Effect of Anodic Aluminum Oxide Chemistry on Adhesive Bonding of

Aug 15, 2016 - Adhesive bonding is one of the oldest techniques used to join different components.(1) This type of structure is formed when an adhesiv...
1 downloads 0 Views 2MB Size
Subscriber access provided by Northern Illinois University

Article

The Effect of Anodic Aluminum Oxide Chemistry on Adhesive Bonding of Epoxy Shoshan Tamar Abrahami, Tom Hauffman, John M.M. de Kok, Johannes M. C. Mol, and Herman Terryn J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.6b04957 • Publication Date (Web): 15 Aug 2016 Downloaded from http://pubs.acs.org on August 20, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry C is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

The Effect of Anodic Aluminum Oxide Chemistry on Adhesive Bonding of Epoxy Shoshan T. Abrahami 1,2, Tom Hauffman 3, John M.M. de Kok 4, Johannes M.C. Mol 2 and Herman Terryn 2,3 * 1

Materials innovation institute (M2i), Elektronicaweg 25, 2628 XG, Delft, The Netherlands

2

Delft University of Technology, Department of Materials Science and Engineering, Mekelweg 2, 2628 CD, Delft, The Netherlands 3

Department of Materials and Chemistry, Research Group Electrochemical and

Surface Engineering (SURF), Vrije Universiteit Brussel, Pleinlaan 2, 1050 Brussels, Belgium 4

Fokker Aerostructures BV, Industrieweg 4, 3351 LB, Papendrecht, The Netherlands

*Corresponding author: [email protected]; Tel +3226293537; Fax: +3226293200

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT

The transition to Cr(VI)-free production is a great challenge in the global aerospace industry that currently still relays on it for the preparation of aluminum for bonding. Proper surface pretreatment is a prerequisite for strong and durable adhesive joint. Despite decades of experience, the nature and contribution of the different adhesion forces between the aluminum and organic adhesive remains under discussion. Herein we studied the adhesion of epoxy resin as a function of the surface chemistry of barrier-type anodic oxides prepared in sulfuric acid- (SAA), phosphoric acid- (PAA) and mixtures of phosphoric-sulfuric acids (PSA) and chromic acid- (CAA) at different anodizing temperatures. X-ray photoelectron spectroscopy (XPS) data measured on model specimens was curve-fitted to calculate the relative amounts of O2-, OH-, PO43and SO42- species at the surface. The amounts of these species were then related to the mechanical performance of the joint measured by the floating roller peel test. Results show that significant initial adhesion is achieved without mechanical interlocking, and independent of the type of electrolytes used for the pretreatment. Conversely, bonding stability under wet conditions is highly influenced by the surface chemistry. The wet adhesion strength increases with the hydroxyl concentration at the aluminum (oxide) surface, indicating that the interfacial bonding is established through these surface hydroxyls. Phosphates and sulfates anions were not found to contribute to interfacial bonding with this type of adhesive.

ACS Paragon Plus Environment

Page 2 of 24

Page 3 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1. Introduction Adhesive bonding is one of the oldest techniques used to join different components 1. This type of structure is formed when an adhesive undergoes a physical or chemical hardening reaction to join two substrates through surface adherence (adhesion) and internal strength (cohesion) 2. Since the 1940s, adhesive bonding has been used to prepare different structural parts of many commercial aircrafts 3. To assure the life-long integrity of the structures, bonded panels are subjected to a multi-step pretreatment. The surface is first degreased to remove superficial contaminations. In the American aerospace industry, this is followed by an FPL or P2 etch that removes the natural oxide and produces a new oxide with finger-like morphology 4. Phosphoric acid anodizing (PAA) then follows. This electrochemical oxidation of aluminum under direct current (DC) conditions results in the formation of a porous oxide that is separated from the substrate by a thin and compact barrier layer 5. The standard pretreatment that has emerged in the European aerospace industry is based on CSA etching and chromic acid anodizing (CAA) which produces a more compact oxide than PAA, but offers an advantageous corrosion resistance 4. A fundamental understanding of adhesively bonded joints requires an examination on both macroscopic and microscopic levels. On a microscopic level, adhesion is only achieved if the adhesive (or primer) comes in molecular contact with the substrate. Hence, physical absorption is a prevailing requirement. Obtaining such contact requires appropriate wetting of the surface. This is typically achieved by simple surface degreasing 5. However, this alone does not guarantee adhesion. Initial- and long-term adhesion strength depends on the formation of physical and chemical bonds between the substrate and the adhesive 6. Numerous studies have shown that bonding between aluminum oxides and organic resins often involves relatively weak

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 24

intermolecular forces 7-10. The kind of bond that is formed and its strength depend on the chemical nature of the substrate, the type of organic resin and their compatibility 11

. On a macroscopic level, mechanical forces originating from the hardening of the

adhesive inside voids, cavities and pores at the surface promote adhesion

12

. This is

typically referred to as “mechanical interlocking” 4. The interface can then be considered as a composite phase that enables better stress distribution and can arrest the propagation of cracks 13. Strict international regulations on hexavalent chromium now encourage the transition to Cr(VI)-free surface pretreatments, thereby eliminating this carcinogenic and hazardous substance

14

. Candidate replacements include anodizing in sulfuric acid-

(SAA), phosphoric acid- (PAA) and mixtures of phosphoric-sulfuric acids (PSA). Pore formation during anodizing is controlled by the type of electrolyte, concentration, temperature and applied potential/current scheme. Depending on the combination of these parameters, oxides with different characteristic morphologies will develop. This includes variations in the porosity, the pore size and interpore distance, barrier layer and oxide thickness. In addition, anodizing in phosphoric and sulfuric acids leads to the incorporation of phosphate and sulfate anions into the oxide, thereby also changing its chemistry 15-17. In spite of its extensive commercial history, the nature and contribution of the different adhesion forces acting at the oxide/resin interface remains under discussion. In the present study we examine to what extent changes in the surface chemistry affect adhesion. We isolate the chemical contribution by stopping the anodizing during the formation of the barrier-layer, thereby avoiding the formation of a porous oxide that would lead to additional mechanical interlocking.

ACS Paragon Plus Environment

Page 5 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

2. Experimental Two types of specimens were used in this study. Model (laboratory) specimens were used for XPS surface analysis and industrial test specimens for floating roller peel tests. Both preparation methods are detailed below. 2.1 Model specimens for XPS analysis. Samples were cut from a 0.3 mm thick sheet of pure aluminum (99.99%, Hydro). To remove imperfections and provide a flat substrate for analysis purposes, specimens were electropolished. This was done after the substrate was etched in an aqueous solution of 25g/L NaOH at 70 °C for 1 minute, followed by rinsing for 15s with deionized water and then ultrasonically rinsed for an additional 3 minutes. The substrate was then electropolished for 6 min in a solution of 80 vol.% (absolute) ethanol and 20 vol.% perchloric acid, at a current density of 70 mA/cm2 and 10 °C. Subsequently, it was rinsed following the above procedure, dried with compressed air and stored in a sealed plastic bag. Later, each sample was given one of the anodizing pretreatments listed in Table 1. Table 1 Summary of the electrolyte composition for the different surface pretreatments. Abbreviation

Pretreatment

Electrolyte composition

PAA

Phosphoric Acid Anodizing

0.3M H3PO4

SAA

Sulfuric Acid Anodizing

*0.1M H2SO4

PSA

Phosphoric-Sulfuric Acid anodizing

0.3M H3PO4 and 0.1M H2SO4,

HcPSA

High concentration PSA

0.8M H3PO4 and 0.5M H2SO4,

CAA

Chromic Acid Anodizing

0.4M CrO3

* 0.05M was used for the preparation of the industrial specimens.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Galvanostatic anodizing at 10mA/cm2 for 4s was performed with SM120-25 powersupply (Delta Elektronika) equipped with an Ethernet interface connection to monitor the cell voltage. Model specimens were anodized in a three-electrode cell filled with 400 mL solution and two AA1050 aluminum cathodes for 4s at constant current density of 10mA/cm2. After each of the described pretreatments, the substrate was thoroughly rinsed for 15s with deionized water and then ultrasonically rinsed for an additional 3 minutes. Anodizing conditions were pre-selected to yield featureless anodic oxides by stopping the oxide growth at the end of the region in which the voltage was increasing linearly with time, the part which is associated with the formation of the barrier layer 18. In order to limit atmospheric contamination samples were placed in the pre-vacuum chamber for analysis no longer than 10 minutes after the pretreatment was completed. 2.2 Panels for floating roller peel test AA2024-T3 alclad (clad layer AA1230) aluminum test panels of 250x95x1.6 mm and 300x95x0.5 mm were used for the thick and thin sheets, respectively. Before specimens were given one of the pretreatments in Table 1, they were degreased, alkaline etched and desmutted. Degreasing was achieved by wiping the panels with ethanol. This was followed by a 2 min. alkaline etching with 40 g/L P3 Almeco 51 (from Henkel) at 35°C and a 1 min. pickling with 35 vol.% HNO3 at RT. After each step, the panel was thoroughly rinsed with running demineralized water, followed by 1 min. immersion rinsing in an agitated beaker of fresh demineralized water. Then the panels were anodized in one of the electrolytes listed in Table 1. Anodizing at constant current density of 5mA/cm2 was performed for 8s. Although the current density is lower than for the model specimens, the time is doubled, so that the final barrier layer thickness should be similar 19. After anodizing, the panels were rinsed

ACS Paragon Plus Environment

Page 6 of 24

Page 7 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

and dried with compressed air. The panels were then bonded (without primer) with FM 73 epoxy film adhesive (from Cytec Engineering Materials) within 10 minutes after the pretreatment of the thin panel was completed. After bonding, the panels were stored in a sealed plastic bag for up to 24 hours before curing. Curing following the manufacturer instructions was achieved using a Joos hot plate press at 6 bar and 120°C for 75 minutes. 2.3 Analysis methods 2.3.1 X-ray photoelectron spectroscopy XPS spectra were collected using a PHI5600 photoelectron spectrometer (Physical Electronics) with an Al Kα monochromatic X-ray source (1486.71 eV of photons). The vacuum in the analysis chamber was approximately 5x10-9 Torr during measurements. High-resolution scans of the Al2p, O1s, C1s, P1s and S2p photopeaks were recorded from a spot size of 0.8 mm using pass energy of 23.5 eV and step size 0.1 eV. Measurements were performed at takeoff angles of 45° and 15° with respect to the sample surface. The reproducibility of the measurements was verified by (at least) two repetitions. XPS data was analyzed using PHI Multipak software (V9.5.0.8). Before curve fitting, the energy scale of the XPS spectra was calibrated relative to the binding energy of adventitious hydrocarbons in the C1s peak at 284.4 eV. Curve fitting was done after a Shirley-type background removal, using mixed Gaussian (80– 100%) –Lorentzian shapes. 2.3.2 Mechanical testing Floating roller peel tests were executed according to ASTM D3167 - 03a

20

. Of

each bonded panel, three strips of 25x250mm were cut with a diamond saw. After fixing the test strips in the apparatus, the unbounded end of the specimen was

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

attached to the lower head of the testing machine. The thin aluminum panel was then peeled off the thick panel with a speed of 100 mm/min. The peeling load versus head movement (or load versus distance peeled) was recorded. All tests were performed at ambient temperature. The first half of the specimen was peeled under dry conditions. Water was then applied at the crack-tip and the second half was peeled under wet conditions. Since only clear cohesive or adhesive failures were observed, failure modes were assigned by visual inspection. 2.3.3 Atomic force microscopy (AFM) Bruker Dimension Edge

TM

Atomic force microscope was used in force tapping-

mode to measure the roughness of selected samples. Commercially available SCANASYST-AIR cantilevers (70kHz resonance frequency and 0.4N/m a force constant) were employed. Images were analyzed by NanoScope Analysis software 1.5 using the surface roughness mode. 3. Results 3.1 Anodic oxidation The plot in Fig. 1 displays the average anodizing voltage measured at 4 s and 8 s for model and tests panels, respectively, vs. the electrolyte temperature. Although larger scatter in some of the data points is caused by slight variations in the exposed surface area, the plot illustrates the dependence of the voltage on three factors; the electrolyte temperature, the nature of electrolyte and the substrate composition. The higher solubility of the oxide at higher temperatures leads to a linear decrease in the final voltage. Alternatively, a lower voltage is reached when the solvent action of the electrolyte is higher, as is the case with additions of phosphoric acid 21. The purity level of a substrate is affecting the final voltages by changing the resistance to ionic transport

22

. Therefore the voltage needed to maintain the same

ACS Paragon Plus Environment

Page 8 of 24

Page 9 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

current density is higher for 99.99% pure aluminum, compared to the 99.31% of the AA1230 Clad layer on AA2024-T3 23. Since the oxide layer thickness is proportional to the voltage (according to the general 1.2 nm/V relationship

18

), a different oxide

thickness is expected for the different substrate compositions (even though the total current that passed during anodizing is the same). In both cases, however, anodizing was stopped at the end of the part in which the voltage raised linearly with time (not shown), to assure ending before pores start to form.

Figure 1 The average anodizing voltage vs. electrolyte temperature measured after 4s at 10mA/cm2 and 8s at 5mA/cm2 for pure (99.99%) aluminum (grey markers) and AA2024-T3 Clad (Clad layer AA1230, black markers), respectively. The dashed lines indicate trend. 3.2 Surface roughness AFM measurements were performed to check if there are significant variations in the surface roughness as a result of the anodizing temperature. Examples for typical AFM images are shown in Fig. 2 and Fig. 3 for PAA oxides prepared on AA2024-T3 clad. Although scalloped morphology is observed due to prior etching, measurements show no significant difference between the surface roughness for anodizing at room temperature and at 50°C. similar results were observed for the other pretreatments.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 24

For comparison, the surface roughness of a model specimens used for XPS measurements is given in Fig. 4 for a PSA oxide prepared at 35°C. AFM measurements on the electropolished (EP) surface were similar to before- and after anodizing. Since only a barrier layer is formed, it takes over the surface morphology of the previous step (EP). Average results for the model specimens used for XPS surface analysis (electropolished and anodized) and the panels for floating roller peel test (etched, pickled and anodized) are listed in Table 2. Electropolished and anodized specimens can be considered smooth. Although the surface is full of nano-scale etching pits that are caused by electropolishing, the average Rq, which is the root mean square of the surface roughness is very low (4nm) and is similar on localized (1x1 µm) and a larger surface area (10x10 µm). This measured roughness is comparable to the roughness found after electropolishing in similar conditions 24. To avoid the effect of intermetallic particles, we used AA2024-Clad instead of bare alloy Table 2: Average root mean-square (rms) roughness as measured by AFM. Sample Image Rq (10x10 µm) Image Rq (1x1 µm) (nm) (nm) Electropolished and anodized

4

4

Etched, pickled and anodized

50

20

ACS Paragon Plus Environment

Page 11 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Figure 2 3D (a) and height (b) AFM images of AA2024-T3 after alkaline etching and acid pickling and anodizing (PAA, RT). Image Rq= 48 nm, Rq 1µm x1µm = 18 nm.

Figure 3 3D (a) and height (b) AFM images of AA2024-T3 after alkaline etching, acid pickling and anodizing (PAA, 50°C). Image Rq= 52 nm, Rq 1µm x1µm = 14 nm.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 4 3D (a) and height (b) AFM images of pure aluminum after electropolishing and anodizing (PSA, 35°C). Image Rq= 3 nm, Rq 1µm x1µm = 3 nm.

3.3 Surface chemistry analysis Surface chemistry on model panels was characterized by angle-resolved X-ray photoelectron spectroscopy (XPS). To assure that no other contaminations are present, a survey spectrum was acquired before each high-resolution spectrum. Typical XPS survey spectra of the different types of anodic oxides are shown in Fig. 5. Incorporation of electrolyte-derived anions is indicated by the presence of phosphor and sulfur in the corresponding oxides.

ACS Paragon Plus Environment

Page 12 of 24

Page 13 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Figure 5: XPS survey spectra of (a) PAA, (b) SAA, (c) HcPSA and (d) CAA barrier-type oxides on model panels.

Next, high-resolution spectra of O1s, C1s, Al2p, S2p and P2s were measured (Fig. 6, the black line). These were then curve-fitted using the method presented in detail in our previous work 25.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 24

Figure 6: Fitted high-resolution XPS spectra with the deconvolution of the O1s and C1s peaks. The measured spectrum is shown in black and the fitted spectrum/ components are indicated with the grey lines, with the average measured binding energies (in eV).

The fitted intensity areas were then used to find a solution for the amount of OH-, PO43-and SO42-, while taking into account all the present species with an overlapping binding energy (CO-, COOX-, PO43-, SO42-, OH- and O2-) in the O1s photopeak. The relative amounts of O2-, OH-, PO43- and SO42- (in %) were then determined by the ratio, as presented in Eq. (1) for OH-.  % 

          

 100



ACS Paragon Plus Environment

Eq. (1)

Page 15 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Calculation results for anodizing at room temperature (RT), 35°C and 50°C are summarized in Fig. 7, for takeoff angles of θ =15° and 45°. All oxides are composed of an oxidized aluminum, with different amounts of hydroxyls and adsorbed water. Results show that anion incorporation has a significant effect on the chemical composition of the corresponding anodic oxides. Incorporation of phosphate and sulfate anions from the respective electrolytes is the main cause for their reduced hydroxyl fraction. Since phosphate incorporation is relatively high, PAA anodizing results in the lowest amount of OH-, followed by PSA, HcPSA, SAA and CAA, respectively. This trend is valid for all anodizing temperatures. More phosphates are found at the surface of the oxide in PAA than sulfates in SAA. However, when the two acids are used together (as in PSA and HcPSA), the incorporation of both anions is lower than in a single component electrolyte, with phosphates incorporation dropping more than sulfates.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 7 Calculated average percentage of O2- (grey), OH- (blue), SO42- (green) and PO43- (red) species on the differently prepared oxide layers at takeoff angles of θ =15° and 45°. Anodizing was performed at room temperature (a) and (b), 35°C (c) and (d) and 50°C (e) and (f).

ACS Paragon Plus Environment

Page 16 of 24

Page 17 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

3.4 Floating roller peel tests Mechanical performance was evaluated by measuring two types of peel strengths; dry and wet peel. Dry peel represents the initial peel strength of the joint. Wet peel represents the performance in the presence of water at the interface, by spraying water at the crack-tip during testing. The measured (average) strengths for both tests are shown in Fig. 8, displayed as a function of the electrolyte temperature. As seen in Fig. 8 (a), the dry peel strength does not vary much between the different pretreatments and, although some increments are registered at higher temperatures, they are relatively small. On the other hand, there is a significant increase in the wet peel strength for anodizing at higher temperatures (Fig. 8 (b)). This trend is observed for all types of electrolyte. Moreover, there is a significant difference between the performances of the different types of oxides under wet conditions. The wet peel strengths after CAA anodizing is the best, while PAA and PSA oxides perform the worst. Visual post-inspection of the panels revealed a distinct behavior. All panels exhibited a cohesive failure after dry peel testing (Fig. 9), with the yellow adhesive clearly visible on both sides of the joint. Surprisingly despite a wide range of performances (max. wet peel is 143 N/25mm for CAA at 50°C and min. is 9 N/25mm for PAA at RT), wet failure always occurred at the interface. This can be concluded by the shiny metal appearance1 of the aluminum substrate on one side of the thin peeled strip and what looks like an intact adhesive on the other side of the joint (Fig. 9). This distinctive behavior was observed on all the tested panels, independent of the pretreatment. 1

The barrier-type anodic oxides in this study are thin (typically less than 50nm, as reported in our previous publication 16) and, hence, their appearance is not completely opaque.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 8 The average measured peel strength under dry (a) and wet (b) conditions. Range bars indicate the maximum and minimum measured values.

Figure 9 Representative macroscopic images of the peeled panels with the surfaces visible on the thick (left) and thin (right) adherends. The dry (top) part of the panel exhibits cohesive failure, with the yellow adhesive visible on both sides of the joint. On the bottom part, the aluminum substrate is fully visible on the thin panels that were peeled under wet condition, indicating an interface failure.

4. Discussion

ACS Paragon Plus Environment

Page 18 of 24

Page 19 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Although the final anodizing voltage is different for model and peel panels, we presume that the incorporation of anions is not significantly affected by the short time and voltage (hence also thickness) variances. A comparison between the calculated hydroxyl percentage and the peel strengths is carried out in Fig. 10, for anodizing at RT, 35°C and 50°C (Fig. 7 (a), (b) and (c), respectively). At all temperatures, the dry peel strength of the different oxides is similar and independent of the amount of hydroxyls. Conversely, there is a positive linear correlation between an increased amount of hydroxyls and the wet peel strength. The dashed lines in Fig. 8 indicate this trend. Since the amount of surface hydroxyls depends on the electrolyte, the wet peel increases in the same trend as the calculated OH-, namely increasing in the following order: PAA < PSA, HcPSA < SAA < CAA, at each temperature. These results indicate that interfacial bonding with epoxy proceeds through surface hydroxyls and that phosphate and sulfate anions do not contribute to interfacial bonding with this type of adhesive. These findings show that interfacial bonding between anodic oxides and epoxy proceeds similarly to that on native and chemically grown oxides that contain no “contamination” anions 26-27. Similarly to the finding by Rider et al. 28, we show that the amount of surface hydroxyls does not alter the failure mechanism. However, the results from both studies differ in the sense that in our study the hydroxyl fraction significantly affects bonding with FM 73 adhesive, while the authors of the previous study did not find such effect. We suggest that the effect was concealed by large variation in the surface roughness. This affirms the need to study the effect of surface chemistry on the featureless oxides.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 10 The average dry- (empty markers) and wet (filled markers) peel strength vs. the calculated hydroxyl percentage at the surface (θ=15°) on barrier-type oxides after anodizing at RT (a), 35°C (b) and 50°C (c).

These experimental results also confirm previous theoretical calculations. A modeled interaction using density functional theory (DFT) calculations by Semoto et al.

29

predicts that the hydroxyl groups on both the oxide and the epoxy sides are the

reacting entities, typically forming hydrogen bonds across the interface. Since this type of bonds is not stable in the presence of water, most of the adhesion is lost when water enters the interface, with the force necessary to separate the joint proportional to the amount of interactions and, hence, the amount of hydroxyls. Clearly the remaining peel strength in wet conditions indicates that some stable bonds are present, which increase proportionally with the fraction of surface hydroxyls.

ACS Paragon Plus Environment

Page 20 of 24

Page 21 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Additionally, there is a clear positive effect between a higher anodizing temperature and mechanical performance. For PAA oxides, this can be linked to the increase in the amount of hydroxyls with temperature, leading to an approximately five-fold increase in the wet peel strength. While the wet peel strength of the remaining pretreatments also increases, their calculated hydroxyl fraction did not vary much with temperature (and even slightly decreased, as in the case of CAA and SAA oxides (Fig. 2)). As AFM measurements confirm, this is not caused by an increased surface roughness at higher temperatures.

5. Conclusions This is the first study in which the adhesion of anodic oxide films has been related to their surface chemistry. Experimental results verify that significant initial (dry) adhesion is achieved without mechanical interlocking, and independent of the anodizing electrolyte. Conversely, we demonstrate that wet adhesion of featureless anodic oxides increases with anodizing temperature irrespective of the electrolyte and that the wet peel strength is highly influenced by the surface chemistry of the oxide. Since a clear correlation between the amount of hydroxyls and the wet peel strengths was found, it appears that interfacial bonding proceeds through the surface hydroxyls. Therefore, wet adhesion strength is also inversely correlated with the amount of phosphates and sulfates that are incorporated into the oxide by anodizing in phosphoric and sulfuric acids.

ACKNOWLEDGMENT This research was carried out under the project number M11.6.12473 in the framework of the Research Program of the Materials innovation institute M2i

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(www.m2i.nl). The authors would like to acknowledge Oscar Steenhaut from the Vrije Universiteit Brussel (VUB) for his help with the XPS measurements, Vincent van den Heuvel from Fokker Aerostructures for his support in the preparations and testing of the bonded specimens and Rob Leonard, also from Fokker Aerostructures, for executing the floating roller peel tests.

REFERENCES 1. Brockmann, W.; Geiß, P. L.; Klingen, J.; Schröder, B. Adhesive Bonding; Wiley-VCH Verlag GmbH & Co. KGaA, 2009, p I-XVIII. 2. Brockmann, W.; Hennemann, O. D.; Kollek, H. Surface Properties and Adhesion in Bonding Aluminium Alloys by Adhesives. Int. J. Adhes. Adhes. 1982, 2, 33-40. 3. Higgins, A. Adhesive Bonding of Aircraft Structures. Int. J. Adhes. Adhes. 2000, 20, 367-376. 4. Venables, J. D.; McNamara, D. K.; Chen, J. M.; Sun, T. S.; Hopping, R. L. Oxide Morphologies on Aluminum Prepared for Adhesive Bonding. Appl. Surf. Sci. 1979, 3, 88-98. 5. Critchlow, G. W.; Brewis, D. M. Review of Surface Pretreatments for Aluminium Alloys. Int. J. Adhes. Adhes. 1996, 16, 255-275. 6. Brockmann, W.; Hennemann, O. D.; Kollek, H.; Matz, C. Adhesion in Bonded Aluminium Joints for Aircraft Construction. Int. J. Adhes. Adhes. 1986, 6, 115. 7. van den Brand, J.; Blajiev, O.; Beentjes, P. C. J.; Terryn, H.; de Wit, J. H. W. Interaction of Ester Functional Groups with Aluminum Oxide Surfaces Studied Using Infrared Reflection Absorption Spectroscopy. Langmuir 2004, 20, 6318-6326. 8. van den Brand, J.; Blajiev, O.; Beentjes, P. C. J.; Terryn, H.; de Wit, J. H. W. Interaction of Anhydride and Carboxylic Acid Compounds with Aluminum Oxide Surfaces Studied Using Infrared Reflection Absorption Spectroscopy. Langmuir 2004, 20, 6308-6317. 9. Mercier, D.; Rouchaud, J. C.; Barthés-Labrousse, M. G. Interaction of Amines with Native Aluminium Oxide Layers in Non-Aqueous Environment: Application to the Understanding of the Formation of Epoxy-Amine/Metal Interphases. Appl. Surf. Sci. 2008, 254, 6495-6503. 10. Salgin, B.; Özkanat, Ö.; Mol, J. M. C.; Terryn, H.; Rohwerder, M. Role of Surface Oxide Properties on the Aluminum/Epoxy Interfacial Bonding. J. Phys. Chem. C 2013, 117, 4480-4487. 11. Packham, D. E. Theories of Fundamental Adhesion. In Handbook of Adhesion Technology, Da Silva, L. F. M.; Öchsner, A.; Adams, R. D. Eds. Springer-Verlag: Berlin Heidelberg, 2011. 12. McBain, J. W.; Hopkins, D. G. On Adhesives and Adhesive Action. J. Phys. Chem. C 1924, 29, 188-204.

ACS Paragon Plus Environment

Page 22 of 24

Page 23 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

13. Kinloch, A. J.; Little, M. S. G.; Watts, J. F. The Role of the Interphase in the Environmental Failure of Adhesive Joints. Acta Mater. 2000, 48, 4543-4553. 14. OSHA, Toxic and Hazardous Substances In Occupational Exposure to Hexavalent Chromium, United States Department of Labor: 2006; Vol. 1910.1026. 15. Xu, Y.; Thompson, G. E.; Wood, G. C.; Bethune, B. Anion Incorporation and Migration During Barrier Film Formation on Aluminium. Corros. Sci. 1987, 27, 83102. 16. Takahashi, H.; Fujimoto, K.; Konno, H.; Nagayama, M. Distribution of Anions and Protons in Oxide Films Formed Anodically on Aluminum in a Phosphate Solution. J. Electrochem. Soc. 1984, 131, 1856-1861. 17. Parkhutik, V. P. The Initial Stages of Aluminium Porous Anodization Studied by Auger Electron Spectroscopy. Corros. Sci. 1986, 26, 295-310. 18. Sheasby, P. G.; Pinner, R. Surface Treatment and Finishing of Aluminium and Its Alloys, 6th ed.; Finishing Publications Ltd.: England, 2001. 19. Wood, G. C.; O'Sullivan, J. P. The Anodizing of Aluminium in Sulphate Solutions. Electrochim. Acta 1970, 15, 1865-1876. 20. ASTM, ASTM D3167-03a, Standard Test Method for Floating Roller Peel Resistance of Adhesives. ASTM International: West Conshohocken, PA, 2003. 21. van Put, M.; Abrahami, S. T.; Elisseeva, O.; de Kok, J. M. M.; Mol, J. M. C.; Terryn, H. Potentiodynamic Anodizing of Aluminum Alloys in Cr(VI)-Free Electrolytes. Surf. Interface Anal. 2016, 48, 946-952. 22. Sulka, G. D. Highly Ordered Anodic Porous Alumina Formation by SelfOrganized Anodizing. In Nanostructured Materials in Electrochemistry, Wiley-VCH Verlag GmbH & Co. KGaA: 2008; pp 1-116. 23. Adeosun, S. O.; Ayoola, W. A.; Bodude, M.; Sanni, S. O. Strength and Hardness of Directionally-Rolled AA1230 Aluminum Alloy. JETEAS 2011, 2, 440444. 24. Hauffman, T.; Blajiev, O.; Snauwaert, J.; van Haesendonck, C.; Hubin, A.; Terryn, H. Study of the Self-Assembling of N-Octylphosphonic Acid Layers on Aluminum Oxide. Langmuir 2008, 24, 13450-13456. 25. Abrahami, S. T.; Hauffman, T.; de Kok, J. M. M.; Mol, J. M. C.; Terryn, H. XPS Analysis of the Surface Chemistry and Interfacial Bonding of Barrier-Type Cr(VI)-Free Anodic Oxides. J. Phys. Chem. C 2015, 119, 19967-19975. 26. Barthés-Labrousse, M. G. Mechanisms of Formation of the Interphase in Epoxy-Amine/Aluminium Joints. J. Adhes. 2012, 88, 699-719. 27. Alexander, M. R.; Beamson, G.; Blomfield, C. J.; Leggett, G.; Duc, T. M. Interaction of Carboxylic Acids with the Oxyhydroxide Surface of Aluminium: Poly(Acrylic Acid), Acetic Acid and Propionic Acid on Pseudoboehmite. J. Electron. Spectrosc. Relat. Phenom. 2001, 121, 19-32. 28. Rider, A. N.; Brack, N.; Andres, S.; Pigram, P. J. The Influence of Hydroxyl Group Concentration on Epoxy–Aluminium Bond Durability. J. Adhes. Sci. Technol. 2004, 18, 1123-1152. 29. Semoto, T.; Tsuji, Y.; Yoshizawa, K. Molecular Understanding of the Adhesive Force between a Metal Oxide Surface and an Epoxy Resin. J. Phys. Chem. C 2011, 115, 11701-11708.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

TOC graphic

ACS Paragon Plus Environment

Page 24 of 24