectra of odd half-integer quadrupolar nuclei Downloaded by 87.242.144.86 on May 21, 2014 | http://pubs.acs.org Publication Date: March 18, 1999 | doi: 10.1021/bk-1999-0717.ch001

(66-76).

The (+w -m) transitions of a quadrupolar nucleus can be shown to be unaffected to first order by the quadrupolar Hamiltonian (see Figure 2A). When second-order perturbation theory is applied, however, the frequencies of these transitions are affected in an orientation-dependent manner. For a sample spun at an angle θ with respect to the static field, the (+w 1800°C) reactions of silicon nitride, silica, alumina and aluminum nitride under reducing conditions or by pyrolysis of polymeric precursors at 600-800°C . Solid-state MAS NMR is of significant utility in studies of the formation, structure and surface chemistry of SiC- and Si N -based ceramics. Numerous Si and/or C MAS NMR studies have been reported for Si N and SiC (318,320342,344-353). The Si and C MAS NMR of various SiC ceramics as shown in Figure 35 provide examples of the utility of solid-state NMR to define the number and type of both carbon and silicon lattice sites in SiC polymorphs and polytypes. The Si and C MAS NMR spectra shown in Figure 35A and 35B for three different silicon carbide polytypes exhibit different resonances due to stereochemically different silicon and carbon sites designated as Type A, Β and C (320). The Si and C MAS NMR chemical shifts for the A, Β and C sites found in the important silicon carbide polytypes 6H, 3C and 15R, where Η = hexagonal, C = cubic and R = rhombohedral lattices, are summarized in Figure 35C. (320). A fundamental limitation of Si NMR is the long relaxation times (e.g., 129 seconds for the β-SiC resonance, 307, 313 and 362 seconds for the three resonances from α-SiC), necessitating very long delay times between successive scans to avoid signal saturation (318,320-322). The utility of solid-state NMR to characterize bulk silicon nitride materials has also been extensively examined. Silicon nitride exhibits a Si MAS NMR spectrum consisting of two distinct Si NMR resonances assigned to oc-Si N and fi-Si N (331334,351). Si MAS NMR spectra of Si N /Si 0 N mixtures and various commercial silicon nitrides show distinct resonances for the silicon site environments in both the a- and β-polymorphs of silicon nitride, in silicon oxynitride, and in unreacted elemental silicon (331). Analytical Si NMR approaches to identify and quantify the three types of Si N (crystalline α-, β- and amorphous phases), have been reported; however very large relaxation times necessitate NMR pulse delay times of 500 seconds for the pure phase materials (289). Nevertheless, Si MAS NMR studies of SiC and Si N indicate that NMR often provides structural details unobtainable by XRD and other techniques. In addition to Si MAS NMR studies of Si N powders, whiskers and thin films, N MAS NMR studies can provide further information when isotopicallyenriched N-Si N ceramics are used (263,338). In N NMR investigations of the oxidation of silicon nitride, differences in the local nitride environments, e.g., nitride (69-52 ppm) versus oxynitride (40 ppm), could be observed (263). The use of both N and 0 MAS NMR for isotopically-labelled silicon nitride materials, including SiAlONs and other oxynitrides, has been reviewed (338). Recently, Si MAS NMR has also been used to identify and quantify Si-O, Si-N and Si-C groups in both amorphous (e.g., Nicalon fibers) and crystalline materials derived from polymeric organosilicon precursors (323-327,345). Fourcoordinate silicon moieties ranging in stoichiometry from SiC to Si0 , including the intermediate structural units C SiO, C Si0 , and CSi0 , have been distinguished and assigned based on chemical shift relationships of organosilicons (Table IX), together with related chemical shift correlations for different oxynitride and carbonitride 29

3

4

13

3

29


29

4

13

13

29

13

29

29

29

3

4

3

29

3

4

2

2

29

3

4

29

3

4

29

3

4

, 5

15

15

3

15

4

17

29

4

3

2

2

4

3


4


(A)

29 i

Tô

c

Na

2

OKNa | 3

ONa

Figure 40.

4

17

One-dimensional isotropic 0 DAS spectra at 9.4 Τ of various mixed alkali (Na.K) silicate glasses, showing nearly complete resolution of bridging oxygens (BO) from 11.8 to 16.3 ppm, and non-bridging oxygens (NBO) from 27.0 to 68.7 ppm for the high K-content glasses. Deconvolution corresponding to a binomial distribution of four-coordinate oxygens with different nearest neighbor sodium and potassium ions is also depicted (288).


101 phosphates, aluminosilicates, and alkali and alkaline earth aluminosilicates using ID and 2D NMR techniques are likely. Other refractory glasses (256) that have been studied by 0, Na, Si and Zr MAS NMR, such as sodium zirconium silicates, could benefit from MQMAS and other two-dimensional NMR approaches. More elaborate 2D NMR studies of amorphous Si0 materials are also needed to discriminate between crystalline and noncrystalline silica domain regions in semiconductor materials (370). In addition to the many structural issues associated with both short-range and intermediate-range order, 2D NMR methods may increase our understanding of "sol-gel" phases used to prepare precursors of many technologically important, specialized glassy materials (126,128) and the complex physical-chemical processes important in the quenching and vitrefication of glass preparations (264-268). e) Cements and Adhesives. Cements and adhesives represent a fruitful area for the application of solid-state NMR studies since these materials are normally prepared as pastes, and require various setting and dehydration processing steps (289). CaOAl 0 Si0 cements, including low-iron content Portland and high alumina content cements, represent some of the oldest known commodity inorganic materials where detailed chemical knowledge about the hydration and setting reactions and related structures is severely lacking. The use of H, A1 and Si MAS NMR to examine these systems has led to significant progress (169,185-188,289,360,361). In particular, Ή MAS NMR, *H CRAMPS and Si MAS and CP/MAS NMR have been successfully used to study various hydrated calcium silicate crystalline phases formed during the setting and dehydration of calcium silicate cements. Recently, both 0 and Si MAS NMR approaches have been used to examine the curing of several hydrated calcium silicate phases over a range of cement compositions (360,361). 0 MAS NMR spectra of calcium silicate hydrates formed from calcium silicates with different Ca/Si ratios have provided structural information about six different 0 resonances in these materials. The relative amounts of the Ca- 0-H (NBO), Si- 0-H (NBO), Si- 0-Si (BO), two Si- 0-Ca (NBO) moieties (the latter having two or three associated calciums) and H 0 were obtained, thus providing information about the different 0-containing structural units during the formation of calcium silicate hydrates from P-2CaOSi0 . While the quadrupolar parameter C could only be estimated for the oxygen sites due to the presence of overlapping resonances with unknown chemical shift dispersion, more definitive two-dimensional 0 DAS and Si isotropic/anisotropic NMR experiments may prove useful for obtaining a detailed understanding of these complex hydration processes. Static and MAS A1 NMR at high spinning speeds and magnetic field strengths have also been useful for obtaining a more detailed understanding of various calcium aluminate phases containing 4-, 5- and 6-coordinate aluminum sites in cement systems (169,185-188). The hydration scheme for many of the important calcium aluminates (CA) involved in both high alumina content and Portland cements is quite complex and the details of interconversions between these CA species have not been fully delineated. Recently, important A1 MAS NMR studies of the structural features of many of these CA intermediates have been reported. For example, the A l MAS NMR spectrum of one of the more complex calcium aluminate phases, CaO-2Al 0 (CA ), has been fit to six different 6-coordinate 17

23

29

9,


2

2

3

2

]

27

29

29

17

29

17

17

17

17

17

17

17

2

17

2

q

17

27

27

27

2

3

2


29

102 aluminum resonances (169,188). The quadrupolar parameters for these six different 6-coordinate aluminum sites in CA are summarized in Table XI, together with related parameters for various aluminum sites found in other calcium aluminates (and hydrates). These results suggest that further solid-state NMR studies using H- A\ CP/MAS, A1 MQMAS NMR and other two-dimensional NMR approaches are likely to more fully expand our understanding of the structural features and hydration reactions of these complex materials found in cements. Besides these silica/alumina and alumina-type cements, other potentially important cement-related materials such as aluminum phosphates and lithium aluminosilicates are also in need of thorough study by solid-state NMR methods. J) Bioceramics and Biomaterials. Recent developments in the preparation and processing of biomaterials including Bioglasses®, alumina, hydroxyapatite and calcium phosphate bioceramics suggest a new area for in-depth solid-state NMR investigations. P MAS amd CP/MAS NMR studies of hydroxyapatites (HA) and their calcium phosphate precursors have been reported (362-368). These studies have been directed toward providing an understanding of the relationship between the structures of the various calcium phosphates and the intricate biomineralization processes leading to hydroxyapatite (HA) formation in bone. Numerous P-OH and P-O-P sites in these different Ca/P-containing bone precursors have been identified by P CP/MAS NMR (364-368). However, Ή- Ρ HETCOR (Figure 12) and other twodimensional NMR experiments seem most likely to successfully unravel the complex crystallization and reorganization processes leading to hydroxyapatite crystallization and maturation in bone materials. Bioglass® materials that are currently used surgically to replace soft tissues and bone have also been examined by Na, Si and P MAS NMR (362,363,367), and recently by 0 MAS NMR for 0-labelled materials (367). These complex bioactive glasses are sodium calcium silicate glasses, containing 6% P 0 , and primarily consist of Q and Q silicate glass networks with associated modifying sodium and calcium ions. They undergo extensive surface chemistry involving silicate network reorganization and the formation of hydroxyapatite, a major constituent of bone, from unknown calcium phosphate percursors. Recent use of CP/MAS Si and P CP/MAS NMR to study the early stages of the surface and interfacial chemistry of these bioimplant materials has been reported (367). The study of silicon biomineralization has recently been approached using solid-state heteronuclear correlation techniques and C- Si REDOR (369). In addition, H- A1 HETCOR and H- Si HETCOR experiments have also been used to explore the interactions of the complex mesophase composite material MCM-41 (373). These materials represent technically important three-dimensional inorganic materials, but also provide model systems for the supramolecular assembly of organosilicates relevant to the biomineralization of silicon at inorganic/organic interfaces. The solidstate two-dimensional HETCOR NMR spectra shown in Figure 41 provide evidence for inorganic-organic interfacial interactions in aluminosilicate-containing MCM-41 mesophases on which trimethylammonium is adsorbed. The 2D Ή-^ΑΙ HETCOR spectrum (Figure 41 A) of the aluminosilicate MCM-41 shows that short-range (< 1 nm) 'H-Âl dipolar coupling is observed between the framework 4-coordinate aluminums and the trimethylammonium head group of the cationic CTMA 2

l

27


27

31

31

3Ι

23

17

29

31

17

2

2

5

3

29

13

!

27

]

31

29

29

+


103


27AI Dimension

I—ι—ι—ι—ι—j—ι—ι—ι—ι—j—ι—ι—ι—ι—ι—ι—ι—ι—ι—I

150

100

-50

0

50

δ(27Α1), ppm F

Figure 41.

Solid-state two-dimensional NMR studies of inorganic-organic interfacial interactions in aluminosilicate containing MCM-41 mesophases. 2D- H- AI HETCOR spectrum (A) of aluminosilicate MCM-41 showing in addition the corresponding 1D AI CP/MAS and H MAS NMR spectra plotted along their corresponding axes. 2D- H- Si HETCOR spectrum (B) of aluminosilicate MCM-41 showing in addition the corresponding 1D Si CP/MAS and H MAS NMR spectra plotted along their corresponding axes. The various cross peaks in each 2D HETCOR spectrum indicate dipoledipole couplings between the nearby protons of the cationic trimethylammonium head and specific framework silicon and aluminums in the MCM-41 mesophases.(373). 1

27

27

1

1

29

29

1

Continued on next page.


104

β

29Si Dimension


()

0

-100

-50

Ô(29Si), ppm Figure 4L Continued.


105

27

Table XI.

Summary of AI quadrupolar coupling constants (C ) asymmetry parameters (rj ) and isotropic chemical shifts (δ) for synthetic calcium aluminates of importance in high alumina and Portland cements (169,173,188). q

Q


Compound CA CA

2

C, A 2

7

CA 3

T|

δ(ρρπι)

Al(l) Al(2)

6.25±0.05

0.88+0.02

75.5+0.5

9.55+0.05

0.82+0.02

69.5±0.5

Al(l)

2.50

0.20

81.9

Al(2)

2.60

0.75

83.8

Al(3)

2.60

0.95

86.2

Al(4)

3.32

0.53

82.7

Al(5)

3.37

0.39

81.6

Al(6)

4.30

0.47

81.2

Al(l)

9.7+0.2

0.40±0.10

85.9+1.0

Al(2)

3.8±0.2

0.70±0.10

80.2±0.3

Al(l)

8.69±0.05

0.32±0.02

79.5±0.5

Al(2)

9.30+0.05

0.54+0.02

78.3+0.5

Q

CAH,

0

2.4±0.2*

C AH

6

0.705±0.010

3

C AH

l3

γ-ΑΗ

3

4

10.2+0.3 0.09+0.02

2

12.36+0.06 10.2±0.2

1.8+0.2"

C ASH, 4

Q

C (MHz)

Al(l)

1.91±0.07

0.73±0.04

10.4±0.3

Al(2)

4.45±0.05

0.44±0.03

11.5±0.3

0.360±0.010

0.19±0.03

13.1+0.1

1.7+0.2*

11.8±0.2


106 27

]

(cetyltrirnethylamrnoniurn) surfactant. The corresponding ID A\ CP/MAS and H MAS NMR spectra are plotted along the axes. The related 2D 'H-^Si HETCOR spectrum (Figure 41B) of MCM-41 shows that the framework silanol of MCM-41 is also in close proximity to the trimethylammonium head group leading to strong 'H-^Si dipolar interactions between the surfactant head group protons and the 4-coordinate framework silicons in MCM-41. Again, the corresponding ID Si CP/MAS and H MAS NMR are plotted along their corresponding axes. The various cross peaks in each 2D HETCOR spectrum thus indicate dipole-dipole couplings between the nearby protons of the cationic trimethylammonium head group and specific framework silicon and aluminums in the MCM-41 mesophases. (373). These two-dimensional NMR results suggest new research avenues where NMR experiments may be used to examine weak interfacial interactions in mesoporous and micellular type systems. Downloaded by 87.242.144.86 on May 21, 2014 | http://pubs.acs.org Publication Date: March 18, 1999 | doi: 10.1021/bk-1999-0717.ch001

29

!

4. Semiconductors. Ion Conductors and Suverconductors. Solid-state NMR

techniques have become increasingly important for studying inorganic semiconductors, ion conductors and superconductors due to the need to understand their short-range order and complex temperature-dependent behaviors. Studies of various superconductors using both static and MAS NMR as well as relaxation measurements have contributed significantly to our understanding of the complex behavior of high-T materials. a) Semiconductors. Binary alloys of nonmetals (GaAs, GaP and GaN), pseudobinary A B,. C alloys (where AC and BC are GaAs, GaP and InP) of isovalent semiconductors such as Ga^n^P, and pseudobinary alloys such as in CeyHg^Te and ΙηΑβχΡ,.χ are widely used in a variety of electronic devices (370-378). Many of the simple binary and pseudobinary semiconductors exhibit variable material properties (such as band gaps) that are dependent on the composition, the presence of dopants and impurities, and the crystal growth conditions. Understanding such relationships can provide a means of fine tuning their electronic properties. While the macroscopic structures of these pseudobinary materials are related to their parent compounds, the microscopic structures of atomic level domains are quite variable. The degree of structural ordering found in these materials, the effects of subtle changes in A-C and B-C bond lengths in pseudobinary alloys, and variations in local chemical bonding are affected by compositional variations in semiconductors, often due to low concentration doping. Solid-state NMR studies of semiconductors are in an early stage of development in terms of spectral resolution, sensitivity and assignment of various structural units based on NMR chemical shifts for nuclides such as P, Ga, In, Sn and Te, despite the fact that most of these nuclides have favorable natural abundances and receptivities. However, extensive quadrupolar line broadening for Ga, As and In makes all but the most symmetric sites difficult to observe, except possibly by using very high magnetic field strengths. One of the earliest NMR studies of semiconductors involved A1, Ga, Ga, In and In MAS NMR studies of binary semiconductors (374). These MAS NMR studies showed that the central transition resonance of these quadrupolar nuclides in binary semiconductors of the cubic zinc blende structure (A1P, AlAs, GaP, GaAs, InP and InAs) was primarily broadened by exchange interactions, whereas for the nitrides GaN and A1N of the hexagonal wurtzite lattice structure, the second-order quadrupolar c

X

X

3l

119

69,71

75

115

69

71

115

27

U3

69,71

I25

115


107 69

71

interaction (C = 2.8 MHz for GaN, C = 1.7 MHz for GaN and C = 2.2 MHz for A1N) was the dominant line-broadening mechanism. More detailed studies of gallium phosphide (374) by Ga MAS NMR showed that lineshape analysis, spin counting and quadrupolar nutation NMR for Ga were useful for quantifying the semiconductor crystal quality for various GaP materials prepared from solid-state metathesis reactions involving gallium halides and sodium phosphide. The importance of atomic cation ordering in Group III-V semiconductor alloys is of significance for the band gap properties of both bulk and thin film materials and can be controlled by growth conditions (375,376). The Group V semiconductor system, Gajn,.,,?, which contains the cations Ga and In has been shown by P MAS NMR to exist in neither a random nor an ordered structure as depicted in Figure 42A for Gao I P. Rather, these systems exhibit some degree of order designated S, where 0 < S < 1. The P MAS NMR spectra of crystalline and thin films of the Gafii^ system, where five possible phosphorus clusters with GaJn _ P sites may exist, have been examined. The P MAS NMR spectrum of the polycrystalline G?^., In P material, obtained at various sample spinning speeds (see Figure 42B), exhibits three resonances assigned to GaJn^P clusters with η = 0, 1 and 2. The predicted random distribution of η = 0, 1 and 2 is expected to be 0.547/0.356/0.087 and the MAS NMR spectrum indicates a cluster distribution of 0.53/0.38/0.09. The P MAS NMR spectrum for GaÎ^P thin films prepared under different growth conditions as shown in Figure 42C exhibit all five types of local phosphorus clusters in a 0.055/0.235/0.374/0.265/0.070 ratio, indicating an intermediate order with S > 0.6 (376). Such determinations of cation ordering in these types of semiconductors make it possible to begin relating this type of structural information to band gap properties and effects of semiconductor growth conditions on the quality of semiconductors. Recent studies of more complex ternary and quanternary semiconductors such as ZnCd chalogenides, ZnSe/GaP materials, and cadmium germanium arsenic phosphides of the formula CdGeAs . P have been reported (377,378). Typically, the cation ( Cd) resonances are dominated by nonlocal effects due to charge derealization and lattice contractions, while the anion ( P) resonances are influenced by both second-nearest-neighbor effects and these nonlocal effects. Single-pulse Cd and P MAS NMR (Figure 43), however, were both found to be highly sensitive to the composition of the CdGeAs . P alloys in the range χ = 0.00 to 0.875, with the Cd NMR resonances varying over 93 ppm and the P NMR peaks over a narrower chemical shift range (378). The changes in the Cd chemical shifts were interpreted in terms of next-nearest-neighbor effects in the second coordination sphere of the cadmiums which consists of eight germaniums, η cadmiums and 4-n zincs, where η varies from zero to four. The P MAS NMR spectra were not as informative from a local chemical environment viewpoint since there is only a 28 ppm chemical range between the pure end-members CdGeP and ZnGeP of these solid-solutions. The use of experiments that depend on the P- Cd heteronuclear dipolar coupling, however, has provided a means to distinguish between different phosphorous units such as the PGe Zn Cd _ sites and non-Cd-bonded PGe Zn sites. Besides these MAS NMR investigations, related studies of CdGeAs . P materials have been reported using both spin-echo P and Cd measurements, and 3ip_ii3 Q R (378). The results of P- Cd SEDOR measurements are given in q

q

q

27

69

69

31

5

05


31

4

n

3I

4

086

31

2 x

x

1I3

31

113

31

2 x

x

113

3,

113

3,

2

31

2

n

2

2

,I3

n

2

2

2 x

31

31

113

,I3

Cd S E D


x

108


(A)

(1)

Ρ

-120

-40

-200

(2)

Ga

-280

In

0

(Ga.In)

-160

-80

ppm Figure 42.

-240

ppm

A structural diagram of both ideal random and fully ordered Ga ln P materials is shown in (A). P MAS NMR spectra of (B) bulk, polycrystalline Ga ln P semiconductor, and (C) thin film Ga ln P material, obtained at various sample spinning speeds. The various P resonances denoted by η = 0, 1 and 2 are assigned to Ga ln . P clusters for partially ordered materials. (376). 05

31

014

086

014 31

n

086

4 n


05

109


(A) 3 i p

40 20

N

M

(B) nscdNMR

R

0 -20 -40 -60 -80 -100 -120

400

ô(3iP),ppm Figure 43.

350

300

250

200

150

ô(H3Cd), ppm

Solid-state NMR showing the compositional variation of the phosphorus and cadmium sites in the Zn Cd . P semiconductor glass system: (A) Ρ spectra and (B) C d spectra (377). 3 1

x

1

x

2

1 1 3


110 Figure 44 for both CdGeAs _ P glasses, where χ = 0.5, 1.0 and 2.0, and for the crystalline CdGeAs! P, material. These results show that for the glassy materials, the strength of the P- Cd dipolar interactions increase as the phosphorus content of the glasses increases (Figure 44A) and that the P- Cd dipolar strengths are comparable for both the glassy and crystalline material with a CdGeAs P composition (Figure 44B). Based on these measurements, various atomic distribution models, including both random zinc blende and ordered chalcopyrite lattice arrangements of the Ρ and As atoms, were evaluated as structural models for these amorphous semiconductor materials. While these results indicate the appplicability of solid-state NMR to study more complex quaternary semiconducting alloys, many of the more advanced CP/MAS and 2D NMR methods are likely to greatly expand our understanding of the structure, bonding and domain regions of these materials. b) Ion Conductors. Inorganic ion conductors are attractive candidates for solid-state electrolytes, electrodes, electrocatalysts and many other materials where ion or vacancy migration are important (118-121). Nonstoichiometric mixed metal oxides of the perovskite structure, in particular, have attracted interest, although many of these systems contain paramagnetic metal ions. The Ba2ln 0 material of the perovskite lattice structure exemplifies an ion conducting system where oxygen migration has been examined by solid-state O NMR over the temperature range of room temperature to 1200°C (381). The lattice structure consists of two-dimensional layers of corner-sharing In0 octahedra and distorted, corner-sharing In0 tetrahedra, with a fixed concentration of oxygen ion vacancies that are ordered in the twodimensional planes as shown in Figure 45A. This structure has three distinct oxygen sites: 0(1) in the equatorial plane of the indium octahedra, 0(2) in the apial sites of indium octahedra and tetrahedra, and 0(3) in the equatorial plane of the indium tetrahedra (Figure 45B). The solid-state static O NMR spectra of this material at various magnetic field strengths at room temperature (Figure 45C) are poorly resolved but can be fit to a sum of two quadrupolar powder patterns (assigned to 0(1) and 0(2) sites) and a narrower Gaussian (assigned to the 0(3) sites). MAS narrows this 0(3) peak, but the 0(1) and 0(2) site resonances remain broad. However, the broad resonances can be narrowed by performing a DAS experiments, displaying the two sharp resonances seen in Figure 45D, with isotropic second-order quadrupolar shifts between 150 and 200 ppm. Higher temperature O MAS NMR spectra (Figure 45E) reveal dramatic changes in the NMR spectra characterized by coalescence to a single motional averaged sharp peak at 210 ppm that is 10-15 times more intense than at RT. This peak is a consequence of both structural changes in symmetry in the materials as well as rapid motion (>36 MHz) of all the oxygens at elevated temperature. These results suggest the usefulness of solid-state NMR approaches to examine ion mobility as a function of temperature and to study the oxygen-site vacancy equilibria in mixed metal oxides such as these ion conductors. c) Superconductors. Solid-state NMR techniques, including both static relaxation studies (385), and MAS approaches, have been used to probe both the chemical and electronic structures of high-T superconductors such as YBaÛgO^ (274,382-387,407-409). Early studies of superconductors involved both Cu and 0 MAS NMR of powdered and magnetically aligned Y B a ^ ^ O ^ (1-2-3) at 8.45 Τ and 2

>0

31

n

x

0 113

31

U3


10

2

10

5

n

6

4

n

n

c

63


,7

(A)

H3Cd-3ip S E D O R CdGeAs2-xP

1.0

g

x

0.8 H

I

φ

•

f

D

A

*

Ο

~ 0.6 H φ

D

Ν


*

*

α

ft

·

• ft g

Ο

0.2

2.0

0.0 0.0

*

* 0.5

1.0 1

1.0

0.5

1.5

2t (ms)

2.0

1

(Β)

i i 3 C d - 3 i p SEDOR 1.0

g

CdGeAsi.oPi.o

H

0.8

Φ

crystal

*~0.6 Ό Φ Ν

glass Ο

C0.2 0.0 0.0

0.2

1

•

0.4

1—

0.8

0.6

1.0

2t ,(ms) Figure 44.

m

3 1

(A) C d - P SEDOR results (normalized intensity versus 2ϊ in ms) for several Ζηβύ , Ρ semiconductor giass systems at different values of χ: χ = 0.5 (closed triangles), 1.0 (closed circles) and 2.0 (open squares); and (B) comparison between the C d - P SEDOR decays for crystalline (open circles) and glassy (closed circles) CdGeAs^P, materials (378). Λ

Λ %

2

113

31

0


112 Ι7

11.7 Τ (382,383). Detailed 0 NMR results at 8.45 Τ for isotopically 0-17 labelled YBa2Cu 0 . show two major features at 300K, an intense paramagnetically shifted peak at ca. 1800 ppm assigned to the two Cu0 planar oxygens 0(2) and 0(3) and a weaker signal near 400 ppm assigned to the column oxygens 0(1) (Figure 46) (382). The intense peak was observed to undergo a 800 ppm diamagnetic shift when the temperature was lowered to 77K. Further work also revealed a weak signal at ca. 3000 ppm with a very large (100 kHz) linewidth assigned to the chain oxygen 0(4). Enhanced resolution of the 0 NMR of magnetically aligned isotopically 0-17 labelled Y B a ^ ^ O ^ shown in Figure 47, reveals a remarkable spectrum where the 19 of the 20 possible transitions (central and satellite) are observed for the four different oxygens of this material: 0(1), peaks 2,4,12,18,19; 0(2,3), peaks 5-8, (10,11), 13-16; 0(4), peaks 1,3,9,17,20. For the 0(2) and 0(3) planar oxygens, a C value of 6.5 MHz and near axial symmetry (η° = 0.20-0.25) were obtained by fitting the peak positions. For the column (bridging) oxygen 0(1), a C of 7.7 MHz and r\ = 0 were observed, and the chain oxygen 0(4) was found to have a C of 0.9 MHz and r| = 0.38. The large chemical shift of the planar oxygens 0(2,3) is due to a anisotropic Knight frequency shift caused by the metallic nature of the Cu0 planes, while the large breadth and large chemical shift of the 0(4) oxygen resonances is likely due to antiferromagnetic spin fluctuations in the CuO chains. The variable temperature 0 NMR spectra of various YBaÛjO^ materials over a range of oxygen compositions (from χ = 0.0 to 1.0) are shown in Figure 48. Changes in the composition of oxygen for YBaÛjO^ from 0 stoichiometry to values as low as 0 were shown to decrease the intensity of the 0(4) peak due to preferential removal of these oxygens in the non-stoichiometric materials. Similar 0 NMR measurements of Y B a ^ ^ O ^ , and other high-T superconductors including Bi Sr CaCu 0 and Tl Ba CaCu 0 have also been reported (383,384,386) as shown in Figure 49. In each of the CuO-materials, two major resonances were observed, a broad, paramagnetically shifted resonance between 1500 and 2000 ppm due to oxygens in the conducting Cu0 planes and a narrower, diamagnetically shifted peak between 0 to 500 ppm due to BaO, SrO or BiO planar oxygens in the insulating planes. A recent 0 NMR study of the high T (125 K) triple-layered material T^Baâ^Ôg.^ also shows these two characteristic 0 resonances at room temperature. However, detailed lower temperature measurements of the paramagnetically shifted peak at 1400 ppm shows that this resonance assigned to the conducting Cu0 planar oxygens shifts dramatically at its T value of 125 Κ for samples before and after annealing as shown in Figure 50. The relationship between the shift in the ô ( 0) values and the ac-susceptibility measurements shown in the inset of Figure 50 indicates that the temperature dependence of this shift is due to changes in the spin susceptibility and hole density of the material (386,387). In addition to the extensive studies of various superconducting systems, both Y MAS NMR and static 0 NMR have also been performed on metal-substituted and related high-T superconductors (274,407-409). Temperature-dependent relaxation studies using 0, Cu and Y MAS NMR have also related NMR behavior to superconducting properties (407-409), but are beyond the scope of this discussion. However, these investigations together with the static temperature-dependent relaxation studies of high-T superconductors over the last decade (385) have added 3

7 x

2

17


q

Q

q

q

Q

2

,7

7

6 5

17

c

2

2

2

8+x

2

2

2

8+x

2

17

c

17

2

c

,7

obs

89

17

c

17

63

8 9

c


113

(A)

(Β)


Vacancy

(Q 67.7 MHz (1) 1000

-1000

(2) 1000

(3) 1000

Figure 45.

-1000

(A) The proposed structure of Ba ln 0 showing the tilting arrangement of the In0 and In0 structural units. (B) The ordering of oxygen vacancies in the layers of four-coordinate indiums is also shown. (C) 0 MAS NMR spectra at RT for Ba ln 0 at various magnetic fields. The spectra consist of three components: two quadrupolar powder patterns (C = 7.8 MHz, η ° = 0.3, δ = 160 ppm; C = 6.9 MHz, η ° = 0.3, ô = -160 ppm) and a Gaussian peak corresponding to 0(1), 0(2) and 0(3), respectively. (D) The 0 MAS spectrum denoted (a) and 0 DAS spectral resonances denoted (b) and (c), the latter taken from slices of the 2D DAS experiment, show peaks corresponding to the 0(1), 0(2) and 0(3) sites. (E) Variable temperature 0 MAS NMR spectra from RT to 1200°C show rapid (>36 MHz) oxygen ion movement between oxide sites (381). 2

4

2

5

6

17

2

2

5

q

ΐ50

q

17

iso

17

17

Continued on next page. In Solid-State NMR Spectroscopy of Inorganic Materials; Fitzgerald, J.; ACS Symposium Series; American Chemical Society: Washington, DC, 1999.

114

(D)

0(3)

(1)

MAS 7.38 kHz

-i

1

1

500

1

1

1

1

(2)

— f

500

1

Γ

-500

0(1) —


1

0 DAS

1

1

1

1

0

1

Γ

-500 DAS

(3)

~ι

1

1

1

1

500

1

0

η

1

r

-500

Shift (ppm)

0(1) Chemical 2000

1000

0

-1000

-2000

Shift (ppm) Figure 45. Continued.



115

Figure 46.

17

Static spin-echo 0 NMR spectra at 8.45 Τ of a random powder of YBa Cu 0 . at (a) 300 Κ and (b) 77 K. The * indicates the resonance from 0(1) in aligned crystallites (382,383). Inset shows a schematic partial structure of the 1-2-3 Y-Ba-Cu oxide superconductor material. 2

3

7

x

(10,11) 3

4

8

12

15

17 18

13 14

ν 40000

20000

1

0 ppm

-20000

r

—ι— -40000

Frequency shift (ppm from H 0) 2

Figure 47.

17

0 MAS NMR spectra at 8.45 Τ and 300 Κ of magnetically aligned YBa Cu 0 . (B I c). The intensities of the five transitions (central and satellite transitions) have a 5:8:9:8:5 ratio. Nineteen of the twenty possible resonances (for the four different oxygens each with five transitions) are observed for the four different oxygen sites: 0(1 ), peaks 2,4,12,18,19; 0(2,3) peaks 5-8, (10,11 are degenerate), 13-16; and 0(4), peaks 1,3,9,17,20 2

3

7

x

0

(382).



116

Frequency Shift (ppm from H 0) 2

Figure 48.

17

0 MAS NMR at 11.7 Τ of various YBa Cu 0 . materials with oxygen compositions (from χ = 0.05 to 1.0), taken at various temperatures in Κ 2

3

7

x

(382).


117


(Ba.KJO, BiO

7\

3C00

20C0

1000

0

-10C0

Frequency Shift (ppm from H2O) Figure 49.

17

MAS 0 NMR at 11.7 Τ and 300 Κ of various superconductors: (A) Ba Ko Bi0 (B) La, S r C u 0 (C) YBa Cu 0 . (D) Bi Sr CaCu 0 and (E) TI Ba CaCu 0 (382). 06

4

2

3J

2

8 5

2

0 1 5

4 l

2

3

7

xl

2

2

8+x


2

8+x>


118

Τ (Κ)

Figure 50.

17

Temperature dependence of the isotropic chemical shift of 0 NMR resonance for conducting Cu0 oxygen sites in TI 6a CaCu O before (o) or after (•) annealing. Inset shows the corresponding ac susceptibility of these samples (386). 2

2

2

2

e+x


119

enormously to our current understanding of the structural nature and mechanisms of these important inorganic materials.


5. Composites Containing Inorganic Particles/Fibers and Matrix Materials,

Composite materials represent a class of technologically important inorganic materials which generally have unique mechanical properties (388,406). Composites are complex chemical substances that contain two major components: a reinforcing material and a matrix material. In addition, fabrication processes commonly involve the use of a third reactive component to improve the "interfacial bonding" between the matrix and the reinforcement material (153,154,256,362,403). The adhesion at the interface between the matrix and reinforcing element (e.g., fiber) ultimately dictates the mechanical performance and thermal stability of the composite. This is particularly important since many composites such as glass and carbonfiber-basedcomposites are made using specific silane coupling agents to promote adhesion (122). Excluding metal-containing composites, most inorganic composites consist of either inorganic/organic or inorganic/inorganic matrix/reinforcement material compositions. Glassfiber/epoxyresin and carbonfiber/inorganicglass or ceramic composites are examples of the former, while silicon nitride-based composites, ceramic matrix composites,fiber-reinforcedceramics and SiC fiber/SiAlON ceramic combinations are in the latter category (388-392). Important problems in the solid-state NMR study of composite materials relate to three fundamental areas: 1) development of sensitive characterization techniques to understand the reinforcement and matrix components themselves, including the préfabrication surfaces and reactions, 2) examination of matrix/reinforcement material following fabrication and various treatments, and 3) examination of the adhesion and/or bonding at the "interface" of the reinforcement material and the matrix substance. C and Si CP/MAS NMR techniques, in particular, have been highly useful for probing the "interfacial region" in epoxy/glass composites and epoxy/carbon fiber composites (404-406). In addition, C and Si MAS NMR studies of the interfacial chemistry of silane coupling agents at the surface of silica particles have also been reported (153,154,404-406). An improved understanding of the functional groups that anchor these coupling agents to the composite material interfaces is critical to determining the ultimate functional properties of both carbon and silica composites. Therefore, molecular level descriptions of "bonding" between the coupling agents and the composite components as derived from nondestructive solid-state NMR measurements could provide direction necessary to chemically engineer interfaces in these and newer composite materials. Of particular importance is the selectivity of solid-state NMR to discriminate the interfacial species from the other fiber/matix components, to provide information regarding the modes of interfacial binding, and to obtain quantitative information relevant to interfacial interactions, void spaces and domain regions (397-402). The study of silicon carbide or aluminafiber/glassand silicon carbide or alumina/ceramic glass composites is another area of interest due to the ability of reinforcementfibersof silicon carbide, silicon nitride or alumina to improve toughness of glasses and ceramics. Other interesting materials include silicon carbide fibeârium silicate, silicon carbide/silicon nitride, and silicon carbide/lithium silicate ceramic/glass composites (258,389). These systems are well suited for both ID and 2D C, A1 and Si MAS NMR studies (5,12,13,53,62,76-87,95-97). 13

29

13

13

27

29

29


120


V. CONCLUSIONS Atomic-level studies of the structure and dynamics of inorganic materials by solidstate NMR spectroscopy have made significant advances in the past decade. Both fundamental and new solid-state NMR methods and approaches have been utilized to obtain important structural and dynamical information pertaining to metal oxides, catalysts, zeolites, ceramics and glasses. These approaches have contributed significantly to advancing our understanding of the chemical and physical properties of inorganic semiconductors, ion conductors, superconductors and electronic materials. Novel solid-state NMR methods for both spin-1/2 and quadrupolar nuclides contained in traditional and advanced inorganic solid materials, are currently being utilized to address chemical issues of relevance to these materials. The use of cross-polarization methods and two-dimensional approaches has been particularily helpful for obtaining connectivity information and structural details for many inorganic systems that were previously inaccessible. The recent development of high-resolution techniques is expected to greatly expand our understanding of quadrupolar nuclides contained in metal oxide catalysts, ternary metal oxide ion conductors, electronic materials and electrochemical systems. The success of solid-state NMR approaches in addressing complex structural and reactivity questions suggests an important role for solid-state NMR in future research and development of advanced inorganic materials.

REFERENCES (1)

Pople, J.A.; Schneider, W . G . ; Bernstein, H.J. High-Resolution Nuclear Magnetic

(2)

Resonance, McGraw-Hill, New York, 1959. Abragam, A. Principles of Nuclear Magnetism, Clarendon Press, Oxford, England, 1961.

(3)

Becker, E.D. High Resolution NMR. Theory and Chemical Applications, 2nd Edition,

(4)

Farrar, T.C.; Becker, E.D. Pulse and Fourier Transform NMR. Introduction to Theory

Academic Press, New York, 1959. and Methods, Academic Press, New York, 1971.

(5)

Ernst, R.R.; Bodenhausen, G . ; Wokaun, A. Principles of Nuclear Magnetic Resonance

(6)

in One and Two Dimensions, Clarendon Press, Oxford, England, 1987. Slichter, C P . Principles of Magnetic Resonance, Springer- Verlag, Berlin, Germany,

(7)

Mehring, M . Principles of High-Resolution NMR in Solids, Springer-Verlag, Berlin,

(8)

Haeberlen, H . High Resolution NMR in Solids - Selective Averaging, Academic Press,

1990.

Germany, 1976.

(10)

New York, 1976. Gerstein, B.C.; Dybowski, C.R. Transient Techniques in NMR of Solids, Academic Press, Inc. Orlando, Florida, 1985. Fyfe, C A . Solid-State NMR for Chemists, C.F.C. Press, Guelph, Ontario, 1983.

(11)

Engelhardt, G,; Michel, D. High-Resolution Solid-State NMR of Silicates and Zeolites,

(12)

Maciel, G.E. ed., Nuclear Magnetic Resonance in Modern Technology, N A T O ASI Series,

(13)

Vol. 447, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1994. Bell, A.T.; Pines, A. eds., NMR Techniques in Catalysis, Marcel Dekkar, Inc., New York, 1994.

(9)

John Wiley and Sons, Chichester, England, 1987.


121 (14) (15) (16) (17) (18) (19) (20) (21)


(22) (23) (24)

Brinkmann, D.; Mali, M . NMR Basic Principles and Progress 1994, 31, 171. Freude, D.; Haase, J. NMR Basic Principles and Progress 1993, 29, 1. Cohen, M . H . ; Reif, F. In Solid State Physics, Volume 5, Seitz, F.; Turnbull, D . eds., Academic Press, New York, 1957. Das, T.P.; Hahn, E . L . Nuclear Quadrupole Resonance Spectroscopy, Academic Press, New York, 1958. Andrew, E.R. Prog. NMR Spect. 1971, 8, 1. Lowe, I. J. Phys. Rev. Lett. 1959, 2, 285. Herzfeld, J.; Berger, A . E . J. Chem. Phys. 1980, 73, 6021. Fyfe, C.A.; Gobbi, G.C.; Hartmann, J.S.; Klinowski, J.; Thomas, J.M. J. Phys. Chem. 1 9 8 2 , 86, 1247. Klinowski, J.; Ramdas, S.; Thomas, J.M.; Fyfe, C.A.; Hartman, J.S. J. Chem. Soc. Faraday Trans. II 1983, 78, 1025.

(25)

Fitzgerald, J.J.; Dec, S.F., unpublished results, 1998. Fitzgerald, J.J.; Hamza, A.I.; Dec, S.F.; Bronnimann, C.E. J. Phys. Chem. 1 9 9 6 , 100, 17351. Gerstein, B.C.; Pembleton, R.G.; Wilson, R.C.; Ryan, L . J. Chem. Phys. 1977, 66, 361.

(26)

Bronnimann, C.E.; Chuang, I.; Hawkins, B.L.; Maciel, G.E. J. Am. Chem. Soc. 1 9 8 7 , 109,

(38) (39) (40) (41) (42) (43) (44) (45) (46)

1562. Bronnimann, C.E.; Hawkins, B.L.; Zhang, M . ; Maciel, M.E. Anal Chem. 1 9 8 8 , 60, 1743. Bronnimann, C.E.; Ziegler, R.C.; Maciel, G.E. J. Am. Chem. Soc. 1988, 110, 2023. Burum, D.P.; Rhim, W.K. J. Chem. Phys. 1979, 71, 944. Burum, D.P. Concepts in Magn. Reson. 1990, 2, 213. Dec, S.F.; Maciel, G.E. J. Magn. Reson. 1990, 87, 153. Santos, R.A.; Wind, R.A.; Bronnimann, C.E. J. Magn. Reson. Β 1994, 105, 183. Maxwell, R.; Lathrop, D.; Franke, D.; Eckert, H . Angew. Chem. Int. Ed. Engl. 1 9 9 0 , 29, 882. Hartmann, S.R.; Hahn, E.L. Phys. Rev. 1962, 128, 2042. Pines, Α.; Gibby, M . G . ; Waugh, J.S. J. Chem. Phys. 1973, 59, 569. Yannoni, C.S. Acct. Chem. Res. 1982, 15, 201. Yannoni, C.S. "Basic Cross-Polarization Magic-Angle Spinning" in Nuclear Magnetic Resonance in Modern Technology, Maciel, G . E . , ed., N A T O ASI Series, V o l . 447, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1994. Schaefer, J.; Stejskal, E.O. J. Am. Chem. Soc. 1976, 98, 1031. Schaefer, J.; Stejskal, E.O.; Garbow, J.R.; McKay, R.A. J. Magn. Reson. 1984, 59, 150. Roberts, J.E.; Vega, Α.; Griffin, R.G. J. Am. Chem. Soc., 1984, 106, 2506. Sindorf, D.; Maciel, G.E. J. Am. Chem. Soc. 1980, 102, 7606. Sindorf, D.; Maciel, G.E. J. Phys. Chem. 1982, 86, 5208. Sindorf, D.; Maciel, G.E. J. Am. Chem. Soc. 1983, 105, 1487. Vega, A.J. J. Magn. Reson. 1992, 96, 50. Vega, A.J. Solid State NMR 1992, 1, 17. Hayashi, S.; Akiba, E . Chem. Phys. Lett. 1994, 226, 495.

(47)

Chuang, I.S.; Kinney, D.R.; Bronnimann, C.E.; Maciel, G.E. J. Phys. Chem. 1 9 8 8 , 92,

(48) (49) (50)

5569. Kinney, D.R.; Chuang, I.S.; Maciel, G.E. J. Am. Chem. Soc. 1993, 115, 6786. Chuang, I.S.; Kinney, D.R.; Maciel, G.E. J. Am. Chem. Soc. 1993, 115, 8695. Chuang, I.S.; Maciel, G.E. J. Am. Chem. Soc. 1996, 118, 401.

(27) (28) (29) (30) (31) (32) (33) (34) (35) (36) (37)


122 (51)

Maciel, G.E.; Ellis, P.D. "NMR Characterization of Silica and Alumina Surfaces", in NMR Techniques in Catalysis, Bell, A . T . ; Pines, Α . , eds., Marcel Dekkar, Inc. New York, 1994.

(52)

Wu, Y . ; Lewis, D.; Frye, J. S.; Palmer, A.R.; Wind, R.A. J. Magn. Reson. 1 9 9 2 , 100, 425. De Paul, S.M.; Ernst, M . ; Shore, J.S.; Stebins, J.F.; Pines, A. J. Phys. Chem. Β 1 9 9 7 , 101, 3240. Blackwell, C.S.; Patton, R.L. J. Phys. Chem. 1984, 88, 6135. Morris, H.D.; Ellis, P.D. J. Am. Chem. Soc. 1989, 111, 6045. Harris, R.K.; Nesbitt, G. J. Magn. Reson. 1988, 78, 245. Hayashi, S. Solid State NMR 1994, 3, 93. Fyfe, C.A.; Wong-Moon, K . C . ; Huang, Y.; Grondey, H . ; Mueller, K . T . J. Phys. Chem. 1995, 99, 8707. Fyfe, C.A.; Grondey, H . ; Mueller, K . T . ; Wong-Moon, K . C . ; Markus, T. J. Am. Chem. Soc. 1992, 114, 5876.

(53) (54) (55) (56) (57) (58)


(59) (60) (61) (62)

(63) (64) (65) (66) (67) (68) (69) (70) (71) (72)

(73) (74) (75) (76) (77) (78)

Fyfe, C.A.; Mueller, K . T . ; Grondey, H . ; Wong-Moon, K . C . Chem. Phys. Lett 1 9 9 2 , 199, 198. Fyfe, C.A.; Mueller, K . T . ; Grondey, H . ; Wong-Moon, K . C . J. Phys. Chem. 1 9 9 3 , 97, 13484. Fyfe, C.S.; Mueller, K . T . ; Wong-Moon, K . C . "Cross-Polarization Process to Less Common Pairs", in Nuclear Magnetic Resonance in Modern Technology, Maciel, G . E . ed., N A T O ASI Series, Vol. 447, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1994. van Wüllen, L . ; Züchner, L . ; Müller-Warmuth, W.; Eckert, H . Solid-State NMR 1 9 9 6 , 6, 203. Grey, C.P.; Corbin, D.R. J. Phys. Chem. 1995, 99, 16821. Fyfe, C. Α.; Wong-Moon, K. C . ; Huang, Y . ; Grondey, H . J. Am. Chem. Soc. 1995, 117, 10397. Frydman, L . ; Harwood, J. S. J. Am. Chem. Soc. 1995, 117, 5367. Fernandez, C.; Amoureux, J.P. Chem. Phys. Lett. 1995, 242, 449. Fernandez, C.; Amoureux, J.P.; Chezeau, J.M.; Delmotte, L.; Kessler, H . Microporous Mater. 1996, 6, 331. Vega, S. Phys. Rev., A 1981, 23, 3152. Massiot, D.; Touzs, B.; Trumeau, D.; Coutures, J . P.; Virlet, J.; Florian, P.; Grandinetti, P. J Solid-State NMR, 1996, 6, 73. Samoson, Α.; Lippmaa, E . ; Pines, A. Mol. Phys. 1988, 65, 1013. Samoson, A."Introduction to D O R NMR", in Nuclear Magnetic Resonance in Modern Technology, Maciel, G.E. ed., N A T O ASI Series, Vol. 447, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1994. Wu, Y . ; Chmelka, B.F.; Pines, Α.; Davis, M.E.; Grobet, P.J.; Jacobs, P.A. Nature 1990, 346, 550. Llor, Α.; Virlet, J. Chem. Phys. Lett. 1988, 152, 248. Mueller, K.T.; Sun, B.Q.; Chingas, G.C.; Zwanziger, J.W.; Terao, T.; Pines, A . J. Magn. Reson. 1990, 86, 470. Medek, Α.; Harwood, J.S.; Frydman, L . J. Am. Chem. Soc. 1995, 117, 12779. Baltisberger, J . H . ; Gann, S.L.; Grandinetti, P.J.; Pines, A. Mol. Phys. 1994, 81, 1109. Jäger, C. NMR Basic Principles and Progress 1994, 31, 133.


123 (79)

Jäger, C. J. Magn. Reson. 1992, 99, 353.

(80)

Jäger, C.; Herzog, K . ; Thomas, B.; Feike, M . ; Kunath-Fandrei, G. Solid State NMR 1995, 5, 51. Haase, J.; Conradi, M.S. Chem. Phys. Lett. 1 9 9 3 , 209, 287. Vega, A.J. J. Am. Chem. Soc. 1988, 110, 1049. Jarvie, T.P.; Wenslow, R . M . ; Mueller, K . T . J. Am. Chem. Soc. 1 9 9 5 , 117, 570. Wang, S.H.; De Paul, S.M.; Bull, L . M . J. Magn. Reson. 1997, 125, 364. Fyfe, C.A.; Grondey, H . ; Feng, Y . ; Kokotailo, G.T. Chem. Phys. Lett. 1990, 173, 211. Feike, M . ; Graf, R.; Schnell, I.; Jäger, C.; Spiess, H.W. J. Am. Chem. Soc. 1 9 9 6 , 118, 9631. Feike, M . ; Jäger, C.; Spiess, H.W. J. Non-Cryst. Solids 1998, 223, 200. Schmidt-Rohr, K . ; Spiess, H.W. Multidimensional Solid-State NMR and Polymers, Academic Press Inc. San Diego, California, 1994.

(81) (82) (83) (84) (85) (86)


(87) (88) (89) (90) (91) (92) (93) (94) (95) (96) (97) (98) (99) (100) (101) (102) (103) (104) (105) (106) (107) (108) (109) (110) (111) (112) (113) (114) (115) (116) (117)

Caravatti, P.; Neuenschwander, P.; Ernst, R.R. Macromol. 1985, 18, 119. Makowka, C.D.; Slichter, C.P.; Sinfelt, J.H. Phys. Rev. B 1985, 31, 5663. Lathrop, D.; Eckert, H . J. Am. Chem. Soc. 1990, 112, 9017. Franke, D.; Maxwell, R.; Lathrop, D.; Eckert, H . J. Am. Chem. Soc. 1991, 113, 4822. Franke, D.; Maxwell, R.; Lathrop, D.; Banks, K.; Eckert, H . Phys. Rev. B 1992, 46, 8109. Franke, D.; Banks, K . ; Maxwell, R.; Eckert, H . J. Phys. Chem. 1992, 96, 1906. Gullion, T.; Schaefer, J. J. Magn. Reson. 1989, 81, 196. Gullion, T.; Schaefer, J. Adv. in Magn. Reson. 1989, 13, 57. Hing, A.W.; Vega, S.; Schaefer, J. J. Magn. Reson. Series A 1993, 103, 151. Blumenfeld, A . L . ; Coster, D.J.; Fripiat, J.J. Chem. Phys. Lett. 1994, 231, 491. Hudalla, C.; Eckert, H . J. Phys. Chem. 1996, 100, 15986. Raleigh, D.P.; Levitt, M . H . ; Griffin, R.G. Chem. Phys. Lett. 1988, 146, 71. Tycko, R.; Dabbagh, G. Chem. Phys. Lett. 1990, 173, 461. Grey, C.P.; Vega, A.J.; J. Am. Chem. Soc. 1995, 117, 8232. Kao, H . M . ; Grey, C P . J. Phys. Chem. 1996, 100, 5105. Harmer, M.A.; Vega, A. J. Solid State NMR 1995, 5, 35. Gullion, T. J. Magn. Reson, Series A 1995, 117, 326. Frydman, L . ; Chingas, G.C.; Lee, Y . K . ; Grandinetti, P.J.; Eastman, M . A . ; Barrall, G.A.; Pines, A. J. Chem. Phys. 1992, 97, 4800. Ganapathy, S.; Vega, S. J. Am. Chem. Soc. 1998, 120, 1078. Bax, Α.; Szeverenyi, N.M.; Maciel, G.E. J. Magn. Reson. 1983, 52, 147. Gan, Z. J. Am. Chem. Soc. 1992, 114, 8307. Dixon, W.T.; Schaefer, J.; Sefcik, M . D . ; Stejskal, E.O.; McKay, R.A. J. Magn. Reson. 1982, 49, 341. Kolbert, A . C . ; Griffin, R.G. Chem. Phys. Lett. 1990, 166, 87. Olsen, K . K . ; Zwanziger, J.W. Solid State NMR 1995, 5, 123. Grandinetti, P.J.; Baltisberger, J.H.; Farnan, I.; Stebbins, J.F.; Werner, U . ; Pines, A . J. Phys. Chem. 1995, 99, 12341. Farnan, I.; Grandinetti, P.J.; Baltisberger, J.H.; Stebbins, I F . ; Werner, U . ; Eastman, M . Α.; Pines, A. Nature 1992, 358, 31. Baltisberger, J.H.; Xu, Z.; Stebbins, I F . ; Wang, S.H.; Pines. A. J. Am. Chem. Soc. 1996, 118, 7209. X u , Z.; Stebbins, I F . Science 1995, 270, 1332. Farnan, I.; Stebbins, J.F. J. Non-Cryst. Sol. 1995, 124, 207.


124 (118) (119) (120) (121) (122) (123) (124)


(125) (126) (127) (128) (129) (130)

(131) (132) (133) (134) (135) (136)

(137)

(138) (139) (140) (141) (142)

Kung, H . H . Transition Metal Oxides, Surface Chemistry and Catalysis, Elsevier, New York, 1989. Rao, C.N.R.; Raveau, B. Transition Metal Oxides,VCHPublishers, New York, 1995. Rao, C.N.R.; Rao, G.V.S. Transition Metal Oxides, Crystal Chemistry and Phase Transitions, National Bureau of Standards, Washington, DC., 1974. Wells, A.F. Structural Inorganic Chemistry, Fifth Edition, Clarendon Press, Oxford, 1984. D.E. Leyden, ed. Silanes, Surfaces and Interfaces, D.E. Leyden, ed., Gordon Breach New York, 1986. Grasselli, R.K.; Brodzil, J.F. eds., Solid-State Chemistry in Catalysis, American Chemical Society Series, A C S Publishing, New York, 1985. Her, R.K. The Chemistry of Silica, Solubility, Polymerization, Colloid, Surface Properties, and Biochemistry, Wiley-Interscience, Inc. New York, 1979. Engelhardt, G.; Koller, H. NMR Basic Principles and Progress 1994, 31, 1. Brinker, C.J.; Scherer, G.W. Sol-Gel Science: The Physics and Chemistry of Sol-Gel Processing, Academic Press, Inc. New York, 1990. Jones, K.; Davies, T . I ; Emblem, H.G.; Parkes, P. Mater. Res. Soc. Symp. Proc. 1986, 75,111. Klemperer, W . G ; Mainz, V . V . ; Millar, D . M . Mater. Res. Soc. Symp. Proc. 1986, 73, 15. Akapo, S.O.; Simpson, C.F. J. Chromatogr. Sci. 1990, 28, 186. Lippens, B.C.; Steggerda, II in Physical and Chemical Aspects of Adsorbents and Catalysts, Linsen, B. G.; Fortuin, J. M . H . , Okkerse, C.; Steggerda, J.J. eds., Academic Press, New York, 1970. Wefers, K.; Misra, C. Oxides and Hydroxides of Aluminum, Alcoa Technical Paper No. 19, Alcoa Laboratories, 1987. Gitzen, W.H. Alumina as a Ceramic Material, The American Ceramic Society, Columbus, O H , 1971. Meier, W . M . ; Smith, J.V. Zeolite Chemistry and Catalysis, Rabo, J.A., ed., A C S Monograph 171, A C S Books, New York, 1976. Barrer, R.M. Zeolites and Clay Minerals as Sorbents and Molecular Sieves, Academic Press, Inc. New York, 1978. Meier, W . M . ; Olson, D.H. Atlas of Zeolite Structure Types, Butterworth-Heinemann, London, 1992. Fyfe, C.A.; Kokotailo, G.T. "Solid-State N M R Investigations of Zeolites and Related Materials", in Nuclear Magnetic Resonance in Modern Technology, Maciel, G . E . , ed., N A T O ASI Series, Vol. 447, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1994. Fyfe, C.A.; Mueller, K.T.; Kokotailo, G.T. "Solid-State NMR Studies of Zeolites and Related Systems", in NMR Techniques in Catalysis, Bell, A.T.; Pines, A. eds., Marcel Dekkar, Inc., New York, 1994. Fyfe, C.A.; Feng, Y . ; Gies, H . ; Grondey, H . ; Kokotailo, G.T. J. Am. Chem. Soc. 1990, 112, 3264. LaPierre, R.B. Zeolites, 1985, 5, 346. Lippmaa, E.; Magi, M . ; Samoson, Α.; Engelhardt, G.; Grimmer, A.R. J. Am. Chem. Soc. 1980, 102, 4889. Magi, M . ; Lippmaa, E . ; Samoson, Α.; Engelhardt, G.; Grimmer, A.R. J. Phys. Chem. 1984, 88, 1518. Lippmaa, E.; Magi, M . ; Samoson, Α.; Tarmak, M . ; Engelhardt, G. J. Am. Chem. Soc. 1981, 103, 4992.


125 (143) (144) (145) (146) (147) (148)

Hater; W.; Muller-Warmuth, W.; Frischat, G.H. Glastech 1989, 62, 328. Smith, J.V.; Blackwell, C.S.; Hovis, G.L. Nature 1984, 309, 140. Haukka, S.; Roat, A . J. Phys. Chem. 1993, 98, 1695. Haukka, S.; Lakomaa, E X . ; Root, E . L . J. Phys. Chem. 1994, 97, 5085. Caravajal, G.S.; Leyden, D.E.; Quinting, G.R.; Maciel, G.E. Anal. Chem. 1988, 60, 1776. Dirken, P.J.; Smith, M . E . ; Whitfield, H.J. J. Phys. Chem. 1995, 99, 395.

(149) (150) (151)

Klinowski, J. Prog. Nucl. Magn. Reson. Spectrosc. 1984, 16, 237. Thomas, J.M.; Klinowski, J. Adv. In Catal. 1985, 33, 199. Thomas, J.M., Klinowski, J.; Wright, P.Α.; Roy, R. Angew. Chem. Int. Ed. Engl. 1983, 22, 614. Pfeifer, H . "Applications of N M R Spectroscopy to Surfaces and Catalysts: Acidic Sites and Absorbed Species", in Nuclear Magnetic Resonance in Modern Technology, Maciel, G E . ed., N A T O ASI Series, Vol. 447, Kluwer Academic Publisher, Dordrecht, Netherlands, 1994. Hoh, K.P., Ishida, H . Koenig, J.L. Polym. Compos. 1990, 11, 192. Bhagawan, S.S.; Tripathy, D.K.; De, S.K. J. Appl. Polym. Sci. 1987, 34, 1581. Kirkpatrick, R.J.; Smith, K . A . ; Schramm, S.; Turner, G.; Yang, W.H. Annu. Rev. Earth and Planet. Sci. 1985, 13, 29. Kirkpatrick, R.J.; Kinsey, R.A.; Smith, K . A . ; Henderson, D.M., Oldfield, E. Am. Mineral. 1985, 70, 106. Smith, K . A . ; Kirkpatrick, R.H.; Oldfield, E . ; Henderson, D.M. Am. Mineral. 1983, 68, 1206. Haddix, G.W.; Narayana, M . "NMR of Layered Materials for Heterogeneous Catalysis", in NMR Techniques in Catalysis, Bell, A.T.; Pines, Α., eds. Marcel Dekkar, Inc. New York, 1994. Smith, K . A . ; Kirkpatrick, R.J.; Oldfield, E . ; Henderson, D . M . Am. Mineral. 1985, 70, 106. Pfeifer, H . Colloids and Surfaces 1989, 36, 169. Hunger, M . ; Freude, D.; Pfeifer, H . J. Chem. Soc. Faraday Trans. 1991, 87, 657. Kummerlien, J.; Merwin, L . H . ; Sebald, Α.; Keppler, H . J. Phys. Chem. 1992, 96, 6405. Haw, J.F. "In Situ NMR", in NMR Techniques in Catalysis, Bell, A.T.; Pines, A . eds., Marcel Dekkar, Inc., New York, 1994.


(152)

(153) (154) (155) (156) (157) (158)

(159) (160) (161) (162) (163) (164)

Peeters, M.P.J.; Wahelkamp, W.J.J.; Kentgens, A.P.M. J. Non-Cryst. Solids 1995,

189,

77. (165) (166) (167)

Muller, D.; Gessner, W.; Behrens, H.J.; Scheler, G. Chem Phys. Lett. 1981, 79, 59. Mueller, D.; Hoebbel, D.; Gessner, W. Chem. Phys. Lett. 1982, 84, 25. Mueller, D.; Rettel, Α.; Gessner, W.; Scheler, G. J. Magn. Reson. 1984, 57, 152.

(168)

Muller, D.; Gessner, W.; Samoson, Α.; Lippmaa, E . ; Scheler, G. J. Chem. Soc. Dalton

(169) (170) (171) (172) (173) (174) (175) (176) (177)

Trans. 1986, 1277. Muller, D.; Gessner, W.; Samoson, S.; Lippmaa, E., Scheler, G. Polyhedron 1986, 5, 779. Samonson, Α.; Kundla, E.; Lippmaa, E. J. Magn. Reson. 1982, 49, 350. Kundla, E.; Samoson, Α.; Lippmaa, E. Chem. Phys. Lett. 1981, 83, 229. Sanz, J.; Serratosa, J.M. J. Am. Chem. Soc. 1984, 106, 4790. Smith, M . E . Appl. Magn. Reson. 1993, 4, 1. Smith, M . E . Solid-State NMR 1994, 3, 111. Lambert, S.F.; Millman, W.S.; Fripiat, J.J. J. Am. Chem. Soc. 1989, 111, 3517. Alemany, L.B.; Kirker, G W . J. Am. Chem. Soc. 1986, 108, 6158. Gilson, J.P.; Edward, G.C.; Peters, A.W.; Rajagopalan, K.; Worsbecker, R.F.; Roberie, T.G.; Shatlock, M.P. J. Chem. Soc. Chem. Comm. 1987, 91.


126 (178) (179)

Ganapathy, S.; Schramm, S.; Oldfield, Ε. J. Phys. Chem. 1982, 77, 4360. Dec, S.F.; Maciel, G.E. J. Magn. Reson. 1990, 87, 153.

(180)

Alemany, L.B.; Massiot, D.; Sheriff, B.L.; Smith, M . E . ; Taulelle, F. Chem. Phys. Lett. 1991, 177, 301. Samoson, A ; Lippmaa, E . Phys. Rev. B, 1983, 28, 6567. Alemany, L.B. Appl. Magn. Reson. 1993, 4, 170. Alma, N.C.M.; Hayes, R.G.; Samoson, Α.; Lippmaa, E . Anal. Chem. 1984, 56, 729. Alemany, L.B. Appl. Magn. Reson. 1993, 4, 172. Clayden, N.J.; Dobson, C.M.; Groves, G.W.; Hayes, C.J.; Rodger, S.A. Brit. Ceram. Proc. 1984, 35, 55. Clayden, N.J. J. Chem. Soc. 1987, 1877. Skibsted, J.; Jakobsen, H.J.; Hall, C. J. Chem. Soc. Faraday Trans. 1994, 90, 2095. Skibsted, J; Henderson, E . ; Jakobsen, H.J. Inorg. Chem. 1993, 32, 1013. Kunath-Fandrei, G.; Bastow, T.J.; Hall, J.S.; Jäger, C.; Smith, M . E . J. Phys. Chem. 1995, 99, 15138. Fitzgerald, J. J.; Piedra, G.; Dec, S. F.; Seger, M . ; Maciel, G Ε. J. Am. Chem. Soc. 1997, 33, 7832. Piedra, G.; Fitzgerald, J.J.; Ridenour, C.F.; Maciel, G.E. Langmuir 1996, 2, 1958. Piedra, G.; Fitzgerald, J.J.; Dando, N.; Dec, S.F.; Maciel, G.E. Inorg. Chem. 1996, 35, 3474. Walter, T.H.; Oldfield, E . J. Phys. Chem. 1989, 93, 6744. John, C.S.; Alma, N.C.M.; Hays, G.R. Appl. Catal. 1983, 6, 341. Huggins, B.A.; Ellis, P.D. J. Am. Chem. Soc. 1992, 114, 2098. Coster, D.; Blumenfeld, A . L . ; Fripiat, J.J. J. Phys. Chem. 1994, 98, 6201. Kunath, G.; Losso, P.; Schneider, H . ; Steuernagel, S.; J.S.; Jager, C. Solid-State NMR 1992, 1,261. Kraus, H.; Prins, R.; Kentgens, A.P.M. J. Phys. Chem. 1996, 100, 16336. Fernandez, C.; Amoureux, J.P. Chem. Phys. Lett. 1995, 242, 449. Rocha, J.; Esculcas, A.P.; Fernandez, C.; Amoureux, J.P. J. Phys. Chem. 1996,100, 17889. Rocha, J.; Lin, Z.; Fernandez, C.; Amoureux, J,P. Chem. Comm. 1996, 251. Schreiber, L.B.; Vaughan, R.W. J. Catal. 1975, 40, 226. Batusis, L . ; Fyre, J.S.; Maciel, G.E. J. Am. Chem. Soc. 1987, 109, 40. Batusis, L . ; Fyre, J.S.; Maciel, G.E. J. Am. Chem. Soc. 1986, 108, 7119. Segawa, K.; Kurusu, Y . ; Nakajima, Y . ; Kinoshita, M . J. Catal. 1985, 94, 491. Segawa, K.; Nakajima, Y . ; Nakata, S.; Asaaka, S.; Takahashi, T. J. Catal. 1985, 101, 81. Eckert, H. "NMR Spectroscopy of Bulk Oxide Catalysts" in NMR Techniques in Catalysis, Bell, A.T.; Pines, Α., eds. Marcel Dekkar, Inc. New York, 1994. Eckert, H.; Wachs, I.E. J. Phys. Chem. 1989, 93, 6796 Hardcastle, F.D.; Wachs, I.E.; Eckert, H.; Jefferson, D.A. J. Solid-State Chem. 1991, 90, 194. Mastikhin, V . M . ; Lapina, O.B.; Krasilnikov, V.N.; Ivakin, A.A. React. Kinet.Catal.Lett., 1984, 24, 119. Mastikhin, V . M . ; Mudrakovsky, I.L.; Nasov, A.V. Prog. NMR Spetrosc. 1991, 23, 259. Smits, R.H.H.; Seshan, K.; Ross, J.R.H.; Kentgens, A.P.M. J. Phys. Chem. 1995, 99, 169. Edwards, J.C.; Adams, R.D.; Ellis, P.D. J. Am. Chem. Soc. 1990, 112, 8349.


(181) (182) (183) (184) (185) (186) (187) (188) (189) (190) (191) (192) (193) (194) (195) (196) (197) (198) (199) (200) (201) (202) (203) (204) (205) (206) (207) (208) (209) (210) (211) (212) (213)


127 (214)

Edwards, J.C.; Zubieta, J.; Shaikh, S.N.; Chen, Q.; Bank, S.; Ellis, P.D. Inorg. Chem. 1990, 29, 3381.

(215)

Weaver, C.E.; Pollard, L.D. The Chemistry of Clay Minerals, Elsevier Science Publishers, Inc. Netherlands, 1993. Schramm, S.; Kirkpatrick, R.J.; Oldfield, E . J. Am. Chem. Soc. 1983, 105, 2483. Schramm, S.; Oldfield, E . J. Am. Chem. Soc. 1984, 106, 2502. Dec, S.F.; Fitzgerald, J.J.; Frye, J.S.; Shatlock, M.P.; Maciel, G.E. J. Magn. Reson. 1989, 93,403. Fitzgerald, J.J.; Hamza, A.I.; Dec, S.F. Am. Mineral. 1989, 74, 1405. Fitzgerald, J.J.; Hamza, A.I.; Bronnimann, C.E.; Dec, S.F. Solid-State Ionics 1989, 32/33, 368. Fitzgerald, J.J.; Bronnimann, C.E.; Dec, S.F.; Hamza, A . I . J. Am. Chem. Soc. 1997, 119, 7105. Fitzgerald, J.J.; Hamza, A.I.; Dec, S.F.; Bronnimann, C.E. J. Phys. Chem. 1996, 100, 17351. Kolodziejski, W.; Klinowski, J. "New Techniques for the Study of Catalysis", in NMR Techniques in Catalysis, Bell, A.T.; Pines, A . eds., Marcel Dekkar, Inc. New York, 1994. Stebbins, J.F. Am. Mineral. 1996, 9, 1315. Xue, X.; Stebbins, J.F.; Kanzaki, M . Am. Mineral. 1994, 79, 31. Xue, X . ; Stebbins, J.F. Phys. Chem. Min. 1993, 20, 297. Jager, C.; Dupree, R.; Kohn, S.C.; Mortuza, M . G . J. Non-Cryst. Sol. 1993, 155, 95. Timken H.K.C.; Schramm, S.E.; Kirkpatrick, R.J. Oldfield, E . J. Phys. Chem. 1987, 91, 1054. Zhang, P.; Grandinetti, P.J.; Stebbins, J.F. J. Phys. Chem. Β 1997, 101, 4004. Millard, R.L.; Peterson, R.C.; Hunter, B . K . Am. Mineral. 1992, 77, 44. Bank, S.; Bank, J.F.; Ellis, P. J. Phys. Chem. 1989, 93, 4847. Liang, J.J.; Sherrif, B.L. Geochim. et. Cosmochimica. 1993, 57, 3885. Bank, J.F.; Ofori-Okai, G.; Bank, S. Clay and Clay Minerals, 1993, 41, 95. Laperche, V . ; Lambert, J.F.; Frost, R.; Fripiat, J.J. J. Phys. Chem. 1990, 94, 8821. Weiss, C.A.; Kirkpartrick, R.J.; Altaner, S.P. Geochim. Cosmochim. Acta. 1990, 54, 1655. Wilson, S.T., Lok, B . M . ; Messina, C.A.; Cannan, T.R.; Flanigen, E . M . J. Am. Chem. Soc. 1982, 104, 1146. MacLachlan, D.J.; Morgan, K.R. J. Phys. Chem. 1990, 94, 7656. Davies, M . E . ; Murray, B.D.; Narayana, M . in Novel Materials in Heterogeneous Catalysis, A C S Symposium, Series 437, Baker, R.T.K.; Murrell, L . L . , eds. A C S Books, New York, 1990. Barrie, P.J.; Klinowski, J. J. Phys. Chem. 1989, 93, 5972. Szostak, R. Molecular Sieves, Van Nostrand, Reinhold, New York, 1989. Grobet, P.J.; Martens, J.A.; Balakrishnan, I.; Mertens, M . ; Jacobs, P.A. Appl. Catal. 1989, 56, L21. Tanev, P.T.; Chibwe, M ; Pinnavaia, T.J. Nature 1994, 368, 321. Zhang, W.; Froba, M.; Wang, J.; Tanev, P.T.; Wong, J.; Pinnavaia, T.J. J. Am.Chem. Soc. 1996, 118, 9164. Bortun, A.I.; Bortun, L.N.; Clearfield, A. Chem. Mater. 1997, 9, 1854. Poojary, D . M . ; Bortun, A.I.; Bortun, L . N . ; Clearfield, A. Inorg. Chem. 1996, 35, 6131.

(216) (217) (218) (219) (220)


(221) (222) (223) (224) (225) (226) (227) (228) (229) (230) (231) (232) (233) (234) (235) (236) (237) (238)

(239) (240) (241) (242) (243) (244) (245)


128

(246) (247) (248) (249) (250) (251)


(252) (253) (254) (255) (256) (257) (258) (259) (260) (261) (262)

(263) (264)

(265)

(266) (267)

(268)

Clerici, M . G . ; Bellussi, G.; Romano, U . J. Catal. 1991, 129, 159. Huybrechts, D.R.C.; DeBruycker, L . ; Jacobs, P.A. Nature 1990, 345, 240. Sankar, G.; Rey, F.; Thomas, J.M; Greaves, G.N.; Corma, A . C . ; Dobson, B.R.; Dent, A.J. J. Chem. Soc. Chem. Comm. 1994, 2279. Serrano, O.P.; Uguina, M . A . ; Ovejero, G.; Van Grieken, R.; Camacho, M . Chem. Comm. 1996, 1097. Anderson, M.W.; Terasaki, O.; Ohsuna, T.; Phillippou, Α.; MacKay, S.P.; Ferreira, Α.; Jocha, J.; Lidin, S. Nature 1994, 367, 347. Kingery, W.D.; Bowen, K.H.; Wholman, D.R. Introduction to Ceramics, 2nd Ed., John Wiley, New York, 1975. Ichinose, N . Introduction to Fine Ceramics, John Wiley and Sons, New York, 1987. Buchanan, R. ed., Ceramic Materials for Electronics, Marcel Dekkar, Inc. New York, 1986. Lines, M . E . ; Glass, A . M . Principles and Applications of Ferroelectric and Related Materials, Clarendon Press, Oxford, 1977. Jona, F.; Shirane, G. Ferroelectric Crystals, Dover Publishers, Inc. New York, 1993. Hench, L . L . ; Ulrich, D.R., eds. Ultrastructure Processing of Ceramics, Glasses, and Composites, Wiley-Interscience, New York, 1984. Hench, L . L . ; Ulrich, D.R., eds. Science of Ceramic Chemical Processing, Wiley-Interscience, New York, 1986. Pask, J.; Evans, Α., eds. Surfaces and Interfaces in Ceramics, Materials Science Research, Volume 14, Plenum Press, New York, 1980. Thompson, D.P. Nitrogen Ceramics, Riley, F.L. ed., Noordhoff, Leyden, 1977. Jack, K . H . Progress in Nitrogen Ceramics, Riley, F.L. ed., Martinus, Nijhoff, 1983. Jack, K . H . Mat. Sci. 1976, 11,1135. Thompson, D.P. "Nitride Ceramics," in Tailoring Multiphase and Composite Ceramics, Tressler, R.E.; Messing, G.L; Pantono, C.G; Newnham, R.G. eds., Plenum, New York, 1986. Turner, G. L . ; Kirkpatrick, R. T.; Risbud, S. H . ; Oldfield, E. Am. Ceram. Soc. Bull 1987, 66, 656. Bray, P.J; Gravine, J.S. " N M R of Ceramics", in Ultrastruct. Pro. Ceram.Glasses, (Proc. Internatl. Conf), Hench, L . L . ; Ulrich, D.R. eds., Wiley-Interscience, New York, 1984. Dupree, R. "NMR Studies of Glasses and Ceramics", in Nuclear Magnetic Resonance in Modern Technology, Maciel, G.E. ed., N A T O ASI Series, Vol. 447, Kluwer Academic Publishers, Dordrecht, Netherlands, 1994. Kemiya, K. Preparation of Oxide Glasses From Metal Alkoxides By Sol-Gel Method, N A S A , Washington, D.C. 1987. Kirkpatrick, R.J.; Dunn, T.; Schramm, S.; Sinter, K . A . ; Oestrike, R. Turner, G. "Magic-Angle Sample Spinning N M R Spectroscopy of Silicate Glasses", in Structure and Bonding Noncrystalline Solids, Walrafer, G.E.; Revesz, A.G. eds., Plenum Press, New York, 1986. Pye, L . D . ; Frechette, V . D . ; Kreidl, N.J. eds., Boron in Glass and Glass Ceramics, Materials Science Research, Volume 12, Plenum Press, New York, 1978.


129

(269) (270) (271) (272) (273) (274) (275)


(276) (277) (278) (279) (280) (281) (282) (283) (284) (285) (286) (287) (288) (289) (290) (291) (292) (293) (294) (295) (296) (297) (298) (299) (300) (301) (302)

Dupree, R.; Holland, D.; Mortuza, M . G . ; Collin, J.A.; Lockyer, M . W . G . J. Non-Cryst. Sol. 1989, 112, 111. Dupree, R.; Holland, D.; Mortuza, M . G . ; Collin, J.A.; Lockyer, M.W.G. J. Non-Cryst. Sol. 1988, 106, 403. Dupree, R.; Holland, D.; Williams, D. S. J. De Physique 1985, 46, 119. Dupree, R.; Holland, D.; McMillan, P.W.; Pettifer, R.F. J. Non-Cryst.Sol.1984, 68, 399. Dupree, R.; Holland, D.; Mortuza, M.G. Phys. Chem. Glasses 1988, 29,18. Dupree, R.; Gencten, Α.; Paul, D . M . Physica C. 1992, 193, 81. Carduner, K.R.; Shinozaki, S.S.; Rokosz, M.J.; Peters, C.R.; Whalen, T.J. J. Am. Ceram. Soc. 1990, 73, 2281. MacKenzie, K.J.D.; Meinhold, R . H . ; McGavin, D.G.; Ripmeester, J.A.; Moudrakovski, I. Solid-State NMR 1995, 4, 193. Brow, R.K.; Kirkpatrick, R.J.; Turner, G.L. J . Non-Cryst. Sol. 1990, 116, 39. Xue, X . ; Stebbins, J.F. Phys. Chem. Min. 1993, 20, 297. Sato, R.K.; McMillan, P.F.; Denison, P.; Dupree, R. J. Phys. Chem. 1991, 95, 4483. Dupree, R.; Holland, D.; Mortuza, M.G. Nature 1987, 328, 416. Schramm, C.M.; de Jong, B.H.W.S.; Parziale, V . E . J. Am. Chem. Soc. 1984, 106, 4396. Schramm, S.; Oldfield, E . J. Am. Chem. Soc. 1984, 106, 2502. Turner, G.L.; Chung, S.E.; Oldfield, E . J. Magn. Reson. 1985, 64, 316. Jager, C.; Dupree, R.; Kohn, S.C.; Mortuza, M . G . J. Non-Cryst. Sol. 1993, 155, 95. Forbes, C . E . ; Hammond, W.B.; Cipollina, N.E.; Lynch, J.F. J. Chem. Soc. Chem. Comm. 1987, 6, 433. Xue, X.; Stebbins, Kanzaki. M . Am. Mineral 1994, 79, 31. Maekawa, H . ; Florian, P.; Massiot, D.; Kiyono, H . ; Nakamura, M . E . J. Phys. Chem. 1996, 100, 5525. Florian, P.; Vermillion, K . E . ; Grandinetti, P.J.; Farnan, I.; Stebbins, J.F. J. Am. Chem. Soc. 1996, 118, 3493. Soroka, I. Portland Cement Paste and Concrete, Chemical Publishing Co., Inc. New York, 1980. Turner, G.L.; Chung, S.E.; Oldfield, E . J. Magn. Reson. 1985, 64, 316. Yang, S.; Park, K.D.; Oldfield, E . J. Am. Chem. Soc. 1985, 111, 7278. Dirken, P.J.; Dupree, R.; Smith, M . E . Mater. J. Chem. 1995, 5, 1261. Bastow, T.J.; Stuart, S.N. Chem. Phys. 1990, 143, 459. Bastow, T.J.; Hobday, M . E . ; Smith, M . E . ; Whitfield, H.J. Solid-State NMR 1996, 5, 293. Bastow, T.J. J. Phys. Condens. Mat. 1989, 1, 4985. Kanert, O.; Schulz, H.; Albers, J. J. Solid State Comm. 1994, 91, 464. Bastow, T.J.; Smith, M . E . Solid-State NMR 1992, 1, 165. A l i , F.; Smith, M.E.; Steuernagel, S.; Whitfield, H.J. J. Mater. Chem. 1996, 6, 216. Bastow, T.J.; Smith, M . E . ; Whitfield, H.J. J. Mater. 1996, 6, 1951. Bastow, T.J.; Hobday, H.E.; Smith, M . E . ; Whitfield, H.J. Solid-State NMR. 1996, 5, 293. Geissberger, A . E . ; Bray, P.J. J. Non-Cryst. Sol. 1983, 54, 121. Zhao, P.; Prasad, S.; Benjamin, M . ; Huang, J; Fitzgerald, J.J.; Shore, J. "Lead-207 N M R Spectroscopic Study of Piezoelectric Lead Magnesium Niobate and Related Materials." Rocky Mountain Conference on Analytical Chemistry, Aug., 1997.


130 (303) (304) (305) (306) (307) (308) (309) (310)


(311) (312) (313) (314) (315) (316)

(317) (318) (319) (320) (321) (322) (323) (324) (325) (326) (327)

Massiot, D.; Conanec, R.; Feldman, W.; Marchand, R.; Laurent, Y . Inorg. Chem. 1996, 35, 4957. Hanna, J.V.; Smith, M . E . ; Whitfield, H.J. J. Am. Chem. Soc. 1996, 118, 5772. Walter, T . H ; Turner, G.L.; Oldfield, E . J. Magn. Reson. 1988, 76, 106. Roller, H . ; Engelhardt, G.; Kentgens, A.P.M.; Sauer, J. J. Phys. Chem. 1994, 98, 1544. Roller, H . ; Engelhardt, G.; Felsche, J. Z. Anorg. Allg. Chem. 1995, 621, 301. Dec, S.F.; Maciel, G.E.; Fitzgerald, J.J. J. Am. Chem. Soc. 1990, 112, 9069. Maekawa, H . ; Florian, P.; Massiot, D.; Riyono, H . ; Nakamura, M . J. Phys. Chem. 1996, 100, 5 525. Newnham, R.E. "Tunable Transducers: Nonlinear Phenomena in Electroceramics", in Chemistry of Electronic Materials (NIST Special Publication 804), 1990, p. 39. Cross, L . E . Ferroelectrics 1987, 76, 241. Dec, S.F.; Davis, M.F.; Maciel, G.E.; Bronnimann, C.E.; Fitzgerald, J.J.; Han, S. Inorg. Chem. 1993, 32, 955. Fayon, F.; Farnon, I.; Bessada, C.; Coutures, J.; Massiot, D.; Coutures, J.P. J. Am. Chem. Soc. 1997, 119, 6837. Neue, G.; Dybowski, C.; Smith, M . L . ; Hepp, M . A . ; Perry, D.L. Solid-State NMR, 1996, 6, 241. Youngman, R.E.; Hanbrick, S.T.; Zwanziger, J.W.; Janicke, M.T.; Chmelka, B.F. Science, 1995, 269, 1416. Prasad, S.; Zhao, P.; Huang, J.; Fitzgerald, J.J.; Shore, J. "Niobium-93 Nutation Spectroscopic Study of Piezoelectric Lead Magnesium Niobate and Related Materials** Rocky Mountain Conference on Analytical Chemistry, Aug., 1997. Marchetti, P.S.; Rwon, D.; Schmidt, W.R,; Interrante, L . V . ; Maciel, G.E. Chem. Mater. 1990, 3, 482. Finlay, G.R.; Hartman, J.S.; Richardson, M . F . ; Williams, B . L . J. Chem. Soc. Chem. Commun. 1985, 159. Wenslow, R . M . ; Mueller, K.T. In press, 1998. Hartman, J.S.; Richardson, M.F.; Sherriff, B.L.; Winsbarrow, B . G . J. Am. Chem. Soc. 1987, 109, 6059. Inkrott, R.E.; Wharry, S.M.; O'Donnell, D.J. Mater. Res. Soc. Symp. Proc. 1986, 23, 165. Marshall, G.L.; Harris, R.R.; Apperly, D.; Yeung, R. Sci. Ceram. 1988, 14, 347. Lipowitz, J.; Turner, G.L. Polym. Prepr. 1989, 29, 74. Seyferth, J.; Strohmann, C.; Dando, N R . ; Perrotta, A.J. Chem. Mater. 1995, 7, 2058. Seitz, J.; Bill, J.; Egger, N.; Aldinger, F. J. Eur. Ceram. Soc. 1996, 16, 885. Schmidt, W.R.; Interrante, L.V.; Doremus, R.H.; Trout, T.K.; Marchetti, P.S.; Maciel, G.E. Chem. Mater. 1991, 3, 257. Narsavage, D . M . ; Interrante, L . V . ; Marchetti, P.S.; Maciel, G.E. Chem. Mater. 1991, 3,

721. (328) (329) (330) (331) (332)

Dybowski, C.; Gaffney, E.J.; Sayir, Α.; Rabinowitz, M.R. Colloids and Surf. 1996, 118, 171. Shinozak, S.S.; Carduner, K.R. Trans. Mater. Res. Soc. Jpn. A 1994, 14, 857. McRenzie, R.J.D.; Meinhold, R.H.; Brown, I.W.; White, G.V. J. Mater. Sci. 1994, 29, 5631. Carduner, K.R.; Carter, R.O.; Milberg, M . E . ; Crosbie, G . M . Anal. Chem. 1987, 59, 2794. Carduner, K.R.; Carter, R.O.; Rokosz, M.R.; Peters, C.; Crosbie, G . M . ; Stiles, E.D. Chem. Mater. 1989, 1, 302.


131 (333)


(334) (335) (336) (337) (338) (339) (340) (341) (342) (343) (344) (345) (346) (347) (348) (349) (350) (351) (352) (353) (354) (355) (356) (357) (358) (359) (360) (361) (362) (363) (364) (365) (366) (367)

Hatfield, G.; L i , Β.; Hammond, W.B.; Reidinger, F.; Yamanis, J. J. Mater.Sci.1992, 25, 4032. Carduner, K.R.; Blackwell, C.S.; Hammond, W.B.; Reidinger, F.; Hatfield, G.R. J. Am. Chem. Soc. 1990, 112, 4676. Zhang, M . ; Maciel, G. Anal. Chem. 1990, 62, 633. Olivieri, Α.; Hatfield, G. J. Magn. Reson. 1991, 94, 535. Harris, R.K.; Leach, M . ; Thompson, D.P. Chem. Mater. 1989, 1, 336. Harris, R.K.; Leach, M.J.; Thompson, D.P. Chem. Mater. 1990, 2, 320. Harris, R.K.; Leach, M.J. Chem. Mater. 1992, 4, 261. Harris, R.K.; Leach, M . J. J. Am. Chem. Soc. 1992, 4, 2, 260. Smith, M . E . J. Phys. Chem. 1992, 96, 1444. Dupree, R.; Lewis, M . H . ; Smith, M . E . J. Amer. Chem. Soc. 1989, 111, 5125. Kwon, D.; Schmidt, W.R.; Interrante, L . V . ; Maciel, G.E. Chem. Mater. 1191, 3, 482. Interrante, L . V . ; Schmidt, W.R.; Marchetti, P.; Maciel, G.E. Proc. Symp. Inorg. Polym. Montreal, Canada, 1990. Schmidt, W.R.; Interrante, L . V . ; Doremus, R.H.; Trout, T.K.; Marchetti, P.; Maciel, G.E. Chem. Mater. 1991, 3, 257. Dupree, R.; Lewis, M . H . ; Smith, M . E . J. Am. Chem. Soc. 1988, 110, 1083. Butler, D.; Dupree, R.; Lewis, M . H . J. Mater.Sci.Lett. 1984, 3, 469. L i , H . ; Butler, I.S.; Denis, F.R.; Harrod, J.F.; Morin, F.G. J. Phys. Chem. 1995, 99, 8490. Carduner, K.R.; Blackwell, C.S.; Hammond, W.B.; Reidinger, F.; Hatfield, G.R. J. Am. Chem. Soc. 1990, 112(12), 4676. Sjoeberg, J.; Harris, R.K.; Apperly, D . C . J. Mater. Chem. 1992, 2, 433. Nordmann, Α.; Cheng, Y.B.; Smith, M . E . Chem. Mater. 1996, 8, 2516. MacKenzie, K.J.D.; Meinhold, R.H. J. Mater. Chem. 1994, 4, 1595. Fitzgerald, J.J.; Kohl, S.D.; Piedra, G.; Dec, S.F.; Maciel, G.E. Chem. Mater. 1994, 6, 1915. Massiot, D.; Conanec, R.; Feldman, W.; Marchand R.; Laurent, Y . Inorg. Chem. 1996, 35, 4957. Bastow, T.J.; Dirken, P.J.; Smith, M . E . J. Phys. Chem. 1996, 100, 18539. Whitmarsh, C.W.; Sherwood, W.; Wu, H.J.; Lewis, R.; Maciel, G.E. Mater. Res. Soc. Symp. Proc. 1994, 346, 593. Weller, M.T.; Brenchley, M . E . ; Apperly, D.C.; Davies, N.A. Solid-State NMR 1994, 3, 103. Bastow, T.J.; Dirken, P.J.; Smith, M . E . ; Whitfield, H.J. J. Phys. Chem. 1996, 100, 18539. Dirken, P. J.; Smith, M . E . ; Whitfield, H. J. J. Phys. Chem. 1995, 99, 395. Cong, X.; Kirkpatrick, R.J. Cement and Concrete Res. 1993, 23, 1065. Cong, X.; Kirkpatrick, R.J. J. Am. Ceram. Soc. 1996, 79, 158. Holland, D.; Lockyer, M.W.G.; Dupree, R. Br. Ceram. Proc. 1996, 55, 145. Lockyer, M.W.G.; Holland, D.; Dupree, R. J. Non-Crys. Sol. 1995, 188, 207. Aue, W.P.; Roufosse, A . H . ; Glimcher, M.J.; Griffin, R.G. Biochem. 1984, 23, 6110. Rothwell, W.P.; Waugh, J.S.; Yesinowski, J.P. J. Am. Chem. Soc. 1980, 102, 2637. Hinedi, Z.R.; Goldberg, S.; Chang, A.C.; Yesinowski, J.P. J. Coll Interf.Sci.1992, 152, 141. Sarkar, G.; Fitzgerald, J.J. S i and P CP/MAS N M R Studies of the Interfacial Interactions of Bioglass Materials", Rocky Mountain Conference on Analytical Chemistry, Aug., 1997. ,,29

31


132 (368) (369) (370)

(371)


(372) (373) (374) (375) (376) (377) (378) (379) (380) (381) (382) (383) (384) (385)

(386) (387) (388) (389) (390) (391) (392) (393) (394) (395) (396)

Wu, Y . ; Glimcher, M.J.; Rey, C.; Ackerman, J.L. J. Mol. Biol. 1994, 244, 423. Janicke, M.T.; Landry, C.C.; Christianson, S.C.; Kumar, D.; Stucky, G.D.; Chemlka, B . F. J. Am. Chem. Soc. 1998, 120, 6940. Knights, J.C., in The Physics of Hydrogenated Amorphous Silicon. I. Structure, Preparation and Devices, Joannopoulos, J.D.; Lucovsky, G . eds. Springer-Verlag, New York, 1984. Taylor, P.C., "Semiconductors and Semimetals", Vol. 21, Part C, in Hyrogenated Amorphous Silicon. Electronic and Transport Properties, Pankove, J.I.; ed. Academic Press, New York, 1984, and references therein. Boshah, K . ; Zamir, D.; Becla, P.; Wolff, P.A.; Griffin, R.G. Phys. Rev. B. 1987, 36, 6420. Tolbert, S.H.; Firouz, Α.; Stucky, G.D.; Chmelka, B.F. In press, 1998. Han, O.H.; Timken, H.K.C.; Oldfield, E . J. Chem. Phys. 1988, 89, 6046. Ryan, M . A . ; Peterson, M.W.; Williamson, D.L.; Frye, J.S.; Maciel, G.E.; Parkinson, B. A. Mater. J. Res. 1987, 2, 528. Tycko, R.; Dabbagh, G . ; Kurtz, S.R.; Goral, J.P. Phys. Rev. B. 1992, 54, 13452. Franke, D.; Banks, K . ; Eckert, H . J. Phys. Chem. 1992, 96, 11048. Franke, D.; Maxwell, R.; Lathrop, D.; Banks, K.; Eckert, H . Phys. Rev. Β 1992, 46, 8109. Williams, G.V.; Talion, J.L.; Michalak, R.; Dupree, R. Phys. Rev. B. Condens. Mat. 1996, 54, R6909. Franke, D.; Hudalia, C; Maxwell, R.; Eckert, H . J. Phys. Chem. 1996, 19, 7506. Adler, S.B.; Reimer, J.A.; Baltisberger, J.; Werner, U . J. Am. Chem. Soc. 1994, 116, 675. Oldfield, E.; Coretsopoulas, C.; Yang, S.; Reven, L . ; Shore, J.; Han, O. H.; Ramli, E . ; Hinks, D . G Phys. Rev. B. 1989, 40, 6832. Coretsopoulas, C.; Lee, H.C.; Ramli, E . ; Reven, L . ; Rauchfuss, T.B.; Oldfield, E . Phys. Rev. B. 1989, 39, 781. Reven, L . ; Shore, J.; Yang, S.; Duncan, T.; Schwartz, D.; Chung, J.; Oldfield, E . Phys. Rev. B. 1991, 43, 10466. Pennington, C.H.; Slichter, C.P. "Nuclear Resonance Studies of Y B a C u O " , in Physical Properties of High-Temperature Superconductors II, Ginsberg, D . M . ed., World Scientific, Singapore, 1990. Howes, A.P.; Dupree, R.; Han, Z.P.; Liu, R.S.; Edwards, P.P. Phys. Rev. B. 1993, 47, 11529. G.P.; Martins, J.L.; Zunger, A. Phys. Rev. B. 1985, 31, 2561. Hull, D. in Introduction to Composite Materials, Cambridge University Press, Cambridge, England, 1981. "Ceramic Matrix Composites" in Composites 1987, 18, 88. Peters, P.W.M.; Chou, T.W. Composites 1987, 18, 40. Bergstrom, L . ; Pugh, R.J. J. Am. Ceram. Soc. 1989, 72, 103. Rice, R.W. Ceram. Eng. and Sci. Proc. 1981, 7-8, 661. Buljan, S T . ; Sarin, V . K . Composites 1987, 18, 92. Lundberg, R.; Nyberg, B.;Williender, K.; Persson, M . ; Carlsson, R. Composites 1987, 18, 125. Sarin, V . K . ; Ruhle, M . Composites 1987, 18, 129. Crimp, M.J.; Johnson, Jr., R.E.; Halloran, J.W.; Feke, D.L. "Colloidal Behavior of Silicon Carbide and Silicon Nitride," in Science of Ceramic Chemical Processing, Hench, L . L . ; Ulrich, D.R. eds., Wiley, New York, 1986. 2

3

7-X


133

(397) (398)

Turan, S.; Knowles, Κ. J. Am Ceram. Soc., 1996, 79, 2892. Xu, X . ; Holmes, J.W.; Hilmas, G.E. Handb. Contin. Fiber-Reinf. Ceram. Matrix Compos. 1995, 431.

(399) (400)

Vicens, J.; Doreau, F.; Chermant, J.L. J. Microsc. 1995, 177, 242. Huang, C.M.; Zhu, D.; X u , Y . ; Kriven, W . M . ; Chao, C.Y. Mater. Sci. Eng. A 1996, 220, 176. Bronsveld, P . M . ; Gideonse, I.; Van der Heide, Α.; Guder, S.; De Hosson, J.H.M.; Sabouret, E . ; X u , X . ; Holmes, J.M.; Hilmas, G.E. Handb. Contin. Fiber-Reinf. Ceram. Matrix Compos. 1995, 431.

(401)


(402) (403) (404) (405) (406) (407) (408) (409)

Razzell, A.G.; Lewis, M . H . J. Microsc. 1993, 169, 215. Lee, K . N . ; Jacobson, N.S.; Miller, R.A. Refractory Oxide Coatings on Silicon Carbide Ceramics, N A S A , Washington, D.C., 1994. Roychem, J.; Zhang, S.; For, W.T. Macromol. 1996, 29, 1305. Koeniz, J.L. Polym. Compos. 1990, 11, 121. Weeding, T . L . ; Veeman, W.S.; Jenneskens, L . W . ; Gaur, H.A.; Schuurs, H . E . C . ; Huysmans, W . G B. Macromol. 1989, 22, 206. Corey, R.L.; Curro, N.J.; O'Hara, K.; Imai, T.; Slichter, C.C.; Yashimura, K.; Katoh, M . ; Kosuge, K . Phys. Rev. Β Condens. Mat. 1996, 53, 5907. Han, Z.P.; Dupree, R.; Gencten, Α.; Lui, R.S.; Edwards, P.P. Phys. Rev. Lett. 1992, 69, 1256. Imai, T.; Slichter, C.P.; Cobb, J.L.; Markert, J.T. J. Phys. Chem. 1995, 56, 1921.