Efficient Bio-Inspired Oxygen Reduction Electrocatalysis with Electropolymerized Cobalt-Corroles Ariel Friedman, Lena Landau, Shmuel Gonen, Zeev Gross, and Lior Elbaz ACS Catal., Just Accepted Manuscript • DOI: 10.1021/acscatal.8b00876 • Publication Date (Web): 26 Apr 2018 Downloaded from http://pubs.acs.org on April 26, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 11 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

Efficient Bio-Inspired Oxygen Reduction Electrocatalysis with Electropolymerized Cobalt-Corroles Ariel Friedman1, Lena Landau2, Shmuel Gonen1, Zeev Gross2*, Lior Elbaz1* 1

2

Chemistry Department, Bar-Ilan University, Ramat-Gan 5290002, Israel Schulich Faculty of Chemistry, Technion-Israel Institute of Technology, Haifa 3200008, Israel *Corresponding authors e-mails: [email protected]; [email protected] ABSTRACT: Fuel cells are considered as the only viable solution for long-range electro-mobility, but very rare and expensive platinum is currently required for catalyzing the bottleneck reaction therein: oxygen reduction. Within the search for catalysts that are not based on precious metals, cobalt corroles were uncovered to fulfill the requirements of high selectivity and low overpotential. We now report on the electropolymerization of a specifically designed catalyst, cobalt(III) complex of tris(4-aminophenyl) corrole, upon which 3D polymeric structures were obtained. Much better catalytic activity was obtained by this approach as compared to monomeric catalyst, manifested by significantly lower overpotentials, as well as higher selectivity to the desired 4e-/4H+ pathway. The performance in alkaline environment makes it the most active molecular catalyst for the oxygen reduction reaction reported to date.

Keywords: Fuel Cells • Corrole • ORR • Electrocatalysis • non-precious metal catalyst performed with them is still flourishing. Within that class, significant progress has recently been reported for 1st row transition metal complexes of corroles (metallocorroles).6-8 Corroles are macrocyclic complexes with structural resemblance to porphyrins, which due to their unique trianionic platform offer enhanced activity and stability to metals chelated by them.5, 912 Recent work revealed that the ORR occurs with much lower overpotentials when catalyzed by metallocorroles rather than by metalloporphyrinsand comparable to the state-ofthe-art catalysts for oxygen reduction introduced so far.13-15 Recently, we showed that by adsorbing the corroles on high surface area carbon (BP2000), the catalytic activity increases significantly with the highest activity in acidic conditions obtained with cobalt corroles, making it comparable to the stateof-the-art catalysts for oxygen reduction introduced so far.16-18 Nevertheless, there is still work to be done in order to further enhance the catalytic activity, mainly in shifting the ORR to the desired 4-electron mechanism. It is well known that monomeric Co porphyrins and corroles reduce oxygen via the 2 electron mechanism, and that faceto-face orientation with appropriate metal center distance is critical for the four-electron reduction pathway.8, 19 Many studies have shown that binuclear complexes and other multi-metal centered complexes catalyze the oxygen reduction reaction at higher onset potentials and mostly 4-electron mechanism and outperform the activity of their monomeric units.20-25 This improvement was

1. Introduction The main energy supply for aerobic respiration comes from the oxygen reduction reaction (ORR), by which molecular oxygen is reduced selectively to water by the perfectly arranged tris-copper and bis-heme centers present in cytochrome C oxidase.12 In alternative energy generation devices such as fuel cells and metal-air batteries, the ORR is also most crucial. Low ORR kinetic rates, operation at high overpotentials, and the consequential energy losses must be prevented for making such devices practical. Platinum-based catalysts fulfill the above requirements best, and they also reduce oxygen predominantly via the desired 4-electrons mechanism. But platinum is one of the scarcest and most expensive metals on earth. This is the main reason for the worldwide efforts on finding ORR catalysts that are not based on precious group metal (PGM) catalysts. Considering that ORR catalysis in the natural systems relies on porphyrin-chelated iron (heme), much attention has been driven to complexes composed of 1st row transition metal ions (mainly Fe and Co) bound by synthetic porphyrins and other macrocycles.3 An interesting outcome is that the state-of-the-art ORR catalysts of this class are obtained via pyrolysis of the above catalysts as to form materials that apparently preserve the M-N4 motif (metal chelated by 4 N atoms).4 What seriously hampers their further development is that it is hard to design/control/identify structures and catalytic sites.4-5 The above aspects are however quite trivial for molecular catalysts, which is actually why research

1 ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

attributed to the vicinity of the metallic centers, which in optimum distance can bind oxygen by two metal ions.26 Accordingly, we postulated that electropolymerization of the cobalt corroles will result in dense corrole layers which will bring the catalytic centers close together to enable concerted reactions, and thus increase the activity and selectivity towards the 4-electron process by virtue of cooperative effects similar to those described above. We now present the advance to 3D polymeric structure composed of well-defined catalytic centers, obtained by controlled electropolymerization of an appropriately designed cobalt corrole on carbon electrodes, as a mean for obtaining superior ORR catalysis. In addition to increase in the catalytic performance, the compact polymeric structures are expected to have a high concentration of active sites which can compensate for the relatively low turnover frequencies usually associated with all PGM-free catalysts for ORR, when compared to Pt-based catalysts.27

Triphenylphosphine, RT. phosphine, RT.

Page 2 of 11

Co(OAc)2⋅4H2O, 2. Triphenyl-

after the CVs (Figure 1, inset) serve as another clear evidence for the deposition of polyCoTAC on the electrode. Similar phenomena was obtained for electropolymerization of phenylaniline subtituted porphyrins,28-31 which gives a preliminary indication that the aniline substituents on the corrole ring are involved in the transformation of CoTAC to polyCoTAC on the electrode surface. The CV of the polyCoTAC-modified electrode in a monomer-free solution revealed stable voltammograms (Figure S1, Supporting Information; red traces), indicating that the deposited film remains electroactive and does not passivate the electrode surface.32

2. Results and discussion The monomeric cobalt corrole CoTAC with three 4-aminophenyl intended to be used for oxidative polymerization, was prepared by the standard procedures drawn in Scheme 1 (Experimrntal procedures, Supporting Information). Electropolymerization of CoTAC was conducted by cycling the potential of an Indium Tin Oxide (ITO)-coated glass electrode between 0.00 V and 0.45 V (vs. Ag wire). The ITO electrode was dipped into an acetonitrile (AN) solution containing tetraethylammonium tetra-fluoro-borate (TEAT, 0.1 M) and CoTAC (2 mM). The rise of both cathodic and anodic peaks that were observed during that process (Figure 1) was attributed to an increase in the surface concentration as a consequence of the deposition of polymerized CoTAC on the ITOcoated electrode. Pictures of the electrode before

Figure 1. Cyclic voltammogram (CV) obtained upon the electropolymerization of CoTAC on an ITO coated glass electrode (2 mM CoTAC in 0.1M TEAT/AN solution, scan rate 100 mV/s). Inset: the ITO electrode before (left) and after (right) electropolymerization.

The electropolymerization of the CoTAC was studied by using electrochemical quartz crystal microbalance (EQCM), on gold-coated quartz crystal under similar conditions to those described before. The change in frequency as a function of the applied potential for the first CV cycle is shown in Figure 2. The resonance frequency of the quartz crystal (which is proportional to the mass of deposited material) decreases only at potentials higher than 0.3 V vs. Ag/AgCl, confirming the deposition of polyCoTAC at this potential. Whereas, an increase in frequency was observed during the backward scan, as the measured currents decreased, hinting on a mass loss. This can be attributed to reduction and de-doping of the polymer, which results in the repulsion of the electrolyte counter anion that was held by the positively charged polymer. The electropolymerization and decrease in QCM frequency continues with cycling and correlates well to the increase of the accumulated

and Scheme 1. The 3-step synthesis of 5,10,15-tris(4-aminophenyl) corrolato cobalt(III)triphenylphosphine (CoTAC, with L = PPh3). Reaction conditions: a: 1. MeOH/H2O/HCl, RT, 1 hr. 2. p-chloranil, RT, overnight; b: 1. SnCl2⋅2H2O, 2. H2O/HCl, reflux under Ar atmosphere; c: 1. Co(OAc)2⋅4H2O, 2.

2 ACS Paragon Plus Environment

Page 3 of 11

charge in the Infromation).

CV

(Figure

S2,

Supporting

by using FTIR-ATR spectroscopy (Figure 3). These measurements revealed an almost complete disappearance of the characteristic NH2 stretching vibrations at 3441 cm-1 and 3331.2 cm-1, in addition to significant reduction of the peak at 1613 cm-1, which is mainly due to NH2 scissoring vibration.3334 This data is consistent with transformation of the primary aminophenyl moieties present in CoTAC to higher N-substitution levels. The FTIR-ATR spectra also reveal that the NH2 frequencies did not fully disappear, pointing towards the presence of unreacted substituents on the corrole ring. These results confirm that in the polymerization process, the aniline groups react and lose protons to become secondary or tertiary amine. For comparison, in polyaniline there are several coupling positions for linking the aniline rings to each other (head-to-tail, tail-to-tail and head-tohead)35, whereas in the case of polyCoTAC, the available coupling positions are limited, since the tail position (para to the NH2 unit) is occupied by the corrole ring. This leaves the ortho position as the only available coupling position on the phenyl ring. On the other hand, polymerization through β position on the corrole ring also needs to be considered. Another possible cross-link to be considered is head-to-head, nitrogen to nitrogen of two different corroles, either single or double bonded, which is expected to from 1, 2Diphenylhydrazine and azobenzene linking units, respectively. Hence, the nature of the bond between the CoTAC monomers may be different from that of polyaniline. In order to study the coupling position on the CoTAC, we synthesized cobalt(III)-tri(tetrafluorop-aminophenyl) corrole (CoTFAC) (Figure S3, Supporting Infromation). CoTFAC differs from CoTAC only in the ortho- and meta- positions on the aminophenyl substituents, where fluorine atoms are replacing the hydrogen atoms. Similar conditions were applied in order to try to electropolymerize the CoTFAC, and in contrast to the CoTAC, polymerization of CoTFAC was not observed (neither electrochemically nor physically – the ITO electrode remained clear – no deposition was observed), even when cycling to much higher potential (1.3V vs. RHE). These observations suggest that the electropolymerization site of the CoTAC is indeed the ortho position on the aminophenyl ring and not through the β positions on the corrole ring or head-to-head. Based on these results, and on the wellestablished aniline electropolymerization mechanism,36-39 we propose an electropolymerization mechanism similar to what

0.06

0

0.04

∆F (Hz)

-100

i (mA) 0.02

-200

0.00 -300 0.0

0.1

0.2

0.3

0.4

0.5

E (V vs. Ag/AgCl)

Figure 2. EQCM (first cycle) of electropolymerization of CoTAC (2 mM CoTAC in 0.1M TEAT/AN solution), scan rate 100 mV/s. The blue trace reflects the changes in current and the black trace changes in frequency.

a

3347 3331.2

0.1

Absorbance

3352

3441

3463.1

0.0 3600

3450

3300

3150

Wavenumbers (cm-1)

b 1601

0.3

1589.8 1613.8

Absorbance

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

0.2

0.1

0.0 1650

1624.3

1600

1550

Wavenumbers (cm-1)

Figure 3. FTIR-ATR spectra of CoTAC monomer powder (black) and polyCoTAC powder scraped from the electrode surface after the electropolymerization (blue) at (a) high and (b) low wavenumbers

The new chemical bonds formed during the electropolymerization of polyCoTAC were studied

3 ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

has been suggested for polymerization of other macrocycles substituted with 4-aminophenyls.40-41 It is generally accepted that the first step of the electropolymerization of aniline is an irreversible oxidation (Electrochemical step; E step), which results in the formation of a radical cation, followed by coupling of two radical anilines to form a dimer (Chemical step; C step). On every newly formed bond, two hydrogen atoms are eliminated to obtain aromaticity (another C step). The dimer is oxidized immediately to dimer-cation (E step) followed by coupling with monomer cation (Equation S1, Supporting Infromation). For the short term, chain propagation occurs, involving repeated steps of

electropolymerization mechanism and structure of polyCoTAC in Scheme 2. It is important to note that so far, only the first reaction resulting in linking unit of o-amino-diphenylamine (a) was proven by us. The following reactions to dihydrophenazine (b) and phenazine (c) only postulated based on polymerization mechanism of aniline and other phenylaniline substituted porphyrins. This mechanism is currently under through investigation – the formation of the polymer on the electrode surface limits the ability to characterize it using conventional techniques such as NMR. Hence the complexity in gathering the molecular information.

E(CCE)n. This is also described in the proposed

Scheme 2. Top: Illustration of phenazine-bridged cobaltocorroles. Bottom: plausible electropolymerization mechanism (the corrole ring is omitted). The bridging unit may change by sequential oxidative coupling steps from o-amino-diphenylamine (a) to dihydrophenazine (b) to phenazine (c).

4 ACS Paragon Plus Environment

Page 4 of 11

Page 5 of 11

Figure 4. SEM images (a,b) of polyCoTAC on a glassy carbon electrode at different magnifications.

The morphology of the newly synthesized polyCoTAC was obtained with SEM imaging, uncovering that the polyCoTAC film is composed of dense, uniform, well-dispersed, threedimensional cauliflower-like structures (Figure 4). Each particle consists of small nano-metric particles with an average size of ~30nm (Figure 4b), which renders this catalyst as a good platform for heterogeneous electrocatalysis of the oxygen reduction reaction (ORR) in terms of potential surface area and roughness.26 The electrocatalytic ORR activity was studied using rotating ring-disk electrode (RRDE) in 0.5 M H2SO4 and 0.1 M KOH aqueous solutions, for both the monomeric metallocorrole and its polymer (Figure 5). To evaluate and compare their electrocatalytic activity, the onset potential (Eonset), half-wave potential (E1/2), and the number of transferred electrons (n) were measured and calculated (Equation S2, Supporting Infromation). The results are summarized in Table 1, which clearly shows that polyCoTAC exhibits better electrocatalytic activity than its monomer, both in acidic and alkaline solutions. This is apparent by the desired positive shift of the onset/half-wave potentials: 110/180 mV in the acidic solution and 40/120 mV in the alkaline solution. Moreover, the number of electrons participating in the reaction was also significantly affected: 2.14 vs. 1.77 in 0.5 M H2SO4 and 3.10 vs. 2.5 in in 0.1 M KOH. The latter results indicate that the two-electron reduction pathway (n=2) is predominant in acidic solution for both CoTAC and polyCoTAC and in basic solution for CoTAC, while polyCoTAC in alkaline solution has a larger contribution from the 4-electron (or 2+2) reduction pathway, approaching n=4. The bare GC electrode also exhibits some catalytic activity in 0.1 M KOH, which can be attributed to quinonelike moieties on its surface.42-43 Whereas, no

a

0.5

j (mA/cm2)

0.0

-0.5

-1.0

-1.5

-2.0

0.0

0.1

0.2

0.3

0.4

0.5

0.6

0.7

E (V vs. RHE) b

0.5 0.0 -0.5

j (mA/cm2)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

-1.0 -1.5 -2.0 -2.5 -3.0 0.0

0.1

0.2

0.3

0.4

0.5

0.6

0.7

E (V vs. RHE)

Table 1. The onset potential (V), half-wave potential (V) and the number of transferred electrons (n; calculated using the Levich equation, S8) of CoTAC and polyCoTAC in 0.5 M H2SO4 and 0.1 M KOH, on glassy carbon and BP2000. Glassy Carbon

BP2000

Onset (V)

/ (V)

Electron number (n)

Onset (V)

/ (V)

Electron number (n)

CoTAC

0.62

0.4

1.77

0.81

0.62

2.18

polyCoTAC

0.73

0.58

2.14

0.84

0.64

3.13

CoTAC

0.79

0.58

2.5

0.84

0.72

3.1

polyCoTAC

0.83

0.7

3.15

0.93

0.83

3.5

0.5M H2SO4

0.1M KOH

ACS Paragon Plus Environment

0.8

ACS Catalysis

activity was

obtained for BP2000. The origin for this effect is still unknown and currently under investigation by our group. Several possibilities for this effect are suggested such as interaction with surface functional groups, ordered vs. disordered phases in the carbon and average pore size. As can be seen in Figure 6, both in acidic and alkaline solutions, the catalytic activity of the polyCoTAC increased significantly by all measured electrochemical parameters after its in-situ electropolymerization onto BP2000 (Figure 6a, red trace), when compared to CoTAC adsorbed from solution on BP2000 (Figure 6a, black trace). We observed an increase in the onset potential to 0.928 and 0.84 V vs. RHE, increase in half-wave potential to 0.832 and 0.638 V vs. RHE and increase in the electrons number to 3.52 and 3.13 for alkaline and acidic environments, respectively. At higher overpotentials in the acidic solution, there is a clear transition from mainly twoelectron reduction pathway to mostly four-electron reduction pathway, more specifically to the 2+2 mechanism. This may be deduced from the additional wave around 0.4 V vs. RHE, attributable to reduction of hydrogen peroxide to water. A similar, but less pronounced behavior, is seen in the alkaline solution for CoTAC@BP2000 (Figure 6b, black trace), but the pathway for polyCoTAC@BP2000 (Figure 6b, red trace) remains mostly four-electron reduction throughout the whole potential range. To put the encouraging results obtained with polyCoTAC@BP2000 on scale, it was compared to the state-of-the-art pyrolyzed (non-molecular) PGM-free commercial catalyst purchased from Pajarito Powder (Figure 6a and 6b, blue trace). In acidic solution, the performance of the latter was clearly better, with about 100 mV higher onset potential and higher limiting currents. But in alkaline solution, the onset potential difference was below 50 mV, and the limiting current was obtained faster for polyCoTAC@BP2000, which hints on faster reaction kinetics for polyCoTAC@BP2000. This makes the polyCoTAC@BP2000 the best, non-heat-treated, molecular catalyst for ORR reported to-date.

Figure 5. RRDE measurements (900 rpm, 5mV/s) for evaluating ORR activity in (a) 0.5 M H2SO4 and (b) 0.1 M KOH of a bare GC electrode (green), GC electrode onto which CoTAC monomer was either deposited (black) or electropolymerized (red).

measured in acidic conditions, as expected. Also important to note is that polyCoTAC exhibits improved kinetics and reach the limiting current faster than its monomer, hinting on faster 0.0

a

-0.5

j (mA/cm2)

-1.0 -1.5 -2.0 -2.5 -3.0 -3.5 0.0

0.1

0.2

0.3

0.4

0.5

0.6

0.7

0.8

0.9

E (V vs. RHE) 0.0

b

-0.5 -1.0

j (mA/cm2)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

-1.5 -2.0 -2.5 -3.0 -3.5 0.0

0.1

0.2

0.3

0.4

0.5

0.6

0.7

0.8

0.9

1.0

E (V vs. RHE)

Figure 6. RDE measurements (900 rpm, 5mV/s) of ORR in (a) 0.5M H2SO4 and (b) 0.1M KOH. With BP2000 carbon (green) CoTAC monomer@BP2000 (black), polyCoTAC@BP2000 (red), compared to the commercial PGM-free Pajarito Powder’s catalyst (blue).

reaction kinetics. For achieving better functionality required for devices such as fuel cells, the attention was driven towards incorporating the polyCoTAC in high surface area carbon that is commonly used as a commercial catalyst support: BP2000. In our previous work we showed that the catalytic activity of monomeric metallo corroles is influenced significantly by the nature of the electrode substrate where the highest activity

3. Conclusion In this work, successful electropolymerization of metallocorrole was demonstrated for the first time. Based on well-elucidated polyaniline electropolymerization, a mechanism for the polymerization of polyCoTAC was suggested. FTIR-ATR analysis confirms the formation of new covalent bonds between the monomers. The polyCoTAC formed a three-dimensional

6 ACS Paragon Plus Environment

Page 6 of 11

Page 7 of 11 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

disk (surface area of 0.247 cm2) and a platinum ring (surface area of 0.186 cm2) (Pine E7R9). The potential of the ring was held at 1.2 V vs. RHE. Glassy carbon rod (3 mm diameter) was used as the counter electrode. The reference electrode was a reversible hydrogen reference electrode (RHE) composed of platinized platinum wire, operating under constant purge of pure hydrogen (at atmospheric pressure). For the measurement of background currents, the electrolyte solution was purged with gaseous Ar (99.999% purity) and for ORR studies it was purged with gaseous O2 (99.999% purity). The number of transferred electrons (n) was calculated via Levich equation (eq.1):

cauliflower like structure which consists of smaller nano-particles. The catalytic activity for oxygen reduction reaction of CoTAC improved significantly after its electropolymerization, by all parameters studied in this work. This is attributed to synergistic activity of the metallocorroles. The activity of polyCoTAC was further improved when polymerized inside high surface area carbon (BP2000). This combination exhibited high performance when compared to the state-of-the-art commercial non-precious metal catalyst in alkaline solution. Further investigation of the structure and the interaction of the polyCoTAC with the BP2000 are currently underway. 4. Experimental Section Materials: The electropolymerization was performed in acetonitrile (AN) 99.9+% extra dry solution (Acros) with 0.1 M tetraethylammonium tetrafluoroborate (TEAT) and 1-2 mM corrole monomer dissolved in the solution. The electropolymerization was carried out under inert atmosphere of Ar. Three-electrode miniature Teflon electrochemical cell (200 µL) was used with either glassy carbon or indium thin oxide (ITO) as working and counter electrodes. An Ag wire was used in this cell as pseudo-reference electrode. The obtained polymetallo-corrole was rinsed with AN and dried afterwards in open air. For testing the monomer deposited on glassy carbon electrode (GCE), 5 µL of solution of 1.26*10-4 M monomer in AN were added dropwise to the disk of the RRDE electrode and left to dry at room temperature for 20 minutes. For testing the monomer on BP2000, a slurry of 10 mg BP2000/1mL ACN/ 0.56 mM CoTAC left for 24h under rotation. Then, the AN was removed and replaced with 1mL isopropanol (IP)/0.2% Nafion. 10 µL of that slurry dried on RRDE electrode for testing. For testing the polymer on GCE, the monomer was polymerized on the RRDE disk electrode from solution of 2 mM monomer/0.1 M TEAT in AN by cycling the potential between 0.00 and 0.8 V vs. Ag pseudoreference (as described above) for 15 cycles. For testing the polymer on BP2000, 10 µL of from slurry of 10 mg BP2000/1mL IP/ 0.2% Nafion dried on RRDE electrode and then coated with polymer with the same procedure as on GCE. In both cases, after the polymerization the electrode was left to dry at room temperature overnight before the measurements.

, = −0.201/ ʋ/ / ∗ Where A is the surface area of the electrode disk, D and ∗ are the oxygen diffusion coefficient (1.5*10-5 cm2s-1 in 0.5 M H2SO2 and 1.9*10-5 cm2s-1 in 0.1 M KOH) and the bulk concentration of oxygen (1.3*10-6 mol mL-1 in 0.5 M H2SO2 and 1.1*10-6 mol mL-1 in 0.1 M KOH) respectively, ν is the kinematic viscosity (0.01 cm2 s-1) and ω is the rotation speed (rpm). Electrochemical quartz crystal microbalance (EQCM) measurements were conducted with Seiko EG&G quartz crystal analyzer (QCA922A). Static cell (092-QCA-FC) used to the EQCM measurements with Pt wire as counter electrode and Ag/AgCl as reference. The QCM electrodes (QAA9M-AU) were AT-cut quartz crystal coated with 300 nm Au (diameter of 5 mm). the calibration resonance frequency was 9 MHz. FTIR-ATR spectra were recorded using a Nicolet iS 50 spectrophotometer, Thermo scientific, with ATR diamond crystal. High resolution scanning electron microscopy (HRSEM) measurements were conducted with Magellan 400 L. The sample was coated with Iridium by sputtering (Quorum, Q 150 T ES). Supporting Information SI includes synthesis procedures, experimental information, graphical schemes, equations and parameters. Acknowledgements The authors would like to thank The Israeli Ministry of Energy, VATAT and the Fuel Choices and Smart Mobility Initiative in the Israeli Prime Minister’ Office for supporting this work. A.F. would like to thank the Israeli Ministry of Energy

Characterization: All of the electrochemical work in this paper was conducted using a BioLogic VSP potentiostat. Rotating ring-disk electrode (RRDE) measurements were conducted with a glassy carbon

7 ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

for his Scholarship. This work is done in the frame work of the Israeli Fuel Cells consortium (part of

the Israeli National Center for Electrochemical Propulsion).

References

1. Chatterjee, S.; Sengupta, K.; Samanta, S.; Das, P. K.; Dey, A. Concerted proton–electron transfer in electrocatalytic O2 reduction by iron porphyrin complexes: axial ligands tuning H/D isotope effect. Inorganic chemistry 2015, 54, 2383-2392. 2. Chatterjee, S.; Sengupta, K.; Hematian, S.; Karlin, K. D.; Dey, A. Electrocatalytic O2-Reduction by Synthetic Cytochrome c Oxidase Mimics: Identification of a “Bridging Peroxo” Intermediate Involved in Facile 4e–/4H+ O2-Reduction. Journal of the American Chemical Society 2015, 137, 12897-12905. 3. Smith, K. M.; Falk, J. E. Porphyrins and metalloporphyrins. Elsevier Amsterdam: 1975. 4. Elbaz, L.; Wu, G.; Zelenay, P. Heattreated non-precious-metal-based catalysts for oxygen reduction. In Electrocatalysis in Fuel Cells, Springer: 2013, pp 213-246. 5. Sharabi, R.; Wijsboom, Y. H.; Borchtchoukova, N.; Finkelshtain, G.; Elbaz, L. Methodology for the design of accelerated stress tests for non-precious metal catalysts in fuel cell cathodes. Journal of Power Sources 2016, 335, 56-64. 6. Mahammed, A.; Gross, Z. Metallocorroles as Electrocatalysts for the Oxygen Reduction Reaction (ORR). Israel Journal of Chemistry 2016, 56, 756-762. 7. Schechter, A.; Stanevsky, M.; Mahammed, A.; Gross, Z. Four-electron oxygen reduction by brominated cobalt corrole. Inorganic chemistry 2011, 51, 22-24. 8. Zhang, W.; Lai, W.; Cao, R. Energyrelated small molecule activation reactions: oxygen reduction and hydrogen and oxygen evolution reactions catalyzed by porphyrinand corrole-based systems. Chemical reviews 2016, 117, 3717-3797. 9. Tanaka, A.; Fierro, C.; Scherson, D.; Yaeger, E. Electrocatalytic aspects of iron

phthalocyanine and its. mu.-oxo derivatives dispersed on high surface area carbon. Journal of Physical Chemistry 1987, 91, 3799-3807. 10. Cao, R.; Thapa, R.; Kim, H.; Xu, X.; Kim, M. G.; Li, Q.; Park, N.; Liu, M.; Cho, J. Promotion of oxygen reduction by a bioinspired tethered iron phthalocyanine carbon nanotube-based catalyst. Nature communications 2013, 4. 11. Gryko, D. T.; Fox, J. P.; Goldberg, D. P. Recent advances in the chemistry of corroles and core-modified corroles. Journal of Porphyrins and Phthalocyanines 2004, 8, 1091-1105. 12. Grigg, R.; Hamilton, R.; Jozefowicz, M.; Rochester, C.; Terrell, R.; Wickwar, H. A spectroscopic study of the protonation of porphins and corroles. Journal of the Chemical Society, Perkin Transactions 2 1973, 407-413. 13. Wang, Z.; Lei, H.; Cao, R.; Zhang, M. Cobalt corrole on carbon nanotube as a synergistic catalyst for oxygen reduction reaction in acid media. Electrochimica Acta 2015, 171, 81-88. 14. Lei, H.; Liu, C.; Wang, Z.; Zhang, Z.; Zhang, M.; Chang, X.; Zhang, W.; Cao, R. Noncovalent immobilization of a pyrenemodified cobalt corrole on carbon supports for enhanced electrocatalytic oxygen reduction and oxygen evolution in aqueous solutions. ACS Catalysis 2016, 6, 6429-6437. 15. Dogutan, D. K.; Stoian, S. A.; McGuire Jr, R.; Schwalbe, M.; Teets, T. S.; Nocera, D. G. Hangman corroles: efficient synthesis and oxygen reaction chemistry. Journal of the American Chemical Society 2010, 133, 131-140. 16. Levy, N.; Mahammed, A.; Friedman, A.; Gavriel, B.; Gross, Z.; Elbaz, L. Metallocorroles as Non ‐ Precious Metal 8

ACS Paragon Plus Environment

Page 8 of 11

Page 9 of 11 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

American Chemical Society 1980, 102, 6027-6036. 25. Le Mest, Y.; Inisan, C.; Laouénan, A.; L'Her, M.; Talarmin, J.; El Khalifa, M.; Saillard, J.-Y. Reactivity toward dioxygen of dicobalt face-to-face diporphyrins in aprotic media. Experimental and theoretical Aspects. Possible mechanistic implication in the reduction of dioxygen. Journal of the American Chemical Society 1997, 119, 6095-6106. 26. Zagal, J. H.; Páez, M. A.; Silva, J. F. Fundamental aspects on the catalytic activity of metallomacrocyclics for the electrochemical reduction of O2. In N4Macrocyclic Metal Complexes, Springer: 2006, pp 41-82. 27. Gasteiger, H. A.; Markovic, N. M. Just a Dream-or Future Reality? Science 2009, 324, 48-49. 28. Chen, S.-M.; Chen, Y.-L.; Thangamuthu, R. Electropolymerization of iron tetra (o-aminophenyl) porphyrin from aqueous solution and the electrocatalytic behavior of modified electrode. Journal of Solid State Electrochemistry 2007, 11, 14411448. 29. Bettelheim, A.; Ozer, D.; Harth, R.; Murray, R. W. Electrochemistry of various substituted aminophenyl iron porphyrins: Part I. Redox properties of dissolved, adsorbed and electropolymerized species. Journal of electroanalytical chemistry and interfacial electrochemistry 1989, 266, 93108. 30. Bruti, E. M.; Giannetto, M.; Mori, G.; Seeber, R. Electropolymerization of Tetrakis (o ‐ aminophenyl) porphyrin and Relevant Transition Metal Complexes from Aqueous Solution. The Resulting Modified Electrodes as Potentiometric Sensors. Electroanalysis 1999, 11, 565-572. 31. Lucero, M.; Ramírez, G.; Riquelme, A.; Azocar, I.; Isaacs, M.; Armijo, F.; Förster, J.; Trollund, E.; Aguirre, M.; Lexa, D. Electrocatalytic oxidation of sulfite at polymeric iron tetra (4-aminophenyl) porphyrin—modified electrode. Journal of Molecular Catalysis A: Chemical 2004, 221, 71-76.

Electrocatalysts for Highly Efficient Oxygen Reduction in Alkaline Media. ChemCatChem 2016. 17. Levy, N.; Mahammed, A.; Kosa, M.; Major, D. T.; Gross, Z.; Elbaz, L. Metallocorroles as Nonprecious ‐ Metal Catalysts for Oxygen Reduction. Angewandte Chemie International Edition 2015, 54, 14080-14084. 18. Levy, N.; Shpilman, J. S.; Honig, H. C.; Major, D. T.; Elbaz, L. A surprising substituent effect in corroles on the electrochemical activation of oxygen reduction. Chemical Communications 2017, 53, 12942-12945. 19. Yeager, E. Electrocatalysts for O2 reduction. Electrochimica Acta 1984, 29, 1527-1537. 20. Kadish, K. M.; Frémond, L.; Burdet, F.; Barbe, J.-M.; Gros, C. P.; Guilard, R. Cobalt (IV) corroles as catalysts for the electroreduction of O 2: reactions of heterobimetallic dyads containing a face-toface linked Fe (III) or Mn (III) porphyrin. Journal of inorganic biochemistry 2006, 100, 858-868. 21. Kadish, K. M.; Frémond, L.; Ou, Z.; Shao, J.; Shi, C.; Anson, F. C.; Burdet, F.; Gros, C. P.; Barbe, J.-M.; Guilard, R. Cobalt (III) corroles as electrocatalysts for the reduction of dioxygen: reactivity of a monocorrole, biscorroles, and porphyrin− corrole dyads. Journal of the American Chemical society 2005, 127, 5625-5631. 22. Hempstead, M. R.; Lever, A.; Leznoff, C. C. Electrocatalytic reduction of molecular oxygen by mononuclear and binuclear cobalt phthalocyanines. Canadian journal of chemistry 1987, 65, 2677-2684. 23. Pailleret, A.; Bedioui, F. Electropolymerized metalloporphyrin metallophthalocyanine and metal Schiff base complex films: applications to biomimetic electrocatalysis and bioelectroanalysis. In N4-Macrocyclic Metal Complexes, Springer: 2006, pp 363-438. 24. Collman, J. P.; Denisevich, P.; Konai, Y.; Marrocco, M.; Koval, C.; Anson, F. C. Electrode catalysis of the four-electron reduction of oxygen to water by dicobalt face-to-face porphyrins. Journal of the 9

ACS Paragon Plus Environment

ACS Catalysis 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

32. Bettelheim, A.; White, B.; Raybuck, S.; Murray, R. W. Electrochemical polymerization of amino-, pyrrole-, and hydroxy-substituted tetraphenylporphyrins. Inorg. chem 1987, 26, 1009-1017. 33. Evans, J. The vibrational assignments and configuration of aniline, aniline-NHD and aniline-ND2. Spectrochimica Acta 1960, 16, 428-442. 34. Wojciechowski, P. M.; Zierkiewicz, W.; Michalska, D.; Hobza, P. Electronic structures, vibrational spectra, and revised assignment of aniline and its radical cation: Theoretical study. The Journal of chemical physics 2003, 118, 10900-10911. 35. Sapurina, I. Y.; Shishov, M. Oxidative polymerization of aniline: molecular synthesis of polyaniline and the formation of supramolecular structures. 2012. 36. Cotarelo, M.; Huerta, F.; Mallavia, R.; Morallon, E.; Vázquez, J. On the polymerization of 2-aminodiphenylamine: An electrochemical and spectroscopic study. Synthetic metals 2006, 156, 51-57. 37. Cotarelo, M.; Huerta, F.; Quijada, C.; Mallavia, R.; Vazquez, J. Synthesis and characterization of electroactive films deposited from aniline dimers. Journal of the Electrochemical Society 2006, 153, D114-D122. 38. Losito, I.; Palmisano, F.; Zambonin, P. G. o-Phenylenediamine electropolymerization by cyclic voltammetry combined with electrospray ionization-ion trap mass spectrometry. Analytical Chemistry 2003, 75, 4988-4995. 39. Losito, I.; De Giglio, E.; Cioffi, N.; Malitesta, C. Spectroscopic investigation on polymer films obtained by oxidation of ophenylenediamine on platinum electrodes at different pHs. Journal of Materials Chemistry 2001, 11, 1812-1817. 40. Walter, M. G.; Wamser, C. C. Synthesis and characterization of electropolymerized nanostructured aminophenylporphyrin films. The Journal of Physical Chemistry C 2010, 114, 7563-7574. 41. Walter, M. G.; Wamser, C. C. Synthesis and characterization of electropolymerized porphyrin nanofibers.

MRS Online Proceedings Library Archive 2007, 1013. 42. Elbaz, L.; Korin, E.; Soifer, L.; Bettelheim, A. Mediation at High Potentials for the Reduction of Oxygen to Water by Cobalt Porphyrin-Quinone Systems in Porous Aerogel Carbon Electrodes. Journal of the Electrochemical Society 2010, 157, B27-B31. 43. Elbaz, L.; Korin, E.; Soifer, L.; Bettelheim, A. Electrocatalytic oxygen reduction by Co(III) porphyrins incorporated in aerogel carbon electrodes. Journal of Electroanalytical Chemistry 2008, 621, 9196.

10 ACS Paragon Plus Environment

Page 10 of 11

Page 11 of 11 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Catalysis

TOC:

11 ACS Paragon Plus Environment