Stability, Composition, and Core–Shell Particle Structure of Uranium

Uranium is typically the most abundant radionuclide by mass in radioactive wastes and is a significant component of effluent streams at nuclear facili...
0 downloads 0 Views 646KB Size
Subscriber access provided by - Access paid by the | UCSB Libraries

Environmental Processes

Stability, composition and core-shell particle structure of uranium(IV)-silicate colloids Thomas Samuel Neill, Katherine Morris, Carolyn I. Pearce, Nicholas K. Sherriff, M. Grace Burke, Philip Chater, Arne Janssen, Louise S. Natrajan, and Samuel Shaw Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.8b01756 • Publication Date (Web): 12 Jul 2018 Downloaded from http://pubs.acs.org on July 16, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 35

Environmental Science & Technology

1

Stability, composition and core-shell particle

2

structure of uranium(IV)-silicate colloids

3

Thomas S. Neill‡, Katherine Morris‡, Carolyn I. Pearce§, Nicholas K Sherriff⊥, M. Grace

4

Burke†, Philip A. Chater+, Arne Janssen†+, Louise Natrajan# and Samuel Shaw‡*

5



Research Centre for Radwaste and Disposal, Williamson Research Centre, The University of Manchester, Oxford Road, Manchester M13 9PL, UK

6

§

7



8

Pacific Northwest National Laboratory, Richland, WA 99354, USA

National Nuclear Laboratory, Chadwick House, Warrington Road, Birchwood Park, Warrington WA3 6AE, UK

9



10

Materials Performance Centre, The University of Manchester, Oxford Road, Manchester M13 9PL, UK

11

#

12

School of Chemistry, The University of Manchester, Oxford Road, Manchester M13 9PL, UK

13

14

+

Diamond Light Source, Harwell Campus, Didcot, Oxfordshire, OX11 0DE, UK

15

KEYWORDS Colloids, uranium(IV), core-shell, uranium silicate, nuclear fuel storage,

16

EXAFS, SAXS

1 ACS Paragon Plus Environment

Environmental Science & Technology

Page 2 of 35

17

18

ABSTRACT

19

Uranium is typically the most abundant radionuclide by mass in radioactive wastes and is a

20

significant component of effluent streams at nuclear facilities. Actinide (IV) (An(IV))

21

colloids formed via various pathways, including corrosion of spent nuclear fuel, have the

22

potential to greatly enhance the mobility of poorly soluble An(IV) forms, including uranium.

23

This is particularly important in conditions relevant to decommissioning of nuclear facilities

24

and the geological disposal of radioactive waste. Previous studies have suggested that silicate

25

could stabilise U(IV) colloids. Here the formation, composition and structure of U(IV)-

26

silicate colloids under the alkaline conditions relevant to spent nuclear fuel storage and

27

disposal were investigated using a range of state of the art techniques. The colloids are

28

formed across a range of pH conditions (9-10.5) and silicate concentrations (2-4 mM) and

29

have a primary particle size 1-10 nm, also forming suspended aggregates < 220 nm. X-ray

30

absorption spectroscopy, ultrafiltration and scanning transmission electron microscopy

31

confirm the particles are U(IV)-silicates. Additional evidence from X-ray diffraction and pair

32

distribution function data suggests the primary particles are composed of a UO2-rich core and

33

a U-silicate shell.

34

U(OH)3(H3SiO4)3-2 complexes in solution indicating they are likely particle precursors.

35

Finally, these colloids form under a range of condition relevant to nuclear fuel storage and

U(IV)-silicate colloids formation correlates with the formation of

2 ACS Paragon Plus Environment

Page 3 of 35

Environmental Science & Technology

36

geological disposal of radioactive waste and represent a potential pathway for U mobility in

37

these systems.

38

TEXT

39

INTRODUCTION

40

Uranium (U) is the most abundant radionuclide by mass in both the nuclear fuel cycle and

41

many higher activity radioactive waste inventories1. Its mobility in engineered and

42

environmental systems is a major concern in a range of scenarios, including waste storage

43

systems (e.g. nuclear fuel storage ponds), contaminated land and geodisposal facilities. The

44

speciation of U is key to controlling its mobility and therefore informing effluent

45

treatment/remediation options. Of particular importance is the oxidation state of U. U(VI),

46

typically present in aqueous systems as uranyl UO22+, is relatively soluble, particularly in the

47

presence of carbonate2. By contrast, U(IV) is poorly soluble under the anoxic and neutral-

48

basic pH conditions expected in radioactive waste storage/disposal and contaminated land

49

scenarios3,4 and is often present as UO2(s)5,6 or non-crystalline U(IV)7–9 in anoxic systems.

50

This means U is considered to be immobile under reducing conditions. Therefore, reduction

51

from soluble U(VI) to U(IV), either biotically10,11 or abiotically12, is seen as a possible

52

immobilization mechanism for U in environmental and waste treatment systems. However,

53

studies have highlighted that colloids can mobilise actinides in a range of scenarios13–16.

54

These include interim storage facilities at sites such as Sellafield, UK, where legacy spent

55

fuel storage ponds are maintained at a high pH and where colloids are present17–20.

56

Additionally, colloids have the potential to mobilize radionuclides in geodisposal facilities21,

57

at nuclear weapons testing sites13, U mine drainage sites22, and during ore deposit

58

formation23,24. It is therefore important to have a detailed understanding of the formation, 3 ACS Paragon Plus Environment

Environmental Science & Technology

Page 4 of 35

59

composition, structure and surface properties of colloidal U(IV) species under relevant

60

(geo)chemical conditions to assess their impact on U speciation and mobility in a range of

61

natural and engineered environments. Despite significant research into colloidal transport of

62

radionuclides, U colloid formation and stability mechanisms are poorly constrained. There is

63

a particular scarcity of knowledge under alkaline, anoxic conditions relevant to spent nuclear

64

fuel storage25 and long term geodisposal26.

65

The formation of U oxide colloids at acidic pH has been well established for both U(IV)27

66

and U(VI)28. Under environmentally relevant anoxic, circumneutral pH conditions, UO2

67

colloids have been shown to form during anaerobic corrosion of spent nuclear fuel21. The

68

resultant colloidal particles were < 250 nm and showed resistance to oxidation, persisting for

69

70 days during exposure to air before oxidation to U(VI)-silicate

70

K2(UO2)2Si6O15·4H2O). In addition, colloidal U(IV)-silicate nanoparticles have been shown

71

to form under anoxic conditions at pH 6.9-9.529 similar to those within radioactive waste

72

storage and disposal environments. The nanoparticles, 1 mM)30,31. Furthermore, recent studies suggest that the

79

presence of U(IV)-silicate solution complexes and colloids are essential precursors to

80

coffinite formation32,33. Understanding the formation of U(IV)-silicate species is therefore

81

essential to understanding U(IV)-silicate mineral formation as well as U(IV) mobility. U

82

silicate solution complexes have also been observed within groundwaters at the underground

83

research laboratory in Horonobe, Japan34. Here, U was associated with low molecular weight

(weeksite,

4 ACS Paragon Plus Environment

Page 5 of 35

Environmental Science & Technology

84

polysilicates in saline groundwaters from 500 m depth providing field based evidence that

85

U(IV)-silicate solution species and/or nanoparticles have the potential to enhance U(IV)

86

mobility in anoxic systems.

87

Studies of actinide(IV) (An(IV)) silicate colloids have found that Th(IV) and Np(IV)

88

silicate colloids can form under similar condition to those favoring U(IV)-silicate colloid

89

formation35–37. X-ray photoelectron spectroscopy (XPS) of Th(IV)-silicate particles suggested

90

that the structure of the individual nanoparticles may not be homogeneous, with evidence for

91

silica enrichment at the particle surface under initially elevated Si concentrations. Enrichment

92

of silicate on the surface of An(IV) particles (where An = U, Th, Np) is thought to stabilize

93

the colloidal nanoparticles via increasing the charge and reducing the hydrophobicity of the

94

particle surface37. This mechanism of stabilization has also been observed for other silicate

95

containing colloidal systems including Fe(III) hydrolysis products38 and amorphous calcium

96

carbonate where silica was observed at the particle surface39. Overall, An(IV)-silicate

97

nanoparticles have been reported across a range of systems, and may have a significant

98

impact on An(IV) mobility in reducing engineered and natural environments where actinides

99

and elevated Si concentrations exist (e.g. groundwater). Information on the formation,

100

composition, structure and stability of U(IV)-silicate phases and colloids at conditions

101

relevant to interim spent nuclear fuel storage and geodisposal of radioactive waste (i.e. pH

102

>10) is crucial to predicting the long term mobility and fate of An(IV) in natural and

103

engineered systems.

104

In this study we have characterized U(IV)-silicate colloids at a range of silicate

105

concentrations and high pH conditions ([Si] 0-4 mM, pH 9-12) relevant to spent nuclear fuel

106

storage and radioactive waste disposal. This was achieved using a multi-technique approach

107

to determine the size, stability and structure of the colloidal nanoparticles. Here, a

108

combination of ultrafiltration, small angle X-ray scattering (SAXS), dynamic light scattering 5 ACS Paragon Plus Environment

Environmental Science & Technology

Page 6 of 35

109

(DLS), zeta potential analysis, scanning transmission electron microscopy (STEM), extended

110

X-ray absorption fine structure (EXAFS) spectroscopy, powder X-ray diffraction (XRD) and

111

X-ray Pair Distribution Function (PDF) provided unprecedented atomic to nanoscale insight

112

into properties of U(IV)-silicate colloids. Results show the U(IV) colloids consisted of

113

particles